By Yasuo Ojima

A new copper continuous converting process was investigated to evaluate the possibility of its application in the commercial operation. The tests were performed both in the laboratory and in pilot plant scale. Bath smelting process with the use of the top submerged lance technology was applied in these tests. Furnace shape was modified to a lengthwise eylindrical one with a settling area. The furnace monitor was put in the settling area to check the furnace from inside, FeOx-Si02, FeOx-CaO and FeOx-CaO-Si02 based slag systems were used to check their efficiency, The optimum slag chemistry to have good metallurgical results was discussed and FeOx-CaO system with some Si02 content turned out to be preferable although it has not been practically used, In this pilot plant test feeding rate of I tIH of solid grain matte was charged consecutively for two weeks and continuous converting could be done successively. This process is expected to overcome the problems of existing processes and be easily applied in existing plants.

Jan 1, 2003

By Jian Yang

The mechanism of resulfurization in the desulfurization process with magnesium vapor produced in situ by aluminothermic reduction of magnesium oxide was clarified in the present work. The influences of various operating parameters on the resulfurization were studied and the methods that could prevent resulfurization were proposed. There are two kinds of mechanisms of resulfurization in the desulfurization process with magnesium. One is decomposition of the desulfurization product of MgS under the inert atmosphere. The other is oxidation of MgS under the oxidative atmosphere. Under the present experimental conditions, lowering operating temperature and oxygen partial pressure in the atmosphere could effectively prevent the resulfurization. Adding CaO onto the melt surface was an effective method for preventing the resulfurization due to transformation of the desulfurization product of MgS into the more stable compound of CaS. Since addition of the activated charcoal powders greatly decreased the transfer rate of oxygen in the atmosphere to the melt surface, it also reduced the resulfurization remarkably.

Jan 1, 2006

By Won C. Park

Experiments showed changes in the mineral content of dolomitic oil shale at temperatures and exposure times which bracket conditions encountered during in situ retorting. Laboratory results correlate with cores from a spent in situ retort at Occidental's Logan Wash test site at Garfield County, Colorado. Dolomite, CaMg(CO3)2, decomposes rapidly to form periclase, MgO, calcite, CaCO3, and CO . Both calcite and periclase are intermediate products that can be stabilized by CO atmosphere at lower temperatures, while steam accelerates the formation 2 of silicates. The decarbonation of calcite appears to involve a direct reaction with both quartz and periclase in forming these silicates. Decarbonation preceeds the formation of akermanite, Ca2 MgSi 207, and diopside, CaMgSi 206, within several hours of heating and is followed by the nucleation of forsterite Mg2SiO4, and monticellite, CaMgSiO4. Under in situ retorting conditions, akermanite and diposide are the major minerals above 800°C. Equilibrium is not attained within 200-300 hours. In situ retorting temperatures above 800°C for extended periods of time should reduce potential ground water leaching by the formation of silicate minerals. These silicates are less soluble than free lime, magnesium or alkali oxides. There is a corresponding decrease in the natural pH of these silicates from approximately 12 down to 7.5 to 9:

Jan 1, 1981

By A. C. Neiva

An energy-dispersive x-ray fluorescence spectrometer was assembled with the aim of analysing alloys and corrosion products of artistic, ethnological and archaeological pieces. The spectrometer is semiportable and consists basically of an 60kV/1.5mA X-ray tube with W anode and a Si-drift X-ray detector with Peltier cooling, with no need of liquid nitrogen. It was used for the analysis of the alloys and occasional corrosion products of several metallic pre-Hispanic pieces of the Museum of Ethnology and Archaeology of the University of São Paulo. Special care was taken to account for the contribution of spurious radiation from both the Pb primary collimator and the Zr detector collimator. The main components of most alloys were Au, Ag and Cu, but Pb, Ca, Fe and other elements were also identified. The characterization of the alloys and corrosion products is important for the subsequent conservation of the collection.

Jan 1, 2006

By Georges J. Kipouros

Anhydrous neodymium trichlorids (NdCl3), containing ~1 weight percent neodymium oxychloride (NdOCI) was prepared by the dehydration of neodymium trichioride hexahydrate (NdC13.6H2O). Dehydration of the hexahydrate was conducted in three steps. First, the hexahydrate was slowly heated in air to about 250 °C until all the low temperature water of crystallization was removed. In the second stop, the neodymium hydroxychloride (Nd(OH)2C1) fanned in the first step was decomposed by heating under argon to 430 ° C. Finally the salt was ground and then treated with HCl gas at 330 °C until practically all of the NdOCl was converted to NdCl3.

Jan 1, 1992

By T. T. Chen

Canadian Electrolytic Zinc has developed the "cement-stabilization of jarosite residue" Garofix) process to stabilize zinc plant jarosite residues for disposal. The cement-jarosite mixtures cure quickly, have good mechanical strength and low hydraulic permeability; they possess good neutralizing capability and chemical stability. In the jarofix process, Portland cement partly decomposes jarosite to form (SO4MOH)12.nH2O, ferric hydroxide and an alkali sulphate. Approximately 40% of the jarosite reacts in mixtures containing 30% cement. The jarofix product also contains various Ca-Al-Fesilicate-sulphate-hydrate phases and gypsum, which bond the individual particles together imparting mechanical strength and reducing the permeability. Most of the reactions take place in the first few hours of curing. Ammonium jarosite is slightly more reactive than sodium jarosite but releases NH3 gas; water-soluble Zn in the jarosite residue is stabilized in the cement reaction products.

Jan 1, 1996

By S. Djaroudib

Keywords: iron recovery, hematite, hydrolysis, polyvinylpyridine The precipitation of hematite (Fe2O3) from ferric chloride media at ambient pressure and at temperatures below 100°C was studied as part of a program to recover a marketable iron product form metallurgical processing streams and effluents. Hematite was formed in preference to ferric oxyhydroxides (e.g. ß-FeO?OH) by controlling the precipitation conditions, especially by adding Fe2O3 seeds. The extent of the hydrolysis reaction was found to depend primarily on temperature and on the free-acid concentration. As to the latter, the controlled addition of an adsorbent of free acid, in our case the anionic resin polyvinylpyridine (PVP), was shown to allow for the nearly complete removal of iron as readily filterable Fe2O3. The hematite product typically contains = 63% Fe and = 1.5% Cl, and its composition does not change appreciably upon repeated cycling using regenerated PVP.

Jan 1, 2005

By S. Ajima

The Naoshima Smelter and Refinery is the most important copper operation of Mitsubishi Materials Corporation. There are a Mitsubishi Continuous smelter and a conventional type of copper tankhouse. The continuous smelter with 240,000 mtpy of anode production was commissioned in May 19914 replacing two existing smelters, i.e an original Mitsubishi Process line and a conventional reverberatory furnace line. In July 1992, the copper tankhouae was expanded for the purpose to close the gap of production capacity between the smelter and the tankhouse. The cathode production capacity was increased from 13,800 to 15,800 mtpm. By these plant modifications, the distribution of minor elements was significantly changed and the impurities load is getting on increase reflecting recent shortage of clean copper concentrates supply. The paper discusses the distribution of minor elements and the impurity control strategy at the smelter end the refinery.

Jan 1, 1995

By J. R. Goode

Up to one half of neodymium and praseodymium production, key ingredients in permanent magnets, is produced illegally. About 60% of cobalt production, critical in lithium-ion batteries and other applications, comes from central African states, and much of it is produced illegally. Tantalum, important in modern electronics, is also primarily sourced from central Africa and, again, much of it illegally. Illegal mineral production, as exemplified here, is often used to fund armed conflict. Furthermore, it is typically conducted with scant regard for human rights and environmental protection. It also leads to depressed prices which in turn limits the possibility of legitimate producers entering the market. Systems of traceability and provenance, along with cooperative supply chain participants can limit the production of illegitimate material and thereby improve conditions in the countries of origin and reduce downward pressure on prices.

By Gary R. Adams

Coating thickness control is typically difficult with touch-up solders for galvanized steel, and corrosion properties and abrasion resistance are sometimes poor. This paper reports on progress in ILZRO-sponsored research to develop an improved touch-up solder. Encouraging results were achieved in torch soldering trials with zinc-tin based alloys. Mouldability and coating thickness control were achieved over a practical working temperature range in which the solders consisted of a viscous mixture of solid primary zinc phase particles in a liquid zinc-tin eutectic matrix The mouldability was dependent on the microstructure of the starting material, and optimum structures could be obtained through control of casting solidification rates and/or by the addition of small amounts of copper. Hardness and preliminary corrosion test results showed potentially good mechanical and corrosion behaviour. The absence of toxic materials ensures environmental friendliness. Comprehensive performance testing is continuing on selected experimental zinc-tin-copper touch-up solders.

Jan 1, 1992

By Richard A. Leiby

The recycling of lead-acid batteries in the United States has become a challenge as to how to balance ever increasing environmental regulation and cost with efficient operations. East Penn's captive secondary lead smelter has developed into a recycling facility producing lead, polypropylene, sulfuric acid, ammonium bisulfite, and non-hazardous discard slag. The emphasis has been to design a facility to comply with environmental regulations, to eliminate wastes, and to produce products, while at the same time, continuing to supply the company's battery manufacturing raw material needs.

Jan 1, 1993

By Jacques J. Eksteen

Metallurgical accounting around toll treatment smelters pose a number of challenges. This paper reviews the requirements for good sampling practice, and how conflicting requirements for good furnace operation and design often makes reliable closure of the metallurgical balance tenuous at best. Typical physical causes of variance and bias will be identified. The propagation of error (in the form of variance) will be discussed for a copper smelter.

Jan 1, 2006

By M. Pakala, Z. Fan, Ray Y. Lin

Deposition of hard chromium coatings using electrodeposition is accompanied by emission of hexavalent chromium mists which is a carcinogenic. Hence alternative chromium deposition technologies are being investigated. Sputter deposition is a strong candidate to economically deposit hard chromium coatings in an environmentally friendly way. Chromium coatings of 2-3 µ m thickness were deposited on plain carbon steel coupons using RF magnetron sputter deposition. Depositions were carried out with 0 to 22 vol% nitrogen in the plasma. Structure of the coatings was studied using x-ray diffraction analysis With increasing nitrogen contents, formation of the two nitride phases was observed. The pure chromium phase was detected in coatings with up to 7% nitrogen in the sputtering gas. The solid solution of nitrogen in the pure Cr phase coating was identified by shifts of Cr x-ray diffraction peaks to higher d-spacing. The microhardness of the coatings deposited at a substrate temperature of 200°C showed an increase in hardness with increasing nitrogen content from 600 kgf/mm2 (5.9 GPa) at 0% nitrogen to I250 kgf/mm2 (I2.25 GPa) at 9.5 % nitrogen and a subsequent decrease in hardness to I 100 kgf/mm2 (11 GPa) beyond 9.5 % nitrogen in the sputtering gas. This corresponds to the formation of the hard Cr2N phase, at 9.5 % nitrogen, and CrN phase, at I5.7 % nitrogen. The reported bulk hardness values of Cr2N and CrN are I600 kgf/mm2 (I5.7 GPa) and I 100 kgf/mm2 (11 GPa) respectively. For pure Cr phase coatings, there is a slight increase in hardness for coatings deposited at 7. I % nitrogen from that without nitrogen in the sputtering gas. This could possibly result from the solid solution strengthening of the Cr lattice by nitrogen. For films deposited at 200°C, phases of the deposited films seem to be the overwhelming factor in controlling the microhardness.

Jan 1, 1998

By Garry W. Warren

The brass foundry industry produces a significant amount of waste sand containing Cu, Zn and Pb which is often classified as a hazardous waste due to Pb content. The potential application of a hydrometallurgical process to treat the sand by extracting metal values and thus detoxifying the material has been investigated. The process involves leaching of metal values followed by cementation. The emphasis of this investigation was on the leaching step, although some preliminary cementation experiments have been performed. In order for any alternative treatment scheme to be successful, the smaller size fractions of the sand must be addressed. Experiments have been performed on five individual size fractions using various lixiviants HCI, acetic acid and HCI/NaCI. Cu extraction was found to be slower than either Zn or Pb. Results obtained in this investigation indicate that copper is present in two forms, an oxide form which dissolves rapidly and is insensitive to the level of oxygen, and a less soluble form, probably metallic which dissolves more slowly and requires an oxidizing agent. The presence or absence of oxygen had no influence on the rate of Zn dissolution indicating that zinc is present mostly in oxide form. Toxicity Characteristic Leaching Procedure (TCLP) tests showed that residues could be produced which meet the toxicity limit for lead. Preliminary cementation experiments have also demonstrated the feasibility of Cu and Pb recovery.

Jan 1, 1991

By Moto Goto

Today, Pierce-Smith converters, coupled together with various types of smelting units, are used in most of the world's smelters. However, due to the "batch" processing nature, and problems associated with fugitive emissions during the transfer of melt and blowing stages, this arrangement will unlikely be adopted in future smelters. Modern day alternative processes include the Mitsubishi Process, Outokumpu Flash Smelting and Flash Converting Process, the Noranda Process, and the Ausmelt Process, but only the Mitsubishi Process is a "truly continuous" smelting and converting operation, producing a constant flow of blister without tapping, and is economically proven by long term commercial operations. This paper reviews recent advances in modern continuous converting technologies, with a special section devoted to operation of the "first standalone Mitsubishi C-furnace" coupled together with a Noranda Reactor, at Port Kembla Copper Pty. Ltd. in Australia.

Jan 1, 2003

By V. I. Lakshmanan

The demand for elements such as nickel, cobalt, titanium and gold in various applications has increased significantly. Innovation to recover these elements now plays a major role in metallurgical processes as established technologies have challenges in treating the types of ores that are available while meeting the increasingly stricter environmental regulations. Alternative chloride based processes have been developed that can be used to recover the value elements from the available feed stocks with potentially lower environmental impact. Chloride-based hydrometallurgical processes have several advantages, including higher leachability of complex ores/tailings and relative stability of chloro-complexes of the metals. Process Research ORTECH Inc. (PRO) has developed mixed-chloride process flowsheets, where innovative solvent extraction process steps are used for the separation of nickel, cobalt, titanium and gold from their respective chloride solutions. This paper will discuss the potential aqueous chloro-chemistry of these metals and separation reaction mechanisms involved in the solvent extraction process.

By O. Norman Lotter

There are many scales of innovation in the pursuit of concentrator performance improvement, including paradigm change, inventive change and incremental change. All are important, but the last is low risk, low cost and has a relatively high probability of success, given the right metallurgical skills. Seeking continuous improvement is also essential to ensure that performance does not decline over time due to ore type changes, personnel changes, equipment wear and other factors. When properly implemented, these small gains offer a very high rate of return for the project cost because they are made from marginal, not total, operating costs of the plant. To be effective this approach requires plant trials that use designed structure and appropriate statistics to test the observed differences arising from the old and new process treatments, be they a change in flotation reagent, in grind, pulp density, etc. However the pursuit of small but financially significant performance gains is often regarded as fruitless because of the range of variance in plant data, and the consequent difficulty of ‘proving’ that a benefit has been achieved. Opportunity for improvement is thus sometimes relegated to the realm of the impossible, or at best, treated with skepticism. Operations managers prefer to look for the larger gains, which are easier to demonstrate and prove. Unfortunately, these are seldom to be found; rather, a large gain can be more easily made by executing a series of small recovery improvements that are together equivalent to the ephemeral single large gain. In this paper we advocate a policy of continuing improvement driven by rigorous performance testing protocols and a formal ‘risk analysis’ approach to judging the efficacy of changes implemented in the plant. Following these simple procedures allows rational decisions to be made on the basis of quantifying risk and reward. In particular we consider the choice of hurdle rate for decision-making which best balances risk and reward. It is shown through case studies from actual industrial practice that this approach is practical and delivers significant financial value to the operation.

By Noel A. Warner

Modern steelmaking is based on direct use of oxygen in high intensity batch reactors. A totally new approach is proposed in this paper, based on the view that pursuit of high intensity is unlikely to lead to successful coal-based continuous steelmaking. By substituting carbon dioxide and water vapor as the oxidants rather than using oxygen directly, the intensity is greatly reduced. Accordingly. subsurface formation of carbon monoxide bubbles can be avoided by careful manipulation of the three participating rate processes, gaseous diffusion, interfacial chemical kinetics and liquid phase mass transfer. Steelmaking can then be carried out without explosive ejection of molten droplets and the generation of micro-spray but rather in a controlled and fumeless fashion. The vital component is the introduction of generic melt circulation technology. Three melt circulation loops in series are envisaged. Starting with a composite feed of iron ore fines, pulverized coal and lime flux, a metallized solid raft floating on molten iron is propelled out of the ironmaking loop onto the first of two downstream steelmaking loops. In the first, a liquid slag is formed, primary decarburization is undertaken not with oxygen but rather with CO2 and H2O and the melt is desulfurized. The semi-product stream enters the third melt circulation loop, where open-channel decarburization is effected along with dephosphorization to yield a low carbon steel product. Alternatively, the melt leaves the last loop to irrigate a packed tower countercurrent to argon at around 100 mbar to continuously produce ultra-low carbon (ULC) steel.

Jan 1, 2003

By Patrick R. Taylor

A non-transferred arc thermal plasma assisted cyclone reactor has been designed, built and operated to evaluate its use in vitrification of wastes. Simulated waste (liquid, slurry or fine particulate) is injected near the plasma flame, where nearly instantaneous dehydration and calcination reactions happen. A non-transferred arc plasma torch was attached tangentially to the cyclone and is utilized as both an enthalpy source and to provide the gas velocities required to generate the cyclonic gas flow patterns. The closed top cyclone flow sends the solid particulates to the wall, where they are captured by a thin film of molten glass that is injected as a powder at a position lower in the reactor. The molten glass is then collected in a crucible. The feasibility of simulant injection directly into the flame zone and its effect on electrode lifetimes has been studied. Several candidate refractory systems have been evaluated for their suitability for extended use under the demanding conditions present in the cyclone reactor.

Jan 1, 2002

By H. Yin, T. Emi

"Advantages of gas/flux injection technology as materialized in the main stay unit processes for steelmaking are depicted covering hot metal pretreatment through secondary refining. Current status of micro-kinetic issues involved in the injection technology are reviewed including gas-in- metal, gas-in-slag, flux-in-metal, metal-in-flux and three-phase dispersion systems with reference to macro-kinetics. Key problems are briefly addressed to further develop injection technology for steelmaking processes.1. FROM PAST TO PRESENTApplication of gas injection to steel industry started in early 1950's when inert gas bubbling via stopper rod, lance, or porous refractory plug was practiced to make the temperature of steel melt in ladle uniform The gas bubbling in ladle was then extended to slightly removing hydrogen ti'om the steel melt tapped from Electric Arc Furnace (EAF) and Basic Open Hearth Furnace (BOH) when vacuum processing facilities were not popular. Later, oxygen gas injection via calorized steel pipe into molten steel bath in BOH Furnace was also put into operation to promote the decarburization to increase the productivity of the process. This line of development has been made in parallel with more profound processes, i.e, top blowing Basic Oxygen Furnace (BOF) for primary steelmaking and side blowing Argon Oxygen Oecarburization (AOD) vessel for decarburizing stainless steels.On the other hand, injection of fluxes into steel bath was first industrialized in Germany in 1960's, Primary objective was to desulfurize steel melt in ladle by injecting CaC2 or CaCrCaO mixture via lance under neutral slag cover with good success. Difficulties in injecting fluxes without clogging and rippling at a desired flux/gas ratio, and durability of injection lance were resolved in due time to bring forth many injection facilities to flourish for versatile refining operation. Top injection of fluxes from main oxygen lance to BOF was also industrialized as LDAC to promote early slag formation. A new process then emerged which injects oxygen gas and fluxes together through concentric annular tuyere, installed at the bottom of the BOE into steel melt. This process, developed in Germany [Oxygen Bottom Maxhutte (OBM)] and brought into maturity in USA (Q-BOP) and Japan in a large scale operation, became the predecessor of the combined blowing (top and bottom blown) BOF which dominates modern steelmaking."

Jan 1, 1996