By Jorge Alberto Soares Tenório, Amilton Barbosa Botelho Jr, Denise Crocce Romano Espinosa, Mónica M. Jiménez Correa

Wastewater from nickel lateritic process still has valuable metals that could be recovered. Using an ion exchange to recovery these metals, the iron becomes a problem due to the fact that it precipitate at pH 2. The aim of this research was to make iron soluble by reducing Fe+3 to Fe+2. A synthetic solution was prepared with sulfate ferric. The reducing agent sodium dithionite was used and the potential was varied (initial potential: 700, 600, 500, 450 e 400 mV) using as a reference the Pourbaix diagram for iron created by HydroMedusa software. The pH was ranged between 0.5 and 2.5, the reducing agent’s concentration was 0.5 M and the reaction time ranged between 30 and 120 min at room temperature. The ferric iron and total iron concentration were verified using a spectrophotometer with 5-sulfosalicylic acid (SSA) to determine Fe(III) and ammonia to determine Fe(II) and Fe(III) in 500 and 425 nm, respectively. The results indicated that total reduction was at 400 mV in any pH between 0.5 and 2, but less than 40% in pH 2.5 at this potential value.

Mar 1, 2017

By Zhong g. Shui-ping

A new type Pb-Ag (0.8wt%)-Bi (0~5.0wt %) alloy used as anode in electrowinning of zinc from sulphuric acid electrolytes was prepared. The electrochemical properties of this ternary lead alloys have been tested and compared with those of Pb-Ag (0.8wt %) anodes used in industry. Results show the anodic overpotential decreases with the increasing of Bi content in the alloys. When the content of Bi was 1.0 wt% and 5.0 wt%, the anodic overpotential is about 40?50 mV and 60?80 mV lower than that of Pb-Ag (0.8wt %) alloy, respectively. The formation of oxide layers on the surface of these alloys was traced by LSV methods and the composition of the anodic oxide layers was characterized by XRD and SEM analysis. The surface layer on the two type anodes examined is mainly composed of a?PbO2 and ß?PbO2. But different structure of the surface layer was observed, Pb-Ag (0.8wt%)-Bi (1.0wt %) has a more fine-grained structure as compared to Pb-Ag (0.8wt %). But the film on Pb-Ag (0.8wt%)-Bi (3.0wt %) alloy is rather friable, cracked and not tightly attached to the anode.

Jan 1, 2008

By Francis C. Furman

Microscopic evidence indicates that the high sinterability of certain commercial dolomites is tied to specific dolomite textural characteristics. This study encompasses detailed characterization of the unprocessed dolomite and sintering doloma results. The chemical and mineralogical compositions, insoluble residue, chemistry homogeneity, crystal size, primary carbonate texture, secondary dolomite texture, deformation structure, porosity type, porosity, and density of the raw dolomite were observed. These characteristics are compared with sintering trials of <74um powder-compacts samples in which holding times were varied. The evolution of the dolomite characteristics are reviewed and related to the final sintered doloma characteristics. The critical characteristics of a single-stage sintering brick dolomite are the following: 1) primary oolitic texture, 2) dolomite purity, 3) dolomite stoichiometry 4) minimal impurities, less than 1 weight {%} Fe2O3 Al2O3 and SiO2, 5) chemical homogeneity, 6) high density, 7) very low porosity, S) very coarse homogeneous crystallinity, 9) nonplanar dolomite texture, 10) abundant strain related slip microdeformation structures, 11) minimal subsequent alteration. Even with grinding to <74um the nonplanar dolomite texture and slip deformation still have a major effect on doloma sintered density. The three newly identified characteristics of single-stage sintered refractory brick dolomite are their primary oolitic texture, secondary nonplanar texture and abundance of stress related microdeformation structures. The primary oolitic texture reflects a homogeneous pure carbonate with respect to chemistry and crystal size secondary nonplanar texture produces crystals with large surface area to volume ratio. Stress related slip deformation moves CO, groups in to the same site of another CO, group but different orientation which is very unstable. All of these characteristics may facilitate the formation of higher density dolorna sinters.

Jan 1, 1995

By Aïda Espinola

Decontamination of synthetic solutions containing cadmium ions using coconut fibers in natura was investigated in laboratory scale. Cadmium ions, a serious pollutant of water ways, where it is detrimental to the environment, may be absorbed by fish and mollusk used as food, which will, eventually, poison humans; these ions are usually present in minero-metallurgical and electroplating industrial effluents. Usually employed for the aqueous effluents treatment are chemical precipitation, adsorption and electrolytic processes. Precipitation is not effective for cadmium removal, because of the high KpS of the cadmium hydroxide, which requires high pH; only sulfide would be efficient in cases of very small amounts. Some vegetal refuses have shown to be practical for absorption processes of several metallic ions. We have applied coconut (Cocos nucifera) shells, which are extremely abundant over most of the extensive Brazilian coast, in the removal of cadmium: it has been verified, in our laboratory, that the surface of the fiber of this coconut is rich in chemical compounds which are active scavengers for Cd2+. For the optimization of the process, hydrosoluble components existing on the surface of the fiber, which may be deleterious, were previously washed out by water, and variables, such as the pH and the proportion of mass of fiber to volume of solution, were adjusted. As much as 99% of the initial contaminant metallic ion has been eliminated, resulting a solution to be discarded which contains ca. 0.1 ppm; this attends to the maximum impurity legally admitted by the environmental control agency of Rio de Janeiro, FEEMA, for cadmium ions in aqueous effluents to be disposed in rivers and in the Guanabara Bay area.

Jan 1, 1998

By S. G. Kumar, R. G. Reddy

"Niobium aluminides offer the advantage of higher high temperature capability compared to other intermetallic aluminides due to the refractory nature of niobium. However, the reaction sequence in Nb-Al system is sluggish and currently there is a great interest in the processing aspects of these materials. In the present study, a systematic investigation was undertaken to compare the effect of different powder metallurgy processing routes on the phase relations and microstructure of 66Nb-22AH2Ti (in atom percent) alloy. The three different process routes adopted were: (i) cold pressing followed by reaction sintering; (ii) cold pressing and hot pressing followed by sintering; and (iii) arc melting, hydride-dehydride process to make the alloy powder followed by cold pressing and then sintering. The samples are analyzed by XRD, Optical Microscopy, SEM-EDS and EPMA. The analysis showed that alloy pellets made from pre-alloyed powders i.e., arc melting followed by hydride-dehydride process, gave good densification and more Nb3Al formation.1. IntroductionTo improve the performance standards of turbine engines, materials scientists are challenged to develop materials that have· high thrust-to-weight ratio with high specific strength, high specific modulus and good environmental properties at elevated temperatures. The conventional high temperature materials like nickel based superalloys are high in density and hence many of the high temperature materials scientists have focussed their attention on intermetallic aluminides like Fe-AI, Nb-AI, Ni-AI and Ti-AI in recent years. The phase relations and properties of alloys based on Fe-AI, Ni-AI and Ti-AI are fairly well known whereas little is known about the alloys based on niobium aluminides."

Jan 1, 1996

By J. Murdoch Mackenzie

Two commercial nickel solvent extraction plants treating laterite leach solutions and using LIX®84-I have been operated in Australia. These circuits employ similar extraction chemistry but differ in their leaching and stripping operations. An alternative process involving elements of both can be conceived. The preparation of the feed solution to solvent extraction plays an important role in nickel extraction using LIX®84-I and the special features of manganese removal and cobalt oxidation in the preparation of the PLS are discussed. This paper compares these three circuit configurations with special reference to the extraction and reductive stripping of cobalt, the transfer of zinc and copper to the strip aqueous, ammonia transfer and sulfur transfer. The potential degradation of the organic and remediation using re-oximation is discussed. Keywords: Nickel, Solvent Extraction, Oxime

Jan 1, 2004

By J. S. Becker

Technology developed and first implemented in the United Kingdom enables very low grade aluminum scraps containing oils, organics, plastics and ferrous metals to be directly charged, without pretreatment, into a unique melting furnace. The system has been in full scale production for over three years. The oxy-fuel-based furnace design incorporates internal afterburning in the furnace&apos;s hot zone, producing excellent thermal efficiency and very low emissions. The furnace is inherently low in NOx. This paper will provide both theoretical background and extensive operating results for this new melting concept. Applications describing both purpose built new furnaces and retrofits of existing reverberatory furnaces will be presented. Extensive operating emissions data will be presented.

Jan 1, 1996

By Konstantinos Salonitis, Joanna Mielnicka, Mark Jolly, Arun Prabhakar

Lead sheets are widely used for roofing applications, radiation protection and sound proofing. Most of the sheets are either produced by rolling cast slabs of lead sheets or via the direct method (DM) of casting of the sheet continuously. The DM method comprises of a rotating water-cooled drum that is partly immersed in a bath of molten lead and sheets are cast out continuously. The direct method of casting lead is more energy efficient compared to the rolling process which requires a casting process before rolling to achieve the required thickness. This work investigates the energy consumption in different stages of the DM process and suggests pointers for improvement. An energy audit of the process is conducted and the consumption is analysed at different stages and compared with rolled lead.

Mar 1, 2018

By K. Osseo-Asare

"The molecular structural and solution chemical characteristics that underlie the surface activity of solvent extraction reagents are highlighted, with particular emphasis on the tendency towards reverse micelle and microemulsion formation. The physicochemical factors that lead to microemulsion-enhanced solvent extraction with chelating extractants are elucidated. Membrane-based contactor systems are described which are uniquely suited for enhanced solvent extraction with microemulsions. The possibility of combining solvent extraction with microemulsion-mediated materials synthesis is discussed. IntroductionThe discovery of new selective extractants has resulted in major breakthroughs which have helped to establish solvent extraction as a versatile separation technology (1-3). A complementary strategy towards new process development is to seek new ways of using the available reagents. This paper explores this second approach. From a molecular structural standpoint, an extractant may be viewed in terms of two components: a polar functional group and a hydrocarbon radical. In the conventional view of solvent extraction, this molecular structure serves two main purposes: The polar functional group provides the binding sites for complexation of metal ions, while the organic group is needed to render the resulting metal-extractant complex organic-soluble. But are these the only properties of the organic and the polar groups that are relevant to the solvent extraction process?In this paper, attention is directed to the fact that solvent extraction reagents possess the molecular structures of amphiphiIes; that is, they are characterized by the presence of spatially separated hydrophilic and hydrophobic groups on the same molecule. A case is made for the view that this amphiphilicity offers interesting opportunities to develop new separation processes which collectively may be described as enhanced solvent extraction (4-6)."

Jan 1, 1996

By K. Osseo-Asare

The molecular structural and solution chemical characteristics that underlie the surface activity of solvent extraction reagents are highlighted, with particular emphasis on the tendency towards reverse micelle and microemulsion formation. The physicochemical factors that lead to microemulsion-enhanced solvent extraction with chelating extractants are elucidated Membrane-based contactor systems are described which are uniquely suited for enhanced solvent extraction with microemulsions. The possibility of combining solvent extraction with microemulsion-mediated materials synthesis is discussed.

Jan 1, 1996

By Lv Guozhi, Niu Liping, Liu Yan, Zhang Zhiqi, He Jicheng, Zhang Ting’an, Dou Zhihe

"CuCr alloy can be extensively used as contact materials in integrated circuit, electrodes, electric contact and high strength conductor. We proposed thermit reduction-electroslag remelting method of preparing the large scale CuCr alloy. But there are pores and oxide inclusions in CuCr alloy prepared by thermit reduction process. This paper studied mainly the effects of ratio of reactant and additive on the inclusion type and their occurrences in CuCr alloy. The slags and CuCr alloy were characterized respectively by XRD and SEM. The results show that when the additive is Na3AlF6, the slag consist of Al2O3 and Cr. When the additive is CaF2, the slag consist of Al2O3, Cr, CaF2 and CaAl4O7. The inclusions in CuCr alloy are mainly Al2O3 and pores which disperse in Cu-rich zone and Cu-Cr phase interface. When 5% CaF2 and 5% KClO3 are added, there are fewer pores and inclusions, and the more better microstructure.1 IntroduceCuCr alloy is the contact terminal material with an eximious properties[1,2], which gradually replaces CuBi alloy becoming the first choice for contact terminal material in the medium and high power vacuum switch after the 1970s. The traditional preparation methods of CuCr alloy mainly contain powder metallurgy, infiltration process and vacuum electric arc melting methods. But the above methods exist some shortcomings, such as poor product quality, high cost of production, processes complex ect[3-9]. CuCr alloy is made by the thermit reduction self-propagating method, which uses CuO, Cr2O3 and Al as raw material to get the high-temperature melt, and then casts to manufacture CuCr alloy ingot, which response equation follows as:"

Jan 1, 2012

By Maria das Graças da Silva-Valenzuela, Mathilde Julienne Gisele Champeau Ferreira, Simeão Lopes Ferreira, Francisco Rolando Valenzuela-Díaz

The use of clays to formulate powder coating can improve physical properties, besides a final product with more sustainable characteristics due to the elimination of some additives, which may be substituted for the clay. We investigate the use of a modified smectite clay to formulate powder coating based on polyester resin. Four compositions of incorporated claywere evaluated (0, 4, 7, and 10wt%). Powder coating were prepared in a twin-screw extruder at 105 °C, and characterized by XRD, FTIR and SEM. Tests of flexibility, adhesion and impact strength in accordance to ASTM standards were performed. Diffractograms of the samples showed the characteristic peak of the modified smectite in d(001) * 37°(2h), indicating exfoliation of the clay. Micrographs by SEM showed the presence of lamellar structure for the clay-based powder coating.Mechanical assays were found for all analyzed coatings, indicating that sample containing 7% of clay presents the best performance.

Mar 1, 2018

By Dandan Jian, Christian Karcher

Information of liquid steel flow patterns inside the mold may be obtained from the velocity at the free surface (meniscus). This meniscus flow may be measured using the contactless electromagnetic technique termed Lorentz force velocimetry (LFV). It is based on the measurement of Lorentz forces acting on a magnet system when an electrically conducting metal melt interacts with the field lines stretched by the magnet system. Force sensor and the magnet system form a so-called Lorentz force flowmeter. In this paper we present a series of model experiments that demonstrate the feasibility of using two identical flowmeters that are arranged in a certain distance one behind the other. In this case, surface velocity may be determined by just cross-correlating the two force signals recorded by the two sensors. This technique is called time-of-flight LFV. A special prototype of a respective measuring device, called meniscus velocity sensor (MVS), has been developed to measure local free-surface velocity. In the present paper we describe experimental results of respective measurements in the model test stand LiMeSCo (liquid metal surface velocity correlation). To check the potential of the time-of-flight technique, in a first step we measure surface velocities during solid-body rotation of metallic substances. We observe that small modulations in the signals that are due to the natural unevenness of the solid body can be used to determine surface velocities. In a second step we apply the time-of-flight technique to liquid metal free-surface flow. Here we use the low-melting eutectic alloy GaInSn as a test melt. In this case we observe that the cross-correlations between the signals are much rarer and much weaker than in the solid-body experiments. We conclude that the presence of the localized magnetic fields, produced by the permanent magnets of the flowmeter, give rise to intense deformation of the free surface and the creation of surface waves. The field acts as a magnetic obstacle. We observe that the flow velocity is decreased right underneath the magnetic field and is accelerated in the side regions. This magnetic obstacle effect may restrict the determination of the local surface velocity in application.

Jan 1, 2012

By A. Mukhopadhyay

Gas stirring, simultaneous arcing, chemical additions are some basic steps in the secondary steel making. From tap to team however, there are enough uncertainties and several in-situ decision making required to match the fmal composition and temperature in the given amount of processing time. Currently available control algorithms rely on overall material and heat balance coupled with a self-learning regression based tuning of model constants. In this paper we demonstrate the capabilities of Computational Fluid Dynamics (CFD) in modeling and analyzing the thermo-chemical aspects of secondary Steelmaking. These models take advantage of scientific and engineering advances in computational tools and provide almost real time speed of analysis. This can be a very effective tool for operator training, process debugging and improvement as well as new innovations. Keywords: Argon purging, Secondary steelmaking, Arcing, Ladle Furnace, Process Control.

Jan 1, 2003

By Cheryl S. Lim

New technologies such as direct reduction and smelting reduction processes are increasingly being used in iron-making and steel-making in addition to conventional blast furnace technology. Critical parameters for control of these processes include the degree of metallization, degree of pre-reduction, and carbon and silica levels. On-line monitoring of these parameters is difficult because measurements often need to be made on hot ores (at or higher than -1000&apos;C) in circumstances where representative sample streams are not readily accessible. A nuclear analyser has been developed which provides continuous, non¬intrusive, real-time measurements of iron, oxygen, carbon and silicon levels in hot ores undergoing reduction. The analyser has been tested in a plant using a direct smelting process on pre-reduced feed to the smelting vessel-, accuracies of 1% relative, 0.5 w&apos;.96 (25% relative) and 1.0 wt.% (9% relative) were obtained for the degree of pre-reduction, carbon and silica respectively. The underlying method, capabilities and potential applications of the analyser will be discussed.

Jan 1, 2001

By Pingchao Ke

A crystalline polyferric sulfate (PFS) adsorbent was synthesized by oxidizing and precipitating ferrous ions under atmospheric conditions. The morphology, structure, composition and specific surface area (SSA) and adsorptive efficacy to As (III) of the adsorbent were characterized by SEM/EDS and TEM images, XRD patterns, FT-IR spectra, BET SSA analyses and adsorption experiments. The adsorbent presents as morphology of near-spherical aggregate and good crystallinity. A small amount of goethite co-precipitated with PFS in the case of the initial ferrous concentration of 1 mol/L and increased the SSA of the aggregates. The absorbent with co-precipitation of goethite showed good adsorption to As(III) and good filtering performance in the high As(III)-content solution of 10–100 mg/L under acidic, neutral and alkaline conditions (pH 2.09–9.01), and its maximal adsorption capacity and adsorption efficiency were 7911 μg/g and 96% separately. After Adsorption, the stability of the absorbents adsorbing As(III) were evaluated by TCLP tests, and the results indicated that the absorbents adsorbing As(III) were extremely stable, and the concentration of arsenic in all leaching solutions were less than 0.01 mg/L.

By Pengfu Tan

In order to understand and control the formation of dioxins and furans in iron ore sinter plants and to possibly avoid expensive end-of-pipe removal stages, thermodynamic calculations on the stability of PCDD/Fs have been combined with sinter process modeling by means of kinetic simulations and computational fluid dynamics. Three thermodynamic databases of PCDD/Fs, derived using the Group Additivity approach and two computational molecular modeling methods, MNDO and PM3, respectively, combined with the SGTE database have been used to model the PCDDIF formation and the PCDD/F isomer distributions in iron ore sintering. The results show very similar conditions for the PCDD/F formation using the different databases. Concerning the isomer distributions of toxic PCDD/Fs, the calculated data derived from the MNDO method showed optimum agreement with measured values from industrial furnaces. The thermodynamic calculations also proved that the isomer distributions found in combustion processes are equilibrium values, while the concentration ratio of PCDDs and PCDFs in the wind boxes does not represent an equilibrium state. A CFD model of iron ore sintering was developed including the kinetics of 15 relevant chemical reactions with the aim of describing the temperature fields and the gas flow patterns in the sintering bed. On the basis of these information and experimental observations reported in the literature possible pathways for the PCDD/F formation in sinter plants have been identified: PCDD/Fs are formed in the critical temperature region of 250 to 450 °C below the combustion zone, are then carried downwards with the gas and condensed close to the bottom of the sinter bed. Transported to the discharge end with the solid mixture, they are again released into the gas phase when the flame front approaches the bottom. PCDD/Fs are also formed in the last wind boxes when the hot off-gases cool down and reach the critical temperature range. Consequently, methods to reduce the dioxin formation reactions are proposed including inhibitor addition to the sinter feed and off-gas quenching.

Jan 1, 2003

By B. Q. Li, Y. Shu, K Lynn

"This paper discusses the effects of magnetic field and internal radiation on the melt flow and solidification morphology during solidification processing of oxide crystals for optoelectronic and remote sensing applications. The numerical solution of the integral differential equation characterizing the internal radiation and the magnetohydrodynamic equations describing the magnetic and transport phenomena is obtained by applying the combined discontinuous and continuous finite element method. The results show that both internal radiation and an externally applied magnetic field can have important effects on the melt flow and solidification behavior during the melt processing of oxide materials.IntroductionOptical single crystals are widely used in optical and electronic devices. These crystals are often grown from high temperature oxide melts under strictly controlled conditions. As in the well-known single crystal growth processes for semiconductor wafers, thermal gradient in the melt is a major contributing fuctor to the oxide melt pool. Unlike the semiconductor single crystal growth processes, however, the oxide melt is semitransparent and internal thermal radiation plays an important role in redistributing the thermal energy in the melt pool. Our recent experience with pilot-scale plant measurements also shows that the oxide melt is electrically conducting, although its electrical conductivity is considered much lower than the liquid metal or semiconductor melt.The fact that the oxide melt is absorbing and emitting in the thermal radiation frequency range makes it difficult to study the thermal energy transport in the melt pool. This is because thermal radiation is governed by a hyperbolic differential equation, which is different from those describing the transport processes in liquids. Also, our understanding of how thermal radiation interacts with other transport mechanisms such as convection and conduction is rather limited at point in time, in particular in high temperature oxide melts for optical single crystal processing."

Jan 1, 2004

By R. W. Adams

A new process has been developed for leaching zinc sulphide concentrates at atmospheric pressure using air or oxygen plus nitrogen dioxide in dissolved or gaseous form as? an oxygen carrier. The process is flexible and can cope with variations in the degrees of retention and regeneration of dissolved nitrogen dioxide in the leaching phase. By controlled addition of concentrate a leach solution with low residual nitrate concentration can be produced. Following separation by filtration of unleached solids and elementa1 sulphur and conventional oxidation/precipitation of dissolved iron, the leach liquor can be treated with metallic zinc to remove the remaining nitrate and other meta111c impurities such as copper, cadmium and cobalt to provide a solution suitable for electrolytic recovery of zinc. Pilot scale testing of the process .has given zinc recoveries in the high nlnet1es, production of a hi.gh grade jarosite-free Pb/Ag residue (50% Pb.) and a saleable high grade of elemental sulphur. .A wide range of concentrates can be treated containing substantial levels of lead and copper as well as zinc. Indicative cost estimates suggest that the new process is competitive with alternative procedures such as pressure leaching.

Jan 1, 1990

By Alhondra de los Santos, Jesús L. Valenzuela, Jose R. Parga

"The present study evaluated the feasibility of using iron species generated by electrocoagulation (EC) as an adsorbent for removal As(III/As(V) from aqueous media. The full potential of EC was evident in that more than 99 percent of arsenic was removed without addition of chemical reagents. The adsorbent iron-species generated by EC was characterized by Chemical Analyses, X-Ray Diffraction and Scanning Electron Microscopy. The experimental data were correlated by employing a Langmuir adsorption isotherm. Thermodynamic parameters such as ?H o , ?S o and ?Go were calculated. The adsorption process was found to be exothermic and spontaneous.1. IntroductionArsenic contamination in potable water supplies is a serious health problem in many countries around the world. Groundwater arsenic contamination in La Comarca Lagunera Mexico was first reported 30 years ago [1]. Arsenic concentration has been found in well water from several communities ranging from 0.25 to 1.0 ppm. The elevated concentration of arsenic in water, above that originating from natural sources, has been attributed to the use of organoarsenical pesticides in the cotton fields and also to the millions of tons of waste slag generated at a local lead smelter [1]. The main arsenic species present in natural waters are arsenate ions 3- 4 AsO (oxidation state V) and arsenic ions H3AsO3, - 2 3 H AsO and 2- 3 HAsO oxidation state III). However, As(V) ions are most prevalent in oxygenated water while As(III) is found for anaerobic conditions, such as in well water or in groundwater. Conventional methods of arsenic removal rely on chemical-based treatment with lime, alum coagulation, iron coagulation and chemical oxidation. Other processes used with varying degrees of success include adsorption onto activated carbon, reverse osmosis, nanofiltration, manganese dioxide, magnetite and ionexchange resins [1-3]. These conventional processes generate a considerable quantity of secondary hazardous waste such as solid sludge, which also pose serious environmental problems. These drawbacks have forced various industries to search for effective, alternative treatment technologies for arsenic with a preference for electrochemical methods."

Jan 1, 2008