On the following pages are abstracts of papers published by the Institute during the year 1935 as TECHNICAL PUBLICATIONS and CONTRIBUTIONS, papers in bound volumes appearing for the first time, and papers in MINING AND METALLURGY. For abstracts of papers that appeared in bound volumes in 1935 but that were published as TECHNICAL PUBLICATIONS in 1934, see the YEAR BOOS dated January, 1935.. Many of the TECHNICAL PUBLICATIONS have been reprinted in bound volumes. Information regarding this disposition, and number of pages in each paper, may be found in the list beginning on page 64. Volume numbers are given as listed at the beginning of the index, page 71. The abstracts are grouped as follows: [Page Metal Mining 17 Uses of Metals 23 Milling and Concentration 23 Iron and Steel Division 26 Nonferrous Metallurgy (Reduction of Ores)...: 34 Institute of Metals Division (Founding and Metallography of Nonferrous Alloys) 36 Page Coal Division 43 Petroleum Division 50 Industrial Minerals Division (Nonmetallics) 57 Mining Geology 60 Mineral Industry Education Division 62 Geophysical Prospecting 62]

Jan 1, 1936

By S. R. Dunbas, D. C. Jillson, E. A. Anderson

THE present work was undertaken to furnish information, lacking in the literature, on the deformation mechanisms active in pure titanium at room temperature. Since it was started, Rosi, Dube, and Alexander' have indicated that slip can occur in coarse-grained (2 to 6 mm diameter) titanium on the {1010} and {1011} planes and twinning can take place on the {1072}, (1122) and (1151) planes. Liu and Steinberg,' working with titanium flakes produced by fused salt electrolysis, found evidence of twinning on the {1032$, {1121), {1122}, (1123}, and (1154) planes. The crystals used in the present work were substantially longer (up to nearly 2 in. in length) and possibly purer. Production of Large Crystals It was the purpose of this part of the work to provide single crystal or large grain specimens for use in the deformation studies rather than to study the mechanism of crystal growth. Accordingly, all further exploratory studies on methods were abandoned when it was found that cold-rolled bars sealed in vacuo in individual Vycor tubes and given three or more cycles of 4 hr at 1200°C and three to five days at 850°C, gave large grains. Eighteen specimens about 0.2 in. square x 2 in. long yielded 33 useful grains, ranging from Va in. to nearly 2 in. in length, with an agreeably wide range of orientations, Fig. l. The 0.25 in. thick strip from which the starting specimens were cut had been reduced 67 pct on 18 in. diameter rolls from a scalped, hot-forged (959" to 1000°C), arc-melted, iodide titanium ingot. Thc bar was at room temperature, but the rolls were at 200°C. Reductions of about 0.03 in. per pass were used. The bar was cut into four segments, each of which was rolled in a somewhat different manner. No effect on the growth of large grains was noted. The composition of the titanium, determined on turnings from the ingot scalping operations, is given in Table I. The Rockwell A hardness of the ingot was 26. The standard starting specimens, about 1/4x1/4x2 in., were milled on all four sides, hand polished on 280 and 400 mesh emery papers, etched for 3 min in a 50 HF-50 glycerine solution, rinsed, and dried in alcohol and ether just before sealing them in Vycor tubes. The average specimen weight was 7.5 g, and the tube volume was 6.5 cc. A vacuum of less than 1 micron pressure was applied. The specimen tubes were placed in an evacuated Inconel muffle to minimize the danger of collapse of the glass tubes at temperature. In practice the specimens were first heated to 1200 °C for 4 hr and then transferred fairly quickly to an 850°C furnace where they were held for three to five days. This cycle was repeated at least three times before the specimens were cooled, removed from the tubes, lightly polished and etched on one surface for examinstion. Those in which large grains had not developed were resealed in Vycor and returned to the cycling. Satisfactory specimens (about one out of every four cycled) were polished with emery paper on all four side;, then metallographically polished using ctchinz between wheels to remove distorted metal and, finally, given a very light etch to reveal the grain boundaries. This was necessary because the surface was roughened by the sublimation of titanium under high temperature vacuum conditions. Specimens were identified by TiXl numbers using supplementary letters to designate specific grains.

Jan 1, 1954

By D. J. Jr. McAdam

PART I.-OUTLINE OF INVESTIGATION, DESCRIPTION OF METHODS AND MATERIAL Previous Investigation of the Influence of Stress on Corrosion IN 1917 Haigh1 presented evidence that under simultaneous corrosion and cyclic stress metals may fail at lower stresses than if the corrosion is prior to the cyclic stress. In 1926 the author, while investigating the cooling effect of water on the fatigue resistance of metals, found that under these conditions steel specimens fail at stresses far below the endurance limit.2 (By "endurance limit" is here meant the fatigue limit obtained with specimens as free as possible from stress concentration and corrosive influences.) This led to an investigation (at the Naval Engineering Experiment Station, Annapolis, Md.) of the influence of cyclic stress on corrosion. This investigation maybe divided into three parts. The first part was a general survey of the conditions necessary to cause complete failure under corrosion and cyclic stress of relatively high frequency. The entire process by which metals fail under these conditions was-called "corrosion-fatigue." "Corrosion-fatigue limits" for a large number of metals were determined and the relationships of these limits to chemical composition, heat treatment and physical properties were established. The conclusion was reached that corrosion-fatigue is due to the accelerating influence of cyclic stress on corrosion. Results of this part of the investigation were presented in five papers.2-6 The second part of the investigation was a preliminary study of the influence of cyclic stress on corrosion. Each experiment was conducted in two stages. The first was a corrosion stage in which the specimen was corroded under cyclic stress; the second was a fatigue stage, in which the previously corroded specimen was tested (without further corrosion) to determine its fatigue limit. The difference between this fatigue limit and the endurance limit was used as a criterion of the "damage" due to

Jan 1, 1931

By J. E. Brantly

In October 1939, a drilling program was commenced on the Atlantic seaboard of Brazil, with three steam rotary rigs of medium capacity. One of these was assigned to the State of Alagbas and the other two to the State of Bahia. During the remaining few months of 1939 and during the year 1940, some eight wells were drilled, two in Alagbas and six in Bahia. Two small producers were found in the latter state. In early 1941 three medium-weight Diesel rigs were added to the equipment, thus permitting the drilling of some 15 wells during the year 1941. The two small producers found in 1940 in the State of Rahia were near the city of Silo Salvador. In 1941 three additional small wells were brought in, in the same area, and a further producer on an isolated structure some 75 km. to the northwest of this production. No commercial production has been found in the State of Alagbas. Approximately 26 wells have been drilled or are drilling, six of which are producers— five in one area and one in another. The program for 1942 calls for the development of the two areas in which wells have been found and also the drilling of several wildcat structures located either by geophysics or surface geology. All production in the area of the several producing wells is somewhat less than 2000 ft. and in the other area about 3800 ft. The area of the several wells is known as the Lobato field, and is practically within the city limits of Sao Salvador. The area 75 km. northwest of the city will be known as the Candeias field.

Jan 1, 1942

IN speaking, on the subject, "Engineer-Citizens," at the Lehigh Valley Mineral Industries Conference dinner, on April 26, at Easton, Pa., George Otis Smith, Director of the United States Geological Survey and President of the American Institute of Mining and Metallurgical Engineers, said in part: "It would be carrying coke to Connellsville to bring to the Lehigh Valley the idea that mineral resources are the foundation of national prosperity. Unfortu-nately, however, this obvious, fact is not everywhere recognized. Too many of our economists, journalists, statesmen and other dopesters of present business con-ditions stress the human factor so strongly that they overlook the material with which men work out their destiny. To them the financial psychology of Wall Street and the political logic of Capitol Hill and the business commonplaces of Main Street all loom far larger than the geology of the Lehigh Valley or the engineering triumphs of Bethlehem, or, the creative thinking at Lehigh and Lafayette. "The present situation in the industrial and .business world is a complex of interacting causes and reacting effects not easily itemized and entered on our trial balance sheet. But, chief among the liabilities of today is the excess of production capacity in most branches of industry. The farmer has no. monopoly in his desire for relief. Whether your professional connections are with steel or cement, coal or oil, copper, or zinc, you; know too well that for, the moment America is over-engined, and you keenly realize the ever-present hazard of industry speeding up regardless of the curves or grades just around the corner.

Jan 5, 1928

By J. E. Brantly

In October 1939, a drilling program was commenced on the Atlantic seaboard of Brazil, with three steam rotary rigs of medium capacity. One of these was assigned to the State of Alagbas and the other two to the State of Bahia. During the remaining few months of 1939 and during the year 1940, some eight wells were drilled, two in Alagbas and six in Bahia. Two small producers were found in the latter state. In early 1941 three medium-weight Diesel rigs were added to the equipment, thus permitting the drilling of some 15 wells during the year 1941. The two small producers found in 1940 in the State of Rahia were near the city of Silo Salvador. In 1941 three additional small wells were brought in, in the same area, and a further producer on an isolated structure some 75 km. to the northwest of this production. No commercial production has been found in the State of Alagbas. Approximately 26 wells have been drilled or are drilling, six of which are producers— five in one area and one in another. The program for 1942 calls for the development of the two areas in which wells have been found and also the drilling of several wildcat structures located either by geophysics or surface geology. All production in the area of the several producing wells is somewhat less than 2000 ft. and in the other area about 3800 ft. The area of the several wells is known as the Lobato field, and is practically within the city limits of Sao Salvador. The area 75 km. northwest of the city will be known as the Candeias field.

Jan 1, 1942

THE LIFE and works of Alexander Agassiz, first president of the Calumet & Hecla Mining Co., were recalled to memory when a monument bearing his statue was unveiled in Agassiz Park, at Calumet, Mich., on Sept. 26, The statue is the work of Paul W. Bartlett, of New York, and was erected by George R. Agassiz, eldest son of Alexander Agassiz. We are indebted to Rodolphe L. Agassiz, now president of the Calumet & Hecla Consolidated, for the accompanying photograph of the statue. The principal address at the unveiling ceremony was delivered by Allen F. Rees, of Houghton, who said, in part: To the world at large Alexander Agassiz was preeminently the man of science. With all his devotion to the industrial life of this district, he found the time to devote to the con-tinuation of his work of scientific research which had been the life work of his fa-ther, Louis Agassiz. Not only did he acquire eminence for his scientific at-tainments and learn-ing, but he was recognized and hon-ored throughout the civilized world for his achievements and accomplishments in the realm of original research. His work in the fields of nat-ural science, in oceanography, in marine zoology, and in other similar lines of research, has added much to our knowledge of the world's mysteries. His life was one of accomplishment also in the industrial world. The union in one life of acknowledged achievement as a scientist and the accomplishment of great results in the prac-tical industrial world is a rare thing, and its possibility has never been exemplified in greater measure than in his life and its results.

Jan 11, 1923

By AIME AIME

AMONG the recent mining and metallurgical developments in England great interest has been shown in the development of an iron-ore field covering 26,0.00 acres in Northamptonshire, containing 500,¬000,000 long tons of ore; and the erection at Corby, by Stewarts & Lloyds, of a modern basic bessemer steel plant and tube works. The entire project was planned to cost about £3,300,000. Many improvements have been made in the varied equipment that is being installed, some of which has set mew records for massiveness. There is, for instance, a new roll crusher, which has been manufactured by Hadfields, Limited, of Sheffield, the largest ever built in England, and weighing 130 tons. This machine, shown in Fig. 1, as erected at the Hadfields shops, is primarily designed to take blocks of iron ore as they come from the steam shovel. The maximum size is 54 by 48 by 36 in., hut occasional pieces slightly larger than this may be accommodated. The capacity is upwards of 500 tons per hour, the product passing to a secon-

Jan 1, 1934

By A. Hultgren

PAGE Outline of Progress of Knowledge and Theories about Gas Evolution in Steel Ingots, and Its Influence on Crystallization and Segregation 2 Object of Present Investigation 16 theoretical Discussion of Process of Solidification 17 Gas Given Off from Rimming Steel during Solidification 17 Equilibrium Diagram of the Iron-carbon-oxygen Alloys 19 Solidification of Pure Iron-carbon-oxygen Alloys 25 Solidification When Carbon Monoxide Is Given Off at Constant Pressure... 25 Solidification When Gas Evolution Is Suppressed 26 Schematic Application on Solidification of Rimming-steel Ingots 27 Influence of Manganese, Sulphur and Phosphorus 28 Experimental Work 30 Liquid Steel and the Mold Gas 30 Ingots Investigated and Methods Used 33 Ingot Structure 42 Structure of Rim Zone 42 Structure of Core 49 Structures Obtained under Special Conditions of Freezing 50 Distribution of Metalloids 55 Other Observations Made 60 General Discussion of Solidification Process 63 Condition of Liquid Steel before Casting 63 Rimming Period 70 Composition of Rim Zone 93 Freezing after Top Is Closed 96 Slag Inclusions and Ingot Scum 102 Reaction between Gas in Blowholes and Surrounding Solid Steel during Cooling 103 Summary 105 Appendix-Preparation and Etching of Ingot Sections 106 References 107 IN 1934, Jernkontoret (The Swedish Ironmasters' Association) appointed a committee for the study of the structure of rimming-steel ingots and the various phenomena associated with their solidification. The members of the committee, including those who have joined it later, have been: I. Bohm, B. D. Enlund, B. Kalling, M. Tigerschiöld, 1. Wohlfahrt and the authors. The present paper? is a somewhat

Jan 1, 1939

By William D. Klopp, Joseph R. Stephens

ThE phenomenon of high ductility associated with a phase transformation, termed super plasticity, has been reported for a number of alloy systems. Abnormally high ductility has been observed during tensile testing of cast eutectic alloys of Pb-Sn and Mg-cu.1 Brasses of Cu-37 at. pct Zn and Cu-40 at. pct Zn elongate up to 180 pct when tested near their transformation temperature.' Enhanced ductility was also observed in Cu-47 at. pct Zn tested near the order-disorder transformation temperature. The most remarkable super-plastic effect reported to date is for the eutectoid alloy A1-60 at. pct Zn, where elongations up to 1000 pct have been reported.3 underwood4 has recently summarized the conditions that normally accompany the superplastic effect which are: 1) a phase transformation or allotropic change or order-disorder transformation; 2) an externally applied stress; 3) presence of an interface between two phases; and 4) a metastable structural condition. In addition, higher ductility is observed when the specimen is tested at slow deformation rates rather than under impact. The purpose of this note is to present evidence of the superplastic effect in a Cr-30 at. pct Co alloy. In addition, low-temperature bend ductility data are given for the alloy in the quenched, metastable, single-phased condition and in the slow-cooled, two-phased, near-equilibrium condition. Sixty-gram alloy ingots were prepared by noncon-sumable arc melting of iodide chromium and electron-beam-melted cobalt. These were cast into rectangular ingots and fabricated to 0.035-in. sheet by rolling at 2300°F. Attempts to roll at slightly lower temperatures invariably resulted in severe cracking, apparently due to presence of the brittle a phase below the transformation temperature of 2230°F. Tensile specimens with a 0.25 by 1.0 in. reduced section were cut from the sheet by electrical discharge machining. The specimens were heated at 2400°F for 1/2 hr to obtain a recrystallized, bcc, single-phased structure. Temperature of the specimens was subsequently raised or lowered to the desired test temperature and held for 10 min prior to testing at a crosshead speed of 0.01 in. per min. Fig. 1 shows the chromium-rich side of the Cr-Co phase diagram.6 The alloy composition investigated is near the point of maximum solubility of cobalt in chromium, and the alloy is two-phased when in equilibrium at temperatures below 2230°F. The results of tensile tests conducted at temperatures indicated by X's in Fig. 1 are summarized in Figs. 2, 3, and 4. Tensile elongations shown in Fig. 2 increase from 11 pct at 1900°F to a maximum of 160 pct at 2250°F. The elongation then decreases to 44 pct as the test temperature is further increased to 2600°F. The proximity of the temperature of highest elongation and the solvus temperature suggests that a superplastic effect is present in Cr + 30 at. pct Co similar to that observed for other alloys that show anomalous ductility. The variation of upper yield stress with temperature is shown in Fig. 3. A small peak in yield stress occurs at 2250"F, coincident with the maximum in

Jan 1, 1967

By S. E. Bronisz, R. E. Tate

s-plutonium samples possessing a strong growth texture have been produced by allowing them to transform under pressure from p to a. A fiber texture with [010] parallel to the pressure axis results. The textured samples are expected to be useful in determining the effects of crystallographic orientation on the physical properties of a plutonium, and initial results of measurements of resistivity and mechanical properties are described. THE crystal structure of a plutonium1 is mono-clinic, P21/m, and many of the metal's properties should reflect the crystallographic anisotropy. Unfortunately, it has not yet been possible to grow useful sizes of single crystals of a plutonium. Therefore, few of plutonium's orientation-sensitive properties have been determined as a function of crystallographic orientation. One way to gain information about at least some of the orientation-dependent properties is to study a highly textured sample. Such samples have been produced by cold rolling a plutonium,2 but they are necessarily very small in one dimension. We have now successfully used two other techniques to produce highly textured samples, not limited to small thicknesses. METHODS OF PRODUCING PREFERRED ORIENTATION The texture is produced by causing the plutonium to transform from ß to a while under pressure. It was observed by Gardner3 that applying a compres-sive load during the transformation resulted in the formation of columnar grains of a plutonium, and Cramer4 observed a similar structure in some diffusion couples rolled in the P phase. Neither of these workers, however, investigated the subject beyond these observations. The more flexible of the two methods developed is that of compressive loading. The technique is to enclose a sample of plutonium in a die assembly before applying the load. It is possible, of course, to dispense with the die and simply press the sample between two platens. In this case, however, the unrestrained sample deforms during the pressing, making it difficult to maintain the load and to control the final sample thickness. This compressive loading technique has been used on specimens ranging from 1/4 to 3 in. diameter, with height-to-diameter ratios ranging from 5 : l to 1:6. The procedure begins with loading the sample, a right cylinder of a plutonium, into the pressing die. Plastic deformation of the sample while it is being pressed is minimized by machining the sample so that its diameter is nearly the same as that of the die barrel. Then the loaded die assembly is placed in a vacuum pressing can that fits on a hydraulic press. After a vacuum is achieved the die assembly is heated to 180°C and equilibrated. The load is then applied and the specimen and die are allowed to cool to about 40° to 50°C before the pressure is removed. The resulting sample is composed of rod-shaped a -plutonium grains, the rod axes being parallel to the cylinder axis and the pressing direction. Photomicrographs of the oriented structure are shown in Fig. 1. Although most of the specimen is composed of grains whose rod axes are parallel to the cylinder axis, a thin, peripheral layer consists of rod-shaped grains whose rod axes are perpendicular to the cylinder axis. Presumably, the highly plastic nature of p plutonium leads to approximately hydrostatic conditions during the initial stages of the P — a transformation under pressure. At this time, the grains in the peripheral layer would have grown parallel to the local force direction. During the latter stages of the transformation, the accompanying volume contraction would have eliminated the radial forces, leaving only the axial force and resulting in the growth of the observed structure. The growth texture did not form without the application of pressure. Attempts were made to produce the texture by repeating the standard temperature cycle without

Jan 1, 1965

Jan 7, 1976

By WILLIAM SLOAN

B RITISH COLUMBIA in its mining activities is going ahead by leaps and bounds both in development and production. Mineral production for 1925 was $61,492,242 in value as compared to $48,704,- 604 in 1924, or an increase of about 26.2 per cent. This is a new record. It is the first time in the history of mining in British Columbia that we have gone over the fifty million mark. But we have got in the habit of making new records. The year 1924, with its mineral production of almost forty-nine million was a new record. And I am confident that when the mining history of 1926 is written it will be found that we have established yet another new record and that we can report another 25 per cent increase over 1925. What is the explanation? It is not only that the world is settling down, and settling up, after the war. It is not only that in the rebuilding, the refashioning in which all nations are busily engaged, the metals that come from our mines are needed. More than anything else, at least as far as we are concerned, it is because British Columbia has the resources and the fact that the province has been fortunate in recent years in finding men with the enterprise and the vision required to push ahead the labor of their development. From the ranks of our own people in Canada we have prospectors who have faith, energy and requisite knowledge. They are combing our hills season after season and they are of the type of manhood that does not know the meaning of the word quit. More and more these men are learning the importance of the guidance furnished by geological reports, and to an ever increasing extent such reports, thanks to the valuable work of the Canadian Geological Survey, covering areas little known to man, are made available to them-but it is recognized that in the opening up of our Province, containing within itself 372,000 square miles, it is essential that we should have the cooperation of our cousins on this side of the line as well as of our fellow citizens of the Dominion and of the Mother Country.

Jan 1, 1926

By Robert Linton

THE PURCHASE of silver by the United States Government under the provisions of the Pittman Act is practically completed. Producers of silver in this country will now have to market their silver in competition with the rest of the world. It therefore becomes of interest to study such data as are available and endeavor to obtain such suggestions as may be afforded therefrom as to the probable future market position of the metal. Conditions influencing the marketing of silver are numerous and complex. It is a commodity entering. into the arts and manufactures, and therefore influenced by the condition of various lines of business which make use of it; it is currency-being used by all countries for subsidiary coins and even as the founda-tion of the system by a very few; and it serves as a frequent basis for speculation. The various factors involved can easily set up so many cross-currents in the flow of the metal that predictions in regard to the market position of silver can never be safely made, although it may be possible to form some idea of prob-able trends over a sufficiently long period. Of course price is determined, as is the case with all commodities, by the inexorable workings of the law of supply and demand.

Jan 6, 1923

(Under this heading will be published notes sent to the Secretary of the Institute by members or other persons introduced by members) Member, Graduate Colorado School of Mines. Four years' experience in West and Northwest. Two years with American Smelting and Refining Co. Wishes to join field party on geological work, mining or areal, where opportunity will be given to be of direct assistance to chief of party in solution of field problems. Age, 26. Unmarried. At liberty June 1. No. 342. Member, technical graduate, aged 30, with' 7 years' experience in concentrating and mining, desires a position of authority with reliable company. At present employed. No. 343. Member. Ambitious, energetic, tactful engineer, college graduate, married, aged 30, desires location with a large coal mining organization. Seven years with present employers -n middle west; has had broad experience in the past eight years on examination, development and construction; successful record in handling men. Position must carry responsible work and a future. Will go anywhere for proper opportunity. Exceptional references as to reliability, character and capacity for work. No. 344.

Jan 3, 1917

With a total value to date of well over $200,000.000.00 for its ore production, the Tintic mining district, which is about 100 miles southwest of Salt Lake City, ranks as one of the three main ore producing areas of Utah. In it are located the biggest silver mines of the country, silver having been the chief metal produced in the camp since its start. Tintic's silver production to date has a total value of over $1 00,000,000, approximately half of the value of the camp's ore production, the balance being roughly divided among lead, gold and copper. Discovery of the camp was made in the late sixties. Lack of transportation and ore reduction facilities delayed extensive development of the area for nearly a decade. In recent years Tintic's ore production has ranged from 350,000 to 400,000 tons annually. In 1924 the camp produced one-eighth of the silver produced in the nation with an output of 7,729,700 ounces. Its lead production was 77,765,000 pounds and its gold production 26,285 ounces.

Jan 1, 1925

THE shipments of high-grade manganese ore, con-taining 35 per cent or more of manganese, from the mines in the United States in 1926 were slightly less than half as large as similar shipments in 1925, accord-ing to the United States Bureau of Mines, Department of Commerce. The shipments in 1926 by 45 producers amounted to 46,258 long tons as compared with 98,324 long tons by 42 producers in 1925. This decrease was due to the falling off of the shipments from Montana. The domestic production of metallurgical ore in 1926 was 26,530 tons; that of chemical ore, 19,728 tons. Montana was the largest shipper with 5713 tons of metallurgical ore and 17,904 tons of chemical ore. The largest individual shipper of metallurgical ore was the Crescent Mine in the Olympic Mountain Region, Clallam Co., Washington, from which the shipments for the year were 3162 tons. The mine was operated by lessees and reverted to the owners in July, and thereafter to the close of the year no .ore was shipped.

Jan 6, 1927

By Gordon E. Frantti

Under the auspices of the Geophysical Committee of Michigan College of Mining and Technology, an investigation was made in Michigan's Upper Peninsula to obtain geophysical data related to the regional subsurface geology in the area covered by Paleozoic sediments. The area surveyed includes that portion of the Upper Peninsula which lies between R18W to R26W and T41N and T49N, covering approximately 1300 square miles. On the index map, Fig. 1, it is represented by the cross-hatched zone west of Munising. Four of the five sites of detailed investigation are indicated by the letters A, B, C, and D. A detailed gravity and magnetic survey had previously been conducted by J. G. Wilson near Perkins, 8 miles north of Rapid River, on a local anomalous area. Results of his work, which showed a large positive magnetic anomaly associated with a gravity anomaly, aroused interest in the possible economic significance of the formations underlying the Paleozoic sediments in this part of the Upper Peninsula.

Jan 1, 1956

By Frederic Benard

Recovery of selenium and tellurium at Copper Cliff by the Ontario Refining Co. has been previously described by the writer.l During 1935 a new building was erected to house this operation and description of the new plant and process form the subject of this paper. The building, of modern steel and tile construction, covers an area of 5900 sq. ft. with a volume of approximately 166,000 cu. ft. The large monitored center bay is flanked by two smaller outside bays, one of which is devoted to the tellurium section. All equipment, ceilings and upper walls, are treated with aluminum paint, giving good illumination and facilitating good housekeeping, essential from a health standpoint in handling material of this nature. Equipment Layout and type of equipment conforms to the requirements of the process as described below. In the selenium section, storage tanks, neutralizing tanks and precipitators are of steel construction, lead-lined and arranged for gravity flow (Fig. 1). The neutralizing tanks are equipped with water-cooled lead coils for controlling solution temperature, agitation being accomplished with compressed air. The precipitators are provided with mechanical agitators, and sulphur dioxide is introduced into the solution through 1/2-in. lead pipes leading from a manifold attached to the cover of the precipitator. Each precipitator has internal cooling coils and an air-jet exhauster to carry off fumes. Neutralized solutions are filtered in a 29-plate wooden filter press using heavy cotton duck as a filter medium, forced feed being maintained by a Welmet centrifugal pump. Dilute solutions are concentrated by evaporation in a vacuum evaporator, constructed of cast hard lead. Heat is supplied by an outside steam chest operating under 15 Ib. steam pressure. The solution is circulated through the steam chest by a pump of antimonial lead at a rate approximating 400 cu. ft. per min. The evaporator is evacuated by a water-jet condenser that creates a vacuum of 26 in. of mercury under normal operating conditions. The capacity of the vessel is 60 cu. ft. and the rate of evaporation 25 cu. ft. per hour.

Jan 1, 1943

By Frederic Benard

Recovery of selenium and tellurium at Copper Cliff by the Ontario Refining Co. has been previously described by the writer.l During 1935 a new building was erected to house this operation and description of the new plant and process form the subject of this paper. The building, of modern steel and tile construction, covers an area of 5900 sq. ft. with a volume of approximately 166,000 cu. ft. The large monitored center bay is flanked by two smaller outside bays, one of which is devoted to the tellurium section. All equipment, ceilings and upper walls, are treated with aluminum paint, giving good illumination and facilitating good housekeeping, essential from a health standpoint in handling material of this nature. Equipment Layout and type of equipment conforms to the requirements of the process as described below. In the selenium section, storage tanks, neutralizing tanks and precipitators are of steel construction, lead-lined and arranged for gravity flow (Fig. 1). The neutralizing tanks are equipped with water-cooled lead coils for controlling solution temperature, agitation being accomplished with compressed air. The precipitators are provided with mechanical agitators, and sulphur dioxide is introduced into the solution through 1/2-in. lead pipes leading from a manifold attached to the cover of the precipitator. Each precipitator has internal cooling coils and an air-jet exhauster to carry off fumes. Neutralized solutions are filtered in a 29-plate wooden filter press using heavy cotton duck as a filter medium, forced feed being maintained by a Welmet centrifugal pump. Dilute solutions are concentrated by evaporation in a vacuum evaporator, constructed of cast hard lead. Heat is supplied by an outside steam chest operating under 15 Ib. steam pressure. The solution is circulated through the steam chest by a pump of antimonial lead at a rate approximating 400 cu. ft. per min. The evaporator is evacuated by a water-jet condenser that creates a vacuum of 26 in. of mercury under normal operating conditions. The capacity of the vessel is 60 cu. ft. and the rate of evaporation 25 cu. ft. per hour.

Jan 1, 1943