By J. C. Danko, R. D. Stout, A. H. Holtzman

The deformation characteristics of pearlite have been studied by light and electron microscopy.1,2 In the electron-microscopic work, deformation was found to take place by 1) ferrite slip which is parallel to the lamellae, 2) slip transverse to the lamellae with both cementite and ferrite deforming, and 3) ferrite-cementite interfacial slip. The transverse slip gives a step-like appearance to the lamellae in light microscopic work. It was thought that spheroidization of deformed pearlite would commence at the regions of maximum cementite deformation, the "stepped" areas. Although there is no possibility for seeing slip in the microstructure if the specimen is polished after deformation, the step-like appearance of the lamellae clearly indicates the transverse deformation. Thus, the areas of cementite deformation are apparent after polishing and the effect of deformed areas on spheroidization may be studied by the usual metallographic techniques. This note reports the result of a metallographic investigation which substantiates that spheroidization begins in the "stepped" areas. An AISI 1080 steel was normalized, re-austeni-tized at 1040°C, and isothermally transformed at 700 ± 4°C for 4 hr. Cubes, 5 mm to a side, were compressed between parallel plates to strains of 20, 40, and 50 pct. After deformation, specimens were heated to 600, 650, and 700°C; withdrawn at increasing time intervals and examined metallo-graphically for the percentage and distribution of spheroidite. The percentage of spheroidite was determined by lineal analysis. A micro structural region considered as spheroidized was one in which a lamellar skeleton was not distinguishable. Table I gives the times necessary for 95 pct spheroidization for each condition of strain and annealing temperature. Fig. 1 shows the microstructure of coarse pearlite compressed 20 pct, then polished and etched. Here the lamellae form a step by bending at two

Jan 1, 1959

By George Burgess

1. Introduction.-THE methods of production of sound steel ingots have been described in several papers read recently before this Institute. It was thought by Director Stratton, of the U. S. Bureau of Standards, and ourselves to be of sufficient interest and importance, as a further contribution to this subject, to compare the properties of rails rolled in one mill according to American practice, from several types of ingot of substantially the same chemical composition but cast by several processes; and to compare in considerable detail the properties of an ingot manufactured by the Hadfield special-feeding process and one of the usual type for rolling into rails. We are greatly indebted to F. W. Wood, President of the Maryland Steel Co., who made this investigation possible by kindly placing his rail mill at our disposal; and he and his associates at Sparrows Point did everything possible to make the experiment a success, including the execution of several of the tests and analyses. 2. Classification and Manufacture of Ingots.-Of the ingots used in this investigation, eight were made in Sheffield and furnished by Sir Robert Hadfield, and one was made and furnished by an American steel company,' as a comparison ingot, and was supposed to represent the usual type of ingot from which rails are made.

Jan 2, 1915

By Andrew Mayer

EARLY in 1942 National Lead Co. was requested by the War Production Board to construct and operate a plant for the Government to produce magnesium by the ferrosilicon process which had been developed by Dr. L. M. Pidgeon in the laboratories of the Canadian National Research Council. A contract with the Defense Plant Corporation was concluded in May 1942 and Magnesium Reduction Co., a wholly owned subsidiary of National Lead Co., was formed to carry out this project. The capacity of the plant was rated at 10,000,000 lb. of magnesium per year, equivalent to an average production of about 14 tons per day. THE PROCESS The process, in brief, is as follows: The raw materials are dolomite and ferrosilicon, 75 per cent grade. The dolomite is calcined, the calcine and ferrosilicon are ground and mixed and the mixture is briquetted. The briquets are charged into tubular retorts of chrome-nickel steel set horizontally in a furnace with the open ends projecting outside the front wall. The retorts are then closed and evacuated. Magnesium is liberated according to the reaction 2(MgO, CaO) + Si = 2Mg + 2CaO, SiO2 It is distilled from the charge and condensed on a removable sleeve in the throat of the retort. Sodium and potassium, if present, are also liberated, distilled and condensed on a "sodium condenser" in the end of the retort. At the expiration of the distillation period the retorts are discharged and the cycle of operations is repeated. For the rated daily capacity of ±. tons of magnesium there are required approximately 170 tons of dolomite, equivalent to about 85 tons of calcine, and 16.5 tons of ferrosilicon. The retort residue, a bulky powder which at present is waste, amounts to about 87 tons. CHOOSING THE SITE The investigation to select the location of the plant was conducted by the Research Laboratories of National Lead Co. This work included geologic and economic surveys of a number of districts, examination of dolomite samples by chemical, spectrographic and petrographic methods and large-scale tests of dolomite from several of the more promising localities. In the last-named tests 2-ton samples were put through the ferrosilicon process in the pilot plant of the Canadian National Research Council, under the guidance of Dr. Pidgeon. The conclusions drawn from the investigation, in regard to the quality of dolomite to be used in the ferrosilicon process, were: First, the dolomite should contain not less than 21 per cent MgO

Jan 1, 1944

By George D. Dub

INTRODUCTION OWENS LAKE is at present a source of important nonmetallic minerals, sodium carbonate (soda ash, Na2CO3); sodium sesquicarbonate (trona, Na2CO3.NaHCO3.2H20) and borax, (Na2B407.10H2O). Owens Lake is a closed basin in the southern part of Inyo County, California, at the southern end of Owens Valley, east of the Sierra Nevada Mountains and west of the Coso and Inyo Mountains. Broadly considered, it is in the Great Basin area, but at no time was it a part of Lake Lahontan. CLOSED BASINS Closed basins are phenomena of arid or semiarid regions where outflow is considerably less than inflow and where accordingly soluble salts concentrate in residual liquid. When inflowing waters originate in areas where the rocks are predominantly marine sediments, the residual basin liquid is primarily a chloride brine; if the rocks are largely igneous, the residual brine tends to be alkaline containing carbonates, and sometimes borates as well. Since normally, both types of rocks occur in regions contiguous to closed basins, residual liquids do not often fit into the two broad divisions mentioned. No two residual brines are exactly alike, just as no two ore deposits are exactly alike. Even out of the same closed basin, it is possible to get widely different analyses of liquids since underground and surface flows, as well as local evaporation rates and other conditions might have a marked influence on residual-liquid compositions. At Searles Lake, The American Potash and Chemical Corporation is building a plant to process a lower-level brine which is considerably higher in sodium carbonate and borax, and lower in potassium chloride, than that company has processed for many years. F. W. Clarke1 has classified waters of closed basins as follows: I Chloride type; largely sodium chloride (NaCI) and of oceanic type, such as Great Salt Lake. Related is the Dead Sea, a bittern residue of magnesium, potassium and sodium chlorides. 2. Sulphate type; largely sodium sulphate (Na2S04) with considerable sodium chloride such as Sevier Lake, Utah; Laramie Lakes, Wyoming; Dale Lake, California. 3. Carbonate type; high in carbonates and fairly high in sulphates, such as Moses Lake, Eastern Washington; and the Nebraska Potash Lakes. 4. Carbonate-chloride type; lower in carbonates than type 3 and about equally rich in sulphates, such as Pyramid Lake, Nevada. 5. Sulphate-Carbonate type; quite high in sulphates and carbonates, such as Pelican Lake, Oregon. 6. Triple type; considerable quantities of carbonates, sulphates and chlorides

Jan 1, 1947

By J. Eric Belford

The Kidd Creek orebody is a massive base metal sulphide deposit with surface dimensions of 168 m by 670 m. The steeply dipping ore- body has been evaluated to a depth of 1 524 m. To date, the mining of the orebody has been divided into three stages. The first stage of mining was an open pit operation which supplied ore from 1966 until 1977 when a depth of 219 m was reached at the widest or north end of the orebody. The second stage of mining, called No.1 Mine, was the development of an underground mine to replace the pit and recover the ore from the floor of the pit to a depth of 792 m. Development of the underground mine started in 1969. Full production of 273 000 tonnes per month was attained in 1977. The third stage of mining called No.2 Mine, was initiated to accommodate a production expansion and included the development of a second underground mining operation to recover the ore from the bottom of No.1 Mine, i.e. the 2600 level; to a depth as yet undetermined but most likely the 4600 foot level. Development of the No.2 Mine began in 1974. Full production of 91 000 tonnes per month will be achieved in 1982. The choice of the 2800 level as the partition between the two underground mines was based on the following factors: The 2600 level is the lowest level which can conveniently be mined through the No.1 Mine crusher on the 2800 level. Development and trial stoping methods for mining at depth could be evaluated in the 2600 to 2800 block utilizing the existing hoisting facilities of No.1 Mine. Early development of the ore in the 2600 to 2800 block would provide additional mill feed sooner than could be achieved by developing from No.2 Shaft. The underground mining plan then is to mine from the pit floor down to the 2600 foot level and at the same time mine from the 2800 level down to at least the 4600 foot level. PLANNING The Kidd Creek operations are designed to follow a logical mining sequence. The grade of ore supplied to the concentrator is the result of following the mining plan. The philosophy of mining has been to mine downward in horizontal slices. In the case of No.1 Mine the slices are 122 m thick while in No.2 Mine the slices will be 183 m thick. The point of this approach is to mine the pillars immediately after creating them rather than allowing them to stand, deteriorate and generate uncontrollable situations. Two types of ore are handled separately to optimize recoverable values in concentrates. The 'A' type ore is a copper zinc ore with some silver and little lead. The 'C' type ore is a zinc silver ore with some lead and copper

Jan 1, 1981

By F. W. Gordon

The Whitwell firebrick hot-blast stove, for furnace use, may be seen in its three main stages of development in the accompnying drawings. Fig. 1 is the stove of 1869, the year in which it was thoroughly tested at the Consett furnaces, England; Fig. 2, the stove of 1876 and 1877, in which it was intended to reduce the cost by increasing the height; Fig. 3, the stove of 1880. Many modifications were made from time to time, generally in the direction of improvement, but the drawings illustrake the main features of progress. In the stove of 1869 the plan was to introduce the gas at A, and pass it up and down between each alternate wall, the air in the reverse direction, passing in at B. The friction in this stove was so great, owing to the restricted area of the passages and the many revervals of the gaseous current, that it was deemed imprudent to build the stoves higher than 28' 6". Another reason mas that the great importance of cleaning was carefully kept in view, and it was very difficult to operate any hand scraper even to this depth. For these reasons the 22' X 28½' stove held the field for several yearn. A slight change made from this was to the 18' X 40' stove, where the height was increased, but the dumber of walls diminished. In this stove the friction was somewhat reduced, but so was the heating surface, and although it cost a little lea it was not any better. The next important change, seen in Fig. 2, was by increasing the height to GO feet and keeping the full number of walls in the stove. The heating surface and mass were much increased in proportion to the cost, and the friction decremed by alterllating over and under two or more walls, instead of one, as formerly. This stove gave admirable satisfactiou, but, although the proper doors were provided, it was very difticult to clean, owing to the long (distance the scrapers lid to traverse. Stove No. 3 is a modification of No. 2. The great question was how to decrease the cost mithotlt impairing in any yaw the

Jan 1, 1881

By C. D. Demond

IN reverberatory smelting, fuel is the chief item of expense, as it commonly is in processes using large percentages of it. Hence the most suitable supply is eagerly sought; that is, the supply which, in the end, yields the greatest net profit. The better grades are not infrequently bought, even at an advanced price, because they are apt to be decidedly more economical. High price, of itself, however, is no merit, for freight is generally the largest part of the cost of fuel, and the nearby supply may yield as high efficiency as that from a greater distance. If a poorer grade is reasonably good, and if its cost is low enough to more than offset the decreased technical efficiency, it is of course the more suitable. Any smelting, operation depends for both efficiency and economy on raising the furnace atmosphere considerably above the "critical" temperature; that is, above the temperature at which smelting is completed. If this temperature is not exceeded, smelting stops, no matter how much coal is burned; and the real value of a fuel depends on the number of degrees that the temperature is continuously kept above this point. For example, if one fuel maintains 2,500° F. and another only 2,100° F., while the "critical" temperature is 2,000° F., the first is worth at least five times as much as the second, although the increase above atmospheric temperature is only one-fifth more in one case than in the other. This "margin of temperature" above the smelting point is much more significant than the total number of heat units developed from the fuel. The case is parallel to that of water flowing from a pipe. The reservoir may contain a billion gallons of water; but, even though the fluid has come to the nozzle, not a drop will run out, where it can be of practical use, unless the level in the reservoir is higher than the nozzle; and the speed and volume of flow depend on how much higher the level is in the reservoir than at this point. If the temperature inn a furnace is not above the critical level there will be no slag to flow over the skimming plate, even though there are enough heat units to bring an unlimited quantity of charge up to the point of slag formation; and just as the value of a water supply for the purpose of putting out a fire depends largely on the effective head, so the difficulties of furnace management

Jan 8, 1914

By George Gauci

INTRODUCTION The Broken Hill orebody was discovered in 1883. The richness of the deposit encouraged rapid development of the field and within fifteen years ten mining companies were operating. By 1940, several companies located in the centre of the field with limited reserves, had ceased operation. These leases have been acquired by Broken Hill South Limited and North Broken Hill Limited. The four companies currently operating in the field are, in order of increasing production rate:¬- Broken Hill South Limited (BH South) North Broken Hill Limited (North BH) The Zinc Corporation, Limited (ZC) and New Broken Hill Consolidated Limited (NBHC) The tonnages treated by each company since the present plants have been in operation are shown in Figure 1. The leases are located as shown in Figure 2, and an aerial view of Broken Hill showing the spread of the City on each side of the line of lode is shown in Figure 3. The present treatment plants date back to the early 1930's when the BH South plant was built. The North BH and ZC plants were built in 1939 and NBHC's in 1952. The three plants built before 1940 have similar crushing and grinding flowsheets. NBHC differs in that it includes rod mills with consequent differences in fine crushing equipment.

Jan 1, 1970

By T. S. Fuller

The tensile properties of steels at elevated temperatures have been studied by numerous investigatorsll primarily for the purpose of determining their suitability for structural uses. Tests with this objective have been confined largely to the temperature range of approximately 20" to 500' C., because of the rapidly decreasing tensile strength at the latter temperature. Tests have also been extended to higher temperatures2 for the purpose of determining the most suitable forging range. This temperature range is also of theoretical interest. The phenomenon if increased tensile strength and decreased ductility .in the so-called "blue-heat" range, approximately 200" to 300" C., is well known. It was suggested to the Bureau early in 1926 that a study of the properties of rail steels in this temperature range might prove of interest in relation to the studies of transverse-fissure failures in rails. There were available from another investigation3 several new rails from several different heats made to approximately the same specification requirements, the complete manufacturing histories of which were known. It was decided to determine, at least in the preliminary series of tests, only the ultimate tensile strength, elongation and reduction of area, because of the difficulty, time and cost involved in determining the proportional limit and yield point at elevated temperatures.

Jan 1, 1930

By Oscar M. Wicken

The mineral magnesite (MgCO3) if pure would consist of 47.7 pct MgO and 52.3 pct CO2. It is one of the calcite group of rhombohedral carbonates which includes calcite (CaCO3), siderite (FeCO3), rhodocrosite (MnCO3), and smithsonite (ZnCO3) among others. The members of this group enter into a wide range of substitutional solid solutions, whose range is still imperfectly known.* MgCO3 and FeCO3 appear to form a complete series of which breunnerite (ferroan magnesite) is a well known variety. Because of the considerable difference in size of the Ca and Mg ions, there is only a limited range in substitution in the MgCO3-CaCO3 series. (Dolomite, not strictly a member of the calcite group, may be regarded as an ordered structure developed when Ca: Mg is approximately 1:1.) The practical consequence of these relationships is that the lime carbonates (calcite and dolomite) are commonly present in magnesite deposits chiefly as mechanical mixtures. Magnesite may be either crystalline or "amorphous" (cryptocrystalline). The crystalline form has a hardness of 3.5 to 4.0. The color may range from white to black through shades of yellow, blue, red or gray. It is rarely found pure but generally contains variable amounts of iron, lime, and silicate minerals. Color cannot be used as an index of purity except under specific local conditions in a single quarry. In a given quarry an experienced man may be able roughly to grade magnesite by intuitively assessing such features as crystallinity and color. Crystalline magnesite occurs in larger deposits, but the cryptocrystalline variety is more common. The latter is fine-grained and compact and shows no cleavage; often it is descriptively called "bone magnesite." The fracture is usually conchoidal, and hardness is 3.5 to 5.0. It is normally white, but sometimes it is light yellow to orange or buff because of included impurities. In addition to lime and iron, which may be present in small amounts, silica may be present as inclusions of serpentine, quartz, chalcedony, or other minerals. In general, commercial deposits of "amorphous" magnesite have lesser amounts of accessory minerals than does crystalline magnesite. The specific gravity of "amorphous" magnesite is 2.90 to 3.0. Pure, crystalline magnesite has a specific gravity of 3.02, but iron carbonate, commonly present, raises the specific gravity to somewhat higher values. Magnesite dissociates, when sufficiently heated, into magnesia (MgO) and carbon dioxide. Either simultaneously or upon further heating the magnesia develops a crystalline structure identical with that of the natural mineral, periclase, which occurs sparingly in nature but not normally in workable deposits. Brucite is another magnesium mineral capable of being directly reduced to magnesia by heat alone. Brucite (Mg(OH)2) has been mined for the production of various grades of magnesia. It theoretically contains 69.1 pct MgO and 30.9 pct H2O. It may be white, but is generally blue or green with a gray cast. It has a translucent appearance. The mineral is soft (hardness, 2.5), and has a specific gravity of about 2.4. Nomenclature of Products The word "magnesite" literally refers to the natural mineral, but common usage has applied it plus a prefatory word to two other

Jan 1, 1960

By N. A. MacLeod

Ball wear in wet grinding mills has been the subject of considerable discussion in the last few years. Its importance to millmen is obvious in view of the fact that ball wear may cost from 2 to 4 per ton of ore for the more fortunate operators and many times this cost when a refractory ore must be reduced to a fine state of comminution. Consequently, any factual information that may be obtained on the nature of ball wear may be applied to introduce changes leading to lower ball consumption and therefore also to lower costs. In 1940, while employed with the Britannia Mining and Smelting Co., Britannia Beach, B.C., I had occasion to investigate factors that might affect ball consumption. We performed a number of tests, which will be briefly described. These tests originated as a result of changing from a 3½-in. ball to a 2-in. ball of different type of manufacture and were motivated by the desire to obtain the best possible type of 2-in. ball. Our testing was helped by the fact that the company operated a one-ton electric furnace, so that it was quite easy to make steel changes. It should be emphasized at the beginning that these tests produced results that in their general application to milling should be interpreted qualitatively rather than quantitatively. As will be evident in the description of the method used in testing, the balls were subjected to an intermittent batch grinding treatment, which may have produced results in rate of steel wear that may not have an accurate correlation with steel consumption in full scale mill operation. However, with this bed and rather arbitrary method of testing, results were obtained that may be of some interest and may stimulate further work on this subject. Unfortunately, owing to pressure of war work, our tests, which we had intended to repeat on a continuous grinding operation, had to be discontinued. Method of Testing Tests Were made in a Small cylindrical mill, rotating at 72 r.P.m. Internal dimensions of the mill were 10½-in. dia. by 9 in. The cylindrical inner surface was lined with rubber and the two ends were formed by steel plates. A charge of 2000 grams dry feed and 2000 C.C. of water was added evev 2 hr., the mill being drained of pulp before the addition of each charge, by tilting and sluicing with water. The mill was run On afternoon and night shift for daily periods of about 15 hr. total grinding time, and each test lasted from 60 to 150 hr. This batch method of testing involved a higher average pulp temperature in the mill, which undoubtedly affected comparative results in Some of the tests. Hardness oF Ball vs. Wear In these tests, special "eutectoid" steel balls were used, some of which were chill-Cut and quenched, some sand-cast and quenched, and some sand-cast and annealed to a dead soft condition. The results obtained, using as mill feed an ore containing considerable free quartz and

Jan 1, 1947

By N. A. MacLeod

Ball wear in wet grinding mills has been the subject of considerable discussion in the last few years. Its importance to millmen is obvious in view of the fact that ball wear may cost from 2 to 4 per ton of ore for the more fortunate operators and many times this cost when a refractory ore must be reduced to a fine state of comminution. Consequently, any factual information that may be obtained on the nature of ball wear may be applied to introduce changes leading to lower ball consumption and therefore also to lower costs. In 1940, while employed with the Britannia Mining and Smelting Co., Britannia Beach, B.C., I had occasion to investigate factors that might affect ball consumption. We performed a number of tests, which will be briefly described. These tests originated as a result of changing from a 3½-in. ball to a 2-in. ball of different type of manufacture and were motivated by the desire to obtain the best possible type of 2-in. ball. Our testing was helped by the fact that the company operated a one-ton electric furnace, so that it was quite easy to make steel changes. It should be emphasized at the beginning that these tests produced results that in their general application to milling should be interpreted qualitatively rather than quantitatively. As will be evident in the description of the method used in testing, the balls were subjected to an intermittent batch grinding treatment, which may have produced results in rate of steel wear that may not have an accurate correlation with steel consumption in full scale mill operation. However, with this bed and rather arbitrary method of testing, results were obtained that may be of some interest and may stimulate further work on this subject. Unfortunately, owing to pressure of war work, our tests, which we had intended to repeat on a continuous grinding operation, had to be discontinued. Method of Testing Tests Were made in a Small cylindrical mill, rotating at 72 r.P.m. Internal dimensions of the mill were 10½-in. dia. by 9 in. The cylindrical inner surface was lined with rubber and the two ends were formed by steel plates. A charge of 2000 grams dry feed and 2000 C.C. of water was added evev 2 hr., the mill being drained of pulp before the addition of each charge, by tilting and sluicing with water. The mill was run On afternoon and night shift for daily periods of about 15 hr. total grinding time, and each test lasted from 60 to 150 hr. This batch method of testing involved a higher average pulp temperature in the mill, which undoubtedly affected comparative results in Some of the tests. Hardness oF Ball vs. Wear In these tests, special "eutectoid" steel balls were used, some of which were chill-Cut and quenched, some sand-cast and quenched, and some sand-cast and annealed to a dead soft condition. The results obtained, using as mill feed an ore containing considerable free quartz and

Jan 1, 1947

By E. L. Jr. Spain

THE deposits described in this paper occur over much of Wayne County and in the southeast portion of Hardin County, Tennessee, and in the northeast and northwest portions of. Mississippi and Alabama respec-tively. The presence of tripoli in this region has been known for some time and descriptions of various occurrences in Tennessee have been made by Jewell1 and Miser2, while Hilgard3, Lowe4 and Logan5 have treated the deposits that occur in the adjacent portions of Alabama and Mississippi, but there has not been a general survey of the entire field summarizing completely the geology of the deposits with respect to their origin and stratigraphic relationships. During 1934, while engaged in surveys of mineral resources through this region for the Tennessee Valley Authority, the writer collected data with this in mind, and has assembled them in this report. He is indebted to H. S. Rankin and N. A. Rose, of the Tennessee Valley Authority Geology Division, for field assistance.

Jan 1, 1936

By Elmer A. Jones

Development work in mines of St. Joseph Lead Co., Southeast Missouri, using trackless loading equipment shows definite advantages: Speed of cleaning, ability to work on steep grades and sharp crosscuts, good later tracking conditions, and possibility of wasting rock in old abandoned stopes. THE Desloge mine is one of a group of mines owned by the St. Joseph Lead Co., in the so-called Lead Belt of Southeast Missouri. It has been operating approximately 40 years producing a daily tonnage ranging from 1600 to 3800, depending on various factors. On an average, the present mine is 300 ft deep with an extreme extent of 2.7 miles by 1.7 miles. Most of the present mining is in the lower horizons of the Bonne Terre dolomite, a fairly soft rock requiring no support except occasional channel iron and roof pins. Due to the contour of the underlying sandstone and porphyry, some development work has been through short stretches of these different formations. In some areas the lower part of the dolomite is quite sandy and generally is considered abrasive. Sizes and Methods of Drifting Have Changed: Development work has, like other phases of mining, changed considerably in the last 20 years, from cleaning by hand to the use of a mechanical method. The conception of a standard drift has also changed. Before the advent of mechanical loading in stopes there were many pieces of main line drift averaging 7 ft high x 9 ft wide. With the coming of the St. Joe shovel the drift was increased to 8 ft high x 10 ft ELMER A. JONES, Member AIME, is Assistant General Mine Superintendent, St. Joseph Lead Co., Bonne Terre, Mo. AIME Columbus Meeting, September 1949. TP 2859 A. Discussion (2 copies) may be sent to Transactions AIME before July 31, 1950. Manuscript received Sept. 16, 1949. wide. Now with the Joy loader and shuttle car, a 9x11 ft drift is coming to be standard size. Methods of cutting drifts have changed considerably over the last few years. Some changes in drilling equipment have been made such as reducing the weight of column, clamp, air feed, and fittings to go with the HC10 Cleveland jackhamer. Other changes have been made in drill steel such as the use of detachable bits; throw-away variety, screw type, and the tungsten-carbide insert bits. Later developments have introduced spiral-welded pipe with victaulic couplings, millisecond exploders, bulky powder, and the use of electric cap lamps. Experimental work is going on continually in various phases of development work, some to be tried and discarded, others gradually to become standard practice. To sum up, the standard method of development now in use at Desloge is as follows: The work is done on a two-shift cycle 7:00 p.m. to 3:00 a.m. and 7:00 a.m. to 3:00 p.m. Two men known as development drillers comprise a crew on each shift. These two men arrive at their work about 7:30 to find a round blasted by the previous shift. After scaling down back and walls they proceed to the cleaning operation, using either a Joy loader and shuttle car, a drag hoist mounted on a slide ramp, or an Eimco Finlay to load into a 21/2 ton mine car. Cleaning may take from 2 to 4 hr depending on conditions such as length of round broken, length of haul, and other variables. After fitting up pipe and setting up columns and drills they are ready to drill a round which should measure 9 ft high x 11 ft wide and break from 5 to 7 ft advance. This may also take from 2 to 3 hr. Then they are ready to charge and

Jan 1, 1951

By Elmer A. Jones

Development work in mines of St. Joseph Lead Co., Southeast Missouri, using trackless loading equipment shows definite advantages: Speed of cleaning, ability to work on steep grades and sharp crosscuts, good later tracking conditions, and possibility of wasting rock in old abandoned stopes. THE Desloge mine is one of a group of mines owned by the St. Joseph Lead Co., in the so-called Lead Belt of Southeast Missouri. It has been operating approximately 40 years producing a daily tonnage ranging from 1600 to 3800, depending on various factors. On an average, the present mine is 300 ft deep with an extreme extent of 2.7 miles by 1.7 miles. Most of the present mining is in the lower horizons of the Bonne Terre dolomite, a fairly soft rock requiring no support except occasional channel iron and roof pins. Due to the contour of the underlying sandstone and porphyry, some development work has been through short stretches of these different formations. In some areas the lower part of the dolomite is quite sandy and generally is considered abrasive. Sizes and Methods of Drifting Have Changed: Development work has, like other phases of mining, changed considerably in the last 20 years, from cleaning by hand to the use of a mechanical method. The conception of a standard drift has also changed. Before the advent of mechanical loading in stopes there were many pieces of main line drift averaging 7 ft high x 9 ft wide. With the coming of the St. Joe shovel the drift was increased to 8 ft high x 10 ft ELMER A. JONES, Member AIME, is Assistant General Mine Superintendent, St. Joseph Lead Co., Bonne Terre, Mo. AIME Columbus Meeting, September 1949. TP 2859 A. Discussion (2 copies) may be sent to Transactions AIME before July 31, 1950. Manuscript received Sept. 16, 1949. wide. Now with the Joy loader and shuttle car, a 9x11 ft drift is coming to be standard size. Methods of cutting drifts have changed considerably over the last few years. Some changes in drilling equipment have been made such as reducing the weight of column, clamp, air feed, and fittings to go with the HC10 Cleveland jackhamer. Other changes have been made in drill steel such as the use of detachable bits; throw-away variety, screw type, and the tungsten-carbide insert bits. Later developments have introduced spiral-welded pipe with victaulic couplings, millisecond exploders, bulky powder, and the use of electric cap lamps. Experimental work is going on continually in various phases of development work, some to be tried and discarded, others gradually to become standard practice. To sum up, the standard method of development now in use at Desloge is as follows: The work is done on a two-shift cycle 7:00 p.m. to 3:00 a.m. and 7:00 a.m. to 3:00 p.m. Two men known as development drillers comprise a crew on each shift. These two men arrive at their work about 7:30 to find a round blasted by the previous shift. After scaling down back and walls they proceed to the cleaning operation, using either a Joy loader and shuttle car, a drag hoist mounted on a slide ramp, or an Eimco Finlay to load into a 21/2 ton mine car. Cleaning may take from 2 to 4 hr depending on conditions such as length of round broken, length of haul, and other variables. After fitting up pipe and setting up columns and drills they are ready to drill a round which should measure 9 ft high x 11 ft wide and break from 5 to 7 ft advance. This may also take from 2 to 3 hr. Then they are ready to charge and

Jan 1, 1951

By D. K. Crampton

INTERNAL stress and season cracking in brass have been studied for many years and the technical literature contains many data on various phases of the subject. A résumé of the literature shows certain fairly well established points upon which various authors are mostly agreed: 1. Season cracking is primarily caused by the presence of relatively high internal stresses, or possibly in some cases by external stresses, or both. 2. A specific corrosion is also essential to season cracking: Certain agents, particularly mercurous salts, mercuric salts and ammonia salts; have such a specific corrosive effect. 3. The tendency to season crack under given conditions increases with increasing zinc content, brass containing less than 20 per cent zinc being relatively immune. 4. In alpha brass the season cracks are intercrystalline; in alphabeta brass they lie between the two constituents; and in beta brass they are transcrystalline. 5. The ordinary impurities or added elements in special brasses have little or no effect on the tendency to season crack. 6. Internal stresses can be eliminated, or at least reduced to a safe 'limit by annealing treatments at temperatures that do not produce visible microstructural changes or appreciable softening of the worked brasses. There are, however, some points in connection with the phenomenon of season cracking which have not been thoroughly investigated, or wherein different authors and investigators are not entirely in agreement. The investigations described in this paper were undertaken to determine: 1. The correlation between mercurous nitrate tests and actual season cracking on long-time atmospheric exposure. 2. The quantitative effect of type and degree of drawing operations on the intensity of internal stress and on the tendency to season crack in brass tubes. 3. The possibility of drawing high-brass tubes in such a manner as to prevent the occurrence of harmful stresses rather than to find a remedy for such stresses once having obtained them.

Jan 1, 1930

By Gifford E. White

Explanations of the basic procedure for making earth-conductivity studies by the Eltran method have already appeared in several placeS. 1,2,3 In its essentials, this method consists of applying step functions of voltage to one pair of earth grounds and measuring the transient potential resulting at a separate pair of ground points. As previously pointed out,' the transient potential resulting from a suddenly applied steady voltage is the indicia1 transfer function of Carson1 6 which has been extensively studied in network theory. The discussion here, with one special exception, will ignore the problem of how the physical configuration of the earth affects the transient response voltage; it appears that this phase of the problem has been solved in only a few special cases having any direct bearing on the prospecting problem. Entirely distinct from the potential-theory aspect of the conductivity problem is the interesting material that can be had from studying the well-known network relations between cause and effect in linear circuits, and thus deducing criteria for the application of the several experimental methods available. To do this, only one assumption need be made about the nature of the earth. The earth is to be considered a linear conductor within the tolerance of ordinary measurements. The discussion will be restricted to collinear electrode configuration like that of Fig. I, since this is the only type of spread practical for use with driving currents that vary with time. Here one pair of grounds carries the driving current, and in line with these and external to them is a RECORDING Fair of potential probes. The problem will be to consider the relation between the different voltages appearing between the potential circuit terminals when various types of driving voltage sources are inserted in the current circuit. Suppose that the grounding points G, and G2 make good contact with the earth, and that a battery of sufficient voltage to produce one ampere of direct current is introduced into the current circuit by the closing of a switch. The potential transient response to such a voltage can be measured by taking an oscillogram at the potential Directors terminals, giving the time function that has been called A(l).4 This time function has been solved for analytically in the case of a homogeneous earth,"' and the

Jan 1, 1946

By Gifford E. White

Explanations of the basic procedure for making earth-conductivity studies by the Eltran method have already appeared in several placeS. 1,2,3 In its essentials, this method consists of applying step functions of voltage to one pair of earth grounds and measuring the transient potential resulting at a separate pair of ground points. As previously pointed out,' the transient potential resulting from a suddenly applied steady voltage is the indicia1 transfer function of Carson1 6 which has been extensively studied in network theory. The discussion here, with one special exception, will ignore the problem of how the physical configuration of the earth affects the transient response voltage; it appears that this phase of the problem has been solved in only a few special cases having any direct bearing on the prospecting problem. Entirely distinct from the potential-theory aspect of the conductivity problem is the interesting material that can be had from studying the well-known network relations between cause and effect in linear circuits, and thus deducing criteria for the application of the several experimental methods available. To do this, only one assumption need be made about the nature of the earth. The earth is to be considered a linear conductor within the tolerance of ordinary measurements. The discussion will be restricted to collinear electrode configuration like that of Fig. I, since this is the only type of spread practical for use with driving currents that vary with time. Here one pair of grounds carries the driving current, and in line with these and external to them is a RECORDING Fair of potential probes. The problem will be to consider the relation between the different voltages appearing between the potential circuit terminals when various types of driving voltage sources are inserted in the current circuit. Suppose that the grounding points G, and G2 make good contact with the earth, and that a battery of sufficient voltage to produce one ampere of direct current is introduced into the current circuit by the closing of a switch. The potential transient response to such a voltage can be measured by taking an oscillogram at the potential Directors terminals, giving the time function that has been called A(l).4 This time function has been solved for analytically in the case of a homogeneous earth,"' and the

Jan 1, 1946

By O.W. Ellis

Recently there has been a considerable revival of interest in the effects of the various elements commonly added to brass for the purpose of increasing its strength. For many years the work of Guillet2 alone gave reliable information in this regard. Even today his determinations of the coefficients of equivalence of the various elements relative to zinc in brass are those universally employed in industry. This is so because these coefficients have stood the test of time—their substantial correctness has been proved in almost universal practice. It is not our intention to discuss here these coefficients or their use. Rather do we wish to emphasize the need for further systernatic studies of the mechanical properties of the ternary systems of copper, zinc, and other individual elements. Since Guillet published the results of his first investigations Millington, 16 Smalley33 and Thiband 45 have added somewhat to our information. In general they have confirmed the findings of Guillet, which may be stated in the following rather general terms: 1. The addition of aluminum to the 70:30 and 60:40 brasses progressively increases their hardness and strength and reduces their ductility and resistance to shock. 2. The addition of small amounts of iron to a 60:40 brass improves its strength without affecting its ductility. 3. The addition of small amounts of manganese to a 60:40 brass causes a progressive increase in its strength and reduction in its ductility. A considerable amount of information has been amassed in regard to the effect of nickel on brass (9, 22, 41) which it is unnecessary to refer to here, in view of the scope of this paper. The situation in regard to these alloys in 1926 was very clearly stated by an anonymous writer,47 in The Metallurgist of February of that year, whose remarks were so to the point that they are well worth quoting: It will he seen that there are still large fields remaining to be studied in each of these systems (those of the aluminum, iron, nickel and manganese brasses) before our knowledge is adequate. When we come to the more complicated systems the position is even less satisfactory, and on account of the very incomplete nature of the work which has been

Jan 1, 1929

By O. W. Ellis

Recently there has been a considerable revival of interest in the effects of the various elements commonly added to brass for the purpose of increasing its strength. For many years the work of Guillet2 alone gave reliable information in this regard. Even today his determinations of the coefficients of equivalence of the various elements relative to zinc in brass are those universally employed in industry. This is so because these coefficients have stood the test of time—their substantial correctness has been proved in almost universal practice. It is not our intention to discuss here these coefficients or their use. Rather do we wish to emphasize the need for further systernatic studies of the mechanical properties of the ternary systems of copper, zinc, and other individual elements. Since Guillet published the results of his first investigations Millington, 16 Smalley33 and Thiband 45 have added somewhat to our information. In general they have confirmed the findings of Guillet, which may be stated in the following rather general terms: 1. The addition of aluminum to the 70:30 and 60:40 brasses progressively increases their hardness and strength and reduces their ductility and resistance to shock. 2. The addition of small amounts of iron to a 60:40 brass improves its strength without affecting its ductility. 3. The addition of small amounts of manganese to a 60:40 brass causes a progressive increase in its strength and reduction in its ductility. A considerable amount of information has been amassed in regard to the effect of nickel on brass (9, 22, 41) which it is unnecessary to refer to here, in view of the scope of this paper. The situation in regard to these alloys in 1926 was very clearly stated by an anonymous writer,47 in The Metallurgist of February of that year, whose remarks were so to the point that they are well worth quoting: It will he seen that there are still large fields remaining to be studied in each of these systems (those of the aluminum, iron, nickel and manganese brasses) before our knowledge is adequate. When we come to the more complicated systems the position is even less satisfactory, and on account of the very incomplete nature of the work which has been

Jan 1, 1929