By H. Y. Sohn, Joshua E. Ramos, Moo Eob Choi

"A new technology for ironmaking based on direct gaseous reduction of iron ore concentrate is under development. This technology would drastically lower CO2 emission and reduce energy consumption by nearly 38% of the blast furnace requirements. Experiments were performed using iron oxide concentrate at 1150oC in a bench-scale facility, which was the highest temperature that could be reached in the facility. The reduction extent was determined at residence times of 3.5 - 5.5 seconds in which the reduction extent approached 43% with 0% excess H2 and 95% with 860% excess H2. Separate kinetics measurements showed that the rate is much faster at 1200 - 1400 oC. Experiments were also carried out using syngas (mixtures of H2 + CO). About 90% reduction in 3.5 seconds with 860% excess hydrogen contained in the syngas demonstrated sufficiently fast reduction for a suspension process and the feasibility of usingsyngas instead of pure hydrogen.IntroductionDespite the improvements in the modern blast furnace (BF) process, it suffers from many drawbacks. The process requires the feed in the form of sinters or pellets and high-grade coking coal. Thus, BF iron production is projected to decrease gradually [1]. The main factors for this are the environmental regulations [2] and the high capital investment cost.A large number of new ironmaking technologies have been developed or are under development [3]. Most of these processes, however, are not sufficiently intensive to replace the blast furnace because they cannot be operated at high temperatures due to the sticking and fusion of particles. Therefore, a new technology is under development for producing iron directly from fine concentrates by a gas-solid suspension technology, which would reduce energy consumption by about 38% of the amount required by the blast furnace and drastically lower environmental pollution, especially CO2 emission, from the steel industry."

Jan 1, 2009

By Masaru Imaizumi, Hiroyuki Nomura, Mitsuharu Takita

"Cast iron possesses many superior characteristics caused from precipitated graphite structure, for example, castability, wear resistance, solid lubrication, damping capacity. But the more graphite hyper-eutectic cast iron contains, the lower its mechanical strength becomes, because graphite gives a negative effect to strength of cast iron. In addition, primary graphite tends to segregate during solidification, so uniform materials are difficult to be produced.In this study, authors introduced semi-solid processing in developing new and high quality cast iron. A series of semi-solid processing experiments were carried out to clarify the effect of stirring condition; solidification temperature and etc. on microstructures and characteristics of cast iron. In particular much attention is paid to the appearance of ternary eutectic zone at the final stage of solidification. As the results advanced hyper-eutectic cast iron was obtained with high quality of both the mechanical strength and wear resistance. As for the mechanical strength, 300MPa and 0.60% are obtained as the tensile strength and the elongation values, respectively, under the controlled stirring condition. This indicates that semi-solid processed hyper-eutectic cast iron is used prospectively without spheroidization.IntroductionCast iron has various good properties such as wear resistance, solid lubrication, damping capacity and machinability. The characteristics of cast iron are mainly decided by graphite structure, namely graphite shape and its distribution in the matrix. Mechanical strength of cast iron is large in the case of small quantity of graphite particles which are precipitated uniformly, however, it becomes small in the case of large quantity of graphite precipitated flakily."

Jan 1, 2000

By Meyer Steinberg

"Some early experiences of a Cooper Union Chemical Engineer on the Manhattan project and his latest studies on CO2 Greenhouse Gas Mitigation Technologies are presented. Mitigating Global Greenhouse effect while maintaining a fossil fuel economy, requires improving the efficiency of conversion and utilization of fossil fuels, use of high hydrogen content fossil fuels, decarbonization of fossil fuels and sequestration of carbon and CO2 applied to all energy consuming sectors of the economy including electric power generation, materials production, transportation and industrial domestic heating. Decarbonization means removal of carbon as C or CO2 either before or after fossil fuel utilization and sequestration means long term disposal of C or CO2. The review will cover the principles of removal and recovery from power plant, stacks, the oceanographic and geological disposal of CO2 and the conversion of CO2 to gaseous and liquid transportation fuels. The global economic aspects of CO2 mitigation technologies are touched upon.IntroductionThis is an odyssey of a chemical engineer. My career started with the production of U235 at the Gaseous Diffusion Plant in Oak Ridge, Tennessee and the production of PU-239 metal at Los Alamos on the Manhattan Project. After 40 years at Brookhaven National Laboratory, I wound up performing studies on CO2 mitigation technologies. The following is a power point presentation on the subject of global warmingThe DOE is proposing to increase its sequestration development program in order to maintain the utilization of our vast resources in coal both for power and for transportation fuel production. Congress is considering steps to promote energy efficiency in attempts to solve not only the CO2 problem, but also the prime problem of energy supply. We will be promoting increases in energy efficiency as time goes on."

Jan 1, 2008

By Malti Goel

"Ferrous and Non-ferrous industry in India is undergoing a transition to meet the growing demand and a new thrust to Research & Development (R&D) is mounting. On one hand, to meet the target laid by the policy in the Iron and Steel sector of 110 million tones production by 2020; on the other, innovations taking place in light metal production technology; both have necessitated greater attention to development of industrial ecological framework. Industrial ecology provides a number of new challenges as well as opportunities for the industry. The development and growth in a particular industry should have a trend towards reduced energy consumption, reduced resource consumption, thereby reducing the cost of production. Technology management strategies will have a key role in achievement of these targets. The paper describes recent developments in technology management, importance of R&D and case studies on adoption of energy efficient & CO2 reduction technologies in metal industry in India. In the end suggestions for future are made.IntroductionInternational Energy Agency [1] has assessed that nearly one third of the World’s energy consumption and 36% of CO2 emissions are attributed to manufacturing industries. In case of ferrous and non-ferrous metals, the resource equality and product quality finally determine the energy share across the countries. In the overall, Iron & Steel industry accounts for about 19% of total industrial energy used. The saving potential for non-ferrous metals is estimated to be anywhere between 13 to 25 % of the energy consumed depending on the level of resource quality. The projections are that energy consumption worldwide in Industry sector would increase 1.8% per annum up to 2030 on average, and up to 2.5% in developing countries."

Jan 1, 2008

By J. A. Bustnes

The present work deals with kinetic studies of the reduction of molybdenum- and tungsten oxides by hydrogen. The experimental method used was therrnogravimetry under isothermal as well as non-isothermal conditions. The non-isothermal kinetics in the case of the reduction of MOO, to Moo2 has been modeled considering surface reaction as rate- controlling. In the case of the reduction of W02 to W a model was developed on the basis of the movement of the reaction front. The activation energies calculated on the basis of the models were in good agreement with those derived from isothermal experiments.

Jan 1, 1994

By Robert E. Moore

Synthetic spinel is proving to be a highly effective refractory for specific applications, but its cost limits applications. Formation of spinel from a raw material such as diaspore or bauxite could provide a simple and less costly starting material. In the study reported here, finely ground (-325 mesh) diaspore from Missouri and bauxite from Guyana and China are combined with hard burned MgO (-325 mesh) in appropriate proportions to yield spinel and spinel with secondary phases. A classical sintering and dilatometer study was completed, followed by a microstructure study to determine completeness of the reactions and morphologies of the reaction products.

Jan 1, 1993

By Fuqiang Zheng, Yufeng Guo, Pengfei Li, Guanzhou Qiu, Tao Jiang, Andrew Yakovlevich Travyanov

Low content of TiO2 and high impurities content of Ca and Mg are the shortcomings of domestic ilmenite. To meet the requirements of the material in the titania produced by chlorination process and titanium sponge industry, enrichment of ilmenite is necessary. In the process of enriching ilmenite, high temperature and reductive condition were beneficial to the formation of anosovite, but the high content of magnesium oxide which was solid soluble in anosovite baffled the following separation. So the effects of pre-oxidation and reductive conditions including reduction temperature, reduction time and hydrogen concentration on the phase composition and metallization rate were studied. The characteristics of reduction samples were analyzed by X-ray diffraction and optical microscope. Results have shown that the reduction product is mainly composed of Fe, Fe(Mg)TiO3 and TiO2 at 1123K, its metallization rate is about 65%,magnesium exists in Fe(Mg)TiO3.

Jan 1, 2015

By B. R. Westphal

The Integral Fast Reactor (IFR) concept being developed by Argonne National Laboratory is based on the pyrometallurgical processing of spent nuclear metallic fuel with subsequent fabrication into new reactor fuel by an injection casting process. During fabrication, a dilute scrap stream containing uranium alloy fines and broken quartz (Vycor) molds is produced. Waste characterization of this stream, developed by using present operating data and chemical analysis, was used to evaluate different uranium recovery methods and possible process variations for the return of the recovered metal. Two methods, comminution with size separation and electrostatic separation, have been tested and can successfully recover over 94% of the metal. Recycling the recovered metal to the injection casting process was evaluated for the different economic and process impacts. The physical waste parameters and the important separation process variables are discussed relative to their effects on the viability of recycling the material. A discussion of the criteria that is being used to establish the acceptable operating limits is also presented.

Jan 1, 1992

By Robert P. Stevens

It is important for a refractory supplier to make systematic petro-graphic examinations of products which have been in service in the furnaces and kilns of customers. The petrographic examination of refractory service samples involves the microscopic study of polished and/or thin sections, supplemented by electron probe microanalysis, as well as the bulk chemical and XRD analysis of zones in the samples. The evolution of the A. P. Green Refractories Company petrographic laboratory is described, and the application of petrographic methods is illustrated in the examination of service refractories from a Portland cement rotary kiln and an AOD stainless steel vessel. The objectives of such studies are to assist the customer in the solution of his refractory problems, and to accumulate data which are of use in the design of improved refractory products.

Jan 1, 1981

By R. Hurman Eric

The dew-point technique of activity measurements take advantage of the volatility of a component in solution. The pressure of the volatile component over a sample is determined from observations of the temperature at which condensation of the vapor occurs. The method is applicable best when the vapor pressure of the components would differ by about two to three orders of magnitude. Experimentally, this is a closed system involving the use of evacuated and sealed transparent quartz sample probes. Furthermore reliable vapor pressure data of the volatile component is essential along with a specialized high temperature furnace capable of giving reproducible results. In this context, the vertical Dew-Point Furnace (DPF) was designed and built after elaborate trails until enough proficiency was gained for reproducible results. Over the years the DPF was modified and improved. The DPF developed was versatile and could easily be used for activity measurements in the isopiestic mode (another method of measuring activities of a volatile component in a solution). The necessary ancillary systems; namely evacuation-flushing-evacuation followed by sealing of quartz sample probes under vacuum were also perfected over the years. As and when necessary the dew-point technique was supplemented by classical equilibration-quenching method employed on the sealed quartz sample probes to reveal necessary phase equilibrium information. The following were studied utilizing the above technique: (i) Activities in CU2S-PbS and FeS-PbS binaries and CU2S-FeS- PbS ternary at 1200°C; (ii) Activities in Cu2S-SnS and FeS-SnS binaries and Cu2S-FeS-SnS ternary at I200°C; (iii) Phase equilibria and thermodynamic in Cu-Pb-S, Fe-Pb-S, Fe-Sn-S, Cu-Sn-S and Ag-Sn-S systems. Most recently the following systems have been tackled: (i) Phase equilibria and thermodynamics in the Ag-Pb-S and Sn-Pb-S systems; and (ii) Activities in Ag2S-FeS-CuzS-PbS quaternary at 1200°C.

Jan 1, 2003

By R. Hurman Eric

The dew-point technique of activity measurements take advantage of the volatility of a component in solution. The pressure of the volatile component over a sample is determined from observations of the temperature at which condensation of the vapor occurs. The method is applicable best when the vapor pressure of the components would differ by about two to three orders of magnitude. Experimentally, this is a closed system involving the use of evacuated and sealed transparent quartz sample probes. Furthermore reliable vapor pressure data of the volatile component is essential along with a specialized high temperature furnace capable of giving reproducible results. In this context, the vertical Dew-Point Furnace (DPF) was designed and built after elaborate trails until enough proficiency was gained for reprodueible results. Over the years the DPF was modified and improved. The DPF developed was versatile and could easily be used for activity measurements in the isopiestic mode (another method of measuring activities of a volatile component in a solution). The necessary ancillary systems; namely evacuation-flushing-evacuation followed by sealing of quartz sample probes under vacuum were also perfected over the years. As and when necessary the dew-point technique was supplemented by classical equilibration-quenching method employed on the sealed quartz sample probes to reveal necessary phase equilibrium information. The following were studied utilizing the above technique: (i) Activities in CuzS-PbS and FeS-PbS binaries and CU2S-FeS- PbS ternary at 1200°C; (ii) Activities in CuzS-SnS and FeS-SnS binaries and Cu2S-FeS-SnS ternary at 1200°C; (iii) Phase equilibria and thennodynamic in Cu-Pb-S, Fe-Pb-S, Fe-Sn-S, Cu-Sn-S and Ag-Sn-S systems. Most recently the following systems have been tackled: (i) Phase equilibria and thennodynamics in the Ag-Pb-S and Sn-Pb-S systems; and (ii) Activities in Ag2S-FeS-CuzS-PbS quaternary at 1200°C.

Jan 1, 2003

By Saynbaatar, Gangping Ma, Jianhua Fu, Qiqige, Jinghua Wang

The influence on the performance of foam concrete made by replacing cement with some industrial waste residues was researched in this paper. The result shows that the 7d and 28d compressive strength of foam concrete increases firstly and then decreases with the increasing amount of industrial waste residue. The proper added range is 10%-20% for steel slag, blast furnace slag and coal ash, but, 8% for desulfurized fly ash. With the proper adding ratio, the compressive strength of foam concrete always increased comparing with the pure cement foam concrete. When adding 48% of the compound industrial waste residues, the 28d compressive strength of the foam concrete reached the 2.9MPa which could match the pure cement foam concrete. The results indicates that there is a synergistic effect among the compound industrial waste residue, and this effect is benefit to improving the compressive strength of foam concrete.

Jan 1, 2015

By Jorge Alberto Soares Tenório, Flávia Paulucci Cianga Silvas, Denise Crocce Romano Espinosa, Ivo André Homrich Schneider, Erika Gusmão, Daniella Cardoso Buzzi, José Roberto de Oliveira

"This study evaluated the Salvinia sp action on metals biosorption in a synthetic sample of acid mine drainage (AMD) in order to determine the time and amount of metals uptake. Biosorptives tests were realized varying the contact time of 5, 20, 60 and 240 minutes. And keeping constant the follow parameters: pH (2.6), biomass concentration (1g.L-1), temperature (25°C) and agitation (175rpm). In order to quantify the metals concentration captured by biomass, the AMD samples will be analyzed by ICP. Biosorbent, Salvinia sp., will be characterized before and after the biosorptives tests through analysis of SEM and IR. The micrographs indicate the occurrence of micro-precipitation and changes in biomass physical structure. The infrared spectra indicate changes in functional groups present in the biomass before and after the biosorptives tests.IntroductionThe current emphasis on environmental sustainability leads the industry in general, to treat their waste. The human activities are increasing, highlighting the industrial and mining activities, and have promoted the contamination of soil, waterways and groundwater by metals (1). The waste must undergo treatment processes aimed at reducing pollution, and therefore, less aggression ecosystems.This means the importance of studies of economic and effective methods to eliminate these metals from wastewater generated. The bioindicators are good investments in this area. The aquatic weeds are plants that inhabit swamps up from truly aquatic environments. They have several morphological and physiological adaptations that enable them to colonize the various aquatic environments. They are used as bioindicators of water quality and have also been used in decontamination of aquatic environments, production of biomass for livestock feed, fertilizers, soil and fish tanks (2)."

Jan 1, 2012

By Masatoshi Ogasawara

Saganoseki smelter & refinery operated two flash smelting furnaces, producing a combined 330,000 metric tons per year (hereinafter mtpy) of copper. [n 1996, however, it successfully shifted to a single fumace operation while maintaining production at the same level. Since then, the production capacity has been further increased to the present 470,000 mtpy by technological improvements. Also, in order to reduce the converter load which represents a bottleneck in efforts to increase production, the matte grade was gradually increased and currently runs at 65 to 66% attaining the low copper content in the slag (hereinafter slag loss) of 0.7 to 0.8%. This ' paper introduces some improvements, recent operation results and thermodynamic analyses.

Jan 1, 2003

By G. C. Yao

Iron and silicon impurities can form needle and branch shape intermetallie compounds in molten aluminum when there is no manganese. It is difficult to separate them from molten aluminum by electromagnetic separation. The Fe-Si-AI and Fe-AI intcrmetallic compounds were transformed into Mn-Fe-Si-AI and Mn-Fe-AI compounds by the addition of manganesc into molten aluminum, In molten aluminum the morphology of these intermetallic compound particles is lumpish and spherical. Migration resistance of these impurity particles is small, which is beneficial to separation. FeSiMnAl4 and FeMnAl6 arc paramagnetic. These impurity particles can be moved by magnetic force and can be separated from the molten aluminum.

Jan 1, 2003

By G. C. Yao

Branch and needle-shaped intermctallic compounds of iron, silicon and aluminum normally exist in the molten aluminum. If a suitable amount of manganese metal is added into molten aluminum, the shape of the intermallie compound particlcs may become lumpish and spherical. According to the difference in electric and magnetic properties of these impurity particles and molten aluminum, these impurity intermctallie compound particles can be separated by applying an alternating magnetic field. In this experiment the alternating magnetic field was formed by a "C" type loop with AC (50Hz) current. The inner vacuum of the fireclay refractory separator is 25>< 15" 130mm3 with a lateral baffle inside. The separator was put into the interspace of the "C" type loop. It was found that the longer the separation time, the larger the amount transferred of impurities. The amount of transferred impurities increases with the increase of separation time and intensity of magnetic field. The addition of manganese metal enhanees signifieantly the efficiency of impurity separation.

Jan 1, 2003

By Mark Tjerkstra

In ,1993, the WMC Resources Ltd.-owned Kalgoorlie Nickel Smelter, underwent a capacity upgrade. This capacity increase was offset by .air quality control restrictions limiting the smelter&apos;s availability to 80%. As the direct. result of this limitation, WMC Resources Ltd commissioned a double absorption contact ,acid ,plant for the desulphurisation of furnace waste gas in August 1996. The history and the impact of the acid plant on S02 emissions and air quality is reviewed. General descriptions of the other aspects of the Kalgoorlie Nickel Smelter&apos;s Environmental Project are also included in the paper. Information on &apos;the design features? and operating practices that relate to or contrast with practices at operations visited by KNS personnel prior to acid plant commissioning provide the paper&apos;s focus. Smelter operation has changed markedly from unstable operation prior to 1997 to continuous" operation with little down time due to mechanical or process failures resulting in increased smelter availability to more than 90%

Jan 1, 1998

By Yilin Fang, Alain Bonneville, Timothy. D. Scheibe, Zhijie Xu

"We present a hydro-mechanical model for geological sequestration of carbon dioxide. The model considers the poroelastic effects by taking into account the coupling between the geomechanical response and the fluid flow in greater detail. The simplified hydro-mechanical model includes the geomechanical part that relies on the linear elasticity, while the fluid flow is based on the Darcy's law. Two parts were coupled using the standard linear poroelasticity. Analytical solutions for pressure field were obtained for a typical geological sequestration scenario. The model predicts the temporal and spatial variation of pressure field and effects of permeability and elastic modulus of formation on the fluid pressure distribution.IntroductionIn order to achieve a substantial reduction of CO2 emissions and alleviate the atmospheric carbon problem, massive scale carbon sequestration is required involving millions of tons of carbon dioxide injection over several decades. The geomechanical response is important upon the injection of substantial supercritical carbon dioxide into deep geological formations. Supercritical CO2 is less dense than brine waters and the buoyancy driven flow of CO2 requires the aquifer to be capped by low permeability rock (""caprock"") to prevent the upward migration of C02 (as shown in Fig.1 ). Massive scale injection of C02 changes the overall stress state in the caprock and formation. This change leads to large deformation that can damage the caprock, create fractures, and open new flow paths for supercritical C02. Therefore, a coupled hydromechanical model becomes essential for the caprock integrity analysis."

Jan 1, 2012

By Katsunori Yamaguchi

A new technique for the removal of tramp-elements from steel scrap has been required from the viewpoint of saving energy and protection of environment. In order to obtain fundamental information on the removal of copper, tin and zinc from molten iron, the extraction method by using of phase separation in the liquid Fe-Pb-C system was investigated at 1453K A mixture of iron, lead and carbon melted in a carbon crucible separates into two phases of lead and iron containing carbon. The compositions on the miscibility gap in&apos; the Fe-Pb-C system are 95A%Fe-4.5%C-0.l %Pb and 99.9%Pb-0.1 %Fe. The distribution ratios of copper, tin and zinc between the lead and the iron phases, Lx=[masso/uX in molten Pb]/(masso/uX in molten Fe), are 2.2, 2.2 and lA, respectively. Seventy percent of copper and tin from iron scrap can be eliminated with comparable lead addition. Gold, silver and palladium are enriched in the lead rich phase, on the contrary platinum and rhodium are more distributed to the iron rich phase than to the lead phase.

Jan 1, 2003

By Jing Lin, Yuan Xu, Qingcai Liu, Dengfu Cheng

"Smelting reduction technology has been developed greatly in recent years. But one of the key problems for this technology is about the refractory that used as lining material in the molten bath. Investigation and test shown that corrosion rate of refractory was much higher and the corrosion mechanism was much more complexity in the molten bath of smelting reduction with iron bath than that of the blast furnace and rotary furnace technology [l-5]. The corrosion behavior and corrosion rate of Al2OrC-ZrO2 series refractory in the melt of smelting reduction with iron bath have been studied by rotary immersion and quasi-static immersion test in this paper. The major factors that affect the interaction between the melt and refractory were investigated. The test results shown that the corrosion rate of AI2O 3-C-ZrO2 series refractory decreased with the ZrO2 increasing when ZrO2 content was from 3% to 10%. Ferrous oxides content, relative moving speed between the melt and refractory and temperature of the molten bath were the important factors that affect the corrosion rate. But the ferrous oxides concentration was the most important one. The corrosion rate was increased as a linear relation with the rising of ferrous oxides content of the melt. The corrosion rate in the quasi-static immersion was much less than that of the dynamic immersion (rotary immersion) for the Al2O 3-CZrO2 series refractory in the same testing condition. The corrosion mechanism of Al2OrC-ZrO2 series refractory is: graphite oxidized in advance, then interaction between the constituents of refractory and melt taken place and deteriorate layer of refractory and new compounds were formed, the properties of refractory was changed.IntroductionSmelting reduction with iron bath is a typical technology [3, 4, 6]. The obvious features of the melt for smelting reduction technology with iron bath are much higher ferrous oxides and much more complexity melt composition and structure than that of the blast furnace technology [2, 5-8]. The properties of the melt were changed dynamicilly and constantly in reduction process. On the other hand, the behavior of the melt depends on the activity and the reduction rate of ferrous oxides in the molten bath[9]. Because of the high concentration of ferrous oxides in slag and high reduction rate in the molten bath, the corrosion behavior and corrosion mechanism of the refractory lining by melt are an important factor in development of the technology of smelting reduction with iron bath. Up to now, improving refractory quality to anti-corrosion of melt and developing high quality and long term refractory used as the lining refractory materials in the molten bath of the final reduction furnace are also the most important questions for developing smelting reduction technology."

Jan 1, 2000