By Dilip K. Das, Douglas T. Pitman

ONE of the major uses of barium in metallic form is as a getter material in vacuum tubes. Because of the high chemical reactivity of the metal, Ba-Al alloys are extensively used. Numerous methods for the preparation of Ba-Al alloys have been published, a few of which1-4 are cited here. Most of these methods were found to be quite elaborate, involving the reduction of BaO, and not too well adapted for the close control of the final composition of small amounts of alloys prepared for laboratory use. A simple laboratory method for the preparation of Ba-A1 alloys in small batches starting from pure metals was devised, so that it was possible to control the desired compositions to within 1 pct. The pertinent features of the alloy system Ba-Al5 are 1) an intermediate compound BaAl, with the melting point of 1050°C, and 2) a eutectic between aluminum and BaAl4 at 98 pct Al. The accompanying sketch shows the experimental arrangement for the preparation of the alloys. Weighed amounts of aluminum and barium were placed in an alumina and a stainless steel crucible, respectively. According to the supplier's specification, the purity of the metals used in the alloys is as follows: a) aluminum rods—99.9 pct Al, and b) barium rods—99.5 pct Ba. The stainless steel crucible, tapered at the bottom and having a 1/16 in. diam hole, rested on top of the alumina crucible. The assembly was placed inside a graphite sleeve which rested on a refractory platform. The platform moved the assembly up and down through the field of a radio frequency coil. A glass bell jar was placed between the crucible assembly and the radio frequency coil to maintain a steady flow of helium around the melt. A small window was cut out on the wall of the alumina crucible to observe the progress of the re- action and to record the temperature with an optical pyrometer. The platform was first raised high enough to move the barium out of the radio frequency coil field in order to allow only the aluminum to melt. The assembly was then lowered so that the barium began to melt and flow out through the small orifice into the molten aluminum. In order to keep the violence of the exothermic reaction under control, the rate of flow of barium was carefully regulated by raising or lowering the crucible assembly. All the samples prepared by this technique were examined by a Norelco X-ray diffractometer using CuKa radiation, The diffraction specimens were prepared by placing the finely powdered samples in flat specimen holders. The Ba-Al alloys prepared with a high barium content were found to consist mainly of BaAl4. The structure of BaAl4 has previously been reported by Alberti and Andress.8 They found that BaAl4 was body-centered-tetragonal with an a0 = b0 = 4.530Å and c0 = 11.14Å. An alloy whose composition was found by chemical analysis to be almost 100 pct BaA1, was used to determine the relative intensities. The d-spacings were obtained from the same alloy to which a small amount of tungsten had been added as a calibrating material. Accurate values for a, and c, were calculated according to the method proposed by Taylor and Floyd.' The calculated values are: a, = b, = 4.566Å and c0 = 11.250Å. The measured d-values for BaAl4 are shown in Table I along with relative peak intensities above background and hkl indices. Acknowledgment The authors are grateful to L. J. Cronin, the head of the Techniques Dept., for suggesting the problem and for his constant interest. References 1Froges and Camargue: German Patent No. 809107, 1951. French Patent No. 935324, 1949. 2E. Bonnier: Annales de physique, 1953, vol. 8, pp. 259-312. 3M. Orman and E. Zemhela: Prac Institute of Metals; 1952, vol. 4, pp. 437-445. 4E. Fujita and H. Yokomizo: Reports Gov. Chemical Industrial Research Institute, Tokyo, 1952, vol. 47, pp. 291-297. 5E. Alberti: Ztsch. fur Metallkunde, 1934, vol. 26, p. 6. 6E Alberti and K. R. Andress: Ztsch. fur Metallkunde, 1935, vol. 27, p. 126. 7 A. Tnslor and R. W. Floyd: Acta Crystallographica, 1950, vol. 3, p. 285.

Jan 1, 1958

By C. S. Barrett, A. Smigelskas

There have been no publications of the deformation and recrystallization orientations of the metal beryllium, yet pronounced textures would certainly be anticipated since it is close-packed hexagonal in structure. Having an axial ratio approximately that of magnesium, beryllium probably deforms by nearly the same slip and twinning mechanisms that operate in magnesium, and the textures are likely to be similar or but slightly different from the magnesium textures. In the tests reported below this is found to be the case; the textures are found to differ from those of magnesium only in the details of the scatter from the average orientation. This report covers not only samples rolled at room temperature, but some rolled at elevated temperatures. Since magnesium has been suspected by some investigators of altering its crystallo-graphic deformation mechanism at elevated temperatures, it was considered possible that beryllium might do so and alter its textures accordingly. No pronounced alterations were found, however. Unfortunately, the theory of deformation textures is not in a state of development that permits one to deduce the deformation mechanism from a knowledge of the textures, which means that the similarity of textures at different rolling temperatures, reported here, cannot be taken as definite evidence that the deformation mechanism is actually the same at all temperatures. The general similarity of the deformation textures of magnesium and beryllium also extend to the recrystallization textures of the two metals, judging by the pole figures for recrystallized sheet presented in this report. Samples were prepared in the form of composite sheets made up of small pieces stacked in a pile. Each piece was trimmed with scissors so that an edge was parallel to the rolling direction, dipped in paraffin, and assembled into the pack by aligning it under the cross hair of a microscope. As the desired orientation was obtained on each piece it was secured in place by touching with a hot wire to melt the paraffin. A stack of ten or fifteen pieces was built up in this way, then trimmed to the shape of a T; the portion to be X rayed was then etched to the shape of a wire about 0.045 in. diam with 6N HCl. This method of shaping the sample is a modification of that used by Bakarian on magnesium.' The absorption of the rays in the sample was so slight that it caused no difficulty in interpreting the films. Exposures were made with a 0.030 in. diam pinhole, using molybdenum radiation (40 kv, 25 ma, Type A film at 5 cm, 2 to 3 hr exposures). With the recrystallized specimens it was found necessary to oscillate the specimen so as to reduce the spottiness of the lines. A range of oscillation of 5" was SUB- cient to produce reasonably satisfactory patterns, though the quality was somewhat inferior to that of the deformation texture patterns, and only two degrees of intensity were read from the arcs on the films. Typical photo-grams for each of the deformation textures and the recrystallization texture are assembled in Fig 1. The pole figures were plotted in the usual way with the intensity of the various portions of the diffraction rings estimated by eye. Seven to nine films were made of each sample and each was carefully read in plotting the pole figures. Typical series included exposures with the beam normal to the rolling direction and at 11, 26, 41, 56 and 71" to the cross direction, plus two exposures with the beam normal to the cross direction, and at 11 and 79" respectively to the rolling direction. The rolling was in each case considered sufficient to develop the final texture: the reduction by cold rolling was 84 pct (from 0.0045 to 0.0007 in. thickness), following prior hot rolling in longitudinal and transverse directions and recrystallization; the reduction by hot rolling at 800°C was 90 pct (0.010 to 0.001 in.), following similar prior treatment; the reduction by rolling at 350°C was 88 pct (from 0.005 to 0.0006 in.) after similar prior treatment. The recrystallization texture was determined on a sample rolled at 350" to a reduction of 88 pct (0.0165 to 0.002 in.) after similar prior treatment, then mounted between steel strips to keep it flat and annealed at 700" in an atmosphere of argon. Discussion of Results The results of the X ray determinations are assembled in the pole figures of Fig 2, 3, 4 and 5 for rolling at

Jan 1, 1950

By J. D. Anthony

The Australian continent possesses significant reserves of a wide range of minerals, including bauxite, coal, copper, diamonds, gold, iron ore, lead, manganese, mineral sands, nickel, phosphate, silver, tin, uranium, and zinc. Australia's identified economic resources of many minerals are very large as indicated in Table 1. A sophisticated and highly experienced mineral industry is now an established feature of the Australian economy and Australia is the world's largest exporter of iron ore, alumina, mineral sands and refined lead and amongst the leading suppliers of many other commodities such as coal, lead and zinc ores/concentrates, nickel, refined zinc, tungsten concentrates and bauxite. The industry exports 70% of its production. This is reflected in the value of Australian mineral exports which have grown from about $200m in 1960/61, comprising 10% of total export receipts, to about $1265m or 29% of export income in 1970/71 to around $7061 representing 37% of Australia's total export income in 1980/81. Details of the more significant minerals are as follows: Japan (42.1%) USA (11.3%) ASEAN (6.3%) UK (5.9%) F.R. Germany (3.8%) Republic of Korea (3.4%) New Zealand (2.6%) Also see Table 2. AUSTRALIA'S MINERAL RESOURCES POLICIES Federal and State Governments' Responsibilities Australia has a federal system of government comprising six States, a self-governing Territory and a Federal Government. Under the Australian federal system the Constitution sets down the powers of the Federal Government. All powers not assigned to the Federal Government in the Australian Constitution reside automatically with the States. Certain of these broad powers result in the Federal Government having a significant influence on resources development. For example, in being responsible for economic management, the Federal Government's fiscal and monetary policies have an important effect on industry as well as on State finances. In particular, the taxation regime employed by the Federal Government is of direct importance to decision-makers in the resources industry. The Federal Government is responsible also under the Constitution for external trade matters; and international trade and commodity matters are increasingly important in Australia's international relationships. Foreign investment is another area where the Federal Government has a role to ensure that national interests are protected. This foreign investment power flows from the Federal Government's control of foreign exchange movements into and out of Australia. However, before enlarging on these and others of the Federal Government's powers and policies, it should be emphasized that the State governments, by virtue of their wide powers to regulate matters within their own boundaries, are more directly involved in the day-to-day administration and regulation of mining operations. For instance, the powers of the State governments include the responsibility-for the granting of exploration rights and mining leases, the approval of mining operations and the levying of royalties and other like charges. Administrative arrangements covering the granting of minerals and petroleum exploration and development titles vary from State to State. Before development rights are granted, State governments consider environment protection and rehabilitation aspects of development proposals. The provision of infrastructure within State borders is a matter primarily of State government responsibility. It is usual practice in Australia for State governments to construct and operate infrastructure services such. as railways, ports and electricity generation and transmission. The States may also provide certain public services such as electricity. and water, port and loading facilities, communications, health and education services which form part of the infrastructure of mining operations. In remote areas the mining companies themselves usually are expected to provide much of this infrastructure. However, the Federal Government is primarily responsible in some fields, such as telecommunications and parts of the railways network. State governments carry out preliminary exploration and geological mapping and some are directly involved in the mining of coal for power generation. The Federal Government's responsibilities in addition to economic management, taxation, international relations, foreign capital and investment, include regulation of exports, environmental matters and matters affecting the Aboriginals of the Northern Territory. FEDERAL GOVERNMENT POLICIES The continued sound development of the minerals and energy resources sector is regarded by the Federal Government as being of very great importance. However, the Government does not seek to participate directly in resource developments. It sees its role rather as that of establishing a sound economic and policy climate in which private companies can identify opportunities, seek out customers and marshall the necessary capital for the development of resource projects.

Jan 1, 1982

By T. Sterry Hunt

Jan 1, 1884

By J. L. Gregg

A STUDY of copper and silver base alloys was made with the object of finding, if possible, useful alloys subject to dispersion hardening. These studies led to the discovery of several alloys showing considerable dispersion hardening, the most important of which, the alloys of copper with iron, nickel, cobalt and chromium silicides, have since been very ably reported by M. G. Corson.1 This paper is offered as a few notes covering alloys other than those described by Corson and some further data on the silicide alloys.

Jan 1, 1929

By J. J. Thomas

THIS investigation was undertaken to determine, if possible, the relation between static and dynamic tensile tests as measured by the work required to break test specimens slowly, in a tensile testing machine, and rapidly, by means of a falling weight. It was hoped that the investigation would throw some light on the role played by ductility under different rates of application of load. FIG. 1.-STRESS-STRAIN DIAGRAM. In problems of design, it is usually assumed that the moduli of elasticity of all steels are equal; viz., about 30,000,000. The stress-strain diagram within the elastic limit is a straight line, as shown in Fig. 1, where OA is the curve of a hard steel and OB that of a soft steel. If the modulus of elasticity is constant, as assumed, the slope of the line OC

Jan 2, 1921

By Roland Kammel

For electrolytic recovery of silver from dilute aqueous solutions improved mass transfer is necessary to achieve favourable current efficiencies and high space-time yields. The many cell designs proposed for this application can be divided into two different groups: cells from which the silver must be redissolved and cells from which the deposit can be reclaimed as a metal. Introduction Electrolytic silver recovery methods have proven advantageous under technical and economic aspects for the treatment of rinse water, still rinses and spent silver solutions in the electroplating and surface finishing industry, of exhausted fixing baths from photographic processing, bleed electrolytes from silver refining processes and leach liquors. Examples of the compositions of typical dilute silver solutions are listed in Table I.

Jan 1, 1984

By Harry V. Welch

Early in the development of the art of metallurgy, it was noted that a distinct difference existed in the character, collection possibility and health hazard of the "smoke" from lead furnaces and those from copper plants. Zinc-plant fumes, although not so detrimental to health, were closely allied in nature to those of the lead works. In Cottrell plants, there are sufficiently distinct differences in operation and amount of construction between those for lead and copper to justify their consideration under separate headings; therefore, while the application of the process at copper-reduction works was covered by the writer some two years ago in the Transactions1,† this discussion will confine itself more distinctly to "fume" collection. General information on the process has been presented in numerous articles and by many authors: Cottre112, Schmidt3, Bradley4, Anderson6, Labbe6, Shiga7, Rathbun8. "Fume" may be defined as material, metal or nonmetal, elemental or compound, evolved as a vapor from a furnacing or chemical reaction and condensing, chilling or reacting within the gas stream to yield a solid form, and in this definition liquid particles are solids in a sense as distinguished from gases or vapors. Such condensed particles are of minute form, on the order of "smoke," and, for example, on the order of a few hundredths of 1 micron (1 micron = 1/25,000 in.) to perhaps 3 microns, with agglomerates, in relatively small proportions of many particles. Metallurgically typical fume products are lead compounds, oxides, carbonates and sulphates; elemental zinc, more commonly encountered as a fume particle of zinc metal with a surrounding "skin" of zinc oxide; arsenic, both metal and oxide and some of its more complex salts such as added sulphates as found in flue dusts; antimony, more particularly its oxide forms; and elemental sulphur, sometimes a troublesome product, in Dwight-Lloyd sintering-plant fumes. These products, particularly the elemental or lower oxide forms, have relatively appreciable vapor pressures at the existing operating temperatures as reported by Welch and Duschak9, Ingold10, Johnstonll, Millar12,13.

Jan 1, 1937

By Milton T. Pana

Computer techniques now have been applied to the solution of a wide variety of scientific and engineering problems in the mining industry, but generally not in great depth in any one area. In mining, the area covered in greatest depth and with the greatest success has probably been mine planning and to a lesser degree production scheduling. A rather comprehensive review of the literature related to mine planning and production scheduling indicates that contributions in these areas have been geographically, as well as organizationally, widespread. Of twenty-six papers reviewed, eleven were from industry, eight from educational institutions, four from computer vendors, two from the Bureau of Mines, and one from a private consultant. The conclusions that can be derived from the literature are: First, the-state-of-the art has advanced to the point that computing ore reserves and developing mining plans with the aid of the computer is now a routine practice; second, the application of the computer to mine planning problems has markedly improved our ability to estimate ore reserves, more accurately define pit limits, and determine an optimum mining sequence. MINE PLANNING The papers in this section deal essentially with the problem of determining the final pit limits of an orebody and the ore reserves associated with a given pit limit. The problem is probably best described by Soderberg25 and more recently by Reibell. 23. There are two techniques currently being applied to this problem by several mining companies: 1) the multiple-cone technique and 2) the Lerch-Grossman algorithm. The multiple-cone technique is the older of the two techniques and has the advantage of being more flexible, allowing an engineer to easily vary pit slopes in different sectors of the design. The technique can also be used to define intermediate pit contours. The Lerch-Grossman algorithm is appealing in that the final solution is given in the form of a true mathematical optimum. The technique is limited, however, in that the size of the blocks in the orebody model are a function of the desired

Jan 1, 1969

By W. H. Bassett, C. H. Davis

The late J. P. Sparrow, chief operating engineer of the New York Edison CO., carried out a series of practical tests on condenser tubes of several copper alloys and reported on the results to the Association of Edison Illuminating Companies at its meeting in September, 1913. In the preparation of these tubes the senior author had the pleasure of cooperating. Copper-zinc alloys in the proportions of 60-40,70-30,80-20, 90-10, and Admiralty metal, which is in effect 70-30 with 1 per cent. of tin, were tried. Monel metal and several copper-nickel alloys, and 8, 5, and 3 per cent. aluminum bronze were also tried. At the time of this report, the aluminum bronze had been in service for 4 1/2 years and seemed to be giving especially good results but later it began to fail and showed no substantial improvement over Admiralty metal. Monel metal was unsatisfactory and the nickel alloys apparently did not give better service than the Admiralty alloy. Previous to the publication of the report, and after considerable discussion, it was agreed that a test where tubes of different kinds could be under laboratory observation would be advisable, so the apparatus described here was set up in The American Brass Co.'s Waterbury Laboratory. This was fitted with tubes of copper, brass, bronze, nickel silver, cupro-nickel and other alloys, and the test started on Oct. 11, 1912. Salt water from East River, New York harbor, was barrelled and transported to the laboratory for the test. A fresh supply, completely replacing the water in service, was obtained at the end of each six months period. Plan of Procedure In general, the procedure was to inspect the tubes at short intervals and to remove those that had begun to leak. The tubes removed were carefully examined and a photographic and microscopic record of the

Jan 1, 1925

By William Mikulas

LITTLE work has been done in the field of the nickel-tin binary system. The complete diagram has been investigated on two occasions, but the results are in very poor agreement. The structure of a compound NiSn, and the solubility of tin in nickel have been determined by X-ray methods. Several investigations have been made of the liquidus curve, and the compositions of the eutectics have been determined. A study of the literature, however, shows that there is no satisfactory agreement between the data presented in the various papers. The present investigation was undertaken in an attempt to determine the equilibrium conditions, and to correlate X-ray with metallographic data. The equilibrium diagram was determined by thermal and metallo-graphic means, and the solubility of tin in nickel further investigated with X-rays. Powder diagrams were made of the intermetallic com-pounds, and three of the structures were partly determined. No attempt was made to determine the range of homogeneity of the inter-metallic compounds.

Jan 1, 1937

By E. L. Tucker

PREVIOUS investigations of E. L. Tucker and R. E. Head' related in particular to the effect of cyanogen compounds on galena, sphalerite, and pyrite, and their behavior in the presence of such com- pounds. The present contribution deals with the float- ability of the copper minerals and of pyrite. All experiments were performed on minus 200-mesh material, the method of preparation being the same as that described in the previous article. Flotation tests were made in a small mechanically agitated machine of 50-g. capacity designed in this laboratory by Gates and Jacobsen." General Naval Stores pine oil No. 5 and potassium xanthate were used in constant amount in all of the experiments; these agents were selected because of their present wide use in the flotation of copper minerals. Lime additions were varied to secure four 'final hydrogen ion concentrations, namely, neutral, 0.0005 per cent CaO, 0.003 per cent CaO, and 0.02 per cent CaO. The variation in lime addition was introduced to include the range of alkalinities employed in actual flotation practice.

Jan 1, 1926

By Paul F. Kerr

QUARTZ of a certain kind, is one of our strategic minerals, and Brazil is probably the one important available source. Crystals of quartz of suitable size and perfection for piezoelectrical application are rare; their most outstanding use is in radio work. Clear quartz, or "crystal," free from twinning, cracks, foreign particles of other disturbing lines of growth, and gaseous or liquid inclusions, is cut into plates which provide excellent control of frequency in broadcasting. The squares or rectangles are less than a millimeter in thickness and ordinarily on the order of 1 in. along each side. They are cut at definite angles with respect to the axes of the crystal, and ground with opposite surfaces parallel. Each small slab must be a section of one crystal, uniform throughout in atomic alignment. The thickness of the chip controls the frequency of a broadcast and it is most important to have the plates oriented and ground with utmost precision. Opposite surfaces are parallel to within 0.001 mm. and expansion or contraction due to the temperature is limited to one part in a million.

Jan 1, 1942

By H. N. Treaftis, J. W. Cahn

THE previous determinations of the solvus of tin in solid lead disagree with one another by as much as 40°C or almost 10 at. pct. Even determinations that appear to be careful differ considerably in both the solubility and its temperature coefficient. Recent kinetic workl -3 on the rate of precipitation of tin from lead-tin alloys and thermodynamic work4 on the heat of solution of tin in lead have given some insight into the time necessary to reach equilibrium in this system. As this time is longer than that used in almost all previous determinations of the solvus, these determinations are questionable. Since the interpretation of recent kinetic results requires accurate values of the equilibrium solubility the present work was undertaken. DISCUSSION OF PREVIOUS RESULTS The methods used in previous studies may be placed into three classes: 1) Several alloys covering a range of compositions are allowed to reach "equilibrium" at a certain temperature.5-7 Some property, such as the X-ray lattice parameter of the lead-rich phase or the re- sistivity of the alloy, is then measured as a function of composition. The solubility limit for that temperature is taken to be that composition at which a discontinuity in the property occurs. However, the recent kinetic work has shown that tin precipitates in two stages. The first stage is rapid but leaves the lead still supersaturated. The second stage is very slow, and it seems from the equilibration times quoted by the investigators of the solvus that the end of the first stage of precipitation was usually mistaken for equilibrium. This is especially true at temperatures below 100°C where the first reaction is still quite rapid (from minutes to months), but where the second stage is so slow that very long holding times are required to reach equilibrium. Alternatively micrographic work8 on several alloys of different compositions seems to have given good results if done carefully. 2) The beginning of precipitation in a homogenized alloy is measured as it cools slowly8-10. Since reactions in solids undercool easily, such determinations will always give too low a temperature for the solvus. 3) Some property of an alloy is measured as a function of temperature while the alloy is above the solvus.5,9,11 The range of temperature can usually be extended slightly into the two phase region. Then the alloy is precipitated at a much lower temperature and slowly reheated. The solvus is taken to be the lowest temperature where the property of the reheated alloy is equal to that previously determined for the homogeneous alloy. Usually one also expects a discontinuity at the solvus in the temperature variation of the property for the reheated alloy. The difficulty in this method is the sluggishness of the dissolution process, and this method may give too high a solvus temperature. EXPERIMENTAL The phase boundary or solvus temperature was determined by a modification of method 3 for a series of chemically analyzed high-purity alloys, ranging from 5.1 to 26.4 at. pct Sn. The resistance, as a function of temperature, of a sample of homogenized alloy (which could easily be undercooled) was compared with the equilibrium resistance which that alloy sample attained after precipitation at room temperature followed by long isothermal anneals at various temperatures. Before each anneal the sample was rehomogenized and reprecipitated. The solvus temperature could be located to within 1°C as the intersection of the resistance vs temperature curves for the homogenized and equilibrium alloys. No attempt was made to locate the phase boundary more accurately since the limiting factor was the precision with which the alloys could be analyzed. This precision was ±0.1 wt pct Sn and corresponds to an error of 1 deg in temperature. This use of isothermal anneals differs from some of the previous investigations in which method 3 was used with baths of slowly rising temperatures. It was found early in the investigation that solvus temperatures tended to be high if the latter method was used even at extremely slow heating rates. For example a

Jan 1, 1961

By John D. Price

R. W. Campbell (Jones and Laughlin Steel Carp., Pittsburgh)—As usual John Price has presented an excellent paper. I know of no one who has devoted more time and conscientious thought to this subject than he has, and his efforts have produced scientific data and conclusions of real value. Results of similar studies made by the Jones and Laughlin Steel Corp. on the blending of Pennsylvania coals may be of interest. During 1935 the late F. W. Wagner and the present writer developed an empirical physical fuel value formula for evaluating the combined physical tests of metallurgical coke, see Table IV. In the development of the formula, the tumbler test, shatter test, screen test, and porosity of coke have been taken into consideration. Each of these tests brings out some physical property not expressed by the others, and in estimation of the importance of these tests as a medium for evaluating coke for the blast furnace, their worth has been graded as follows: It was thought that some additional penalty should be applied to cokes that do not show a uniform screen size, assuming that coke larger than 4 in. was not desirable and that this size was an indication of irregular size. Therefore the screen test factor is further corrected by applying a penalty of 1 pct for each 1 pct material greater than 4-in. size as shown by the screen test. The physical fitness of coke for blast furnace use depends upon four fundamental characteristics: l—gen-era1 strength, as indicated by the shatter test; 2— abradability, or the resistance of cell walls to reduction in size by attrition, as indicated by the tumbler test; 3—porosity; and 4—size and uniformity. Each of these characteristics is not of equal importance, but surely, in an attempt to determine an accurate physical value, the individual value of each should be taken into consideration. The formula is used as a yardstick, so to speak, in determining variations in the normal production of metallurgical coke and in making comparisons between normal coke and experimental blends with other coals. Table IV gives results of coking tests on raw and washed high volatile coals and these same coals with blends of coke breeze, anthracite coal, char and low volatile coals, all from Pennsylvania. The table also gives the source of the coals and coke breeze, as well as their proximate analyses. It will be noted that the washing of the raw high volatile coal increased the physical fuel value from 26.17 to 39.16, showing the effect of removing shale and slate which produces a detrimental fracturing and weakening of the coke. It is a well known fact that many Pennsylvania high volatile coals contain an excess of resinous material or binder which has a tendency to weaken the coke, owing to its high evolution of gases during carbonization. Tests were therefore made with coke breeze, an inert material, in an attempt to alleviate this condition. Blends of washed coal with 5 pct and 7.5 pct coke breeze collected from the coke plant quenching sump (82.9 pct through 1/8-in. screen) resulted in cokes with a physical fuel value of 20.75 and 16.73 respectively, lower than results obtained from 100 pct raw high volatile coal. It will be noted that the percentage of + 4-in. coke increased but that the tumbler test was very low. Undoubtedly better results could have been obtained if the coke breeze could have been crushed extremely fine. During World War II the government asked the coking industry to consider the use of anthracite coal as a substitute for high quality low volatile coal, which was extremely scarce at the time. The next series of tests was made with blends of raw and washed high volatile coals and 5, 10, and 15 pct Pennsylvania No. 5 buckwheat anthracite (100 pct through l/8-in. screen). It was necessary to use some raw high volatile coal in these blends because of insufficient washer capacity at the time. It will be noted that the physical fuel values

Jan 1, 1954

By Walter C. Smith

THE Cerro de Pasco Copper Corp. began to produce bismuth at the Oroya smelter in 1929, at which time the only important consumption of that metal was in the manufacture, of pharmaceutical compounds, and the normal supply of metal exceeded the demand. With a new and major producer entering the field, additional uses for bismuth had to be developed. A survey indicated that the most promising opportunity lay in fusible alloys containing bismuth. A large number of bismuth alloys were known and a few of them were being used in the manufacture of automatic sprinkler heads and safety plugs. The literature cover in,- the- alloys was found to be sketchy and contradictory. Research, development, and educational work carrried on by the Corporation during the past fifteen years has resulted in greatly enlarged uses for the metal. In general the low-melting bismuth alloys are of high specific gravity, relatively soft, of low tensile strength, brittle to shock, yet subject to plastic

Jan 1, 1945

SULPHUR is a very well known mineral and apparently is produced in many places. It is engendered from an unctuous earthy and powerfully hot substance so that it is considered among experienced workers to bear a resemblance to the element of fire. This is called by these same men the masculine seed and the prime agent of Nature in the composition of metals. Because of its great dryness and heat it has, as experience shows, affinity with fire, which is easily introduced in it when brought near. And once introduced the fire is quenched only with difficulty before its unctuousness is wholly consumed. Although it shows itself to us of such a hot and dry nature, we must not think that sulphur is a substance so pure that it can stand by itself or that in order to attain its form it has no need of its portion and part of moisture like every other mixture. This is shown to us by its easy fusion, in which it resembles the metals. This thing is found in many places and in many varieties of color; some are white, others yellow and orange, and some others between gray and black. They also say that some red is found. It does not occur in that arrangement of veins like other minerals, but most liberal Nature makes whole mountains of it as is seen in the Aeolian islands, [26] near Sicily, in Etna or Moncibello which is the island of Sicily, at Pozzuoli, in the territory of Rome, in the Sienese domain at San Filippo, and in many other similar places. It is a substance that has a very strong odor and is most unpleasant to smell. It is very fixed in its substance so that it is never corrupted by time, by boiling, or by the moisture of water. For although it may stand in water a long time it never becomes soft nor does it ever decrease or increase in weight. It is brittle and easily crushed very fine. It is said that a trace of garlic rubbed on the mortar helps anyone who wishes to reduce it to impalpability. Its ores have a form more like earth than like stone although they some¬times have the color of a certain soft rock. The places where it is found are easily recognized by the great odor that they give out and by the very hot baths that often spring forth near it. What I have already told you about quicksilver that is contrary to the

Jan 1, 1942

By J. W. Schroeder

SEAMLESS pipe, the product produced from piercing a solid round billet of steel by the Mannesmann process, was first produced in the latter half of the 19th century, the Mannesmann machine having been patented in 1885. The products of other processes also have been termed seamless pipe; for example, the cylindrical section produced by "cupping," which consists of forming a cup from a flat plate or disk and further elongating the cup into a tube by passing it through a set of reducing dies. The purpose of this paper is to discuss some of the more important metallurgical factors and their relationship to the economical production of seamless pipe produced by the Mannesmann piercing process. The first seamless tube plant in America was established at Shelby, Ohio, in 1891, and was employed in the manufacture of bicycle tubing. For a number of years the bicycle industry was the only user of seamless tubing, and this tubing was produced by hot-rolling pierced billets imported from Europe and finishing on the cold drawbench. At the turn of the century, the automotive industry was responsible for an increase in the demand for seamless tubing. The growth of this industry was the dominant factor leading to the phenomenal growth of the petroleum industry, which in turn created a tremendous demand for seamless pipe. In addition; the old lapweld iron boiler tubes for stationary and locomotive boilers were replaced gradually by seamless tubes. Since 1929, the production of seamless steel pipe and tubes has increased over loo pct. In 1929, 1,459,9031 net tons of seamless pipe was produced, including both hot-finished and cold-drawn material, as compared with 3,087,3122 net [ ] tons in 1948. Table I gives the distribution of seamless pipe by classes for 1948. METALLURGICAL PROBLEMS From a metallurgical standpoint, the production of seamless pipe has presented many problems. Practically every type of steel, carbon and alloy, with the exception of the superalloys developed during World War II, has been pierced and rolled successfully into tubing. This includes bessemer, open hearth, by the stationary and duplex processes, and electric steels. The range of sizes produced is no less staggering to the imagination, when it is considered that the hypodermic needle, which is 0.016 in. diam with a wall thickness of 0.004 in., and pipe for gas or oil transmission lines, with a 26 in. OD, are both seamless tubes. Between these extremes, the range of diameters and wall thicknesses meets most present-day demands for seam-

Jan 1, 1951

By James P. Kimball

Jan 1, 1885

By P. H. G., Durville

ANY metal which contains even a small percentage of aluminum possesses certain peculiarities of appearance and properties which are exhibited both when the metal is melted and after it solidifies. Pure aluminum, or an alloy containing a small proportion of aluminum, can be melted without flux-except for a layer of charcoal-because a film of aluminum oxide and metal forms at the surface of melted aluminum. Although very thin, this film is air-proof, and it prevents the metal underneath from oxidizing. This oxidized film does not move easily on account of its toughness and high surface tension. One very important point in connection with this process of still casting has not been strongly enough stressed, namely, that the same kind of surface film with the same peculiarities forms over the surface of all melted alloys that contain even a small proportion of aluminum. Experienced foundrymen know how desirable it is to cast aluminum under its "skin" or under the surface of the film which tends to remain still. In the case of red copper, when in fusion, the surface shows pure copper only. This' is due to the fact that liquid copper constantly absorbs the copper oxide which forms on the surface. By closely examining melting copper the oxide can be seen dissolving in the bath, and going into solution just as pulverized sugar dissolves in water. When copper is cast in the open, either in wire bars or cakes, the surface of metal exposed to the air is covered by a film of black oxide that cannot be absorbed by the metal.

Jan 1, 1927