By A. B. Kinzel

ALTHOUGH the iron-carbon diagram has undergone many changes in the last 20 years, the region below the eutectoid line and up to approxi-mately 1.7 per cent carbon has been little affected. This region is generally considered to consist of cementite and ferrite. Graphite has been noted occasionally in the hypereutectoid steel region, and the ready formation of graphite nodules in malleable cast iron is a phenomenon difficult to interpret in the light of cementite, supposedly stable at sub-eutectoid temperatures. In this case the graphite formation has been partly explained by the presence of silicon, and many have believed that silicon acts to change the stable state rather than to accelerate reactions so as to arrive at the stable state in a briefer period of time. Consider-ation of this phenomenon indicates that cementite is not the stable phase in the temperature composition zone referred to. In the course of examining a low-carbon steel tube taken from a petroleum cracking still, which had been in service for approximately three years at temperatures somewhat below the eutectoid temperature, observations were made that shed light on this entire subject. The tube in question analyzed:1 C, 0.15 per cent; Mn, 0.49; Si, 0.02; S, 0.023; P, 0.015. The microstructure of the tube after service is shown in Figs. 1 and 2. From these it is evident that cementite as such is absent, and that in its place nodular graphite has been formed. In order to check this observation further, samples taken from the tube were heated at 850° C. for varying periods of time. The small samples were put into a large hot furnace, and the total time is recorded. The structure of the

Jan 1, 1934

By St. John, JOHN Ancel

AT THE New York meeting of the Institute of Metals Division in February, 1927, Jeffries and Tarasov presented a paper on Tungsten and Thoria,1 in which the experimental facts were interpreted in accordance with the prevailing point of view that the thorium is present as the oxide, thoria. In discussing that paper the writer of this article stated that his own investigations, which had been unavailable to Messrs. Jeffries and Tarasov, showed that the so-called "thoriated" tungsten filament failed to disclose any sign of the oxide when subjected to X-ray diffraction analysis, but did give plenty of evidence of the presence of metallic thorium and, in certain cases, of a material believed to bean alloy of tungsten in thorium. Since these results were completely at variance with the results reported in the paper under discussion and with other papers which had preceded it from time to time in the past, it was felt that further discussion should be withheld until the new evidence could be presented adequately. Arrangements were therefore made to present that evidence at this meeting. MATERIAL EXAMINED The material examined was high-emission filament such as is used in radio tubes, supposed to contain about 0.75 per cent. thoria. The actual analysis was not stated.

Jan 1, 1927

By Earl Oliver

SEVERAL notable papers, and free discussion on many controversial subjects, marked the various sessions of the Petroleum Division at the annual meeting. The Division first convened on Tuesday afternoon, Feb. 16, and wound up with a dinner and technical meeting on Thursday night. H. C. Fowler presided at the opening session, which was devoted to problems of engineering research and production engineering. Joseph Chalmers abstracted his paper on the flow of air and gas through porous media, in the preparation of which E. L Rawlins and D. B. Talia-ferro contributed. G. H. Fancher told how much he and his associates at Pennsylvania State College were interested in this field, and described the problems they had met in conducting test work. He made a plea for standardization of testing methods. Mr. Fowler then read an abstract of written discussion by Professor Barb, which was followed by discussion by Dr. Fancher and Mr. Chalmers of technical points in connection with the Chalmers' paper. H. H. Hill abstracted written discussion from Messrs. Wilde and Moore, of the Humble company. The second paper, by K. B. Nowels, on computing pressure drop in the pipe of flowing oil wells, was abstracted by the author. Messrs. Blair Smith, G. W. Coggeshall, and I. I. Gardescu participated in the discussion, and the chairman abstracted written discussion prepared by Mr. Rawlins. Most of this had to do with the viscosity of gas¬oil mixtures, on which subject Mr. Nowels said there was great need of accurate technical information.

Jan 1, 1932

Jan 1, 1915

By L. F. Mondolfo

R301 is a clad aluminum alloy, composed of a core of a duralumin-type alloy clad with a magnesium silicide alloy. It differs from other well-known clad alloys in that the cladding and the core respond to the same heat-treatments. and therefore the cladding contributes appreciably to the mechanical properties of the material. In Table I are reported the compositions of the core and cladding alloy for the material used for the experiments. Table i.—Chemical composition of R~OI Used for the Experiments Element Core Cladding Cu........................ . 0.01 Fe......................... . 0.42 Si......................... 0. 0.71 Mg........................ . 0.99 Mn ........................ . 0.54 In clad aluminum alloys where the core contains copper and the cladding does not, at elevated temperatures the copper tends to diffuse from the core through the cladding. This fact is well known and many investigations have been conducted to determine the features of this diffusion. Most of those investigations cover materials clad with pure aluminum; the present investigation covers a material clad with an alloy. Since the cladding thickness on R~OI varies with the gauge, as shown in Table 2, several gauges were investigated. Material and Procedure he material used was sheet of the following gauges: o.o2~, 0.040, 0.064, 0.102, 0.170 Cut in pieces approximately 3 by 5 in., it was in the cold-rolled state and was soaked for increasing times at the following temperatures: glo°F., 940°F., 970°F. A Lindberg cyclone furnace was used for the experiments. The procedure was as follows: The furnace was started empty with controlling pyrometer set at the determined temperature. After the furnace had reached that temperature, it was run for some 20 to 30 min. empty, in order to allow the temperature inside to become stabilized. Then the first samples were introduced. A load thermocouple, with recording pyrometer, was connected with the sample of the heaviest gauge. About 10 min. was required for the material to reach temperature and the soaking time was counted from that point. After zoo min. soaking, the second group of samples was introduced without stopping the furnace. After 200 min. more, the third group of samples was introduced, and so on, until the last sample had been introduced. Every time the furnace was opened and new samples were added, a drop of temperature was registered by the thermocouple connected with the material

Jan 1, 1946

By L. F. Mondolfo

R301 is a clad aluminum alloy, composed of a core of a duralumin-type alloy clad with a magnesium silicide alloy. It differs from other well-known clad alloys in that the cladding and the core respond to the same heat-treatments. and therefore the cladding contributes appreciably to the mechanical properties of the material. In Table I are reported the compositions of the core and cladding alloy for the material used for the experiments. Table i.—Chemical composition of R~OI Used for the Experiments Element Core Cladding Cu........................ . 0.01 Fe......................... . 0.42 Si......................... 0. 0.71 Mg........................ . 0.99 Mn ........................ . 0.54 In clad aluminum alloys where the core contains copper and the cladding does not, at elevated temperatures the copper tends to diffuse from the core through the cladding. This fact is well known and many investigations have been conducted to determine the features of this diffusion. Most of those investigations cover materials clad with pure aluminum; the present investigation covers a material clad with an alloy. Since the cladding thickness on R~OI varies with the gauge, as shown in Table 2, several gauges were investigated. Material and Procedure he material used was sheet of the following gauges: o.o2~, 0.040, 0.064, 0.102, 0.170 Cut in pieces approximately 3 by 5 in., it was in the cold-rolled state and was soaked for increasing times at the following temperatures: glo°F., 940°F., 970°F. A Lindberg cyclone furnace was used for the experiments. The procedure was as follows: The furnace was started empty with controlling pyrometer set at the determined temperature. After the furnace had reached that temperature, it was run for some 20 to 30 min. empty, in order to allow the temperature inside to become stabilized. Then the first samples were introduced. A load thermocouple, with recording pyrometer, was connected with the sample of the heaviest gauge. About 10 min. was required for the material to reach temperature and the soaking time was counted from that point. After zoo min. soaking, the second group of samples was introduced without stopping the furnace. After 200 min. more, the third group of samples was introduced, and so on, until the last sample had been introduced. Every time the furnace was opened and new samples were added, a drop of temperature was registered by the thermocouple connected with the material

Jan 1, 1946

By R. W. Raymond

(Chattanooga Meeting, October, 1908.) THE immense commercial value of the Gayley dry-blast process has been established beyond controversy. The testimony of practical blast-furnace managers, on both sides of the Atlantic, agrees that it reduces the cost of pig-iron about $1 per ton; but from the same testimony it appears that this direct economy does not by any means cover its commercial advantages-in fact, that under conditions frequently encountered in practice, it presents other benefits of even greater immediate financial importance. To this point I shall recur in a later part of the present paper. The history of the reception given to this invention, especially on the other side of the Atlantic, has repeated an experience familiar to American engineers. First, the reports of our practice were rejected as theoretically impossible, according to generally accepted notions and formulas; then the figures were reluctantly accepted ; and finally the attempt has been made to explain how they could have been obtained. As to the Gayley dry blast, we Americans have been for several years in the last stage of the discussion, and the rest of the professional world is rapidly coming to it. Meanwhile, the remark has been repeatedly made that, whatever Mr. Gayley's process may turn out to be worth, it was not an invention on his part, but simply the energetic and persevering execution of a procedure already proposed by others. This question I wish to discuss first in the present paper. I. WHAT DID MR. GAYLEY INVENT Realizing that this is not the place for detailed argument on an issue of patent law, I shall not undertake to quote and criticise the publications prior to Mr. Gayley's first patents. It may be admitted, without such critical analysis, that the possi-

Jan 1, 1909

By J. L. Moriarty, Irving Johnson, H. M. Feder

The crystallization of ternary alloys has been studied as a coprecipitation phenomenon by measuring the substitutional carrying of trace metals with CeCd11 precipitating from liquid cadmium. The Doerner-Hoskins logarithmic distribution law has been found to apply in all cases; the coprecipitation coefficients obtained were: 1.48 (La), 1.06 (Th), 0.63 (Pr), 0.24 (Gd), 0.17 (Sm), 0.13 (U), 0.10 (Er), 0.09 (Sr). Li, Na, K, Ba, Y, Sc, and Zr were not measurably carried. It has been observed that coprecipitation was most extensive for those tracers which form with cadmium an intermetallic compmdnd isostructural with CeCd11 or closely related thereto. For these tracers an inverse relation between Solubility in cadmium and coprecipitation coefficient was noted. THE partition of impurities between the liquid and solid phases of a metal or a congruently melting intermetallic compound has been extensively studied by the methods of zone melting.' However, when the composition of a liquid alloy and of the solid phase crystallizing from it differ grossly, partition of an impurity cannot be investigated in this manner. Partition of the impurity under equilibrium conditions may be studied by investigation of the appropriate phase diagram and partition under nonequi-librium conditions may be studied by observation of coring in the solidified alloys.2 The nonequilibrium case is of special interest in metallurgical practice because many complex alloys are cooled too rapidly to permit the uniform diffusion of impurities throughout the crystallizing phase(s). With this in mind, the present study was undertaken to obtain quantitative data on the phenomenon of coprecipitation via substitutional solid solution in certain metallic systems. It will be noticed that rather than adopting metallurgical ter- minology we have chosen to refer to the partition of impurities during alloy crystallization as coprecipitation.3 In the terminology of coprecipitation the impurity is referred to as the tracer and the precipitating phase as the carrier. From aqueous solution, coprecipitation may occur as a result of adsorption on the surface of the carrier, by occlusion of the liquid within the crystals, or by solid solution of the tracer in the carrier. By slow cooling of liquid metallic solutions it is relatively easy to form large, regular crystals of the carrier; the effects of adsorption and occlusion may be minimized and the influence of substitutional solid-solution formation may be made to predominate. Previous studies of the crystallization of some intermetallic compounds4 and of copper, silver, and gold5 have shown that the coprecipitation or partition behavior of trace metals is entirely analogous to that observed in aqueous systems when ionic substitution occurs, e.g., coprecipitation of Ra++ with BaSo4. The precipitation of CeCd11 from liquid cadmium was chosen for study. This choice was influenced by the following consideration. If the relative atomic sizes of the tracer atom and the atom for which it substitutes determine the tendency to coprecipi-tate, then a lattice having a substitutional site of well-defined size would be desirable. In CeCd116 (structure type cubic BaHg117) the cerium atom is completely surrounded by a cage of twelve nearly equidistant cadmium atoms. Thus, atoms much larger or much smaller than cerium should be poorly accommodated in this cage. The choice of a lanthanide central atom allowed the testing of the size hypothesis with a number of lanthanide tracers which differed in size but not in valence or electro-negativity. EXPERIMENTAL The general technique of this investigation was to prepare a slightly undersaturated solution of carrier in liquid cadmium to which a tracer was added. The concentration of tracer was always so low that saturation over the entire temperature range investigated was never exceeded. The solution was cooled in a stepwise fashion. After each step a por-

Jan 1, 1964

By R. W. Raymond

After the publication of the Atlanta paper of Mr. Robert W. Hunt on " Specifications for Steel Rails of Heavy Sections Manufactured West of the Alleghenies,"* I received from Mr. B. F. Fackenthal, Jr., the following comments: "I note that, in giving the chemical composition of rails, Mr. Hunt does not consider the question of copper. Yet we all know very well that its presence is more or less injurious, as it tends to red-shortness. Bessemer pig-iron carrying

Jan 1, 1897

By James Johnston

Synopsis.—A description of the working of the mills of this company and the metallurgical practice in vogue, by which a remarkably complex silver ore, averaging 54 oz. of silver per ton (run-of-mine ore), is treated to give a 95.66 per cent. extraction. The main features of the processes are: The cyanide amalgamation of the high-grade ore. The cyanide treatment of the low-grade ore, after extremely fine grinding and close classification, in a caustic soda solution. The use of a wet desulphurizing process to break up refractory silver minerals. The substitution of aluminum dust for zinc dust as a precipitant. The recovery and shipment of over 13,000,000 oz. of silver in bullion at 997 to 999 fine since this metallurgy was inaugurated, about 2.5 years ago. On the completion and successful operation of the mill to treat their high-grade ore,' the Nipissing Mining Co., under the general management of R. B. Watson, started a series of investigations of the possible treatment of the low-grade ore by the cyanide process, so that they would be in a position to market only silver bullion. These tests were run in July, 1911, on a large scale, by G. H. Clevenger, on an average mixture of Nipissing ore. The results obtained by a partiai amalgamation followed by cyanide treatment gave an extraction varying from 90 to 93 per cent. and were sufficiently encouraging to warrant Charles Butters, the company's Consulting Metallurgist, in recommending that the new low-grade ore mill under contemplation should be a cyanide mill, instead of a concentrator. The cost of such a mill, capable of treating 200 tons per day, to obtain a 90 per cent. extraction at a working cost of $3 per ton of ore treated, was estimated at $250,000. In coming to a decision as to which type of mill should be erected, the concentrator, with the subsequent shipping of concentrates to a smeltery,

Jan 1, 1915

Mining Methods J. HURRAY RIDDELL,Chariman Guy N. BJORGE, Vice- Chairnan ROLAND D. BANKS, Secretary Alluvial Mining CLINTON BERNARD O. B. PERRY BENERE H. GRANT C. M. ROMANOWITZ Open-Cut Mining Iron G. E. DIERL P. G. HARRISON EARL E. HUNNER

Jan 1, 1939

THE Institute of Metals Division of the A. I. M. E. has joined with the American Society for Steel Treating and the American Welding Society in support of National Metal Week in Philadelphia, Oct. 8 to 12. Individual and joint technical sessions, plant inspection trips, and a general exposition to be held in Commercial Museum have all been arranged. With the coming of the Institute of Metals Division into the circle, the scope of the exposition has been broadened to cover non-ferrous metals, and exhibits of much interest are promised. Headquarters for the Institute of Metals and the American Society for Steel Treating will be at the Benjamin Franklin Hotel, and for the American Welding Society at the Bellevue-Stratford. The American Society for Steel Treating and the Welding Society will hold technical sessions each forenoon at their hotel headquarters. The Institute of Metals Division will hold sessions Tuesday morning and Wednesday and Thursday afternoons; that for Wednesday being a joint session with the American Society for Steel Treating. The latter society will hold independent afternoon sessions on Thursday and Friday. Registration and information desks will be open at the hotels throughout the week, and an attractive program of entertainments has been arranged.

Jan 1, 1928

By R. W. Diamond

THREE mills are now operated by the Consolidated Mining & Smelting Co. of Canada, Ltd.: (1) The Sullivan Concentrator, Chapman Camp, B. C. (near Kimberley, B. C.), (2) the, St. Eugene Concentrator, Moyie, B. C., and (3) the. Tadanac (Customs) Concentrator,Trail, B. C. Differential flotation is the only concentration method employed in all three plants. Tables are used for pilot work only. Values in all ores treated are as minerals of some or all of the metals -lead, zinc, gold or silver. Occasional customs ores contain small amounts of copper. Sulfide iron content of ores treated varies from a FIG. 1.-THE SULLIVAN CONCENTRATOR, CHAPMAN CAMP, B. C. (NEAR KIMBERLEY, B. C.). low figure in some ores to 38 per cent. iron in Sullivan ore. Gangue minerals vary considerably. A few customs ores are somewhat oxidized and as a result present difficulties. Flotation equipment and control are similar in the three mills, and the flow sheets at the St. Eugene and Tadanac mills, while much simpler, are modeled after that of the Sullivan Concentrator. In this paper I will not detail treatment nor equipment in any of our plants but will describe special features in, or in connection with, all of them. I will then deal with flotation reagents, describing our use of each of them, particularly where differing from general practice. I will conclude with comments on special subjects related to differential-flotation.

Jan 1, 1927

By Klaus Detert, Joseph Ziebs

The progress of primary recrystallization has been studied in alloys of nickel with 0.01, 0.1, and 1.0 at. pct Ta. It can be shown that in one particular alloy containing 0.1 Ta and 0.02 02 a large grain structure (0.5 mm diameter) could he developed by primary recrystallization in thin sheetswhich were cold-worked to 97.5 pct reduction in thickness. Electron transmission microscopy demmstrates that this phenonmena was linked to the occurrence of fine precipitates at subboundaries. A discussion of how fine precipitates can exert under certain circumstances a rather distinct retarding effect on nucleation rate is included. IN a former investigation, the recrystallization and texture formation in a series of binary nickel alloys including pure nickel were studied.' Nickel alloys with some tantalum added displayed peculiarities during primary recrystallization which have been studied in more detail by the present investigation. The alloys were prepared by powder-metallurgy techniques similar to the previous investigations.' Pure metal powders were thoroughly mixed to obtain alloys with 0.01, 0.1, and 1.0 at. pct Ta, referred to as alloy A, B, or C, respectively. The metallic impurities were kept below 0.005 at. pct except iron and cobalt with slightly higher values, by using highly purified nickel and tantalum powders.' The mixtures were pressed into bars and sintered at a temperature of 1300°C. The sintering atmosphere was either high vacuum, dry hydrogen, or wet hydrogen. The sintered rectangular bars were rolled 60 pct to a thickness of 3 mm, then annealed under dry hydrogen at 1000°C and again cold-rolled to about 97.5 pct reduction of thickness. After this heavy deformation, the sheet thickness was 0.07 5 mm. In order to study primary recrystallization which occurred in measurable times between 400" and 600°C, samples of the rolled sheets were annealed in a salt bath at various temperatures for various times in order to study the progress of recrystallization by hardness measurements and microscopic examination. For optical observation, the samples were polished and etched in a solution of 65 cu cm HNO3, and 18 cu cm acetic acid in 20 to 100 cu cm H2O, depending of the particular sample and annealing treatment. For transmission electron microscopic observations, thin foils were prepared by the combined window and Bollmann techniques.273 The electrolyte consisted of 23 pct perchloric acid and 77 pct acetic acid held at 15°C. Polishing was performed at a current density of 0.4 amp per sq cm. The examination of the thin films was accomplished by a Siemens Elmiscope-type electron microscope operating with an accelerating voltage of 100 kv. RESULTS The progress of primary recrystallization was very accurately followed in these alloys in order to establish the time when recrystallization started and ended during an isothermal anneal. Table I gives some of the data obtained by these studies. The time for beginning is a mean value, where somewhat less than 5 pct of the matrix has recrys-tallized. The end of recrystallization is the time when at least 95 pct of the matrix has recrystal-lized. Listed are three different B alloys, with 0.1 Ta distinguished by different sintering atmospheres which influence the rate of primary recrystallization. By the above method, the state of the grain structure when primary recrystallization was completed, but grain coarsening had not started, could be clearly defined. The average grain diameter of the recrystallized matrix is also given in Table I. The grain size did not depend on the temperature of the isothermal anneal. With one exception the grain size of the primary recrystallized matrix was found to be rather fine

Jan 1, 1965

By W. P. Sykes

THIS investigation was undertaken primarily to establish the relations existing between temperature and mechanical properties in molybdenum, nickel, and an aluminum-copper alloy. Molybdenum (m.p. 2500° C.) was chosen because it is partly similar to tungsten and partly similar to the common ductile metals. Also it is known to furnish, by proper treatment, a desirable material to use in studying relation of grain size and physical properties. The molybdenum used was of the quality that is drawn into wire 0.003 in. in diameter for use as filament supports in incandescent lamps; chemical analysis shows less than 0.1 per cent. of impurities. Nickel belongs to the same class as iron. Its melting point is 1450° C. and an allotropic change at about 370° C. results in a loss of magnetism above that temperature. This feature made nickel doubly valuable for the purposes of these tests. The nickel used was obtained from the Driver-Harris Co. as 0.090 in. (2.3-mm.) wire, annealed; analysis showed 99.8 per cent. nickel and 0.150 per cent. iron. Aluminum is one of the low melting-point metals. Some tensile tests at elevated temperatures have been reported by Bengough but the possibility of learning more with the low temperature and sensitive apparatus available recommended this metal. The samples marked Al are an aluminum-copper alloy; they contained 3 per cent. copper, 0.42 per cent. iron, and 0.21 per cent. silicon. The presence of the copper somewhat complicates the analysis of the results; but the action of copper in aluminum has been studied so that its influence might have been foretold, in part at least. The material and analyses were furnished by the Aluminum Castings Co. The nickel wire, which was deformed at 400° C., was drawn under a bath of molten lead and through a die, which also was immersed in the bath. A thermocouple was suspended in the molten metal to indicate

Jan 1, 1921

By AIME AIME

The Following List Comprises The Names Of Those Persons Elected As Members Or Associates, Who Accepted Election During May And June, 1908 MEMBERS. William H. Bainbridge Searchlight, Nev. William N. Brown, . Gainesville, Va. Willis S. Caypless, .. . . . . Denver, Colo. William B. Clark, Baltimore, Md.

Jan 7, 1908

Univ of Alabama-University, Alabama-Mining and Metallurgical Society William L Mason, Faculty Sponsor, E C Wright, Dept Head Univ of Alaska-College, Alaska-Mining Society of the Univ of Alaska Douglas W Huber, Faculty Sponsor, E H Beistline, Mining & Metallurgy Dept Head, Troy L Pewe, Geology Dept Head, James Crawford, Chapter Counselor Univ of Arizona-Tucson, Arizona-Miners Society Willard C Lacy, Faculty Sponsor, J D Forrester, Mining & Metallurgy Dept Head, F W Galbraith, Geology Dept Head Univ of California-Berkeley, California-Mineral Technology Association H E Hawkes, Faculty Sponsor, Joseph A Pask, Dept Head

Jan 1, 1959

By H. S. Martin

The Phosphate Recovery Corporation operates three flotation plants, NOS. 1 and 2 concentrators about three miles northeast of Mulberry, Florida, and No. 3 plant at Wales, Tennessee. These plants represent the first commercial phosphate flotation operation and are also believed to be the largest nonmetallic flotation operation in the world at the present time. The details of this paper will be confined to plant No. 2, this being the newest and largest concentrator in Florida, and the flow sheet being practically the same as at plant No. 1. The No. 3 plant has been operated but a short time and has been shut down since December, 1932, on account of the decrease in phosphate rock production. The phosphate washers usually are located centrally on a known deposit so that about two hundred acres of ground can be mined economically to each washer location. The washers are moved to new areas when the distance becomes too great for economical pumping. The flotation plants are built either adjacent to a washer, so that current debris may be utilized, or on the site of a former washer where there is sufficient accumulated debris available for mining, and the flotation plants must also be moved from time to time. Most of the water used in the Florida flotation plants is recovered after passing through a circulating system where most of the fine SUSpended matter is settled out, but some make-up water is obtained from deep wells near the plant. Power is obtained from the Tampa Electric Co. through the distribution facilities of the International Agricultural Corporation. Flotation concentrate is hauled from the plant by trolley over the International Agricultural Corporation's trolley system, to the drying plant at Prairie, one mile northwest of Mulberry. Ore Treated In the pebble phosphate district of Florida, the phosphate mineral, or collophane, is usually found in horizontal beds of varying thickness

Jan 1, 1934

[Univ. of Atabama-University, Alabama-Mining and Metallurgical Society. William L. Mason, Faculty Sponsor; E. C. Wright, Dept. Head. Univ. of Alaska-College, Alaska-Mining Society of the Univ. of Alaska. Douglas W. Huber, Faculty Sponsor; E. H. Beistline, Mining & Metallurgy Dept. Head; Troy L. Pewe, Geology Dept. Head; James Crawford, Chapter Counselor. Univ. of Arizona-Tucson, Arizona-Miners Society. Wiltard C. Lacy, Faculty Sponsor; J. D. Forrester, Mining & Metallurgy Dept. Head; F. W. Galbraith, Geology Dept. Head. Univ. of Catifornia-Berkeley, California-Mineral Technology Association. H. E. Hawkes; Faculty Sponsor; Joseph A: Pask, Dept. Head.]

Jan 1, 1961

By F. C. Farnham

THERE has been very little, if any, uniformity in the reference datum used for magnetometer surveys. It has been the practice to choose a base station at which the magnetic field is assumed to be normal and call the difference in field strength between a given station and this base the anomaly at the given station. For small-scale surveys latitude and longitude corrections may or may not be applied, but for large-scale surveys such corrections usually are applied. The United States Coast and Geodetic Survey maps showing lines of equal magnetic intensity are commonly used to determine the normal latitude and longitude variation by scaling values from the map for given points and computing the change per mile north and the change per mile east. This method has been quite satisfactory for isolated surveys, but when two surveys originating at different base stations were extended until they joined, difficulty arose, not only because of discrepancies between base-station values, but also because of differences between the latitude and longitude correction factors used for the separate surveys. It is the purpose of this paper to describe a reference datum for magnetometer surveys which, it is believed, will eliminate most of the difficulty arising from this source. In order to be satisfactory, a general datum for magnetometer sur-veys should be as close as possible to the observed field and still he based on some assumed distribution of magnet poles, in order that the "normal" value of any component of the field for any given point may be computed to as many significant figures as desired. Such a field has been com-puted, and a comparison of the intensity of its vertical component with the average vertical intensity for the United States as shown by the U.S.C.G.S. map of lines of equal intensity for 1935 is shown in Fig. 1.

Jan 1, 1939