Search Documents

By Gerhard Derge, Harold Markus

The introductory paper1 of this series described the potential behavior of tin in sodium carbonate and bicarbonate solutions whose pH ranged from 8.4 to 11.2 and demonstrated that significant and reproducible results could be obtained by proper attention to experimental technique. In examining the corrosion of tin under such conditions, it is desirable to know the effects of anions, aside from carbonate, that are likely to be present in commercial materials packaged in tin. Therefore, in this paper the potential behavior of tin in carbonate solutions to which sodium fluoride, chloride, bromide, iodide, sulphate, nitrate, monobasic phos-phate, dichromate, perborate and acetate have been added will be dcscribed. For most of the additions, solutions containing 0.001 and 0.01 moles of the added material were studied. The experimental procedure was exactly the same as that described in the first paper; the pH of the electrolyte was controlled by adjusting the ratio of carbonate to bicar-l,ol~ate as follows: pH 0.1 M NaHC0............................................ 8.4 2 parts 0.1 M XaHCOr, 1 pa.rt 0.1 M NaZCO?................. 9.5 1 part 0.1 M NaHCOs, 2 parts 0.1 M iVa.,C03. ................ 10.0 0.1 M Na2C0............................................. 11.2 The reagents used were all of C.P. grade. The anions studied may be divided into three groups: (1) anions that had little or no effect upon the potential curves—sulphnte, nitrate, and acetate; (2) those that helped to prevent corrosion at low pH only -fuoridc, chloride, bromide, and iodide; (3) those that helped to prevent corrosion at high pH also—phosphate, pcrborate, and chromate. Potential Measurements f The time-potential curves represntative of group 1 are shown in Fig. 1. These are the curves for 0.005 M sulphate ion and their similarity

Jan 1, 1939

By Harold Markus, Gerhard Derge

The introductory paper1 of this series described the potential behavior of tin in sodium carbonate and bicarbonate solutions whose pH ranged from 8.4 to 11.2 and demonstrated that significant and reproducible results could be obtained by proper attention to experimental technique. In examining the corrosion of tin under such conditions, it is desirable to know the effects of anions, aside from carbonate, that are likely to be present in commercial materials packaged in tin. Therefore, in this paper the potential behavior of tin in carbonate solutions to which sodium fluoride, chloride, bromide, iodide, sulphate, nitrate, monobasic phos-phate, dichromate, perborate and acetate have been added will be dcscribed. For most of the additions, solutions containing 0.001 and 0.01 moles of the added material were studied. The experimental procedure was exactly the same as that described in the first paper; the pH of the electrolyte was controlled by adjusting the ratio of carbonate to bicar-l,ol~ate as follows: pH 0.1 M NaHC0............................................ 8.4 2 parts 0.1 M XaHCOr, 1 pa.rt 0.1 M NaZCO?................. 9.5 1 part 0.1 M NaHCOs, 2 parts 0.1 M iVa.,C03. ................ 10.0 0.1 M Na2C0............................................. 11.2 The reagents used were all of C.P. grade. The anions studied may be divided into three groups: (1) anions that had little or no effect upon the potential curves—sulphnte, nitrate, and acetate; (2) those that helped to prevent corrosion at low pH only -fuoridc, chloride, bromide, and iodide; (3) those that helped to prevent corrosion at high pH also—phosphate, pcrborate, and chromate. Potential Measurements f The time-potential curves represntative of group 1 are shown in Fig. 1. These are the curves for 0.005 M sulphate ion and their similarity

Jan 1, 1939

Jan 1, 1882

By G. A. Beske, P. Hilsch, J. Wulff

The effects of the growth precipitates on the su-perconduching properties of an Al- 15 al. pel Zu alloy have been studied using magneization, transition lem-perature, and residual resistivity measurements. Aging at 230C for 1/2 to 11 he produces an increase in Hfp, Ike field of first penetration, and tut increase in trapped flux. The upper critical field, Hc2 remains constant for such aging tunes. Aging at 200°C produces a decrease in Hfp and an increase in trapped flux. The transition temperature remains constant at Tc - 1.227° ± 0.02°K for aging at 220°C for tims of from 1/2 to 10 hr, and for aging at 200°C it remains constant at Tc. = 1.18° i 0.02°K for times from 1/2 hv to 26 hr. The observed behavior indicates that the superconducting matrix when aged at 220°C behaves tike a type U su-perconducior, but when aged at 200°C behares like a type I superconductor. The magnetization changes after aging can be attributed to the growth and clutnge in distribution of the precipitate in a matrix of fixed composition. IT has been realized for some time that the superconducting properties of alloys are highly structure-sensitive. This is evident in the work of Mould and Mapother1 who examined the properties of an aluminum alloy. Precipitation effects have also been briefly mentioned in other studies.2-4 Bonnin and coworkers5 have observed a sharp inc rease in trapped flux in an A1-Mg alloy when the residual resistivity reaches a value that indicates it is a type II superconductor. Recently Blanc, Goodman, and Nemoz5p have reported on precipitation effects in A1-Ag alloys. Detailed studies of precipitation in Pb-Sn and Pb-Cd alloys made by Livingston6 serve to show that the upper critical fields are enhanced by quenched-in solute. Furthermore. at various stages in the precipitation process? the upper critical field is determined largely by the remanent solute. The observed magnetic hysteresis and trapped flux in such alloys result from the interaction between precipitate and the flux filaments in the mixed state. The flux trapping appears to depend largely on the precipitate distribution and is greater if the superconductor is type II than if it is type I. To examine the effect of precipitation in another alloy system, particularly one in which the composition of the superconducting phase does not change significantly during the course of precipitation, the Al-Zn system seems interesting, especially in view of the transition temperature and resistivity studies of Chiou and seraphim.' Furthermore, the recent detailed electron-microscope studies of an Al-Zn alloy by Richards and Garwood8 provide a guide for relating superconducting properties to changes in structure. For these reasons, magnetization, transition temperature, and residual resistivity measurements for varying times of heat treatment at two temperatures were made with a -15 at. pct Al-Zn alloy. The results are reported in this paper. I) EXPERIMENTAL The alloy used was prepared by Cominco Products Inc. from 99.9999 A1 and 99.999 Zn. It was chill-cast, swaged, and drawn to 0.125-in.-diam rod. The analyzed composition was 15.6 at. pct Zn (31.1 wt pct). A jeweler's saw was used to cut the 0.125-in.-diam rod into the 0.875-in. lengths needed for magnetization measurements. The ends of the cylinders were slightly beveled to remove the sharp edges. A portion of the original 0.125-in.-diam rod was drawn into 0.010-in.-diam wire and used for transition temperature measurements. Specimens were suspended from wires within a vertical furnace during heat treatment. All were homogenized at 500°C for a minimum of 3 days and subsequently solutionized for times in excess of 6 hr. The solutionizing temperature was held constant to +3°C. Individual specimens were homogenized, quenched, and aged several times and no effects indicating loss of zinc were noted. The suspended specimens were quenched by cutting the wires and allowing the specimens to fall into a silicone oil bath held at the aging temperature. They were then isothermally transforked by aging in the same bath used for quenching. After aging for the required time (approximately 10 min aging was necessary before the upper critical field reached a fixed value), they were briefly (1 to 2 sec) dipped into an acetone bath at room temperature to remove adherent oil and then immediately transferred to liquid nitrogen where they remained until inserted into the helium bath (usually within an hour). The temperature of the aging bath was held constant to +3°C for longer aging times. The cryostat used for the measurement of superconducting properties consisted of outer and inner dewars for liquid nitrogen and liquid helium, Stokes 6-in. booster diffusion pump and Stokes Model 212 mechanical pump, temperature controller to measure and control the temperature of the helium bath, and a superconducting solenoid with inserted search coils to provide the magnetic field and measure the magnetic moment of the specimens. A schematic diagram of the cryostat is shown in Fig. 1. An ultimate temperature of 0.85°K was reached with this apparatus. The temperature controller used is similar to the one described by Blake and chase.' A 0.5 pct Allen-Bradley carbon resistor and a nichronle heater (200

Jan 1, 1968

By E. W. Greene, J. B. Duke

This paper deals with the application of froth flotation techniques to the beneficiation of kaolin clay and phosphate slimes, two very fine particle sized materials. The kaolin problem involves the removal of a small amount of a contaminating mineral (anatase), while the phosphate problem involves the concentration and recovery of a much larger percentage of apatite. Due to these differences, and also different response to flotation, the two problems are discussed in separate parts of the article. An idea of what is meant by "Ultrafine Minerals Or Slimes" as used in the title can be had by an examination of Fig. 1. Particle size distributions are presented for a crude kaolin clay, a coarse fraction and a fine fraction. The crude kaolin as mined was blunged with water, degritted through a 325-mesh Tyler screen, and dispersed with sodium silicate. The dispersed crude was then centrifuged in the laboratory into the coarse and fine fractions shown in the figure. The distribution curves were obtained by the well known sedimentation technique of Casa-grande1 using a long arm centrifuge to obtain equiva- lent spherical diameters down to 0.2 p on the finer fraction. Fig. 1 shows the coarse fraction kaolin to be 50% finer than 3 p, while the crude kaolin is 509 f'lner than 1.4 p, and the fine fraction 50% finer than 0.46~. For comparison 53 p on the horizontal scale would represent Stokesian diameters which would just pass a 325-mesh Tyler screen, taking into consideration the Andreasen sieve correction factor of 1.22 times the screen opening. 2 Another helpful comparison is the surface areas, which in square meters per gram, are 0.044 for 53 p particles, 0.77 for 3p, 1.65 for 1.4 p and 5.0 for 0.46 p particles. Fig. 2 is an electron micrograph of a similar fine fraction kaolin showing the hexagonal plate-like particle shapes.

Jan 1, 1962

Jan 1, 1884

By Paul M. Tyler

ROUGHLY one-half the value of mineral products at mines or quarries must be spent for wages. In view of the steady increase in hourly wages that continued for several decades prior to the onslaught of the recent depression, it is perhaps surprising to discover that labor's share of the gross proceeds of the mining and quarrying industries of the United States declined to 46.8 per cent in 1929, compared with 52.2 per cent in 1919 and 53.2 per cent in 1909. The actual percentages vary in different branches of the industry and in different localities but the downward trend is unmistakable. For the period 1909 to 1919 it was quite marked in every industry and from 1919 to 1929 it was apparent in all but six: namely, gold and silver lode mining, placer gold mining, crude gypsum production, marble quarrying, asbestos production, and fluorspar Tninino mining

Jan 1, 1933

By Richard E. Chism

Some years ago, when I was seeking an illusive fortune and gaining a precarious existence in the primeval forests of Brazil, there penetrated, even to my headquarters in that far-off land, the story of a new-found mining district, where mountain peaks were ribbed with silver, and valleys teemed with virgin gold. Such were the stories that caused hundreds of men to seek their fortune in Sierra Mojada, and to return heaping curses, loud and deep, upon the vivid imaginations that had evolved the glittering fiction. Nevertheless, the rumors had some foundation of truth. The ribs of silver exist, if not the placers of gold; and a flourishing town, of some three thousand people, with two leading mining companies and several smaller ones, in operation, represents what was permanent in the excitement of 1879. Geographical Situation. The town of Sierra Mojada is situated in the State of Coahuila, Republic of Mexico, in latitude 27' 24' N., and longitude 26' 40' W. of Washington, 4' 36' W. of the City of Mexico, and 103' 43' TV. of Greenwich. It lies about 70 miles, in an air-line, N. E. of Escalon station, on the Mexican Central Railroad; but by the present wagon-road, which makes a long detour to turn the mountain range, the distance to the station is about 105 miles. The nearest towns are Huajuquilla, in the State of Chihuahua, about 125 miles due west, and Cuatro Cienegas, in the State of Coahuila, 112 miles to the eastward. Between these points and the town of Sierra Mojada, and to the north of this town, the country is an immense desert, entirely uncultivated, almost uninhabited, and very little known. This

Jan 1, 1887

By Ross E. BROWNE, Ross B. HOFFMANN

IT seems strange that a theory so devoid of value in its application to our practical problems should attract such widespread acclaim. This appears still more remarkable when one considers the foundation on which it is built. The criticism naturally suggested is as follows: First; the special theory of relativity is based on an assumption which is counter to the fundamental conception of relative motion. Second; the theory claims only a slight modification of Newtonian mechanics-a modification so minute that, even if true, it would have no practical value in its application to any visible occurrence here on earth.

Jan 1, 1931

By R. W. Raymond

It is impracticable to prepare for the present number of the Bi-Monthly Bulletin a detailed account of the memorable Joint Meeting of the Iron and Steel Institute and our Institute, held in London, the last week in July, and of the, innumerable festivities, entertainments and excursions which accompanied and followed it, in England, Scotland, Wales and Germany. This preliminary sketch, from which all " useful particulars "' have been carefully omitted, is published unofficially, as a convenient answer to the manifold inquiries of members who did not go, and who are now trying to alleviate their unavailing regret by indulging their curiosity. Perhaps they secretly hope to hear that they did not lose so very much, after all-that the affair was not all that could have been desired or dreamed; that there were serious drawbacks, shortcomings and disappointments; and that it is just as well to have stayed it home, and now to hear about it. Let them lay no such flattering unction to their souls. The month they have missed would have been the time of their lives. They will never, never know how good a time it was, or adequately repent of their folly, if they could have gone with us, and voluntarily did not go of course, those who would but could not, have our immeasurable pity, without blame. I shall present here no consecutive and minute story, but only a series of general paragraphs concerning different aspects and stages of our experience. THE WEATHER. The proverbial good fortune of the Institute attended its visiting members and guests at every stage of the late London meeting and the numerous excursions which accompanied or followed it. Even the process of crossing the Atlantic was made delightful by smooth seas, through which the great modern transatlantic liners made their way without disagreeable

Sep 1, 1906

By J. Greenspan

The anisotropy of fracture and slip, that is, the brittleness and ductility of the beryllium single crystal, is characteristic also of po1ycrystalline beryllium in which the grains are oriented in a preferred manner. Beryllium with grain orientations resulting from hot working either unidirectionally or bidirectionally is ductile or brittle in directions given by the anisotropy and orientation of the grains. Textures developed from various hot-working sequences are given, and tensile results are correlated with textures. Not only texture, but fine grain size is necessary for obtaining high tensile elongation. Ultimate tensile strength and elongation are both correlated with grain diameter. Of particular interest is the case in which unusually high tensile elongations of 30 to 40 pct are obtained when basal planes are oriented to carry THE beryllium crystal (of nominal purity) is probably unique among metals with respect to its unusually acute anisotropy of slip and fracture. While extensive slip can occur on the system (1010) [ll20] starting at about 19,000 psi, the (0001) plane is particularly vulnerable to fracture at 4500 psi or less. Fracture occurs also on the (11zo) plane at about 26,000 psi.1"3 Further, there seems to be no other slip System which contributes significantly to

Jan 1, 1960

By M. G. Corson

THE iron-silicon alloy series has always been one of the most puzzling among the binary alloys. Examining the well known mechanical properties of the iron-rich alloys only we meet the following situation: The ultimate strength and yield point of alloys worked and annealed under the usual conditions represent nearly a straight line function of the silicon content up to 4.5 per cent. silicon (Fig. 1). Starting at the ultimate strength of 35,000 lb. and at a yield point of 16,000 lb. for pure electrolytic iron, one reaches a maximum strength of 93,000 lb. and a maximum yield point of 74,000 lb. at 4.5 per cent. silicon. This corresponds to an increase in ultimate strength by 13,000 lb. per each per cent. of silicon added and nearly the same rate applies to the yield point. The data mentioned are taken from the investigation by T. D. Yensen,1 and while they do not exactly corroborate the results obtained by earlier investigators, they seem to be the most correct. Plastic properties of the alloys are controlled by a much more complicated relationship. Up to 2.5 per cent. Si, the elongation stays close to 50 per cent. (in 2 in.) and the area reduction amounts to 85 per cent;, a situation that forms the usual feature of all alloys representing strictly solid solutions. The plasticity of the latter is always nearly equal to that of their base metal. Beyond 2.5 per cent. silicon, the situation becomes much more complicated. Yensen observed an enormous drop in elongation and area reduction at about 2.65 per cent. silicon, where the first hardly reaches 10 per cent. and the second is still lower; he found, however, a considerable recovery in plasticity at about 2.8 per cent. Si and up to 4.5 per cent. Si it is represented by 20 per cent. for the elongation and 30 per cent. for area reduction.

Jan 1, 1928

ALBERT Ladd Colby, who died suddenly of influenza at Torquay, England, on Apr. 30,1924, was born in New York City, on June 26,1860. He was educated in the public schools of New York, at the College of the City of New York, and received the degree of Ph. B. from the Columbia School of Mines in 1881. He continued his studies at Columbia, acting occasionally as assistant to Prof. C. F. Chandler, until 1883. For the next three years he was Assistant Professor of Chemistry in Lehigh University; then head chemist and metallurgical engineer of the Bethlehem Steel Co., at Bethlehem, Pa., occupying the latter position until 1903. As head chemist his active and inventive mind devised several improvements in apparatus for increasing the rapidity and accuracy of the analytical work; as metallurgical engineer, he was, from time to time, in charge of the blast-furnace, open-hearth, bessemer, and puddling departments; he had entire charge of the inspection, assignment, and economic use of all metallurgical materials, and he early gave his attention to the formulation of specifications for metallurgical materials—an activity in which he long held a distinguished part in this country, and as a representative of his own country in England and Europe. He also sewed as expert for his company in patent suits, again laying the foundation for valuable service later as a consulting engineer. In this latter capacity he was excelled by few, if any, contemporaries in the iron and steel industry. His mind was ingenious, thorough, clear, and keen, both in the preparation of evidence and its presentation to the Court. He very quickly appraised the value of evidence, or of an answer to a question, and knew how to secure the infermation, either from the available literature of any language, or by special researches or plant studies. In the executive control of literary research for patent purposes, his long training, infinite capacity for digging through long series of articles in English, German or French, and clear formulation of the vital subject matter for the guidance of assistants, made him invaluable. He was also an adept in collecting information on special branches of his profession. For example, when the science of metallography began to assume importance, he made the first really comprehensive bibliography covering the literature of all siderurgical countries; for the newly formed International Nickel Co. he gathered all the information extant on the subject of nickel steel, both in the literature and in the minds of experts in America and Europe. Two books testify to the thoroughness of his work in this capacity, vie.: "American Standard Specifications for Steel,"

Jan 1, 1924

By W. Vickers

SALKOVITZ1 has given a number of useful angles between planes for use with the Laue method in determining the orientation of bismuth single crystals. Bismuth is usually considered as having a face-centered-rhombohedra1 structure with its axial angle 87°34', Fig. 1. A similar figure given by Sal-kovitz appears to be in error in that the angle there marked as 87°34' should be 92°26. The primitive cell is a single rhombohedron of axial angle 570 14. The structure is almost face-centered-cubic and hence high accuracy in measurements is essential if there is to be no confusion in indexing poles or zone axes. It is easier to get this accuracy if zone axes are plotted on the stereogram because they will lie near the basic circle where the net has a more open scale. The zone axes can be read from the film, using a Greninger chart, and can be plotted more accurately than poles. Also, the angles between points near the basic circle can be read more accurately than those between poles near the center. In order to use the zone axes the angles between directions have been calculated from a formula given by Niggli,2 and are given in Table I. Miller indices

Jan 1, 1958

By R. F. Yap, N. Arbiter, C. C. Harris

A fully-instrumented driving mechanism has been constructed to study the power, aerating and solid suspension characteristics of several laboratory flotation machines. Machines operating over normal flotation speed ranges give substantially constant power numbers in liquid systems indicating that they operate close to fully baffled turbulent flow conditions. Owing to lack of geometrical scaling, power numbers for different sizes of cells of the same make are different. Even larger differences occur between cells of different manufacturers. For a given impeller, varying the tank size did not significantly affect the power consumption. Tank geometry and baffling has a slight effect on power consumption with shrouded impellers. For a given impeller speed, suspension height decreases while power increases with increasing mass of solids in suspension. While power consumption is hardly affected by particle size and clearance between the impeller and tank bottom, the suspension height significantly increases as clearance increases and as particle size decreases. Aeration was found to affect not only power but also the suspension characteristics of the machine. For closely sized particles, drastic sedimentation occurred when a critical value of the air flow number was exceeded. The critical air flow number decreased with increasing particle size. This effect was less marked with a wide particle size range. The self-aerating capacity of flotation machines increases with cell size at a given speed for the same impeller-shroud system, but decreases in the presence of frother and solids. Equations have been established for correlating all of the studied variables. Data taken from the literature were also correlated with these equations. The modern mechanical flotation machine has, over a period of 60 years, displaced other designs to become the dominant type. Once the correct chemical environmental conditions have been established, the major requirement, selective mineral-air adherence, is essentially a function of two operating variables — impeller speed and air rate. The special nature of this dependence is such that in the same apparatus, but under different operating conditions, adherence can be either prevented or destroyed. Another aspect of this observation is that flotation machines though differing in detail to a considerable extent can produce similar metallurgical results. It must be concluded that having determined the correct reagent levels, establishing the correct operating conditions are at least as important as machine design. Since about 1960, after 30 years of fairly stable circumstances, manufacturers have been developing new types of machines whose major feature is emphasis on pulp flow characteristics by virtue of new im-peller-stator designs. As far as can be ascertained, these new designs necessitate radical departures from accepted impeller speed-air rate values. Performance data are still awaited. Flotation machine development has been empirical, as is selection of operating conditions. The purpose of the work at Columbia University has been to elucidate the fundamentals of the subject so that the purely mechanical aspects of the flotation process can be understood in hydrodynamic terms.1-6 Hopefully, this might lead to intelligent selection of a particular machine and its operating conditions for a specific ore based on a minimum of testing, or even to new types of flotation machines. The present investigation is the most comprehensive to date.7,8 Earlier work, which was largely exploratory, has been repeated and extended and employes the most accurate measuring techniques available. Additionally, sufficient hydrodynamic data were obtained under flotation conditions to delineate the relevant operating ranges. Attention has been given to scaling in that several geometrically scaled tanks and impellers have been constructed and tested; it has been pointed out elsewhere that undistorted geometrical scaling rarely pertains in flotation machine design.5 This paper is divided into sections dealing with relevant combinations of the three phases: liquid, air and solid. Summaries of the literature have been given in previous publications2-4 and will not be repeated here. Recently, several reviews of mixing have appeared, which can be usefully referenced.9-11 It is of interest to note that flotation is not included

Jan 1, 1970

By J. H. Swisher

In measuvements of the solubility of nitrogen in fer-rilic Fe-P alloys, tile nitrogen solubility is found to be Less in pIrospliorus-bearing alloys than in pure iron. The reduction in solubility is about 20 pct in a 1.0 wt pct P alloy at 1300°C and about 30 pct in a 0.23 wt pct P alloy at 440°C. Diffusion coefficient measurements at 1150 and 585°C show that phosphorus also decreases the nitrogen diffusivity in iron. In previous work on the Fe-P-N system, phosphorus was found to reduce the nitrogen solubility in liquid iron slightly.&apos; Indirect evidence for similar behavior in a Fe at low temperature was obtained by Dickenscheid and Brauner.&apos; These authors found that phosphorus reduces the height of the internal-friction peak due to dissolved nitrogen. The results of Dickenscheid and Brauner were confirmed by J. C. Swartz of this Laboratory in a single internal-friction experiment using the same specimen stock as in the solubility measurements described below. In the present investigation, the solubility of nitrogen in a fer rite-stabilized Fe-1.0 wt pct P alloy was measured in the temperature range from 800" to 1300°C. Additional experiments were performed in the temperature range from 440° to 585°C, using an Fe-0.23 wt pct P alloy and NH3-H2 gas mixtures. EXPERIMENTAL The experiments were performed in a vertical tube furnace wound with platinum wire. For experimental temperatures of 800°C and above, a mixture of 5 pct Hz in N2 was used as the reacting gas. The gas mixture was prepurified from oxygen by passage over platinized asbestos at 450°C, and subsequently over anhydrone to remove water. Flow rates of the gases were measured with capillary flow meters. The temperature was measured before and after each experiment with a Pt/Pt-10 pct Rh thermocouple. The specimens used for the high-temperature solubility measurements were in the form of rectangular plates, 0.534 by 1.6 by 3.8 cm. The specimens were cleaned in trichloroethylene and annealed for 2 hr in hydrogen at the beginning of each experiment. In measuring the nitrogen solubility, the specimens were held in the reacting gas until equilibrated, then cooled in a water-cooled copper block at the bottom of the furnace. The time needed for equilibration at 1150°C was determined by measuring the average nitrogen content of the 1.0 pct P alloy as a function of reaction time. As will be described, the nitrogen diffusivity in the alloy at 1150°C is only slightly less than its calculated diffusivity in pure iron. At temperatures other than 1150°C, the reaction time used in measuring the nitrogen solubility was about twice the calculated equilibration time for pure iron at the same temperature. With a few exceptions, the procedure for the low-temperature solubility measurements was the same as that described above. The compositions of the NH3-H2 gas mixtures were determined by collecting gas samples from the gas train and analyzing them for NH3 by titration with HC1. The specimen thicknesses were less than those used for the high-temperature experiments, eg., 0.124 and 0.051 cm for measurements at 585° and 440°C, respectively. Nitrogen concentrations were obtained by chemical analysis, using the Kjeldahl method. The Fe-P alloys were made by adding ferrophos-phorus to electrolytic Plastiron (Type 104 A). Commercial ferrophosphorus, containing 3 pct Mn and 0.35 pct Si as the major impurities, was first purified by melting under an FeO slag. In a separate heat, the electrolytic iron was melted and vacuum-carbon-deoxidized prior to making the ferrophosphorus addition. The principal impurities and their concentrations in weight percent in the 1.0 pct P alloy are as follows: Mn, 0.01; Si, <0.01; C, 0.01; 0, 0.003; and N, 0.0012. The impurity levels in the 0.23 pct P alloy are con-

Jan 1, 1968

By S. F., French

IN reviewing the design of the ore haulage system for the Morenci project, the reader should bear in mind that the railroad and its equpiment cannot be considered as an independent railroad provided only for the purpose of transporting ore from one point to another, but as an integral part of the operation which begins at the electric shovels loading ore at the mine, and ends where the ore, after having been crushed in the primary crushing plant, is deposited in the bins at the secondary crushing plant. Obviously then, the problem consisted of designing a system that would function to the best possible advantage in complete co-ordination with the other units.

Jan 1, 1942

By Louis G. Bailey

This paper .reviews some of the key developments which have been made in the synthesis of the III-V compound semiconductors and the associated progress in obtaining high-quality material for device development. The history of the investigation of the semi-conducting properties of these materials has indicated the need for synthesis techniques capable of producing rnaterial of high chemical purity and physical perfection. The progress in the area is described, and the present status of quality of several compounds is discussed. In addition, recent studies of localized epitaxial deposition of GaAs into semi-insulating GaAs substvates for the development of arrays of devices ave reviewed. In conclusion, some important areas for future research and developrnent are discussed. INTEREST in III-V compounds as semiconductors dates back to the period 1950 to 1952, when Goryunova, Ioffe, and, in particular, Welker determined that 111-V compounds were structural analogs of the group IV elements carbon, silicon, germanium, and tin and that they were also semiconductors.&apos;-3 Since that time interest in the properties of these materials has ex- panded rapidly. During 1953 and 1954, the first reports of rectification, photoconductivity, and optical absorption in these materials came from several investigators. In 1955, recombination radiation from samples of GaAs, InP, and GaSb was reported by ~raunstein .&apos; This radiation was produced by injected minority carriers from point and large-area contacts. From 1955 to 1960, efforts increased on preparing large, pure specimens of these materials for the study of basic physical phenomena and device exploration. By 1960, materials preparation and the understanding of the physics of some of the materials had advanced to where some very interesting and potentially useful phenomena came under study. The first observation of electric-field-induced changes in the optical absorption edge (Franz -Keldysh effect) of 111-V compounds was reported for GaAs by Moss in 1961.&apos; In 1962 the study of recombination radiation advanced rapidly. Keyes and Quist6 and Pankove and Berkey-heiser7 reported high radiative efficientices obtained from recombination, and then the first injection electroluminescent lasers in GaAs were announced by Hall ef al.,&apos; by Nathan et al.,O and by Quist ef al.,&apos;O and in Ga(As, P) alloys by Holonyak and Bevacqua." Hil-sum has reviewed the early work leading to the first observations of laser action in GaAS." Recombination processes in GaAs, Gap, and the other 111-V com-

Jan 1, 1968

By L. J. Ingvalson, Roy H. Miller

IN 1948, as part of a program to expand the copper tube mill facilities of the American Brass Co. plant at Kenosha, Wisconsin, plans were formulated to convert the 100 ton capacity anode casting furnace at the Great Falls, Montana plant of the Anaconda Co. to the production of 3 in. phosphor -ized billets. The furnace was rebuilt completely and construction was started on an addition to the building. Members of the Great Falls staff visited various billet casting plants to draw upon the experience of other producers of this type of casting. Many features of other plants were incorporated into the Great Falls plant but, in addition, many new designs were made and perfected to make the plant the most advanced of its type. Construction was begun in 1949, with the intention of having the plant in production in the early part of 1951. In January 1951, as the plant was being rushed to completion, the government placed restrictions on the production of copper tubing. As a result, work was halted and the plant lay idle for two years. Interest was reactivated in May 1953 with the lifting of restrictions on copper. Plans were laid to go into production in July and the first charge was taken out July 1, 1953. Basically the plant is designed to produce from cathode copper a 3 in. diam billet, 50 in. long. weighing 110 lb, and containing 0.013 to 0.036 pct P, at a rate of 150,000 Ib per operating day. These billets are to be pierced and drawn into tubing. Furnace The furnace is a 100 ton capacity reverberatory type, gas fired furnace; 21 ft long and 9 ft wide. Gas is introduced to the furnace through two 38 hole Mettler gas burners. These burners are of chrome nickel alloy with four jets per hole. The furnace is charged with cathodes from the Electrolytic Copper Refinery plus return scrap from the casting operation by means of a Wellman Seaver Morgan Co. 7,000 lb capacity charging machine. The charge crane has a 20 ft boom and fork peel provided with an air ram to push material off the peel. The machine travels on overhead tracks and can be moved in any direction. The boom can be raised and lowered and swung through an arc of 180". With well stacked units of 6,000 lb, an experienced operator can put the first charge into the furnace in 40 min. After charging, the steel framed silica brick charge door is put in place and sealed with clay. After melting and skimming off the slag, the copper is blown until an oxygen content of 0.40 pct is reached. The metal is then heated to 2180°F, covered with coke, and poled. Poling is continued until a 3 in. diam test billet, 8 in. long, shows a flat set. The oxygen content is usually 0.030 pct at this time. At the end of poling, a temperature of 2160" to 2180°F is desired. In the side of the furnace opposite the charging door is the taphole slot, extending 36 in. upward from the bottom of the furnace. It is 4½ in. wide at the outside face and widens to 9 in. at the inside face of the furnace. It is filled with a wet mixture of sand, fireclay, and crushed coal. Flow of metal

Jan 1, 1957

By John V. Hamme

ONE of Tungsten Mining Corp.&apos;s Vance County, N. C., mill near Henderson was the installation of a new crushing plant with a capacity of 45 to 50 tph. During 1953 the milling rate was jumped from 650 tons to 800 tpd simply by expanding existing facilities, eliminating bottlenecks, and making changes in the existing and new circuits. Previous expansions in 1951 and 1952 raised mill capacity from 300 tons to 650 tpd. In its latest move, Tungsten Mining decided that expansion of existing facilities would be more economical than building that normal production was uninterrupted. For the engineering and design of the new crushing plant and mill expansion the services of the Southwestern Engineering Co., Los Angeles, were obtained. The Southeastern Construction Co., Charlotte, N. C., carried out construction, alterations to existing facilities, and the installation of equipment

Jan 10, 1954