By S. K. Wu, Ray Y. Lin, Sunil Annaji

Infrared joining of TiAI using aluminum foils as the filler material was investigated at temperatures between 1050 °C and 1350 °C in a flowing argon environment for times varying between 15 and 60 seconds. Using aluminum foils, the attempt was to form the Al3Ti phase in the joint as a result of reaction between Al and TiAI at temperatures above the melting point of Al. It has been found based on X-ray diffraction and TEM analysis that, Al3Ti, indeed is the product of infrared joining of TiAI using Al as the joining alloy. Al3 Ti was detected even in the joint processed at 1050 °C for only 15 seconds. Since the aluminum foil used in this study contains 27 at% Si, the t 2 phase in the Ti-Al-Si ternary system is believed to have also formed at the joint/base TiAI interface. Cross sectional studies on the joined specimens have shown different degrees of reaction depending on the temperature and time of joining. Micro hardness evaluations across the joint show that the hardness near the center of the joint is typically smaller than that near the joint edge next to the base material. However, as the joining temperature and time increase, the increment of the hardness at the center of the joint is faster than that around the periphery of the joint.

Jan 1, 1996

By lchiro Aoi, Hideo Nakae, Makoto Yoshida, Makoto Ishino

"The influence 6f gravity on the microstructure of unidirectionally solidified Cu-Pb monotectic, Ag-Si and Fe-C eutectic alloys is studied. In order to examine the influence of gravity in a lg environment, both the upward (opposite to direction of gravity) and downward (direction of gravity) unidirectional solidifications are carried out. The results are as follows: (1) For the upward solidified Ag-Si eutectic alloy, the eutectic Si continuously grows. On the other hand, in the downward solidified Ag-Si alloy, the Si grows discontinuously and disperses into the ex-Ag matrix. (2) No morphological difference in the eutectic growth is observed between the upward and downward solidified Fe-C eutectic alloys. (3) In the case of the upward solidified Cu-Pb monotectic alloy, a banded structure, which consists of Pb-rich layers and Cu-rich layers, is observed. However, such a banded structure -is not observed in the downward specimen. (4) The banded structure is not found in the upward solidified Cu-Pb-0.05 mass % Al and Cu-Pb-0.1 mass % Al alloys. In the Cu-Pb-0.05 mass% Al alloy, a fibrous -L 2 phase grows continuously parallel to the growth direction at low growth rate. Only 500 mass ppm addition of aluminum induces the morphological change of the monotectic L2 phase.IntroductionThe influence of gravity on the solidification of eutectic and monotectic alloys has been investigated in microgravity environments [l-9]. The purpose of these studies was to obtain a homogeneous microstructure of eutectic or monotectic alloys, most of which alloys tend to solidify with macro-segregation under gravity. However, in most of the previous experiments, e.g., in free fall systems, in aircraft or in space laboratories, the growth rate was too high to realize a planar solid/liquid interface. This would be due to the limited time for solidification. Thus, it was difficult to examine the influence of gravity on the planar coupled growth of the eutectic or monotectic alloy. In this study, both the downward U.D.S. (unidirectional solidification by gravity) and upward U.D.S. (opposite direction to gravity) are carried out in order to examine the influence of gravity on the coupled growth in a lg environment [l0, 11]. In the case of the downward U.D.S. using the current Bridgman method, the molten alloy must be confined between the crucible and the solid."

Jan 1, 2000

At its Copper Cliff Smelter, Inco Limited processes a bulk copper-nickel concentrate in two Inco oxygen flash furnaces, The furnace matte is converted to low iron matte for further processing, and the molten converter slag is recycled to the flash furnaces. The flash furnace slag is discarded. Natural gas or coke supplies a minor proportion of the process heat requirements, thus limiting the flash furnace matte grade to the target 45% CuNiCo. Coke addition to the furnace offers a potential means of establishing a reducing barrier on the surface of the molten bath. Such a practice would be conducive to producing sulfur deficient (partially metallized) matte. At the same iron content, the iron activity of sulfur deficient matte is higher than that of regular matte. A supernatant coke barrier could, therefore, be expected to lead to higher nickel and cobalt recoveries, reduction or even elimination of magnetite furnace bottom build-up and increased sulfur elimination as S02 in the flash furnace. Preliminary experiments were conducted in a miniplant flash furnace to investigate the effect on process metallurgy of the suggested modified scheme. This paper presents the experimental results and discusses key aspects of the possible operation of the Inco flash furnace with a coke barrier separating the freeboard from the molten bath.

Jan 1, 2003

By F. J. J. van Loo, J. K. Kivilahti, M. Paulasto

"Activation mechanism and interfacial reactions in brazing of ShN4 with different AgCuTi filler alloys has been investigated thermodynamically and experimentally. During brazing the AgCuTi filler alloy is divided into two liquids Ll and L2, where the (Cu,Ti)-rich liquid L2 gathers at the ShN4 interface and reacts with it. The concentration of Ti in L2 is high, but due to the strong attractive interaction between Cu and Ti, the activity of Ti in L2 is considerably low. In reaction between ShN4 and Cu-containing brazes a Ti-Cu-Si-N compound is typically formed at the interface. In absence of Cu, in joints brazed with AgTi based filler alloys, extremely Ti-rich solution reacts with ShN4 and as reaction products TiN and TisSh[N] are formed. IntroductionAdvanced ceramics like silicon nitride are increasingly used as structural components in demanding applications as well as in electronics industry. Complex, multicomponent structures for engineering applications generally require interconnections and therefore joinability of ceramics largely determines the possibilities of metal-ceramic structures to enable demanding functions. Brazing with active filler metals, most of which are based on the Ag-Cu-Ti system, has been commonly employed for joining of ShN4 to other ceramics and metals. The interfacial microstructures formed when ShN4 is brazed with Ag-Cu-Ti braze alloys have been discussed in several recent studies [1-7]. However, some inconsistencies exist in the reported results. The formation of layers of TiN and titanium silicides, possibly TisSh, next to the ShN4 has been reported in several studies [1-5], while in another investigation, a layer of an orthorhombic TiSi- Cu-N phase was found beyond the TiN layer [6]. In few investigations the thermodynamics of the ShN4-Ti system has been considered, but no detailed thermodynamic analysis of the chemical interactions between the braze and ShN4 has been provided. In order to resolve which chemical reactions are possible under various joining conditions and thereby to be able to control the brazing of ShN4 the reactions in brazing has to be studied using both microstructural and thermodynamic analysis."

Jan 1, 1996

By Rolf R. von Oppenfeld

Onsite hazardous waste processors often find obtaining a Treatment Storage and Disposal (TSD) permit one of their first major challenges. Some processors may spend the time and money required by the permitting process, only to find out later that a permit was not necessary. This paper will present and analyze four strategies that processors may use to avoid obtaining a TSD permit. Some facilities will be able to remove their waste streams from RCRA's oversight by ensuring the material is not "hazardous" waste. Parties that treat waste while it is in process may be able to avoid generating "waste" altogether. Certain treatment facilities have been specifically exempted by EPA. Finally, treatment of waste while it is in generator storage tanks may be allowed without a RCRA TSD permit. Hazardous waste point of generation, an important determination relating to these strategies, will also be discussed. Generators and processors will find this paper useful when evaluating their permit exemption potential

Jan 1, 1996

By A. A. el-Geassy

High-grade iron ore fines rejected from the DRl plants (>96%Fe20) were isothermally reduced in 30-60%COIH2 gas mixtures at 973-1273K. The freshly reduced reaction products were then subsequently carburised in either H2/CO or H2/CO/S mixtures at 823-1073K for 30-120 min. The thermogarvimetric technique was used to follow up both of reduction and carburisation reactions as a function of time. The carburised samples were characterized by X-ray and Mossbauer techniques. Chemical and carbon analyses were also applied. The influence of temperature and gas composition on the reduction behavior was investigated. The calculated values of apparent activation energy, application of gas-solid mathematical formulations were correlated with the microstructures to predict the reduction mechanism, The influence of carburization time, temperature, CO contents in H2/CO or H2/CO/S were investigated. A conversion extent of Fe to Fe3C was taken as a measurable index for the efficiency of carburization reaction under the different experimental conditions.

Jan 1, 2003

By Seetharama C. Deevi, Mohammad R. Hajaligol, Sarojini Deevi

"Carbides and nitrides of iron are being considered as magnetic materials for high-density recording due to their chemical stability and high-saturation magnetization values (> 100 emu/g). Iron carbides and iron nitrides with magnetic properties suitable for magnetic media were synthesized by employing a novel synthesis procedure based on fluidization of powders in reactive atmospheres. Fluidized-bed reactors of laboratory, bench, and pilot scale were employed for the synthesis of iron carbide, FeSC2, by reducing and carburizing U-Fe203 in the temperature range of 300 to 550 ºC. A temperature of 400· ºC and a reaction time of 2 to 3 h are found to be optimal for the synthesis of iron carbide. When the carburization was carried out in a reducing and carburizing atmosphere such as carbon monoxide, nucleation and growth of FeSC2 occurred directly from Fe304 with no intermediate phases such as FeO or Fe. Longer carburization times resulted in the deposition of carbon on the surfaces of FeSC2 particles due to Boudouard reaction, and higher temperatures favored the formation of a mixture of carbides such as FesC2 and Fe3C. Iron nitrides were synthesized by reducing u-Fe203 in the temperature range of 350 to 550 ºC, followed by nitriding in the temperature range of 350 to 550·ºC. The powders were characterized using X-ray diffraction, scanning electron microscopy, thermogravimetric analyzer, and a vibrating sample magnetometer.IntroductionRecent demand for high-quality recording of optical, electrical, and audio signals generated interest in magnetic tapes with high-recording densities as compared to the conventional magnetic tapes based on U-Fe203. At present, commercially available magnetic tapes contain maghematite, U-Fe203, as a magnetic material with a saturation magnetization of90 emu/g and a coercive force of 400 Oe. Recording of signals at a higher density per unit volume of magnetic material demands magnetic materials with high-saturation magnetization and a reasonable coercive force. Although metallic iron particles possess a saturation magnetization of 130 to 150 emu/g and a high coercive force of 1000 Oe, the gradual oxidation of iron-to-iron oxides (of lower saturation magnetization) prevents the use of iron particles for high-density recording. In contrast, iron carbides such as FesC2, Fe7C3 and iron nitrides such as Fe4N and Fe3N possess excellent magnetic properties coupled with good electrical conductivities and high hardness. The carbides and nitrides of iron have generated significant interest as magnetic materials for the next generation of magnetic tapes due to their unique magnetic properties and relatively greater oxidation resistance as compared to metallic iron particles [1-4]."

Jan 1, 1994

By E. J. Peterson

Oil shale retorting induces mineral and chemical reactions to occur on the macroscopic and microscopic levels in the kerogen-bearing marlstone. The nature and extent of the reactions is dependent upon process variables such as maximum temperature, time at temperature, atmosphere, and raw shale composition. This report describes the investigation of the mineral, chemical, and trace element release properties of spent shales retrieved from an experimental in situ retort at Occidental Oil Shale, Inc. 's Logan Wash site in Garfield County, Colorado. Correlation between mineralogy of the spent materials and the mobility of major, minor, and trace elements are indicated, and relationships with important process parameters are discussed. The progress .of carbonate decomposition reactions and silicat ion reactions is indicative of the processing conditions experienced by the shale materials and influences the mobility of major, minor, and trace elements when the solids are contacted by water. Shale minerals that are exposed to the extreme conditions reached in underground retorting form high temperature product phases including akermanite-gehlenite and diopside-augite solid solutions, kalsilite, monticellite, and forsterite. The persistence of relatively thermally stable phases, such as quartz, orthoclase, and albite provide insight into the extremes of processing conditions experienced by the spent shales. Leachate compositions suggest that several trace elements, including vanadium, boron, fluoride, and arsenic are not rendered immobile by the formation of the high-temperature silicate produce phase akermanite-gehlenite.

Jan 1, 1981

By B. R. Baldock

The converting of high-grade nickel matte for production of low-sulphur matte or nickel metal is a process which has eluded metallurgists in the past because of the limitations of conventional converting furnaces. The high temperatures required and the refractory nature of nickel oxide has prevented practical success in a process which has been known to be theoretically feasible for a long time. The Ausmelt top submerged lancing system is capable of operating under close control of the smelting conditions. High temperatures and both rapid oxidation and rapid reduction can be achieved. These features have provided the basis for successful pilot plant trials of the desulphurisation of high-grade matte from the Kalgoorlie Nickel Smelter. Sulphur level in product was lowered from 20 to 25% to as low as 0.2%, with iron levels in matte in the range of 1.0 to 3.5%. The theoretical background of matte desulphurisation is surveyed and the pilot plant operations described. The implications of the results in relation to commercial plants and possible refinery operations are summarised.

Jan 1, 1993

By V. M. Lsoitko

Statistical methods of technological mineralogy are used to model processing flowsheets in order to improve ore dressing efficiencies. The procedure involves determining geological and mineralogical characteristics of ores, classifying ore types and metallurgical procedures, and developing computer programs to interpret essential mineralogical parameters from on-stream analysis data. The on-stream analysis data include magnetism, radioactivity, luminescence and assays. The data are interpreted by computer and appropriate adjustments are made automatically in the plant.

Jan 1, 1989

By Lauri Holappa

Copper converting is mostly performed in Peirce-Smith converters. The process is still very similar to the original one developed in the early 20th century. It is a batch process in a horizontal cylindrical reactor with air blowing via tuyeres along the length of the reactor side. The Peirce-Smith converter has its roots in Bessemer's inventions in the 1850's as he tested both horizontal and vertical vessels for steel converting. However, for steel making a vertical pear-shaped converter with air bottom-blowing was established. In the course of time, there was a distinct necessity for oxygen usage instead of air due to harmful effects of nitrogen to steel properties and its cooling effect. In-bath blowing of oxygen did not succeed, however, and top-blown oxygen converter with oxygen lance (LD or BOF) was first developed in he 1950's and emerged rapidly to a dominating position. Somewhat later oxygen bottom-blowing via special shrouded tuyeres was developed (OBM or Q-BOP) but has attained only fractional share. Bottom-blowing technique had, however, impact on the current combined blown converters which adopted the benefits of both top and bottom blowing. In copper converting Peirce-Smith type converters have kept their position until today although new processes have been introduced and at least few of them seem to be emerging. In one respect copper converting has a clear leading position i.e. in the progress of continuous converting processes (Mitsubishi, Ausmelt). These processes utilise top-blowing lances instead of in-bath blowing tuyeres. A different principle for continuous converting is flash converting by Kennecott Outokumpu, which makes smelting and converting independent of each others. Solid ground matte is used as a feed for flash converting in a reactor shaft similar to Outokumpu matte flash smelting. A comparable process has been presented by Inco too. The paper discusses principal physico-chemical and process technical similarities and differences in copper and steel converting. Although these processes are metallurgically quite different it seems that during the modem history of ferrous and non-ferrous metallurgy, starting from the 1850's, the exchange of knowledge between these disciplines has been quite intensive. In long-term perspective, many similarities in the development can be found but also divergences due to different ambient circumstances.

Jan 1, 2003

By Denise Corrêa de Oliveira

Common dry batteries use zinc as the negative electrode. Producers commonly use additives such as mercury to prevent corrosion and to increase the mechanical resistance of the zinc anode. Alkaline batteries also contain it, as an anti-corrosive agent. When mixed with the common municipal solid waste, heavy metals as zinc and mercury pollute soil and ground water supplies, moving to the food-chain and affecting human health. Due to these possible damages, this kind of waste must be properly disposed, or recycled. Thus, even in low amounts (ppm) in batteries, mercury has to be eliminated or, at least, its content should be reduced. This work presents the use of pyromettalurgical processes, to reduce mercury content and recover zinc. The tests involved batteries treatment at temperatures from 300° to 1000°C. Mercury is eliminated up to 650°C, and zinc is evaporated at higher temperature treatment. C

Jan 1, 2001

By Filiz Sahin

This paper presents a synthesis of TiB2 via carbothermal reduction method using a mixture of TiO2, B4C and C prepared in molar ratio of 2:1:3. Reduction experiments were carried out in a high temperature graphite furnace in a graphite crucible under argon atmosphere at different time (0, 15, 30 and 60 min.) and temperatures (1400, 1500 and 1600 °C). The products obtained were investigated using XRD technique.

Jan 1, 2008

By Ajay K. Singh

The surface quality demands for galvanized and galvannealed steel sheets by the automotive and appliance industries have been getting increasingly stringent over the past few years. Intensive efforts by Hot-Dip-Galvanizers to meet these demands have resulted in substantial improvement to the hot dip coating process. However, elimination of zinc bath contaminants which directly affect the coated strip surface quality continues to remain a tough challenge. As part of our effort to improve the zinc bath cleanliness, Inland Steel Company has developed a test method to quantitatively measure the contaminants in incoming zinc spelters and establish a specification for incoming zinc quality. The test is currently being used for auditing the incoming zinc quality. The zinc suppliers are also using this test for quality control purposes. The purpose of this paper is to describe the test method and how it has improved the galvanizing operation at Inland.

Jan 1, 1992

By Min Chen, Lei Xu

Sintering behavior and performance of high alumina refractory based on the ternary subsystem MgAl2O4-CaAl4O7-CaAl12O19 were investigated using ZrO2 as an additive up to 8 wt.% by solid state reaction sintering. It was found that the added ZrO2 could dissolve in the CA6 grains in the form of a solid solution, which enhanced the isotropic growth of CA6 grains and then improved the sintering. As a result, the densification process was improved and areas with enrichment of ZrO2 showed a more compact structure. With further increase of ZrO2 addition, tetragonal ZrO2 were found to locate in the grain boundaries for exceeding the solid solubility limit, which enhanced the thermal shock resistance, indicating that addition of ZrO2 exhibited a positive effect on sintering behavior and performance of this refractory. In addition, it is considered that the optimal amount of ZrO2 addition was about 4% considering the performance together with the cost.

Jan 1, 2015

By L. A. Harris

The formation of coke during coal liquefaction can eventually result in catastrophic failure of the conversion system. Coking typically proceeds by the formation of liquid crystals (mesophase) and the subsequent separation of these crystals from the plastic phase formed during heating of coal. The anisotropy of the mesophase makes it readily detectable in the optical microscope under polarized light. This study examines the solids formed during coal liquefaction processing by optical and electron microscopy. Observations on the relationships between the coke morphology, minerals and inert macerals are presented.

Jan 1, 1982

By Mahesh C. Meyer Jha

AMAX has developed a chloride refining process to produce pure nickel and cobalt metals from mixed sulfide .precipitates, Metal chloride solutions, generated in a hydrochloric acid leaching step and purified in a solvent extraction circuit, are converted to metal oxides .and HCI gas by pyrohydrolysis. A pilot plant consisting of a 30-inch diameter fluidized bed reactor and other ancillary units was designed, constructed, and operated for over one year. Process design was aimed at minimizing energy consumption, maximizing conversion efficiency, and achieving simplicity of operation and control. The operation provided valuable information on process scale up parameters, process control strategies, and materials of construction., Several process variables such as bed temperature, solution composition, solution feeding system, bed particle size distribution, and fines recycle system were investigated to determine their effects on process efficiency and the physical and chemical characteristics of the product.

Jan 1, 1985

By K. Walanabe

Kosaka Smelter & Refinery has a history of more than a century as a metallurgical department belonging to Kosaka mine. It has treated for a long time the "Black Ore" or the complicated concentrates dressed from it. The "Black Ore" is composed of black sulfides. It contains not only valuable metals such as gold, silver, copper, lead and zinc but also some impurities like arsenic, antimony and bismuth. With the development of Kosaka's floatation technology, five kinds of concentrates (copper, zinc, lead, pyrite and barite) have been separated from the "Black Ore" but the separation was not complete and each concentrate contained some unfavorable impurities. In 1980s the highly appreciated yen and the drop of the metals prices forced many domestic mines to close their operations. Since then Kosaka Smelter has changed its way of operation to a custom smelter. Now more than 95% of copper concentrates are imported to take advantage of this technology of "Black Ore" treatment. It mainly treats the raw materials that contain high gold and silver like the "Black Ore". Recently, Kosaka has been working on the recycling of the metals from the printed circuit board scraps and sludge which contain some precious metals. The volume of the recycled metal is continuously increasing.

Jan 1, 2003

By Raj P. Singh

Applications of cementation in the recovery of metal ions from process solutions have been known for a long time. Cementation reactions involve electrochemical precipitation of a noble metal from solutions of its salts on a more electropositive metal which, in tum, progressively dissolves. For example, addition of zinc metal powder in a solution containing zinc and cobalt ions would allow for the precipitation (separation) of cobalt according to the following chemical reaction. This paper pertains to the recovery of cobalt from cobalt process solutions via a cementation reaction on aluminum shavings (metal scraps from cans etc). Specifically, we report on the characterization of cobalt process solutions, a by-product obtained from cobalt chemicals, and the kinetics of cobalt, nickel and manganese cementation from process solutions on aluminum shavings.

Jan 1, 2000

By Uchil Jayagopal, P. V. Krupakara, S. Manjunath

"This paper deals with the corrosion characterization of quartz particlate ZA-27 alloy metal matrix composites (MMCs). Quartz particles of size 50-80 microns are used as reinforcement. MMC's are prepared according to ASTM standards. Composites containing. 2, 4, and -6% by weight of quartz and unreinforced matrix were tested using 1 -N hydrochloric acid: The composite was found to be more corrosive resistant than matrix alloy. In each test the corrosion resistance of both alloy and composites were found to decrease with the exposure time.1. IntroductionMetal matrix composites- (MMCs) offer designers many added benefits, as they are particularly suited for applications requiring good strength at high temperature, good structural rigidity, dimensional stability, and light weight 1-5. The trend is towards safe usage of the MMC parts in the automobile engine, which work particularly at high temperature and pressure environments Particles reinforced MMCs has been the most popular over the last two decades.ZA alloy MMCs have most popular families being represented by. ZA-27 alloy reinforced with ceramic particulate. Although the incorporation of the second phase into a matrix material can enhance the physical and mechanical properties of the base metal, it could also significantly change the corrosion behavior.ZA alloys have been used extensively in industry. This is attributed to their excellent fludity, castability and good mechanical properties. Among the zinc-based foundry alloys, the ZA family of alloy have been widely used during the past few years. ZA alloys have many advantage over aluminium based ones, especially high strength with a low casting temperature 8."

Jan 1, 2000