Search Documents

By Ernest Burchard

A RECONAISSANCE of the chrome and manganese'1ore deposits of Culm was made in the spring of 191s by Albert Burch representative of the U. S. Bureau of Mines and the writer representing the U. S. Geological Survey. The object of the study was to obtain authentic information for use of the: United States Government as to the location, character, size, and availability of the Cuban deposits of the ores of these important steel-alloy metals. The Cuban Government courteously detailed Sr. E. I. Montoulieu, a mining engineer connected with the Treasury Department, to act as escort and associate throughout the work on the Island. Mr. George A. Wright, of Baracoa, Cuba, a mining engineer especially familiar with the chromite deposits of Oriente Province, was a member of the party from Feb. 25 to Mar. 20. It was possible to visit most of, the chrome-ore deposits that seemed to be of promise, but there was not sufficient time to visit all that were brought to our attention, some of which may have merit. Furthermore, no attempt was made to examine the extensive chromiferous iron-ore deposits of the Mayari, Moa, and Cubitas districts, as these deposits cannot be regarded as sources of chromium except indirectly. At the close of the field work the essential data concerning the quantity and quality of ore probably available for shipment during 1918 and 1919, in the event of the continuation of the European war, and of the tonnage of ore in reserve, were furnished to such Government bureaus as were interested, including the Shipping Board and the War Industries Board, and as soon as chemical analyses of the chrome ores could .be obtained, a press bulletin on the subject was published by the Geological Survey. In the present paper the engineering data, and tonnage estimates contained in the unpublished notes of Mr. Burch have been freely used, and their helpfulness is hereby gratefully acknowledged. Many thanks are due Senor Montoulieu and Mr. Wright for their valuable work in the field; to the officials of the Spanish American Iron Co. and of the various other companies; and to individuals holding chromite claims, for courteously facilitating the work of the party. In the study of material for the present paper, chemical analyses have been made by R. C. Wells and petrographic determinations and descriptions were furnished by Miss E. F. Bliss, both of the U. S. Geological Survey.

Jan 9, 1919

By S. Pearson, L. Rotherham

Measurements have been made of the variation of internal friction with temperature for OFHC copper, and for a series of binary solid solutions of high purity copper with zinc, gallium, germanium, arsenic, and silicon, to investigate the effect of alloying elements in substitutional solid solution on grain boundary viscosity. The apparatus used was of the torsional pendulum type developed by KeI1 modified so that the specimen and vibrating system could be maintained in a high vacuum. The activation energy for grain boundary relaxation in copper is 33,000 cal per mol. This is considerably less than the activation energy for self-diffusion, in disagreement with Ke's theory2 that the two activation energies should be the same. All the alloying elements increase the activation energy for grain boundary relaxation to approximately 44,000 cal per mol, increasing the grain boundary viscosity at a given temperature. The results are discussed in terms of theories of grain boundary slip put forward by MottQ and by Ke.+ Experiments have also been made to investigate the effect of small amounts of oxygen on the variation of internal friction with temperature for copper. EXPERIMENTS described in this paper were designed to investigate the effect of alloying elements in substitutional solid solution on grain boundary viscosity, using the internal friction method developed by Kel for measuring grain boundary viscosity. It was considered desirable to make the system under investigation as simple as possible by making experiments on a comprehensive series of binary alloys of copper with the elements immediately following it in the periodic table, i.e., zinc, gallium, germanium, and arsenic. These elements are within the range of favorable size factor for solution in copper, and the systems have been extensively investigated by Hume-Rothery and his co-workers." Later, in order to study the effect of the relative size of the solvent and solute atoms, experiments were made on a series of Cu-Si alloys, since the apparent atomic diameter of silicon when in solution in copper—the diameter necessary to assign to the solute atoms to account for the lattice constant of the solid solutiona—is almost the same as that of the solvent atoms. Preliminary experiments were made to measure the variation of internal friction with temperature for pure copper. Ke made some experiments on copper," but found that the curves obtained were not reproducible in consecutive experiments. The copper was maintained in an argon atmosphere during the experiments but, although he took precautions to exclude oxygen, Ke came to the conclusion that the precautions were not entirely satisfactory, and that the lack of reproducibility must be due to absorption of oxygen by the copper. Experiments have therefore been made to investigate the effect of small amounts of oxygen on the variation of internal friction with temperature for copper. Previous Work Ke made extensive experiments on high purity aluminum and was able to show that the grain boundaries behave viscously at high temperatures. He found that the relative rate of movement of the grains could be expressed as Where v is the velocity of slip, A is the constant, u is the shear stress, H is the activation energy, R is the gas constant, and T is the absolute temperature. By assuming that the boundary layer was one atom thick, he obtained a value for the viscosity which, when extrapolated to the melting point, gave good agreement with the viscosity of the liquid metal at the melting point. Ke also made experiments on other high purity and commercial purity metals:, and on some alloys." " He came to the conclusion2 that the activation energy for grain boundary slip was the same as for self or volume diffusion and for steady state creep in single crystals. Rotherham, Smith, and Greenough" have shown recently that the activation energy for grain boundary slip is not the same as for self-diffusion in tin,

Jan 1, 1957

By G. A. Beske, P. Hilsch, J. Wulff

The effects of the growth precipitates on the su-perconduching properties of an Al- 15 al. pel Zu alloy have been studied using magneization, transition lem-perature, and residual resistivity measurements. Aging at 230C for 1/2 to 11 he produces an increase in Hfp, Ike field of first penetration, and tut increase in trapped flux. The upper critical field, Hc2 remains constant for such aging tunes. Aging at 200°C produces a decrease in Hfp and an increase in trapped flux. The transition temperature remains constant at Tc - 1.227° ± 0.02°K for aging at 220°C for tims of from 1/2 to 10 hr, and for aging at 200°C it remains constant at Tc. = 1.18° i 0.02°K for times from 1/2 hv to 26 hr. The observed behavior indicates that the superconducting matrix when aged at 220°C behaves tike a type U su-perconducior, but when aged at 200°C behares like a type I superconductor. The magnetization changes after aging can be attributed to the growth and clutnge in distribution of the precipitate in a matrix of fixed composition. IT has been realized for some time that the superconducting properties of alloys are highly structure-sensitive. This is evident in the work of Mould and Mapother1 who examined the properties of an aluminum alloy. Precipitation effects have also been briefly mentioned in other studies.2-4 Bonnin and coworkers5 have observed a sharp inc rease in trapped flux in an A1-Mg alloy when the residual resistivity reaches a value that indicates it is a type II superconductor. Recently Blanc, Goodman, and Nemoz5p have reported on precipitation effects in A1-Ag alloys. Detailed studies of precipitation in Pb-Sn and Pb-Cd alloys made by Livingston6 serve to show that the upper critical fields are enhanced by quenched-in solute. Furthermore. at various stages in the precipitation process? the upper critical field is determined largely by the remanent solute. The observed magnetic hysteresis and trapped flux in such alloys result from the interaction between precipitate and the flux filaments in the mixed state. The flux trapping appears to depend largely on the precipitate distribution and is greater if the superconductor is type II than if it is type I. To examine the effect of precipitation in another alloy system, particularly one in which the composition of the superconducting phase does not change significantly during the course of precipitation, the Al-Zn system seems interesting, especially in view of the transition temperature and resistivity studies of Chiou and seraphim.' Furthermore, the recent detailed electron-microscope studies of an Al-Zn alloy by Richards and Garwood8 provide a guide for relating superconducting properties to changes in structure. For these reasons, magnetization, transition temperature, and residual resistivity measurements for varying times of heat treatment at two temperatures were made with a -15 at. pct Al-Zn alloy. The results are reported in this paper. I) EXPERIMENTAL The alloy used was prepared by Cominco Products Inc. from 99.9999 A1 and 99.999 Zn. It was chill-cast, swaged, and drawn to 0.125-in.-diam rod. The analyzed composition was 15.6 at. pct Zn (31.1 wt pct). A jeweler's saw was used to cut the 0.125-in.-diam rod into the 0.875-in. lengths needed for magnetization measurements. The ends of the cylinders were slightly beveled to remove the sharp edges. A portion of the original 0.125-in.-diam rod was drawn into 0.010-in.-diam wire and used for transition temperature measurements. Specimens were suspended from wires within a vertical furnace during heat treatment. All were homogenized at 500°C for a minimum of 3 days and subsequently solutionized for times in excess of 6 hr. The solutionizing temperature was held constant to +3°C. Individual specimens were homogenized, quenched, and aged several times and no effects indicating loss of zinc were noted. The suspended specimens were quenched by cutting the wires and allowing the specimens to fall into a silicone oil bath held at the aging temperature. They were then isothermally transforked by aging in the same bath used for quenching. After aging for the required time (approximately 10 min aging was necessary before the upper critical field reached a fixed value), they were briefly (1 to 2 sec) dipped into an acetone bath at room temperature to remove adherent oil and then immediately transferred to liquid nitrogen where they remained until inserted into the helium bath (usually within an hour). The temperature of the aging bath was held constant to +3°C for longer aging times. The cryostat used for the measurement of superconducting properties consisted of outer and inner dewars for liquid nitrogen and liquid helium, Stokes 6-in. booster diffusion pump and Stokes Model 212 mechanical pump, temperature controller to measure and control the temperature of the helium bath, and a superconducting solenoid with inserted search coils to provide the magnetic field and measure the magnetic moment of the specimens. A schematic diagram of the cryostat is shown in Fig. 1. An ultimate temperature of 0.85°K was reached with this apparatus. The temperature controller used is similar to the one described by Blake and chase.' A 0.5 pct Allen-Bradley carbon resistor and a nichronle heater (200

Jan 1, 1968

||Abad, Leopoldo F., Min Engr, Div of Mines, Bureau of Science Manila, P I '23 Abadilla, Quirico A, Geol, Lago Pet Corp Box 172, Maracaibo, Venezuela '20 ||Abbey, Robert Graham, The W W Sly Mfg Co Train Ave, Cleveland, Ohio '21 Abbott, A. N., Mines Supt, Mazapil Copper Co, Ltd Concepcion del Oro, Mexico '23 Abbott, Clarence E., Mgr, Mines & Quarries, Tenn Coal, Iron & R R Co, 1242 Brown Marx Bldg, Birmingham, Ala. '04 Abbott, Louis Benjamin, Chief Engr , Consolidation Coal Co , Elkhorn Div Jenkins, Ky. '16 Abbott, Robert R., Met Engr , Peerless Motor Car Co Cleveland, Ohio '12 ||Abbott, Wells Osborn, Ray Consolidated Copper Co Hayden, Ariz. '23 Abeel, George H, Jr., Cons Min Engr 4612 West 17th St , Los Angeles, Cal '18 Abel, Albert E., Asst to Pres, Valley Mould & Iron Corp Sharpsville, Pa. '19 Abernathy, George Elmer, Prof of Geol & Min , Kansas State Teachers College, Pittsburg, Kans. '20 Abey, Hiroshi, Min & Met Engr, Min & Met Dept, The Higher Technical School, Osaka, Japan. '17 ||d'Ablaing, Philip R, Chem , Anaconda Copper Min Co Great Falls, Mont '25 Aborn, Robert H , Research Assoc., Mass Inst of Tech Cambridge, Mass '19 Abouchar, Sylvain Sley, Min. Engi & Geol , care of S H Sekaly, 13 Rue El Nimr, Cairo, Egypt '17

Jan 1, 1923

By L. A. Weitzenkamp, N. M. Bashara

A study of the electrical conductivity of gold films less than 200 in thickness indicates a negative temperature coefficient of resistance and a thermal actiuatlon energy of less than 0.25 ev. The films consist of discrete metal islands of linear dimensions from a few angstroms to 1000A. Films were able to withstand applied fields up to 60,000 v per cm before breakdown occurred. A model for the conduction mechanism is proposed which involtes a Potential barrier due to work junction, irriage forces , and an electrostatic potential arising from separating an electron from a neutral island leaving behind a positively charged metal island. Activation energies of less than 0.25 ev ave consistent with this model, which includes a tunneling andor Thermal mechanism for conduction between the separate metal islands. An apparent satuvation effect in conductivity at high fields is observed experimentally. The saturation effect may be explained by the influence of the electrostatic contribution to the potential barriers for the transition through several islands adjacent to the original island which was activated to give up an electron. The proposed model gives Poor quantitative agyeement for the intermal electrical field between islands. ThIS paper will relate the structure of discontinuous metal films to the electrical properties and will emphasize the following topics: 1) the relation of the conduction mechanism to particle size and a comparison of particle size from electrical measurements with electron-microscope studies; 2) the saturation of the conductivity at high electric fields; and finally, 3) a comparison between the external field applied and the apparent field between particles. che- latter comparison points to a need for a modification in the model for the conduction mechanism first proposed by orter' and expanded by Neugebauer and webb2 which will be dealt with in the discussion. The paper is based on results on gold films on glass microscope slides. The clms were vacuum-evaporated and were about lOOA thick, thickness being measured by interferometry. It has been observed that metal films of this thickness do not exhibit bulk metallic conduction. Films thinner than some critical thiclmess, depending upon substrate temperature and other factors, have conductivities which increase with increasing temperature with thermal activation energies of less than 0.25 ev. Electron-microscope studies3 have shown that these films consist of discrete metal islands having linear dimnsions from a few angstroms to approximately 1000A. When the metal is being vacuum-deposited on the substrate, islands on the order of a few angstroms appear first. As the deposition continues the islands may tend to agglomerate into larger particles and may eventually grow together into a continuous film,3''' In our tests the conductivity of the gold films was found to be about ten orders of magnitude less than the bulk conductivity of gold. When oxygen was introduced into the test chamber the conductivity decreased by a factor of about one-third. This can be related to an increase in work function for gold caused by adsorption of oxygen, as reported by Oullet and Rideal.s Exposure to an atmosphere of water vapor caused an increase in conductivity by a factor of 2 or 3 when a low field was applied. When the films were exposed to water vapor under a high field the conductivity increased by as much as two orders of magnitude. The activation energies measured were much less than the work function for gold, 0.25 ev or less, with the smaller activation energies observed for thicker films. It will be shown that the activation energy is a function of particle size and spacing. In general the model for the potential between metal islands would include the effective work function, the image force, the applied field, and an electrostatic term. The electrostatic contribution arises from the potential required to separate an electron from a conducting sphere. According to Neugebauer and webb2 the maximum potential due to the field and the electrostatic term only is

Jan 1, 1967

By P. J. Burkhardt, L. V. Gregor

The oxidation kinetics of single-crystal silicon has been investigated using extremely dry oxygen as the oxidant. Two techniques were used. The first involved a flow system with which incremental thickness measurements were made. This sytem provided an oxygen ambient at atmospheric pressure which had a moisture content of less than 0.1 ppm of water. The second technique involved measuring the change in volume of oxygen with time in a closed system. A temperature range of 900O to 1200 "C and a pressure range of 20 to 760 Tory were covered. Both techniques showed that a simple parabolic rate law holds only at the higher temperatures. At lower temperatures, the data up to 5000Å can be fitted well to a linear-parabolic equation. The two constants in this rate equation are examined in terms of a physical model. The parabolic portion of the low-temperature oxidatLon fits along the high-temperature curve of an Arrhenius plot. The parabolic rate constant for the flow-system technique can be expressed by k = 2 x 10-9 exp (L 31 kcalRT) sq cm per sec. The manostatic technique gave k = 1 x 10-exp (- 23 kcalRT) sq cm per sec. By extending the thickness range to over 104. a rate law of X = At seems to fit all of the data better than the linear-Pavabolic law. Here the exponent n increases from 0.518 at 1150 V to 0.637 at 900°C. PASSIVATION of silicon planar devices through thermal oxidation is of such great importance that considerable effort has been devoted to the study of the process.17 Much of this work involves hydrothermal oxidation, in which H2O is the oxidant: whereby H2 is produced. It has been proposed that the reaction proceeds by the formation of Si-OH groups and hydroxyl diffusion through the film to react with the silicon surface. Thus, the silicon oxide layer probably contains residual hydrogen in some form after oxidation in H2O and it has already been established that hydrogen has a marked effect on the electronic properties of oxide-passivated silicon surfaces. Silicon is oxidized by oxygen at elevated temperatures; but the rate of oxide formation is considerably lower than that for 0." By using dry O2 as the sole oxidant, the presence of residual hydrogen is presumably avoided. At present, the mechanism of thermal oxidation by dry O2 is a matter for conjecture, and the presence of small amounts of H2O was reported to have a marked effect on the rate of oxide formation10 (perhaps on the electronic properties of the surface, as well). Hence, this study of the kinetics of silicon oxide growth in 0, was undertaken: 1) to determine the oxidation rate at atmospheric pressure in a system designed to exclude rigorously all traces of H2O in the ambient 0,; 2) to obtain oxidation-rate data in situ in dry O2 by means of a continuous monitoring of the amount of 0, consumed during oxide growth. These objectives are complementary—the first assesses what effects (if any) are obtained by excluding H2O from the reaction, and the second expands this information while at the same time avoiding the uncertainty inherent in relying upon incremental measurements of oxide growth to furnish kinetic data. EXPERIMENTAL PROCEDURE The conventional silica open tube in a resistance-heated oxidation furnace is subject to sources of trace H2O, even after the input O2 is thoroughly dried and the outlet gas stream is passed through a trap to prevent

Jan 1, 1967

By Kenneth E. Gray

The turbulent flow drag coefficients, or friction factors, have been experimentally determined for the cut-tings normally encountered in drilling operations. The gas law and average drag coefficients for characteristically flat particles (limestones and Shales) and for angular to sub-rounded particles (sandstones) were used to extend Newton's equation to a more useful form. The resulting equations are expressions for the slip velocity of a particle as a function of the particle size and shape, the bottom-hole injection Pressure, and the Bottom-hole temperature. The velocities necessary to lift actual rock cuttings as observed in the laboratory were compared with velocities predicted from the derived equations. Results indicate that there is no single correct circulating velocity and that the commonly used 3,000 ft/min linear velocity may he sufficient to lift only very mall particles. The advantage, in terms of horsepower requirements, of cycling high pressure air to obtain lower compression ratios was shown. INTRODUCTION A promising departure from standard rotary hydraulic drilling is air or gas drilling. In many instances the rate of penetration and bit life increases resulting from this method have been very substantial. Further the application of air drilling in areas of lost circulation or water sensitive pay zones has been highly successful. Purpose For the drilling contractor, the practical question remains, "How much air pressure and volume should I have?' lt is necessary to have a reasonable knowledge of the air velocities and pressures required in air drilling operations for the proper design and most advantageous use of surface equipment and for adequate removal of cuttings from the borehole. Eased on experience, most operators agree that at least 3,000 ft/min linear velocity is necessary for satisfactory hole cleaning.' It was the purpose of this investigation to evaluate the drag coefficients, or friction factors, for the cuttings normally encountered in drilling operations, i.e., sandstones, limestones and shales, and to utilize the values obtained to develop an expression for the minimum velocities and pressures (hence the volumes) necessary to lift these cuttings. THEORY Several investigators have done extensive work on the ability of drilling mud to lift bit cuttings. They conclude that the ability of a drilling mud to lift cuttings is dependent on the density difference between the rock being drilled and the drilling mud, the cutting size and shape, the mud flow constants, and the flow state (laminar, transitional or turbulent) of the mud. However, drilling muds are not true fluids but have a variation of viscosity with velocity in laminar flow and a constant apparent viscosity in turbulent flow. A survey of the literature revealed that no experimental work had been done to determine the velocities necessary to lift actual rock cuttings using a compressible fluid such as air or gas. In 1953, Nicolson6 stated that in air drilling fluid mechanics the particles could be assumed spherical in shape and that ; constant drag coefficient of 0.5 could be used due to the highly turbulent flow of the circulating air. By equating the turbulent resistance on the particle to the gravitational force on the particle, he obtained the expression, ^ = 2.67^y ,.......(1) where V, is slip velocity of spherical particle, ft/sec; D is particle diameter, in.; p, is particle density, 1b/ft8; and p, is fluid density, lb/ft3. However, as stated earlier, most operators seem to agree that adequate hole cleaning can be obtained by circulating a sufficient volume of air to give a linear velocity of 3,000 ft/rnin in the annular space. Basic Equation The velocity with which a solid particle freely falls through a fluid will increase until the accelerating force, gravity, is equal to the resisting forces, buoyancy due to the fluid displaced by the particle and friction due to the relative motion of the particle through the fluid. When the accelerating and resisting forces become equal,

By J. J. Taber

The turbulent flow drag coefficients, or friction factors, have been experimentally determined for the cut-tings normally encountered in drilling operations. The gas law and average drag coefficients for characteristically flat particles (limestones and Shales) and for angular to sub-rounded particles (sandstones) were used to extend Newton's equation to a more useful form. The resulting equations are expressions for the slip velocity of a particle as a function of the particle size and shape, the bottom-hole injection Pressure, and the Bottom-hole temperature. The velocities necessary to lift actual rock cuttings as observed in the laboratory were compared with velocities predicted from the derived equations. Results indicate that there is no single correct circulating velocity and that the commonly used 3,000 ft/min linear velocity may he sufficient to lift only very mall particles. The advantage, in terms of horsepower requirements, of cycling high pressure air to obtain lower compression ratios was shown. INTRODUCTION A promising departure from standard rotary hydraulic drilling is air or gas drilling. In many instances the rate of penetration and bit life increases resulting from this method have been very substantial. Further the application of air drilling in areas of lost circulation or water sensitive pay zones has been highly successful. Purpose For the drilling contractor, the practical question remains, "How much air pressure and volume should I have?' lt is necessary to have a reasonable knowledge of the air velocities and pressures required in air drilling operations for the proper design and most advantageous use of surface equipment and for adequate removal of cuttings from the borehole. Eased on experience, most operators agree that at least 3,000 ft/min linear velocity is necessary for satisfactory hole cleaning.' It was the purpose of this investigation to evaluate the drag coefficients, or friction factors, for the cuttings normally encountered in drilling operations, i.e., sandstones, limestones and shales, and to utilize the values obtained to develop an expression for the minimum velocities and pressures (hence the volumes) necessary to lift these cuttings. THEORY Several investigators have done extensive work on the ability of drilling mud to lift bit cuttings. They conclude that the ability of a drilling mud to lift cuttings is dependent on the density difference between the rock being drilled and the drilling mud, the cutting size and shape, the mud flow constants, and the flow state (laminar, transitional or turbulent) of the mud. However, drilling muds are not true fluids but have a variation of viscosity with velocity in laminar flow and a constant apparent viscosity in turbulent flow. A survey of the literature revealed that no experimental work had been done to determine the velocities necessary to lift actual rock cuttings using a compressible fluid such as air or gas. In 1953, Nicolson6 stated that in air drilling fluid mechanics the particles could be assumed spherical in shape and that ; constant drag coefficient of 0.5 could be used due to the highly turbulent flow of the circulating air. By equating the turbulent resistance on the particle to the gravitational force on the particle, he obtained the expression, ^ = 2.67^y ,.......(1) where V, is slip velocity of spherical particle, ft/sec; D is particle diameter, in.; p, is particle density, 1b/ft8; and p, is fluid density, lb/ft3. However, as stated earlier, most operators seem to agree that adequate hole cleaning can be obtained by circulating a sufficient volume of air to give a linear velocity of 3,000 ft/rnin in the annular space. Basic Equation The velocity with which a solid particle freely falls through a fluid will increase until the accelerating force, gravity, is equal to the resisting forces, buoyancy due to the fluid displaced by the particle and friction due to the relative motion of the particle through the fluid. When the accelerating and resisting forces become equal,

By V. Kondic, W. M. Rumball

HUNT and Jackson' have recently suggested that binary eutectics might be classified according to the entropy of fusion of the component phases. Such a classification was in fact proposed2 some time ago by the authors and the purpose of this communication is to present some supporting evidence. As pointed out by Hunt and Jackson' typical metals of low entropy of fusion, ?S, tend to form normal eutectics (using Scheil's terminology3). Where one phase is metallic (low ?S) and the other nonmetallic (high AS) then anomalous structures are formed. These anomalous structures may either be regular (e.g., Bi-Sn)or irregular (e.g., A1-Si). Finally Hunt and Jackson suggest that where both phases are of high ?S regular faceted structures are formed. In the proposed classification2 the ratio of the entropies of fusion is taken as the quantitative parameter, i.e., ?Sa/?SB = E, where e > 1.0. An extensive literature survey has been carried out2,4 for reliable photomicrographs of eutectic structures. The structures, numbering 151, have been classified into two classes, viz., normal (i.e., lamellar and rodlike) and anomalous. The latter group has been arbitrarily subdivided into regular and irregular anomalous eutectics. Details and sources of the structures are given elsewhere.2,4 In the absence of better thermodynamic data the value of E has been determined for each of the systems making the following assumptions and approximations: l) The entropy of fusion of solid solutions may be calculated additively;5 ii) Inter metallic compounds are treated similarly but with the addition of the following term for fully ordered structures.5 -4.573(Ni lOg10 Nl + N2 log10 N2) where Nl and N2 are the atomic fractions. It might be argued that the entropies of fusion are meaningless as the eutectic phases form at some temperature (T,°K) below their true melting point (Ta or Tb). As AS, = Lo/To if La the latent heat of fusion of a, is assumed independent of temperature, the actual entropy change AS& is given by La/Te. The ratio of entropies of fusion then becomes Fig. 1 shows E' plotted against cumulative totals for normal and anomalous systems from which it is seen that normal eutectics predominate at low values of E'; e.g., some 90 pct of normal systems lie below E' = 1.5 with 65 pct of anomalous systems above this value. Fig. 1 also shows that the regular anomalous structures occur mostly at low values of c' possibly suggesting growth more akin to normal than anomalous growth. The choice of c as a classification parameter was based on nucleation concepts, it being observed that metals widely separated in Sundquist and Mondolfo's8 nucleation series were anomalous and those close together normal. The basis of these classification views is really outside the intended scope of this communication but it is hoped to explain them fully in the near future.7 Having arrived at this entropy of fusion classification by nucleation considerations it is interesting to note that Hunt and Jackson's ideas are based on growth considerations. Elsewhere one of the authors4 has shown that an even better classification of the metallographic structures reviewed is obtained from purely conventional heterogeneous nucleation concepts. It has been found that systems having a value of the parameter +b less than 0.28 are almost certainly normal and above this anomalous: V, is the gram atomic volume. This parameter is nevertheless closely related to c and c', these being an approximation of p. The parameter is also related to the other classification3,8,9 which have met with any success in the past. All these classifications are to be reviewed shortly by the authorsU7 A significant thing about the classifications based on

Jan 1, 1968

By T. B. Massalski, C. S. Barett

THAT metals and alloys of the body-centered-cubic structure tend to become unstable at low temperatures is so nearly universal that any exceptions are worthy of special attention. Studies of the exceptions may disclose unrecognized examples of metastability or may shed light on the nature of some of the factors that stabilize the body-centered-cubic phase. Among the structurally analogous body-centered-cubic 3/2 electron compounds, the ß-phase in the Cu-Zn system deserves further attention for, although this phase is known to undergo partial mar-tensitic transformation on cooling below room temperature to the temperature of liquid nitrogen when the composition is less than about 42 wt pct Zn, it does not transform on cooling .when there is more than this amount of zinc present.1-4 The present authors recently found that an alloy containing 48.35 wt pct Zn could be transformed, however, if deformed severely at room temperature or lower temperatures.V his discovery led to the suggestion that the jerky flow of ß-brass single crystals6 and some of the unusual temperature variations of the yield strength and hardness are due to strain-induced transformation during the tensile tests. The present investigation is an extension of that work to cover the entire available range of compositions of Cu-Zn ß-phase alloys and certain interesting compositions of the ß-phase in the Cu-Zn-Ga system. Particular attention is given to the structure of the transformation product resulting from cold work, which is found to vary with alloy composition, and to the temperature range in which transformation can be induced in the various alloys. The composition limits of the body-centered-cubic phase in the Cu-Zn system, based on a recent review by Raynor7 and the precision determinations of Beck and Smith: are shown in Fig. la; in the ß region the alloys are disordered and in the ß region they are ordered. The rate of ordering is so rapid that a high degree of order is found in any of these alloys immediately after quenching. Experimental The nine binary and four ternary alloys of this investigation were prepared from cathode copper (99.99 pct purity), electrolytic zinc (99.99+ pct), and gallium (99.98+ pct). All alloys were cast in transparent Vycor tubing, homogenized at temperatures between 800° and 890°C, and quenched in water. Ternary alloys were cast in small amounts (-5 g) to predetermined compositions to fall along a line of constant electron concentration in the ternary system. Changes of weight during the casting operation of the ternary alloys were not greater than 1 part in 2500 from the intended nominal weights and therefore their compositions were accepted without chemical analyses. All binary alloys were cast in larger amounts (100 to 150 g), homogenized, and hot rolled after preheating to 800°C. The central portion of the rolled strip of each alloy was annealed for eight days and quenched in brine. All binary alloys were analyzed chemically. The compositions, heat treatments, and metallographic appearances of all alloys are tabulated in Table I. Various samples were subjected to heat treatment or cold work at several temperatures and were then examined metallographically or by means of X-rays. Specimens about 6x6x3 mm in size were examined metallographic ally to confirm the presence of the ß-phase after quenching. Cold work was introduced by fastening each sample between two pieces of steel, cooling the assembly to the desired temperature, and transfering it rapidly to a vise where moderate or severe compression was immediately applied. Cold working at liquid helium temperature was done by a chisel-shaped tool mounted on an X-ray spectrometer, described elsewhere.% A!! metal-

Jan 1, 1958

By B. A. Wilcox, A. H. Clauer

The tensile and creep deformation characteristics of fiber reinforced composites have been studied, primarily at room temperature. The matrix was an alloy of Mg-14 wt pct Li-1 wt pct Al (LA141A alloy) and the reinforcing fiber consisted of continuous wires of a high strength precipitation hardening stainless steel (AFC-77 alloy). The ultimate tensile strength and strength-to-density ratio of composites were much improved over that of the mmix, both at room ternperatwe and up to 200°C. Creep studies at room temperature revealed logarithmic weep behavior for wires and composites and steady state creep for the nonreinforced matrix. It was concluded that creep of the fibers controlled composite creep. The instantaneous logarithmic weep rate of the composite, 6, was related to the average tensile stress on the fibers, where n = 3.4. Mg-Li alloys are the lightest structural metals commercially available, e.g., the alloy LA141A (Mg-14 wt pct Li-1 wt pct Al) is 27 pct less dense than beryllium Although Mg-Li alloys have moderate tensile strengths at normal strain rates and ambient temperature, their creep strength is relatively poor, even at room temperature. Reinforcement by fibers offers a means of increasing the tensile strength as well as overcoming the limitations of low creep strength. With a proper choice of reinforcing filament, composites could be designed with higher strength-to-density and modulus-to-density ratios than the matrix alloy. This communication reports a study on the tensile and creep characteristics of alloy LA141A reinforced with continuous wires of a high-strength precipitation hardening stainless steel (AFC-77 alloy). The matrix has a bcc structure, with possible precipitates of AlLi and MgLi2A1,3 and is ductile at room temperature Stainless steel wire was chosen as the -reinforcing filament since previous work at Battelle4 showed that a good bond between wire and matrix could be produced in this system. For all volume fractions of reinforcing wire, the theoretical composite strength-to-density ratio is greater than that of the matrix and the modulus-to-density ratio is somewhat lower than that of the matrix. EXPERIMENTAL PROCEDURES The 0.004-in. diam AFC-77 wire was obtained from two suppliers: National-Standard Co.* and Crucible 0.13 Si, 0.18 V, 0.011 P, 0.012 S, balance Fe. In the as-received condition, wires from both sources had room-temperature ultimate tensile strengths of 585,000 to 590,000 psi with approximately 2 pct total elongation and 40 pct reduction in area. Composite preparation was accomplished by the vacuum infiltration technique. This involved placing the continuous wires in a mild steel tube (1/8-in. ID), capping one end of the tube with a sheet of the matrix alloy, and evacuating the other end of the tube. When the capped end was placed in a crucible of the molten matrix alloy and held for 31/2 min at 70O°C, the liquid metal was drawn up the tube approximately 7 to 8 in. A cross-sectional view of a typical composite is shown in Fig. 1. This preparation technique promoted excellent bonding between the matrix and wires, and porosity was rarely observed. Test specimens for both creep and tension studies were prepared by machining off the steel tube. Tensile tests on the wires and composite specimens were made in an Instron using a cross-head speed of 0.01 in. per min. The composite specimens had no reduced section and were held in self-tightening grooved serrated grips. Most of the specimens broke in the effective 1-in. gage section. Even though several tests fractured in the grip section, their ultimate strengths were essentially the same as those of specimens which fractured in the gage section. Creep specimens of the composite were gripped in a similar manner, and

Jan 1, 1970

By Seymour G. Epstein

Using a modified capillary-reservoir technique, electromigration of dilute solutions of silver in liquid bismuth has been measured with relatively good precision. The effects of experiment duration, temperature. current density, and silver concentration have been investigated. Chemical diffusion coefficients of silver in liquid bismuth were also measured at temperatures ranging from 300°to 600°C. The effective valence of silver in bismuth was calculated as a function of temperature from a comparison of electric mobilities and diffusion coefficients. In an alloy containing 1 wt pct Ag, the electric mobility of silver increased from 1.65 x X sq cm per v-sec at 300°C to 2.38 x 10-4at 600°C; the diffusion coefficient in-creased from 3.0 to 17.5 x 10-5 sq cm per sec over the same temperature range. Calculated values of effective valence decreased from 0.28 at 300°C to 0.10 at 600°c. ALTHOUGH there has been considerable progress in the theoretical treatment of electron-transport properties in liquid metals, the mechanisms of mass-transport phenomena in liquid metals are still not clearly understood. This is especially true for the case of electro migration, alternatively termed elec-trotransport or electrodiffusion, which is mass transport induced by an applied electric field. A thorough knowledge of the mechanisms governing electromigration will considerably aid in understanding the electronic state of an impurity atom in a liquid metal. Electromigration has been long observed and studied in liquid metals and alloys. However, no satisfactory theory to explain the observed effects has been developed. The disparity in the present theoretical treatments, summarized by Verhoeven,1 has been attributed to the difficulty in describing the momentum transfer between electrons and ions and to the lack of precise measurements in liquid metals, especially at elevated temperatures. Prior to the last decade most of the electromigration studies were qualitative, in that only the direction of migration of alloy constituents was determined with any degree of reliability. These results have been summarized by schwarz,2 who was able to measure the electric mobility of several elements in mercury. More recently electromigration in liquid metals has been measured by a variety of techniques, with a varying degree of success. Mangelsdorf3,4 made precise measurements on dilute amalgams at room temperature, using a technique relating changes in composition to changes in alloy resistivity, but was unable to make measurements at elevated temperatures. Using a modification of this technique, Verhoeven and Hucke5 measured electromigration and resistivities in liquid Bi-Sn alloys. However, the resistivity technique is not sensitive to small composition changes and is impractical for very dilute alloys. Verhoeven and Hucke6 also measured electromigration of several solutes in liquid bismuth by adapting the capillary-reservoir method for determining diffusion coefficients in liquids. The reported precision of these measurements was poor, however, primarily due to the large uncertainties in the chemical analyses to determine concentration changes. Belashchenko7 has summarized the recent Russian investigations of electromigration, many of which, however, are of questionable accuracy. The present study was initiated to develop an experimental technique which would be both versatile and sufficiently sensitive to yield precise measurements of electromigration of solutes in dilute metal alloys at elevated temperatures. Using this technique, a comprehensive study of silver in liquid bismuth was made to determine the effects of experimental variables on the apparent electric mobilities. Chemical diffusion coefficients of silver in liquid bismuth were also measured over the same temperature range for comparison with the electromigration data. EXPERIMENTAL TECHNIQUE Electromigration Measurements. Electromigration of silver in liquid bismuth was measured by the capillary-reservoir technique, similar to that used by Verhoeven and Hucke,6 but modified to yield more

Jan 1, 1967

By R. V. Sara

Determination of the Hf-C phase diagram was conducted primarily by metallographic and X-ray diffraction studies on appropriate alloys. The only intermediate phase observed in this binary system was HfC. This phase was found to be homogeneous between 34.0 and 48.0 at. pct C at 2200°c and between 36.0 and 49.3 at. pct C at 3150°C. The lattice-parameter variation was also determined for HfCI-, compositions prepared at 2200° and 3150°C. The most most refractory composition, with a melting point of 3830°c, was established at 47.5 at. pct C from melting-point data. Solidus temperatures of 2240' and 3150°C occur on the high-kafnium and high-carbon sides of the monocarbide, respectively. The invariant point between HfC and carbon is located at 66.0 at. pct C, whereas the 2240°C solidus corresponds to the peritectic temperature at which hafnium is formed from HfC and hafnium-rick liquid. Hafnium has a melting temperature of 2208°C and is capable of taking carbon into solution to the extent of 10.5 at. pct at this temperature. ALTHOUGH the Hf-C phase diagram has not been previously evaluated experimentally in its entirety, the belief has been that the general configuration would resemble the chemically similar Group rV carbide systems, Ti-C and Zr-c.' These binaries are characterized by a single carbide phase with a simple NaC1-type structure which is maintained over wide compositional ranges. This family of carbides has high thermal stability that increases substantially as the atomic number of the metal component increases. This trend characterizes HfC as one of the highest melting materials. According to Agte and Alterthum,2 the melting point for this monocarbide is 3890°C, a value that has been quoted quite extensively for the past several decades. Recently, in repeating the work of Agte and Alter-thum, Adams and Beall3 determined the melting point of HfC to be 3895°C. A significant departure from the commonly accepted version of the Hf-C system was reported by Avarbe and his coworkers,4 who proposed that there is an extreme stabilization of a hafnium in a narrow field to 2820°C, above which it melts peritectically to form HfC and liquid. Their study was also concerned with the melting temperature of various HfCI-, compositions, but the peak melting point was taken from the work of Agte and Alterthum. Avarbe and his associates were not concerned with the high-carbon region of the system. However, three widely varying temperatures have been reported for the HfC-C solidus by other investigators. Cotter and Kohn5 observed approximately 2800°C; Portnoy et al.' reported 3260°C; and, more recently, Krikorian7 indicated 2915°C. Equally as uncertain is the solidus between hafnium and HfC. As noted above, Avarbe et al. report a peritectic temperature of 2820°C, Krikorian7 measured 2150°C, and Benesovsky and Rudy' estimated 2000°C on their diagram. I) EXPERIMENTAL PROCEDURE The starting materials for this study consisted of reactor-grade hafnium hydride obtained from Fair-mount Chemical Co., Newark, N.J., hafnium carbide supplied by Wah Chang Corp., Albany, Ore., and Union Carbide spectroscopic-grade graphite, SP-1. The graphite analysis indicated impurities at levels of only 0.5 ppm or less. According to the suppliers, the hydride and carbide contained the typical impurities listed in Table I. The samples required for these studies were prepared by dry blending either graphite and hafnium hydride or hafnium hydride and hafnium carbide powders for approximately 5 min in a "Spex Mixer Mill". The latter combination was used only for preparing several samples in the HfC1-, melting-point studies. Small pellets, varying between 3/16

Jan 1, 1965

By Rollin A. Slater

This paper presents a composite of ideas on materials handling systems by describing the design of an over-all system for a hypothetical steel pellet plant located on the Great Lakes. The bulk materials handling industry has served for years as the skeleton and the central system of nerves and nourishment for the body of basic industries. During the past two decades, this body has undergone substantial growth and mutation to meet the surging demands of our national economy for more and better products. The steel industry has kept pace with spiralling demand by innovation which has resulted in new processes and improved designs which generally yield greater production from fewer units. Materials handling technology has likewise improved its techniques and currently has a new, stronger generation of equipment to perform its necessary supporting function. Drawing upon excerpts from several recent plant designs, this paper describes a basic approach to the selection and application of modern bulk materials handling systems to an entirely new steel plant. Specific details are not available for publication, and therefore the plant described herein is a composite of ideas. This imaginary plant will be located on the United States side of the Great Lakes and its owner will be called the Hypothetical Steel Corp. for purposes of discussion. TYPES OF EQUIPMENT The basic bulk materials handling systems and components required in a plant so situated are: lake boat unloaders; railroad train unloading systems; storage pile stackers and reclaimers; large bins and regulating feeders; and the conveyor systems — with their attendant controls— which connect the foregoing. PROGRAM OF DEVELOPMENT The initial work on the plant must be that of the process engineers who develop and refine the basic data, i.e., the logistics of all raw materials, waste materials and products within the plant. During this phase of study, the materials handling engineer may advance his planning only in basic areas such as movements at the dock and movements at the railroad. This initial planning work is concerned only with defining logical plant locations in the light of channels, currents, existing traffic, governmental regulations, locations of existing railroads and available rights-of-way. These systems alone have their own individual criteria which must be respected and accommodated in the final layout. All other elements, such as the arrangement of the blast furnaces, power house, coke plant, by-product plant, scrap preparation plant, BOF shop, and facilities for continuous casting, degassing, calcining, etc., are dictated by their own specific needs and their relation to each other. In the arrangement of these latter facilities, the materials handling system is secondary and must be designed to accommodate. BASIC LOGISTICS The result of the process engineer's work can be expressed in terms similar to those shown in Table I. Plants are customarily rated in terms of annual tons of ingots. Therefore, the basic size of this plant can be determined by referring to the BOF Shop wherein it is sized at 5 million tpy. From the base, the required hot metal can be traced to the blast furnace, which in turn indicates the amount of required flux, iron bearing materials and coke —which in turn establishes the demand for coal. Likewise, the total demand for flux can be determined by the combined demand of the lime plant and blast furnace. The generation of fines and waste products, which have significant value but are not usable as such, create the need for a sintering plant. From projections such as the foregoing, the complete flow of materials can be established and accommodated. The basic premise upon which this typical materials balance is predicted is that the plant will be a producer of high tonnages of non-SpecialtV- products. All basic raw materials (flux bearing, iron bearing, coal) will be prime quality. For example, the basic iron charge will be pellets, and the iron ore fraction will be sized lump, all of which

Jan 1, 1970

By F. Gordon Smith

ALTHOUGH several geological indicators of the critical type are known, including quartz inversions and decomposition of hydrous minerals such as serpentine, there are very few of the general type. Solid solutions are excepted, but the limitations of use are very restricted and interpretations are sometimes ambiguous. General methods for determining temperature and pressure conditions during the crystallization of minerals would have considerable scientific and economic value. It is not the purpose of this paper to discuss the various methods of geological thermometry and barometry, but to present one general method, applicable to all minerals, and to describe what progress has been made in the methods of measurement. The general method, in brief, is a study of the stress conditions in and around various types of foreign inclusions which are trapped in minerals during growth. The method depends upon the fact that any homogeneous gas, liquid, or solid will in general have coefficients of thermal expansion and volume compressibility different from those of any given mineral. Therefore stress must develop in and around all types of inclusions in minerals if the temperature or the pressure, or both, are changed from the conditions which prevailed during the growth of the mineral. The methods of measurement consist of determinations of the temperature-pressure conditions of fit of the inclusions in the host mineral. The types of inclusions in minerals are: I—gas, or liquid plus vapor, when observed at room temperature, due to crystallization under pneumatolytic conditions; 2—liquid, or liquid plus vapor when observed at room temperature, due to crystallization under hydrothermal conditions; 3—glassy solid, or devitrified glass, due to crystallization under magmatic or high temperature metamorphic conditions, in a siliceous liquid; and 4—crystals, due to overgrowth of other minerals crystallizing simultaneously or of other minerals which crystallized previously. A survey of the literature shows that much valuable earlier work on inclusions, especially that car- ried out in England in the last century, has dropped out of current knowledge. The following is a brief summary of the significant contributions to the problem up to the present day. Davy in 1822 asserted that fluid inclusions in minerals consist of an aqueous solution of salts and a gas bubble, the whole being either at lower or higher pressure than atmospheric.' At intervals from 1823 to 1862, Brewster contributed information concerning other types of inclusion consisting of 1—aqueous solution, a much more expansible liquid, and a gas; 2—aqueous solution, salt crystals, and a gas; and 3—the very expansible liquid and a gas. The very expansible liquid fills the gas space between 20" and 30°C. Compression strain effects were seen around inclusions in diamond, topaz, and other minerals.'-" Sorby in 1858 and 1869 further advanced the study begun by Davy, stating that fluid inclusions represent a sample of the mother liquor of crystallization and that the degree of filling of aqueous inclusions at room temperature defines the temperature-pressure relations during formation of the host. The degree of filling may be measured by determining the minimum temperature of filling of the inclusion by the liquid phase. The very expansible liquid in some fluid inclusions is liquid carbon dioxide. The temperature at which salt crystals in fluid inclusions completely dissolve in the fluid is the minimum temperature of formation. Inclusions of glass or devitrified glass indicate crystallization from a melt. Inclusions of crystals in minerals are often centers of strain, which may be seen by optical effects or by radial tension cracks. Sorby realized that an analysis of stress-strain relations about inclusions could be used to provide precise data on the temperature of crystallization, but the matter was never pursued.' , Hartley (1876, 1877),".'" Hawes (1881)," Wright (1881),'V ohnsen (1920),I3 and Holden (1925)"

Jan 1, 1953

By F. Gordon Smith

ALTHOUGH several geological indicators of the critical type are known, including quartz inversions and decomposition of hydrous minerals such as serpentine, there are very few of the general type. Solid solutions are excepted, but the limitations of use are very restricted and interpretations are sometimes ambiguous. General methods for determining temperature and pressure conditions during the crystallization of minerals would have considerable scientific and economic value. It is not the purpose of this paper to discuss the various methods of geological thermometry and barometry, but to present one general method, applicable to all minerals, and to describe what progress has been made in the methods of measurement. The general method, in brief, is a study of the stress conditions in and around various types of foreign inclusions which are trapped in minerals during growth. The method depends upon the fact that any homogeneous gas, liquid, or solid will in general have coefficients of thermal expansion and volume compressibility different from those of any given mineral. Therefore stress must develop in and around all types of inclusions in minerals if the temperature or the pressure, or both, are changed from the conditions which prevailed during the growth of the mineral. The methods of measurement consist of determinations of the temperature-pressure conditions of fit of the inclusions in the host mineral. The types of inclusions in minerals are: I—gas, or liquid plus vapor, when observed at room temperature, due to crystallization under pneumatolytic conditions; 2—liquid, or liquid plus vapor when observed at room temperature, due to crystallization under hydrothermal conditions; 3—glassy solid, or devitrified glass, due to crystallization under magmatic or high temperature metamorphic conditions, in a siliceous liquid; and 4—crystals, due to overgrowth of other minerals crystallizing simultaneously or of other minerals which crystallized previously. A survey of the literature shows that much valuable earlier work on inclusions, especially that car- ried out in England in the last century, has dropped out of current knowledge. The following is a brief summary of the significant contributions to the problem up to the present day. Davy in 1822 asserted that fluid inclusions in minerals consist of an aqueous solution of salts and a gas bubble, the whole being either at lower or higher pressure than atmospheric.' At intervals from 1823 to 1862, Brewster contributed information concerning other types of inclusion consisting of 1—aqueous solution, a much more expansible liquid, and a gas; 2—aqueous solution, salt crystals, and a gas; and 3—the very expansible liquid and a gas. The very expansible liquid fills the gas space between 20" and 30°C. Compression strain effects were seen around inclusions in diamond, topaz, and other minerals.'-" Sorby in 1858 and 1869 further advanced the study begun by Davy, stating that fluid inclusions represent a sample of the mother liquor of crystallization and that the degree of filling of aqueous inclusions at room temperature defines the temperature-pressure relations during formation of the host. The degree of filling may be measured by determining the minimum temperature of filling of the inclusion by the liquid phase. The very expansible liquid in some fluid inclusions is liquid carbon dioxide. The temperature at which salt crystals in fluid inclusions completely dissolve in the fluid is the minimum temperature of formation. Inclusions of glass or devitrified glass indicate crystallization from a melt. Inclusions of crystals in minerals are often centers of strain, which may be seen by optical effects or by radial tension cracks. Sorby realized that an analysis of stress-strain relations about inclusions could be used to provide precise data on the temperature of crystallization, but the matter was never pursued.' , Hartley (1876, 1877),".'" Hawes (1881)," Wright (1881),'V ohnsen (1920),I3 and Holden (1925)"

Jan 1, 1953

By John P. Hager, Igor A. Wilkomirsky

The thermodynamic properties of the Pb-Ag system have been determined between 775° and 950°C by the cell: Electrotransport measurements on silica-saturated PbO-SiO2 melts established that the conduction was entirely ionic and that lead is present only in the divalent state. The activities of lead and silver exhibit Positive deviations from ideal behavior. In dilute solutions the activities of lead and silver follow Henry's law. The values obtained for yhb and yig at 1200°K are 1.49 and 1.69, respectively. Determination of a portion of the liquidus curve agrees well with the established phase diagram. provides an accurate means for the thermodynamic study of liquid alloy systems. However, Wagner and wernerl have shown that cells of type I are limited to alloy systems for which the reaction at the alloy-electrolyte interface will be extremely small. The traditional electrolyte for cells of type I has been a low melting point mixture of group IA chlorides, to which a small amount of the compound ACIZa has been added. However, the choice of a chloride electrolyte may not always be practical, in that the Gibbs free energies of formation of the compounds ACIZ, and BCIZb may not be sufficiently different to minimize Reaction [I]. On the other hand, the Gibbs free energies of formation of the oxides of metals A and B may be sufficiently different to minimize Reaction [I]. In this case, the use of molten oxide electrolyte would be clearly advantageous. In the present study, the thermodynamic properties of the Pb-Ag system have been investigated using the cell: Previous galvanic cell studies on the Pb-Ag system2'= are not reliable due to the displacement reaction between the alloys and the chloride electrolyte. Wagner and ~erner,' using Laitinen and Liu's' value at 450°C for the standard electrode potential of Reaction 111, have estimated the percent error in the activity of lead bPb) when using a chloride electrolyte. At 1000°C the error for xpb = 0.10 is 12 pct. Taking the Gibbs free energies of formation for PbClz and Ag cI,' and the equations of Wagner and Werner,' the error in apb at 1000°C and Xpb =0.10 was calculated to be 140 pct. However, using the Gibbs free energies of formation for Pb O' and an estimated value for Ag 20, the error in apb when using a molten oxide electrolyte at 1000°C was estimated to be less than 1 pct for The virtual reaction of cell I1 for the passage of n Faradays of positive electricity from left to right in the cell is: where 5 is the Faraday equivalent (23,063 cal per v equivalent), E is the electromotive force of the cell in volts, and n is the number of Faradays of electricity required for the transfer of 1 g-atom of lead through the cell. The value of n should be equal to 2 since lead is generally divalent in oxide melts. However, the presence of either tetravalent lead ions or electronic conductivity through the molten oxide electrolyte will result in a value of n greater than 2. Bockris, Kitchener, and Davies' have determined the amount of ionic conductance in a liquid PbO-SiO2 mixture (xPbO= 0.50) at 920°C by measurement of the volumes of CO and C& evolved at a carbon anode during electrolysis. From their data a value of 2.13 * 0.16 was calculated for n. Although their measurements indicate the possible presence of multivalent lead ions and/or electronic conductivity, their measurements were not at silica saturation and no definite conclusions can be drawn. However, as a result of the electrotransport measurements described in the next section the ;due of n can be taken as equal to 2.

Jan 1, 1969

By J. J. Gilman

Zinc monocrystals, when compressed nearly parallel to their basal planes (within 20), deform in a new way; and certain deformation markings, called "-bands," are typical of this new mode. Characteristics of these bands are described. Mechanical behavior of low angle zinc monocrystals was investigated in some detail. Recrystallization did not occur upon annealing of banded specimens that were free of deformation twins. -Bands do not seem to be the result of nonbasal slip, but rather, a result of a microbuckling mechanism. u-Bands differ qualitatively and quantitatively from ortho kink bands. A dislocation model, consistent with some of the features of u-bands, is described. THE plastic deformation of zinc monocrystals with slip planes (0001) nearly parallel to the stress axis was studied in this investigation. In a previous investigation, it was shown that some low angle zinc crystals (those with slip planes making angles of more than about 2.5+1° with the compression axis), deform by ortho kinking while others (those with slip planes making angles of less than 2.5+1° with the compression axis) deform in a new way.' This new mode of deformation will be described in some detail here. Some of its striking features are: 1—it operates only for compressive stresses, 2—its temperature dependence is anomalous, and 3—it exhibits a new type of "yield-point" behavior. The mode of deformation to be discussed is not new in the sense that no previous evidence of its existence had been reported. The markings that it creates on the cleavage surfaces of zinc crystals have been described by several investigators.'" However, this is the first time that it has been made to operate under controlled conditions so that its response to mechanical variables, temperature, and aging treatments could be investigated and its geometry completely described. Apparently. Jillson' as well as Holden3 and Pratt" believed that the small bands they observed were simply small versions of ortho kink bands. In fact, two of these authors3,6 "alled the markings "micro kink bands." In spite of the precedence, it is felt that this term is not entirely suitable because these bands do not have the same genesis as kink bands, and they are qualitatively different in structure. As will be indicated by later discussion, the bands seem to be related to the tensile deformation bands observed in aluminum. The present author has chosen to call the bands "micro deformation bands," or simply ",ubands," and the deformation process, ''p-banding." Experimental Methods Crystals were grown from 99.999+ pct Zn obtained from the New Jersey Zinc Co. The details of the technique are given elsewhere." It should suffice to say that the crystals were seeded for orientation control, and precision pyrex tubes were used for molding them. About 40 crystals were used, yielding some 130 specimens. Fig. 1 illustrates the typical form of the specimens and shows how the orientation angles are defined. The crystal specimens were usually 1 3/4 in. long and about 150 mil in diameter. The angle between the slip or cleavage plane (0001) and the specimen axis is designated by xo, while a is the angle between the maximum slope of the (0001) plane and the nearest close-packed direction [1210], vary ing from 0°to 30°. The crystals were cut into specimens with a jeweler's saw and the ends were squared by filing (specimens held in V-block). Crystals of this orientation are stiff toward bending, so this procedure introduced only deformation localized at the ends. Then the specimens were polished either chemically in 50 pct HNO³ or electrolytically in 20 pct chromic acid. The mechanical tests were made with an Instron testing machine. This machine weighs by means of electric strain gages on elastic bars and is quite stiff, since the full-load deflection of its load cells is at most 0.002 in. Most of the testing was done at a

Jan 1, 1956

By G. Krauss, J. M. Thompson, H. Y. Kumagai

Boron-doped p-type and arsenic-doped n-type source materials were used to deposit thin silicon films on amorphous fused quartz substrates by cathodic sputtering in argon atmospheres. All as-sputtered films were found to have high electrical resistivities of about 104 ohm-cm, despite controlled variation of the substrate temperature from 50O to 400°C. The high resistivity of the n-type films persisted even after postdeposition heat treatments as high as 1000°C, while p-type films showed a sharp decrease in re-sistivity to values on the order of 1 ohm-cm or lower after heat treatments above 650°C. X-ray and electron diffraction, together with transmission electron microscopy of the p-type films, revealed that the improved electrical properties resulted from two distinct processes. A primary crystallization or recovery within the pains, which were approximately 200Å diam in the as-sputtered films, accompanied the initial sharp drop in resistivity at 650°C. Following this process, a secondary recrystallization or discontinuous grain growth was nucleated in films heated at 1000°C. The resulting significantly increased size of certain grains and the corresponding decrease in grain boundary area accompanied an additional decrease in resistivity after heat treatment at 1000°C. The properties of thin silicon films are of interest because of their possible application in device technology. Although evaporated silicon films on amorphous substrates1-3 and both sputtered and evaporated germanium films4-' have been studied in some detail, sputtered silicon films have not been widely investigated. It has been observed that evaporated silicon films deposited at substrate temperatures below approximately 600°C are amorphous.1,3,9,10 At substrate temperatures higher than this, the films are polycrys-talline, sometimes exhibiting a fiber texture with the fiber axis normal to the substrate surface.' Similar results have been obtained with germanium films, although in this case the substrate temperature for the amorphous to crystalline transformation is reported to be as low as 150OC.5 The mechanism of film deposition by cathodic sputtering differs markedly from that of thermal evaporation. It might be expected, therefore, that the properties of sputtered and evaporated silicon films would also differ. The purpose of our study was to determine the effects of deposition conditions and heat treatments on the electrical resistivity, structure, and composition of thin silicon films sputtered on fused quartz substrates. EXPERIMENTAL DETAILS Apparatus. A schematic diagram of the sputtering apparatus is shown in Fig. 1. The vacuum chamber was enclosed by an 18-in.-diam by 12-in.-high Pyrex bell jar mounted on a stainless-steel base plate. Access holes in the base plate were used to supply argon gas to the chamber, to allow for various electrical feedthroughs, and to provide mechanical motion to the shutter between the source material and substrate. The chamber was evacuated by a pumping system consisting of a 720 liter per sec oil diffusion pump backed by a 13 cu ft per min mechanical pump. Ultimate pressures of less than 1 x 10-6 torr could be achieved. The substrates were securely mounted on the stainless-steel substrate holder by quartz tabs held in place by stainless-steel screws. Temperatures of the substrate holder were measured by a thermocouple inserted within the holder. A quartz lamp was used to heat the holder and temperatures as high as 420°C could be maintained. Deposition Conditions and Procedure. The substrates used were polished fused quartz slides 116 by 1-12 by 3 in. and were outgassed at 200°C for 1 hr at a pressure less than 1 x 10-5 torr before film deposition. This was followed by a presputtering period of 2 hr during which the movable stainless-steel shutter was so positioned that deposition on the substrate was prevented. At a sputtering voltage of 5000 v dc and an argon pressure of 0.03 torr, the cathode cur-

Jan 1, 1967

By W. W. Mullins

The development, by the mechanism of volume diffusion, of a grain boundary groove on an interface separating a solid phase and a saturated fluid phase is calculated under the following assumptions: 1) isotropy of the interfacial free energy 's, 2) applicability of the Gibbs-Thompson formula relating curvature and chemical potential, 3) a nearly planar groove surface. The groove profile is found to have a .fixed shape and linear dimensions that are proportional to (time)1/3. The constant of proportionality is evaluated and involves ?s in such a way that the latter my be evaluated from grooving kinetics. A grain boundary that intersects an interphase interface will tend to produce a groove along the line of intersection (Fig. 1). The ultimate motivation for the formation of the groove is the reduction in interfacial free energ that occurs as the grain boundary contracts. Smith has discussed the way in which the free energy of the interfaces determines their dihedral angles at the groove root and has given a detailed analysis of the effect of the dihedral angles upon the nature the microstructures developed in polyphase alloys. Herring2 has extended the considerations to the case in which the free energy of an interface depends on its orientation and has thus added torque terms to the condition for interface equilibrium. Although the grain boundary and the interphase interface may quickly achieve the proper equilibrium angles where they intersect, as determined by the balance of equivalent tensions and torques,"2 the groove will generally continue to grow (though with decreasing speed). Thermodynamically, this continued growth reflects the fact that the lowest free energy cannot be achieved until the entire grain boundary has been eliminated; mechanistically, the growth occurs in response to inhomogeneities of chemical potential that are caused by the constraint of fixed dihedral angles at the groove root. The latter point is illustrated in Fig. 1, which shows that atoms* near the groove are on the convex side of a cylindrically curved surface and therefore have a higher chemical potential than atoms on the flat interface beyond. Thus atoms tend to leave the curved groove shoulders and force the groove to deepen. When both phases are solid additional chemical potential gradient may arise from whatever strain fields are necessary to insure continuity of material across the interface. In the discussion that follows, this complication due to strain will not occur since we always assume one phase to be a fluid and the other a solid. The transport processes that may operate to permit growth of the groove are surface (interface)* diffusion, volume diffusion in the phase on either side of the interface, and evaporation-condensation when one phase is gaseous. (Also a melting-freezing process is responsible for groove enlargement on a solid-melt interface as discussed in Sec. VI). The theory of grain boundary grooving has been discussed in detail for the processes of surface diffusion and of one type of evaporation-condensation.3'4 The theoretical predictions for the mechanism of surface diffusion have been confirmed in an experimental study of grooving kinetics in copper.5 In this paper, the theory of groove development by volume diffusion will be presented. Volume diffusion can occur either by atomic migration in the solid S or by diffusion of S atoms in the fluid phase, or solvent, adjacent to the groove surface. As discussed in Sec. V, volume diffusion in the solid should be less important than surface diffusion in forming a groove. Apart from verifying this statement then, the main interest of the present analysis centers on diffusion in an external solvent. The solvent may be either a liquid (e.g., water, or-

Jan 1, 1961