By M. Baeyertr

Since 1915 many papers and books have covered industrial applications of X-rays from various angles. Two of the more recent are a paper by Fink and Archer, which describes in detail the technique of radiography, and a paper by Clark2, which embraces the whole field of X-ray metallogmphy. This paper, therefore, is confined to work of the X-ray Laboratory of the Western Electric Co., which naturally divides into two categories: radiography and diffraction patterns of various types. Radiography Radiography is the field in which the application of X-rays has had most general appeal among the industries which produce or use metals and alloys. Equipment permitting the examination of heavy sections of metals less permeable than aluminum or other light alloys requires apparatus capable of generating hard X-rays over a considerable period of time. The equipment used in the work presented in this paper is practically identical with that described by Fink and Archer in their paper on radiography in industry and is easily capable of penetrating 1/8 in. of lead. Radiography is used in two major groups of problems: (1) in the development of cquipment and tools and (2) in studies of materials. So far there has been no instance in which the use of radiography for routine inspection is justified. This is partly due to the fact that the manufacture of telephone apparatus involves the production of many identical parts by standardized procedures and equipment that has had development and trial before being put on a regular production basis. It is during this stage of development of equipment and tools that radiography has been used to particular advantage.

Jan 1, 1931

By W. L. Dennen, V. H. Wilson

THIS paper is a description of the opera¬tion and results of a Humphreys Spiral Silt Cleaning Plant at the Powderly Colliery of The Hudson Coal Co. during the first nine months of operation and follows a pre¬liminary description given at the Anthracite Institute in May, 1947, in a paper titled "Preparation of Anthracite Sift for Boiler Fuel in a Humphreys Spiral Test Plant" by H. H. Otto, V. H. Wilson and W. L. Dennen. This plant is considered a full size operating test plant and, like all new plants, numerous minor changes in the methods of operation have been made from time to time to secure the results desired. Views of the silt preparation plant and of the screening house are given in Fig 1 and 2. This plant consists of 48 spirals in 8 batteries of 6 spirals each, 36 of which were to be operated as primary spirals and the remaining 12 as secondary spirals. A brief description of the plant and its operation follows. The only material cleaned at the plant during 1947 was that carried in the underflow from the Thickener which handles the Breaker waste water. This underflow, amounting to approximately 2000 gpm of water and containing 12.6 pct of solids, is pumped .to vibrating screens where the plus 316-in. material is removed. (Fig 3). This oversize material drops into a pocket from which it is trucked to the run-of-mine

Jan 1, 1948

By Francis M. Walters

THE problem of making iron-manganese alloys of scientific purity is a rather difficult one. They cannot be prepared in air because of the readiness with which the metals oxidize at the temperature of melting; and they cannot be prepared in vacuum because of the, high vapor pressure-of- manganese. The very property of: manganese which permits it to be purified interferes with the utilization of the best method of making pure alloys. Accordingly, it is necessary to use a gas atmosphere which will not affect the-properties of the alloys. The gases available for the purposes are hydrogen; helium and argon. Nitrogen forms intermetallic compounds with manganese very readily. Hydrogen, while valuable as a deoxidizer and having the advantage of being comparatively cheap, is explosive over a wide range and, has a rather high thermal conductivity. Helium is reported as, costing little but is difficult to secure at a reasonable price and also has a conductivity nearly as high as hydrogen. Since argon has a sufficiently low thermal conductivity, it has been selected for use in one induction furnace for melting, under a controlled, gas atmosphere, in spite of its cost, which is so high (70 cents to $1.50 per cubic foot) that it must be stored and purified.. Such a gas atmosphere-as argon makes necessary the use of the, high-frequency induction method of heating. This involves, a non-metallic container for the gas; .which is most conveniently of fused quartz or glass. The next

Jan 1, 1929

By ROBERT R. ABUOTT

(Cleveland Meeting, October, 1912.) THE practice of carbonizing steel for the purpose of case-hardening has assumed great commercial importance within the past, 10 years. Formerly, case-hardened steel was held in more or less contempt, since it. was considered a cheap substitute for tool-steel. This is no longer the case. The development of the motor-car industry, and coincidentally that of modern alloy-steels, has resulted in overcoming many difficulties formerly experienced in case-hardening. This result has been accomplished by increased knowledge regarding the analysis of the steel which would respond most readily to case-hardening, and by more careful methods of treatment of the carbonized steel. The ordinary method of carbonizing consists in packing the steel with the carbonizing-material in cast-iron boxes and placing them in a furnace at a temperature of from 1,500° to 1,900° F. for a time sufficient to give the required depth of cc case." The steel is then either quenched directly from the box, or is allowed to cool without unpacking, and finally given a single hardening-heat., or, for special work, two or three heats. During the year 1911, more than 100,000 tons of carbonizing-material was sold in the United States, at an average price of probably $55 per ton. More than 85 per cent. of this material consisted of granulated bone. Within the past four years, many manufactured compounds have been placed on the market, consisting largely of some form of carbon or carbonaceous material, with or without the addition of chemicals. Steel will absorb carbon placed in contact with it at the temperature of the atmosphere. The reaction is exceedingly slow, but. increases rapidly with increasing temperature. Below * Metallurgical Engineer, The Peerless Motor Car Co.

Dec 1, 1912

Jan 1, 1903

By R. A. L. Black, J. E. Jennings

The problems of slope stability in open cast mines are examined. A criterion, the instantaneous stripping ratio, is suggested for use in the design of pit slopes and as an index of control at all stages of the exploitation of the orebody. This criterion may also be related to safety and to the maximizing of profits. Two approaches to safe design of slopes, one from the point of view of soil mechanics and the other from the point of view of rock mechanics, are described and critically compared. The effect on slope stability of the regional tectonic stress field is discussed. Explanation is given of the application of the Terzaghi effective stress concept to problems in both soil and rock environments, including possible effects when borehole deformation techniques are used to measure stresses in rock in situ. A company embarking on open cast mining is faced with two basic questions: 1) will the venture be profitable and 2) can it be carried out with safety? The two questions are obviously interrelated because both depend upon the slope angles adopted for the pit. The cost of open cast mining depends largely upon the stripping ratio, defined as the volume of overburden that must be removed to the volume of ore recovered. The steeper the slope angles, the more favorable the stripping ratio, but the stability of the slopes, and therefore the safety of men and materials in the pit, require that the angles be made relatively flat. Consequently, the design depends upon a compromise: the slopes must be steep enough to result in economical mining and flat enough to ensure safety. Today there is a world trend towards deeper mining by open cast methods. This is mainly due to the higher cost of underground mining and the lower cost of open excavation resulting from the introduction of large modern earth and rock-moving machinery. Deeper open cast mining has led to a very great increase in the volumes of wasted overburden, and much thought is being given to the considerable economic benefits which would result if pit slopes could be made steeper by even one or two degrees. The result has been an increasing interest in research into slope stability problems in the expectation that the application of scientific principles will provide solutions leading both to economies and to more predictable operation of the mines. In at least four places, the U.S., Australia, Western Germany and Southern Africa, comprehensive investigations are at present in progress, and it is the object of this paper to review some of the more important aspects of these programs. RELATION BETWEEN ECONOMY OF OPERATION AND SLOPE ANGLES The main object of any industrial enterprise in a free economy is to make a profit. In mining, where profits must be made from a wasting capital asset, a further definition of the profit motive is imposed, namely that the economic aim should be to maximize the total possible profit. But since profits deferred for a number of years are not as valuable as profits that are immediately available, it is usual to discount deferred profits at some rate of interest which reflects their current or present value in the hands of the investor. Thus, in mining the logical aim can be defined more closely still: to maximize the present value of the total future profits. In commercial terms the present value represents the market value of the operation as a going concern. Many factors enter into the forecast of current and future profits. They include the volume of production, the price of the salable product and the cost of production. Current profits can be estimated with reasonable accuracy by the operating engineers; but it is the task of economists and management to assess future trends in the mineral markets and in the economy as a whole, and together with the engineers, they can then estimate the future cost and profitability of the mining operations. In open cast mining, the rate of ore production once decided on remains a virtually constant factor unless a major change in the capital structure of the mine is made. But one factor over which the operator has a considerable measure of control is the ratio of the volume of ore mined to the volume of waste over-

Jan 1, 1963

By Ivor Jenkins

Processes employing 'controlled at-mospheres in the heat-treatment of metals and alloys are now well established on an industrial scale, and the general principles involved and the advantages to be gained in the use of the technique have received considerable publicity over a period of years. During this time the greatest emphasis has been on the establishment of the process in industry, the main effort being devoted to development work on various types of atmospheres, their useful fields of application and the design of suitable heat-treatment furnaces in which they are to be used. The various types of controlled atmospheres are fairly well standardized, but there still remains a considerable field for the investigation of related problems, in connection with both the gas-generating equipment and the surface chemistry of the heat-treatment of metals, especially in complex controlled atmospheres. This paper describes certain investigations of this nature that were carried out in England up to 1939. The development of processes employing controlled atmospheres has been asso-ciated to a very large extent with the heat-treatment of steels, both because of the major importance of steel in industry and the many diverse and dificult prob-lems of surface chemistry involved when steels of such a wide range of composition are heated in the presence of active gases. Controlled atmospheres such as disso-ciated and burnt ammonia or charcoal gas are used in the heat-treatment of low-carbon and high-carbon steels, but from certain points of view a suitable atmosphere generated by the partial combustion of city gas is to be preferred. Both the ammonia derivatives are comparatively expensive, and even if the burnt ammonia is regenerated, thereby reducing operating costs, the capital expenditure of the gas plant may make it prohibitive for the smaller type of furnace installation. Charcoal-gas generators are not without their operating difficulties especially those associated with the quality of the charcoal, clinker formation and the removal of carbon dust from the generated gas. City gas has the advantage of being comparatively cheap and "on tap" in most if not all industrial centers. The use of raw city gas as a protective atmosphere in the heat-treatment of steels has been described,' but it presents certain difficulties because of its complex composition and its explosive nature when mixed with air. These factors, together with the tendency toward sooting at elevated temperatures, arising mainly from the hydrocarbon gases present, all militate against its use as a protective atmosphere in industrial furnaces. The following analysis, based on the analyses of city gas in different localities in Great Britain, indicates the wide limits existing

Jan 1, 1948

By Ivor Jenkins

Processes employing 'controlled at-mospheres in the heat-treatment of metals and alloys are now well established on an industrial scale, and the general principles involved and the advantages to be gained in the use of the technique have received considerable publicity over a period of years. During this time the greatest emphasis has been on the establishment of the process in industry, the main effort being devoted to development work on various types of atmospheres, their useful fields of application and the design of suitable heat-treatment furnaces in which they are to be used. The various types of controlled atmospheres are fairly well standardized, but there still remains a considerable field for the investigation of related problems, in connection with both the gas-generating equipment and the surface chemistry of the heat-treatment of metals, especially in complex controlled atmospheres. This paper describes certain investigations of this nature that were carried out in England up to 1939. The development of processes employing controlled atmospheres has been asso-ciated to a very large extent with the heat-treatment of steels, both because of the major importance of steel in industry and the many diverse and dificult prob-lems of surface chemistry involved when steels of such a wide range of composition are heated in the presence of active gases. Controlled atmospheres such as disso-ciated and burnt ammonia or charcoal gas are used in the heat-treatment of low-carbon and high-carbon steels, but from certain points of view a suitable atmosphere generated by the partial combustion of city gas is to be preferred. Both the ammonia derivatives are comparatively expensive, and even if the burnt ammonia is regenerated, thereby reducing operating costs, the capital expenditure of the gas plant may make it prohibitive for the smaller type of furnace installation. Charcoal-gas generators are not without their operating difficulties especially those associated with the quality of the charcoal, clinker formation and the removal of carbon dust from the generated gas. City gas has the advantage of being comparatively cheap and "on tap" in most if not all industrial centers. The use of raw city gas as a protective atmosphere in the heat-treatment of steels has been described,' but it presents certain difficulties because of its complex composition and its explosive nature when mixed with air. These factors, together with the tendency toward sooting at elevated temperatures, arising mainly from the hydrocarbon gases present, all militate against its use as a protective atmosphere in industrial furnaces. The following analysis, based on the analyses of city gas in different localities in Great Britain, indicates the wide limits existing

Jan 1, 1948

By R. T. Hukki

IT is no great exaggeration to say that present grinding practice and economics are largely determined by lining design. A record of outstanding liner wear can be achieved with any liner surface pattern that will positively lock the outer layer or layers of grinding media. With no slippage, lining wear is bound to be slight. At the same time, popular practice calls for tumbling loads of about 50 pct of mill volume to obtain maximum grinding capacity. Innumerable parallel grinding investigations have verified that optimum speed for such a mill lies within 70 to 85 pct of theoretical critical speed. If the mill is speeded up to 100 pct of critical, little or no grinding can be accomplished. Earlier Work on Supercritical Grinding: First investigations concerning grinding at supercritical speeds seem to be very old. Remarkable work on the subject has been performed by White,&apos; and his experiments have been described and summarized by Richards.&apos; White&apos;s contributions seem to have passed unnoticed by Fahrenwald,2,3 whose extensive experiments have been well presented, yet apparently very little appreciated. Additional work on grinding at supercritical speed has been reported, e.g., by Lewenson and Tscherny,&apos; USSR; Anselm and Grunder,&apos;, Germany: and Rose and Evans." Great Britain. Subcritical and Supercritical Speeds: In the formula of the critical speed given in the textbooks of mineral dressing, no factor indicating the coefficient of friction is generally included. If this factor = 1.0, which is equivalent to grinding conditions in a mill provided with heavily ribbed lining, the formula of the critical speed holds as such and grinding is possible at subcritical speeds only. In a mill equipped with a smooth or relatively smooth lining, the numerical value of the friction factor in the denominator of the formula becomes <1.0, indicating that grinding at supercritical speeds should be possible in such mills. It has been recently shown by the author&apos; that a wide supercritical speed range will become available for grinding—and especially for fine grinding—if the basic conditions within the mill have been selected properly. Mathematical analysis of mill dynamics at supercritical speeds&apos; has indicated that the mill speed may be increased if: 1) total mass of grinding medium decreases, 2) mass of the individual grinding piece increases, and 3) the coefficient of friction between the outer layer of medium and the mill lining decreases. It is obvious that the mass of the individual grinding piece will be affected by its shape and by its specific gravity. The coefficient of friction decreases with: 1) increasing smoothness of liner surface, 2) increasing roundness of the grinding piece, 3) increasing fineness of material to be ground, 4) decreasing pulp density, and 5) decreasing hardness (abrasiveness) of the mineral to be ground. In a mill equipped with heavily ribbed lining, practically no size reduction will take place between the lining and the outer layer of tumbling medium, because slippage is prevented. In the overwhelming majority of today&apos;s mills the grinding accomplished is by virtue of cataracting and/or cascading media with some action within the tumbling charge. Sub-critical speeds only can be applied. In grate-type or peripheral discharge mills equipped with a smooth lining a tumbling load of any kind of common medium occupying about 50 pct of mill volume will behave in such a way that practically no slippage will take place. This has been verified in experiments run by the author in the laboratory and in pilot plant mills&apos; equipped with smooth lining. Again, the operation is limited to the subcritical range. In a mill with a smooth lining, grinding will be possible either at subcritical speeds or within a wide supercritical speed range as soon as the basic requirements for a desired speed are fulfilled. In a mill operated at supercritical speed, any point on the liner surface proceeds at a speed greater than that indicated by the formula of the critical speed, while any grinding piece situated in the outer layer of the medium against the lining proceeds in the same direction at a speed less than that indicated by the critical speed. This speed difference produces a very effective attrition grinding zone between the liner surface and the outer layer of the medium. The share of attrition grinding of the total grinding accomplished increases rapidly with increasing speed in the supercritical speed range. The smooth surface of the mill lining may be well illustrated by the surface of a bucking board. The outer ball layer may be similarly represented by the lower surface of a muller. If the bucking board, the material to be ground, and the muller all proceed in the same direction at the same speed, no grinding will result. This is the general situation in the mills of today. If, however, the muller is pulled with respect to the board, moving or stationary, grinding will be accomplished effectively. Although grinding in today&apos;s mills is primarily the result of cataracting and/or cascading media, the principal place of grinding at high supercritical speeds will be the attrition zone.&apos; In the mineral dressing laboratory of the State Institute for Technical Research. Helsinki, Finland, large quantities of different ores have been ground in a pilot plant ball mill (3x3 ft) at a top speed about 230 pct of the critical. With the same mill, theoretical investigations concerning the grinding characteristics of ball mills equipped with a smooth lining have been carried out up to the speed of 313 pct&apos; of the critical. With a smaller mill, the grinding characteristics with a variety of grinding media have been investigated at speeds up to 2000 pct of the

Jan 1, 1959

By J. W. Spretnak, G. W. Cunningham

A study has been made of the growth and disappearance of voids in the interface of pressure bonded copper. The formation of visible voids is primarily due to spheroidization and coalesence of microvoids produced during the application of pressure. The microvoids could be prevented from forming by the application of high pressures or by increasing the ductility of the copper. Migrating grain boundaries were found to be more effective in void removal, than stationary grain boundaries. DURING the course of an investigation on the mechanism of pressure bonding, it was found that voids formed in the bonding interface which inhibited migration of the interfacial boundary and grain boundaries in the bond region. Therefore, an effort was made to determine the nature of the voids and how they form, grow, and disappear. This paper reports the results of such an investigation. The existence of interfacial voids is not solely a characteristic of massive components of metal which have been bonded by the application of heat and pressure, but is a phenomenon which has been observed in sintering as well. Simonsen attempted to study the sintering process by hot-stage microscopy and thereupon observed the formation of interparticle porosity as sintering proceeded. It was assumed that the porosity was due to grooves created at the location where grain boundaries joined the surface of the particle. Pranatis, Castelman, and seigle2 have also observed voids along the areas of contact in wound-wire specimens used for sintering studies. They did not discuss the point in detail since this behavior was not general, but they did suggest that the voids might develop as a result of stresses along the interparticle contact area. In previous investigations on pressure bonding, workers3 have suggested that voids may exist in the region where mating surfaces are placed in intimate contact, but the existence of the voids was not verified and no attempt was made to study the growth and disappearance of these voids. Durst noted the existence of pores in roll-clad structures prepared by cold reducing two sheets to force them in contact and then annealing to improve the bond. Since his unbonded regions contained a gas which he assumed to be insoluble, he proposed a mechanism which consisted of spheroidization of the unbonded regions and a growth of the contact area, but no speculations were made regarding disappearance of the gas filled pores. One interesting comment made by Durst was the suggestion that flattened voids with sharp corners which are produced during roll bonding will have a greater driving force for spheroidization than the more rounded pores created by pressing metal powders and thus spheroidization and neck growth will occur at lower temperatures. In this study it was necessary to demonstrate conclusively that voids can actually exist in the interfacial bond area. Experimental work was then directed toward a study of the mechanism whereby the voids grow and subsequently disappear.

Jan 1, 1963

By A. J. Griest, P. D. Frost, J. R. Doig

During the past 5 years, research directed toward the development of titanium alloys having improved strength-ductility relationships and heat treatability has been carried out at Battelle for the U. S. Air Force.1"3 In the course of this work, a method of heat treating ß-stabilized titanium alloys was developed which produced a wide range of useful properties.4 The heat treatment consisted of two steps: a) solution treating at temperatures in the a-ß phase region, and b) overaging at a lower temperature in the range 800°to 1100°F. Corollary to the alloy development work, research was conducted on the mechanism of the heat-treatment reaction. The investigations of Frost and co-workers on isothermal transformation in Ti-Cr5 and Ti-Mn8 alloys disclosed the existence of the transition phase, w, during the course of the decomposition of metastable ß phase. Subsequent work at Battelle7,8 &apos;and at Case Institute by Brotzen and co-workerss further clarified the nature of the decomposition process. Beta decomposition was found to proceed by the following series of reactions: 1 2 3 4 a + Ti, My (in eutectoid systems). ßo, ßr, and ßU refer to ß phase of original, enriched, and ultimate alloy contents, respectively. Omega is a transition phase having a complex structure. 10-13 Step 4, of course, occurs only in ß-eutectoid systems. This paper presents data correlating transformation behavior with mechanical properties for the following alloys: Ti-8Mn, Ti-8Mn-2A1, Ti-4Mn-4A1, Ti-6Al-4V, and Ti-4Fe. The isothermal decomposition of ß in titanium-manganese alloys of similar composition has been investigated by Frost and coworkers8 and the effect of various annealing treatments on alloys in this system has been studied by Holden, Ogden, and Jaffee.14 The compositions Ti-8Mn-2Al, Ti-4Mn-4A1, and Ti-6A1-4V, were studied in the present work in an effort to define more clearly the effect of aluminum on the response to solution and aging treatments. Ogden, Holden, and Jaffee15 have invesitgated the effect of aluminum on the response of a similar alloy (Ti-8.8Mn-2.46A1) to annealing treatments, and Luini and Lee16 have made an exploratory investigation of the heat-treatability of the Ti-4Mn-4Al alloy. The Ti-4Fe alloy was studied as an example of a moderate1y active eutectoid system. Holden, Ogden, and Jaffee 17 have studied Ti-Fe alloys and have presented some hardness data for aging at 400°C for alloys of Ti-2.56, 5.01, and 7.35 iron after quenching from the a-ß field (750°C). EXPERIMENTAL PROCEDURES The experimental procedures generally used in the precipitation-hardening study are outlined in the following sections. Departures from these techniques are noted in the discussions of the individual alloys. Table I presents the nominal and actual compositions of the alloys studied, together with the swaging and rolling temperatures. In all cases, these temperatures were in the a-ß field and the microstructures consisted of an equiaxed a-ß mixture. Melting and Fabrication—Except for the commer-

Jan 1, 1960

By H. R. Ogden

The notch sensitivity of titanium alloys is affected by impurity content, microstructure, and heat treatment. Using notch tensile properties to evaluate notch sensitivity, three commercial titanium-base alloys were investigated over the temperature range of -320o to 390°F. The alloys studied were Ti-5Al-2.5Sn, Ti-6Al-4V, and Ti-2Fe-2Cr-2Mo. Six interstitial levels were studied for each alloy in four mi-crostmctural conditions. The ff- 0 alloys were studied in both the annealed and heat-treated condition. All tests were conducted using 1/4-in. diam round tensile samples. The notched samples had a 50 pct notch with a notch sharpness (a/r) of 53, corresponding to Kt 6.3. Notch sensitivity was increased by increased interstitial content, low temperature, and acicular-type microstructures. The heat-treated, high-interstitial content - 13 alloys were more notch sensitive than the same alloys in the annealed condition. In addition, minima in the notch tensile-temperature curves were observed at temperatures near 32°F. These minima became more pronounced with increasing interstitial content. 1 HE increaseduse of titanium alloys in high strength applications at subzero temperatures requires that a better under standing of the low-temperature behavior of the alloys be obtained. At low temperatures, metals generally exhibit increased strength with lowered ductility and tohness. Notch sensitivity and the factors which influence it become more important as the strength level is increased and the temperature is decreased. Some of the factor s which affect notch sensitivity in ti- tanium alloys are composition, interstitial content, microstructure, and heat-treatment condition. In this paper, the results of a study of these variables on the notch sensitivity of three titanium alloys at temperatures from —320o to 390o are reported. The notch geometry selected for this program was chosen to provide a severe test of notch sensitivity. The ability of the metal to flow without initiating fracture under these severe conditions is reflected in the notch-strength values. Since notch strength is, in part, determined by the constraint exerted by the combined tensile stresses, the behavior of notch specimens reflects the properties of the material under combined stresses. For example, a material with a high notch-unnotch strength ratio may be expected to withstand the biaxial stresses encountered in a pressure vessel better than a material with a low ratio of notch-unnotch strengths. This implies that maximum strength alone is not a sufficient criterion for applications of this type. It further may be concluded that the various conditions that promote poor notch behavior also will affect adversely the performance of materials under combined stresses. In the alloys studied, these included low temperatures, high interstitial levels, and hasformed microstructures. EXPERIMENTAL PROCEDURES Three alloys, Ti-5Al-2.5Sn, Ti-6Al-4V, and Ti-2Fe-2Cr-2Mo, were purchased from commercial producers as 2-in.-dam rod stock. Oxygen and nitrogen were added to these alloys by remelting to obtain a variety of interstitial contents as shown in Table I. In order to Compensate for the much more potent strengthening effect of nitrogen compared with oxygen, an oxygen equivalent content is used to describe the total oxygen plus nitrogen contents studied. It has been suggested previously1 thatnitro-gen is approximately twice as effective in strengthening as oxygen, and carbon, to the extent it is in so-

Jan 1, 1962

By R. N. Thurston, E. A. Nesbitt, G. Y. Chin

A general relalionship between the amount of glide shear (due to slip) and the macroscopic shape change has been developed. Since the deformation can be large, finite strain analysis is employed. In this treatnzent, the shape change is expressed by a deformation gradient matrix, F - [axi/aXj1, where X and x refer to the initial and final positions of a particle. This matrix is readily evaluated in terms of the amounl of glide shear, a , and the direction cosines of the slip-plane normal and the slip direction for a single active slip system. In the case of deformation from slip on several systems, the product F(a) of the several deformation gradient matrices is first calculated. Then, by assuming that the final configuration is reached by a long series of small shears of magnitude a, occurring more or less alternately in the several slip sys- IN problems of crystal plasticity, it is often necessary to relate the amount of glide in the operating slip systems to the macroscopic strain components. This relationship is relatively simple when only small strains are considered. In this case the separate strain contributions from several slip systems are additive. Such a procedure is incorrect in the case of large plastic deformation. To the authors&apos; knowledge, no general treatment of the latter problem has appeared in the literature. In specific instances, Mark, Polanyi, and schmid3 have derived the relationship between glide and axial elongation during tensile pulling of a single crystal when only one slip system is active. A similar relationship for duplex slip was worked out by v. Goler and Sachs.4 Taylor and Elam5 have also studied in detail problems of large plastic deformation. Due to uncertainties as to the slip systems at the time, terns, the final deformation gradient matrix can be obtained. Mathematically, the problem is reduced to finding the limit of F(dN as N — m while a — 0 in such a way that the Product Na = 0, a ftnite conslant designatzng the accunzulated amount of shear. It turns out that this limit is simply , where F, is the matrix whose elements are the coefficients of a in the F(a) matix. Application is made of the present treatment to a fcc crystal of Perlrzalloy compressed on the (110) plane and contrained to elongate zn the [112] directzon. In addition, it is shown that one rnay readily obtain from the general analyszs the well-known formulas relating elongation, amount of glide shear, and amount of lattice rotation for crystals deforming by single and double slip under tension. however, they were mainly concerned with proving that slip occurs on {111}(110) systems in fcc metals. The present general treatment arose out of recent investigations of magnetic anisotropy in cold-worked Fe-Ni alloys6 as well as some related problems in strength anisotropy of single crystals.&apos; Detailed application of the general analysis will be provided in the case of a Permalloy single crystal compressed on the (110) plane and constrained to elongate only in the [112] direction. It will be seen that, as expected, the small strain approximation leads to significant errors after moderate straining. It will also be shown that the present general treatment yields the formulas of Mark et al. and of v. Goler and Sachs in those specific cases. GENERAL CONSIDERATIONS Consider a homogeneous deformation in which a material point initially at moves to both positions being referred to the same set of Cartesian axes. Such a deformation can be

Jan 1, 1967

By D. G. Westlake

Resistance was measured as a function of temperature, 77° to 350°K,for niobium with hydrogen concentrations up to 3.76 at. pct. Cooling curves exhibited a discontinuity in slope that was attributed to the initiation of hydride formation. A thermal hysteresis was explained in terms of diffusion and the effects of mechanical constraint on nucleation and growth. The heat of solution of hydrogen in saturated Nb-H solid solution was 2. 737 * 0.045 kcal per g-atom, including an unknown stress contribution. The critical ternperatures for hydride formation during cooling and for embrittlement are correlated but not coincident. This, too, has been explained in terms of mechanical constraint and stress-itlduced tratzsfomtation. Nb-H alloys undergo a ductile-brittle transition with decreasing temperature.&apos;-3 Similar behavior has been noted for v-H.1,5 For the latter system, there is evi-dence6 suggesting coincidence of the temperature of minimum ductility and the critical temperature T, for initiation of metal hydride precipitation during cooling. A decrease in ductility due to the presence of brittle hydride particles is readily explainable. The fact that ductility begins to decrease at some temperature higher than T,4,5 has led us6 to suggest that precipitation may be strain-induced locally during tensile testing. Wood and Daniels&apos; have reported that a plot of temperatures for 10 pct reduction in ductility vs hydrogen concentration in niobium is not coincident with, but parallels, the solvus.7,8 They believe this indicates a correlation of precipitation and embrittlement. Unfortunately, the two reported solvuses 7,8 to which Wood and Daniels refer are not in agreement with each other. Furthermore, neither solvus was determined experimentally: each was a plot of calculated solubilities. Thus. neither is highly dependable for determining whether embrittlement coincides with initiation of hydride precipitation. Longson 9 studied phase relations in the Nb-H system between 77° and 473°K by dilatometry. Comparison with metallographic observations convinced him that discontinuities in the slopes of his dilatometric plots were coincident with the initiation of hydride precipitation. Plotting the logarithm of the hydrogen concentration vs the reciprocal of the temperature at which precipitation was initiated during cooling, he obtained a straight line shown in Fig. 1. Walter and chandler,&apos;&apos; using X-ray techniques to detect the for mation of a second phase? have obtained three experimental points in the temperature range 295° to 338°K which fall within Longson&apos;s experimental error for this plot. A similar plotg of temperatures at which dissolution was completed during heating was a parallel line shifted toward higher temperatures. A straight-line plot was obtained, also, for the temperatures of the ductile-brittle transitions,9 but it was shifted toward still higher temperatures. Longson calculated an activation energy of 2.980 * 0.300 kcal per mole for the hydrogen embrittlement mechanism, compared with 3.180 * 0.400 kcal per mole for hydride formation. Despite this agreement, he concluded, "It seems unlikely that embrittlement results from hydride formation..." because hydrogen embrittlement was observed at temperatures above the solvus. It is our contention that embrittlement is correlated with precipitation of the hydride.6 Because only Longson has investigated Nb-H phase relations at sub-ambient temperatures, we deemed it advisable to re-determine the temperature dependence of the solubility using the resistometric technique already proven successful for the V-H system.6 Coincidence of our solvus with temperatures for embrittlement would

Jan 1, 1970

By M. H. Pilkuhn, H. Rupprecht

p layers on n-type substrates of GaAs were prepared by difhsion of zinc into these substrates. Experimental details about the diffusion technique will be presented. It will be shown that inhomogeneity in the substrate doping level and crystal shucture defects cause nonplanarity in the junction plane. These nonplanarities give rise to high threshold current densities. From incremental sheet-conductivity measurements the zinc profile is derived. Data about surface concentration and gradient of the zinc concentration at the junction are presented. Finally, some results of laser diodes, which were made of wafers with extremely planar diffusion fronts, are discussed. ThE investigations reported here are part of a program concerned with the materials aspect in the fabrication of GaAs laser diodes. This includes studies of the influence of crystal defects introduced both during the growth of the crystal and as a consequence of subsequent diffusion. Compared with the progress made in the investigation of structure defects, for instance by X-ray microscopy in materials like silicon, no similar results are known so far for the case of GaAs. The further progress in laser diodes will depend very much upon our knowledge of these structure defects and subsequently upon our ability to avoid them. Laser diodes of GaAs had been made mostly by diffusing an acceptor impurity, normally zinc, into an n-type substrate. This procedure was found more convenient than the inverse one for various technical reasons. We will follow this line and restrict ourselves to zinc diffusion only in this paper. DIFFUSION TECHNIQUES AND EXPERIMENTAL DETAIL In order to set a refgrence for our experiments, we used a standard procedure for the diffusion runs. The diffusions were carried out in a sealed quartz tube for 2-1/2 hr at 850°C. One milligram zinc arsenide (ZnAsz) per cu cm of the tube volume served as zinc source. Under these conditions the junction depth was between 25 and 30 p. It is assumed, according to the investigations of the zinc arsenide system by V. Lyons and V. ilvestri,&apos; that ZnAs2 dissociates completely at 850°C into ZnsAsz and Asg. Since there is a condensed phase of ZnsAs2 in the tube at 850°C, the partial pressure of zinc is controlled by the pressure of the arsenic formed by the dissociation of ZnAs2. Due to the fact that the zinc partial pressure resulting from the dissociation of ZnsAsz is only a weak function of the partial pressure of arsenic, the amount of the initial ZnAs2 is not very critical. Experimentally, we found that the junction depth, as well as the surface concentration, was practically the same, if the ingots of ZnAs2 varied between 0.2 and 5.0 mg per cu cm. The wafers were oriented with the main faces in (100). Surface damage due to cutting and lapping was removed by a chemical-etch treatment in a rotating beaker (etch solution: HzSOr, H202, and HzO in a ratio 3:l:l). The GaAs substrate material was n type and doped with tellurium, selenium, silicon, or germanium. It was grown by means of horizontal or Czochralski techniques. After the diffusion process, junction depth and planarity were checked either by grooving with a

Jan 1, 1964

By Oscar Johnson

The industry has been canvassed for information on methods of handling grinding steel at milling plants, an important subject overlooked in most descriptive articles on milling plant arrangements. The data collected are offered in this paper as a guide to designers and planners who have loading and storage problems to solve. WITH capacities of milling plants expanding from a few hundred tons per day to many thousand, replenishment of grinding media is an important phase of mill operation. Information on this aspect of milling procedure, solicited from several mining companies, is summarized here. At International Nickel&apos;s Copper Cliff concentrator the normally strenuous job of changing rods is considerably simplified by the use of the Garrow rod charging machine, Fig. 1. The overhead crane, Fig. 2, brings a bundle of rods, weighing four to a ton, to the loading platform of the machine, positioned in front of the mill. The rods roll one by one down the slight incline of the platform onto a conveyor which sends them into the mill. A modified version of the Garrow machine, Fig. 3, is used at the Federal mill of St. Joseph Lead Co. An overhead crane places the portable steel structure in position in front of the discharge end of any one of the five 9x12-ft rod mills. It then raises a bundle of about twenty 3-in. rods to the discharge platform of the charging machine. The rods are 11 ft 7 in. long and weigh about 278 lb. By tripping a lever the operator allows one rod at a time to roll onto the inclined rollers. A slight push by the operator sends the rod smoothly into the mill. The Union Miniére du Haut Katanga rod charging machine, Fig. 4, is mounted on a pair of wheels at the forward end with swiveling castors at the back for steering it to position for use or storage. Wheels are equipped with locking brakes to maintain the machine in position while it delivers rods to the mill. The device is made in two parts. The first consists of the base, which carries the supporting wheels, grooved rollers, and drive. The other part serves as the rod deck, which can carry up to six 3-in. x 12-ft rods. A short boom built integral with the base reaches through the mill trunnion and delivers the rods into the mill barrel. Three grooved guide rollers ,are provided to receive the rods from the sloping charging deck. One rod at a time is fed to the rollers and thus delivered into the mill. Two of the rollers are driven by 11/2-hp motor through a V-belt drive. The third roller is driven off the first by a single V belt in a groove below the rod groove and on the same center line. Rods are delivered to the charger by an overhead crane in bundles of three to six as needed. The power is supplied by cables plugged into power outlets, suitably located near the rod mill discharge end. The Oliver Iron Mining Co. uses a rod charger, Fig. 5, suspended from a monorail by cables. It is constructed .of structural steel and has two decks, each capable of carrying five rods of 4-in. maximum diameter. The rods ride in grooved free-turning rollers. Legs extending down from the mill end of the mechanism act as supports when the unit is ex-

Jan 1, 1955

By Wilson Lundy

THE history of the production of sulfur from salt domes in Louisiana and Texas originated with the operations of the Union Sulphur Co. at Sulphur, La., followed by the Freeport Sulphur Co. at Bryanmound, Tex. Including the present development of Grande Ecaille by the Free-port Sulphur Co., which constitutes the tenth dome to be equipped for the production of sulfur in the Gulf Coast, less than 10 per cent of all the known domes have proved to contain sulfur in commercial quantities. The Grande Ecaille salt dome is in the tidal marsh of the Mississippi River delta in Plaquemines Parish, Louisiana. It is 10 miles southwest of the right descending bank of the river approximately 45 miles below the city of New Orleans and is within 4 miles of the shore line of the Gulf of Mexico.

Jan 1, 1934

By A. T. Aldred, K. M. Myles

The vapor pressure of chromium over solid V-Cr alloys has been measured by the torsion-effusion method in the temperature range 1450" to 1650°K. The chemical activities as well as the free energies, entropies, and enthalpies of formation of the alloys have hem computed from the vapor-pressure data. The activities of both chromium and vanadium exhibit fairly small negative deviations from Raoult&apos;s law over the entire composition range. The values of the excess entropies and the enthalpies of formation found at 1550°K are considered in terms of the changes in the clzaracteristic properties of vanadium and chromium that occur upon alloying. RECENT interest in the theory and properties of transition-metal alloys has shown the need for relevant thermodynamic data. The present investigation of the V-Cr system was undertaken as part of a more general study of thermodynamic properties of transition-metal alloys. The system was chosen because of the reported complete solid solubility of the components at all temperatures1 and because the difference in magnitude of the vapor pressures of vanadium and chromium allowed a simple effusion technique to be used. The torsion-effusion method was employed to minimize compositional changes in the alloys during the experiments. EXPERIMENTAL Equipment. The torsion-effusion apparatus, shown diagrammatic ally in Fig. 1, consists of a torsion system suspended inside a vertical vacuum chamber whose lower end is surrounded by a high-temperature vacuum furnace. An auxiliary optical lever and screen are used to determine the angle of rotation of the effusion cell. The torsion fiber is an annealed, high-purity, tungsten wire usually between 0.003 and 0.007 cm in diameter and about 43 cm long. The wire supports a concave mirror and a rigid tantalum connector tube. The effusion cell is fastened to the lower end of the connector tube by a dovetailed yoke and har- ness arrangement. The cells, which are 1.27 cm in diameter and 4.4 cm long, were made by electron-beam welding tantalum endcaps onto a 0.025-cm-wall tantalum tube. The two orifices, formed by drilling, have similar areas ranging from 0.011 to 0.031 sq cm. The noninductive sheath-type furnace consists of a single-phase tantalum heating element 6.35 cm in diameter, 15 cm high, and 0.013 cm thick; the element is completely surrounded by radiation shields in an evacuated chamber. The power system includes a 17-kva self-saturating saturable core reactor with an integral magnetic amplifier and a water-cooled, 15-kva, step-down power transformer with a multitap secondary. Temperatures are controlled to within ±1/2o at 1600°K by means of a unit that includes a reference voltage source, a dc electronic null detector, a current-adjusting proportional band relay, and the self - saturating reactor. At 1650°K the temperature variation within the cell, vertically and horizontally, is 3/4oK. Unwanted motions of the torsion system are damped by the movement of an aluminum vane, which is mounted on the connector tube, between the poles of an electromagnet. When not in use the magnet is withdrawn and rotated 90 deg to prevent its interaction with the rotation of the system. Measurements. The vapor pressure, p, is re-

Jan 1, 1964

By K. P. Gupta

The Cb-rich boundary of the (Cb,Al) a phase field at 1250OC is near 41 pct Al. The Al atoms tend to occupy the C. N. 12 sites in this structure. A homologous (Ta,Al)a phase was identified. No a phase was found in the Mo-Al system at 1200°C. The first binary o-phase with a non-transition element as a major component was found1,2 in the Cb-Al system. The composition of this phase was reported2 as approximately 34 at. pct Al, based on X-ray diffraction patterns taken of alloys in the as-cast condition. Further study of the composition of this o-phase, therefore, appeared desirable. Since Si was previously found3,4 to occupy preferentially the lowest C.N. sites (I and IV) in the a phase, and preliminary resultsa indicated that Al may show similar ordering, one of the aims of the present work was to obtain more complete information on ordering in (Cb, Al) o. Among the binary systems of Al with Ti-, V-, and Cr-group elements, the Ti-Al, Zr-Al, V-Al, and Cr-Al systems are known to comprise no o-phase. In the present work a Ta-Al and a Mo-Al alloy were studied in an effort to find additional o phases with Al as a major component. EXPERIMENTAL PROCEDURES AND RESULTS An alloy with the intended composition of Ta + 40 at. pct Al was prepared by arc melting in He atmosphere. In both the as-cast condition and after annealing for 10 days at 1250°C and quenching in cold water this alloy consisted of two phases, as seen in the X-ray pattern and the microstructure. One of these phases was identified as the o-phase; the observed and calculated d-spacings are shown in Table I. The lattice parameters of this o-phase are a = 9.972 A, c = 5.214 A and c/a =0.5228, as determined from a Debye-Scherrer pattern using Fe K a radiation. The d-spacings for the unknown second phase are given in Table 11. The alloy contained approximately 25 pct of the unknown phase after annealing, as estimated on the basis of microscopic examination. A Mo-Al alloy was prepared by arc melting, with an intended Al-content of 35 at. pct. The alloy button was annealed for 7 days at 1200°C and water quenched. The X-ray pattern of the alloy in both the as-cast and the annealed state showed the reflections of Mo3Al (Cr30 type structure) and an unknown phase different from a. Six Cb-Al alloys were prepared in the composition range 30 to 50 pct Al. All alloys were arc melted in He atmosphere. After annealing for three days at 1175oC in evacuated silica capsules and quenching in water, the alloys with 30 to 40 pct Al contained three phases, namely the o-phase, Cb3Al (Cr3O-type structure) and an unknown phase. The alloys with more than 40 pct Al contained two phases, namely, what appeared metallographically, the o-phase and the same unknown phase. In the alloys containing less that 38 pct Al, the unknown phase was not present after annealing for 4 days at 1250°c,

Jan 1, 1962

By C. E. Violet, R. J. Borg, E. M. Howard

The miscibility gap in the Au-Ni system has been determined by Mossbauer spectroscopy, with used as a probe. The phase boundaries were determined from the compositional dependence of both the isomer shift and Curie temperature. X-ray diffraction measurements were also used to confirm the Mossbauer results. 1 HE purpose of this research is to demonstrate the application of Mbssbauer spectroscopy to the determination of phase boundaries and to redetermine the miscibility gap by an independent and novel technique. The techniques evolved in this study are readily applicable to other polyphase systems and are generally as quick and accurate as the more conventional methods, e.g., metallography, X-ray diffraction, thermal analysis, and so forth. To be sure, not all polyphase systems will lend themselves favorably to Mijssbauer investigations, but this is a problem met in the use of conventional methods as well. The Mbssbauer spectrum responds to a different set of physical parameters, and consequently provides an entirely independent method of analysis. It is especially useful if the system has either a ferromagnetic or an antiferromagnetic transition. The Au-Ni system was selected because alloys containing more than -60 at. pct Ni become magnetically ordered at low temperatures; also the miscibility gap is quite well established (see Ref. 7 for a compilation of pertinent references, also Fig. 11, and thus provides a reliable test of this novel procedure. As Fe is the most commonly used Mijssbauer isotope, there exists a wealth of information concerning its behavior in iron-containing alloys and compounds. However, as yet there have been relatively few experiments using it as a probe to investigate nonferrous systems. By choosing a nonferrous alloy system, we are able to demonstrate that its use is not restricted to systems containing iron as one of the major constituents. Wertheim and ~ernick&apos; have used the same method to investigate Cu-Ni, and demonstrated that one can obtain a systematic variation in the isomer shift and magnetic hyperfine field. However, we believe this to be the first time these techniques have been used to establish phase boundaries. Two hyperfine interactions were measured and used to determine the phase boundaries, viz., the magnetic hyperfine splitting and the isomer shift which in this alloy system are both strong functions of composition. Calibration curves were established based upon single-phase solid solutions obtained by quenching from temperatures well above the maximum of the miscibility gap, see Fig. 1. Solid solutions containing 25, 50, 65, 75, 85, 92, and 96 pct Ni as well as pure nickel were used in the calibration procedure. Fig. 2 shows the Curie temperature, TC, and the isomer shift, v,, as determined from the Mbssbauer spectra, and variation in lattice parameter as determined by X-ray diffraction, as functions of composition. The compositions of the two-phase systems quenched from temperatures within the miscibility gap are obtained by comparing their respective values of TC and v0 with the calibration data. I) EXPERIMENTAL Mbssbauer sources were made by fusing the component metals in a tungsten arc melter, which has a water-cooled copper hearth. Both nickel and gold were 99.999 pct pure, and the melting was done in an atmosphere of purified argon. The alloys were rolled, diced,

Jan 1, 1969