By R. W. Moore, A. B. Kinzel

Although the iron-carbon diagram has undergone many changes in the last 20 years, the region below the eutectoid line and up to approximately 1.7 per cent carbon has been little affected. This region is generally considered to consist of cenlentite and ferrite. Graphite has been noted occasionally in the hypereutectoid steel region, and the ready formation of graphite nodules in malleable cast iron is a phenomenon difficult to interpret in the light of cementite, supposedly stable at sub-eutectoid temperatures. In this case the graphite formation has been partly explained by the presence of silicon, and many have believed that silicon acts to change the stable state rather than to accelerate reactions so as to arrive at the stable state in a briefer period of time. Consideration of this phenomenon indicates that cementite is not the stable phase in the temperature composition zone referred to. In the course of examining a low-carbon steel tube taken from a petroleum cracking still, which had been in service for approximately three years at temperatures somewhat below the eutectoid temperature, observations were made that shed light on this entire subject. The tube in question analyzed:' C, 0.15 per cent; Mn, 0.49; Si, 0.02; S, 0.023; P, 0.015. The microstructure of the tube after service is shown In Figs. 1 and 2. From these it is evident that cementite as such is absent, and that in its place nodular graphite has been formed. In order to check this observation further, samples taken from the tube were heated at 850" C. for varying periods of time. The small samples were put into a large hot furnace, and the total time is recorded. The structure of the sample after 5 min. at 850" C. is shown in Figs. 3 and 4, and the nest of pearlite surrounding the graphite nodules is most satisfactory evidence of the character of the nodules. As the length of time of heating at this temperature increases, the pearlitic zone increases, with final restoration

Jan 1, 1935

By R. W. Moore, A. B. Kinzel

Although the iron-carbon diagram has undergone many changes in the last 20 years, the region below the eutectoid line and up to approximately 1.7 per cent carbon has been little affected. This region is generally considered to consist of cenlentite and ferrite. Graphite has been noted occasionally in the hypereutectoid steel region, and the ready formation of graphite nodules in malleable cast iron is a phenomenon difficult to interpret in the light of cementite, supposedly stable at sub-eutectoid temperatures. In this case the graphite formation has been partly explained by the presence of silicon, and many have believed that silicon acts to change the stable state rather than to accelerate reactions so as to arrive at the stable state in a briefer period of time. Consideration of this phenomenon indicates that cementite is not the stable phase in the temperature composition zone referred to. In the course of examining a low-carbon steel tube taken from a petroleum cracking still, which had been in service for approximately three years at temperatures somewhat below the eutectoid temperature, observations were made that shed light on this entire subject. The tube in question analyzed:' C, 0.15 per cent; Mn, 0.49; Si, 0.02; S, 0.023; P, 0.015. The microstructure of the tube after service is shown In Figs. 1 and 2. From these it is evident that cementite as such is absent, and that in its place nodular graphite has been formed. In order to check this observation further, samples taken from the tube were heated at 850" C. for varying periods of time. The small samples were put into a large hot furnace, and the total time is recorded. The structure of the sample after 5 min. at 850" C. is shown in Figs. 3 and 4, and the nest of pearlite surrounding the graphite nodules is most satisfactory evidence of the character of the nodules. As the length of time of heating at this temperature increases, the pearlitic zone increases, with final restoration

Jan 1, 1935

By J. A. Cordier

USINOR has conducted four blast furnace tests with formcoke made from marginal coals in the pilot plant of HBNPC ("H. B. N." process) in four different blast furnaces of various sizes and with medium and high grade burdens. The tests in which up to 30% of the blast furnace fuel burden was replaced by HBN formcoke yielded good results on furnaces ranging in hearth diameters from 5.6 to 9.5 m. The tests demonstrated that: - the slight increase of pressure drop in the stack did not prevent smooth operation at record production rates with the same blowers - the total coke rate was not significantly affected, but there was a slight increase of the calorific value of the top gas - the hot properties of the formcoke are satisfactory as seen from the samples withdrawn at the tuyeres and tapholes. At the end of the two months test on BE nº 2 of Dunkerque, the hearth was as permeable and clean as with good standard coke. Our conclusion is that HBNPC formcoke made from lean coals is an adequate substitute for conventional coke in the range of 20 to 40% replacement, which is of interest to USINOR.

Jan 1, 1977

The International Mining Convention held in Nelson, B; C., May 17 , to 19, was attended by nearly 500 delegates, of whom about 100 were from Spokane, 150 from the Slocan district, and the others from different points in Canada and the United States. Arrangements were in charge of the Nelson, Slocan and Eastern British Columbia Mining Men's Club, under the direction of Secretary Fred A. Starkey, assisted by the City of Nelson, Associated Boards of Trade of Eastern British Columbia and Nelson Board of Trade. The Columbia Section of the American Institute of Mining Engineers; cooperating with the Western Branch of the Canadian Mining Institute, provided the technical program, under the management of Secretary E. Jacobs, of Victoria, and Secretary L. K. Armstrong, of Spokane. Three technical sessions were held, at which the following were read: Difficulties of the Electrolytic Zinc Process, by Thomas French. Sketch of the Geology and Ore Deposits of Nelson and Kootenay Region, by Arthur Lake's. Advantages of Local Organization of National Societies, by W. H. Linney. Review of Kootenay Mining, by Bruce White. Milling of Partially Oxidized Ores, by S. S. Fowler.

Jan 7, 1917

By R. W. Smith, R. W. M. Lai, J. Leja

J. Leja (Professor, Dept. of Mineral Engineering, U.B.C. Vancouver, Canada) — I would like to offer some comments on the behavior of contact angle with time, treated in this paper. The authors should be congratulated for a clear exposition of these uncommon departures in the correlation between flotation and contact angle, in systems of importance to industrial practice. Some nine years ago Professor J. H. Schulman (presently at Columbia University, New York) and I reported on a similar study conducted at the Ernest Oppenheimer Laboratory, Cambridge, England.' The systems used by us had, how- ever, no direct practical application at that time, as mercury in solutions of xanthates was tested with a variety of alkyl-aryl polyoxyethylene frothers which were then new to flotation practice. Further, the paper dealt with findings contrary to the then widely held belief that the contact angle established in collector-solution is unaffected by the addition of a frother. Correlation with flotation, or lack thereof, was not sought, though we did suggest that in many cases the selectivity of frothers might be influenced by the dynamic contact angles. We also stated (on p. 243,

Jan 1, 1968

By L. J. Gurevich

IN the course of the examination, at the Bureau of Standards, of fusible tin boiler plugs for the Steamboat Inspection Service, it became evident that an investigation should be undertaken to determine the precautions necessary in the manufacture of acceptable plugs. The results of the tests of these plugs show that their manufacture has improved, though at present not all of the plugs tested are satisfactory. Table 1 gives the result of tests of some 1500 plugs from about 100 makers. Records of the tests show that several of the makers were able to produce satisfactory plugs with every pouring. The Steamboat Inspection Service has the following specifications for fusible plugs: "Fusible plugs for use in boilers of steam vessels under the Jurisdiction of the Steamboat Inspection Service shall be made of bronze casing with the bore tapering continuously and openly from end to end, and filled from end to end with tin not less than 99.7 per cent. pure and to contain not more than 0.1 per cent. of lead and not more than 0.1 per cent. of zinc. The small end of the bore may be countersunk not more than 1/32 in. in depth and width, but no recess, thread, or cavity other than this countersink shall be allowed."

Jan 8, 1919

By Frederick N. Rhines

Pure copper that has been allowed to oxidize at an elevated temperature in the air is found to be covered with two distinguishable layers of oxide scale. The outer of these, which is very thin, is composed of cuprie oxide, while the inner layer, comprising the bulk of the scale, is made up chiefly of cuprous oxide (Fig, la). If a small quantity of an alloying element, such as silicon, is present in the copper, silica particles are found disseminated through the cuprous oxide, deposited most abundantly near the metal surface, and, in addition, silica particles occur to a limited depth within the copper itself (Fig. 1b). It is this inner layer, composetl of oxide particles precipitated in a matrix of metallic copper, that is known as the "subscale" or the zone of internal oxidation. Under a low oxygen pressure it is possible to produce the subscale without the formation of external layers of copper oxides, thus leaving the metal surface bright and apparently clean while oxidation has occurred, in fact, to a considerable depth within the metal (Fig. 2). Although little is yet known in a detailed way of the mechanism of internal oxidation, the general nature of the process is evident. By virtue of the considerable solubility of oxygen in copper,' it is possible to bring the alloying element in contact with oxygen within the metallic solid solution. If the oxide of the alloying element is more stable than cuprous oxide, the foreign oxide may form and, since most oxides are relatively insoluble in copper, it will not long remain in solution, but mill separate as a precipitate. As the metallic solute is exhausted in the zone of precipitation, oxygen that is constantly being supplied at the surface diffuses farther into the alloy and thus produces an ever-thickening shell of subscale. The distribution of the reacting elements in the subscale and adjoining zones must be somewhat as indicated in Fig. 3. The conditions requisite to internal oxidation to be anticipated are thus: (I) a solubility of oxygen in the alloy, (2) the ability of oxygen to diffuse at an appreciable rate into the alloy, (3) the possibility of the

Jan 1, 1940

By Frederick N. Rhines

Pure copper that has been allowed to oxidize at an elevated temperature in the air is found to be covered with two distinguishable layers of oxide scale. The outer of these, which is very thin, is composed of cuprie oxide, while the inner layer, comprising the bulk of the scale, is made up chiefly of cuprous oxide (Fig, la). If a small quantity of an alloying element, such as silicon, is present in the copper, silica particles are found disseminated through the cuprous oxide, deposited most abundantly near the metal surface, and, in addition, silica particles occur to a limited depth within the copper itself (Fig. 1b). It is this inner layer, composetl of oxide particles precipitated in a matrix of metallic copper, that is known as the "subscale" or the zone of internal oxidation. Under a low oxygen pressure it is possible to produce the subscale without the formation of external layers of copper oxides, thus leaving the metal surface bright and apparently clean while oxidation has occurred, in fact, to a considerable depth within the metal (Fig. 2). Although little is yet known in a detailed way of the mechanism of internal oxidation, the general nature of the process is evident. By virtue of the considerable solubility of oxygen in copper,' it is possible to bring the alloying element in contact with oxygen within the metallic solid solution. If the oxide of the alloying element is more stable than cuprous oxide, the foreign oxide may form and, since most oxides are relatively insoluble in copper, it will not long remain in solution, but mill separate as a precipitate. As the metallic solute is exhausted in the zone of precipitation, oxygen that is constantly being supplied at the surface diffuses farther into the alloy and thus produces an ever-thickening shell of subscale. The distribution of the reacting elements in the subscale and adjoining zones must be somewhat as indicated in Fig. 3. The conditions requisite to internal oxidation to be anticipated are thus: (I) a solubility of oxygen in the alloy, (2) the ability of oxygen to diffuse at an appreciable rate into the alloy, (3) the possibility of the

Jan 1, 1940

By R. F. Mehl, B. Lustman

THE formation of intermediate phase layers in cementation processes has been subjected to extensive qualitative investigation though to relatively little quantitative study; this work has recently been fully summarized by F. N. Rhines.1 It is necessary here only to enumerate the general conclusions drawn concerning the kinetic laws governing the growth of intermediate layers and to state what is known concerning the structural changes accompanying the generation of phase layers. I. When the intermediate phase is protective in type-i.e., when its density is less than that of the base metal, so that a continuous coating is formed and maintained the isothermal growth of the phase follows a simple parabolic equation: X2 = kt [I] where X is the thickness of the alloy layer, k the reaction rate constant, and t the time. The applicability of this equation to diffusion processes is tested by plotting the square of the thickness versus time, or by plotting the thickness versus the square root of time; the resultant achievement of a straight line in such. a plot has been con¬sidered sufficient proof of the validity of this equation. Exceptions have been found where liquid phases are involved in the reaction, where the diffusion layer is cracked,2 and where thin semimetallic oxide and sulphide coatings are formed on metals.3 In the first two cases the thickness increases linearly with time, and in the latter it is a logarithmic function of time. 2. The rate of thickening varies with temperature according to the Arrhenius equation k = Ae-Q/RT [2] where k is the parabolic rate constant of Eq. I, or some other rate-descriptive function, A is the action constant, e the base of natural logarithms, Q the heat of activation, R the gas constant, and T absolute temperature. This equation has been found to be generally valid except when transformations occur during reaction in either the base metal or in the reaction layer; in such instances Eq. 2 is still applicable with different values for the constants A and Q above and below the transformation temperature. 3. All phases that are stable at the temperature at which diffusion occurs will appear in the interdiffusion of two components. In some cases certain of the phases may be too thin to be observed and identified easily. Nonequilibrium phases have never been noted in thick reaction layers; i.e., layers of a thickness that may be discerned microscopically. The relative, thickness of each phase in a diffusion layer is proportional to the concentration gradient and to the rate of diffusion in that phase .4 The reaction layers tend to have a

Jan 1, 1942

By Henry Rawdon

ONE of the most vital problems in the manufacture of steel at present is the occurrence of the defects that have been popularly termed "snow flakes," "flakes," or "scabs." Particularly is this the problem of many manufacturers who during the past 2 yr. have undertaken large-scale production for the first time. A study of the microstructure of such defective material throws considerable light upon the nature of these defects and is essential before measures may be taken for the elimination of the defects. Flakes do not appear to be found in the plain carbon steels; they have been found, however, in abundance in some of the simple alloy steels that are being used in such vast quantities; viz., nickel steel of the approximate composition, 0.40 carbon and 3.5 per cent. nickel, and in the chrome-nickel type. The present article summarizes the characteristic features of defective steel of the flaky type as they have been found by laboratory study of numerous specimens, and it aims to show the conditions within the metal that are favorable to the occurrence of this type of defect without entering into the details of mill practice (size of ingot, design of molds, rate of cooling, distribution of cooling stresses, etc.), all of which conditions appear to play a role in the production of these defects.

Jan 2, 1919

By T. R. Graham, J. R. Long

This report is concerned with part of a series of investigations carried on by the Federal Bureau of Mines on alloys, particularly nonferrous alloys, made with electrolytic manganese. A broad general program instituted after commercial quantities of electrolytic manganese became available was necessary in order to compare the effects of electrolytic manganese with those of the ordinary commercial grades. Representative analyses of these two materials show the commercial manganese metal to contain up to 2 per cent iron, a maximum of I per cent silicon and 0.06 per cent carbon, while the electrolytic manganese rarely exceeds 0.01 iron, 0.02 sulphur, with no silicon or aluminum. In the literature, the emphasis has been largely on high-strength casting alloys containing up to 5 per cent manganese, and few data are available on wrought manganese alloys. These factors, coupled with the strategic position of copper and zinc, have given impetus to the Bureau's War Research Program for the development of alloys containing nonstrategic manganese for the purpose of supplementing or providing alternates for the more strategic metals. The alloy reported here was studied, along with several other ferrous and nonferrous alloys, as possible cartridge-case material, and was chosen after a review of the properties of the ternary alloys of copper-manganese-zinc. Preliminary Work In a cursory survey of this system, alloys ranging from 60 to 95 per cent copper, o to 50 per cent manganese, and 5 to 40 per cent zinc were investigated. The alloys containing 60 per cent copper were found to fall into the two-phase alpha plus beta region of the system, and since those containing 70 per cent would not permit a saving, only alloys containing 65 per cent copper were considered. The tensile properties of these 65 per cent alloys are plotted in Fig. I as a function of manganese content for annealed material and for four conditions of cold-work In the annealed condition the increases in strength and decreases in elongation are minor up to 15 per cent manganese; beyond this, the changes become more significant. In the cold-worked condition, the first 5 to 10 per cent of manganese appears to have the greatest strengthening effect, the rate of increase dropping off as the manganese increases beyond this amount. These effects are more pronounced with moderate than with severe cold reduction. It is also interesting to note that while the elongation of annealed material drops regularly with increasing manganese, the elongation in the cold-worked state is relatively little affected by increasing manganese content, particu-

Jan 1, 1944

By J. R. Long, T. R. Graham

This report is concerned with part of a series of investigations carried on by the Federal Bureau of Mines on alloys, particularly nonferrous alloys, made with electrolytic manganese. A broad general program instituted after commercial quantities of electrolytic manganese became available was necessary in order to compare the effects of electrolytic manganese with those of the ordinary commercial grades. Representative analyses of these two materials show the commercial manganese metal to contain up to 2 per cent iron, a maximum of I per cent silicon and 0.06 per cent carbon, while the electrolytic manganese rarely exceeds 0.01 iron, 0.02 sulphur, with no silicon or aluminum. In the literature, the emphasis has been largely on high-strength casting alloys containing up to 5 per cent manganese, and few data are available on wrought manganese alloys. These factors, coupled with the strategic position of copper and zinc, have given impetus to the Bureau's War Research Program for the development of alloys containing nonstrategic manganese for the purpose of supplementing or providing alternates for the more strategic metals. The alloy reported here was studied, along with several other ferrous and nonferrous alloys, as possible cartridge-case material, and was chosen after a review of the properties of the ternary alloys of copper-manganese-zinc. Preliminary Work In a cursory survey of this system, alloys ranging from 60 to 95 per cent copper, o to 50 per cent manganese, and 5 to 40 per cent zinc were investigated. The alloys containing 60 per cent copper were found to fall into the two-phase alpha plus beta region of the system, and since those containing 70 per cent would not permit a saving, only alloys containing 65 per cent copper were considered. The tensile properties of these 65 per cent alloys are plotted in Fig. I as a function of manganese content for annealed material and for four conditions of cold-work In the annealed condition the increases in strength and decreases in elongation are minor up to 15 per cent manganese; beyond this, the changes become more significant. In the cold-worked condition, the first 5 to 10 per cent of manganese appears to have the greatest strengthening effect, the rate of increase dropping off as the manganese increases beyond this amount. These effects are more pronounced with moderate than with severe cold reduction. It is also interesting to note that while the elongation of annealed material drops regularly with increasing manganese, the elongation in the cold-worked state is relatively little affected by increasing manganese content, particu-

Jan 1, 1944

By W. Smith, F. G. Rinker, D. Beggs

Early in 1965 the Surface Combustion Division of the Midland-Ross Corporation was awarded the contract to engineer and construct a taconite pelletizing plant for the National Steel pellet plant, administered by the Hanna Mining Co., near Keewatin, Minn. This plant, which will have an annual capacity of 2,400,000 long tons, will produce pellets from magnetite concentrate using a new process developed through a joint research program by Midland-Ross, Hanna Mining, and the National Steel Corp. The work that culminated in the decision to construct this plant is the result of a research program for the development of the Midland-Ross heat fast process for the production of prereduced or metallized pellets. PELLETIZING PROCESS There are many acceptable methods for producing oxide pellets from ground iron ores and concentrates, and all of these give an acceptable product for blast furnace utilization. The vertical shaft furnace, the traveling grate, and the grate-kiln have been installed in many pelletizing plants in the northern hemisphere; therefore, the acceptance of these methods and the problems associated with them are well understood. However, this research project investigated a method for improving upon these processes to produce a high quality oxide pellet at a low operating cost.

Jan 9, 1966

By Richard Smith

After a brief history of the phosphate industry of Tennessee, the distribution and origin of the phosphate rocks are described. Then the mining and treatment, together with costs of production, and the uses of the rocks are given. THERE are three distinct varieties of phosphate rock, in Tennessee, known commercially as: (a) the "brown" rock, which is the residual product of the weathering and natural concentration of certain phosphatic Ordovician limestones; (b) the "blue" rock, which is an unaltered phosphatic stratum of Mississippian or Devonian age; and (c) the "white" rock, which is the result of chemical replacement and deposition. Before 1894, South Carolina and Florida had supplied most of the phosphate of the United States, South Carolina leading until that date and Florida from then until the present time. In December, 1893, the blue phosphate of Tennessee was discovered almost simultaneously on Swan Creek, in Lewis County, by two independent parties-by one as the result of a careful and systematic search for a workable deposit of the long known kidney phosphate, and by the other through mistaking it for a "bloom" of coal. Leases were taken and, with further prospecting disclosing other deposits in the region, the development progressed as rapidly as could be expected without railroad transportation. In January, 1896, Judge S. Q. Weatherly, who was interested in the development of the blue phosphate, while riding along the road south of Mt. Pleasant, noticed some slabs of a brown rock in place above the limestone. He took samples, and had them analyzed, thus discovering the high-grade brown phosphate of this district. This discovery was kept a secret until July, 1896, when mining was started at the village of Mt.

Jan 9, 1924

By B. J. Kochanowsky

To improve blasting methods it is necessary to know how the explosive force acts and how rock resists this force. Because of the tremendous power developed within milliseconds and the great number of other factors directly affecting the technical and economic results, an analysis of the fundamentals of blasting theory is difficult. But since the rules used for layout design and for calculations of size of explosive charges are based on theoretical assumptions, complete knowledge of blasting theory has great practical importance in mining. Analysis of Blasting Theory: It is interesting to note the opinion of blasting experts with respect to contemporary blasting theories. F. Stussi,' Professor of the University of Zurich, stated: "We do not have enough experience yet to change our army engineering regulations in blasting and base it on new fundamentals. It is our duty to collect more practical data and to do more research in blasting to close this gap." K. H. Fraenkel,' editor of the Manual on Rock Blasting published in 1953 in Sweden and written by well-known Swedish, German, Swiss, and French blasting and explosive experts, said: "To the best of our knowledge no suitable formulas for civil blasting work are to be found in the American, French or German literature."

Sep 1, 1955

By Garth M. Crosby

Hugh E. McKinstry (Professor of Geology, Laboratory of Mining Geology, Harvard University, Cambridge, Mass.) Pre-Cambrian age for the Coeur d'Alene mineralization, as indicated by isotope studies and recently discussed by Silverman, Long, and Kulp' would explain some features of the mineralogy of the district that have long been a puzzle. In the Silver Belt, especially in the Sunshine mine, lead-zinc min erali zation passes downward into tetrahedrite ore. Although commercially speaking this is a rich silver zone, the silver is, quantitatively, a mere impurity amounting to a small fraction of 1 pct. In effect the zonal change is from lead-zinc down into copper mineralization—-the usual zonal change that occurs in many districts. In the Burke-Mullan portion of the district, on the other hand, lead-zinc ore does not pass downward into copper mineralization of the Sunshine type. Instead, pyrrhotite appears in depth while the tenor in lead and zinc declines. The change occurs at increasingly greater depth away from the Gem stocks, deepening irregularly by some 3000 ft within two to four miles. As noted by Crosby, biotite, grunerite, and garnet appear in the deep zone. The marked difference between this apparent zonal change and the more nomal change to a copper zone is quite explainable if already existing pre-Cambrian veins have been locally metamorphosed by a Tertiary intrusive. The chief obstacle to this explanation is the evidence that mineralization cuts Laramide intrusives, but evidence on this point is conflicting as indicated by Crosby's observations and summary. This is not the first instance of a problem in determining the time-relationship of mineralization to a spatially associated intrusive. At the Noranda mine veins of chalcopyrite extend into a diabase dike which apparently cuts the ore, although Price2 concludes that the ore is later. However, at the Normetal mine diabase of a similar dike is thought3 to intrude the orebody but is cut by stringers of chalcopyrite. In the Sullivan Mine, B. C.,4 galena follows a fracture in a larnprophyre dike which, itself, cuts the main orebody. In the Sudbury district dikes of olivine diabase are clearly younger than the nickel ore, yet where they cut the Creighton orebody they contain stringers of chalcopyrite. In the laboratory, Hawley5 has developed veinlets of sulfide (chalcopyrite) it] silicate gangue by heating specimens of ore in a stream of H2S at 410 °C. From this and other evidernce. it seems clear that sulfides can be transferred from one site to another — at least through short distances — at temperatures well below their melting points. It would seem then that even if sulfide Mineralization in the Gem stocks can be shown unequ ivocably to be later than the intrusive the possibility of "remobiliza tion" need not be more than local. Thus the zonal relationships are quite in accord with a pre-Cambrian age for original deposition of the lead, zinc, copper, silver, and uranium in the Coeur d'Alene district. REFERENCES 1. A. Silverman, A. Long, and J. L. Kulp: Discussion of: The Gem Stocks and Adjacent Orebodies, Coeur d'Alene District, Idaho. Mining Engineering, May 1960, pp. 470-471; AME Trans., 1960, vol. 217, p. 117. 2. Peter Price: Geol. & O. D. at the Home Mine, Noranda, Quebec. Can. Inst. M & M Bull 263, 1934, p. 108; also,Trans. CIMM 1939, pp. 108-140. 3. w. L. Brown Nometal Mine in structural Geology of Canadian Ore Deposits, Montreal, 1948, p. 690. 4. C. O. Swanson and H. C. Gunning: Geology of the Sullivan Mine. Can. Inst. Mining & Met. Trans. vol. 48, 1945, p. 653. 5. J. E. Hawley: Heat Effects on Sulphides and Possible Applications. Univ. Toronto Studies, Geol. Ser. No. 46, 1941, p. 34.

Jan 1, 1961

ST. LOUIS SECTION H. A. BUEHLER, Chairman, CHARLES T. ORR, Vice-Chairman., THOMAS T. BREWSTER, Vice-Chairman, L. L. HUTCHISON, Vice-Chairman, W. E. McCOURT, Secretary-Treasurer, Washington University, St. Louis. CHARLES J. ADAMI, EUGENE MCAULIFFE, A. C. TERRILL, JAMES A. CASELTON, JAMES D. ROBERTSON. The annual meeting of the St. Louis Section was held at the St. Louis Club, Saturday evening, Mar. 10, 1917. Philip N. Moore, President, and Bradley Stoughton, Secretary of the Institute, were the guests of the Section. The meeting was preceded by a dinner, at which 70 were present, and was presided over by F. W. DeWolf. Addresses were made by Mr. Moore and Mr. Stoughton. The routine reports of the officers were- presented and the Executive Committee named above was elected for the current year. The special business of the meeting was a report of progress concerning the arrangements for the Institute meeting to be held in the St. Louis Section district, Oct. 8 to 13, 1917. The general program for the meeting met with the cordial approval and cooperation of the members of the Section. It was evident that the members are united in an endeavor to arrange a successful meeting. W. E. McCOURT, Secretary.

Jan 4, 1917

By H. L. Luo

SYSTEMATIC investigations of the Fe-Ga system have been reported only very recently."' The maximum solid solubility of gallium in a-Fe is nearly 50 at. pet at 900°C. However, from Ref. 1, it was not evident that the a-Fe solid solution could be retained successfully beyond 17.38 at. pet Ga by solid-state quenching. The present investigation reports the retention of a-Fe solid solution at 50 at. pet Ga by quenching from the liquid. An ordered phase of CsC1-type B2) structure was observed between 34 - 50 at. pet Ga. Since it was considered very probable that the CsCl structure would occur at high temperatures, alloy filings were also quenched by the conventional quenching technique. In addition to the CsCl phase, a second ordered phase of BiF3-type (DO3) structure was found in the range 25 - 30 at. pet Ga. Alloys were prepared from elements of 99.99 pet purity or better, induction-melted in alumina crucibles under hydrogen. After reweighing, the alloy ingots were cast into wires under argon. From the weight losses and the reproducibility of the lattice parameters, compositions were estimated to be within ± 0.3 at. pet. The techniques of quenching from the liquid state were reported before.3-5 Prior to quenching, a small section of cast alloy wire (30 - 50 mg) was melted in an alumina insert under an argon flow. The quenched specimens were in the form of flakes, typically 1 sq mm in area. For solid-state quenching, alloy filings passing 200 mesh were sealed under a reduced helium atmosphere in a thin-bottom silica tube. After heating for -30 min at the desired temperature in a vertical furnace, the sealed tube was rapidly dropped into ice water so that the thin bottom of the tube broke on impact. The quenched alloy filings were always ferromagnetic and could be collected by a magnet. X-ray diffraction patterns were taken with iron-filtered cobalt radiation in a 114.6-mm-diam Debye-Scherrer camera. High-angle lines were always resolved and spacings were computed relative to ? (CoKa1) = 1.78890Å. Lattice parameters were obtained from extrapolation against the Nelson-Riley function. The variation of lattice parameter with composition is shown in Fig. 1, together with the data of Dasarathy and Hume-Rothery.1 Uncertainties in the present measurements are within the dimensions of the symbols or indicated by error bars. X-ray diffraction lines indicative of CsC1-type ordering could be clearly identified for alloys of 34 - 50 at. pet Ga quenched from the liquid and alloys of 35 - 41 at. pet Ga quenched from -975°C. Within experimental error, no difference in

Jan 1, 1968

At 8 o'clock on the evening of Thursday, July 25th, the special train chartered by the Provincial Government for the Institute's use, pulled out of Toronto. Ten parlor cars and two dining cars made up the train. The culinary arrangements were under the personal supervision of Mr. McConkey, of Toronto. [ ] The Hon. Frank Cochrane, Minister of Mines, Lands and Forests, was the efficient host of the party. He was assisted by the Hon. Dr. Pyne, Minister of Education, and by Mr. T. W. Gibson and Dr. W. G. Miller. On arriving at Cobalt, the delegates were met by the following Committee Mr. A. A. Cole, representing the T. & N. 0. Railway; Messrs. R. W. Leonard and D. B. Rochester, deputies from the Cobalt Chamber of Mines ; Messrs. Run¬ning and Martin, from the Cobalt City Council; Messrs. McLeod and Ferland,

Jan 1, 1907

By C. E. Sims, H. M. Banta, S. L. Hoyt

OVER the past few years, metallic arc welding has been extended to steels of the hardenable type. As compared with other methods of fabrication, production has been facilitated, service performance frequently has been improved, and the overall results have been so favorable that engineers and production men have placed great emphasis on this application of welding. The metallurgist and welding engineer, however, have been confronted with new problems, since, for one reason, the harder steels are more apt to crack and special precautions must be taken if sound joints are to be procured. Some of the factors that are pertinent to this problem are metallurgical, and it is an object of this contribution to discuss steel manufacture and processing methods and to show how their control assists in reducing the hazard of cracking. By this time, the problem of cracking specifically underbead cracking, or "hard cracks," or parent-metal cracks-is well known, and a large amount of work has been published, both here and abroad, dealing with this subject.1 The tests described are made under restraint to facilitate cracking and, are so designed that a semiquantitative, or at least a relative, value of the cracking tendency is obtained. As one would expect, it has been reported that the incidence of cracking increases with the carbon and alloy content of the steel. More specifically, the cracking tendency is said to increase with the hardenability of the steel, though it is now recognized that the situation is not so simple. The phenomenon itself, on the other hand, has been but loosely described, and it is in only broad generalizations that this cracking has been related to steel metallurgy. Thus, while it has been abundantly demonstrated that the hardenable aircraft steel, S.A.E. 4130, must tend to crack when arc-welded, the problem still remains of why two lots of the same composition and the same hardenability can vary so greatly in cracking tendency, or what it is about the prior metallurgical history that so strongly affects the results. Further, while the efficacy of preheating and postheating in preventing cracking is recognized and utilized in production, the mechanism by which they function seems not to have been described. These points are thought to be significant in the production of steel for fabrication by metallic arc welding and, hence, of interest to mill and process metallurgists and welding engineers. Consequently, it is another object of this paper to discuss the mechanism of parent-metal cracking, including the influence of the condition of the steel and the control of cracking by manipulation of the time-temperature conditions during and after welding. A new method of rating the cracking. tendency is also discussed, and the results of the test are related to steel composition and structure or prior history. The work to be described was the outgrowth of work in 1940-41 at Battelle Memorial Institute 0n two projects, one

Jan 1, 1945