By M. J. Marcinkowski, A. Szirmae, R. M. Fisher

Room -temperature hardness measurements obtained from single and polycrystalline samples of a 47.8 at, pet Cr-Fe alloy which were aged for various times al 500°C show a two-fold increase over that of the unaged alloy after annealing for 1000 hr. A detailed examination of the deformation markings in the neighborhood of the hardness imbressions reveals that twinning becomes an increasingly more important mode of deformation as aging proceeds. this observation is shown to be inconsistent with the Proposals that the transformation is eve of order-disorder On the other hand, the results are in agreement with previous observations of Fisher et al. of a coherent chromium-rich precipitate which forms in an iron-rich matrix as a result of a miscibility gap in this alloy system as proposed by Williams . Using the coherent precipitate hypotlzesis as a model, a detailed analysis of the various possible strengthening contributions to both the slip mid twinning stresses is made. In the case of' slip, lattice friction within the chromium-rich phase and the chemical energy associated with the interface between the two phases contribute about 60pet to the total strength. The contributions from coherency strains and modulus differences are thought to contribute the remaining 40 pet of the strength but are difficult to evaluate because of uncertainties regarding the flexibility of the dislocation line. All of the factors have nearly the same or else a smaller effect on the twinning stress in the aged alloy. Twinning is never observed in the unaged alloy because the twinning stress is much higher- than that for slip. With increased aging times, the various contributions to the total stress for both twinning and slip increase, but most of those for slip increase much more rapidly, so that, in the fully aged alloy, it surpasses the stress for twin propagation. When a twin is nucleated by the chance occurrence of an internal stress concentration during a test, the subsequent twin burst results in a low hardness reading. FeRNTIC Fe-Cr alloys from about 15 to 80 at. pet Cr content show considerable change in properties such as hardness, electrical resistivity, saturation magnetization, and so forth, after aging in the vicinity of 500°C.* The most marked change is a large increase in hardness accompanied by a sharp decrease in ductility, so the phenomenon has often been referred to as the 475°C (885°F) em-brittlement problem. Changes in microstructure are rather subtle and most investigators have not been able to observe any X-ray diffraction or metal-lographic changes during aging. There is little doubt that the phenomenon is inherent to the Fe-Cr binary system and is not directly related to the formation of a phase. Two distinct schools of thought have developed during the past decade concerning this problem. Masumoto, Saito, and sugiharal have concluded, from their own specific-heat measurements, that atomic ordering occurs in this temperature range. Pomey and Bastien2 have also attributed the changes in physical properties with aging in the neighborhood of 500°C to atomic ordering. In addition, Takeda and Nagai3 claimed to have found X-ray verification for superlattices corresponding to the compositions FesCr, FeCr, and FeCr3. However, all known attempts to observe superlattices in Fe-Cr alloys using neutron diffraction, which should be much more sensitive, have been unsuccessful. These have been reported by Shull et al.4 for 25 at. pet Cr, williams5 for 75 at. pet Cr, and Tisinai and samans6 for a 28.5 at. pet Cr. steel. The second and more prevalent opinion ascribes the 475°C embrittlement phenomenon to the formation of a coherent precipitate due to the occurrence of a miscibility gap in the Fe-Cr system below about 550°C. This latter concept was first indicated by the results of Fisher, Dulis, and Carroll,7 who were able to extract fine particles about 200Å in diameter from samples of 28.5 at. pet Cr steels aged from 1 to 3 years at 475°C. The extracted material was found to be nonmagnetic, to have a bee structure with a lattice parameter between that of iron and chromium, and to contain about 80 at. pet Cr. Williams and paxton8 and williams5 confirmed these results and first explicitly proposed the existence of a miscibility gap below the a region in the equilibrium diagram. Alloys aged within this gap

Jan 1, 1964

This discussion of the paper of Chester W. Washburne should have been printed following the remarks of H. A. Wheeler, in Bulletin No. 100, April, 1915, pp. 835 and 836, but was inadvertently omitted. ROSWELL H. JOHNSON:-There is one reason why the hydrostatic interpretation of gas pressure is not wholly acceptable. As we go clown in the sands we seem to get excesses of gas. Particularly in this field it becomes excessive in quantity relative to the amount of water in the sand. If this holds in other fields as well it must mean that there has been an ascension of water, because these sedimentaries when laid down, were filled with connate water. If we do get an ascension of connate water, produced by some such phenomena as its expansion by heat or by the formation of new gas by pressure upon organic materials at great depth, we can hardly expect the pressure to be controlled merely hydrostatically. * In reply to Mr. Wheeler's inquiry as to gas wells with pressure higher than hydrostatic pressure, I would cite the original wells given by Orton on which he based the hydrostatic theory. He used in his calculation a head of 600 ft. above tide, assuming the outcrop of the Manitoulin Islands to be in Lake Superior, whereas the Trenton does not outcrop at Lake Superior. The Manitoulin Islands are in Lake Huron, the level of which is 580 ft. above tide. No allowance is made for the lower density of the fresher water near the outcrop, the weight taken for the whole column being the water of high density found at the wells.

Jan 5, 1915

By Arne Bergholm

Australian rutile was chlorinated in the presence of CO or carbon. The chlorination velocity in CO was found to be strongly influenced by temperature and proportional to the CO concentration, but independent of the Cl, concentration. In the presence of carbon, the reaction velocity is much higher. The reactivity of the carbon and the distance between the carbon and the rutile surfaces are important variables. The reaction velocity is approximately proportional to the Cl, concentration and independent of the CO concentration of the surrounding atmosphere. Experiments with fluidized-bed chlorination of carbon-rutile mixtures indicate that the motion of the bed has little influence on the reaction velocity. At low temperatures, the chlorination velocity of dense tablets is much greater than that of TiO, coke mixtures suitable for fluidization. The reaction mechanism is discussed. In the industrial production of TiCl, rutile is chlorinated in the presence of carbon. Disregarding intermediate steps, the reaction may be expressed by the following equations: The ultimate object of this study was to find out whether the reaction velocity was higher in fluidized bed operation compared with chlorination of pelle-tized carbon-rutile mixtures. From a literature survey and preliminary experiments it was learned that some basic knowledge about the reaction mechanism was needed for a good experimental design. Therefore the following sets of experiments were carried out: 1) Studies on the reaction velocity in the chlorination of rutile with CO as the only reducing agent. 2) Chlorination of separate rutile-carbon tablets. 3) Chlorination of rutile-carbon tablets at different temperatures with various kinds of carbon, various grain sizes, and various tablet-making techniques. This series of experiments was carried out not only with pure chlorine but also with mixtures of chlorine with argon, CO and CO,. 4) Chlorination of rutile-carbon tablets made in a strictly standardized manner. 5) Chlorination of static-bed rutile-carbon mixtures. 6) Fluidized-bed chlorination of the same mixture. The experiments 4 to 6 formed the final and direct test of the main question: Static bed vs fluidized bedo. Although there are many patents and papers dealing with the general aspects of chlorination, only few experiments from which detailed information can be obtained have been reported in the literature. Pamfilov and coworkersl3 have studied chlorination of TiO, with CO or carbon as the reducing agent. They found that the weight decrease per hour at 600o to 800°C amounted to 11 to 14 pct with CO and 45 to 51 pct with carbon. They suggest that phosgene might be an intermediate in the chlorination of TiO,. Takimoto and Hattori have chlorinated reduced titanium oxide (TiO) and found a very high rate of TiC1, -production. They proved that the composition of the gas from the chlorination of rutile-carbon mixtures contained mainly CO. They reported for instance 74.7 pct CO, and 5.6 pct CO at 800°C at which temperature the Boudouard equilibrium composition is 12 pct CO and 88 pct CO. Seligman and Segerchano6 have studied the chlorination of TiO. They proved that Ti0 and chlorine react rather rapidly at temperatures as low as 300°C. Above 400°C, the reaction was complete. At 500°C the velocity of this reaction was much higher than was chlorination of TiO, + C. McTaggart,7 Nishimura, et al. and Wilskam have chlorinated mixtures of carbon and various kinds of rutile or beneficated ilmenite. Nishimura, et al. also report the results from reduction of TiO, with H2, CO, or carbon. At 900°C only 1 pct Ti O is formed in 2 hrs. At 1100°C 23.1 pct Ti, 0, was formed if elementary carbon was present. No carbide formation occurred below 1400°C. McIntosh and Cofferll have observed that the CO, content of the exit gases from chlorination of rutile and calcined petroleum coke is appreciably higher than found in the Boudouard equilibrium. At 900°C the ratio (CO, /CO + CO) is about 80 pct, whereas the equilibrium value is about 2 pct. W. E. Dunn12 has studied the chlorination rates of several TiO,-bearing minerals with CO + Cl, or COCl . Chlorinations were carried out either in a fluidized reactor or a fixed-bed reactor, both having a 30-mm diameter. The results obtained in both reactors were comparable. It was proved that benefi-ciated ilmenite (i.e., ilmenite from which the iron oxide had been removed by chlorination) was chlorinated 10 times faster thanrutile. Sore1 slag showed an intermediate rate. When phosgene is used, the

Jan 1, 1962

By J. E. Hilliard

Various methods are given for estimating the number per unit volume and average size of convex particles from measurements on a projection through a slice of the structure. The determination of the size distribution is considered specifically for spherical particles. The results are applicable to any type of transmission microscopy and also to the correction of measurements made by reflected light on semitransparent materials. WITH the advent of electron transmission microscopy, the metallurgist is confronted with the problem of relating a projected image to the three-dimensional properties of the structure. This paper deals with the estimation of the number per unit volume and size of particles dispersed in a matrix. The case of convex particles will first be treated (the results will be applicable as approximations to particles of more general shape) and then spherical particles will be considered specifically. The latter represent a special case frequently encountered in practice and one which is also amenable to a calculation of the effect of overlap on the observed particle-size distribution. Although the present treatment was prompted by the needs of the electron microscopist, the results are applicable to transmission studies with any type of radiation. In addition, they can be used in the analysis of semitransparent materials by reflected light, the depth of light penetration corresponding to the thickness of the slice or section used in the transmission studies. 1) CONVEX PARTICLES 1.1) General Expression for N,. We will suppose that a "center" (such as the center of mass) is assigned to each particle. The convention used for defining the center is immaterial providing it does not depend on the orientation or location of the particle. Consider a slice through the structure having a pair of parallel faces a distance t apart. It will be assumed that the slice is randomly located with respect to its perpendicular distance from some fixed point, but it is not necessary to assume that its orientation is random. Our problem is to deduce the relationship between the number of par- ticle images seen on an orthogonal projection through the slice with the number, Nv, of particles per unit volume in the original structure.* *Symbols are listed in the Table. The expected number of particles with centers lying within the slice is Nvt per unit area. In addition, there will be elements in the slice contributed by particles whose centers lie without. The number of such elements will be the same as the number of intersections occurring on a two-dimensional plane through the structure; namely N~K, where K is the mean distance, Fig. 1, between tangent planes to a particle averaged over all particles, i.e., Where Ni is the number of particles of class i having the same shape and size, and pi (4, 8) is the probability that an i particle will have a given orientation with respect to the slice. If the particles are randomly oriented, then K is independent of the orientation of the slice and equal to the mean cali-per diameter. The total number of particle elements in the slice is therefore Nv(t + K) per unit area, but fewer will be seen as separate images on the projection plane because of overlap. If MA is the number of elements "lost" by overlap, the number of images per unit area will be NA = Nv(t + K) -MA 121 MA is a function of the slice thickness and must vanish at t = 0. As t increases, NA at first increases, reaches a maximum, and thereafter decreases as the overlap term MA becomes predomi-

Jan 1, 1962

By John S. Johnson, Thomas Fraser

SIZING is the process of separating mixed particles into groups of particles all of the same size, or into groups in which all particles range between certain definite maximum and minimum sizes. In coal preparation, sizing is generally accomplished by passing the coal over screens. Separation by differential settling in air or water currents has been adapted to the special field of separating very fine sizes, and these processes are in commercial use to a relatively small extent in the coal industry. Separation with screens is a very old industrial practice. Agricola described the use of screens for ore treatment in the middle ages. In the literature of the British coal industry references were made to the screening of coal as early as 1589, but the practice of extensive sizing for the market did not become general until the last half of the nineteenth century. In America, the practice of sizing developed first in the Pennsylvania anthracite region, beginning with the use of rakes' in the mine working places to recover coarse coal. This mining procedure left the fines in the mine. Preparation outside the mine started with the installation of station¬ary cast-iron plates with 4 to 6-in. square holes. The run-of-mine coal was dumped upon the platforms, the large pieces of rock were picked out by hand, and the large lumps of coal were broken with hammers. The term "breaker," which still applies to the anthracite-preparation plant, originated with this practice, but the term is no longer descriptive of the entire function of the plant. In 1884, the first power-operated anthracite coal breaker' was erected by Gideon Bart at his colliery at Wolf Creek near Minersville, Pa. This plant utilized a system of rolls for breaking the coal and revolving screens for sizing. The plant was driven by a steam engine. It 'could handle

Jan 1, 1943

By Robert Rhea Goodrich

This research was done partly in the non-ferrous laboratory of the Department of Metallurgy of Columbia University, under the direction of Dr. Edward I?. Kern, and completed elsewhere. Acknowledgment is due to Prof. Arthur L. Walker, Dr. Edward F. Kern and Dr. William Campbell of the Department of Metallurgy, for their kind advice and for the inspiration derived from their instruction. This report is given under the following heads: Petrographic Description (Microscopic Study); Sampling and Preparing Ore for Treatment; Chemical Analysis; Treatment of Ore. Petrogeaphic DescRiption Texture: variable. Fine to medium mixed aggregate. Original Structure: Obscurc. Secondary structure: Fractured; healed. Mineralogy (Minerds are grouped for interpretation purposes and are arranged, in each group in approximate order of abundance)

Jan 1, 1916

By Walter Kauzmann

ALL viscous or plastic flow of incompressible matter is the result of shear strain; the changing shape of any body that is being plastically deformed can be completely described in terms of the shear strain occurring at each point in the body.[t] Furthermore, the relative amounts of shear strain occurring in different parts of a body under stress depend upon the relative rates of shear strain at those different points, so that if the dependence of the shear rate of any material on the temperature, shear stress, previous history, etc., were understood, the principles of plastic deformation would be known, and we could calculate how a body made of a given material, having a given shape, and subject to a specified system of forces, would change its shape with time. It may be said, then, that the problem of plasticity resolves itself into, first, the problem of the rates of pure shear processes, and second, the application of what is known about pure shear to actual cases. It is the purpose of this work to investigate the former problem -i.e., the dependence of shear rates on temperature, stress, etc.-from the standpoint of recent developments in the field of chemical-rate theory and with particular reference to the phenomena occurring in the creep of metals and in the plastic flow of crystalline solids in general. It is left for the mechanical engineer, and perhaps the expert in hydrodynamics, to deal with the problem of applications1 RESOLUTION OF MACROSCOPIC SHEAR INTO MICROSCOPIC MOVEMENTS; RESEMBLANCE TO CHEMICAL REACTIONS Just as any large body is made up of many small units, or atoms, so macroscopically observable shear is the result of many microscopic unit shear processes; just as the understanding of the behavior of large bodies demands the understanding of the atoms of which it is made, so the understanding of macroscopic shear demands the understanding of these fundamental unit processes. The study of shear from this "atomistic" point of view has made considerable progress. There has been fairly complete understanding of shear processes in gases for a long time, at least for nonturbulent flow, as a chapter on gaseous viscosity in any text on the kinetic theory of gases will prove. In recent years Andrade2 and Eyring3 have presented important theories for the flow of liquids and amorphous solids. Becker,4 Orowan,5 Taylor,6 Burgers,7 and Kanter8 have considered the

Jan 1, 1941

By Charles E. Hughes

HERBERT HOOVER had to sit through an hour and a half of eulogy of himself at Carnegie Hall last night, said the Sun and New York Herald of Feb. 19. When his turn to answer came he remarked that, although one of the speakers had referred to him as a modest man, he would never, in view of this experience, be able to prove it. The occasion was the presentation by the Civic Forum to Mr. Hoover of its medal of honor for distinguished service, the only recipients in past years having been General Goethals, Thomas A. Edison, and Alexander Graham Bell. Only by distortion of intent could there be said to be anything political in the affair, which was carefully described by the chairman, Charles E. Hughes, as non-partisan. Nevertheless, the praise bestowed on the former Food Administrator by the former Republican candidate for President, proved specially interesting to a much applauding audience which filled the hall to the uppermost gallery. A piece of real news was supplied by Horace V. Winchell, whom Mr. Hoover succeeded on Tuesday as President of the American Institute of Mining and Metallurgical Engineers. He said that Mr. Hoover, when in Europe after the . armistice, caused to be collected the literature of the war in all Europe.

Jan 1, 1920

By Y. G. Shiau, J. E. Burke

Several attempts have been made to account for the fact that grains in a fully recrystallized metal will coarsen on annealmg. Two fundamentally different hypotheses have been advanced, with several variations of each. One school considers that the cause of grain growth is the surface energy of the grain boundary. The theory of Jeffriesl that grain size and grain size contrast control growth is an example. The second school considers the primary cause to be a difference in the lattice energy on either side of the grain boundary. The more perfect grains are considered to grow at the expense of their less perfect neighbors, with a decrease in free energy, and a consequent increase in the stability of the system. Burgers2 presents the case for the strain or lattice imperfection theory of grain growth quite completely. The latter theory is attractive, since there is no doubt that differences in lattice energy or lattice perfection can cause grain boundary migration. A recrystallization nucleus grows for this reason as was beautifully demonstrated by van Arkel and Ploos van Amstel.³ Although it is generally stated that grain growth does not precede recrystallization, several workers4-5 have shown that small strains may induce a single crystal in an aggregate to grow, or at least may cause some grain boundary migration. The origin and nature of the imperfections that are considered to be responsible for normal grain growth have never been clearly described, but it is generally agreed that they are a consequence of the difficulty of atomic reorientation in the solid state, and that they do not seriously differ from the type of imperfection that can be introduced by mechanical deformation. An object of the present work was to determine whether the introduction of mechanical deformation would cause grain growth in a specimen which would not otherwise show it under the conditions used. It was also planned to determine the effect of such deformation on the rate of growth in a specimen which would show growth in the unstrained condition. Recently Maddigan and Blank6 have indicated that slightly strained specimens of alpha brass can undergo considerable growth prior to recrystallization if annealed at low temperatures. French7 has reported that at deformations less than 17 pet it is very difficult to detect the beginning of recrystallization in the same material. It was therefore planned to broaden this work to include a complete study of the microscopic behavior of alpha brass under condition~ of temperature, time, grain size and deformation such that recrystallization would not occur or would occur to only a Small extent. Experimental Procedure The brass was prepared by melting cathode copper and commercially pure zinc

Jan 1, 1949

By J. E. Burke, Y. G. Shiau

Several attempts have been made to account for the fact that grains in a fully recrystallized metal will coarsen on annealmg. Two fundamentally different hypotheses have been advanced, with several variations of each. One school considers that the cause of grain growth is the surface energy of the grain boundary. The theory of Jeffriesl that grain size and grain size contrast control growth is an example. The second school considers the primary cause to be a difference in the lattice energy on either side of the grain boundary. The more perfect grains are considered to grow at the expense of their less perfect neighbors, with a decrease in free energy, and a consequent increase in the stability of the system. Burgers2 presents the case for the strain or lattice imperfection theory of grain growth quite completely. The latter theory is attractive, since there is no doubt that differences in lattice energy or lattice perfection can cause grain boundary migration. A recrystallization nucleus grows for this reason as was beautifully demonstrated by van Arkel and Ploos van Amstel.³ Although it is generally stated that grain growth does not precede recrystallization, several workers4-5 have shown that small strains may induce a single crystal in an aggregate to grow, or at least may cause some grain boundary migration. The origin and nature of the imperfections that are considered to be responsible for normal grain growth have never been clearly described, but it is generally agreed that they are a consequence of the difficulty of atomic reorientation in the solid state, and that they do not seriously differ from the type of imperfection that can be introduced by mechanical deformation. An object of the present work was to determine whether the introduction of mechanical deformation would cause grain growth in a specimen which would not otherwise show it under the conditions used. It was also planned to determine the effect of such deformation on the rate of growth in a specimen which would show growth in the unstrained condition. Recently Maddigan and Blank6 have indicated that slightly strained specimens of alpha brass can undergo considerable growth prior to recrystallization if annealed at low temperatures. French7 has reported that at deformations less than 17 pet it is very difficult to detect the beginning of recrystallization in the same material. It was therefore planned to broaden this work to include a complete study of the microscopic behavior of alpha brass under condition~ of temperature, time, grain size and deformation such that recrystallization would not occur or would occur to only a Small extent. Experimental Procedure The brass was prepared by melting cathode copper and commercially pure zinc

Jan 1, 1949

By G. K. Manning, W. E. Few

WORK on the effect of vacuum heat treatment of 0.040 in. diam sintered and wrought molybdenum wires has been sponsored by the Office of Naval Research at Battelle for the past several years. An electrical resistance furnace' capable of maintaining a vacuum of less than 0.1 micron of mercury at temperatures as high as 4000 °F was used for heat treating the wires. Early in the work, it was found that the introduction of a few microns pressure of oxygen into the furnace resulted in a rapid increase in the oxygen content of the wire specimens and the appearance of a discrete oxide phase. Subsequent elimination of the oxygen atmosphere caused the disappearance of the oxide phase. This was used to determine the solid solubility of oxygen in molybdenum over the temperature range of 2000" to 3000°F.2 It was observed that, with the disappearance of the oxide phase, the wires regained some ductility. Single-phased wires possessed from 5 to as much as 40 pct elongation in 2 in. Later, attention became centered on determining the cause of this wide range in ductility. Wires containing less than 0.002 pct C, less than 0.0007 pct 0, less than 0.0005 pct N, and less than 0.00003 pct H exhibited the erratic ductility noted above. These percentages represent approximately the limit of accuracy of presently available methods of analysis and thus it became apparent that chemical analysis would be of little help in the study. A number of possible explanations for the wide range in ductility were suggested during the course of the work. It was first suspected that variations in the grain size of the recrystallized wire specimens might be responsible. Wire from several lots of material was available. One of these lots tended to develop very large grains when recrystallized, the others all developed an ASTM grain size of 3 to 4 when heated above 2700°F. No correlation between grain size and ductility could be found. It was thought that back diffusion of oil from the diffusion pump might cause contamination of the wire, principally with carbon, but when wires were treated without cooling the cold trap in the pumping system,

Jan 1, 1956

By I. D. Hagar

WHEN the history of American business during these momentous war years is written, an absorbing chapter will be devoted to the Maclntyre Development, in northern New York. It will tell of a timely mining project, deep in the wilds of the Adirondacks, blasted into being by Axis torpedoes. It will recount the labors of 1500 engineers and workmen, miles from a highway, rail line, or power source, who built a huge enterprise in a few short months' time. And it will list these major contributions to the war effort: more than a quarter million tons per year of ilmenite, source of titanium dioxide-man's most opaque white pigment-to be used in paints for warships, tanks, guns, planes and the plants that build them; as a co-product, over 500,000 tons each year of magnetite-an important type of iron ore- to help feed the cavernous maw of America's wartime steel industry.

Jan 1, 1942

By M. J. Bradley, P. H. Dike

THE art of melting nonferrous metals, in smelting, casting, and in compounding of alloys, is highly dependent on a knowledge of the temperature of the metal. This knowledge may reside in the experience and judgment of the melter, or it may be based on measurement by suitable instruments. It-is our purpose to discuss briefly the instruments available for such measurements, and more at length the present, practice in molten metals, without recommendation. In the limits of time and space allotted, we can do little more than mention the available methods of measurement that are directly applicable in this field. In the 1939 edition of the Metals Handbook, issued by the American Society for Metals, pages 285-310, there is a more extensive discussion of pyrometry than can be attempted here, which should be referred to for details we must omit. For reasons that will appear, thermoelectric pyrometry will constitute the major portion of our discussion of the subject, only limited attention being given to radiation or optical pyrometry. METHODS OF MEASUREMENT THERMOELECTRIC PYROMETRY A thermocouple consists of two dissimilar wires, or a wire inside a tube of a dissimilar material, joined together at one end, which is placed in the region or medium where the temperature is to be measured, while the other ends are connected through suitable lead wires to a voltage-measuring device, which may be a millivoltmeter or a potentiometer. An electromotive force is generated in the circuit, which is proportional to the difference in temperature between the hot junction and the junctions of the lead wires to the measuring instrument. If this latter temperature is maintained constant, the e.m.f. measured varies only with the temperature of the hot junction. Every thermoelectric pyrometer is calibrated for a particular cold-junction temperature such as 0°F., 32°F. or 75°F., but usually it is more practical to compensate instrumentally over the probable range of cold-junction temperatures than to maintain the junction at the particular temperature for which the instrument was calibrated. Thermocouple Materials Only a very few pairs of metals are in frequent use for pyrometric measurements. The most generally used are iron-constantan for temperatures up to 1500°F. in oxidizing and up to 1800°F. in reducing atmospheres and chromel-alumel, which may be used in oxidizing atmospheres at temperatures up to 2400°F. for intermittent service. The accuracy of the latter deteriorates rapidly at temperatures above 2200°F. Platinum vs. platinum-rhodium thermocouples may be used up to a temperature of 3000°F , but they are easily contaminated by slow absorption of

Jan 1, 1946

By George J. Clark

One of the major problems of operation in the anthracite industry is the disposal and handling of refuse—not because of its complexity but because of the quantity and type of material involved. It is the purpose of this paper to describe the kinds of refuse, methods of disposal, quantities of material to be handled and equipment used, together with present day application at specific operations in the Northern, Eastern Middle, Western Middle and Southern anthracite fields. For the purpose of this paper, refuse is considered to be any material that has no present or foreseeable future value and that must be handled and disposed of in the process of mining and preparing anthracite for market. Included in this classification are tunnel rock, mine rock, cleaner plant refuse, breaker refuse, old timber, ashes and silt. Disposal Methods Old timber is disposed of either by burning or by depositing on the refuse bank. Burning is preferred because timber on the refuse bank is a potential fire hazard. Ashes are deposited on a separate bank, mixed with other refuse, or flushed into old mine workings. In many places, the latter practice has caused considerable difficulty in preparation of coal mined from these areas. In depositing ashes on the surface, it is wise to refrain from mixing them with material containing coal as such contamination may prevent reclamation of the coal in future years. Tunnel work, mine rock, cleaner plant and breaker refuse compose the bulk of the material to be disposed of and handled, and are referred to collectively as "refuse" in this paper. Waste material in or adjacent to the coal beds may be removed at the working face wherever possible. This can be done in flat or lightly pitching beds, and in the Northern field represents a sizable percentage of this type of refuse handled. In the other three coal fields, this method of disposal cannot often be used. Refuse not removed at the working face is taken to the surface and generally is deposited on banks; occasionally it is crushed and flushed into old mine workings. Breaker refuse often is used for constructing berms for silt-retention basins. Disposal Problems The problem of handling refuse is different for each operation, owing to topographical conditions, quantity of material to be handled, anticipated requirements and types of equipment in use elsewhere at the operation. Preparation plants with limited refuse-disposal areas, excessive grades to reach the required elevation and long hauls to disposal areas not readily accessible require the selection of equipment to best meet the conditions. The quantity of refuse to be handled from a given amount of raw material varies considerably throughout the four fields. In mine coal, this varies from a low

Jan 1, 1949

By R. E. Lindstrom, D. G. Peterson, H. J. Heinen

Alkaline alcohol solutions were investigated by the Federal Bureau of Mines for improving the desorption rate of gold and silver from metal-laden activated carbon generated in gold processing circuits. Factors affecting the desorption, such as temperature, alcohol content, type of alcohol, and alkalinity, were studied. Nearly complete metal desorption was obtained in 5 to 6 hr at 80º C using a solution containing about 20 vol-pct alcohol and 1 pct sodium hydroxide. Sodium sulfide was shown to be effective for selectively precipitating silver from the carbon strip solutions, thereby providing a means for producing high- purity gold by subsequent electrolysis.

Jan 1, 1976

By J. J. Foster

MOST of us will, I think, agree that never before in the history of the coal industry has the human side of our business been so important as today. Since, even in wholly mechanized mining, labor cost is such a large percentage of out total cost we are all deeply concerned not only about the present attitude of our employees but particularly about the future, when the industry returns to a "survival of the fittest" basis. Many things could and should be done about our employee relations in the coal business. Failure to recognize these obligations and do something about them may lead to serious consequences, the least serious of which will be the loss not only of many of our better employees but a large portion of our potential employees, as they graduate from our schools to other in¬dustries. Some of these things should be handled by the industry as a whole whereas others should be done by individual companies. Due to varying conditions and size of organizations it would, at best, be necessary to vary a program to meet the individual needs of each operator.

Jan 1, 1945

By Robert B. Kistler, Ward C. Smith

The borate industry is one of the few sectors of the mining and mineral-processing industry which the United States still dominates. Since about 1927, the United States has supplied over half of the world's total boron and borate raw materials, and many of the chemical derivatives as well. Chiefly responsible for this record are companies producing sodium borates from two large deposits in southern California, at Boron (Kramer) and Searles Lake. The sodium borates, or products derived from borax and borax-containing brines, are the preferred borates for industry because they are soluble in water and combine readily with most other chemicals. Calcium borates are required for certain end uses, and these are produced from smaller colemanite-ulexite-probertite bodies. Sodium-free borate compounds also are produced from boric acid, which can be manufactured from either sodium or nonsodium borate minerals. During the past hundred years, the use of boron compounds throughout the world has risen from a few tons per year to the equivalent of over a million tons of B2O3. Leadership in supplying borates shifted from country to country and from region to region during this period, generally as the result of the development of newly discovered deposits that were better in quality, more accessible, or more economically exploitable than previous sources (Table 1). Primary Products and End Uses The principal borate products offered by primary producers in the United States are listed in Table 2. In general, these products are utilized worldwide by almost all consumers, regardless of the original source of the primary borates, In the United States, the primary borates all originate in southern California. Colemanite is produced as crude or processed crude ore from the Death Valley area and is utilized by the fiber glass and ceramic industries without further treatment. Production from Searles Lake, CA is from brines that are processed in chemical plants where borax and other compounds are recovered and the principal borate products are produced. At Boron, CA, the world's leading producer is mining a deposit of mineral borax and operating a chemical refinery. The mineral borax is mined together with included clay, and refined borax or "10-mol" is one of the refinery products. The mineral and the chemical compound are identical, Na2B4O7 • 10H2O. In addition to ship¬ping all major refined borate products from [ ]

Jan 1, 1983

By D. A. Belforti, M. P. Lepie

Spectroscopically pure copper was melted on sapphire plaques in a zydrogen atmosphere. The surface tension of the liquid metal was determined using the sessile drop technique. Measurements were made by direct observation with the aid of a specially const,mcted telescope. The value obtained, 1268 dynes per cm, is compared to that found in the literature. THERE is at this time considerable interest in the use of ceramics for vacuum tubes. The crystalline material is superior to the more conventional glass in mechanical strength, chemical inertness, dielectric properties, ability to withstand high temperatures, and so forth. However, ceramics are much more difficult to seal hermetically with metals than are the glasses. For this reason an investigation was undertaken to determine the wetting and adhesion of metals to ceramics. The sessile drop technique offers a convenient means at elevated temperatures for measuring liquid surface tension, wetting angle, density, spread- ing coefficient, and work of adhesion. Thus, from the contour of a drop of liquid at rest on a solid surface one can obtain a quantitative evaluation of the degree to which the two substances will bond. To this end a special apparatus was constructed so that various molten metals could be observed. Standardization of the apparatus was done initially by measuring the surface tension of copper since this is well documented in the metallurgy literature. Although there are many methods available for the measurement of surface energy,'+ the sessile drop technique has been used most extensively for molten metals and ceramics.5"' Fig. 1 illustrates the dimensions to be measured. From these values, the surface tension of the liquid can be obtained using the Bashforth and bdams' equation and tables.

Jan 1, 1963

By R. A. Haney, S. J. Gigliotti

Over the past ten years, analysis of the acceptability of face ventilation systems has been based on numerical criteria rather than solely a study of air flow and methane patterns in the face area. This type of analysis has become possible primarily because of the instrumentation and mathematical models developed by the Ventilation Division, Pittsburgh Health Technology Center, Mine Safety and Health Administration (MSHA). To properly use these mathematical models, large amounts of methane and airflow data must be collected in the face area during mining activities. To supplement underground testing of face ventilation systems, a full scale model of a face area was built. This model includes a full scale model continuous miner, a face ventilation system, a gas release system, and a remote methane detection system. The remote methane detection system consists of an array of twelve methane sensors located throughout the face area. Data from the sensors are transmitted to strip chart recorders. Methane, air quantity, and other data collected during a test are entered into a computer for analysis. This paper presents the data entry system, the models used for data analysis, the test results, and the application of these results to a face ventilation system.

Jan 1, 1983

By H. C. Stumpf, L. A. Willey, V. L. Fink

Very few studies of the aluminum-sodium system have been reported. Heycock and Neville1 were unable to detect any solubility of sodium in liquid aluminum. Mathewson2 prepared an equilibrium diagram consisting of two horizontal lines at the melting points of the two metals. He was unable to detect solubility at either end of the system. Scheuer3 first developed a method for the chemical determination of sodium in aluminum and then studied the solubility of sodium in liquid aluminum. His method involved heating aluminum with excess sodium under hydrogen until the two liquids were at equilibrium, chilling the melt, and analyzing the aluminum-rich layer. He reported the solubility to be 0.10 pct sodium at 700°C, 0.115 pct at 750°C, and 0.128 pct at 800°C. This paper on the aluminum-sodium system is the twenty-first in a series from the Aluminum Research Laboratories describing equilibrium relations in aluminum alloy systems. Materials The alloys for this investigation were prepared from electrolytically refined aluminum (99.99 pct) and sodium of reagent quality conforming to specifications of the American Chemical Society. Chemical analysis of the aluminum showed the fol- lowing impurities: 0.002 pct Si, 0.002 pct Fe, 0.002 pct Cu, <0.001 pct Mn, 0.002 pct Mg and 0.001 pct Na. The sodium content of all alloys was determined by either chemical or spectro-graphic standard procedures5 No. IIA and No. SI I respectively. Determination of Miscibilitv The boundary of the miscibility gap was determined by a modification of the method of Scheuer3 and of that used by Henry and Cordiano. As finally developed the method was as follows: A fused alumina crucible 25 mm id with 75 mm depth and 1.5 mm wall thickness was placed on the bottom of a container made from a 4-in. length of 1 1/2-in. iron pipe and pipe caps. ?&apos;he space around the sides of the crucible was filled with 40 mesh crystalline alun-dum. A charge of 60 g of aluminum and 10 to 15 g of sodium was placed in the crucible, the sodium first being trimmed and rinsed with iso-pentane to remove kerosene. The container was tightly capped, filled with argon (99.6 pct pure), and heated to the desired temperature (between 670 and 800°C). A positive pressure of argon (about 8 mm of mercury) was maintained through a small pipe to the upper cap. After soaking for from 2 to 5 hr, the container was quenched by directing a stream of water onto the base, so that solidification of the aluminum-rich layer was rapid and essentially unidirectional. Analyses were made on drillings taken from the bottom of the ingots after machining off the surface layers. Pre-

Jan 1, 1949