By A. M. Turkalo

IT is a well-known fact that martensitic steels show a greater resistance to brittle fracture than do pearlitic and bainitic steels. It was, therefore, thought worthwhile to investigate the mode of brittle fracture with respect to structure by studying the effect of various austenite decomposition products on the propagation of brittle fracture in steel by means of electron microscopy. Newly developed replication techniques together with the advantages of the electron microscope such as great depth of field, available high magnification and easy adaptation to stereophotography make electron microscopy very suitable for fracture studies. EXPERIMENTAL PROCEDURE An essentially plain carbon steel containing 0.56 pct C, 1.30 pct Mn, 0.02 pct P, 0.03 pct S and 0.22 pct Si was used in this investigation. The following table gives the heat treatments used to obtain the various austenite decomposition products: The resulting austenite grain size from the 870°C austenitization treatment was about an ASTM No. 7 grain size. The specimens which were 2 in. long, 1/4-in. diam bars were austenitized in a tube furnace through which argon gas was blown. The tube was not, however, air-free and the specimens were not completely oxide-free. Isothermal treatments were done in a lead bath. With the exception of the fully hardened specimen and the one as-isothermally transformed at 300°C the heat treated specimens were notched in the following fashion with a jeweler's saw. A cut about 0.08 in. deep was made perpendicular to the length of the bar. The specimen then was rotated about 45 deg and another cut about 0.08 in. deep was made. In the case of the hard martensitic and bainitic specimens, only one cut was made and the depth was not controlled. The design of the two-cut notch caused fracture to initiate at the point of intersection of the two saw cuts. The specimens were broken at -196°C in a Charpy impact testing machine. In order to hold the specimens securely in the impact machine two square pieces of mild steel were made about 5/8 in. long having the same cross section as that of a standard Charpy specimen but containing a hole 1/4 in. diam through the center of the cross-section. These adapters were slipped over the ends of the test specimen which was then secured tightly by means of set screws in the adapters. The specimen with the adapters was cooled to -196°C in liquid N,, then placed in the impact machine and broken within 3 sec. One half of the broken specimen was used for the electron microscope study of the actual fracture surface. The other half was nickel-plated and a cross section through the notch and fracture was polished for electron microscope examination. Carbon replicas of the fracture specimens for the electron microscope study were made essentially according to Bradley's evaporation technique.' Both direct carbon and two-stage carbon replication techniques were used. In the case of the direct carbon technique, a thin layer of carbon was evaporated first at an angle of about 45 deg to the mean fracture surface and then another film of carbon was evaporated normally to the fracture surface. The carbon replica was freed electrolytically.2 The specimen was made an anode in a 10 pct Nital polishing solution. It was etched intermittently by shutting off the power now and then. The freed replica was washed in 40 to 50 pct water solution of nitric acid for 10 min or so, then washed in water and picked up on a screen for examination. The two-stage carbon replication technique involved first making a primary replica of cellulose * acetate from which a carbon replica was then made. One side of a strip of cellulose acetate wet with acetone was pressed lightly against the surface of the specimen, allowed to dry and then stripped. Prior to the deposition of carbon, which was done at 90 deg to the cellulose acetate replica surface, chromium was evaporated at 45 deg. After the carbon evaporation the cellulose acetate was dissolved in acetone according to the Jaffe method3 leaving the carbon replica preshadowed with chromium for examination.

Jan 1, 1961

By J. O. Nelson, C. J. Altstetter

Single crystals of hcp cobalt, 3 mm in diameter and up to 35 cm long, were grown using an electron-beam, zone-melting technique. The martensitic-phase transformation was studied in single-crystalline and polycrystalline specimens by making length-change measurements as a function of temperature under various elastic compressive stresses. Upon thermal cycling, single-crystalline or polycrystalline specimens repeatedly transformed almost entirely on the same variant of close-packed plane provided the maximum temperature did not exceed 600°C. Cycling to 1000°C resulted in transformation on more than one {111} variant. This behavior is termed multivariance. The multivariant transformation occurred very rapidly at an M, temperature 2° to 6°C lower than the M, of a transformation which would result in a single-crystal product. Elastic compressive stresses (up to 253 g per sq mm) tended to lower the A, and raise the M, temperatures, decreasing the width of the temperature vs dilatation hysteresis loop. The transformation habit plane and transformation shear direction of an as-grown single crystal were not grossly affected by elastic compressi?ie stress. This was evidenced by similar dilatations on the temperature us dilatation loops joy specimens with and without compressive stress. A dislocation mechanism is proposed to explain the observed results. IT has been shown that, on heating, cobalt transforms martensitically from the hcp to the fcc phase.' The transformation habit plane is (0001)hcp || (lll)fcc and the transformation shear direction is (1010)hcp || (112)fcc. The transformation involves a shear of 1g°28', which may be achieved by a shearing of a/6(112) of every two planes with respect to the plane beneath, thus changing the ABABAB stacking of hcp to the ABCABC stacking of fcc. Associated with the phase change is a 0.3 x 10"3 contraction in the habit plane and a 4.2 X 10"3 expansion perpendicular to the habit plane resulting in a 3.6 x X volume increase on heating.' On cooling, an identical volume decrease takes place. The temperature at which the fcc phase begins to form on heating (A,) is reported as 430°C, and the temperature at which the hcp phase begins to form on cooling from an elevated temperature (A&) is reported as 390oC1,3 Consequently, temperature vs dilatation plots have the form of a hysteresis loop. If heating or cooling is reversed during a transformation, a smaller hysteresis loop results. Upon heating, the transformation is always complete; whereas, fcc is often retained at room temperature as a metastable phase entrapped in the polycrystal-line hexagonal matrix.1,4,5 Two obstacles in the theory of the allotropic-phase transformation of cobalt have been: 1) a detailed knowledge of the product nucleus, and 2) a plausible method of propagation of the transformation. Bilby,8 christian, 7 and seeger 8,9 have suggested a "pole mechanism" as a means of propagation of partiai dislocations from plane to plane. A pole dislocation and a Shockley partial come together at a node. The a/6(112) Shockley partial rotates about the pole dislocation effecting the transformation shear. The pole dislocation must have a 2a/3(111) screw component which causes extension of the transformed region by two atomic planes with each full rotation of the Shockley partial. Bollmannl0 suggested, on the other hand, that transformation propagation occurs due to the stress fields of intersecting (111)-type stacking faults. As faults intersect, a stress distribution is set up about their intersection which is in turn reduced by the emergence of another fault on the second nearest plane. This process continues with the final result of a complete phase transformation. In view of the similarities between deformation and transformation in cobalt, the effect of stress on the transformation would, hopefully, yield valuable information concerning nucleation and propagation. In the present work single-crystalline and polycrystalline specimen length changes were measured as a function of temperature at various compressive loads. PROCEDURE Several orientations of single crystals of hcp cobalt in lengths up to 25 cm were grown by electron-beam floating zone melting from 99.95 and 99.999 pct, 3-mm-diam cobalt rod as supplied by Johnson

Jan 1, 1964

By C. D. Wiseman

THE concept of alloying to increase the strength of metals originated during the bronze age. However, at the present time there is no single theory capable of explaining all of the observed strengthening effects of alloying elements on the mechanical properties. In general, it may be said that solid solutions are stronger than the pure metal and that the strengthening effect increases with increasing alloy content. Various theories for solution hardening have been proposed, the first of which was presented by Rosenhain who suggested that the alloying elements roughened the slip planes, thereby requiring a higher stress to initiate slip. Recent work by French and Hibbard2 confirmed Norbury's3 conclusion that those alloying elements which cause a greater change in lattice parameter have larger effects on hardness. However, a given change in lattice parameter produced by different alloying elements does not cause the same change in hardness. A further refinement was suggested by Dorn, Pietrokowski, and Tietz4 who considered differences in valence between the solute and solvent with the change in lattice parameter to explain the plastic properties of aluminum alloys. Allen, Schofield, and Tate5 further investigated the valency contribution to solution strengthening by testing some copper-base solid-solution alloys having constant electron densities. Tensile tests performed on these alloys gave identical stress-strain curves even though the atomic size effect, which varied by a factor of two, was neglected. The advent of dislocation theory6-8 provided a new and powerful tool capable of explaining many phenomena of plastic deformation and indicated new approaches to solution hardening. The basic con- cept of recent theories is that solution hardening is not due to stresses associated with randomly dispersed solute atoms, but rather to a nonuniform distribution of the solute. This conclusion was reached by consideration of the effective tension present on each dislocation line and the ability of a dislocation to pass an obstacle. cottrell suggested the possibility that the internal stresses due to randomly distributed solute atoms would offer essentially no resistance to the passage of dislocations. He reasoned that an edge dislocation may be considered as a rigid line discontinuity. As the dislocation moved through a crystal, the random stress fields would be equally distributed along its length. Since half of the stress fields would be acting to move the dislocation forward and the other half trying to move it back, the net effect on the dislocation would be zero. Thus the randomly distributed solute atoms would not contribute appreciably to solution strengthening. Mott and Nabarro10 considered the dislocation as a flexible, rather than a rigid, discontinuity. They obtained a simple model for a dislocation moving in a lattice having precipated particles, where the dislocation would actually bend around the obstacle until it would loop back onto itself to rejoin and then continue onward. Their work indicated that the minimum radius of curvature of the dislocation line, under the action of an external stress and in the region of an internal stress, would be such that the dislocation would be unable to pass through a matrix containing small closely spaced precipates by the looping process. The dislocations would tend to remain rather straight, approaching the condition of Cottrell's rigid dislocation. Hence, the strengthening must not be due to random solute atoms; however, it might be due to the concentration of atoms, either as clusters of like atoms or as short-range ordered regions, or to the concentration of solute atoms around dislocations. To date, four mechanisms of solution strength-

Jan 1, 1959

By W. M. Albrecht, W. D. Klopp, R. I. Jaffee, B. G. Koehl

Kinetic studies were made of the reactions of tantalum with oxygen, nitrogen, and air at 400o to 1500°C. The tantalum-oxygen reaction is linear from 500° to 1250°C. The tantalum-nitrogen reaction follows a cubic rate law at 400° to 700°C and a parabolic rate law at 800" to 1475°C. The reaction behavior in air is initially parabolic followed by a transition to linear behavior. In the search for high-temperature materials, considerable interest is being shown in the refractory metal, tantalum. It is the third highest melting metal with a melting point of 2996°C. Also, tantalum has excellent ductility, making it one of the most workable refractory metals. In considering high-temperature applications of tantalum, the oxidation kinetics of the metal must be known. Such information also serves as a basis for the development of corrosion resistant tantalum-base alloys. Therefore, this study was made to investigate the reaction of tantalum with air, nitrogen, and oxygen. LITERATURE Several oxides of tantalum have been reported. The pentoxide, Taz05, is the only oxide of tantalum whose identity has been established. A high-temperature modification, aTa2Os, has been reported by several investigators.1-4 A low-temperature phase, ßTa2O5, undergoes an allotropic transformation at 1320o to 1350oC. 5-8 Four other oxides of tantalum have been reported. The oxides TaO2, TaO, and Ta4O have been reported by schonberg.9 A suboxide Ta2O, was observed by Wasilewski 6. However, the presence of oxides lower than Ta2O5 is questioned by Lagergren and Magneli.7 In oxidation studies, vermilyeal0 and Peterson, et al.,12 reported one possible phase intermediate between Ta and Ta2O5. Only Ta2O5 was formed in the tantalum air reaction, as reported by Michae1.l3 Several studies have been made on the kinetics of the tantalum-oxygen reaction. vermilyeal4 investigated the range 50° to 300°C and found that the rate of growth of a thin adherent oxide film could be described by the Cabrera-Mott theory. Gulbransen and Andrew15,18 studied the reaction kinetics of tantalum in oxygen pressure of 1/10 atm at 250° to 450°C. At all temperatures the reaction followed the parabolic rate law for periods up to two hours. The oxidation behavior in the range 500" to 1000°C was found to be linear at oxygen pressures of 0.2 to 600 psi according to Peterson. et al.l1 At very low pressures (1 x 10-3 to 2 X lo-' mm of Hg) Gebhardt and seghezzi17 reported linear oxidation at 800° to 1500°C. The reaction of tantalum with air is similar to the reaction with oxygen. Studies have been made by Waber, et a1.,12 and Michae1.l3 Two nitrides of tantalum, TaN and Ta2N are known. Their structures have been determined by Brauer and Zapp 18,19 The tantalum-nitrogen reaction kinetics have been investigated by Gulbransen and Andrews. 15, 16 The reaction follows the parabolic rate law at 500° to 850°C at a nitrogen pressure of 1/10 ,atm. At the same temperature, the tantalum-nitrogen reaction is much slower than the tantalum-oxygen reaction. EXPERIMENTAL TECHNIQUES Material— The material used in this study was high-purity, electron-beam-melted tantalum obtained from the Temescal Metallurgical Corp. The hardness of the as received ingot was 76 Vhn. The analysis of the material is given in Table I. Methods—Cylindrical specimens of tantalum approximately 0.9 cm in diam and 0.5 cm in length

Jan 1, 1962

By G. M. Willis, F. L. Hennessy

The oxygen pressure in equilibrium with silver and Ag2O-B2O3 melts has been measured between 800' and 900°C, to obtain the thermodynamic properties of the liquid. The compound Ag20. 4B20:1 appears to exist in the liquid, which shows marked heat content and entropy effects. A KNOWLEDGE of the thermodynamic properties of binary liquid silicates, borates, and phosphates would be of considerable assistance in the interpretation of the behavior of multi-component metallurgical slags. However, the literature contains comparatively few studies of the thermodynamics of binary slags. The system Ag20-B,O, attracted our attention as it was known to give a single liquid phase,',' in which high contents of silver could be obtained (up to 61 pct Ag according to Foex2). Further, it would be expected that the partial pressure of oxygen over melts in equilibrium with metallic silver could be used to determine the activity of Ag2O in the Ag,O-B,O, system. In many respects, it may be expected that the reaction of a basic oxide with boric oxide would be analogous to its reaction with silica. Liquid immiscibility frequently occurs in both borate and silicate systems. With B2O3 and SiO reaction with a basic oxide presumably involves a breakdown of the three-dimensional network of the acid oxide by reaction with oxygen atoms common to more than one silicon or boron atom. Ag2O-B2O3 was therefore investigated as a model of a slag system in the hope that its thermodynamic properties would assist in understanding those of other systems. Several methods for determining the activity of a component in a slag have been described in the literature. Chang and Derge" used high temperature electromotive force measurements to obtain the activity of SiO2 in CaO-SiO2 and Ca0-Al203-Si02 slags, but the cell reaction in their work is not clear. low has used rate of volatilization and vapor pressure measurements combined with phase diagrams to obtain activities in the systems KO-SiO,, Na,O-SiO, and Li,O-SiO," and PbO-SiO26 Taylor and Chipman7 extrapolated their results for the distribution of FeO between liquid iron and CaO (+Mg0)-FeO-SiOl slags to obtain the activity of FeO in the binary FeO-SiO2 system. In principle, one of the most direct methods for obtaining the activity of a metallic oxide in a phase is by comparison of the equilibrium oxygen pressure for the system metal-pure oxide with that of metal oxide-containing phase. Schenck and othersa have studied the stabilization of Ag2O on combination with other oxides (MO,) in the solid state by measurements of the oxygen pressure in systems of the type Ag-Ag,O-xM0,-MOy-0, (gas). Schuhmann and Ensio" have determined the activity of FeO in iron silicate slags in equilibrium with solid iron, using CO/CO2 mixtures to establish known partial pressure of oxygen. Although the method gives the activity of FeO without ambiguity, the slag is not a binary system, and interpretation of the results in terms of the hypothetical binary system FeO-SiO, is not possible. If a metal is solid at temperatures at which the properties of the slag containing its oxide are to be studied, this method has the considerable experimental advantage that the metal can be used as the container for the slag, and contamination by contact with refractories is avoided. In this work, crucibles for Ag2-B,O, melts were made from silver, and the liquid brought to equilibrium with definite pressures of oxygen gas. The oxygen pressure PO, thus fixes the activity of Ag20 in the liquid silver borate. For the reaction at a given temperature. is substantially constant, is directly proportional to the square root of the equilibrium oxygen pressure. Varying the oxygen pressure changed the silver oxide content of the liquid and it was possible to obtain the activity of Ag2O over a range of composition. Experimental Procedure In principle, the method consisted of bringing melts in silver crucibles or boats to equilibrium at a fixed temperature under a definite pressure of oxygen and analyzing the glass after solidification. Materials: B2O3 glass was prepared from A.R. quality boric acid by fusion in platinum. The silver

Jan 1, 1954

By M. Metzger, L. E. Hendrickson

Grain boundary attack in 16 pct HCl was found to be substantially the same at low penetrations in zone-refined aluminum (individual impurities 0.1 at. ppm), superior electrolytically refined aluminum (51 at. ppm), and aluminum with various impurities at much higher levels. It was concluded that impurity atom segregation affecting corrosion would have been detected and that the corrosion susceptibility did not originate in this segregation but in the structure of the boundary. It was pointed out that the significance of most previous studies in this system had been obscured by an unrecognized autocatalytic copper reaction. Although general corrosion rate was also impurity-insensitive , there was shallow pitting attributed to iron seg-regation and a hillocked surface texture associated with copper; these were interpreted as due to cathodic damage affecting- cathode distribution. THE grain boundary corrosion suffered by high-purity aluminum in hydrochloric acid has been the object of some interest (the earlier work is summarized in Ref. 1). The central metallurgical question here is whether the corrosion susceptibility of a boundary originates in its structure or in impurity atom segregation. An attempt to study this question revealed large catalytic effects associated with small quantities of the copper impurity in the aluminum, 220 ppm, or in the corrodent, and these magnified the preferential boundary attack and obscured the intrinsic susceptibility question.' After the catalytic effects had been examined,"' test conditions could be designed to avoid them and methods developed for studying the shallow boundary penetrations prevailing when they were absent.= It then became possible to determine whether intrinsic boundary corrosion in aluminum involves impurity segregation. The older work provided no firm information on grain boundary segregation of specific solutes influencing corrosion although several studies suggested iron segregates.4,5 perryman4 found in 10 pct HC1 that the slowly developing (microns per month) grain boundary grooves were deeper in material of higher iron content (range 10 to 550 ppm, with 5 to 80 pprn Cu) but he did not measure the depths of general corrosion, which were probably several times greater, and his reference surfaces may have varied more than did the groove depths. Metzger and Intrater's results for 20 pct HC~,' which yielded higher time-average rates (mm per month) and deeper penetrations, suggested that boundary segregation of iron (range 4 to 230 ppm, with 22 pprn Cu) decreased the penetration rate. However. in the stronger acid the autocatalytic l.E. HENDRICKSON, Student Member AIME ,and M. METZGER, Member AIME, are Research Assistant and Professor of Physical Metallurgy, respectively, Department of Mining, Metallurgy and Petroleum Engineering, University of Illinois, Urbana, Ill. Manuscript submitted March 11, 1968. IMD effect of the copper impurity is greater1,2 and it is now evident that their corrosion rates had been much magnified by this effect and did not provide a proper basis for the analysis of segregation. In exploratory studies of other solutes (made under the same conditions), 1000 ppm additions of Mg, Mn, or Si or 100 ppm Ca were without effect.1 Montariol6 noted that boundary attack in 22 pct HC1 persisted after zone refining although with fewer deep fissures (ranges 0.06 to 4 ppm Cu, 4 to 23 ppm Fe). Autocatalytic effects may have influenced these results also and those of Perryman.4 The present objective was, as a first step, to see whether quantitative tests designed to exclude autocatalytic influences would indicate the existence of low-level impurity effects on intrinsic boundary corrosion. Comparison of electrolytically refined with zone-refined aluminum of lower copper and iron contents revealed no differences in boundary corrosion, but certain impurity-sensitive differences in general corrosion morphology were noted and investigated further at higher impurity levels. I) EXPERIMENTAL PROCEDURE A) Material. A selection from commercially available material was made with the cooperation of several producers. An electrolytically refined lot (III-A, 1 ppm Cu, 2.4 ppm Fe) studied previously3 provided a starting point. Since material of substantially higher copper content could not be used if the autocatalytic corrosion reaction were to be avoided,2,3 a lot (III-B) of about the same purity was added as a check, two zone-refined lots (I-A and I-B) with copper and iron an order of magnitude lower were selected for comparison, and an intermediate lot (11) was included. Analytical data are given in Table I. For copper in I-B and iron in I-A and I-B, the actual concentration is thought to be near the limit given, i.e., about 0.1 ppm. For titanium, vanadium, and chromium in III-B, the actual amounts are thought to be, like those in III-A, substantially lower than in the zone-refined lots (these elements concentrate in the solid on freezing). Data are given later for some additional lots surveved. B) Specimen Preparation and Procedure. one by 3 cm blanks with a notched stem were cut from 1-mm cold-rolled sheet, annealed 24 hr in air at 650°C, and quenched in an air stream (42°C per sec initial cooling rate, 100 sec to cool to 100°C). The high annealing temperature maximized diffusivities and approach to equilibrium impurity distributions. A water quench, in principle more efficient in preserving the distribution established, was undesirable because the boundaries were almost plane and they tended to shear and migrate during the quench and thus to be separated from any existing impurity atmosphere. Test procedures, previously described,3 involved electropolish-ing, etching 2 min in 10 pct HF at 24.0°C, and expos-

Jan 1, 1969

By E. W. Dewing

The nature of solid solutions of sodium in non-paphitic carbon at temperatures near 1000°C has been investigated by an electrolytic technique. The activity coefficient is found to vary strongly with the heat-treatment temperature of the carbon, and an analysis of the energy terms involved suggests that this is due to variations in the Fermi level. The diffusion coefficient for sodium is in the range implying that the sodium atoms (or ions) are not bound to specific sites on the carbon, in agreement with lack of evidence for specific compounds in the activity -composition curves. In the light of These results phenomena occurring in aluminum reduction cell linings are dis-cussed. It is concluded that sodium migrates by diffusion through the carbon lallice and not the pores, and that A14C9 is formed within the lining hy The excess of NaF invariably found in used linings is formed by this reaction and by air oxidation: There has recently been much interest in the swelling of carbon which occurs when it is made cathodic in an aluminum electrolysis cell, and there is general agreement that the phenomenon is due to the penetration of sodium atoms, derived from the reaction on the carbon lattice. (NaF and AlF3 are constituents of the fused-salt electrolyte.) The low-temperature lamellar compounds of potassium with graphite are well-known, and one compound between sodium and graphite has been reported.4 There is, however, virtually no information on the basic chemistry of the interaction of sodium with nongraphitic carbon at high temperatures, although Dell3 has made some fundamental studies of rates of penetration. At the time the present work was carried out these were not available. Rapoport and samoilenkol had measured rates of physical expansion in a dilatometer, using the fractional increase in length of a carbon specimen after electrolysis in a cryolite bath for 2 hr as an index of susceptibility to cathodic swelling. Work here with a similar apparatus showed that expansion (of a 1.5-in.-diam cylindrical specimen) ceased in less than 20 hr, and that the final expansion was much more reproducible than the value at some intermediate time. This suggested that an equilibrium was being set up, and that a thermodynamic approach was required. The results obtained are not as accurate as had been hoped, but they are the only ones of their type available and have enabled useful conclusions to be drawn. The experimental work was divided into two parts: an investigation of the activity-concentration diagram for sodium in carbon, and a rough determination of the diffusion rate. For the former, most of the experiments were made with petroleum coke even though this is not a form of carbon used in cell linings. It has the advantages, however, that it is a homogeneous material, that it is low in ash, and that its structure is reasonably well understood. Anthracites and coal cokes gave results of the same type as obtained with petroleum coke, but the reprodu-cibility from specimen to specimen was extremely poor. EXPERIMENTAL 1) The Activity-Composition Diagram for Sodium in Carbon. The petroleum coke was ground, pressed at 40,000 psi into plates 19 by 9 by 2 mm without added binder, and heat-treated. The sodium activities were established by an electrolytic technique. The carbon was made anodic in a cryolite bath with an aluminum cathode, and a controlled potential, E, applied so that the sodium activity at the anode was given by ln Na = 1n asa - EF/RT [21 where as, is the sodium activity generated by Reaction [I]. The relative activity is sufficient for many purposes and is simply given by The value of Na not at present known, but when the thermodynamics of the Na-A1 system have been worked out it can be derived from the equilibrium

Jan 1, 1963

By T. L. Joseph, G. Bitsianes

The gaseous reduction of dense iron ore is a topochemical process in which reduction takes place at distinct interfaces between solid phases or layers. Under normal conditions, these interfaces remain parallel to the exterior surface of the ore body as they move inward. Certain conditions, such as cracking, high porosity, impurities, entrapped residual oxides, may cause departures from normal topochemical behavior. THE gaseous reduction of dense iron ore proceeds at interfaces between several solid phases or layers.',' Under normal conditions, these interfaces progress inward and remain parallel to the exterior surface of the ore body. This topochemical behavior is clearly illustrated in Fig. 1 which shows partially reduced specimens of natural and synthetic hematite. Using a coordinated sequence of macro, micro, and X-ray examinations, the authors1-'2 found that the number of interfaces and participating phases was in agreement with the Fe-0 system. Above 570°C, reduction of the ore involved a maximum of three common boundaries between four solid phases: iron, wiistite (Fe,O), magnetite (Fe,O,), and hematite (Fe,O,). Below 570°C, reduction proceeded through two interfaces between three phases: iron, magnetite (Fe,O,), and hematite (Fe,O,). The decrease in the number of phases below 570°C was due to the instability of wiistite below this temperature. The sequence of phases was also consistent with the equilibrium requirements. For example, the layers of iron oxides that were formed in topochemical fashion were always orientated in the order of increasing oxygen content. Thus, in Fig. 1 an outer layer of metallic iron is followed in turn by a thick intermediate band of black wiistite, by a thin layer of light magnetite, and finally by a relatively large core of hematite. This arrangement of the oxide layers was due to restrictions in reducing conditions which were imposed by the physical structure of the solid. The highly reducing gas on the outside of the particle gradually lost its reducing power as it penetrated into the specimen. On a macro scale, the layers of the various oxides appeared to be sharply defined and uniform in composition. Microexamination of the sections, however, revealed that the interfaces did possess measurable widths which varied with the porosity and chemical activity of the oxide phase undergoing reduction. For example, Fig. 2 shows three interfaces in a dense hematitic ore which was partially reduced at 850°C. At the iron-wiistite interface where the greatest porosity developed, the reaction proceeded over a zone 25 to 30 microns in width. Toward the interior, the interfaces became progressively narrower until at the magnetite-hematite boundary the reaction zone was about 1 micron wide. In this region the structure was exceedingly dense; the hematite possessing a porosity on the order of 3 pct. A careful micro study across polished layers of the various oxides revealed generally homogenous and single-phase structures. As reported in a previous paper,' the wiistite layer was characterized by an increase in oxygen content with depth of penetration. The topochemical behavior of reduction was studied in six types of ore of different origin, composition, and physical structure. In most cases, reduction proceeded at the boundaries of well defined layers or phases, and this behavior may be regarded as normal for most dense fine grained ores. Deviations from Ideal Topochemical Behavior A number of deviations from the normal topochemical behavior were noted. In these cases, the continuity of the reduction interfaces was disrupted in one of four ways: 1—Cracking of the specimen interrupted the geometric configuration, and the interfacial advance was no longer parallel to the exterior surface. 2—As a result of high porosity, the interfaces were spread over an appreciable distance and all but obliterated. 3—Impurities in the ore promoted a variety of deviations, including cracking. 4—A residual oxide phase was entrapped in the reaction product and left behind the advancing macro interface. Results from Cracking: A crack leading into the interior of an ore specimen presents a path of least resistance for the counter-flow of reducing gases and gaseous reduction products. Higher reducing conditions can be maintained along such cracks and reduction accordingly will propagate well ahead of the normally advancing reduction interfaces. Cracking was caused by a number of factors, one of which was the thermal spalling of impurities in the massive form. A more general type of cracking was due to reduction and was found in all dense varieties of natural and synthetic hematite, particularly in the temperature range of 500" to 700°C. The effect is shown clearly in Fig. 3. In this case, a dense sphere of pure hematite was partially reduced at 650°C for 100 min. The macrosection shows that one large reduction crack had penetrated the specimen and disrupted the normal topochemical advance of the interfaces. The outer layer of iron was only slightly affected but the thin dark layer of wiistite, adjacent to the ferrite, had widened perceptibly as it progressed along the crack. Farther inward, the magnetite layer was greatly disrupted and had penetrated irregularly to form islands of unaltered white hematite. A great deal of internal cracking is evident in the magnetite phase. From a practical point of view, the cracking of dense ores in the blast furnace could lead to desirable as well as undesirable effects. The general result

Jan 1, 1956

By Thomas P. Forbath

THE sudden realization that known sulphur reserves amenable to mining by the Frasch hot water process are nearing exhaustion focused attention on widely scattered surface deposits throughout the world. These deposits are not necessarily of lower sulphur content than ores located underneath Louisiana or Texas salt domes which usually average about 30 pct sulphur disseminated in limestone matrix. Their near surface occurrence, however, renders exploitation by the Frasch process impossible. As is well known, the Frasch process depends on the presence of 500 to 1000 ft of overburden and cap rock above the sulphur deposits to permit melting underground sulphur in place by diffusing hot water under pressures of 200 to 600 psig in the formation and raising the molten sulphur to surface by air lift. This process renders possible the production of pure sulphur which is 99.5 pct pure without any subsequent treatment. Surface deposits contain sulphur in the same range of concentrations as the salt dome deposits, i.e., from 10 to 50 pct sulphur, associated with various gangue materials such as silica, limestone, and gypsum. The pirincipal distinction, then, does not lie in the percentage of sulphur contained in the ore, but in the geological nature of the deposit. A recent study' of the world sulphur supply situation estimated 1950 sulphur production in the free world countries at 5.6 million long tons, of which the United States produced 5.2 million tons, or 93 pct of the total. While America's domestic needs alone would have been covered by national production, about 1.4 million tons were exported during the same year. Despite all the steps which are being taken to restrict use of elemental sulphur and to force the fullest possible development of alternate sulphur sources here and abroad, the deficit in elemental sulphur production will probably increase with time. As a result of intensive prospecting for oil throughout the Gulf Coast area discovery of significant new salt domes is held unlikely. With the growing scarcity of sulphur and what appears to be an inevitable rise in price, recovery from deposits not amenable to Frasch-process mining assumes greater economic importance. Untapped Reserves The most important deposits in this category are located in Sicily, where elemental sulphur occurs in Miocene limestone and gypsum formation. Sulphur content of these ores ranges from 12 to 50 pct with an estimated average of 26 pct. Although quantitative estimate of these reserves is not available it is held that they exceed 50 million tons of sulphur. Similar deposits occur also on the mainland which contribute about one-third of Italy's total current annual production of 230,000 tons, but these are known to be nearing exhaustion. Significant surface deposits of volcanic origin are located in South America, Japan and western United States, silica being characteristic gangue con-stituent. The largest of these deposits are in South America. More than 100 extend over a zone 3000 miles long, paralleling the west coast of South America. 'Total sulphur content of these deposits has been estimated to be as high as 100 million tons. The main islands of Japan also possess at least 40 known volcanic sulphur deposits with probable reserves of 25 to 50 million tons.' Prospected reserves in western United States might amount to 2 million long tons, principal deposits being located in the northwestern part of Wyoming, southern Utah, and eastern California. Volcanic deposits of lesser importance are found around the Mediterranean, in Turkey and Greece, and in Africa, Egypt, Abyssinia, and Somaliland. Beneficiation Methods Different methods of beneficiation have been used in these various locations. In Italy the Calcarone kiln and Gill regenerative furnaces are used exclusively. Both utilize heat liberated by burning part of the sulphur in the ore to liquify or vaporize the remaining sulphur, which is recovered by solidification or condensation. The Calcarone kiln is of conical shape, generally 35 ft in diam at base and 18 ft high. A kiln of 25,000 cu ft capacity burns for about two months and yields about 200 tons of sulphur. The Gill furnace consists of a series of chambers with domed roofs. Sulphur is burned and melted in one chamber at a time and the hot combustion gases are used to preheat the ore charge in the subsequent cell. These furnaces operate on a cycle of 4 to 8 days. The recovery yield of both systems is about 65 pct. Sulphur losses amount to 25 pct through the combustion to sulphur dioxide; about 10 pct is retained in discarded calcines. Ores containing less than 20 pct are not considered suitable as furnace feed. These methods are not only wasteful because of the low recovery obtained, but represent a serious atmospheric pollution problem. Sulphur produced ranges from 96 to 99 pct purity and thus does not match Texas or Louisiana sulphur. Owing to the present shortage, sulphur in the Middle East sells

Jan 1, 1954

By C. Dirksen

This study investigates whether oxygen consumption during segregated forward combustion may be affected by natural convection. Linear theory indicates that thermal instability occurs in a horizontal porous medium when the modified Rayleigh number N 'Ra exceeds a critical value of about 40. Most experimental results, including those described here, indicate this value to be about an order of magnitude smaller. N ', is derived from "differential similarity" and the proper time scale factor is also obtained. The critical value of N'ra for a horizontal, water-saturated porous medium at atmospheric pressure subjected to a uertical temperature gradient was found to be about 3.0. The ambiguity in the value of N'R, arising when fluid properties cannot be assumed constant is indicated. Natural convection was observed for oblique systems below N 'Ra , while simultaneous horizontal flow did not affect N Racrit. The expected range of values for the various parameters pertaining to segregated forward combustion is indicated and the corresponding values of N 'Ra calculated. Only under very favorable conditions, such as high permeability, high pressure and low top temperature, can the critical value of N 'R, be exceeded. Thickness of the convection layer should not become too large, since the time required to obtain significant mixing is proportional to the square of the thickness. For an oblique combustion frant the conditions for significant mixing may be less strenuous. LNTRODUCTION Laboratory1,2 and field314 experiments have shown that a markedly upgraded oil can be produced by in situ forward combustion. Under certain conditions injected air may move through a high permeability, gas-saturated channel over the oil-saturated layer, while combustion takes place, exclusively, at the horizontal interface (Fig. 1). Such a channel may be a natural gas cap, or it may result from a forward combustion process in which injected air and combustion gases fingered through the top of the formation, causing a premature breakthrough at the production well. In this particular case of segregated forward combustion, the air stream moves parallel to the combustion front. Molecular diffusion and transverse mechanical dispersion will be insufficient to cause all the oxygen in the air stream to reach the combustion front. When the oxygen in the air stream is not completely consumed in the combustion process, it will reach the production well and create a serious fire hazard. In addition, the reduced efficiency may make the process economically unprofitable while also serious corrosion problems may be experienced in the production we11.3 This undesirable situation should, therefore, be prevented. However, in a situation as depicted in Fig. 1, an unstable temperature gradient exists in the gas phase. The combustion is taking place at the lower boundary at a nearly constant temperature that may be anywhere from 600 to 1,200F, depending on the conditions. The upper boundary of the gas phase is overlying, impermeable rock; its temperature might be around 100F, but may increase to 300F or higher due to conduction and convection as the combustion process continues. This represents a steep temperature gradient and it is conceivable that under those conditions free or natural convection will take place in the gas

Jan 1, 1967

By Niels Hansen

The substructure formed by drawing at room temperature in aluminum (99.5 and 99.998 pct purity) and in recrystallized aluminum aluminum-oxide products containing from 0.2 to 4.7 wt pct of aluminum -oxide was examined by transmission electron microscopy, and the flow stress of the drawn materials was measured by tensile testing at room temperature. A sub-grain structure was present after a reduction in area by drawing of 10 to 20 pct, and the subgrain size was observed to decrease with increasing deformation. The tensile data show that the increase in flow stress (0.2 pct offset) by drawing from 10 to 95 pct depends on the reduction in area, not on the composition of the materials. Dispersion strengthening and subgrain bowzdary strengtlzening contribute to the flow stress, and these strengthening processes have been found to be linearly additive. The flow stress (0) can be related to the subgrain size &) by the Petclz relation = uo + k . t, where go is dependent on the composition of the products and k is approximately the same far all materials. THE microstructure of dispersion-strengthened aluminum aluminum-oxide products consists of small oxide plates distributed in an aluminum matrix. The matrix structure depends on the manufacturing history, and in hot-worked as well as cold-worked products the matrix is divided by subgrain (or dislocation) boundaries. For hot-extruded products it has been shown1 that dispersion strengthening and subgrain boundary strengthening are linearly additive, and the flow stress (0.2 pct offset.) at room temperature has been related to the subgrain size (ts) by a Petch equation,2,3 s = so + k . ts-1/2, where s0, increases with increasing oxide content. For cold-worked products containing subgrains no systematic work has been reported, and it was the aim of the present study to examine the microstructure and the relationship between the flow stress and the subgrain size for such products. The behavior of' aluminum aluminum-oxide products depends on the purity of the aluminum matrix, and aluminum of the matrix purity (99.5 pct) was included in the investigation. The literature contains few data about the behavior of this impure aluminum, and aluminum of a higher purity (99.998 pct) was therefore also examined. As regards the relationship between the flow stress and the subgrain size in cold-worked dispersion-strengthened products, no systematic work has been reported. For aged cold-worked structures containing fine precipitates (Fe-Mo carbide) a Petch relation has been found,4 and it has been shown that the k value NlELS HANSEN is Head, Metallurgy Department, Danish Atomic Energy Commission, Research Establishment Riso, Denmark. Manuscriot submitted January 9, 1969. IMD is approximately the same as in iron, whereas the s0 value is higher owing to the presence of the precipi-tates. Investigations of metals such as tungsten,' ferrous metals,4,6 and molybdenum7 cold drawn or swaged at room temperature have shown that the flow stress can be related to the subgrain size by a Petch relation when ts is taken as the subgrain size perpendicular to the direction of deformation. For aluminum no work has been reported on the relationship between the flow stress and the subgrain size after deformation at room temperature, whereas for aluminum tensile strained at different temperatures in the range -183" to 375°C a Petch relation has been found by taking ts equal to the subgrain size.' In the present study two aluminum materials (99.998 and 99.5 pct) and three aluminum aluminum-oxide products (containing 0.2, 1.0, and 4.7 wt pct oxide) were drawn at room temperature to reductions in area from about 10 to about 95 pct. The structures were studied by transmission electron microscopy, and the flow stress (0.2 pct offset) was measured at room temperature. EXPERIMENTAL Materials. The materials are given in Table I together with the chemical analysis. The three aluminum aluminum-oxide products were manufactured from aluminum powder that had been compacted and Table I. Chemical Analysis of Materials Al203 Fe SI Material wt pct wt pct wt pct 99.998 pct* - 0.0004 0.0012 Aluminum 99.5 pctt - 0.36 0.16 Aluminum AlMD13† 0.2 0.16 0.12 Aluminum- -Oxide AlMD105† 1.0 0.26 0.18 Products SAPISML960s† 4.7 0.22 0.19 *Other impurities: O.0004 pct max each of Cu and Zn (supplier's analysis). †Other impurities: 0.03 pct max Cu. 0.02 pct max each of Mn, Mg, Zn, Ti. Table 11. Mean Diameter of Aluminum-Oxide Particles in Extruded and in Cold--Drawn Aluminum Aluminum-Oxide Products Mean Diam. of A1203-Plates* Material State A AlMD105 Extruded 540 Cold Drawn 97 pct 510 SAP ISML 960 Extruded 770 Cold Drawn 95 pct 820 *The standard deviation of the mean is approx. 5 ±pct.

Jan 1, 1970

By K. A. Gschneidner, O. D. McMasters, T. J. O’Keefe

X-ray diffraction, differential thermal, ad rnetallo-graphic methods were used to establish the Dy-Pb Phase diagram. Lead additions lower the 1377°C transformation temperature of dysprosium to 1360°C leading to an inverted peritectic reaction. The 327°C melting point of lead is lowered by dysprosium additions to about 326°C yielding a eutectic reaction. A second eutectic reaction occurs at 13.3 at. pct Pb and 1200°C. The dysprosium-richest intermetallic compound DysPb3 melts congruently at 1695°C and crystallizes in the hexagonal Mn5Si3 (D8,) type structure. The peritectic decomposition temperatures for the remaining compounds are Dy5Pb, at 1555C, DyPb2 at 955C, and DyPb3 at 880°C. A fifth compound near the DyPb stoichiometry exists over a 310°C temperature range decomposing at 1130°C by means of an inverted peritectic reaction and melting incongruently at 1440°C. The crystal structures of the compounds are discussed. A systematic study of the rare earth-lead alloy systems is underway in an effort to supply information concerning the alloying behavior of the rare earth metals. The Dy-Pb phase diagram is the fourth system to be investigated in this study. The Yb-Pb,1 Y-Pb,2 and Eu-Pb 3 diagrams have been published recently. Utilization of the rare earth series of metals as a research tool in this manner should yield a better understanding of alloy formation. EXPERIMENTAL PROCEDURE Materials. The lead used in this investigation was obtained from Cominco Products, Inc., and was specified to be 99.99 pct pure. The dysprosium was prepared in this Laboratory by the calcium reduction of the fluoride followed by distillation of the dysprosium. The major impurities in the dysprosium in ppm are: A1 (<40), Ca (400), Er (<50), Gd (<200), Ho (<200), Mg (<50), Si (30), Ta (400), Tb (<100), Y (<50), 0 (651, H (15), N (not detected), F (430), C (35). Alloy Preparation. Most of the alloys were prepared by melting weighed amounts of dysprosium and lead in sealed tantalum crucibles. The tantalum crucibles were sealed by are-welding in a He-Ar atmosphere welding chamber. Thus the alloys are in contact with He-Ar at about 1 atm pressure. Homogenization was achieved by holding them in the liquid state for about 1 hr, cooling, inverting the crucibles, remelting, and repeating the process at least twice. Since these alloys were prepared in sealed tantalum crucibles, chemical analysis for final composition was thought to be unnecessary. No detectable reaction of these alloys with the tantalum crucible was observed by metallographic examination. Metallographic evidence was also used to confirm the homogeneity of some of the alloys prepared in this manner. The compositions of a few alloys, which were prepared by nonconsum-able are-melting, were corrected for the small weight losses involved by assuming that the weight loss is due to vaporization of lead. The specimens obtained from the alloy samples were prepared under a dry-argon atmosphere because they were rapidly attacked by air and moisture. Thermal Analysis. Differential thermal analysis methods were used to determine the liquidus curves and reaction horizontals of the system. Both Pt vs Pt + 13 pct Rh and W + 5 pct Re vs W + 26 pct Re thermocouples were used to measure the temperature. An X- Y recorder was used to record the specimen temperature and differential electromotive force between the specimen and molybdenum standard. The arrest temperatures were measured potentiometri-cally. The accuracy limits (* values) associated with the reaction temperatures obtained by this method were estimated on the basis of both the reproducibility of the particular temperature value and the accuracy of the thermocouple at a given temperature. Liquidus temperatures were obtained from cooling arrest data while both heating and cooling arrest data were used to establish the horizontals of the diagram. Heat treatments during the thermal analyses of the alloys between 40 and 70 at. pct Pb were necessary in order to approach equilibrium conditions. The samples were held at temperatures between the various peritectic horizontals for l to 2 hr before the thermal analyses were continued. The entire range of compositions was investigated at the expense of a minimum amount of materials by adding appropriate amounts of lead to master alloys. More than sixty alloys were analyzed by this differential thermal method and for each alloy the results given herein are taken from two or three heating and cooling cycles. X-Ray and Metallographic Methods. Slice specimens for metallography and powder specimens for X-ray diffraction were prepared from rod-shaped samples which had been melted in sealed 0.62 5-cm-diam tantalum crucibles. The specimens were heat-treated in sealed tantalum crucibles which were protected by sealing them in argon-filled quartz ampules. Quenching was accomplished by breaking the ampules in ice water after heat treatment. X-ray powder specimens were sealed in 0.3-mm-diam glass capillaries under a dry-argon atmosphere. Copper, iron, and chromium radiation were used to obtain the powder patterns for these alloys. More than 150 powder patterns were obtained for specimens of various compositions and heat treatments. Included in these were several patterns for specimens which had purposely been oxidized. Patterns from specimens which had been accidentally exposed

Jan 1, 1969

By ALFREDO INTZAUGARAT, MIGUEL BERRO

During the years 1943 through 1945, there was a decrease in the total oil production in Argentina. In the fields of Comodoro Rivadavia (Chubut Territory) and Mendoza and Salta Provinces, the production obtained was as shown in Table I. The only place where there was a small increase was Plaza Huincul, in the Neuquen Territory and Lunlunta, in the Mendoza Province.

Jan 1, 1946

By Thomas C. Wilder, Walter E. Galin

Measurements of the electromotive force of the cell at 995°C have shown that the cell may be used to detennine the zinc content of molten Cu-Zn alloys to the nearest 0.05 wt pct. The cell is used for brass melts to which no ZnO is added intentionally, because essentially all oxygen in the Cu-Zn-O system is present in the form of ZnO. The cell is also used to detev,nine the thernodynamic activity of zinc for Cu-Zn al1oys of the brass composition range, from which the equilibrium partial pressure of zinc for such alloy may also be calculated. The electrochemical measurement of the concentration of the most active metal in other engneering- alloy systems by a similar technique is also considered. IN recent years there have been many studies concerning the direct electrochemical measurement of oxygen content in molten engineering metals.&apos; These investigations employ galvanic cells in which the electrolytes are various solid mixed-oxides which conduct current by movement of oxide ion vacancies under the influence of an oxygen potential gradient. Similar cells have also been used to measure the thermodynamic properties of mixing of solid alloys,&apos; one component of which has a much greater affinity for oxygen than the other component(s). One alloy system of obvious engineering importance comprised of two metals of greatly differing affinity for oxygen is copper-zinc. At the casting temperature of molten brasses, the zinc concentration is very difficult to control not only because its vapor pressure is very high, but also because of its high affinity for oxygen to form ZnO. Inasmuch as brass castings may be required to have a zinc concentration within very narrow limits, it would be advantageous for the brass industry to have a means for quickly measuring the zinc content in the molten alloy just prior to pouring. A calculation based on earlier thermodynamic studies of oxygen and zinc in dilute solution in binary Cu-O and CU-Z&apos; alloys indicates that the oxygen concentration of molten 70 wt pct Cu-30 wt pct Zn brass must be much less than 1 ppm for the separate phase ZnO not to exist in the ternary Cu-Zn-O system. Thus it can be assumed that all molten brasses, both in the laboratory and in the foundry, are sufficiently saturated with oxygen for the separate phase ZnO to be present. In view of the foregoing reasons, the cell investigated at 995°C for the purpose of measuring the zinc concentration in molten copper-zinc alloys, particularly those of brass compositions. In this cell the left hand electrode is a reference electrode comprised of a mixture of the pure powders of nickel and nickel oxide, to which a platinum contact is made. The electrode of interest is a molten Cu-Zn alloy of unknown zinc concentration with a tantalum wire contact. The electrolyte is the commercially available (Zircoa) calcia stabilized zirconia. The ZnO in the Cu-Zn electrode compartment is not intentionally added, but is naturally present as a result of the infinitesimal amount of oxygen required for its formation in this alloy system. In cell [A] nickel oxide is reduced at the cathode where O= represents the electrolyte. At the anode dissolved zinc of the Cu-Zn alloy is oxidized to form ZnO(s) in its standard state Thus the overall reaction is for which the molar free energy change is where 5 is the Faraday equivalent (23,063 cal per v equivalent), is the electromotive force of the cell in volts after correction for the Pt-Ta thermocouple, FOf (ZO) and AFF (NO) are the standard molar free energies of formation of the respective oxides, and a2n is the thermodynamic activity of zinc in the molten Cu-Zn alloy. The reference state of zinc in this case is taken to be the pure liquid. At constant temperature all the terms of Eq. [I] are constant except and azn Thus since all other participants in the electrochemical reaction are in their standard states, the change in the electromotive force of Cell [A] is represented only by a change of the thermodynamic activity of zinc at constant temperature. The zinc concentration is related to the activity by sampling the alloy for chemical analysis after cell measurements are taken. EXPERIMENTAL A typical cell construction is shown in Fig. 1. This and other experimental details were similar to that described earlier with the exception of some minor modifications which are detailed below.

Jan 1, 1970

By Dilip K. Das, Douglas T. Pitman

ONE of the major uses of barium in metallic form is as a getter material in vacuum tubes. Because of the high chemical reactivity of the metal, Ba-Al alloys are extensively used. Numerous methods for the preparation of Ba-Al alloys have been published, a few of which1-4 are cited here. Most of these methods were found to be quite elaborate, involving the reduction of BaO, and not too well adapted for the close control of the final composition of small amounts of alloys prepared for laboratory use. A simple laboratory method for the preparation of Ba-A1 alloys in small batches starting from pure metals was devised, so that it was possible to control the desired compositions to within 1 pct. The pertinent features of the alloy system Ba-Al5 are 1) an intermediate compound BaAl, with the melting point of 1050°C, and 2) a eutectic between aluminum and BaAl4 at 98 pct Al. The accompanying sketch shows the experimental arrangement for the preparation of the alloys. Weighed amounts of aluminum and barium were placed in an alumina and a stainless steel crucible, respectively. According to the supplier&apos;s specification, the purity of the metals used in the alloys is as follows: a) aluminum rods—99.9 pct Al, and b) barium rods—99.5 pct Ba. The stainless steel crucible, tapered at the bottom and having a 1/16 in. diam hole, rested on top of the alumina crucible. The assembly was placed inside a graphite sleeve which rested on a refractory platform. The platform moved the assembly up and down through the field of a radio frequency coil. A glass bell jar was placed between the crucible assembly and the radio frequency coil to maintain a steady flow of helium around the melt. A small window was cut out on the wall of the alumina crucible to observe the progress of the re- action and to record the temperature with an optical pyrometer. The platform was first raised high enough to move the barium out of the radio frequency coil field in order to allow only the aluminum to melt. The assembly was then lowered so that the barium began to melt and flow out through the small orifice into the molten aluminum. In order to keep the violence of the exothermic reaction under control, the rate of flow of barium was carefully regulated by raising or lowering the crucible assembly. All the samples prepared by this technique were examined by a Norelco X-ray diffractometer using CuKa radiation, The diffraction specimens were prepared by placing the finely powdered samples in flat specimen holders. The Ba-Al alloys prepared with a high barium content were found to consist mainly of BaAl4. The structure of BaAl4 has previously been reported by Alberti and Andress.8 They found that BaAl4 was body-centered-tetragonal with an a0 = b0 = 4.530Å and c0 = 11.14Å. An alloy whose composition was found by chemical analysis to be almost 100 pct BaA1, was used to determine the relative intensities. The d-spacings were obtained from the same alloy to which a small amount of tungsten had been added as a calibrating material. Accurate values for a, and c, were calculated according to the method proposed by Taylor and Floyd.&apos; The calculated values are: a, = b, = 4.566Å and c0 = 11.250Å. The measured d-values for BaAl4 are shown in Table I along with relative peak intensities above background and hkl indices. Acknowledgment The authors are grateful to L. J. Cronin, the head of the Techniques Dept., for suggesting the problem and for his constant interest. References 1Froges and Camargue: German Patent No. 809107, 1951. French Patent No. 935324, 1949. 2E. Bonnier: Annales de physique, 1953, vol. 8, pp. 259-312. 3M. Orman and E. Zemhela: Prac Institute of Metals; 1952, vol. 4, pp. 437-445. 4E. Fujita and H. Yokomizo: Reports Gov. Chemical Industrial Research Institute, Tokyo, 1952, vol. 47, pp. 291-297. 5E. Alberti: Ztsch. fur Metallkunde, 1934, vol. 26, p. 6. 6E Alberti and K. R. Andress: Ztsch. fur Metallkunde, 1935, vol. 27, p. 126. 7 A. Tnslor and R. W. Floyd: Acta Crystallographica, 1950, vol. 3, p. 285.

Jan 1, 1958

By G. B. Misra

While investigating on the aerodynamic resistance of airways supported with peripheral timber sets, at regular intervals, the following theoretical equations were developed by the author to estimate the resistance coefficient of such airways: [ ] for S < 1, where f is Darcy-Weisbach resistance coefficient of the airway, C is modified drag coefficient of the supporting member, D is equivalent diameter of the bare airway, 8 is ratio of the approach velocity over the sets to the average velocity of the bare airway, A is cross-sectional area of the bare airway, a is projected frontal area of the sets, A., is cross-sectional area of the air stream at the vena contracta inside the set, S is spacing of the sets, f, is resistance coefficient of the bare airway, l is length of aerodynamic influence of sets, p is perimeter of the bare airway, p, is setted portion of the perimeter of the bare airway, pe is unsetted portion of the perimeter of the bare airway, and P shielding factor. The equations were verified experimentally in a model rectangular airway supported with one- (bars), three-, and four-piece sets of square-section timber of three different sizes and were found to hold true. The work has been further extended to one-, three-, and four-piece sets of round timber of 2.6, 3.2, and 3.8 cm diam with the same experimental set up. Tests have been carried out for spacings of 25, 50, 75, 100, 150, and 200 cm over a regime of flow defined by the Reynolds number (with respect to the equivalent diameter of the bare duct) ranging from about 1.5 X 106 to 5 X 106 using the same experimental techniques. The values of f are calculated in the manner indicated in [Ref. 1]. Unlike with square-section timber, the resistance coefficient f of the airway setted with round timber shows a distinct variation with the Reynolds number of flow. This conforms to observations made by Sales and Hinsley.2 In order to have a comparable value of f for all types of sets with all sizes of timber, it was necessary to select the value of f at a fixed Reynolds number of flow. Since f is chiefly a function of the drag coefficient of the sets, the appropriate Reynolds number RE is that with respect to the diameter of timber in the set. Considering the diameters of timber used and the regime of flow over which measurements were made, f was chosen at a value of RE = 20,000 in all cases. The f vs. S curves are maximal in nature and in conformity with theory, the f vs. 1/S curves are straight lines up to a value of S = 1 beyond which they show a distinct flexure. The observed values of 1, the length of aerodynamic influence of sets, agree with the relation 1 = 42 e, developed for square-section timber sets, thus suggesting that the shape of timber has little influence on the length of aerodynamic influence. The value of the modified drag coefficient CD for round timber was calculated in the same way as for square timber in Ref. 1, taking the contraction factor Z = 1.5 for round-edged constrictions. CD has an average value of 0.96 with a standard deviation of 6.08% as compared to the free stream drag coefficient of 1.2 at RE = 20,000 for long cylindrical obstructions The shielding factor [ ] is plotted against S/1 in [Fig. 1]. The curves are more or less independent of the size of timber, but are different for the different types of sets, possibly due to their different degree of symmetry. Values of f calculated by the author&apos;s [Eqs. 1 and 2], using experimental values of CD&apos; and [ ] and taking I = 42 e, are plotted in [Fig. 2] against experimentally measured values of f for different types of sets with different sizes of round timber. The values agree closely with a standard deviation of only 5%, thus establishing the veracity of the theoretical equations developed by the author for round timber as well. A comparison was made between the Xenofontowa4 equations (the only other reasonable relations available for the estimation of the resistance coefficient of supported airways) and the author&apos;s [Eqs. 1 and 2] by comparing in [Fig. 3] the values of the resistance coefficient f computed by the Xenofontowa relations with those experimentally measured by the author. In order to make

Jan 1, 1975

By K. E. Nelson

The effect of thorium and zinc variations on the strength and 100-hr creep characteristics of Mg-Th-Zn-Zr alloys was investigated. Optimum resistance to creep at 650° and 700°F are attainable within a certain range of thorium and zinc contents. This range does not conform to that which develops maximum tensile properties. RAPID advances have been made during the last few years in the development of magnesium alloys for elevated temperature applications demanding high resistance to creep. The beneficial effect of rare-earth metals on the creep resistance of magnesium alloys has been emphasized by a number of publications1-13 and such alloys are now in commercial production. The use of thorium as an alloying ingredient in magnesium was mentioned by McDonald and also in two Alien Property Custodian patent applications.10,17 The initial observation of Sauerwald that thorium contributes still higher creep resistance to magnesium than is attainable with rare-earth metals has recently been substantiated.&apos;" " In fact, it has been demonstrated that the useful temperature range of magnesium alloys is appreciably extended by the use of thorium. In all cases, it was observed that zirconium must be included in the alloys in order to render them fine grained and more readily castable. Several recent publications:2-27 indicate that a still further improvement in creep resistance and a further extension of the useful temperature range can be realized by the addition of zinc to alloys. The primary purpose of this paper is to present the results of a comprehensive study of the effect of zinc on the strength and creep characteristics of Mg-Th-Zr alloys. Compositions covering the range of thorium content from M to 6 pct and zinc content from 0 to 5 pct have been investigated. The creep characteristics at 650" and 700°F reported in this paper are based on results of tests of 100-hr duration. It is appreciated that creep tests of 100-hr duration might not yield adequate data for design purposes for parts with much longer expected life. However, for the purposes of the present discussion, it is felt that the combination of stresses and temperatures used in the 100-hr creep tests have yielded a clear representation of the compositional variation of creep resistance at the temperatures investigated. Creep tests of 1000-hr duration are now in progress on a few of the most promising alloys. Preparation and Testing of Alloys The alloys studied in this intensive investigation were prepared in 25 lb capacity mild steel crucibles. The thorium, zinc, and zirconium were alloyed and poured as described in earlier publications The thorium was introduced into the melt in the form of a Mg-Th hardener," the zinc added in the metallic form, and the zirconium alloyed in the form of the commercial hardener containing magnesium and 30 to 50 pct Zr.10, 26 Fluxing practices for melting and refining were the same as for magnesium-rare-earth metal-zirconium alloys. The melts were sampled for analytical determinations and poured into separately cast 1/2 in. diameter standard tensile bars. The test bars were given a precipitation treatment of 16 hr at 600°F in laboratory furnaces. It has been shown by other tests that a high temperature solution treatment followed by an aging treatment is unnecessary for the development of optimum properties in Mg-Th-Zn-Zr alloys. The selection of 600°F as the aging temperature was based on an attempt to achieve metallurgical stability without coalescence of the undissolved phases and the attendant loss in strength. The thorium, zinc, and zirconium contents of each melt were determined chemically. The zirconium contents are reported in two parts, "soluble" and "insoluble," referring, respectively, to the portions present in the alloy which are soluble and insoluble in dilute HCl acid. Distinction is being made between these two components of the zirconium content in the alloys because it has been found that only that portion of the zirconium content which is soluble in dilute inorganic acids affects the structure and properties of the alloys. The usual impurities consisting of copper, iron, manganese, and nickel were determined spectroscopically. The analysis for each melt is listed in Table I. A description of the methods of tension and creep testing has been detailed in earlier papers. The tests were performed with the cast skin re-

Jan 1, 1954

By Ray W. Carpenter, Ralph Hultgren, Raymond L. Orr

Heats of formation of Au-Zn alloys of compositions Au3Zn and AuZn were rneasured at several temperatures by liquid tin solution calorimetry. The data for Au3Zn show that much smaller heat and entropy effects are associated with the a2- a1 transformation than for the a1 - a transformation. This result is consistent with reported X-ray diffraction studies which indicate that the a1 and (a2 phases have ordered structures which only slightly differ, whereas the a phase is disordered. The heat of formation of AuZn(ß&apos;) does not change significantly between 322o and 8000 K, confirming that the ß&apos; alloy remains highly ordered to high temperatures. Not many measurements have been made of the energies of order-disorder transformations in alloy phases. In many cases these energies may be conveniently determined by measuring heats of formation as a function of temperature. Many alloy phases approximately obey Kopp&apos;s law of additivity of heat capacities; as a consequence their heats of formation do not change with temperature. In ordered alloys, however, a decrease in degree of order with increasing temperature will contribute an endothermic component to the heat of formation. Thus, for ordered phases where other anomalous contributions to heat capacity in the alloy or its pure components are absent, a measured change in the heat of formation may be attributed to the energy of disordering. A portion of the Au-Zn phase diagram1" is shown in Fig. 1. The composition AuZn(ß&apos;) has a well-ordered superlattice structure of the CsCl type at room temperature. The alloy is considered to remain ordered to its melting point,1 although, from X-ray diffraction data and electromotive force measurements of zinc activities, Terpilowski3 concluded that considerable disordering began at -673°K. The Au3Zn composition is a disordered fee solid solution (a) at high temperatures. Between 693o and 543oK, the ailoy orders to form the a1 phase, having a structure based on the L12(AuCu3) type, but with a regular distribution of ordering faults in the c direction, making it tetragonal. Below 543oK, the alloy orders further by means of slight atomic shifts, without diffusion, yielding a complex long-period orthorhom-bic superlattice structure, a2.4-7 Heats of formation of Au3Zn(a2) and AuZn(ß&apos;) were measured at 363°K by Biltz et al.8 by aqueous solution calorimetry. Heat capacities of several alloys between 14.9 and 38.4 at. pet Zn in the range from 373" to 723°K were measured by Iwasaki ef al.6 Stoichiometric Au3Zn, however, was not included in the alloys measured, the nearest composition being 26.1 at, pet Zn. Also, the heating rate used for the measurements, 2 deg per min, may not have permitted equilibrium to be reached in the neighborhood of the transformations. Heat contents of solid and liquid AuZn were measured between 488o and 1138°K by Kubaschewski.9 It was decided to determine the ordering energies of Au3Zn and to check on the possible disordering of AuZn by measuring the heats of formation of these alloys at several temperatures. The present paper reports measurements by liquid tin solution calorimetry of the heats of formation of the three phases of Au3Zn at temperatures within their regions of stability, and of AuZn at a low (322°K) and a high (800°K) temperature. EXPERIMENTAL Alloy Preparation and X-Ray Examination. Ten-gram ingots of Au3Zn and AuZn were prepared by melting weighed amounts of gold (99.95 pct Au) and zinc (99.99 pet Zn) together in sealed evacuated Vycor tubes at 1060°K, followed by rapid quenching. The resulting ingots were homogenized at 900°K for 10 days. The Au3Zn alloy lost no weight in preparation, the loss from the AuZn alloy was enough to introduce an uncertainty of only 0.1 at. pet in its composition. Filings for X-ray examination were taken from various parts of each ingot and strain-annealed at 723°K for 20 min in vacuo. The Au3Zn filings were quenched rapidly to retain the disordered phase. Diffraction patterns were determined with an X-ray dif-fractometer using copper Ka radiation.

Jan 1, 1968

[ ]

Jan 1, 1942

By S. H. Williston

IT not often that bore hole surveys can be checked by actual. civil engineering methods. A recent Arizona survey was checked by normal surveying methods and the comparison of the results should be of value to both oil and mining men. During the summer of 1948 the Phelps-Dodge Corporation, at its Copper Queen property near Bis-bee, Ariz., drilled a 1245 ft, 8 in. diarn, churn drillhole in a mineralized area and cased part of it, intending to use it to transfer mill tailings for stope fill. The hole, as frequently occurs, was not straight, and, in endeavoring to locate the bottom in the underground workings, they found no evidence of the hole at the underground coordinates directly below the surface location. The noise of the drilling tools was reasonably clear, but the direction of sound was uncertain. Preliminary tests with available equipment were not successful in locating the bottom of the hole. Because of the mineralized character of the area and the fact there was some casing in the hole, any magnetic method of well surveying would give results of doubtful value. Sperry-Sun gyroscopic well-surveying instruments were finally used to locate the bottom of the hole. These instruments consist of a gyroscope to determine azimuth and either a pendulum or bubble inclino-meter. A multiple shot camera photographs both instruments on a single film and superimposes the photograph of a watch. Coordination of depth with time at the surface makes it possible to select the corresponding picture for any depth. After making several runs of the empty instrument housing from the top of the hole to the bottom to make sure there were no obstructions in the hole, three surveys on wire line were completed during the afternoon. The three surveys, in which readings were taken at different points in the hole on each survey, were computed and gave the following locations of the bottom of the hole in relation to the surface collar: survey No. 1—24.92 N, 30.30 W; survey No. 2—24.24 N, 31.11 W; survey No. 3—26.54 N, 27.72 W. Then the data from the three surveys were combined into a single set of calculations which gave a location for the bottom of the hole: combined surveys—24.27 N, 30.16 W. (Fig. 1.) Immediately upon the determination of the coordinates at the bottom of the hole, a drift on the 1300 ft level was started toward the indicated loca- tion some 38 ft northwest of the coordinates of the surface location, The bottom of the hole was located within the drift round in which it was expected, and the transit survey run to the actual location of the hole indicated N 27.18, W 29.71. This shows a discrepancy between the well survey and the transit survey of 0.45 ft in the westerly direction and 2.91 ft in the northerly direction. All surveys, both gyroscopic and transit, fell well within the width of an ordinary drift. While this is satisfactory for almost any and all mining requirements, a theoretical examination was made as to reasons for the discrepancy. A study of the course of the hole indicates that considerable right turn or spiral existed, and in all probability the surveying instrument was pulled out of alignment while traversing the turn by approximately 0.05 ft at the top and another 0.05 ft in the opposite direction at the bottom of the instrument. If such an allowance were to be made, the survey calculations would almost exactly correspond with those determined by transit. This sort of discrepancy would be minimized by the use of stabilizing guides. It is unfortunate that physical laws probably effectively prevent the use of gyroscopic instruments in EX and AX diamond drill holes. The directive power of a gyroscope falls off inversely at some rate between the third power and the sixth power of the diameter. Present instruments can be run in casing 53/4 in. ID or over and might be adapted to somewhat smaller diameters, but the difficulty of reducing these diameters to 11/4 in. or 2 in. is almost insurmountable at the present time. Acknowledgment The author wishes to express his appreciation to the Phelps-Dodge Corporation for permission to publish this article, and to the Operating and Engineering Departments for their cooperation on the survey; also to Donald Hering, of the Sperry-Sun Well Surveying Co., who actually made the survey and calculated the results.

Jan 1, 1951