By C. McDermid

At the request of Mr. C. McDermid, Secretary of the Institution of Mining and Metallurgy, Salisbury House, London, E. C., England, the following reports of standardization committees are here republished. Mr. McDermid invites members of-the American Institute of Mining Engineers to write him and express their opinion of the various proposals made by the committees. COPY OF THE REPORT OF THE WEIGHTS AND MEASURES STANDARDIZATION COMMITTEE OF THE INSTITUTION OF MINING AND METALLURGY, as adopted by the Central Standardization Committee; Dec. 20, 1906, and submitted to the Council, Jan. 16, 1907.

Mar 1, 1907

By H. K. Birnbaum

The termination of a twin lamella in the interior of a crystal requires accommodation of the strains at the tip of the twin which result from coherency of the twin and matrix. In zinc and magnesium crystals,

Jan 1, 1960

By M. C. Manderson

The sharp drop in world phosphate demand that took place in 1975 due to temporarily high prices, now seems to be reversing itself. And prices for both phosphate rock and phosphate fertilizers, which declined dramatically from their 1975 highs, now appear to be bottoming out. This recent price weakness has delayed new mining ventures that had been planned for completion by around 1980. While there is ample capacity to supply near-term rock needs, the stage seems to be emerging for a better supply-demand and price environment in the late 1970's and early 1980's.

Jan 1, 1979

By R. W. Smith, G. W. Delamore, J. A. Spittle

RECENT work by the authors1 has demonstrated that the crystals constituting the equiaxed zone in small ingots originate, on quenching, in the chilled liquid. Whether any partial remelting2 takes place of the den-drites nucleated in the chilled region was not examined. However, the claim3 that this normally occurs, leading to crystal multiplication, has been disputed.4 Thus, for an equiaxed zone to form in the central region of an otherwise columnar ingot, it is necessary to transport crystallites from the chill zone to this region. In view of the work of Uhlmann et al.,5 it was considered desirable to examine the transport process further. Experimental Technique and Results. In the earlier experiments by the authors.1 a stainless-steel crucible 17/8 in. diam, 41/2 in. high, ad containing an alloy of A1-4 wt pct Cu, was quenched from 660°C into a bath of Wood's metal maintained at 100°C. Under these conditions a central zone of equiaxed crystals was obtained. However, if a 2250-G unidirectional magnetic field was applied for 2 sec immediately following the instant of quenching, or subsequently, the equiaxed zone did not appear. Careful thermal analysis showed that the short application of the field had virtually no effect on the thermal conditions of the melt. It thus appeared that the crystallites which were ultimately to grow large enough to form the equiaxed zone existed in the liquid immediately ahead of the interface, occlusion being prevented by the convective fluid flow induced by freezing from the walls of the cylinder. When this relative movement was prevented by the Lorenz forces induced by the application of the magnetic field, the crystallites were caught up in the rapidly advancing dendrite solid-liquid interface. To test this assumption, a small ingot of super-purity aluminum was partially melted and poured into a heated stainless-steel mold which was then immediately quenched into molten Wood's alloy. The resulting structure is shown in Fig. 1, and consists of columnar grains with a central fine-grained zone. Thus the unmelted solid present at the beginning of solidification had been transported ahead of the columnar interface. Discussion. There appears to be little or no information available on the interaction of suspended particles with a metallic solid/liquid interface. However, some information is available for transparent organic sys-

Jan 1, 1969

By Young C. Kim, Francis Martino, Ish Chopra

For the past two and one-half years, various emission control strategies were jointly developed by the University of Arizona and the Homer City Owners to com- ply with the clean air requirements at its Homer City Power Plant. Some of the available options for the SO2 emission control by the Homer City Owners were:l)cleaning of run-of-mine coal,2) scheduling of mining operations at its captive mines, 3) blending the captive mine coal with externally purchased low sulfur coa1,and 4) placing a partial FGD system. This paper describes two specific emission control strategies developed and implemented. These are: 1) production scheduling at the mining face to minimize sulfur variability, and 2) external purchasing of low sulfur coal for further blending. The main objective of this paper is to share our experiences on implementing the developed strategies. This paper emphasizesthe need for proper mine planning on a short-term basis, if the power plant is to meet the desired objective.

Jan 1, 1983

By Lucius W. Mayer

WHILE the mind of the financier does not normally run along channels similar to those of his technical adviser, engineers, because of their exactness, are ever more called upon to manage affairs where financial matters are involved. It is, true, not a relatively large number have thus far functioned in this capacity. It is also true that the essentially financial mind could not serve in a responsible engineering position; for to be a successful engineer one requires precise thinking, making due allowance for factors of safety. To be a financier seems to require less aptitude for exact thinking than of enthusiasm and confidence in capitalizing prospective possibilities. Both require imagination, the engineer being, more conscious of the limitations of natural conditions. It is to be regretted that the engineer' stands so far aloof from financial matters. Many consider them- selves successful, as did Steinmetz, as long as their reward is the consciousness that they are giving supreme service to mankind. They are 'generally happy in their work and, like our honored brothers who are teachers, gain their greatest satisfaction, not in the amount of their remuneration so much as in the service rendered society and in the excellence of results achieved. Indeed, these sentiments bespeak character and command respect.

Jan 1, 1924

By AIME AIME

IN many countries the lack of liquid petroleum supplies has centered interest upon the hydrogenation of coal and coal tars for the preparation of motor fuel. In the United States, hydrogenation has been of greater interest for grading up low-value petroleum fractions to the more valuable volatile fuels and for the preparation of a variety of premium products, including aviation gasolines, solvents, Diesel fuels, and lubricating oils. Chemically, the basic reason for this process is that, as shown in Table 1, the ratio of hydrogen to carbon (H/C ratio) in available raw materials is quite different from that characterizing the products sought.

Jan 1, 1936

By J. J. Van Nouhuys

THE economics of aerial survey and the technical processes by the aid of which vertical and oblique aerial photographs are turned into line maps showing the most profuse topographical detail such as contours, rivers, roads, plantations, habitations and cultivated lands do not concern us here. They have been ably and exhaustively described in the publications of the British War Office, handbooks on surveying methods and on photogrammetry and in the South African mining, engineering and geological press. Suffice it to mention that for geological interpretation vertical photographs are used on such scales as 1/5000 to 1/10,000, overlapping each other by 55 to 60 per cent in the direction of flight and some 10 to 20 per cent sideways on to the next sequence or strip. Through this duplication in the overlap the stereoscopic examination becomes possible. The standards by which monochrome aerial photographs are interpreted can be grouped under the following headings: 1. Continuity.-The continuity of topographic relief not obtainable on the ground owing to the smallness of man relative to that relief. Here lies the greatest value of aerial survey with relation to geology. An immediate alignment can often be made of drainages running in different directions on each side of a hill; saddles and gorges in the mountainsides; abrupt termination of outcrop or indubitable signs of faulting. Most conclusive evidence is thus often obtained about faults which may be perfectly visible at one place on the ground but cannot elsewhere be identified because of decreased throw. Similarly, dikes can often be followed notwithstanding frequent interruption and disappearance under the soil. Scattered outcrop in scrub-covered or bush-covered country can be compared with field work. The same applies to geological contacts. Once these have been 3stablished at a few points on the ground, the intervening stretches can be drawn in.

Jan 1, 1937

By R. C. Gifkins, K. U. Snowden

The value of the index n in power ktivs for the stress sensitivity of minimum creep rale at lead is derived front results drawn from lite literature and from previously unpublished nork on commercial (99.99 pel) and high-purity (99.999 pel) lead polycryslalline and hi crystal specimens. In tests al 0.5Tm (22 to 50'C) for slvesses below 250 psi, n fulls to mily for poly-cr,yslullirle specimens, single crystals, and bicrystals, and toy grain boundary sliding in bicrystals. Between 250 and 500 psi there is a tyansilion range and, for the polycrystalline specimens al least, u high-stress regime for 500 to 1500 psi where n is 5 or 6. These results are such that none of the suggested stress taws can he used to extrapolate to very loir stresses. Meclianisms for deformation in Ike grains and toy grain boundary sliding in the low-strcss regime are outlined. In particular, the mechanism for grain boundary sliding involves sliding controlled by diffusion from tensile to compressire Ledges. predictions based on this model give promising numerical agree-nicul with experiment. II is suggested that the mechanism for grain boundary sliding may he important in other circumstances, e.g., in creep of ceramic materials or superplaslicity, because it can operate with lille or no dislocation aclirity. WhEN the stress dependence of secondary creep rate is represented by a power law the values taken by the stress exponent n are found to vary between 1 and 7, see, c.g., Garofalo.' In Eq. 1 11 u is the applied stress and A a constant. The case for accepting values of v = 1 rests principally upon tests at high temperatures (>0.9Tm) and there have only been isolated tests at lower temperatures (rather than plots of creep rate against stress) for which the creep rates are such that some form of Nabarro-Herring creep with n = 1 is applicable. Hanson5 and Greenwood and cole6 plotted creep rate against stress for tests made in the vicinity of 0.5Tw, and found a "creep yield", so that below a certain low stress the creep rate was linearly related to stress: these observations appear to have been subsequently ignored. Various models have been proposed which agree with a large body of experimental results in which n equals -5 at high stresses (e.g., weertman7 and McLean8). Various alternatives to Eq. [1] have been proposed principally as a means of unifying creep data, but sometimes, it seems, in order to obviate the necessity for assuming a series of regimes of deformation associated with the various values of n; further refer- ence to these will be made in the section on stress laws. This paper calls attention to extensive results which show n = 1 for the creep of lead at room temperature (0.5 T,). RESULTS Fig. 1 is a composite diagram based on figures in the literature6,9,10 with additional results obtained by the present authors and their colleagues11,12 in the course of a number of investigations not directly concerned with stress sensitivity. In Fig. 1 In creep rate is plotted against In stress. The curves show results for two kinds of material. Lead I is of commercial purity (99.99 pct Pb) and lead IT a specially refined material, hydrogen-purified to remove oxygen; it contains 99.999 pct Pb. Curve A is for lead I in polycrystalline form (grain diameter 0.02 to 0.05 cm) at room temperature (22' to 26°C). Curve B1 is for lead I, polycrystalline, tested at 50C. Curve B2 is for lead 11, polycrystalline (grain diameter 0.02 cm), tested at room temperature (22 O- Curves C to F relate to tests made of bicrystals of lead 11: all of the same nominal orientation ("Y" in Ref. 12). Curves C and V are for creep within the component crystals of the bi crystals at 22°C (AB and CD in Fig. 2). Curve E is for creep measured in a gage straddling the boundary, approximately 0.15 mm either side (BC in Fig. 2). Curve F shows rates of grain boundary sliding (as distinct from strain rates in the other curves), obtained by averaging the offsets of six marker lines on the bi-crystal boundaries. The principal feature of the results is that the stress sensitivity falls into two distinct regimes, according to whether the stress is below approximately 250 or above 500 psi (there is a transitional range between 250 and 500 psi). The new result is that below -250 psi two of the curves (A and BI) give a value of n 1, and the other curves also drop below n - 2 to -1.5 but do not extend to low enough stresses to show clear evidence of n 1. At very high stresses the curves tend to give values of n - 6, as previously determined in other investigations. Curve R2 for the high-purity lead in polycrystalline form at room tenlperature almost merges with B, and thus gives new significance to the values for stresses of 150 and 200 psi; previously'3 these points had seemed to fall away from the curve of slope -3, but they now can be seen as almost completing a transition to n = 1. It should be noted that there was originally considerable apparent scatter in the results for the high-purity lead. However, this was found to be associated with annealing conditions or variations in residual content of oxygen and curve B2 was constructed using the highest rate (i .e., the rate for the purest lead) determined for each stress during the course of various investigations over the years: altogether, some forty tests were used in constructing curve R2.

Jan 1, 1968

By F. R. Brotzen, D. L. Davidson

ALTHOUGH much effort has been devoted to the problem, the nature of plastic flow in bcc metals is still not fully understood. Some of the difficulties encountered stem from the scarcity of information on orientation effects and the uncertainty as to the glide system in these metals. In an attempt to provide some of this information, the present investigation was carried out, using zone-refined molybdenum single crystals deformed in tension and in direct shear. Considerable evidence exists to indicate that the primary slip system for molybdenum is (110) <111>.1,2 Figs. 1 and 2 indicate that this is, indeed, the case for direct shear at room temperature (see Ref. 3 for a description of the shear-testing equipment and procedure). Moreover, from Fig. 2, the shear stress on the (123) is lower than that on the (112). This would be the case if, as has been suggested,4,5 slip on these two planes is in reality com-

Jan 1, 1965

By L. W. McKeehan

IT is no longer necessary, if it ever was, for your annual lecturer to apologize for including in his remarks frequent references to the arrange-ment of metal atoms in crystals and for basing his arguments that metals behave as they do upon their crystal structure. Neither will any objec-tion be raised because the large metallic crystals of which we will speak are hard to prepare and of negligible commercial interest. The particular set of physical properties we propose to discuss-ferromagnetic proper-ties-may require more justification. Very few in this audience are primarily, or even remotely, interested in the ferromagnetic behavior of the metals they handle. By no means all of you ever deal, by choice or by necessity, with metals which display any ferromagnetism at all, and even those who study or control ferrous metallurgy must usually depend upon electrical engineers for assistance in ferromagnetic applications. My excuse for talking about such an obvious specialty is, like all Gaul, divided into three parts. In the first place, the members of the com-mittee who select the annual lecturer must wish the speaker to confine himself to matters he has at least thought about before he prepares his speech. In the second place, the study of ferromagnetism in crystals has, as you will soon realize, suffered in the not-too-distant past from inade-quate metallurgy. Further progress probably depends upon proper use being made of the skill and knowledge of some members of the Institute of Metals Division who have not, before today, been asked to think about the problems presented here. Finally, there is at least a sporting chance that the ferromagnetic properties of a few metal crystals will give some insight into the more generally interesting properties which they share with nonferromagnetic metal crystals.

Jan 1, 1934

By Floyd Kelley

THE literature of the last decade is rich with information relating to the cause and means of control of grain growth in pure metals, but is deficient concerning the role diffusion plays in grain growth, although during this period many new products that depend on diffusion for their properties and success have been developed. Among these are cementation products, produced by calorizing, chromizing, and carbonizing, or by mixing, pressing, and sintering powdered metals such as Syke&apos;s iron-molybdenum die material, Genelite, and Elcon Metal (copper, tungsten) etc. This is a fertile field for new developments, but before it can be util-ized to the fullest extent there must be a thorough investigation of the processes by which diffusion and grain growth take place. Grain growth plays no small part in the process and certainly the physical properties of these products depend largely on the grain size and state of equilibrium produced. The field of investigation does not end here, but may be extended to the effect of diffusion on impurities, segregations and dendrites in the broad field of ferrous and non-ferrous metallurgy. A number of years ago the author investigated several of these cases and noted, with striking regularity, the pronounced effect of diffusion in promoting recrystallization and grain growth. An example of this phenomenon is given in his paper on chromizing1 which contained photomicrographs of large radial or columnar crystals produced by diffusion of chromium in the solid state. Another manifestation of this effect was discussed by Austen,2 who showed the part hydrogen plays in the decarburization of steel and the effect of diffusion upon the grain structure.

Jan 1, 1928

By A. H. Larson, T. P. McNulty

RECENTLY, an investigation of the absorption of sulfur dioxide gas in molten binary copper alloys was conducted. A Sieverts-type apparatus, consisting of a mercury-filled gas dispensing buret and a mercury manometer, was used initially for determining the volume of gas absorbed as a function of pressure. The equilibration behavior of the alloys studied indicated that the mercury in the gas measuring system was absorbing sulfur dioxide. Owing to the widespread use of mercury as a displacement medium in absorption studies, an investigation was made to determine the nature and magnitude of the mercury - sulfur dioxide absorption effect. The gas measuring system was modified by substituting a Worden Quartz Products Type PDHV fused-quartz-spiral pressure gage for the mercury-filled dispenser and manometer. The dispensed gas volume at known temperature and atmospheric pressure was measured by evacuating a Pyrex vessel of known volume and by admitting sulfur dioxide into the vessel until the attached quartz pressure gage registered atmospheric pressure. Atmospheric pressure was measured concurrently with a separate mercury barometer. The volume of the empty sample chamber and its attendant apparatus was determined by measuring the equilibrium pressure accompanying the addition of a measured volume of sulfur dioxide into the initially evacuated system. The volume of the mercury sample was calculated from the density of mercury at the temperature of the study (25°C). Measured volumes of sulfur dioxide were then dispensed into the system and the equilibrium pressure accompanying each gas addition was determined. From the difference between the system volume and the mercury volume, the number of moles of gaseous sulfur dioxide remaining in the system at each pressure was calculated. The difference between the number of moles of gas dispensed into the system, denoted Enso2: and the number of moles of gas remaining in the system after absorption equilibrium had been attained, denoted nso2(g), was equal to the number of moles of absorbed gas, denoted nSO2. The number of moles of absorbed gas was then converted to absorbed volume, denoted VSo2, in cu cm at stp conditions of (PC and 760 mm Hg. Table I contains calculated values of Snso2, nSo2(g), and VSo2 for different sulfur dioxide pressures. In the original system, denoted Run I, volume limitations of the gas dispensing system prevented absorption studies at equilibrium pressures near atmospheric pressure, so a different gas dispensing system, denoted Run 11, was used for determining the last pressure reading in Table I. The data in Table I are expressed in terms of the absorption of sulfur dioxide in 49.68 cu cm of mercury. In Fig. 1, these data are expressed in terms of the absorption of sulfur dioxide in 100 cu cm of mercury. Since the absorption data plotted in Fig. 1 show a linear relationship, the volume of sulfur dioxide absorbed in mercury is a function of the first power of pressure. The absorption reaction is So2(gas) = SO2 (in Hg) The first-power pressure dependence, coupled with the fact that the sulfur dioxide could be removed from the mercury by applying vacuum, indicated reversible

Jan 1, 1967

By R. I. Jaffee, E. S. Bartlett, D. N. Williams

The oxidation resistance and fabricability of molybdenum powder-metallurgy alloys containing up to 20 wt pct nickel in the form of a fine dispersion were studied. The effects of dispersion distribution and of amount and type (pure nickel or nickel compounds) of additive were considered. A definite improvement in oxidation resistance was observed, but the amount of improvement fell far short of requirements for an oxidation-resistant alloy. Fabricability by hot-rolling was limited. INVESTIGATIONS at Ohio State university1 and Battelle Memorial institute2 have indicated that the attainment of a truly oxidation-resistant molybdenum-base alloy for high-temperature service, with the coincident retention of high-temperature strength and toughness, will be a difficult, if not impossible, feat. Among the most promising alloy systems studied was the molybdenum-nickel system shown in Fig. 1. Alloys in this system show good oxidation resistance at temperatures well above the normal melting point of molybdenum trioxide because of the regenerative formation of protective nickel-molyb-date (NiMoO4) on the surface of the alloy during exposure at high temperatures. Unfortunately, the required alloy content to obtain oxidation resistant molybdenum-nickel alloys far exceeds the limits of the narrow terminal solid-solution boundary, and closely approaches the peri-tectic composition involving the brittle intermetal-lic compound, MoNi. Because of the peritectic reaction, fusion alloys are characteristically brittle, since the MoNi phase, being the last to form, tends to occur as a continuous grain-boundary network around each molybdenum grain. An added problem with this system is that the protective nickel-molybdate layer formed at high temperatures is unstable, undergoing one or more allotropic modifications upon cooling. The volume changes associated with this modification during cooling are such as to cause violent expulsion of the protective molybdate coating from the surface of the piece. This is, of course, quite detrimental in material exposed to cyclic temperature during service. The research reported here resulted from an attempt to overcome the aforementioned problems associated with the molybdenum-nickel alloys primarily by controlling the amount, size, and location of the MoNi phase. By using powder-metallurgy techniques of alloy preparation and sintering the blended molybdenum-nickel powder mixtures at a temperature below the peritectic reaction temperature, molybdenum-nickel alloys with a randomly dispersed MoNi phase were produced. MATERIALS The molybdenum powder used in the preparation of alloys for this study was commercial hydrogen reduced, minus 325-mesh (Tyler) material. Master alloys, by which nickel was added, consisted of elemental carbonyl nickel powder (12 average particle size), an alloy of 50 wt pct Ni-50 wt pct Cr, and compounds of MoNi, Ni,Si, and Ni2B. The nickel-chromium powder was prepared by filing a vacuum-arc-melted ingot, separating impurities magnetically, and screening to minus 200-mesh. The MoNi powder was prepared by pulverizing a hydrogen-sintered powder-metallurgy compact to minus 325-mesh material. Further sizing of this powder for study of effects of dispersion distribution was accomplished by air classification of the minus 325-mesh powder. The Ni2Si and Ni2B powders were prepared by crushing vacuum-sintered powder-metallurgy compacts to minus 200-mesh material. EXPERIMENTAL PROCEDURE Specimen Preparation—The general procedure followed in the preparation of alloys for testing is described as follows: 1) Blending. Either hand-blending of the powders in a ceramic mortar and pestle for X 1/2 or mechanical blending was used. Hand-blending seemed preferable for optimum homogeneity. 2) Compacting. Most of the blended powders were pressed to green compacts at pressures of 15 tons per sq in. in a single-action die, although some were pressed at 80 tons per sq in. A 1 X 11/4 X 1/4-in. green compact was the standard size for oxidation test material, and 7 X 1/2 X 1/4-in. compacts were used for fabricability test specimens. 3) Sintering. All green compacts were sinteredat

Jan 1, 1959

By Larry Dale

An approach for predicting the development of mineral resources on public lands has been developed as an aid to resource agencies. It consists of new techniques for evaluating the economic potential of the resource, the uncertainty about mine cost estimates, and the uncertainty about the occurrance of mineral deposits. New mineral sup- plies from inferred and hypothetical resources can be predicted by using these techniques. A case study illustrates their application in predicting development of copper resources in western Montana.

Jan 1, 1982

By William Campbell

(Cleveland Meeting, October, 1912.) THE structure of iron and steel, though the object of so much study and research for the past 25 years, is by no means thoroughly understood. In the first place, we have three or more distinct iron-carbon thermal diagrams, each with its own supporters, and each representing a theory of the structure and constitution of cast-iron. In the second place, by reason of the fact that austenite, the solid solution of carbon in iron, decomposes in the solid state into ferrite, or pure iron, and cementite (Fe3C), and that quenching from above this transition-range, no matter how rapid, cannot entirely prevent the change and thus preserve the austenite by itself at ordinary temperatures, it happens that under the microscope we find, in addition to the ferrite, Fe3C, and austenite, which the thermal diagram of steel requires, it series of transition-products with distinctive structures, to which have ,been given the names martensite, troostite, sorbite, etc. Now these transition-products, in addition to the solid solution, austenite, have been the source of much controversy, at times very bitter. One side would insist that, say, troostite was an entity, which the other side would deny, pointing out that it must be a transition-mixture, with a particular structure. That austenite was a solid solution of carbon in iron has been denied by one school ; we have been told that Fe24C dissolved both Fe3C and Fe, and thus gave rise to a whole series of quenching-products-all this in spite of the fact that no matter how the thermal diagrams differ in regard to cast-iron, they all agree in regard to the solid solution, austenite, for Fe24C finds no place on the diagram. Thus it happens that while the authorities fight both in regard to the iron-carbon diagram and the structures met with in hard- * Associate Professor of Metallurgy, Columbia University in the City of New York.

Dec 1, 1912

By E. A. Gulbransen, K. F. Andrew

Thermodynamic information on the solubility of hydrogen in exothermic metals is limited. Thus, the overall solubility decreased as the temperature rose, which suggests the heat of solution of hydrogen in the metal is negative; yet the terminal solubility in the metal phase increased, which suggests an endothermic reaction. A thermodynamic analysis, therefore, was made of the several equilibria involved when hydrogen dissolved in the metal. Equations were derived expressing the solubility, terminal solubility, and decomposition pressures of hydrogen in terms of the heat, entropy, and free energy of solution of hydrogen in the given phase. The relations between the thermodynamic functions for the a-zirconium and 8-hydride phase were developed. The thermodynamic quantities were determined experimentally by the measurement of the decomposition pressures over a broad composition and temperature range. Two new methods of analyzing the experimental data were developed for determination of the terminal solubility. STUDIES&apos;, &apos; of the impact strength of zirconium at room temperature indicated that small quantities of hydrogen, of the order of 10 parts per million, embrittles the metal. Micrographic&apos; and X-ray diffraction&apos; studies showed this embrittlement to result from the precipitation of a second phase upon slow cooling. These studies suggested that the terminal solubility of hydrogen in the metal phase increased with increase of temperature. This behavior appeared to contradict the effect of temperature on exothermic hydrogen occluders such as zirconium. For these metals, the solubility of hydrogen should decrease with increase of temperature. Before these facts could be understood, a thorough analysis of the several equilibria was essential. It was the purpose of this paper to consider the several equilibria involved when hydrogen was reacted with zirconium from both the theoretical and experimental points of view. Since the overall solubility of hydrogen in the metal has been considered by a number of workers, it was proposed to study the composition range 0 to 6 atomic pct H in detail. Literature Schwartz and Mallett&apos; determined the terminal solubilities of hydrogen in the metallic phase from diffusion studies. They extrapolated concentration-penetration curves to the boundary between the solid solution phase and the hydride phase at the surface. Their results showed values of 2.6 atomic pct at 400°C and 5.2 atomic pct at 500°C. Extrapolations of the data to room temperature suggested very low values for the terminal solubilities. This study confirmed the hydrogen embrittlement results and indicated that the terminal solubilities increased as the temperature was raised. The solution of hydrogen in zirconium over the complete concentration range was studied by Hall, Martin, and Rees3 and by others. The results showed that hydrogen was absorbed up to a maximum composition of 66 atomic pct or ZrH This composition represented the t-hydride phase. The maximum amount of hydrogen absorbed increased with pressure and decreased with temperature. Due to this temperature behavior, zirconium was classed as an exothermic occluder." In 1930 Hägg studied the crystal structures of the Zr-H alloys over a broad composition range. Four hydride phases were found. However, the range of homogeneity of the several phases was not studied. Gulbransen and Andrew" recently studied the phase diagram of this system by X-ray diffraction methods and by a thermodynamic method based on decomposition pressure measurements. The results showed that only two hydride phases existed for low temperatures, the 6 and the .-phases of Hagg.&apos; Both phases had broad regions of homogeneity. The lower limit of the two-phase region of a and d-phases suggested a terminal solubility of 4 atomic pct at 500°C. This value was in agreement with the results of Schwartz and Mallett.&apos; To avoid hydrogen embrittlement at low temperatures, it was necessary to heat the metal in high vacuum at elevated temperatures. To choose the conditions of temperature and high vacuum, it was

Jan 1, 1956

By John J. Collins

Page Purpose and scope..................... 521 Core sampling......................... 521 Sludge sampling....................... 527 Combining core and sludge assays ...... 533 Deviation and surveying of drill holes. . . . 537 Conclusions........................... 544 Acknowledgments...................... 545 Bibliography.......................... 545 Purpose and Scope The purpose of this paper is to review a few of the problems involved in the interpretation of diamond-drill core and sludge samples, with the hope that it will stimulate discussion and bring forth some of the information on the subject that has been accumulated by various organizations. The release of these data would benefit the mining industry as a whole. Particularly valuable would be the details of drilling programs that have been tested by actual mining operations, as most of the available published material is unsupported by production records. The scope of this paper is limited to a few of the commonest problems of interpreting diamond-drill core and sludge samples and the deviation of holes. It does not include the description of routine operations performed by the drillers, nor the estimation of ore reserves. The methods of calculating reserves have been described,25,26,31,32,50,65 but more informa- tion is needed on the results shown by actual mining operations. Core Sampling The accuracy of diamond-drill-hole Sampling depends in large measure on the percentage of core recovery. As a general rule, the longer the run, the poorer is the recovery. Although the longer runs allow cheaper drilling costs, the determining factor should be the percentage of recovery desired. The problem is one of balancing accuracy against costs. Holes of larger diameter may show improved recovery, except as Joralemon* points out that there are some conditions in which small holes give better core recovery than large holes. This is particularly true, he says; in rocks like shattered quartzite, where larger core tends to break in angular fragments and grind up, while the diameter of smaller core is less than the distance between joint planes and grinding is not so serious. In a large measure the length of the sample run should depend on the type of deposit. Favorable drilling may allow uniform sample runs of 5 ft., 10 ft., or perhaps 20 ft. In veins or beds of relatively narrow widths and changing characteristics, however, the ore zone may be overrun and ground in a core barrel full of waste rock. Generally it is desirable to break the sample at a change in the rock or ore. Such a change; often indicated by a color change in the sludge water, should be a a for the driller to make a "dry" block and to pull out that run regardless of the length. Such a procedure permits the segregation of waste from ore samples so

Jan 1, 1946

By M. E. Wadsworth, T. L. MacKay

Sintered UO, samples were leached in sulfuric acid solutions of various concentrations. A pressurized system was used so that it was possible to investigate the kinetics of the reaction to 270°C with oxygen overpressures as high as 900 psi. The rate was observed to be a function of the concentration of hydrogen ions and directly proportional to the partial pressure of oxygen. Evidences are presented which indicate that a UO2 surface site reacts with a molecule of water to form a hydroxyl complex which in turn can dissociate with the characteristics of a weak acid. A rate determining step has been proposed which involves the reaction between an oxygen molecule and the hydroxyl complex on the surface of UO,. ThE 2 principal methods for uranium dissolution are carbonate and acid leaching. The sulfuric acid leach is the more popular and is used for the treatment of the majority of the ores of Africa, Canada, and the United States. Low recoveries in basic leach circuits led investigators at the University of British columbia1 to study leaching of uranium ores in pressurized vessels. Early in the study of dissolution of uranium it was found that only uranium in the hexava-lent state could be leached in acid or basic circuits. Therefore, the use of oxygen over-pressure in an autoclave offered an interesting approach to solving the low recovery problems of carbonate leaching. UO, was used in this study because it could be obtained in high purity and also because it is representative of the most refractory of the primary uranium minerals. A pressurized system was used to provide a means whereby important temperature and pressure parameters could be varied for the evaluation of the kinetic processes. The mechanism for the dissolution of UO2 should be similar for any of the uraninite type minerals. At the present all of the kinetic studies that have been conducted have been in carbonate media. Peters and Halpern2 carried out a kinetic study of the leaching of pitchblende. Their specimens were pitchblende ores selected on the basis of high grade and homogeneity. Pearson and wadsworth3 conducted a kinetic study of the dissolution of UO2 in carbonate solutions with results very similar to those obtained by Peters and Halpern. EXPERIMENTAL The UO2 as received* was found by spectroscopic *Mallinckrodt reagent, supplied by the Atomic Energy Commission. analysis to have a purity of 99.94 pct 0.03. It was ground in a mechanical agate mortar and screened through a 400-mesh sieve. Thin flat disks of UO2 were prepared by pressing the sized powder in a specially constructed die at a total pressure of approximately 25 tons per sq in. The pressed disks were approximately 0.25 cm thick, 1.6 cm diam, and 3.5 g in weight. As pressed, the samples were approximately 65 pct of theoretical density. It was essential that a binder such as poly-vinyl alcohol be added before pressing to prevent formation of cracks when fired. It was found by trial and error that pressed disks sintered close to 1870°C in a hydrogen atmosphere, reach densities between 91 and 91.5 pct of the theoretical density. At this density the samples had no measurable porosity based upon a 2-hr emersion in boiling water. An X-ray examination of these sintered UO2 disks showed them to be identical with the original UO2 received. Reaction of UO2 with the alundum furnace core was prevented by placing molybdenum between the samples and the core according to the method of Corwin and Eyerly.4 Leaching studies were carried out in a specially designed autoclave, the details of which have been presented e1sewhere.6 The main features of the equipment as applied to a kinetic study are: 1) solution samples may be removed during the course of a single run; and 2) temperature and agitation are carefully controlled. Two-ml samples removed from the autoclave during the course of a run were analyzed for U3O8 content with a Beckman model DK-2 spectrophotometer by the method of

Jan 1, 1959