By Richard V. Hughes, Rudolf J. Pfister

The necessity for getting more water into sands of low permeability in any secondary-recovery water-flood operation in order to recover all the available oil always has been a major problem. In the early days of water-flooding the addition of soda ash and caustic soda to fresh input waters was recommended and tried without success in the Bradford field. The most frequent difficulty was sand plugging. The use of natural and artificial brines often has been suggested for water-flooding, in the belief that laboratory observations of decreasing fresh-water throughput rates in measuring water permeabilities of consolidated sand cores might be partially explained by swelling of clays. A review of available literature bearing on the subject and related laboratory experiments are presented herein, offering an explanation for failure in use of soda ash and caustic soda waters and supporting the recent concept that every water used for input purposes in the secondary recovery of oil should possess such physical and chemical characteristics as to keep the clay content of the producing sands in a permanently flocculated condition. Produced brines meet this requirement. Their use is recommended as a means of increasing intake rates of tight sands and oil recoveries, as a solution to brine-disposal problems, and as a means of conserving a natural resource. Introduction There is a general belief among those engaged in the secondary recovery of oil by water-flooding that one of the most important requirements for the success of any such project is an adequate supply of good, fresh water. Fresh waters have the advantages of being more easily stabilized than salt waters and of being usable about the lease for all purposes. The use of brines for water-flooding never has been given much consideration in the Pennsylvania Grade area. The use of brines in Mid-Continent operations has been considered largely as a substitute for fresh waters, which were economically unobtainable for many operations. Estimated recoveries for some water-drive fields indicate that less of the original oil in place will be left upon abandonment than with the above-average practices used in Pennsylvania Grade water-flood operations. Lower residual oil saturations than 25 pct of the pore space following the water-flooding of Third Bradford sand cores in the laboratory are unusual. In comparison, water-flushed sands surrounding any virgin oil pool are found to be practically devoid of oil. Such lower natural residual oil saturations may be the result of a time factor much longer than economic under artificial water-flood operations, but neither the producer of primary oil nor the producer of oil by secondary recovery can obtain maximum recoveries unless full advantage is taken of all natural forces and

Jan 1, 1947

By Leonard D. Jaffe

In recent years, the advantages of tempered martensite as a microstructure for steel parts have been well established. For parts that must not fracture brittlely when loaded at high rates, at low temperatures, or under conditions of combined stress, tempered martensite is especially desirable. One of the factors that determine whether a steel part will have a martensitic structure after heat treatment is the hardenability of the steel. Despite the large amount of recent research, there are still many unsettled basic questions concerning hardenability and its relation to chemical composition, and, indeed, considerable disagreement among investigators in the field. Much of the uncertainty that beclouds the existing knowledge of hardenability arises from the fact that hardenability is still a wholly empirical concept, and has not been quantitatively related to the more fundamental knowledge of isothermal decomposition of austenite. Hardenability is, essentiaily, a measure of the time required for small percentages of austenite to decompose, during continuous cooling, to pearlite, bainite, proeutectoid ferrite, or proeutec-toid carbide. In the practical heat-treat- ment of steel, also, the decomposition of austenite is usually not isothermal but rather during cooling, or, in general, is not at a single constant temperature. Thus, both hardenability and practical heat treatment involve anisothermal decomposition of austenite. In a previous publication1 the author and his collaborators outlined the principles that govern the relations between isothermal and anisothermal decomposition of austenite, and reviewed the experimental information available in 1945. To avoid repetition, familiarity with that article (Paper I) will be assumed, and attention given primarily to work carried out or published since 1945. The method generally employed was explained in Paper I: anisothermal transformation is studied through investigation of the effect of holding austenite at one temperature upon its subsequent decomposition at another temperature. Both temperatures are below the stability range of the austenite. This paper is confined to studies in which only a small amount of transformation occurred at the first temperature. This is the only case of importance in practical heat treatment when an essentially martensitic structure is sought. Materials and Procedure It was necessary to use different steels for the studies involving proeutectoid ferrite and for those involving proeutectoid carbide, beeause the two constituents have not been found to form in the same steel. Several steels were tried and rejected

Jan 1, 1949

By Margaret Dienes, Karl L. Fetters

IT is recognized that ingot structure is important in determining the quality of finished steel. Such elements of ingot structure as the size, shape and distribution of primary crystals; the size, shape and distribution of shrinkage cavities; the degree and kind of segregation (both macro and micro); the distribution of nonmetallic impurities and gas cavities are each the result of solidification phenomena. These structural features vary with variations in ingot practice: Their control requires a knowledge of their correlation with the variables of ingot practice. The structures of full-sized commercial steel ingots have been studied extensively by the Steel Ingots Committee of the Iron and Steel Institute.1 This work has contributed much to our knowledge of ingot structure and the factors that control it. These investigations of necessity have been limited in scope because of their costliness and the great amount of time required. Studies of the structure of small steel ingots have not been very satisfactory because of the rapid rate of freezing of the ingots. Their structures are thus difficult to resolve and to interpret. Medium sizes of steel ingots in the ranges of 150 to 500 lb. do offer opportunity for study, but their cost also becomes greater and their use less expeditious. Experimental models for the study of steel-ingot structure have been made of nonferrous metals. Gathmann2 used lead-tin alloys and reported that they were satisfactory for determination of the location of the major shrinkage cavities and the "planes of weakness" resulting from the pattern of crystallization. Certain features of mold design have been illustrated by these results. Bezdenezhnihk3 has used copper and aluminum ingots similarly and has shown the effect of mold-wall thickness on the depth of columnar grains. These studies of nonferrous models have been useful, but their results have been limited because the analogy with steel ingots obviously is not a close one. Model wax ingots have also been useful in pointing out important features of mold design. Gathmann4 watched the solidification of wax ingots, through a glass-walled mold, and has reported the effects of mold type on the location of the shrinkage cavities. Segregation was simulated by using a mixture of paraffin and stearine and adding a red dye that on freezing segregated preferentially to the stearine. Brearley5 also used wax models to determine .the effects of some of the principal features of mold design. Carlsson and Hultgren6 used stearic acid to show that the columnar crystals of ingots tend to slope upward progressively from the mold wall toward the center of the ingot. As with the nonferrous ingots, the wax ingots have

Jan 1, 1943

By J. A. Norden

MUCH has been written concerning the hoisting equipment of various mines -throughout the country, but most of the literature on the subject, if not all, describes equipment of extraordinary capacity and the small and medium-sized outfits have been neglected. The hoisting equipment here described is capable 'of handling about 1200 tons per day. It has not been worked, to capacity, but 600 to 700 tons, together with men and materials, have been handled in two shifts without any great effort. Only one shaft extends from the surface to the lowest levels of the mine; see Fig. 1. It is composed of three compartments, two of which are used for hoisting and the third for water, air, and electrical lines, and for sinking purposes. In 1909, this shaft was raised from the 1000-ft. (304-m.) level to the 700-ft. There a station was cut and an air hoist installed. At this time all mining operations were confined to the upper levels of the mine; that is; above the 700-ft. The. ore was-dropped to this level through chutes from the 300-, 400-, 500-, and 600-ft. levels and then lowered in cars on cages to the 1000-ft., which is the main haulage adit, the mill and railroad bins being about 3000 ft. from the shaft. Orebodies were, in due time, developed on the 1000-ft. level and below. Therefore, in 1913, the shaft was sunk to the 1150-ft. level and thereafter sinking was continued at regular intervals until the 1500-ft. level was reached. But, hoisting from the 1300-ft. level was a difficult, and slow process with the antiquated air hoist, so, in 1916, it was derided to raise the shaft to the surface and install a modern, electrically operated hoist. This was completed early in 1917 and the hoist was in operation in March of that year.

Jan 8, 1920

By F. F. Schmidt, H. R. Ogden, E. S. Bartlett

Continuing tantalum alloy development studies have been concerned with a more detailed investigation of promising binary, ternary, and more complex tantalum alloys containing Groups IV-A, V-A, VI -A. VII-A, and VII-A metal additions. A primary objective of these studies was to improve the elevated temperature strength of tantalum with minimum degradation of fabricability and low-temperature ductility by alloying. Several alloys were found to exhibit hot tensile strengths in the excess of 25, 15, and 10 ksi at 2700°, 3000°, and 3500°F, respectively, combined with excellent cryogenic toughness and ductility. Particularly outstanding in this respect are alloys in the system Ta-Mo-W. Ternary parameter curves describing hot-strength, low-temperature ductility, recrystallization temperature, weld ductility, and fabricability are presented for the Ta-Cb-V, Ta-Hf-W, Ta-Mo-Hf, Ta-Mo-V, Ta-Mo-W, and Ta-V-W systems. At present, only four metals qualify for large scale structural applications at temperatures above about 1800°F. These are tungsten, tantalum, molybdenum, and columbium. Research and development work on these refractory metals has progressed to the point where efforts are now primarily directed toward the improvement of high- and low-temperature mechanical properties through alloying. High melting point combined with excellent low-temperature ductility, fabricability, toughness, weldability, and high solubility and tolerance for both substitutional and interstitial solutes are important attributes of tantalum. Conversely, its high density and relative scarcity compared with other refractory metals are the major deterrents to the use of tantalum. Early studies in the Battelle alloy development program established base line data on the mechanical and metallurgical properties of high-purity tantalum.' These studies were extended to include a preliminary investigation of the effects of various alloying elements on the established base properties.2,3 Recent studies involved a more detailed investigation of promising binary alloys containing Cb, Hf, Mo, Os, Re, Ru, and W, and ternary Ta-Cb-V, Ta-Hf-W, Ta-Mo-Hf, Ta-Mo-V, Ta-Mo-W, and Ta-V-W alloys. Results of major importance obtained are given in this article. EXPERIMENTAL PROCEDURES Electron-beam-melted tantalum (Wah Chang) and high-purity alloying elements were consolidated as 150-g ingots by multiple nonconsumable arc melting under a partial atmosphere of helium. Homogeneity of the button ingots was checked radiographically. Alloy buttons measured about 1-1/2 to 1-3/4 in. in diam by about 0.35 and 0.50 in. thick. Nominal alloy compositions were checked on each alloy button by weighing after arc melting. In most instances, weight losses were within 3 pct of the total weight charged. Subsequent chemical analyses on a number of selected alloys showed interstitial contents to range as shown below: Range of Interstitial Content, ppm 0 C N H 25-75 50-100 10-50 1-5 Metallic alloying additions were found to agree well with nominal compositions based on weight change data. Fabrication directly from the cast button to sheet was conducted at low (75° to 900°F), intermediate (1800° to 2000°F), or high (3000°F) temperatures, depending upon alloy content and hardness. Evacuated stainless steel or molybdenum packs were used for fabrication at intermediate and high temperatures, respectively. The temperature required to complete recrystal-lization in one hour was determined by hardness measurements and metallographic observations (longitudinal test sections) after vacuum annealing at 180°F intervals in the range 2010° to 2910°F. All mechanical property evaluations were conducted on recrystallized sheet, nominally 0.04 in. thick. Weldability of the various alloys was screened using manual TIG welding techniques. Bend ductility (bend axis perpendicular to weld axis) was the criterion used for evaluation. Tensile specimens employed 0.200 by 1 in. gage lengths, and bend test specimens measured about 1 by 1/4 in. Low-temperature tensile tests were conducted using a crosshead speed of 0.02 in. per min up to the point of yielding, and 0.05 in. per min to fracture. High-temperature tensile tests were conducted in vacuum using a crosshead speed of 0.01 in. per min

Jan 1, 1963

By Arthur Knapp

No oil territory in the world has been so rich in large producing wells, in a comparatively small area, as the Baku field. Particularly is this true of the Bibi Eibat field, which formerly produced millions of "poods," of " gusher," or as it is called in Russia, " fountain " oil. The Bibi Eibat and Balachany fields have been exhausted of gas and ruined by water, but the Surachany and Benegadi fields are still fountain territories and many outlying districts that have only been prospected produce rich fountains. The method of controlling fountains, or gushers, is the result of growth, along with the Russian system of drilling, where large diameters and riveted casing have been in vogue. The screw casing is seldom used except to exclude water. Formerly the method of finishing wells and the condition of the casing at the top of the well would not permit the use of gates, manifolds, and connections as is standard elsewhere. The life of the flowing wells is very short, particularly those 10 in. (25 cm.) or more in diameter, which produce large quantities of sand and often flow for but a few days and are then a complete loss. More than 1,000,000 poods in 24 hr. have been claimed in several instances, but in no case was the flow for more than a few days. The oil sands of this district are free uncemented sands and vary in thickness from paper thin to a maximum of 10 ft. (3 m.). The sands are interlaid with strata of soft clay. In spite of this, the practice has been to drill into such sands and produce from the open hole without screen or liners. Sometimes the casing is set below the oil sand but in this case holes from 2 ½ to 3 in. in diameter are drilled opposite the oil sand, which would not have the effect of a screen.

Jan 1, 1920

By B. Ancker, E. R. Parker

The small-angle dislocation-boundary density of nickel and some of its alloys was investigated as a function of strength. It was found that the strength is a linear function of the density for pure nickel and for Ni-Ti alloys, but not for Ni-Co alloys. The results are interpreted in terms of dislocation theory. THE processes by which metals deform are still poorly understood, even though there has been a concentrated research effort in this field during the past fifteen years. Single crystals and individual grains in polycrystalline aggregates often develop a subgrain structure when deformed. Substructure formation occurs as a result of local plastic bending and its development is augmented by annealing at moderate temperatures.' Investigations made to date, largely qualitative in nature, have shown that the substructure is composed of a network of small-angle boundaries. The purpose of the present paper is to present some quantitative data on substructure (obtained by X-ray techniques) and to correlate the results with the strength of the metal in which the substructure existed. Nickel and some of its alloys were used for the experiments. The presence of certain kinds of foreign atoms greatly alters the formation and effect of the substructure. Polycrystalline tensile specimens were prepared from high purity nickel, two Ni-Ti alloys, and two Ni-Co alloys; the composition of these materials is given in Table I. Tensile specimens having a reduced section 1/4 in. diam by 3 in. long were machined from materials which were refined, cast, forged, and swaged in the authors' laboratories. The specimens were annealed for 1/2 hr at 1150°C, a treatment which produced grains having a diameter of approximately 0.5 mm. This rather large grain size was used to facilitate later examination of the substructure. Duplicate specimens of pure nickel and of each alloy were strained various controlled amounts in tension at room temperature and recovered for 1 hr at 800°C. (This strain induced prior to recovery will be referred to hereafter as the "prestrain.") One of each of the recovered specimens was pulled in tension at room temperature to obtain the stress-strain curves. The other bar was cross-sectioned in the gage length, carefully polished, and deeply etched to remove all cold-worked material. This specimen was then examined by the X-ray microscopic technique2 to determine the nature and magnitude of the substructure. The use of duplicate specimens permitted a direct correlation between tensile properties and substructure characteristics. X-ray microscopic studies were made with an apparatus constructed to have an average resolving power of about 4 microns. The monochromatic radiation reflected from grains which were oriented favorably was recorded on fine-grain photographic plates. These were examined at Xl00 which represents the true magnification, since there was essentially none in the X-ray system. This permitted detection of angular differences between subgrains of as little as 10 min. A very large number (over 100) of grains for each specimen was examined at this magnification and the number of substructure boundaries per grain was tabulated. An accurate relative measure was obtained under fixed experimental conditions, e.g., same grain size, resolving power, magnification, etc. The greatest source of error lay in counting the subboundaries, but this proved to be surprisingly small when repeated counts were made by different investigators. Furthermore, as the subsequent analysis indicates, whatever human error was introduced was not significant. Analysis of the Substructure Data When the number of substructure boundaries per grain was plotted against the frequency, skew (asymmetrical) distribution curves of the type shown in Fig. 1 were obtained. These are smoothed curves for the 1 atomic pct Ti in nickel alloy subjected to various prestrains and are representative of the curves obtained with all the metals. Since skew-distribution curves cannot be analyzed by elementary statistical methods, detailed investigations were undertaken in order to 1—test the consistency

Jan 1, 1955

By Roswell H. Johnson

What becomes of the water which must have filled the oil and gas sands at the time of deposition, has long puzzled students of oil and gas and has found expression in Munn's well-known article on the hydraulic theory. Both Munn and Clapp have pointed out that in the Appalachian field the deeper sands carry increasingly less proportionate amounts of water. It seems to me probable that the principal source of oil and gas has been in the shales in proximity to the sands which now contain these products. The sand spits which mark off the lagoons from the sea comply particularly with the requirements of a limited sand imbedded in shales rich in organic matter. Cunningham Craig has objected to this view that the rich organic muds of lagoons are found only at the surface. That such muds do extend to considerable depth 1 am assured by Prof. Douglas W. Johnson, who has made an extensive study of the Atlantic Coast marshes. As any particular sand body becomes weighted by a heavier and heavier overburden, the result of increasing deposition, a part of the very large percentage of water in the uncompacted sand and mud is forced out. The water percentage of freshly settled mud is vastly higher than that of the resultant shales, or even of a very porous sand. If beds of less compressible material meet or underlie the shales in question, there will frequently be a lateral motion along such beds to some point where the upward movement will be resumed. We find in our laboratory work here that oil, gas, and water have extremely slight capacity for gravitational sorting while in a state of rest, but when moving the gravitational sorting is readily accomplished. As the oil, gas, and water pass a body of larger pores, the gas, owing to its lack of capillary attraction, is retained in the large pores. This has been predicted by Washburne, Blatehley and others on the ground that the water has a higher capillarity and grips the finer pores in such a way that there will be a greater proportion of oil and gas in the large

Jan 1, 1915

By W. R. Hibbard

The increased strength of a polycrystal-line metallic aggregate compared with that of its individual crystals generally has been associated with complex stress distributions at the grain boundaries resulting from atomic irregularity between grains. This disregistry, together with the necessity for adjacent crystals to deform compatibly regardless of the single crystal crystallo-graphic strain mechanism, complicates this mechanism so as to increase the metal's resistance to deformation. Although Taylor1 has shown from purely mechanical considerations the requirement for at least five active slip systems to absorb the complexities during the homogeneous deformation of polycrystalline face-centered cubic metals, experimental studies by Barrett and Levenson2 indicate that this is feasible only in a qualitative sense because of deviations from homogeneous deformation. Seitz and Read in their review3 state: " Unfortunately . . . present knowledge of the grain boundary influence is not sufficient to complement the work in single crystals and provide us with a good foundation for treating polycrystals." The purpose of this investigation was to attempt to clarify the gap between single crystals and crystalline aggregates by an analysis of the effects of dcformational stresses. Some of the results were described by C. H. Mathewson in his 1943 Campbell Memorial Lecture.zl Previous Investigations Since the performance of single crystals deformed under pure stresses has been relatively thoroughly investigated, the most significant researches are concerned primarily with deviations from single crystal behavior of large grained specimens. Qualitative grain boundary effects involving the observed amount of slip werc reported by Carpenter and Elam5 in 1921. Individual crystals in a two or three grained aluminum specimen deformed by tension acted in the normal manner described by Taylor and Elarn4 except for marked modifications at the grain boundaries. There the power to withstand deformation was considerably increased, leaving a ridge on the specimen where decreased slip occurred, often noticeable yi in. from the boundary. Adcock,6 Yamaguchi,' Seumel, Hirstg and others have also reported this phenomenon as a qualitative trend. Yet attempts by O'Neill'o and Ljunggrenll to measure a difference in hardness at grain boundaries in undeformed specimens were unsuccessful. Miller12 measured quantitatively the reduction in slip near the boundary between the single crystal and polycrystalline areas of zinc specimens. These effects consisted of two parts: I. Next to the polycrystalline interface thc distribution of stresses was so altered

Jan 1, 1949

By Willis Burns

I. INTRODUCTION. These notes are submitted, not as a discussion of the modern practice of electrolytic-copper refining, but as the record of a refinery that was among the pioneers in the field and that is to-day, and has been for 17 years, operating under conditions not to be found in any similar plant in the country. I refer to the current density, which is at least 60 per cent. higher than that regularly employed elsewhere, and to the fact that the anodes treated are the direct product of the converter rather than of the reverberatory furnace. The writer has no knowledge of any other refinery treating anodes of this character.

Jan 8, 1913

By John Chipman

Published data on the equilibria of carbon in binary Fe-C austenite with H2-CH4 and CO2-CO gas mixtures are used to obtain the constants of an equation repre -senting the activity coefficient of carbon throughout the stable austenite range of temperatutre mid compositiotl. Calculated values for the solubility of graphite are found to be in agreement with the best-published direct observations. Its heat of solution is 10,680 calper g-atom. The free energy of formation of cementite is culculated from the equilibrium compositions of austenite and of gas. Its entropy and heat of formation are also obtained. BASIC knowledge of the high-temperature properties and treatment of steels is contained in the Fe-C diagram and its extensions for the effects of alloying elements. The application of thermodynamics to the Fe-C system, with addition of alloying elements, can serve to simplify and systematize this knowledge. The points of beginning are the binary fee solution, austenite, concerning which our information is reasonably complete, and the binary carbide, cementite. Further studies must include the other phases of the binary system, a and liquid, and for these an accurate knowledge of the ? phase boundaries is essential. These studies should provide a firm base for systematic study of the effects of alloying elements on all phases of the system, their transformations, and precipitation phenomena. With the aid of the simplifying thermodynamic concepts of activity coefficients and interaction parameters it is to be hoped that the results of these studies will be amenable to computer solution thus making the information on multicomponent systems more readily available than would be possible in multidimensional diagrams. Studies of the thermodynamic properties of austenite have utilized equilibrium measurements on the reactions:

Jan 1, 1968

By Allen L. Hatch

A survey of all phases of the world's lead and zinc production in 1968 from ore through to refined metal was conducted by sending questionnaires to individual companies and the results of this survey are tabulated at the end of the paper. The paper goes on to review changes in the geographical distribution of the world's lead and zinc mine and metal production and in the trading patterns of raw materials, present and future utilization of metal production capacity, developments in metal smelting and refining processes and the growing importance of marketing, product development and research in the 1950's and 1960's.

Jan 1, 1970

By Lyall Zickrick

Experiments of previous investigations have indicated that calcium-copper alloy, when used as a deoxidizer for molten copper, results in a sound copper casting of good physical and electrical properties. Braden-berg and Wiensl have obtained successful results in casting sound copper using calcium for deoxidizing. Masing2 has obtained deoxidized copper of high density and high conductivity by use of calcium. Pratt,3 in 1907, patented the use of calcium for the deoxidation and degasification of copper. Schumacher, Ellis and Eckel,l in 1929, conducted a series of experiments on deoxidizing copper with calcium. They concluded that so long as there is only a small percentage of residual calcium the mechanical and electrical properties of the copper deoxidized are not impaired, and the deoxidation is thorough. For this investigation, a copper-calcium alloy high in calcium and 10 variously deoxidized copper ingots were prepared. The investigation concerns itself with the casting properties and structure of these variously deoxidized ingots, their working and annealing characteristics, and the resulting physical and electrical properties of the worked materials. Preparation of Special Copper-calcium Alloy and Experimental Ingots For use as a deoxidizing agent, an alloy of copper and calcium with fairly high calcium content was prepared, by melting pure electrolytic copper in a graphite crucible in an ordinary gas-fired pot furnace. The molten copper was kept well covered with calcium chloride slag. Small chunks of calcium were wrapped in thin copper sheet, placed on the end of a graphite rod and plunged down into the molten copper and thoroughly stirred. Upon completion of the calcium additions the crucible content was poured out into a cake about one inch thick. Analysis of this alloy gave 4.4 per cent calcium. The alloy was brittle and easily broken into small chunks. Some calcium was lost during the addition, owing to

Jan 1, 1933

By Carl J. Christensen

This paper presents the development of diamond coring of the Weber sand section in the Rangely Field, Colorado. The description and operation of the diamond-coring equipment is included as well as the economics and results obtained by its use. Diamond coring is compared with the other methods used for drilling the Weber sand. Two types of diamond coring are discussed. The first and the one used most extensively is the regular 6 ?x 3¾-in. diamond bit and bottom hole 50-ft barrel. The second type, which has also been used successfully by Stanolind, consists of a 4 13/16 x 2 11/32-in. cutting bit and reverse circulation coring equipment. The first type will be referred to as regular or conventional diamond coring while the latter type will be referred to as reverse circulation diamond coring. Introduction Diamond coring has been used for many years in mines, quarries, surface coring at dam sites, laboratory work, and so on, but, until recently, had never been used very extensively in coring oil sands and other oil-bearing strata. It was demonstrated early in its development that hard forma-tions could be cut rapidly and that core recoveries far exceeded those obtained with conventional hard rock bits and quite often 100 pet recovery was obtained. However, the poorly constructed diamond-coring equipment and resulting high costs of early diamond coring slowed down its progress. Early in the development Of the Rangely Weber field, Rio Blanco County, Colorado, the Rangely Engineering Committee selected key wells that were to core the Weber section in its entirety. These cores were to be analyzed and various sections tested to gather sufficient information so that accurate reservoir studies could be made. The number of wells selected were kept at a minimum inasmuch as the productive Weber section, which is found at an approximate depth of 6000 ft, is thick, being as much as 600 to 700 ft on top of the structure. The Weber section is also comparatively hard to drill. For instance, one well took 60 days to core 490 ft of Weber sand with conventional coring equipment. It was noticed, however, that Core Labora-verse diamond plug cutter could quickly cut a plug from. one of these hard cores. This fact led to the serious consideration of diamond coring the Weber sand. The first diamond coring at Randy was performed by Stanolind in August 1946 andl although we experienced some difficulties, the results definitely indicated that diamond coring would be successful at Rangely for .coring the Weber sand. As more wells were cored and the equipment improved somewhat, diamond coring became less expensive than drilling the Weber sand with the conventional rock bit. In less than one Year diamond coring has definitely Proved its usefulness in oil-field drilling operations in the Rocky Mountain area where formations quite often drill very hard. The practice of spot coring in hard oil-bearing formations with conventional coring equipment is giving way diaimond coring of the entire sections, thus givng an operator the complete picture.

Jan 1, 1948

By D. G. Westlake

Alloys of poly crystalline Nb-H have been tensile tested at 77" and 120°K after slow-cooling and after quenching from room temperature. A rationale has been developed to explain the effect of cooling rate on ductility in terms of microstructure. The inferior ductility of the slow-cooled alloys in this temperature range can be attributed to the precipitation of coarse hydride particles that fracture in the early stages of plastic deformation. Quenching Produced much smaller hydride particles and a decreased tendency for initia-tion and popagation of cracks. Prismatic dislocation loops, punched into the matrix of quenched alloys, eliminate the yield point and may Play some role in the low temperature ductility of the quenched alloys. The difference in ductility between quenched and slow-cooled V-H alloys was even greater than that observed in the N b-H alloys. It is well known that the ductility of Nb-H and V-H alloys decreases with increasing hydrogen concentra-tion and with decreasing temperature.1-l1 The follow-ing are some of the numerous mechanisms that have been adopted in attempts to explain these observations: 1) hydrogen-dislocation interarction,4'6 2) lowering of the crack surface energy by adsorbed hydrogen,9'10 3) localized lowering of the niobium bond strength,9 and 4) exertion of pressure inside voids by molecular hydrogen.6 A recent study1' indicates that, in some way, the embrittlement is related to the precipitation of a hydrogen-rich phase, because embrittlement and hydrogen solubility have the same temperature dependence. Most of the investigators observed that at very low temperatures there was a return of the ductility. Thus, hydrogenated niobium and vanadium may be said to exhibit a low temperature ductility minimum."1'8'9 It has been reasoned by most observers that diffusion is required for the embrittlement mechanism to be operative, and that as hydrogen becomes immobile at very low temperatures, the ductility increases. This investigation of the mechanical behavior of Nb-H al-loys under various conditions is an attempt to gain a better understanding of the low temperature ductility minimum. EXPERIMENTAL Tensile specimens, with gage length dimensions 20 by 3 mm, were machined from sheet stock" and both faces were ground on wet 600 grit Sic paper to obtain a final thickness of 0.5 mm. Annealing as described earlier12 resulted in average grain diameters of 0.3 mm. The recrystallized niobium tensile specimens were electropolished in 90 parts H2S04, 10 parts HF (48.9 pct) by volume, at 287°K and 30 v. Hydrogen, which may have been present in the starting material and/or added during specimen preparation, was removed by annealing at 1073°K in a dynamic vacuum of 2 X 10-6 torr. Hydrogenated specimens (1.15 at. pct H) were prepared by reaction with a known quantity of pure hydrogen (obtained by thermal decomposition of UH3) at 1073oK, followed by cooling at the rate of 100" per hr. These were vacuum encapsulated, homogenized at 573°K for 3 to 5 hr, and furnace-cooled. Tensile tests were conducted on an Instron machine at a strain rate of 4 x l0-5 per sec. The gripping device was such that the specimen was positioned below the crosshead. Thus, subambient test temperatures could be obtained by immersion of the device in a cooling bath of either liquid nitrogen or Freon-12. The temperature of the Freon-12 was controlled within ± 0.1°K of the desired temperature by automatically monitoring the flow of liquid nitrogen through a copper coil in the bath. Slow-cooling to 77°K was accomplished as follows. The testing device was surrounded by a rubber jacket, open at the top and with small holes in the bottom. Liquid nitrogen, brought up to the bottom of the jacket, entered the holes and vaporized quickly. The temperature was monitored at the specimen with a copper-constantan thermocouple, and a constant cooling rate of 2 deg per min was easily achieved by controlling the level of the liquid nitrogen outside the jacket. RESULTS AND DISCUSSION Low Temperature Ductility Minimum. Resistometric studies of both Nb-H12 and V-H13 indicated that at tem-peratures less than 150°K, virtually all of the hydrogen

Jan 1, 1970

By L. S. Darken, H. A. Wriedt

An investigation has been made of nitrogen absorption by the lattice defects in a low-carbon steel afte~ Plastic deformation. Specimens in which defects were distributed by various combinations of cold rolling and vacuum heat treatment were equilibrated with controlled ammonia + hydrogen mixtures at 300° to 450°C to study the relation between the solubility and the thermodynamic activity of nitrogen. The results are interpreted in terms of nitrogen being absorbed upon two different types of defect sites, called A sites and B sites. The concentrations of these sites are calculated for specimens with various histories of straining and annealing; and the thermodynamic relations descrihing the equilibrium distribution of nitrogen among the A, B, and ordinary interstitial sites in ferrite are evaluated as follows: THE generalization that the solute atoms in a solid solution interact with imperfections in the solvent lattice is now universally recognized and the subject of an extensive literature. All types of imperfections—point, line, or surface—exhibit these interactions, but the relative importance of each type depends upon its concentration, the strength of its interaction with the particular solute atom, and whether the interaction is attractive or repulsive. The strength and sign of the interaction vary with the vectorial displacement of the solute atom from the imperfection in the crystal. The concentration of lattice defects increases during plastic deformation and the effect of the imperfections upon the solute atoms is usually perceived only after cold work or irradiation. Two experimental methods have previously been used to observe the effects of interaction between nitrogen atoms and lattice imperfections in a iron. Internal friction, which was first used for this purpose by Dijkstra,1 has been applied more often than the electrical-resistivity method of Cottrell and Churchman.2 The method of the present investigation has not been used before.* Uniform specimens of steel with a metastable defect structure are produced by cold rolling and subsequent heat treatment below the recrystallization temperature. Variations in the defect structure are obtained by varying the amount of strain and the heat-treatment conditions. The specimens are then saturated with nitrogen at moderately elevated temperatures in ammonia + hydrogen mixtures having various thermodynamic activities of nitrogen below saturation with Fe4N. From the nitrogen contents of analyzed samples, the metastable equilibria of interactions between the defects and nitrogen can be established and the concentration of sites for nitrogen atoms in the lattice defects calculated. A steel was used in the present experiments instead of purified iron or iron alloys because the amount of nitrogen absorbed at defects is larger in the steel over a much wider range of experimental conditions and could therefore be measured more accurately. The effect of alloy composition is discussed in Part II of this paper; it is sufficient to say here that impurities and phase heterogeneity in ferritic alloys favor the generation and/or retention of larger defect concentrations during plastic deformation and annealing at 300° to 500°C. MATERIALS AND EXPERIMENTAL PROCEDURE The experimental specimens were prepared from stock of a low-carbon steel, which will be called "X steel" here, with the composition: C, 0.12 pct; Mn, 0.43 pct; P, 0.010 pct; S, 0.034 pct; Si, 0.007 pct; As, 0.086 pct; Cu, 0.022 pct; Ni, 0.009 pct; Cr, 0.003 pct. The stock was all from a single ingot made by the basic open-hearth process, which was hot-rolled to strip 0.080 in. thick.. This hot-rolled strip, given the code designation "XH", was the starting material for preparing a series of cold-rolled sheets. The latter are designated "XC27",

Jan 1, 1965

By A. U. Seybolt, R. A. Oriani

The pressure and composition of the solid solution of nitrogen in chromium has been investigated as a function of temperature. The partial molal heat of solution, the activity of nitrogen in solid solution, and the partial molal free energy have been computed. The enthalpy of three reactions is summarized: N + 2Cr(3) = Cr2N(4), H° = —28,500 cal per mol 1/2N2(p) + 2Cr(8) = Cr2N(3)1 ?HO = —23,500 cal per mol 1/2N2(p) = N, ?H° = 5,000 cal per mol. WORKERS who have investigated the problem of the preparation of ductile chromium have been concerned with the effects of minor amounts of impurities upon this refractory metal. In particular, gaseous impurities such as oxygen and nitrogen have been suspected of causing trouble because of many known cases where brittleness in transition elements has been definitely traced to these elements. In order to evaluate the possible effects of the nitrogen impurity in chromium, it appeared desirable to learn something of the dependence of the nitrogen solubility upon temperature and pressure. Previous Work Maier3 in 1942 in his treatise on sponge chromium reviewed the thermodynamics of the chromium nitrides Cr2N and CrN, both of which are well-estab- lished compounds, but which apparently have not been studied in much detail. Maier presented some free energy-temperature expressions for the reactions 2 Cr,N = 4 Cr + N2 [1] and 4 CrN = 2Cr2N + N2 PI based mainly on the work of Satoh2 and Sano." Pearson and Ende3 in 1953 briefly reviewed the thermodynamics of Cr-N using the same data available to Maier, and also derived a free energy-temperature expression for reaction 1. Of the two nitrides mentioned previously, the present investigation was only concerned with Cr,N, since this nitride is in equilibrium with the metal phase, at least over most of the temperature range, Blix4 in 1929 established the structure of Cr2N (close-packed-hexagonal) by X-ray diffraction methods, and indicated that its homogeneity limits extend from 11.2 pet to 15.1 wt pet N. At a temperature of 1200°C, 38 mm Hg from the Maier expression and 43 mm Hg from the Pearson

Jan 1, 1957

By D. W. Mitchell

INE operators have a choice of several classi- fications of mechanical loaders. Within each classification there are many types and makes available. Table I lists loaders on which manufacturing data as to operating characteristics are available. This paper discusses the conditions met in a mine as they affect these characteristics. It is assumed that management will provide satisfactory engineering, supervision, power, maintenance, loader service within a concentration of workings, and a balanced working cycle served by balanced production equipment. These are factors which affect the optimum operational efficiency of a loader. The conditions which determine loader choice are: Height of Vein—The main limitation to the use of a loading machine is the height to which the vein is mined; i.e. a loader cannot be higher than the place in which it is to work unless rock is taken. Since there are several low vein loaders being developed and successfully applied, this does not appear to be a requisite of an efficient mining operation. The maximum useable height of a loader should be equal to the working seam thickness less a working clearance for travel and operation. A—Working seam thickness = B—Artificial roof support thickness = C—Safe headroom below support = (generally about 6 in.) D—Height of roadway = E—Total of B + C f D =_______________________ A—E = maximum loader height F—Distance from top of roadway to bottom of roof support = G—-Height of loader's coal or ore line (see Table I) = H—Difference between F and G = Size of largest broken particle + a safety factor of 2 to 3 in. H is a loadability factor and is important because the clearance over the top of the conveyor chain to the roof or roof support must be greater than the largest broken particle or else the particle and/or the conveyor chain may be broken. From this standpoint it might be desirable to use a lower height machine even though it may have a smaller capacity, though this is warranted only when increased lump realization offsets lower man-day and machine pro- duction rates. Ivan Given has stated, "Loading should not be handicapped by securing lump only to grind it in the breaker." Width of Working Place—The width of a working place is the greatest width a place may be safely driven. The working place includes not only the face but the roads the loader must tram when mucking out more than one face. The width is limited by the system of placing props with sufficient room between them for the machine runner (about 2 ft). Maximum width of place in which the loader will operate at maximum efficiency is determined by the type of mounting. With track-mounted loaders, maximum width of place is determined by maximum angular swing of the loading head and proximity of track to the face. The use of double track leads to added expense and operational complexities. Several mines that have used double-track systems have found that a substantial saving is made by the use of machines that load out wider places. Trackless loaders may work in rooms of any maximum width. Minimum width of place in which a loader will operate is determined by width of the loader plus a safe movement area for the operator. Often a barodynamic study of the mine will show that either an increase in room width and/or a change in the system of propping may be made by using roof bolting, full or part-width room timbers, removable aluminum I-beams at the face, etc. Increasing the width of a working place will, in general, increase loader operating efficiency by providing more material per fall and by decreasing the preparation and moving time per ton. A change in the system of propping that would increase the minimum width might permit the use of a higher capacity loader with safer working conditions. Proper face tirnbering is necessary to insure safety from roof falls and because the speed of preparation and loading generally increases since the men work with greater assurance and there is less chance of kicking out posts. Maximum Room Length—With the exception of the scraper and the duckbill, the limit to room

Jan 1, 1952

By William H. Grady

FactoRs entering into the market value of coal are its grade, and the cost of labor, material, and capital. Reduction in these costs cannot be expected in the future, and it therefore follows that greater economy in their use must be accomplished if it is desired to hold the present markets; more tons of product per unit must be obtained in a given time from both men and material, and means devised for increasing the percentage of lump and domestic sizes. This paper is presented for the purpose of inviting discussion and stimulating thought in regard to the influence of methods of procedure and plans of mining, upon the quality of coal, the economical use of labor, material, and capital, and the cost of production. Even the better methods of the present day leave much to be desired, and a review of the reasons and necessities for their use may be of value in pointing the way to more economical mining. The writer does not attempt to discuss untried methods of mining, but rather to state clearly and concisely a summary of the results obtained under the several methods of procedure that have been adopted. In some instances a high degree of concentration has been effected, and comparisons of the results obtained with the results of lesser degrees of concentration form an interesting study. It is believed that much may be accomplished in improving the quality, and in the more economical use of labor, material, and capital, by concentration, and it is to concentration in particular that your study is invited. The writer, who has occasion to visit many mines, most of which are under different management, has been inclined to the opinion that improvement has been retarded in many ways and that mining has not as yet been entirely freed from the early-day practices which were forced upon it. Practices resulting in lack of concentration, to which reference will be made, are: The absence of robbing, necessitating the frequent interposition of barrier pillars; lack of system and of proper supervision, resulting in losses of life and coal. These practices could not well be

Jan 1, 1915

By G. J. Heuer, J. N. Dew, G. C. Clark

The effect on well behavior of partial permeability barriers, changes in producing rates and well spacings have been calculated through use of a radial, unsteady-state, two-phase-flow mathematical model. This model allows for variations in permeabilities and porosities with distance from the wellbore. The numerical methods necessary to solve the problem require use of a highspeed digital computer, in this case an IBM 704. In each instance, pressure and saturation gradients, gas-oil ratios and recoveries around a well producing by solution-gas drive have been calculated as a function of time and distance from the wellbore. Comparisons are made to show the effect of changes in producing rate and of varying permeability near the wellbore and out in the formation on the production and pressure history of the well. The effect of different well spacings on producing rate and ultimate recovery is considered. Although the mathematical description of the reservoir is simplified in comparison to an actual reservoir, the results do give some insight into the difficult problem of spacing and proration in a heterogeneous solution-gas-drive reservoir. Results show that for the cases considered spacing has little effect on ultimate recovery and that permeability barriers removed from the well decrease producing rate for a period of time but have only a small effect on ultimate production. INTRODUCTION The effect of spacing and producing rate on the production characteristics and ultimate recovery of a well producing by the solution-gas-drive mechanism have been topics of interest to the oil industry for many years and the subject of many hearings before state regulatory bodies. The problem is very complicated because of the difficulty of simulating in the laboratory a reservoir producing by the solution-gas-drive mechanism under anything like normal field conditions. This paper gives the initial results of a study aimed at determining the effect of these factors on production from reservoirs simulated by a mathematical model. Two-phase, unsteady-state equations are used to calculate pressures, saturations, and rates of oil and gas flow as a function of time and distance from the wellbore. The model is radial, and reservoir properties may be varied with distance from the wellbore. A decrease in permeability at a given distance results in a low-permeability ring concentric with the wellbore through which all the fluids from more distant portions of the reservoir must flow. The current mathematical model allows for variation of permeability, porosity and saturations as a function of distance from the well. Any desired drainage radius for the well may be selected. Drainage radii of 745 and 1,053 ft, which correspond to 40- and 80-acre spacing, were chosen for the calculations which follow. A large amount of the input data has been held constant. No investigation was made into the effect of changes in fluid properties and relative permeability characteristics on oil and gas production behavior. Fluid properties and relative permeabilities are essentially those of the White Mesa portion of the Greater Aneth area in southeastern Utah. A recently concluded hearing before the Utah Oil and Gas Conservation Commission to determine spacing for the field aroused interest in the possible effect of permeability constrictions located some distance from the well on production and recovery. This interest stimulated the present study. In this paper, no attempt has been made to simulate any field production characteristics exactly. Only the solution-gas-drive mechanism has been investigated, and production by liquid expansion has not been considered. This investigation is exploratory in nature but does give some insight into the problems of spacing and proration in a solution-gas-drive field having permeability variations. THE MATHEMATICAL MODEL The mathematical model is similar to that proposed by West, Garvin and Sheldon.' Approximately the same techniques have been used in arriving at a solution. The equations are nonlinear, partial differential equations which have been known for some time. The particular equations used for this study neglect the effects of capillary pressure and gravitational forces. The advent of modern digital computing equipment has made their solution practical. Basically, the method solves for pressure, saturations, and oil and gas flow rates as a function of distance and time. In our model, distance to the