THE purpose of this paper is to direct attention to the lower part of the austenite transformation diagram, or TTT curves, where considerable uncertainty still exists as to the blending of the bainite and martensite reactions. The dissimilarities between these two low temperature trans- formations have been summarized recently by Troiano and Greninger.1 Of particular importance to the present work is the fact that martensite formation, unlike bainite formation, is not suppressed by the fastest quenching rates attainable. However, most of the investigations in this direction have been concerned primarily with the start of the martensite transformation [(M,)] during cooling, rather than with the quantitative aspects of the subsequent reaction on either further cooling or isothermal holding. Several years ago, Cohen2 suggested a form of transformation diagram which reconciled, at least schematically, the isothermal characteristics of the bainite transformation with the insuppressible nature of the martensite transfoi mation. In essence, the diagram consisted of a family of horizontal lines (representing the progress of the austenite-martensite reaction during quenching) which were interrupted in point of time by the bainite family of C-curves extending down from higher temperatures. This picture received later support by metallographic3 and dilatmetric4,5 studies, but the techniques employed were not sufficiently critical to substantiate some of the details. Elmendorf6 and Grange and Steward7 have shown that the Greninger-Troiano metallographic techniques may be used not only for [M,] determinations, but for studying the course of further austenite decomposition. In fact, the latter investigators have observed the amount of martensite formed as a function of temperature below [M,] in fourteen commercial steels. In the present paper, the Greninger- Troiano technique has been combined with the lineal method of Howard and Cohen9 to provide a unique, quantitative treatment of the austenite-martensite reaction. Furthermore, isothermal transformations have been similarly measured on holding at temperatures above and below M,, thus permitting a fairly detailed presentation of the lower part of the conventional austenite transformation diagram. EXPERIMENTAL DETAILS Materials The steels, listed in Table I, were selected for study because they exhibit a satisfactory range of M, temperatures and have not received as much attention as the lower carbon grades. They were prepared as 30 lb induction furnace heats in the laboratories of the Vanadium-Alloys

Jan 1, 1947

By David R. Mitchell, B. M. Bird

DENSE-MEDIA processes utilize the familiar laboratory float-and-sink procedure on a commercial scale. Just as wood chips float on water and sand sinks, so coal floats and refuse sinks when placed in a medium intermediate in specific gravity between the coal and refuse. Liquids intermediate in specific gravity between coal and refuse used in commercial plants are of four types: (1) organic liquids of high specific gravity-halogenated hydrocarbons; (2) dissolved salts in water; (3) pseudo liquids obtained by suspending solids, such as sand or magnetite, in water, and, (4) fluidizing a mass of sand or other solids by air currents. Those most widely used for cleaning coal are solutions of calcium chloride in water and a suspended sand or magnetite pseudo liquid. Laboratory float-and-sink testing is an intermittent operation during which every opportunity is given for particles lighter than the medium to float and particles heavier to sink. Commercial processes are continuous; vertical and horizontal currents of the separating medium occur as either part of the process or unavoidedly produced by the introduction of feed and withdrawal of products, 'so that the exact separation of the laboratory technique is not duplicated by commercial processes. However, separations close to the theoretical are obtained in commercial machines by careful technical control of the process. Most machines in commercial installations are crowded to get as much out of the equipment as possible, so that careful technical control is necessary is get the recoveries and grade of product desired. Sizes usually cleaned are plus ¼ in. or plus 1/8 -in. in the United States and plus 1/16-in. in Great Britain. Coal as small as 1 mm. has been cleaned in some experimental installations. The separation of coal from refuse in sizes finer than about 1/8-in. is made difficult by viscosity effects and hence at the present time cleaning is confined to the coarser sizes. Technical advances in the art of cleaning coal by dense-media processes is progressing rapidly and it is likely that equipment, media, and procedures will be developed to clean sizes down to 0.5 mm. efficiently and at low cost.

Jan 1, 1950

By Horace Winchell

SCOPE OF DISCUSSION THE laws here referred to Are those which define the status of the prospector for mineral deposits in the soil or beneath it, establish his methods of procedure, protect him in his possession while searching for the subterranean treasures, and give him assurance of title when all required conditions have been fulfilled and valuable minerals discovered. Regulations for the operation of mines and the safety and health of mine employees are likewise subjects of Federal and State legislation, but are not within the scope of the present program. Various features of our present laws will be discussed in detail by able students of the subject, and specific remedies will be proposed for the most glaring defects. It is my purpose to present in this paper a summary review of the reasons why revision is needed and demanded by the great majority of those in daily contact with the industry.

Jan 4, 1914

By T. J. Smolik, Harman, D. W. Fuerstenau

By means of electrokinetic measurements, the surface properties of the aluminosilicate polymorphs (sillimanite, andalusite, and kyanite) and also mullite have been found to depend on the ratio of A10 bonds to SiO bonds in the surface. The Al-toSi ratio in the surface is dependent upon the crystal lographic properties of the mineral, which in turn determine coordination numbers of A1 and of Si, cleavage characteristics, and density of the various solids. Mullite with a greater bulk Al-toSi ratio has the highest zpc of the aluminosilicates. By treatment in dilute acids or by cycling between acidic and basic solutions, alumina is selectively dissolved from the surface of these orthosilicates. This shifts the apparent zpc to lower pH values as the fraction of SiO groups in the surface increases. Thus, surface properties can be altered by procedures that alter the A l-to-Si ratio in the surface. Flotation of these aluminosilicates results from electrostatic interaction of the collector ions with the mineral surfaces. As a result, flotation response shifts in accord with any shift in apparent zpc by pretreatment. Separation of minerals by flotation is based on differences in the physicochemical properties of their surfaces.'-3 For many minerals, adsorption of flotation collectors results from their functioning as counter ions in the electrical double layer at solid-water interface. In such systems, separation depends on differences in the zero point of charge (zpc) of the various minerals. The zpc is defined as the concentration of potential determining ions in solution at which the surface is uncharged. The potential determining ions for inorganic oxide-water interfaces are hydrogen and hydroxyl.4,5 This work is concerned with the effects of crystal structure, composition, and surface preparation on the surface properties and flotation behavior of aluminosilicates. Differences resulting from crystal structure were studied by measuring electrokinetic potentials and determining the flotation behavior of three different aluminosilicate materials having the same chemical composition (Al2O3 SiO2), namely andalusite, kyanite, and sillimanite. Furthermore, the effect of the Al2O3-to-SiO2 ratio on flotation behavior and surface properties was investigated by including synthetic mullite, 3A12O3 .2SiO2. Gaudin and co-workers 6,7 have clearly shown how crystal structure determines the native floatability of certain minerals. Those solids in which the surface is comprised mainly of broken residual bonds possess naturally hydrophobic surfaces. It was found by Bakakin8 that for a number of oxidized lead minerals, differences in floatability were due to the distance of Pb atom from the surface. Only limited work has been done on relating electrical properties of surfaces to crystal structure and composition. Healy et. a1.9 found that the zero points of charge of various manganese dioxides ranged from about pH 1.5 to pH 7.5, and these differences in the zpc's were interpreted in terms of the atomic packing in the various crystals. The research presented here clearly shows that crystal structure and chemical composition do affect the surface properties of aluminosilicates and, in addition, that these effects can be altered by changing conditions under which the surfaces are prepared. CRYSTAL STRUCTURE OF THE ALUMINOSILICATES Sillimanite, andalusite, and kyanite are composed of regionally metamorphosed rocks differing mainly in degree of metamorphism. All three minerals have the same chemical composition, Al2O3 - SiO2, of which sillimanite is the high temperature polymorph and kyanite and andalusite the lower temperature polymorphs. Andalusite and sillimanite crystallize in the orthorhombic system while kyanite crystallizes in the triclinic system. The structure of these three minerals is essentially chains of aluminum-oxygen octahedra linked laterally by silicon and aluminum. The arrangement of these chains in the three minerals is shown in Fig. 1.l4

Jan 1, 1967

By W. Rall, A. J. Birkle

The effect of fast-neutron irradiation on the micvo strcture of a common reactor pressure-vessel steel, A212 Grade B, was studied using thin-foil transmission electron microscopy. The dislocation density of the irradiated material is considerably greater than that of the nonirradiated control material. Annealing studies indicated that dislocations and hardness ill the irradiated material annealed out—as docs the radiation-induced embrittlement according to other- investigators— at temperatures STEELS in nuclear reactors are affected by neutron irradiation. In the American Society for Testing Materials (ASTM) A302B and A212B steels commonly specified by designers for reactor vessels, between 650° and 800°F. However, the dislocations and hardness in control samples cold-worked to 9 and 70 pct did not anneal out readily, and a high dis -location density was observed, even after a 1-hr anneal at 850°F. Based on the hypothesis that cllrster defects, rather than the increased dislocation density, are primarily responsible for mdicltiotz-iudziced e)nbriftlen7ent, reconzmendations are made for reducing the susceptibility to such ernbrittlement. exposures at a temperature of 550°F or lower to neutron dosages encountered during a 20- to 30-year life (-3 X 10'' nvt, >1 mev) may increase the nil-ductility transition temperature (NDT) as much as 300" or 400".'9 Therefore, to prevent brittle failures in reactor structures, extreme caution is required to reduce thermally induced stresses during all reactor shutdowns and startups when the temperature is below the NDT of the pressure vessel.

Jan 1, 1964

By Roland D. Parks

Corundum, little publicized as an industrial abrasive, has, in its small way, contributed greatly to the production of many specialized items vital to our war program and to Our allies. Optical elements Of the highest quality for range finders, bombsights, and scientific instruments; precision metal parts for torpedoes and airplane engines; quartz crystal plates for military radios; armorplate and malleable castings for tanks and guns; and eyeglasses for everyone; these are some Of the products that corundum has helped to produce in the quantities needed and on time. Unlike metals and many other raw materials, corundum is not incorporated into any Of these finished products. It is simply a grinding medium used to produce the desired finish or precision; an operating supply or tool, so to speak. With a Mobs' scale index of 9, corundum ranks next to the diamond in hardness among the natural minerals and is superior to emery and garnet. The gem varieties of corundum, including the Oriental ruby and sapphire, are frequently more highly prized as jewels than the diamond. It is the intent Of this paper to deal Only with a description of the corundum industry, the administration of wartime control, and certain economic aspects as seen by the author. Several references are listed to assist anyone who wishes further information on the geological occurrence of the mineral. Ore Production and Consumption For the past two decades, south Africa has been the world's sole producer of corundum ore. A possible exception is Russia, where, it is understood, there was considerable production during the thirties for domestic consumption but for which statistics are lacking. The United States is the world's principal consumer of corundum ore; imports lor the period 1934 through 1940 averaging 3000 Short tons per year, The years 1935 and 1936 were close to the 5000-ton mark, and imports during 1941, the last prewar year for which statistics have been released, were approximately 6000 Short tons. Again lacking statistics on Russia, the United Kingdom ranks second, but far below the United States in consumption of ore. Historically, corundum has been found in some 35 countries throughout the world, but the principal deposits are in South Africa, Canada, Madagascar, Russia and the united States. Deposits are generally small and subject to rapid exhaustion. Thus, the United States was the principal world producer for the period 1870 to 1900, when operations ceased except for two years during World War I. India was a producer of ore from 1898 through 1921, with peak output in 1916 through 1918 Canada came into production in 1901 with substantial output of ore and finished grain until 1914; the production thereafter was smaller until 1921. Madagascar has produced ore since 1910 but has had important output in only a few scattered years. South African production started in 1912

Jan 1, 1948

By Roland D. Parks

Corundum, little publicized as an industrial abrasive, has, in its small way, contributed greatly to the production of many specialized items vital to our war program and to Our allies. Optical elements Of the highest quality for range finders, bombsights, and scientific instruments; precision metal parts for torpedoes and airplane engines; quartz crystal plates for military radios; armorplate and malleable castings for tanks and guns; and eyeglasses for everyone; these are some Of the products that corundum has helped to produce in the quantities needed and on time. Unlike metals and many other raw materials, corundum is not incorporated into any Of these finished products. It is simply a grinding medium used to produce the desired finish or precision; an operating supply or tool, so to speak. With a Mobs' scale index of 9, corundum ranks next to the diamond in hardness among the natural minerals and is superior to emery and garnet. The gem varieties of corundum, including the Oriental ruby and sapphire, are frequently more highly prized as jewels than the diamond. It is the intent Of this paper to deal Only with a description of the corundum industry, the administration of wartime control, and certain economic aspects as seen by the author. Several references are listed to assist anyone who wishes further information on the geological occurrence of the mineral. Ore Production and Consumption For the past two decades, south Africa has been the world's sole producer of corundum ore. A possible exception is Russia, where, it is understood, there was considerable production during the thirties for domestic consumption but for which statistics are lacking. The United States is the world's principal consumer of corundum ore; imports lor the period 1934 through 1940 averaging 3000 Short tons per year, The years 1935 and 1936 were close to the 5000-ton mark, and imports during 1941, the last prewar year for which statistics have been released, were approximately 6000 Short tons. Again lacking statistics on Russia, the United Kingdom ranks second, but far below the United States in consumption of ore. Historically, corundum has been found in some 35 countries throughout the world, but the principal deposits are in South Africa, Canada, Madagascar, Russia and the united States. Deposits are generally small and subject to rapid exhaustion. Thus, the United States was the principal world producer for the period 1870 to 1900, when operations ceased except for two years during World War I. India was a producer of ore from 1898 through 1921, with peak output in 1916 through 1918 Canada came into production in 1901 with substantial output of ore and finished grain until 1914; the production thereafter was smaller until 1921. Madagascar has produced ore since 1910 but has had important output in only a few scattered years. South African production started in 1912

Jan 1, 1948

By Leonard Waldo

The recent and rapid development of the physics of engineering materials at temperatures as low as that of liquid air and as high as that of the electric are, has drawn renewed attention to the absence of tables, properly printed and spaced, for the convenient and accurate translation of temperature from centigrade to Fahrenheit scales and vice versa. It is to be noted that the Fahrenheit scale is the almost universal usage in foundries and shops in the United States, though the laboratories of the same works employ the centigrade notation. The growing use of the electric furnace in Germany and France calls for much American citation all in centigrade high temperatures, and while the arithmetical calculation is simple, it becomes burdensome when often repeated. I have been surprised at the numerous reprints of Table I. from centigrade to Fahrenheit degrees, first privately printed for personal use, which have been made by works, blue-prints, text-books, and technical journals, and I hope that Table II., from Fahrenheit to centigrade degrees, will be equally useful. For mental calculation the easiest rule to convert centigrade into Fahrenheit is to add 32° to twice the centigrade reading less one-tenth of this product: Thus 1000' C. = 2000" — 200" + 32" = 1832" F., and to convert Fahrenheit to centigrade, subtract 32" from the Fahrenheit reading, multiply by 10 and divide by 2 and 9 successively : Thus 1000° F. = 1000° — 32° = 968° X 10 = 9680° - 2 = 4840° - 9 = 537.77° C. Another and often very convenient method is by 'use of a graphic construction as follows :

Jan 1, 1913

By Roy A. Lindgren

Since the year 1643, when the first blast furnace in America for treating iron ore was built at Saugus, Mass., out of mica schist quarried in the neighboring district, the procurement of a suitable refractory for furnace lining has been a problem of concern to the operators of furnaces. The stacks built of mica schist continued to smelt iron ore until about 1836, when, according to F. H. Norton, the first firebrick were produced1, at Queens Run, Pa. Other writers speak of brick having been molded and burned in Massachusetts about the year 1834. In 1841, Andrew Russell began to produce medium refractory plastic clay brick near East Liverpool, Ohio, that were used for lining blast furnaces1. The well-known Kentucky clay-producing district was not opened up until the year 1871, but since then it has produced a large percentage of the linings for iron blast furnaces. While some strides have been made by the refractories industry during the 100 years that have passed since the first firebrick were produced, it has been only during the last two decades that any real progress has been made towards bettering the product, even though the method of production had improved. Perhaps the fault lies with the user of the brick rather than with the producer, for not sooner demanding a superior product. During the past 15 years the tonnage produced per lining has increased from 500,000 gross tons to 1,000,000 gross tons, and now some furnaces are producing 1,600,000 gross tons and better on a single lining. It is true that enlarged capacity of furnaces and improved practice have accounted for some of this increase in tonnage, nevertheless better quality in firebrick must be given credit for its share. However, we are not yet ready to say that we have reached a maximum life of furnace lining. We believe that a better product can be produced and that the refractories industries of America will, through their extensive research depart-

Jan 1, 1937

By Dwight E. Woodbridge

DuriNg April, Max, and June, 1910, I was in charge of an examination of the greater part of the Moa iron-ore area in Oriente Province, Cuba, on the north coast, near the east end of the island. My instructions, on arrival at the properties, were to check former estimates of tonnages and grades, and to re-examine the ore comprised in claims covering 44,727 acres. This work included the running of lines dividing the properties into co-ordinate planes, the boring of many thousand feet of holes spaced at the intersections of these co-ordinates, the taking of samples of the ore penetrated, the analysis of these samples for their various constituent minerals, and the determination of the results as to tonnages, depths, and grades, both for individual properties and for the entire group. Each section of every one of the thousand holes drilled was to be compensated for depth and grade with every other, a series of simple arithmetical calculations of no slight magnitude, the mere mechanical labor of which consumed much time, but finally resulted in giving a complete average of all the essential facts for the entire area of 18,000 hectares, Had it not been for the more than willing, active, and able co-operation of the officers of the Spanish-American Iron Co., from Charles F. Rand, President, and Jennings S. Cox, General .Manager, down to the most humble water-carrier, the work would have consumed far more time than it did. The lands thus systematically explored by me were comprised in the following denouncements: Punta Gorda, Yaminiguey, Baracoa secunda, Sagua, Moa, Yajrumaje, Lirio, and Cabanas, all of which were massed as the Moa group, so called, and cover an area of 13,832 hectares, or 34,179 acres. Some 10,000 acres additional to this was included in neighboring properties, lying between Moa and the east end of the island, the Buena Vista,

Jan 1, 1912

By H. J. French

WITHIN the past few years, particularly because of the rapid growth of the airplane industry during the war, considerable attention has been paid to the manufacture of light-wall cold-drawn seamless and welded steel tubing for structural purposes. While the manufacture of such tubing is not, in itself, a difficult matter, some difficulties have. been encountered in producing the same under specifications requiring definite physical properties. It is the purpose of this paper to describe the methods of manufacture and the properties that may be obtained by such methods for tubing coming within about ½ to 2 in. (12.7 to 50.8 mm.) outside diameter and 10 to 22 Birmingham wire gage (0.134 to 0.028 in. wall thickness). Such tubing is largely used as structural material in the aircraft industry, and it is of the utmost importance that the physical and chemical properties should be known, and also that the various factors entering into the manufacture should be under such control as to allow these properties to be varied and held within definite limits. In general, tubing may be divided into four classes: namely, specialty tubing, such as riveted-sheet or plate, lock jointed, etc.; brazed tubing; welded tubing; and seamless tubing. Welded tubing may be divided into hot product, such as lap welded and butt, welded, and cold product, such as acetylene and electric welded. Seamless tubing may be hot rolled or cold drawn.

Jan 9, 1919

By Roy Lindgren

Since the year 1643, when the first blast furnace in America for treating iron ore was built at Saugus, Mass., out of mica schist quarried in the neighboring district, the procurement of a suitable refractory for furnace lining has been a problem of concern to the operators of furnaces. The stacks built of mica schist continued to smelt iron ore until about 1836, when, according to F. H. Norton, the first firebrick were produced1, at Queens Run, Pa. Other writers speak of brick having been molded and burned in Massachusetts about the year 1834. In 1841, Andrew Russell began to produce medium refractory plastic clay brick near East Liverpool, Ohio, that were used for lining blast furnaces1. The well-known Kentucky clay-producing district was not opened up until the year 1871, but since then it has produced a large percentage of the linings for iron blast furnaces. While some strides have been made by the refractories industry during the 100 years that have passed since the first firebrick were produced, it has been only during the last two decades that any real progress has been made towards bettering the product, even though the method of production had improved. Perhaps the fault lies with the user of the brick rather than with the producer, for not sooner demanding a supe¬rior product. During the past 15 years the tonnage produced per lining has increased from 500,000 gross tons to 1,000,000 gross tons, and now some furnaces are producing 1,600,000 gross tons and better on a single lining. It is true that enlarged capacity of furnaces and improved practice have accounted for some of this increase in tonnage, nevertheless better quality in firebrick must be given credit for its share. However, we are not yet ready to say that we have reached a maximum life of furnace lining. We believe that a better product can be produced and that the refractories industries of America will, through their extensive research depart-

Jan 1, 1936

By Sandip K. Mitra, John E. Dorn

The Basinki-modified Seeger equation for deformation of metals by means of thermally activated intersection of dislocations was used to ascertain the various factors responsible for the strain hardening of poly crystalline aluminum and a series of a solid solutions of magnesium in aluminum. The analyses were based principally on the rate of change of strain rate with stress and the Cottrell-Stokes ratio. From measurements of these quantities on a series of strain-hardened states, the force displacement diagram for intersection, the density of dislocations in the entanglements, and the contributions of the athermal local stress and long-range stress interactions were deduced. Poly crystalline aluminum was observed to have the same force-displacement diagram for intersection as single aluminum crystals, and the corresponding diagram for the magnesium alloys differed in a manner that suggested that small amounts of magnesium may decrease slightly the stacking fault energy of aluminum. Although poly crystalline aluminum had about the same initial density of dislocations as the single crystals, the density of dislocations increased much more rapidly with strain in the polycrystals. This factor and the higher back stresses generated in the poly crystalline aluminum were the major factors responsible for the higher strength of the poly crystalline aluminum, As the magnesium content of the alloys was increased, the initial density of the dislocations also increased. Most of the alloy strengthening arose from this factor; alloying effects due to short-range order strengthening, Suzuki locking, Cottrell pinning, and so forth, were estimated to be quite small. The gveater rate of strain hardening in the alloys was deduced to be due primarily to the greater increase in the density of the dislocations with strain as the magnesium content was increased. It is the purpose of the present investigation to shed additional light on the average plastic behavior of a grain in a polycrystalline aggregate, by analyses, based on dislocation theory, of appropriate experimental test results. These deductions when compared with those from single-crystal data will then serve to illustrate the major items of difference between the plastic behavior of single crystals and the average behavior of a grain in a

Jan 1, 1963

By C. Laird, C. E. Feltner

An investigation into the effect of a material's slip character on its high strain fatigue properties has been carried out using copper and Cu-7.5 wt pct A1 as representative wavy and planar slip mode materials, respectively. In copper, the constant term and exponent in the Coffin-Manson equation, ?EpNf1/2 = const, are unaffected by the temperature of testing or the history of the metal. On the other hand, in Cu-7.5 wl pcl Al, while the exponent is invariant, the constant is increased with respect to copper and increased further with decrease in temperature. The life in Cu-7.5 wt pct A1 is double that of copper at room temperature and about four times at 78°K. Fractoflaphic studies indicate that these diffevences in life are associated with the early stages of cracking. In copper, severe surface rumpling provides crack nuclei at pain boundaries independent of' testing temperature or the history of the metal. In Cu-7.5 wt pct Al, the planar slip mode of deformation prevents grain boundary folding; crack nucleation is therefore mainly transgranular and the increase in life with respect to copper is associated with a prolonged linking-up stage of such transgranulay cracks. At the lower temperature the increased difficulty of cross slip inhibits multiplication of trans-granular cracks and retards the linking-up process, giving a further enhaancement in life. It is expected that such behavior will be found general in materials of wavy and planar slip mode, respectively. STAGE II crack propagation in high strain fatigue takes place by a repetitive process of crack tip blunting in the tension part of a fatigue cycle followed by resharpening of the crack in the compression part.1-3 This mechanism has come to be called the "plastic relaxation process".3 At very high strains (lives to failure less than 103 cycles), most of the life of a specimen is spent in crack propagation by the plastic relaxation process.4,5 Since the differences in the cyclic strain hardening behavior of metals and alloys are comparatively small in this strain range,6,7 the amount of blunting at a crack tip depends primarily on the applied strain amplitude. The rate of crack propagation in this life range is therefore nearly constant with respect to material and temperature of testing. In the longer life portion of the high strain fatigue range (l03 to 103 cycles to failure), a considerable fraction of the lives is spent in crack initiation and Stage I growth. Grain boundaries have frequently4,5,8 been found to be the sites for this growth which is also associated with a surface folding process.4'5 Such folding behavior may also be general in any material having a grain structure and capable of plastic deformation. It has therefore been suggested475 that the universality of the Coff in-Manson law,9'10 constant,* where ?Ep is the plastic strain range and Nf the number of cycles to failure, is reflected in the approximate invariance of both the crack initiation and propagation behavior. It happens that, in most investigations of the phenomena associated with failure,4,5,8 materials with a wavy slip mode have been used as vehicles for the studies, or else "normally" planar slip mode materials have been tested under conditions giving rise to wavy glide deformation, e.g., stainless steels cycled at high temperature.'' The purpose of the present investigation was to determine whether or not different cracking phenomena would occur when the slip mode of a material is planar and if the associated life to failure would be different than that of a wavy slip

Jan 1, 1968

By W. C. Phalen

INTRODUCTION NOBODY will dispute the fact that the conservation in every legitimate manner of our valuable high-grade phosphate-rock deposits is a present-day problem of importance. The table and curve, given herewith, show. that during the past 10 years the exportation of high-grade rock has averaged very close to half the total output of the entire country. The bulk of this exportation is from Florida, for obvious reasons. It is plain that the deposits in this State, more particularly, are being wastefully depleted under a system of selecting the cream of the product for exportation to Europe, leaving the comparatively low-grade rock, running from 65 to 70 per cent., and under, in bone phosphate of lime, for our own n fertilizer manufacturers to work up when all the best rock is gone. In this paper the writer has endeavored to make a point of describing in some detail the important methods of production and conservation in Tennessee. These ought to prove of educational value to our American agriculturists and fertilizer manufacturers, and should result in a demand for the highest-grade rock, both for direct application to the soil and for use in making acid phosphate. It is certainly evident that the European

Jan 10, 1916

By M. Metzger, J. C. Bilello

Microyielding in 99.999 pct Cu occuwed in two distinct parabolic microstages and was substantially indeoendent of grain size at the relatiz~ely large grain sizes stzcdied. The strain recouered on unloading was a significant fraction of the forward strain and was initially higher in a copper-coated single crystal than in poly crystals. Results were interpreted in terms of cooperative yielding and short-range dislocation motion activated otter a range of stresses, and a formalism was given for the first microstage. It was suggested that models involving long-range dislocation motion are more appropriate for impure or alloyed fcc metals. THERE are still many unanswered questions concerning the degree and origin of the grain size dependence of plastic properties. In the microstrain region, a theory of the stress-strain curve proposed by Brown and Lukens,' based on an exhaustion hardening model in which the grain boundaries limit the amount of slip per source, accounted for the variation with grain size of microyielding in iron, zinc, and copper.' This theory assumes N dislocation sources per unit volume whose activation stress varies only with grain orientation. Dislocations pile-up against grain boundaries until the back stress deactivates the source, which leads to a relationship between the axial stress and the strain in the microstrain region given by: where G is the shear modulus, D the grain diameter, a the flow stress, and a, is the stress required to activate a source in the most favorably oriented grain.3 If this or other grain-boundary pile-up models are correct, then the reverse strain on unloading would be much larger for a polycrystalline specimen than for a single crystal. Also, the microplasticity would become insensitive to grain size if this could be made larger than the mean dislocation glide path for a single crystal in the microregion. These questions are examined in the present work on polycrys-talline copper and a single crystal coated to provide a synthetic polycrystal. EXPERIMENTAL PROCEDURE Tensile specimens 3 mm sq were prepared from 99.999 pct Cu after a sequence of rolling and vacuum annealing treatments similar to those recommended by Cook and Richards4-6 to minimize preferred orientation. Grain size variation from 0.05 to 0.38 mm was obtained by a final anneal at temperatures from 310" to 700°C. Dislocation etching7 revealed pits on those few grains within 3 deg of (111). For all grain sizes dislocation densities could be estimated as -107 cm per cu cm with no prominent subboundaries. The single crystals, of the same cross section, were grown by the Bridgman technique with axes 8 deg from [Oll] and one face 2 deg from (111). An anneal at 1050°C produced dislocation densities of 2 x 106 cm per cu cm and subboundaries -1 mm apart in these single crystals. A Pb-Sn-Ag creep resistant solder was used to mount the specimens, with a 19 mm effective gage length, into aligned sleeve grips fitted to receive the strain gages. All specimens were chemically polished and rinsed8 to remove surface films just prior to testing. The synthetic polycrystal was made by electroplating a single crystal with 1 µ of polycrystalline copper from a cyanide bath. Mechanical testing was carried out on an Instron machine using two matched LVDT tranducers to measure specimen displacement, the temperature and the measuring circuit being sufficiently stable to yield a strain sensitivity of 5 x 107. At the crosshead speeds employed, plastic strain rates were, above strains of 10¯4, about 10¯5 per sec for polycrystalline specimens and 10-4 per sec for the single crystals. Plastic strain rates were an order of magnitude lower at strains near l0- '. A few checks at strain rates tenfold higher were made for reassurance that the initial yielding of polycrystalline copper was not strongly strain-rate dependent. Test procedures followed the general framework outlined by Roberts and Brown.9,10 An alignment preload of 8 g per sq mm for polycrystals, and 2 to 4 g per sq mm for single crystals, was used for all tests. These gave no detectable permanent strain within the sensitivity of the present experiments; although at these stress levels, small permanent strains are detectable in copper with methods of higher sensitivity.11 12 stress and strain data are reported in terms of axial components. RESULTS General. The initial yielding is shown in the stress vs strain data of Fig. 1. For polycrystals, cycle lc, the loading line bent over gradually without a well-defined proportional limit, and almost all of the plastic prestrain appeared as permanent strain at the end of the cycle. The unloading curve was accurately linear over most of its length with a distinct break indicating the onset of a significant nonelastic reverse strain at the stress o u, indicated by the arrows. The yielding in subsequent cycles, Id and le, had the same general character. The single crystal behavior, shown to a different scale at the right of Fig. 1, was different in that initially the nonlinear reverse strain was unexpectedly much greater than for polycrystals. It should be noted that these soft crystals had a small elastic

Jan 1, 1970

By Tony B. Szwilski, K. Unrug

INTRODUCTION Since the introduction of longwall coal mining systems, reliable predictions of roof support requirements at the face and the roof caveability in the gob area have been major contributors to the success of the longwall face by means of safety and face productivity. That is, the successful operation of a longwall is well-served by good regular caving of the gob. In recent times, with the advent of increased coal face mechanization and capital investment, the evaluation of the feasibility of longwall mining has become essential. In the United States, where a face unit for a face length of about 150 metres may cost around $6 million, a quantitative system that would assist in selecting the best equipment for the coal would prove extremely beneficial. There have been many such varied investigations in the past few years. A vast -amount of work has been invested principally by West Germany [3, 7, 8, 91 , Poland [I, 101 , United Kingdom [4, 5, lo], France [4], and South Africa [4]. It is the object of this paper to review this previous research work and give an outline that may be used as guidelines for long- wall evaluation. Essentially, for the initial design phase for a longwall system, account must be taken of the geometry of the coal panel, its position relative to the surface (depth), direction of the coal cleat system, faults and in-situ stresses and other neighboring workings in the same coal seam and other seams both above and below. The advance of the coal panel disturbs the stress field and in doing so creates an abutment zone around the face. At this stage the condition of homogeneity of the surrounding rock mass does not apply. The magnitude of the rock strata pressure may exceed the ultimate strength of the rocks and create zones of clastic, plastic and elastic material, the limits of which are difficult to determine. The collapse of the gob and resulting expansion of the displaced waste roof rock, create a statically undefined support complicating an already unclear rock structure. For example, it is often a point of debate whether, indeed, the vertical strata pressure develops to regain the original magnitude of virgin stress. Under these post-failure circumstances an analytical approach based on simplified and idealized assumptions can only be considered a very general approximation. Theoretical concepts, however, may be adequately supplemented by empirical methods that are based on numerous underground observations and surveys [3, 4, 7, 8]. These methods employ the use of rock indices that very handily correspond to the competence of the roof rock mass. Scale model work [3, 41 , using equivalent materials representing the surrounding rock mass within the coal seam zone, have given valuable qualitative and sometimes quantitative data in addressing the behaviour of the rock mass around longwall panels. To characterize the state of art of caveability predictioqthe principal concepts will be reviewed with special emphasis placed on practicality for the planning of longwall operation. It has been the general observation of the authors that many of the literature surveys published in English often neglect reference to other international mining literature. It is with this point in mind that an overall review has been written including mining concepts identified with the principal coal mining countries. THEORETICAL CONCEPTS Arching Theory For the development of this theory, assumption has been made that an extracted height, h, in a coal seam results in an extracted panel of width, w . Also, the coal seam is horizontal and the rock strata of both the roof and floor are homogeneous. The primary (virgin) stress distribution will change in the roof as well as the floor. As a result of lack of support caused by the excavation (in the gob area) an additional load is developed due to the redistribution of the load around the sides of the panel, referred to as the abutment, R, where: [ ]

Jan 1, 1982

By Robert Rhea Goodrich

This research was done partly in the non-ferrous laboratory of the Department of Metallurgy of Columbia University, under the direction of Dr. Edward I?. Kern, and completed elsewhere. Acknowledgment is due to Prof. Arthur L. Walker, Dr. Edward F. Kern and Dr. William Campbell of the Department of Metallurgy, for their kind advice and for the inspiration derived from their instruction. This report is given under the following heads: Petrographic Description (Microscopic Study); Sampling and Preparing Ore for Treatment; Chemical Analysis; Treatment of Ore. Petrogeaphic DescRiption Texture: variable. Fine to medium mixed aggregate. Original Structure: Obscurc. Secondary structure: Fractured; healed. Mineralogy (Minerds are grouped for interpretation purposes and are arranged, in each group in approximate order of abundance)

Jan 1, 1916

By John C. Draper

The principal object of an underground coal mine transportation system is to move coal from the face where it is produced to the outside of the mine where it is prepared for market. In addition to the movement of coal, a transportation system must also move supply materials to the inside ; it must move men in and out of the mine ; and it must move rock and other debris out of the mine for disposal. Usually, mine haulage is divided into three categories named for the various areas of the mine served : 1) Pace Haulage. This is used at face from the mining machine to the intermediate transport system. 2) Intermediate or Secondary Haulage. Generally this is used between face haulage and main haulage. Sometimes this is merely an extension of the main haulage. 3) Main Haulage. This extends from the secondary haulage to the outside and is usually either a track or conveyor system, sometimes a combination of both. Transportation modes of coal in the various areas pose different problems, but the whole system must be synchronized. For instance, at the face the coal should be removed quickly from the various places to facilitate the movement of machines, whereas the intermediate system just passes the same coal on to the main transportation system. Selection of the transportation system must be based on the seam height, mining methods used to extract the coal, capacity required, ease of coal handling, and haulage efficiency. When driving rooms, mine cars can be used. They often simplify supply haulage and rock handling because they can also handle these items. Conveyors could be used and would have a greater haulage capacity but they cannot handle supplies easily or segregate the rock. When using a different mining method, such as longwall, mine cars cannot be used because there is not sufficient space to move the cars at the face nor can the cars haul the coal without delays which would cause excessive losses in production. As for ease of handling

Jan 1, 1981

By Morris Cohen, Robert C. Ruhl

Fe-Ni-B alloys were inresligated by X-ray diffraclion after splat quenching. Although this rapid cooling did not produce a measurable supersaturation of dissol1ed boron in either binary Fe-B or Ni-B alloys, a marked increase in dissolved boron was achieved by the splal quenching of lernary Fe-Ni-B alloys. Boron additions up to 2.0 wl pcl to Fe-13Ni and Fe-24Ni alloys cause an increase in retained austenite from 0 to 59 pet and to 92 pet, respectively. The martensitic phase in the Fe-13Ni-9 at. pct B alloy is .found to conlain about 0.6 at. pet interstitial boron, as evidenced by the tetragonality of this phase, and about 3.6 at. pct substilutional boron, us deduced from the lattice paratrieler decrease, the balance of the boron being precipitated as (Fe,Ni)aR. The austenitic Fe-Ni-B plznses also contain both interstitial and substitutional boron. Iron-Boron System. The phase diagram and related information about the solid solutions and intermediate phases in the Fe-B system are given by ansen,' Elliott.2 and Pearson.1 The equilibrium solid solubility of boron in both ferrite and austenite is quite small: the maximum solid solubility of 0.02 wt pct B (0.11 at. pct B) occurs in iron at the eutectic temperature of 1150°C. while the maximum solubility in a iron is less than 0.01 wt pct.l There is disagreement in the literature as to whether these solid solutions are substitutional or interstitial. Based on the measured activation energy of boron diffusion in iron, it appears likely that boron moves interstitially in austenite. 4 However, this observation does not rule out the possibility that some of the dissolved boron may also occupy substitutional sites in this phase. Investigations of internal friction of boron in iron have suggested that boron is interstitial there.' Shevelev, 5 on the other hand, reports a decrease in the ferrite lattice parameter with dissolved boron content, thus indicating a substitutional solution. Unfortunately. Shevelev's methods and analysis are unclear. Goldhoff and spretnak6 have measured the lattice parameters of pure iron and an Fe-0.005 wt pct B (0.027 at. pct) alloy at both room temperature (ferrite) and from 920° to 1200°C (austenite). They reporte: a lattice contraction in the ferrite of 0.0003 ± 0.0002 due to boron, thus indicating a predominately substitutional solution. Appreciable (0.0010 to 0.0060) lattice contractions were found in boron-containing austenites, but these effects were much larger than could be accounted for by the substitutional solution of all the boron present. Nickel-Boron System. Elliott 2 gives a summary of thephase diagram and recent work on this system. The solubility of boron in nickel reaches a maximum of 0.03 wt pct at the eutectic temperature of 1080°C. Iron-Nickel System. ansen' presents the equilibrium diagram for this system and also discusses the metastable austenitic and martensitic phases along with the a=? transformations. The lattice parameters of Fe-Ni ferrites have been recently redetermined by Abrahamson and Lopata.7 Their data, Fig. 1, show an unusual change in slope at about 1.7 at. pct Ni. Very few measurements of the lattice parameters of Fe-Ni martensites are available in the literature. The values of Roberts and Owen8 are considerably higher than those measured in the course of the present work: they find that a, is constant at 2.874? from 8 to 30 at. pct Ni. Both the slope change in the ferrite parameters and the occurrence of a maximum plateau in the marten-sitic lattice parameters vs composition denote the

Jan 1, 1970