By Kenneth K. Humphreys, J. W. Leonard, T. S. Spicer

INTRODUCTION Reasons for Thermal Drying The continuing increase in the percentage of - '/4 in. ( -6.3 mm) coal produced as a result of the increased use of mechanical mining methods has, over the years, tended to shift considerable portions of the work of producing salable coal to the fine coal cleaning section of the preparation

Jan 1, 1979

By Otto H. Henry

The purpose of this investigation was to determine the equilibrium diagram of the lithium-magnesium pair as a first step in studying the possible usefulness of these alloys as ultra-light structural materials. Review of the Literature The behavior of lithium towards magnesium was first investigated by Masing and Tammann.(1)† In order to prevent oxidation the alloys were made in iron tubes under an atmosphere of hydrogen; temperatures were measured with a glass-protected thermocouple. These investigators found that lithium and magnesium form two series of solid solutions separated by a miscibility gap between 85 and 95 per cent magnesium; that the alloys with 81 and 95 per cent magnesium showed a homogeneous structure under microscopic examination, while the alloy with 89 per cent magnesium contained two distinguishable crystallites; that the curve indicating the beginning of crystallization rises from the melting point of lithium to that of magnesium; and that no compounds of lithium and magnesium are formed. The equilibrium diagram was not plotted because no definite data were obtained for determining the solidus and the position of the miscibility gap in the solid state. The difficulties encountered in this investigation were: (1) that it was necessary to heat them as high as the melting point of magnesium in order to obtain homogeneous melts; at such temperatures the alloys attacked the glass protecting the thermocouple; and (2) that at temperatures above 400" C. the lithium united with the hydrogen to form lithium hydride, thus contaminating the alloys. By applying the same methods as those used in the lithium-magnesium system, Masing and Tammann determined the equilibrium diagram of the

Jan 1, 1934

By Edward Wichers

THE purpose of this paper is to set forth the matters of principal interest in connection with work done in the past few years on the purification of the metals of the platinum group, including the study and modification of methods already in the literature and the development of new procedures. For the most part, the results will be given in summary form, reserving the publication of detailed data and directions for a forthcoming paper to be issued by the Bureau of Standards. In recent years increasing interest has been shown in the preparation of the pure platinum metals, both by those concerned with the manufacture of the metals and their alloys for scientific and industrial purposes and those who are engaged in the study of the chemical or physical properties of the elements. The purification of the metals usually has been regarded as a matter so involved and difficult as to require the attention of specialists. It is hoped that this paper will show that any of the metals can be prepared in any desired degree of purity by relatively simple straightforward chemical methods. For the most part, it is thought that the methods given are suitable for small-scale refineries as well as for the laboratory; also, that they will bring the time required for the purification of any of the metals within reasonable limits. The new procedure suggested for purifying platinum should prove to be much shorter than any methods described in the literature.

Jan 1, 1928

By G. Carman Ridland

In conjunction with a geological investigation of the silver-bearing veins at Contact Lake, Northwest Territories, Canada, a survey was made with a Geiger-Miiller counter of the gamma-ray emissions from the rocks in the vicinity of the mine workings. Discontinuous pitchblende veins have been encountered occasionally in the silver-bearing fissures, and the geophysical survey was undertaken with the hope that abnormally high gamma-ray intensities, if detected, might lead to larger and more continuous pitchblende discoveries. Before the instrument was used at Contact Lake, preliminary tests were made, first with laboratory specimens at Princeton University, and later over known pitchblende deposits at the Eldorado property, LaBine Point, N.W.T. The Geiger-Müller counter, as adapted for field use, is described; the technique of transporting and operating the instrument is outlined; and the general precautions to be observed are discussed. The results obtained at Great Bear Lake show that the instrument is capable of detecting not only a pitchblende ore shoot in a shear zone, but also the mildly radioactive "host rock" at a considerable distance from the ore body. Hence, use of the Geiger-Müller counter is urged, not just for the detailed search for an ore body in a shear zone, but for the detection of possible radioactive "host rocks" in large-scale reconnaissance surveys of unexplored regions made by prospectors and members of federal geological survey parties. Location.—Along the rocky eastern shores of Great Bear Lake, in the Northwest Territories of Canada, lies one of the world's great radium-producing areas. The Eldorado mine, owned and operated by the Eldorado Gold Mines, Ltd., is at LaBine Point; while the Contact Lake mine, operated by Bear Exploration and Radium, Ltd. (B.E.A.R.), lies 9 miles to the southeast of LaBine Point and 2 miles south of Echo Bay, an indentation in the eastern shore line of Great Bear Lake. Geology.—The Eldorado company obtains its radium by the mining of the mineral pitchblende, which is found associated with a complex variety of metallic and nonmetallic minerals1 in quartz-carbonate veins occurring in metamorphosed pre-Cambrian sediment aries. Most of the pitchblende is intimately associated with a brown quartz and belongs to an early hydrothermal stage of mineralization during which safflorite-rammelsbergite and minor cobalt-nickel minerals were also deposited. Some pitchblende occurs with a group of minerals belonging to a later stage of mineralization in which the gangue is mainly dolomite and sometimes ferruginous rhodochrosite. Associated with this group are native silver and lead-zinc-copper sulphide minerals. The Contact Lake property owes its existence to the mining of rich, native silver ore shoots, which are

Jan 1, 1946

By A. T. Beckwith

THE Lehigh Navigation Coal Company Inc. operates steep-pitch, relatively deep mines in the Panther Creek Valley, at the eastern end of the southern anthracite coal field. Commercially minable coal beds are the Mammoth,† Primrose, Orchard, and Buck Mountain,‡ their respective thicknesses average 50, 15, 1o and 12 ft. Sand slates immediately overlie and underlie these beds, though in some locations sandstone or conglomerate beds occur. Underground operations extend to a depth of 1200 ft. below the surface, and comprise a bulk of virgin work on the lower levels, and a small amount of remining on the upper levels. With increase in depth, ventilation has become a more important factor. DEVELOPMENT In early days slopes or drifts were driven in the outcropping coal on the hillsides. Subsequent development was by water-level tunnels, with portals above high water in Panther Creek. These tunnels have been maintained because they intercept and drain much water that enters the mined-out portion of the bed and otherwise would follow down to the deep workings. Below these tunnels, the coal was customarily developed by slopes. Muleways, which are zigzag chutes easy to travel, were also driven to connect lower openings with the water levels. When it became necessary to go still deeper, the slopes were abandoned, and vertical multicompartment shafts were sunk from the surface. Levels have been at vertical intervals of from 195 to 250 ft. Recent practice has been toward the latter spacing; splitting the total lift, however, by starting to mine from chutes extending halfway up to the level above. Chutes customarily are spaced at 50, 60 or 70-ft. centers along the gangways. At some mines, additional shafts have been sunk from the surface to the level containing the main pumping station, and these carry the discharge lines from the pumps. As the mines are ventilated by the exhausting system, both the hoisting and so-called water shafts serve as intakes. The main fan is always on the surface, and is connected with the return airways from the various levels by an air hole or a vertical shaft. For economy, when the present deepest levels were developed, main return-air shafts or air holes were not extended to the new level, but connections were made from the new level to that above by two or more holes. It is doubtful that this method will be continued, as complications in the system, increased resistance to flow, and other difficulties undoubtedly will counterbalance any economies this provision may afford.

Jan 1, 1942

By M. Cohen, S. A. Kulin

AT a recent symposium on thermodynamics in physical metallurgy1 two opposing theories of the austenite-martensite transformation were presented. Both theories agreed that this type of reaction involves a nucleation process which requires activation and that the activated nuclei develop into the well-known martensite plates with tremendous speed. However, there were essential differences in the two points of view concerning the nature of the nucleus and the mechanism by which the nucleus propagates. According to Cohen, Machlin, and Paranjpe,' the nucleus is a strain center with sufficient elastic energy to initiate a cooperative displacement among the atoms of the parent phase when a sufficiently low temperature is reached. This displacement propagates as a wave in shear-like fashion to transform the austenite into martensite without benefit of diffusion. On the other hand, Fisher, Hollomon, and Turnbull3 regard the nucleus as a solute-poor region (in the austenite) of a size which becomes supercritical relative to coherent growth into martensite when an appropriately low temperature is reached. This growth process is taken to be an atom-by- atom transfer from the receding austenite lattice to the advancing martensite lattice through the coherent interface that exists between the two phases. The present paper is not conceded with the divergent views as to the nature of the nucleus but describes some critical experiments which differentiate between the two proposed mechanisms of propagation. Fisher' has summarized the latter issue in the following way: According to the cooperative displacement theory, the speed of formation of mar-tensite plates should not be decreased by lowering the temperature, and martensite should form with extreme rapidity at very low temperatures; whereas with the alternate growth process, the speed of the martensite transformation should be retarded at very low temperatures, decreasing to zero at the absolute zero. The atom-by-atom growth mechanism predicts a marked slowing down of the reaction rate with decreasing temperature because the rate of self-diffusion in the austenite is involved in this picture. For example, Fisher, Hollomon and Turn-bull5 estimate that the activation energy for this growth process in steel is (0.34)2(0.36)* times the activation energy for self-diffusion in y-iron. The two most recent determinations of the latter quantity are 67,900" and 74,2007 cal/mol, which may be averaged as 71,000 cal/mol. This, in turn, gives a value of 3000 cal/mol for the activation energy of the atom-by-atom process, and hence the rate of growth should vary as e 8,000/RT where R is the gas constant

Jan 1, 1951

By Otto H. Henry, Edward L. Badwick

Up to the present time, according to Hansenl and Haughton,² the constitution of the bismuth-indium system has not yet been published. The generally accepted value for the melting point of indium, as listed in most scientific journals and textbooks, is 155°C. Recently, however, H. M. Davis3 has determined a new melting point for indium of 157.3²C O.l°C. Since bismuth has been used in preponderance as an alloying element in the majority of low-melting alloys, and indium has been used with considerable success in lowering the melting points of low-melting alloys, 4,6 an interest has been developed in the application of these two metals, making a complete knowledge of the constitution of its alloys desirable. In this investigation, the melting point of indium reported by H. M. Davis has been found to be substantially correct. A value of 157. ²°C ± O.5°C was determined. The two eutectic compositions have been placed at 34 and 50 pct bismuth with their respective eutectic temperatures as 72.4°C ± 0.5°C and 90°C ± 0.5°C. The bismuth-indium phase diagram has been determined by thermal and microscopic analysis and is shown in Fig I. Thermal Analysis Granulated bismuth and indium shot, having a guaranteed purity of 99.99 and 99.95 pct, respectively, were melted in a carbon crucible by means of a laboratory heater. To minimize oxidation of the alloys, a heavy mineral oil (Nujol) having a high- flash point was used. A platinum-platinum rhodium thermocouple of fine wire encased in a thin-walled Pyrex glass tube, about 1/8 in. in diameter, was connected to a type K potentiometer for temperature measurements. The thermocouple was calibrated against the melting points of tin, bismuth, and the silver-copper eutectic and the boiling point of water. Since the temperature readings could be reproduced to 0.²°Cl and the accuracy of the temperature standards in this range is slightly better than 0.5°C, it scems reasonable to assume that the temperature readings are reliable to approximately 0.5°C. The cooling rate could be controlled by varying the amount of insulation surrounding the crucible. Three or four layers of asbestos paper, 1/16 in. thick, sufficed to give a cooling rate of from I° to ²°C per minute. Undercooling was slightly noticeable. This condition was minimized by vigorous stirring, since the advantage of using slower rates was too small to justify the greater expenditure

Jan 1, 1947

By Alexander Squire

One of the principal factors that have contributed to the hesitancy of design engineers to use metal-powder parts is the difficulty experienced in the determination of the mechanical properties of compacted components. Because standard test methods cannot usually be applied in the inspection of such parts, and because adequate special test methods have not been developed, it has been considered desirable to investigate the methods that are applicable. These may then be included in specifications for metal-powder materials and components in order that the design engineer may be assured that the subject parts possess the desired mechanical properties for satisfactory performance. It is known that direct relationships exist between usually nonmeasurable properties as tensile strength and elongation and shear strength and the angle through which compacts may be plastically deformed before fracturing. These correlations are valuable in the inspection of specific parts, but it is necessary to set up standards before they may be satisfactorily employed. Apart from the use of correlations, the number and character of the inspection methods that are applicable to almost all powder parts is limited to three—chemical analysis, density, and hardness. The last of these may or may not be a pertinent characteristic, since the indentation hardness of many powdeied-metal materials is so low as to have little significance. It is, however, occasionally desirable to use hardness measurements as an indication of the uniformity of the structure of pieces of a given type. Chemical analysis reveals very little about the physical properties of metal-powder compacts, since the unpressed powder is usually of a composition almost identical with that of the finished pieces. Density determinations are simple to perform and have the advantage of being nondestructive in character. If the dimensions of a machine part are known (and usually they are), the average density may be determined by weighing a given number of pieces and dividing by the calculated volume of the parts. More accurate measurements may be made by the water-displacement method. It is recognized that mechanical properties of metal-powder materials are related to their density, but usually these relations are determined for only one type of powder, processed under a given set of conditions. Comparisons of the pioperties of compacts formed from different types of powders are made on the basis of compacting pressures instead of density, and for this reason the results obtained by using powders of different types appear widely variant.

Jan 1, 1947

By W. M. Mobley

The coal industry in Alabama, centered in Birmingham, has pioneered coal-bene-ficiation practice in the United States. The nature of the coal seams and mining methods employed have necessitated use of equipment and methods best adapted to the local conditions. Although all of the 30 or more coal seams now being mined in the state receive beneficiation, only the three most important producers of coking coals, the Pratt, Mary Lee and Black Creek, are discussed in detail. Nature of the seams, washability characteristics and equipment used are given as examples of the extent of work and progress in this field. The coal seams in Alabama are relatively thin and pitching, making mining difficult and expensive. Most of them are characterized by thin partings of rock or shale in the seam itself, as well as laminations of bone and rash. Mechanical mining methods have increased the occlusions from roof and floor to such an extent that nearly all the coal mined in the state must receive some treatment before it can be put on the market. During the year ending Sept. 30, 1943,' 18,129,792 tons of coal were mined in the state and 14,364,177 tons, or 79.2 per cent, received treatment. Excluding from the total the 1,223,014 tons produced by small wagon mines and the hand-picked lump coal, the amount re- ceiving beneficiation would be more than 90.00 per cent. This is, by far, greater than in any other coal-producing state. The earliest record of coal beneficiation in Alabama was the installation in 1890 of an experimental Lurig washer by Alexander Cunningham, for the Sloss Iron and Steel Co. at its blast furnace in Birmingham.2 In 1894 the Jeffrey Manufacturing Co. introduced the English Robinson washer, a combination of a hydraulic classifier and centrifugal machine. Erskine Ramsay, who has contributed so much to the coal industry, saw its possibilities as well as its mechanical defects and soon had his inventive mind at work. He added a sludge tank of his own design, and many Robinson-Ramsay washers were installed in Alabama and other states. The Stewart jig appeared in 1900, followed by the Montgomery jig in 1910 and both have found extensive use. Increased interest in this field led to new designs, such as the American, Elmore, Burke and Faust. The first Baum-type Norton jig was operated in 1930 and within the last five years six large installations of this type have been made by the McNally-Pitts-burg, Jeffrey and Link-Belt Companies. Wet-washing tables were introduced in 1922 but not extensively used until recently. The two most popular types are the Deister-Overstrom and Deister Plat-O. The coal-cleaning equipment used in Alabama has been relatively simple, yet efficient, but as the amount of impurities in the raw coal has been increased by mechanical mining and labor costs have become higher, much interest has been shown in sand cones, froth flotation and

Jan 1, 1947

History of Reverberatory Smelting in Montana, 1879-1933. By FREDERICK LAIST (Trans, vol 106 31,800 words ) The development of the art of reverbera¬tory smelting from 1879, when smelting first started in Butte, up to the present time is described. The paper traces the development of the reverberatory furnace, as regards both constructing and operating, from the initial 10-ton furnaces to the present-day 600-ton furnaces and the changes in operating practice which accom¬panied the gradual enlargement of the furnaces and the reasons therefor are described and explained The results obtained from an investigation (made in the course of the Carson litigation) into the various methods of charging reverberatory furnaces are given These investigations proved that the method of charging a reverberatory had very little to do with its performance It was also found, at the same time, that the depth and extent of the bath maintained in the furnace had very little to do with its performance Numerous operating results are included and the article is illustrated Development of Copper Converting at Butte and Anaconda. BY WILLIAM KELLY AND FREDERICK LAIST (Trans , vol 106 4400 words.) This paper is based on recollections of one of the authors, W M Kelly, who has been identified with the development of smelting and converting at Butte and Anaconda since early times The article starts with a description of the circumstances surrounding the first intro¬duction of copper converting at the Parrot Works in Butte under the Manhes patents It briefly recounts the difficulties which were encountered and the steps taken to overcome them Among these were the absence of means for punching tuyeres in the original converter This difficulty was overcome crudely by drilling holes in the windbox opposite the tuyeres, said holes being closed by wooden plugs Later these plugs were replaced by steel slides and still later by the Dibblie ball valve, which has remained standard ever since The development of the converter from both struc¬tural and operating standpoints is traced from the early beginning to the present day Developments in Lead and Copper Converting at Tooele. BY B L SACKETT (Trans, vol 106. 3900 words) This paper shows the development at this Utah lead and copper smelter from separate converting of the two kinds of matte produced to a more efficient and economical treatment of the combined mattes This was accompanied by the use of relatively large amounts of silicious ore in the converting of lead matte as well as copper matte, which greatly improved the quality of converter slag produced, both from the standpoint of its copper content and its desirability for

Jan 1, 1935

By W. W. West

MACHINERY used for size reduction of materials may be divided into three classes-depending upon the manner in which the crushing force is applied. In the first class could be listed the primary crushing units, such as the jaw crusher and gyratory crusher-which crush to coarse sizes by applying pressure intermittently between converging surfaces. In the second class may be listed crushing units, such as the hammer mill, roller mill, and ball mill, which crush principally by grinding or attrition. In the third class is the impact mill which, as the name infers, crushes by impact. The second and third classes generally include machinery used as secondary units for intermediate or fine crushing and grinding. Theory of Crushing by Impact Throw a stone into the air and give it a severe blow while it is momentarily suspended, and it shatters into several pieces. The impact crusher uses this "batting" principle, but carries it one step further. As the material to be reduced enters the crushing chamber, it receives a severe free-air impact blow by hard-hitting beaters suspended from rotor discs. The shattered particles formed are then driven at high velocity against impact blocks, where a further reduction in particle size takes place. The rebounding particles from the impact blocks are again caught by the beaters, and the process repeated until the material is swept out of the open bottom of the crusher. Impact Crushing Versus Attrition Crushing Fig. 1 shows a Hammermill type of attrition crusher. This particular mill has central feed and is reversible. Because of the central feed, an impact section can be designed into it at the feed entrance for preliminary crushing, followed by the cage bar attrition area for final sizing. The material is caught and held in a crushing chamber enclosed by grate bars or perforated plate. It remains in this chamber until it is reduced to particle size small enough to pass through the openings between the bars or in the plate. In this manner the top particle size discharged from the mill is closely controlled. As the swinging hammers pass through the bed of material, the material is broken down by a scrubbing action between hammers and material, material and grate bars, and material against material. This attrition produces a rounded particle shape, accompanied by slivers and a comparatively high percentage of fines. The crusher is especially useful in industries where the material treated is not too abrasive, such as limestone, cement or coal plants. It can be readily understood that from the maintenance standpoint, it is not suitable for hard abrasive materials such as refractories and aluminum oxides. One common type of impactor is shown in Fig. 2. The bottom of this type crusher is entirely open and the passage of the material through the crushing chamber is almost instantaneous. Liberal clearances are maintained between the impact hammers and the anvil type breaker blocks. This eliminates practically all attrition. It is the elimination of attrition that makes the impactor particularly adaptable for reducing hard, abrasive materials. The impactor is also well suited for the reduction of wet or frozen materials, which clog an ordinary Hammermill. Particles broken by impact, when examined under the microscope, show a distinct tendency toward rough, cubical shape, with a minimum of fines. Another important factor in impact crushing is that crushing is accomplished along natural cleavage lines, thus freeing foreign ores or materials.

Jan 1, 1952

By R. S. Busk, E. G. Bobalek

THE relation between gases and metals has been a subject of increasingly active investigation during the past years, principally devoted to the study of metal-hydrogen systems. It has been found that hydrogen is soluble in most molten metals to an appreciable extent and somewhat soluble in most solid metals.1,2 In every known case there is a sudden decrease in solubility at the melting point. Thus a freezing mass of metal containing hydrogen in excess of the solid solubility must in some way expel that excess during the freezing process. This leads to internal blowholes, and such effects as pinhole porosity. Gas trapped in metal that is to be fabricated by a working process such as extrusion or rolling may be the cause of blisters. For some cases, notably in copper and iron alloys, the presence of hydrogen can lead to extreme embrittlement of the metal. The aluminum-casting industry has long recognized the importance of hydrogen in its techniques. Excess gas in molten aluminum alloys often leads to the formation of "pinhole porosity" in the solid casting.3 To prevent this hydrogen pickup it is necessary to avoid overheating the melt and to protect it from such sources of hydrogen as water. In spite of all precautions, it is sometimes necessary to extract hydrogen from the melt just before pouring by bubbling with a gas such as chlorine or nitrogen. Recently it has been found that somewhat similar effects are possible with magnesium alloys, in that the presence of hydrogen can induce or aggravate microporosity.4-6 This paper is primarily concerned with a presentation of some facts concerning the solubility of hydrogen in magnesium and its alloys, with some discussion of the significance of these facts in a practical sense. In any study of gas-metal systems it is important to bear in mind a clear distinction between adsorption on surfaces and absorption within the lattice.1 Considerable attention has been directed toward determining whether hydrogen is truly soluble in any solid metal, or whether the gas extracted from a sample was present at surfaces (external and internal) only.7 Most present day evidence supports the idea of true solution in addition to adsorption. A second important factor when dealing with gas solubility is the dependence of such solubility on external pressure. For diatomic gases such as H2, solubility in both liquid and solid metals apparently is proportional to the square root of the pressure, indicating a breakdown to a monatomic gas before diffusion into the lattice .2 For true equilibrium values of solubility, therefore, the pressure at the metal surface must be constant and, preferably, known. Very little has been published concerning the hydrogen-magnesium system. Winterhager has presented the most

Jan 1, 1946

By R. A. F. Penrose

I. INTRODUCTION. THE superficial alteration of ore-deposits is a recognized principle of geology, in the same way as is the superficial alteration of any of the common rocks. Its importance in some classes of ore-deposits is also well understood, as in many precious-metal deposits; while in other classes, its importance has been proved in individual cases, as in the Lake Superior iron-deposits. The causes and effects of superficial alteration in many classes of deposits, however, are not so generally understood; and it is the object of the present paper to show that such changes almost invariably give rise to exceedingly important chemical and physical phenomena, while in many deposits, the question as to whether they can or cannot be profitably worked depends largely on the extent and character of this alteration. The various treatises on ore-deposits published in the United States and Europe make frequent mention of superficial alteration, but have not treated the subject fully. As early as 1554, however, before which time but little accurate information was had on the geologic nature of ore-deposits, Prof. J. D. Whitney in his classic volume, The Metallic Wealth of the United States, describes the alteration-products, or gossans, in certain deposits and mentions others. On the more purely chemical side of the question, the work of Bischof, Daubrée, Roth, Rose, Hunt, Breithaupt, Blum, Julien, Deville, Debray, Volger, Moissan, Fremy, Lévy, Fouqué, and others has afforded much valuable information and many useful suggestions. The chemical principles brought out by these various authors have been applied, to a certain extent, to the solution of the phenomena of

Jan 1, 1913

By Eugene Leonardon

THE search for oil has required, and without a doubt supplies, a tremendous amount of information on the structure, composition, physical properties, and history of sedimentary rocks. The earliest and most complete source of knowledge is the sample or core of the rock itself, the uses of which are well known. The purpose of this paper is primarily to discuss a new method for obtaining these cores, and to illustrate its use in connection with electrical logs. Most cores have been obtained through a special adaptation of rotary drilling, and the results have been remarkably good, considering the mechanical problems involved. Unfortunately, because of the time and expense, this method cannot be used for the entire length of the drill hole. Even though ingenious contrivances have been evolved in order to reduce the time spent in round trips, such as wire-line coring equipment, mechanical coring still remains too expensive to be carried out con-tinuously. In practice, therefore, one is finally compelled to estimate the probable depths of the more interesting horizons and, allowing a wide margin of safety, to core through those sections only. It is true also that interesting results have been obtained by examining the cuttings brought to the surface by the mud circulated in the well during the process of drilling. Be that as it may, the inescapable fact remains that key horizons may be passed inadvertently, for one reason or another, while the drilling operations are being performed. The only continuous record of the formations encountered is that furnished by electrical surveys. Obviously, it would be desirable to make the electrical survey first and to take the samples from the wall of the hole according to the indications on the electrical log. In this way, it would be possible to core only the exact sections desired, eliminating the otherwise inevitable estimates as to the point at which to start coring, and thereby reducing to a minimum this expensive operation. At the same time this method would provide a maximum' of useful samples.

Jan 1, 1939

By B. W. Frazier

IN the numbers of the Engineering and Mining Journal of June 27th and July 11th, 1874, there appeared some very complete statistics of the working of some anthracite blast-furnaces belonging to a large establishment in this country, followed by calculations of the heat requirements of the furnaces, similar to those which have been made for European furnaces by Mr. I. Lowthian Bell, Prof. Gruner, Prof. Akerman and others. To the author of these valuable papers, Mr. John A. Church, of New York, the thanks of American iron metallurgists are due for this attempt (the first, to my knowledge at least), to attack systematically and scientifically the problem of economy of fuel in our anthracite blast-furnaces, by applying the formulas obtained from European practice and from the experiments of European metallurgists, to the determination of the amounts and the modes of distribution of the heat production and absorption in our furnaces. In order to facilitate a comparison of the results thus obtained for the anthracite furnaces in question with those obtained for the best types of European coke furnaces, I have reduced to the same standard of heat units (the product of the ton and the degree Centigrade), and placed side by side, the calculations of the heat requirements of one of the furnaces of the Clarence works, as given by Mr. Bell, of a furnace at Pouzin, on the banks of the Rhone, given by Prof. Gruner, and of the anthracite furnaces for 1869-73, as given -by Mr. Church. Table I shows the different conditions of working of the three furnaces, of which Table II gives the respective heat requirements. I have made this latter table in such a manner as to give for each furnace its heat requirements, both according to the views of Mr. Bell and those of Prof. Gruner. Mr. Bell assumes that all the carbonic acid produced by the decomposition of the carbonate of lime of the charge, is reduced to carbonic oxide by contact with solid carbon ; also, that the carbon of the pig iron is a portion of that deposited in the ore in the upper part of the furnace, by the dissociation of carbonic oxide. Prof. Gruner, on the other hand, assumes that all the carbonic acid of the carbonates of the charge escapes unreduced, and that the carbon deposited in the upper part of the furnace, by the dissocia¬tion of carbonic oxide, is again converted into carbonic oxide or

Jan 1, 1875

By G. L. Corrigan, J. R. Coleman

Four factors that largely determine the end product obtained when cement and water are mixed are the chemical compo ition of the cement, the fineness to which the cement is ground, the amount of mixing water used, and the procedure used in mixing the slurry. In order to study the effect of two of these factors, the other two, the chemical composition and method of mixing, are kept constant, leaving as variables fineness and water-cement ratio. Through years of experimentation and usage it has been well established that the reduction of cement clinker to a very fine state by grinding improves its cementing value, principally because the reaction between cement and water takes place only at the surface of the cement particle, further action being hindered by the accumulation of reaction products that tend to coat the unreacted material. Therefore, the more finely ground a cement, and the greater the surface exposed in proportion to its mass, the more rapid is the hydration rate. Similarly, the greater the surface exposed, the greater the proportion of the cement that reacts, and the lower the amount of residue that is unreacted and so remains inert and unable to make any contribution to cementing properties.1 Although it is more expensive to manufacture a finely ground cement than a coarser cement, the advantages of fine grinding of construction cements were so marked that the fineness of cement has increased considerably in past years. When the manufacture of special oil-well cements was begun, it was necessary to consider properties of cement that previously were considered of minor importance, foremost of these being pumpability. Since, with the water-cement ratio constant, a finely ground cement will produce a neat slurry of higher consistency and shorter time of pumpability than will a coarser cement, there is a tendency to grind oil-well cements to a lower degree of fineness. Therefore, in order to produce oil-well cements that will make a slurry having a long time of pumpability, cements are manufactured that because of their coarseness generally are poorer cementing materials than some of the more finely ground construction cements. On the other hand, often it is necessary to pump oil-well cements for long periods of time to place them properly behind a string of casing in a deep well, and since high strength is not of foremost importance for such cement, there is room for considerable controversy concerning the proper fineness range.

Jan 1, 1941

By A. L. Mular

The flotability of crushed zinc oxide pellets which were doped to produce more n-type or less n-type (more p-type) properties was studied with a Halli-mond tube. Flotation data are presented to show that the pH at which 50% recovery occurs and the collector concentration for 50% recovery depends upon the concentration of doping agent added substitu-tionally for zinc in zinc oxide. The time of sintering of pellets has a slight effect on flotation behavior. A speculative model is proposed to explain the observed behavior in light of the fact that zinc oxide is a semiconductor and has a space charge region at the surface. Experimental verification is necessary before the proposed model can be established as correct. In recent years, the attachment of flotation reagents to minerals has been shown to depend upon the behavior of an electrical double layer which exists in the liquid near the mineral-liquid interface.' Thus, a mineral placed in water will undergo a surface re-arrangement, most likely be preferential dissociation of lattice atoms or by surface adsorp-tion-desorption reactions, to form a dissociation electrical double layer with the solution. Among the many factors which influence adsorption processes, the past history of the mineral itself is one of the most important. Because of trace impurities, minerals from different localities may exhibit marked differences in flotation behavior. This is not unexpected, since investigators who have studied the detailed structure of the double layer's3 have known for some time that the impurity content of many minerals may exert strong influence on double layer variables. For this reason, their studies were usually made with minerals of high purity. The precise relationship between impurities in a mineral and double layer parameters such as capacity and electrostatic potential has been obscure. However, impurities in a semiconductor type mineral which is in contact with a solution have been recently shown to produce changes in the properties of a space charge layer which extends into the bulk of the semiconductor to a distance of one micron or more.4 The double layer is influenced by the space charge layer, whose origin is best discussed in terms of the band theory of solids. A qualitative description of the behavior of impurities in the bulk of a semiconductor, from a chemical point of view, is useful at this point. Briefly, impurities or defects (lattice vacancies, interstitials, etc.) in semiconductors such as PbS, ZnS, FeS2, Cu2S, NiS, NiO, Fe2O3, ZnO, CdS, MnO2 and many others, behave somewhat like acids or bases in water. For example, water dissociates into hydrogen and hydroxyl ions according to

Jan 1, 1965

By R. L. Perrine

The rise of drain holes drilled from a well to improve productivity is becoming increasingly common. This paper presents data on the productivity increase that may he expected. The data were obtained by use of an electrolytic tank mode1 of a reservoir. Parameter varied in the study to show their effect on productivity include the length, number, and arrangement of drain holes, formation thickness, and damage near the well-hore. The most important results are that very large increases in productivity can be expected only ill damaged wells. The distance, to which drain holes penetrate is of primary importance. Additional length is more effective than increasing the number of drain holes. INTRODUCTI O N In planning the use of drain holes to improve productivity, it is important to he able to estimate the increase in production that can be obtained for a given expenditure. It is also important to know what combination of parameters related to the use of drain holes can he chosen to give the largest production increase. This paper presents data on the productivity increase that may be expected, as obtained by use of an electrolytic tank model of the reservoir. In this study, :! number of parameters were varied to show their effect on productivity. These included the length, number, and arrangement of the drain holes. The presence or absence of a damaged zone of low permeability around the well-bore and the thickness of the producing formation were also considered. The productivity increase that might be expected due to drain holes is presented as the ratio: productivity of a well after drain holes are drilled and completed to the productivity of the same well in an undamaged state without drain holes. The symbol Q/Qo is used to represent this productivity ratio. Thus, the comparison in each case is with a formation of uniform and undamaged permeability. Additional notation includes I;, for the radial extent of the damaged zone, which is assumed to be cylindrical and concentric with the wellbore. Thus the effect of an actual block is approximated by a discontinuous varia-tion in permeability. For purposes of this paper, the permeability within the damaged zone, denoted by kb, is assumed to be 1/25 that in the remainder of the formation, or k. A necessary assumption in making comparative tests using an electrolytic model is that reservoir flow behavior can be approximated by single-phase, steady-\tate flow according to Darey's Law. In addition, the formation must be assumed to be homogeneous with equal horizontal and vertical permeability. The well-hore diameter in this study is assumed to be 11¾ in. and the drainage radius of the well equal to 500 ft. The drain holes are considered to have been completed without damage. THE ELECTROLYTlC MODEL 'She producing formation was modeled by forming a sheet of phosphor-bronze into a cylinder 40% in, in diameter to represent the boundary of the drainage area. This was enclosed in a waterproofed plywood box, and the box filled to an appropriate level with a dilute sodium chloride solution. Solution concentration was adjusted to give a total resistance from

Jan 1, 1956

By Irwin Roman

THE literature of geophysics as applied to the discovery of mineral deposits has been very extensive during the past few years,1 but there seem to be few references to the use of the method of least squares for obtaining better interpretations of the observed data .2 There seems to be a general reluctance among geologists and engineers to acquire the technique of least squares, in spite of the fact that a thorough knowledge of the theory is not necessary for the use of the method.

Jan 1, 1932

By C. Z. Serpan, L. J. Wittenberg

The density of liquid plutonium was determined, by a pycnometm'c technique, from 664 to 788°C and exhibited a temperature dependence, which could be expressed as:. P= C17.63 - 1.52 x 10-"t] +0.04 g per cc where t = OC. These density values compare favorably with the values previously obtained by a technique utilizing Archimedes' principle. The apparatus and method were evaluated when the densities 0.f molten tin and bismuth were measured and found to be in agreement with accepted literature values. PLUTONIUM or an alloy of plutonium in the liquid state has been proposed as a fuel for a fast-breeder type nuclear power plant.' Since knowledge of the liquid density of plutonium is required for the proper design of such a system, this study was undertaken. In addition, the density and volume expansion coefficient of liquid plutonium are of interest for comparison with these same properties of the six allotropic modifications of the solid metal. Comstock and GibneyZ were first to report a value for the density of liquid plutonium. The value for only one temperature, 665"C, was calculated from data obtained by the radiography of the meniscus, Fig. 3. Recently, the density at a series of temperatures has been reported by Knight,3 who obtained his values by using a differential volumeter, and by 01-sen, Sandenaw, and Herrik, who obtained their values from measurements of the loss in weight of a tungsten bob immersed in the liquid. The density of liquid plutonium reported here was determined by a vacuum pycnometer method. In an evacuated system, the tips of calibrated tantalum pycnometers were lowered beneath the liquid sur-

Jan 1, 1962