By Kotaro Ogura

"Ethylene has been produced in aqueous solution from CO2 by the electrochemical reduction driven by a natural energy. This process is useful for storing a large amount of the natural energy. In the closed system, the conversion efficiency of CO2 is almost 100%, and the maximum selectivity for the formation of ethylene is more than 70%. On the other hand, the current efficiency for the competitive reduction of water is less than 10%. The electrolysis is practicable under such special conditions as three-phase interface consisting of gas, solution and metal, concentrated solution of potassium halide, low pH and copper or copper halide-confined metal electrode. These requirements are thoroughly examined, and the grounds to reply upon are revealed. A series of chemical apparatuses including an electrolytic cell in a large scale are designed for the ethylene production, which allow us continuously to supply raw CO2 and to extract the product.IntroductionIn connection with the depletion of the petroleum reserve, much attention has been paid to the utilization of natural energies such as sunlight, wind force and waves. However, these energies are always changeable, and some means of storing them are necessary for the common use. In general, natural energies are transformed to the electric energy at the time of utilization, but the electricity is not very storable. This is one of the reasons why the application of natural energy is not so expanded. On the other hand, the storing of natural energy by plants is very skilful. In the photosynthesis, solar energy is transformed to chemical energy by fixing carbon dioxide."

Jan 1, 2009

By C. E. Abbey

Cobalt, iron and manganese play various roles in copper electrowinning using lead–calcium–tin alloyed anodes. Cobalt catalyzes electrochemical water decomposition resulting in lower anode potential and reduced corrosion rates. Iron reduces cathodic current efficiency, but is used to reduce higher oxidation states of manganese that oxidize organics in solvent extraction. Manganese also produces anode scale and is generally considered a problematic impurity. The effect of the combined interaction of these three metal ions on the anode potential has not been quantified yet. The current work used a three factor, two level, three replicate central composite design of experiments to analyze the effects and potential interactions among cobalt, iron and manganese. The experiments consisted of chronopotentiometric analysis to assess anode potential after 24 h of operation. Higher [Co], lower [Mn] and either high or low [Fe] yielded lower anode potentials. Two regression models were developed to predict anode potential as a function of [Co], [Fe] and [Mn]. A method to estimate electrical energy consumption for copper electrowinning is also presented.

By Darryl Lovato, Ramiro Pereyra, Daniel S. Schwartz

"During an annual inventory of nuclear material, a plated steel container which contained plutonium oxide failed. The container had been packaged for temporary storage but had been overlooked and remained in storage for more than 23 years. Although it was determined that the failure occurred through the slip-top rim, a metallurgical evaluation was requested to help to determine the integrity of the container.Optical metallography and scanning electron microscopy were used to analyze the character and degree of corrosion in the container. The depth of corrosion, measured at approximately 10 µm, did not pose a threat to the integrity of the container. However, the corrosion morphology and chemistry did suggest that a galvanic cell had developed between the tin and steel from the condensation of water. The morphology also suggests that the attack of the steel took place over a series of cycles due to changes of the environment.IntroductionMetallographic analysis was requested as part of the investigation into the mechanism of the failure of a slip-top container (#38621) containing plutonium oxide (PuO2) powder. The container had leaked during a special nuclear material (SNM) annual inventory causing contamination and closure of the vault. A photograph of the container and interior container is shown on the right in Figure 1. An initial investigation established that the source of contamination was the consequence of the failure of multiple layers of containment. Initially by the deterioration of the interior plastic bottle and polyvinyl chloride (PVC) bagout bag, and finally through the lid and steel container interface at a location where tape had not adhered properly [1]. Although the source of the breach was established, it was determined that metallographic analysis was important to establish the extent of deterioration of the steel container."

Jan 1, 2008

By Francis Vanbellen

Umicore Precious Metals Refining operates an integrated precious metals smelting and refining plant in Hoboken, Belgium. Once a smelter and refiner of complex concentrates, the plant today?s feed consists exclusively of industrial and consumer recycled products, making it the world?s largest recycling facility for precious metals. Unlike the fairy tale of the Frog Prince, it took much more than a princess? kiss to successfully realize this makeover. A completely renewed plant has been built over the past decade. The most visible technological innovation was the commissioning of the Pb-Cu smelter. Its flexibility towards very different types of feed makes it perfectly suited as main entry to the Hoboken flow sheet. A new Cu-leaching & electro winning plant and precious metals refinery make up the Precious Metals Operations (PMO) whose targets are fast throughput and maximized yields for gold, silver and the platinum group metals. The Base Metals Operations (BMO), flexibly process the by-products from the PMO, valorizing ?impurities? like indium, tellurium, selenium and others. Off gas and waste water treatments ensure compliance with strict environmental standards. Precious metals recycling is an art that goes beyond mastering a unique flow sheet. Umicore Precious Metals Refining offers a complete recycling service, taking care of sampling and assaying, metals management and logistics. The quality of this integral service is recognized through the attribution of ISO certifications for our operational activities, sampling and the environmental care. And it?s an art that follows Michelangelo?s experience: ?Art is 5% of inspiration and 95% of transpiration.?

Jan 1, 2006

By Kazuya Kitatani, Gen Sasaki, Naoto Ohta, Hideharu Fukunaga, Makoto Yoshida, Jin Pan, Kenya Nagahisa, Toshihiro Ishikawa

"A sintered SiC (Tyranno-SA) fiber-reinforced MAS glass matrix composite was fabricated by using a slurry infiltration method and hot-pressing. The microstructure and mechanical properties were investigated: To prepare the preform, the MAS glass slurry including a dispersing agent was infiltrated into a bundle of the fibers. The preform was then hot-pressed under the conditions of 1473 K, 30 MPa, 3.6 ksec. A unidirectionally-reinforced oxide matrix composite with 50% Vf. of the fiber and a density of 2.84 g/cm3 was obtained. As the mechanical properties at room temperature, the three-point flexural strength- and quasi-static adsorbed energy were 500 MPa arid 6,000 J/m2, respectively. Without graphite or an h-BN pre-coating on the surface of the fiber, pull-out and bridging of the fibers from the matrix was found, and this leads to a high value of the adsorbed energy. By TEM observation, nano-scale crystalline products were found between the fibers and the glass matrix. The push-out test reveals that this layer causes the appropriate debonding of the interface during the fracture process of the composite.Introduction It is known that the CFCCs (continuous-fiber-reinforced ceramic matrix composites) are characterized by their non-linear fracture behavior, which is' hardly found in monolithic ceramic materials. It is inevitable for the CFCCs to exhibit a large fracture toughness so 'that debonding of the fiber/matrix interface; pull-out and bridging of the fibers then' occurs during the fracture process. This series of fracture behavior is known as the so-called ""the mechanism of toughening of the CFCCs"". Thus, different from the MMCs in which strong interfacial bonding is necessary, the interfacial strength of the CFCCs has to be controlled. As techniques for controlling the interfacial strength, it is also known that both a CVD-graphite coating and an h-BN coating are effective to induce the mechanism of toughening[1,2]. In the case, of the Si-C-O or Si-Ti-C-O fibers/glass or crystalline oxide matrix composites, it is reported that the formation of the in-situ graphite layer, which is also effective to increase the fracture toughness of the CFCCs, is often found during the fabrication process such as hot-pressing. The lower the crystallinity of the Si-C-O fibers, the higher is the tendency to form the in-situ graphite layer as found by the chemical reaction between the fibers and the glass matrices[3-12]. On the-other hand crystallized stoichiometric 'SiC fibers are attractive for high temperature service because of the higher phase stability compared to the Si¬C-O or Si-Ti-C-O fibers. However, in the previous, studies, the mechanical properties and the interfacial chemical reaction of the crystallized SiC fibers / glass matrix Composites have still been unknown. In this study, a polycrystalline 'sintered SiC fiber-reinforced MAS glass composite was fabricated. The mechanical properties and microstructure were then investigated. The slurry infiltration technique followed by hot-pressing was used to prepare the composites. The formation of the in-situ graphite layer and the relationship between microstructure and mechanical properties at room temperature were examined by the TEM observation of the fiber/matrix interface."

Jan 1, 2000

By Robert P. Stevens

It is important for a refractory supplier to make systematic petro-graphic examinations of products which have been in service in the furnaces and kilns of customers. The petrographic examination of refractory service samples involves the microscopic study of polished and/or thin sections, supplemented by electron probe microanalysis, as well as the bulk chemical and XRD analysis of zones in the samples. The evolution of the A. P. Green Refractories Company petrographic laboratory is described, and the application of petrographic methods is illustrated in the examination of service refractories from a Portland cement rotary kiln and an AOD stainless steel vessel. The objectives of such studies are to assist the customer in the solution of his refractory problems, and to accumulate data which are of use in the design of improved refractory products.

Jan 1, 1981

By Toshiro Kuji, Masakazu Fujita, Tetsuji Saito

"The magnetic properties of the magnetic materials were deeply dependent on the microstructures. In this study, the novel technique to produce the desired microstructures in a controlled manner was proposed. The technique consisted of the production of the amorphous alloys and the control of the crystallization process. The technique was applied to improve the magnetic properties of Nd-Fe-B permanent magnets. The microstructural control of the magnets exhibited the excellently high energy-products of higher than 430 kJm-1. The relationship between the magnetic properties and the microstructures of the Nd-Fe-B permanent magnets was discussed.IntroductionThe intrinsic properties of the materials are basically determined by the properties of the constituent elements or the compounds. However, it is often noticed the difference between the observed properties and the theoretical values expected from the intrinsic properties of the materials. This indicates that the observed properties of the materials are determined not only by the properties of the constituent elements. In other words, the observed properties of the materials are also strongly dependent on the morphology of materials. This means that the microstructural control may creates a great improvement of the properties of materials.In Nd-Fe-B permanent magnets, the superiority arises from the uniaxial intermetallic Nd2Fe14B compound which has a large saturation magnetization and a high anisotropy field [1,2]. The magnetic properties of the Nd-Fe-B permanent magnets are dependent on the microstructure, that is, the size, shape and degree of the crystallographic alignment of the Nd2Fe14B phase. Currently, the Nd-Fe-B permanent magnets have been produced by either sintering or melt-spinning [3,4]. In the sintered magnets, alignment of the Nd2Fe14B phase is achieved by the prior green compaction of the crushed ingot powders in an applied magnetic field [3]. In the melt-spinning approach, alignment of the Nd2Fe14B phase is achieved by hot deformation [5]. Amorphous melt-spun ribbons are comminuted and then are consolidated into bulk form by hot pressing before hot deformation. As-hot-pressed magnets have randomly oriented Nd2Fe1~ grains [6]. Subsequent die upsetting of as-hot-pressed magnets gives rise to the crystallographic alignment of the Nd2Fe14B phase."

Jan 1, 1998

By Charles I. Richman

Aquispirillum magnetotacticum (AM) is gram-negative hetrotrophic bacteria that belongs to a class ,of magnetotactic bacteria that have an ecological niche in marine marches and fresh water swamp sediments. Thiobacillus Ferrooxidans (TF) is a Gram-negative, acidophillic chemoliths that may have similar chemical conditions within the cytoplasmic membrane as Aquaspirillum M. to support growth of Magnetosomes. Magnetosomes are cellular bodies that accumulate under slightly aerobic conditions. Magnetotactic motion occurs in an external magnetic field and depends on the medium viscosity. The Atomic Force Microscope equipped with a magnetic tip shows the presence of Magnetosomes in these bacteria strains. The size, shape of magnetosomes in AM and TF strains are characterized.

Jan 1, 1998

By Lloyd R. Nelson

The feasibility of producing low carbon (LC) ferromanganese (FeMn) by lime-'ore' melt refining of high-grade ferromanganese silicon (FeMnSi) was investigated. Thermodynamic simulations demonstrated significant benefits in moving from a single-stage ladle operation to a two-stage counter-current reladling operation (to emulate the commercial Penin Process). The theoretical alloy silicon content was predicted to be refined from 1.57 to 0.005 per cent silicon, at a 6.2 per cent higher manganese yield (yield predicted to increase from 82.3 to 88.5 per cent). Extension of this counter-current refining principle, to a multistage Counter-Current Reaction Launder (CCRL) was investigated using the Slag Metal And Gas Klnetics (SMAK) software to model the mass transfer kinetics of the multicomponent coupled reaction system. Simulation results suggested that commercial production of 50 000 tonnes per annum (tpa) of refined LC FeMn, containing less than 0.5 per cent silicon, at manganese yields of up to 90 per cent, should be feasible in a compact CCRL (7 m long by 0.7 m wide).

Jan 1, 1994

By A. Haxhiaj, Mitovica, E. Haxhiaj

"The paper discusses problems encountered during the release and possibility of using the thermal gas quantity Mathematical models are used to calculate the positive thermal effects of the gases and losses of thermal quantity with gases in the melting process of electric furnaces. The paper discusses in details the percentages of CO, CO2, H2S, O2 and the humidity in gases and their impact on the technological process in electrical furnaces in Drenas. The paper also confers the quantity and temperature of gases, the transfer of thermal quantity and dust with gases in the environment. The paper presents the percentage of humidity in the load which is added in electric furnace for melting and its impact on thermal and environmental balance in the technological process of melting in electric furnaces. Key words: Furnace, load, temperature, humidity, gases.IntroductionNickel easily reacts with gases in the atmosphere of the furnace in which the nickel ore is processed. Such reactions can explain challenges in producing high quality nickel. Reductive atmosphere with the surrounding gases composed of sulphurous anhydrite has harmful effects on the production of nickel. This is mainly due to solubility of hydrogen as well as nickel oxide in the melted metal. Nickel reacts with carbon monoxide and forms carbide of nickel and nickel oxide which dissolve in the melted metal. Carbon monoxide also dissolves in the melted metal. The presence of carbon dioxide and water vapor in the atmosphere of the furnace impact the decrease of acidity in reductive atmosphere of the furnace. The carbon dioxide reacts with nickel and forms nickel oxide and carbon monoxide. Water vapor reacts with nickel and forms hydrogen and nickel oxide that have negative impact on the structure of nickel and its alloys. In this paper the analytical and experimental analyses are proposed that lead to minimization of the negative effects of gasses and humidity in the melting process. As the practical example, the electrical furnace in Drenas is analyzed.1. The Load and Its CompositionThe basic function of the rotational furnace is drying and reductive roasting of the ore which directly is loaded into the electrical furnace for melting. It is important to mention that the degree of roasting and pre-reduction of iron-nickel oxides is reached if the roasting process of the load in the rotational furnace is done at the temperature of 900°C to 1000°C, with the reductive atmosphere in the furnace and with minimal amount of oxygen in the processing gas. The optimal process of roasting and pre-reduction of the load in its mass is around 13 wt%. With the removal of the humidity and the sterile pare of the ore, with the positive impacts in utilization of the thermal and electrical energy in the melting process in electrical furnaces."

Jan 1, 2013

By Entov Vladimir M., Gilmer R. Burgos, Andreas N. Alexandrou

"Processing of metal alloys in their mushy state represents a new trend in metal processing. As part of this process, known also as thixocasting, a specially prepared slurry at a temperature in the mushy region is injected into a die. Parts produced using this technology offer better mechanical properties than those produced by casting, and comparable to those of forged alloys.In thixocasting, semisolid slurries are highly concentrated suspensions of rounded rosette-like crystals in eutectic liquid. The mechanical behavior of the slurry is determined by the structure and properties of the skeleton formed by the alpha phase particles. The skeleton structure is almost never at equilibrium, and its evolution is, governed by a number of kinetic phenomena of different c11'aracteristic time-scales. Therefore, the skeleton structure depends on the mechanical and thermal history of the material. As a result of these kinetic processes, the rheological properties of the material, such as effective viscosity and yield stress, decrease with structure breakdown, and increase with its development. In the present investigation, the behavior of semisolid slurries during processing is modeled using the conservation equations, and a Herschel-Bulkley fluid model. The rheological parameters are assumed to be functions of the solid volume fraction, and of a structural parameter that changes with processing history. The evolution of the structural parameter is described by a first order kinetic differential equation that relates the rate of build-up and break-down of the solid"

Jan 1, 2000

By B. M. Satish

The aim of the present work is to study the effect of annealing on the vibration damping capacity of high-chromium (16%) ferromagnetic steel. The alloys were prepared from raw materials of 99.9% purity melted in a high frequency induction furnace under high vacuum. The samples were heat-treated in vacuum at various temperatures (800 to 1200°C) for 1 hour followed by slow cooling (120°C/h). The inverted torsional pendulum method was used to evaluate the vibration damping capacity. The results indicated that the vibration damping capacity of the alloys is influenced by annealing and there exists a critical annealing temperature after 1000°C. The damping capacity increases quickly below the critical temperature since the magnetic domains move more easily.

Jan 1, 2009

By Qing-Yun Huang, Xiao-Yi Zeng, Bing Xie, Hong-Yi Li, Jia-Rong Yan

"In order to utilize vanadium resource in vanadium-titanium magnetite ore efficiently, vanadium distribution ratio between hot metal and slag should be improved during BF process, meanwhile the precipitating of Ti(C,N) in slag must be minimized. Effects of temperature, Ti02 content in the slag and basicity on vanadium distribution between slag and hot metal were investigated by experiment and thermodynamic calculation. The results indicated that high temperature, low Ti02 content and high binary basicity of slag were beneficial to increase the vanadium distribution ratio. The effects of temperature and Ti02 content in slag on vanadium distribution were stronger than that of slag basicity.IntroductionVanadium is an important element that is widely used in industrial fields. Most of vanadium resource is hosted in vanadium bearing titanomagnetite [l]. Vanadium bearing titanomagnetite is thus one of the domainate raw materials to produce the vanadium products. In other words, the comprehensive utilization of vanadium bearing titanomagnetite is beneficial for vanadium resource utilization. Vanadium bearing titanomagnetite sources are abundant in Pan Xi of China [4]."

Jan 1, 2013

By E. Gutierrez-Miravete

Hot pressing processes are widely used to shape metallic, ceramic, and glass components. The process is an essential step in manufacturing ceramic fibre-glass matrix composites. The paper describes the use of computer simulation by the particle method, to the analysis of the deformation and flow of glass during hot pressing. The hot glass is represented by an assembly of interacting particles which deform in response to the applied pressure. The results, which should be regarded as complementary to continuum-based studies, provide useful insight about the hot pressing process.

Jan 1, 1990

By Shadia J. Ikhmayies

Polycrystalline CdTe thin films were prepared by vacuum evaporation on glass substrates. The I-V plots which were linear were used to find the resistivity. A value of 2.10×106 .cm was obtained. The transmittance was measured in the wavelength range 400-1100 nm. The bandgap energy was found to be 1.48 eV. X-ray diffraction pattern shows that the material deposits in the zinc blend structure with one strong reflection from the C(111) plane. The scanning electron microscope image shows a uniform surface with a small density of large (mµ1£) grains scattered on the surface.

Jan 1, 2009

By Liya Bochkareva, David Hui, Sergey Eremeev, Maksim Kireitseu, Igor Nedavniy

The principal goal of the present paper is to demonstrate an application of modern software engineering tools for modeling virtual reality and molecular dynamics of novel nanocomposites. The main technical components of presented system are I) software and nanoengineering tools for modeling of virtual reality, molecular dynamic and 30 video images of novel diamcindscontaining nanocomposites and 2) Problem tracking system to be used during modeling of virtual reality. A computational scheme and software, which utilizes neural networks and/or Microsoft. Net technique was developed to predict properties of nano-structured materials and optimization and control of nano-devices. Developed software and IT nanoengineering tools can be used by both industrial and private single users. For commercial companies proposed technology may provide better cost-effective alternative to the existing solutions for nanoengineering and modeling their virtual realit. For private users (students, professors, and engineers) proposed technology and IT tools can provide simple and cost-effective solution for nanoengineering while studying, exploring virtual reality and modeling novel nanostructures and its properties leading to an innovation or a discovery. Because of using novel software and methodologies, users can easily operate proposed technologies by available computers and operating systems (Pentium III or IV). In addition, users can upgrade it by their own self-written models, if necessary. The proposed technologies could replace or be used along with technologies for modeling such as 30 max studio and others.

Jan 1, 2004

By S. C. Sharma, M. Krishna, N. Sanmukha

"The oxidation behavior of an aluminium composite with 0, 2, 4, and 6% by weight of hematite at 200 to 500 °C has been investigated. Within the experimental temperature ranges a parabolic weight gain was observed. The, weight gain as a function of oxidation time becomes linear after an initial period on oxidation formation, an oxide scale was found whose morphology depends on temperature, cooling rate and sub-scale formation at the interface between the matrix and reinforcement. The presence of hematite particulate reinforcement has very little effect on the oxidation behavior. The interface oxidization rate was found to be higher than that of other regions. The, oxidation products were either metallic oxides or ceramic oxides. The exposure time of specimens to oxidation was 1000 minutes at various temperatures. In the present work key principles of alloy oxidation were discussed. Also the paper emphasizes various reactions taking ' place and the activation energies involved in the oxidation reactions.IntroductionMetal matrix composites (MMCs) reinforced with ceramic particulate, whiskers, or fibers have received increasing attention due to their potentially high fracture toughness and strength 1-5. Particle reinforced Aluminium MMCs find potential application in several thermal environment, especially in the automobile engine parts, space applications, such as drive shafts, cylinders, pistons, and brake rotors6.With the exception of gold, no metal or alloy is stable at room temperature, they tend to form their respective oxides. Most of the metals in the solid or liquid state are morphologically unstable when exposed to air at higher temperatures. An investigation relating to the temperature profiles of the piston area in a diesel engine has shown that the temperature can reach as high as 500¬800 K in certain regions of the piston. As the piston and cylinder areas are exposed to high temperature environment, the MMCs should have sufficient stability on both mechanical and chemical strength (oxidation). Oxidation occurs at grain boundaries in alloys and at the interface of the particulate and matrix in MMCs, which usually enhances intergranular fracture, resulting in premature failure and severe brittleness 8-10. Therefore for high-temperature applications, it is essential to have a thorough understanding of the oxidation behavior of aluminium MMCs."

Jan 1, 2000

By Qiang Zhong, Bin Xu, Qian Li, Wei Gao, Yongbin Yang, Yaxuan Wang

Lump coal with high volatility is used for providing heat and reductive gas, and ensuring permeability in COREX. However, it is apt to be pulverized in transport and storage process. Therefore, comprehensive utilization of the pulverized coal to produce coal briquettes with appropriate binders is significant, among which the molasses binder cannot meet the technological requirements. In this paper, coal tar pitch binder and BJ additive were used in briquetting and carbonizing process of coal powder. The results showed that BJ effectively activated cold state cohesiveness of the pitch and make it bond the coke particles to a firm briquette at room temperature .Carbonizations of coal and coal tar pitch achieved obvious constriction and formed a carbonized skeleton. The drop resistance of wet briquettes reached over 50 times/1meter. When cured at 1000 °C for 1h under nitrogen atmosphere, the compressive strength of carbonized briquettes came to 6.43 Mpa.

Jan 1, 2016

By Jozef Zmik, Sergey Dobatkin, Martin Fujda, George Raab, Libor Kraus

"The present work, likewise, deals with grain refinement of medium carbon steel AISI 1045 having different initial microstructure resulting from thermal and/or thermomechanical treatment (TM) applied prior severe plastic deformation. In case of TM treated steel, structure refinement was conducted in two steps. Preliminary structure refinement has been achieved due to multistep open die forging process which provided total strain Eef ~ 3. Uniform and fine recrystallized ferrite structure with grain size of the order of 2-5 µm and with nest-like pearlite colonies was obtained. The further grain refinement of steel samples having different initial structure was accomplished during warm Equal Channel Angular Pressing (ECAP) at 400°C. The microstructure development was analyzed in dependence of effective strain introduced ( Eef ~ 2.5 - 4). Employment of this processing route resulted in extensive deformation of ferrite grains where mixture of subgrains and ultrafine grain was found regardless the preliminary treatment of steel. As straining increases the dynamic polygonization and recrystallization became active to form mixture of polygonized subgrains and submicrocrystalline grains having high angle boundaries. The intensive straining and moderate ECAP temperature caused the partial cementite lamellae fragmentation and spheroidization as straining increased. The lamellae cementite spheroidization was more extensive in TM treated steel samples. The deformation behavior of for both steel structural state confirm the strength increase; however the work hardening behavior was modified with respect to initial structure of steel prior SPD processing.IntroductionIn the last years, ultrafine grained materials have attracted considerable research interest because they tend to possess high strength without sacrificing toughness and ductility. Microstructural refinement of steel is usually achieved by alloying and/or by thermomechanical treatment process, which modifies phase transformation. Recently, advancement of severe plastic deformation (SPD) techniques provides another efficient access for grain refinement of metals and alloys. The fabrication of bulk materials with ultrafine grain sizes has attracted a great deal of attention over the past two decades because of the materials' enhanced properties [ 1, 2]. In last decade a worldwide effort in manufacturing process to obtain ultrafine grain structures in steels is persisting."

Jan 1, 2011

By Xie Zhang, Chongyang Zhao, Qingyun Huang, Bing Xie, Xiaopeng Zhen

"Extracting vanadium from vanadium containing hot metal into vanadium slag by BOF is the main vanadium production process in China. In this paper, the influence of Si content in hot metal on the quality of vanadium slag is analyzed. Synthetic vanadium slag with different SiO2 content were melted at 1673 K and then cooled to 303K at the cooling rate of 3?/min. Optical microscopy, SEM, EDS and XRD were used to analyze the mineralogical phases and crystallization behavior of vanadium slag. The results show that vanadium slag mainly contains spinel phase and silicate phase; V is enriched in the spinel phases while Si is concentrated in Fe2SiO4 CaFeSi2O6 and (Fe,Mn)2SiO4 as silicate phase. The melting point of slag increases gradually with the addition of SiO2; whereas viscosity decreases with an addition of 15~19% SiO2 and increases with an addition of 19~27% SiO2.IntroductionVanadium is an important element which is used almost exclusively in ferrous and non-ferrous alloys. The major vanadium products include FeV, V2O5, V2O3, VN and Al-V-Ti alloy. Furthermore, vanadium slags are mostly produced by oxidizing the elements in V-containing hot metal during a duplex refining process. Therefore, the process of removing vanadium from hot metal has its significance on the subsequent process[1].The extraction of vanadium is greatly affected by the mineralogical composition of vanadium slag[2], the distribution of the elements between the spinel and silicate phases and its physic-chemical properties. These characteristics of vanadium slag have been studied in some details. It has been reported that Si mainly exists mainly in the form of silicate which wraps the spinel crystals while small amount of Si stands as phosphorus quartz or diopside[2]. Chen et al.[3, 4] points out, when SiO2 content in vanadium slag increased every 1%, V2O5 decreased 1.48%. Moreover, silicate phases would embarrass the oxidation of V-containing spinels through decreasing the exposing probability[5]. Meanwhile, melting point and viscosity of vanadium slag has been greatly influenced by the SiO2 content. Therefore, this work attempts to analyze the above-mentioned questions systematically."

Jan 1, 2012