Search Documents

By Chr. Krause

Within the scope the collaborative research centre 599 (Medical University of Hanover, University of Veterinary Medicine Hanover, University of Hanover) the behaviour of the degradation of magnesium materials as implants are investigated by using animal experiments (rabbits). Thus extruded cylindrical pins from the magnesium alloys MgCa0.8%, WE43 and LAE 442 were implanted intramedullary in the tibiadiaphyses. The implantation duration was 3 and 6 month. After the explantation 3 point bending tests were carried out to investigate the possible changes of the mechanical properties. Clearly changes in dependence of the implantation duration could be determined. The three magnesium alloys show a decrease of the mechanical resistance with an increasing implantation time. To evaluate the degradation process, wich is the reason for the changes, micrographs and element analyses (EDX) have been accomplished after the 3 point bending tests. The micrographs show for all used magnesium alloys corroded surfaces but no preferred corrosion on the grain boundarys. The element analyses show beside a layer which is rich in calcium and phosphorus an agglomeration of rare earth elements in this layer. With these results a using of magnesium alloys as a material for implants can be announced.

Jan 1, 2006

By Q. Li

"The precursor of In2O3 was prepared by hydrolysis precipitation/hydrothermal method using In(NO3)3 solution as the feed material and ammonium hydroxide as the neutralizing agent. The crystallinity, morphology and particle size of the products were characterized by SEM, XRD, BET and LPSA. The results showed that the hydrolysis product consists of an aggregate of cubic In(OH)3 particles with a short rod morphology. In the hydrothermal process, the structure, morphology and size of the particles changes through the mechanisms of Ostwald ripening and phase transition, respectively. When the hydrothermal temperature was less than 280 ?, the Ostwald ripening process took place, which changed the morphology of the particles from short rods to cuboids through dissolution-recrystallization. When the hydrothermal temperature was higher than 280 ?, the processes of Ostwald ripening and phase transition took place successively. Firstly, the morphology of the particles changed from short rods to cuboids through Ostwald ripening, and then, the phase transition from cubic In(OH)3 to orthorhombic InOOH occurred and the morphology of the particles changed from cuboids to polyhedron. INTRODUCTIONDue to its excellent electrical conductivity and optical transparency, indium tin oxide (ITO) film has been wildly used in flat-panel display, solar cell, antistatic coating and EMI shielding (Medvedovski et al., 2008). Indium oxide powder is one of the fundamental materials for preparing ITO film. Along with the development of ITO targets of both high density and large size, high quality indium oxide powders, such as single phase, nano-size, spherical morphology and mono-disperse, have been in high demand (Nakashima and Kumahara, 2002; Betz et al., 2006; Kim et al., 2007). The main preparation methods for indium tin oxide or indium oxide powders include chemical precipitation (Nam et al., 2001; Xu and Yu, 2007), melt atomizing-combustion (Chen et al., 2000) and spray pyrolysis (Ogi et al., 2009). Among them, chemical precipitation has been preferred, since it is simple, easy to control and suitable for industrial scale-up. In chemical precipitation method, indium oxide powders were prepared through the following steps: firstly, indium hydrate precursor was precipitated from an indium salt solution by neutralization using an alkali, such as ammonia; and then, indium oxide (In2O3) powders can be obtained from the precursor through calcination (Li et al., 2006), or solvothermal method (Lee and Choi, 2005), or hydrothermal processing/roasting (Xu et al., 2005; Chen and Li, 2007), respectively. However, the indium oxide powders obtained by direct roasting are polycrystalline, dispersable with a wide size distribution (Liao, 2006). The disadvantages of the solvothermal method are high cost, complicated after-treatment processes, as well as bad performances of the powders (Udawatte and Yanagisawa, 2000). Therefore, among three methods of obtaining indium oxide from the hydrolysis precursor, the hydrothermal process/roasting method is the most feasible to synthesize high quality In2O3 powder with uniform crystallinity and size (Kim et al., 2002; Zhu et al., 2004; Xu et al., 2005; Xu et al., 2005; Chen and Li, 2007; Seetha et al., 2009). However, current research on hydrothermal process-roasting method has been limited to the synthesis of a certain ITO or In2O3 powders under specific conditions. A systematic study on the phase transition, as well as the change of the morphology and size of the particles in the hydrothermal process is still missing. In this paper, the effects of hydrothermal processing on the mineralogy, morphology and size of products were investigated. The results showed that the evolution of crystal structure, morphology and size in the hydrothermal process was affected through the mechanisms of Ostwald ripening and phase transition successively. These results are novel and have guidance for improving the hydrothermal process for In2O3"

Jan 1, 2012

By J. L. Huisman, G. Schouten

After pyrometallurgy and hydrometallurgy, bio(hydro)metallurgy is the latest development in the ongoing search for efficient and economic metal winning processes. In addition to bioleaching, other biotechnology-based applications are getting more and more accepted. In this paper a number of proven and commercial processes will be presented that can be applied for nickel and cobalt recovery and refining. These processes are based on the ability of biomass to convert the redox state of sulphur compounds under ambient conditions. They can be applied to recover sulphate from effluents or SOx from off gases and convert it to H2S or dissolved sulphide that can be reused in production or effluent treatment. Not only does this minimize the costs on resources but it also reduces waste production and improves the quality of discharges even to the point where reuse becomes feasible.

Jan 1, 2005

By A. M. Bell

"Hallnor mine is in the township of Whitney, Porcupine district. To date, its production of gold has been second largest in the east Porcupine field. Ore was discovered in the property in 1936 by diamond drilling in overburdened country. This drilling was undertaken by Noranda Mines following the discovery of ore in conglomerate at Pamour 1 mile to the east.Milling commenced at the Hallnor in June 1938, and to the end of 1945 432,000 oz. gold had been produced from 889,000 tons of ore, giving an average recovery of 0.49 oz. a ton.The West mine of Pamour, the Broulan orebody, and the veins on the Hallnor and Bonetal are all parts of a mile long vein system that has been separated into three sections by cross faulting. In consequence, they could well have been described in one paper. In treating them individually the viewpoint obtained from each may lead to conflicting opinions, and any conclusions advanced in this paper on the general structure should be modified by the conclusions advanced in papers on the neighbouring properties.GENERAL GEOLOGYRock FormationsThe Hallnor orebodies occur within 400 feet of the contact between lavas and sediments, and may lie in either lavas or sediments. The lavas near the ore consist of flows of pillowed andesite and one flow of more acid and less sheared and chloritized lava locally named trachyte. These flows strike east-west and dip steeply. At the surface on the east side of the property the volcanics have been intensely altered to a massive carbonate rock having a north-south thickness in excess of 1,000 feet . This carbonate body extends west across the property with a plunge of 45° (Fig. 1)."

Jan 1, 1954

By Gordon L. Kidd

The object of this paper is to show the relations of the East Coulee coal area to the near-by Willow Creek, Wayne, Rosedale, and Drumheller areas, all being parts of the Drumheller field. The word ?area? is here used in a more local sense than that employed by Dr. J. A. Allan, whose. 'area' is rather comparable with the 'mining division' in British Columbia. I have drawn freely from the published information, particularly from Dr. Allan's report on the "Geology of Drumheller Coat Field, Alberta", and from Dr. E. Stansfield's paper on " A Chemical Survey of Alberta Coals", to whom thanks are due. The Drumheller field is served by branch lines of the two principal Canadian railways. The C.N.R. traverses the district by its Goose Lake line from Calgary to Saskatoon; and the C.P.R. by a line from Calgary to Acme and then southeasterly to Drumheller, where it effects a junction with the C.N.R., over which the C.P.R. has running rights as far as Rosedale. From Rosedale, a joint line built during the summer of 1928 extends about forty miles down the Red Deer river to the mouth of Bull Pond creek. From that point the C.P .R. turns more southerly to connect with the Bassano-Empress line. The C.N.R., it is expected, will eventually proceed eastward to connect with a transcontinental line. The joint line from Rosedale down the Red Deer river opened up the Willow Creek and East Coulee areas.

Jan 1, 1929

By E. H. Chown

Scattered outliers of the Chibougamau Formation and the more continuous Mistassini and Otish Groups lie unconformably on an Archean basement abutting the Grenville Front. All the Aphebian rocks are deformed and offset by faulting related to the Front. The older Chibougamau Formation is exclusively elastic in origin, whereas the two later, time-equivalent groups include carbonatedominated (Mistassini) and elastic (Otish) sequences. Known syngenetic mineralization within these formations is limited to various radioactive showings in the Mistassini and Otish elastics, and the iron formations of the upper Mistassini Group. Three distinct types of epigenetic mineralization occur within the sedimentary rocks; pitchblende fracture fillings in all types of rocks in the Otish Group, widespread Mississippi-Valley type galenasphalerite showings at certain levels in the Mistassini Group, and chalcopyrite-pyrite bearing veins in or near argillaceous horizons of the Mistassini Group and Chibougamau Formation. The Otish elastic basin is part of a large area of the central Ungava peninsula which contains a variety of radioactive showings, the most promising being of the unconformity type, The final control for many individual showings appears to be local physico-chemical changes within faults and fracture zones. The overall structural control is in part supplied by the faulting episode related to the Grenville Front, which in turn limits the mineralization to the depth zone appropriate for open fracturing. The lead-zinc showings exhibit a strong stratigraphic control as well as close ties to secondary porosity developed by f aulting. The ore solutions were probably derived during the low grade metamorphism of the formations. Chalcopyrite- pyrite veins have provi ded the only mine production (Icon Mine) to date. They appear later than the low-grade metamorphic fluid circulation, and deposition is related to favourable structures and stratigraphy. The veins are clearly related to major faults. Thus, whereas stratigraphic settings appropriate to individual types of deposits are important, an overall structural setting may be demonstrated for a wide range of mineralizations. Detailed structural interpretations of individual showings may be the most fruitful pursuit in developing a concrete prospecting model.

Jan 1, 1984

By A. Y. Senchenko, Y. V. Kulikov

"Different methods aiming at specific energy calculation and design of AG/SAG circuits are used in mining. They include JK DWT/SMC test, SAGDesign test and CWi/RWi/BWi tests. The simplest methods with no secret equations and giving energy required for grinding in kWh/t were proposed by F.?. Bond and J.H. Starkey. D.J. Barratt proposed to use results of CWi/RWi/BWi tests for AG/SAG mill sizing. The present paper gives an alternative for forecast of specific AG/SAG energy. The principle is similar to the theory proposed earlier and consists in cumulative AG/SAG energy calculation using indices of rod and ball grinding (RWi+BWi) without impact crushing index (CWi). Then total energy is divided between two grinding stages using special formulas based on extensive statistical information. The forecast indices of AG/SAG and ball grinding are similar to the SAGDesign testing results. Hereinafter the predicted indices are used for mill sizing of the whole grinding circuit. The method considered in the paper enables prediction of AG/SAG energy based on the test results according to Bond method. The proposed method version was not widely published earlier. The aim of the work was to elaborate cost-effective, reliable and accessible way to determine specific AG/SAG energy. At this stage of method development, it is recommended to use it only for works at preliminary Geometallurgy stage (Scoping, Pre-Feasibility). At design stage the obtained data should be confirmed by appropriate testing using alternative JK DWT/SMC and SAGDesign methods.INTRODUCTIONAppropriate crushing and grinding testing is required to design efficient comminution circuits. It is obviously important to obtain accurate information about ore hardness properties since the main energy consumption at the plant is associated with comminution processes. Moreover, it is required to apply the processes that make it possible to minimize operating costs and efficiently use capacity of the installed equipment installed.When studying ore hardness properties, it is required to take into account that breakage of the material is performed using different equipment. That is why accurate selection of the equipment and the circuit calculation without relevant testworks is impossible. Ideally, the testworks should provide answers to the following questions: determination of ore hardness properties, determination of specific energy consumption for comminution as well as obtaining of sufficient amount of statistically significant results from the tests. The results from crushability and grindability testworks in the first place provide assessment of ore hardness properties and in addition correlate with throughput of the respective equipment. The data obtained can be used for modeling of comminution circuits at the stage of the technology development"

Jan 1, 2016

By John Jiang, Brian R. Hart, Stamen S. Dimov, Aparup Chattopadhyay, Barun K. Gorain

"This paper presents a systematic approach to metallurgy diagnostics using an integrated gold deportment methodology developed for complex refractory gold and copper-gold ore bodies. Quantification of gold deportment for these ore bodies is a challenging task due to reasons such as lower grades, high variability of visible and invisible gold content in different sulphides and iron oxide phases, significant presence of disseminated and composite carbonaceous matters along with associations of various copper sulphide phases. Some case studies are presented in this paper to demonstrate the value of a high confidence gold deportment methodology in developing insights for problem diagnostics and to identify opportunities for metallurgical improvements. A holistic approach involving different fields of expertise is critical for successful development and delivery of solutions for complex ore bodies.INTRODUCTION Studies were initiated on various complex ore deposits and also on samples representing various process streams. These complex copper-gold single refractory, double and triple refractory gold ores are mainly composed of silicates and/or carbonates with moderate amounts of clay and mica, along with minor amounts of sulphides and organic carbonaceous matter. Variable proportions of visible gold and “invisible gold” (sub-microscopic gold) were noted in different mineral phases for various ore types and process stream samples. Invisible gold commonly occurs as solid solution or as colloidal-sized particles in different sulphides and other phases for different refractory ores. The dominance of invisible gold and presence of highly preg-robbing along with finely disseminated carbonaceous matters adversely affects gold recovery in flotation and leach circuits for most of these double and triple refractory ores. This paper discusses applications of an integrated gold deportment technique developed for different types of gold and copper-gold ores, namely, complex copper-gold, double and triple refractory gold ores (Chattopadhyay & Gorain, 2014; Chattopadhyay et al., 2016). Various process streams from flotation and gold leaching circuits were investigated. Different concentrates and tailings samples from flotation circuits whereas feed and discharges from pressure oxidation (POX) and carbon-in-leach (CIL) residues were used from gold processing circuits."

Jan 1, 2017

By Dave M. Jakelski, Gerhard W. Heinrich, Peter F. Wells, Daniel F. Suarez, Jamie B. Beauchamp

"A need for increased copper concentrate production and for less nickel contamination in that concentrate at Falconbridge's Strathcona Concentrator during 1993 required the installation of a third flotation column and improvements in the operation of the existing circuit. Innovations in wash water distributor and launder design were fundamental in achieving objectives on a new 3 meter diameter column. Minnovex plug-type spargers were tested on a 2.1 meter diameter column in order to reduce maintenance requirements. The paper details the measures taken to enhance column flotation circuit performance and the results obtained.IntroductionFalconbridge's Strathcona Mill receives 10% of the ore feed from a rich copper zone in the Strathcona mine. This ore typically grades 7% copper and 1 % nickel and, because of its high copper content, it is processed in a separate circuit ('C' circuit) which consists of conventional grinding, rougher flotation with the concentrate being treated with lime to pH 12.3 and cyanide followed by column flotation. The columns are operated with mechanical flotation scavengers and the scavenger concentrate is returned to the column feed. Testwork conducted in 1991 showed that the original flotation column (Column 2) could only produce 5.5 mtph of concentrate with less than 0.5% nickel (Figure 1).Between 1991 and spring of 1993, production was increased at times by open circuiting the scavengers. Metallurgical improvements were obtained by improving the wash water distributor of Column 2 and by wash water sprays in conventional cells (1 ). However, the scavenger concentrate assayed 0. 7 -0.8% nickel and was not acceptable for long term operation. When Copper ore production targets were significantly increased for 1993, it became clear that an additional flotation column was required. The new flowsheet employs mechanical scavenger cells on the column tails as in Column 2 circuit (Figure 2). A -parallel configuration was chosen as pulp solids fraction has been shown to be a critical variable and the second column in series would receive a lower density feed."

Jan 1, 1994

By J. Y. Liu

In Comparison to the application of HPGR (high-pressure grinding rolls) in the cement industry and in iron ore processing, the introduction of this energy-efficient comminution technology to processing of nonferrous base-metal ores has progressed slowly as yet. In the field of minerals industry, challenges lies not only in the large variety of the feed material with respect to particle size, density, hardness, moisture and mineralogy of the material but also in complexity of the processing flowsheet, which need to be addressed from case to case based on result of HPGR comminution test work. Whereas conventional comminution test with HPGR in lab-scale or pilot scale needs quite a large amount of feed material, a compressive stressing test of particle-bed in piston-die device provides an effective way to study interparticle breakage behavior of ore material with much less feed. In the present study the effects of interparticle breakage on comminution of a copper ore has been investigated by compressive stressing of particle bed in a piston-die device. The feeds to the particle-bed stressing tests were four narrow size fractions in the size range of 0.3~3.35 mm and a broad size fraction of 0/3.35 mm. The pressures applied were in the range between 30 and 180 MPa. The results showed that the specific energy consumption increases linearly with the pressure; the product fineness increases also with the pressure, but the magnitude of this increase declines as the pressure goes up. Under the same stressing intensity, the product size distribution curve becomes steeper as the particle size decreases, so there is no self-similarity between product size distributions of different feed sizes. The suitability of a material-characterization model for interparticle breakage was verified for this ore. In addition, the effect of interparticle breakage on comminution of this ore with respect to its influence on the downstream flotation were analyzed in terms of size-metal distribution and mineral liberation.

Jan 1, 2016

By H. R. Shakeri, R. Mayer, M. J. Worswick, A. Rahem

The current focus of research and development in transportation industry is to use lightweight materials such as aluminium alloys for more structural components. In this regard, maintaining safety of the passenger and vehicle is the most important; therefore crashworthiness of components made of lightweight materials must be evaluated prior to sizable application of these materials. The focus of the present study is to understand failure and damage mechanisms during the axial crushing of aluminium tubes made of A1Mg3.5Mn alloy of 2 and 3.5 mm thickness. Due mainly to complexity of the crushed tubes, a microstructural approach is considered. In this study optical, stereo as well as scanning electron microscopy techniques have been used to study damage and failure mechanisms in these types of tubes, which are essential energy absorbing components in passenger vehicles.

Jan 1, 2006

This paper outlines the position and capabilities of Western Canada's bituminous coal industry, and indicates the increasing importance of Japan as an export market. The use of coal in Japan is reviewed, especially as regards future trends, and an appraisal is made of Canadian coal in comparison with domestic Japanese coal and imports from other countries. The importance of maintaining a solid nucleous within the Canadian bituminous coal industry is emphasized. I N RECENT years, Japan has emerged as a valuable market for Canadian exports. The first major product exported in volume to Japan was wheat, which has become very successfully established in Japanese markets. Following this, iron ore gradually found a market in Japan, with exports usually based on long-term contracts. This iron ore was produced entirely in British Columbia In 1958, the Western Canadian bituminous coal industry -jointly with the Dominion Coal Board -sent an official mission to Japan to investigate the

Jan 1, 1964

By E. Asselin, G. K. Yue

"In the present study, electrochemical measurements, especially cathodic potentiodynamic polarization (CPC) and cyclic potentiodynamic polarization (CPP), have been employed to study the kinetics of ferric reduction on chalcopyrite in aqueous Fe(II)Fe( III)H2SO4 solution at 90 °C and 110 °C. Results from the calculation of speciation in the above solution reveal that, at both 90 °C and 110 °C, the real Fe3+/Fe2+ ratio is much lower than the nominal ratio, which leads to smaller VALUES (for the reversible potential of the ferric/ferrous couple. Exchange current densities of the ferric/ferrous couple were obtained and are on the order of 106 10 5 A/cm2 a t 9 0 °C and 1 07 10 6 A/cm2 at 110 °C, respectively. The Tafel slopes from the CPP method are higher than those from the CPC method at both 90 °C and 110 °C. The transfer coefficients were about 0.360.59 at 90 °C and 0.370.65 at 110 °C. Based on the exchange current densities obtained, the rate constant kc was calculated. It was found that kc at 90 °C was slightly larger than at 110 °C, especially for the results obtained by the CPC method. The average rate constants are 862.17 cm/s for CPC and 65.30 cm/s for CPP at 90 °C, and 477.69 cm/s for CPC and 63.53 cm/s for CPP at 110 °C for nominal Fe3+/Fe2+ ratios ranging from 1:1 to 1000:1. INTRODUCTIONChalcopyrite is one of the most abundant copper-bearing minerals, accounting for approximately 70% of the world’s known copper reserves (Wang, 2005). Most of the currently proposed leaching processes are based on sulfuric acid with ferric ions and/or dissolved oxygen as oxidants. Some of these processes have been piloted in attempts to implement these technologies on an industrial scale, such as Activox (U.S. 5,232,491, 1993), Nenatech (U.S. 5,993,635, 1999), Dynatec (U.S. 5,730,776, 1998), AAC/UBC (U.S. 6,503,293, 2003), Total Pressure Oxidation (U.S. 5,698,170, 1997), CESL (U.S. 5,874,055, 1999) and Galvanox (U.S. 7,846,233, 2010).To date, much effort has been devoted to understanding the kinetics and mechanisms of the oxidative processes (Biegler & Horne, 1985; Córdoba, Muñoz, Blázquez, González, & Ballester, 2008, 2009; Ghahremaninezhad, Asselin, & Dixon, 2010; Hirato, Majima, & Awakura, 1987; Hiroyoshi, Kuroiwa, Miki, Tsunekawa, & Hirajima, 2004; Warren, Wadsworth, & El-raghy, 1982) or the cathode reduction reactions of chalcopyrite itself (Arce & González, 2002; Biegler & Swift, 1976; Biegler, 1977; Nava, González, Leinen, & Ramos-Barrado, 2008), by chemical or electrochemical methods. However, as the most important cathodic processes in chalcopyrite leaching systems, the cathodic reductions of ferric ions or dissolved oxygen are worth measuring due to their effects on the overall leaching rate, as predicted by mixed potential theory."

Jan 1, 2012

By X. -G. Chen, K. Liu

Nowadays, great interests are rising on aluminum alloys for the applications at elevated temperature, driven by the automotive and aerospace industries requiring high strength, light weight and low cost engineering materials. As one of the most promising candidates, Al-Mn-Mg 3004 alloys is found to possess considerably high mechanical properties and creep resistance at elevated temperature resulted from the precipitation of a large number of thermally stable dispersoids during heat treatment. In present work, the effect of Fe contents on the evolution of microstructure as well as high temperature properties of Al-Mn-Mg 3004 alloys has been investigated. Results show that the dominant intermetallic changes from a-Al(MnFe)Si at 0.1 wt.% Fe to Al6(MnFe) at both 0.3 wt. % and 0.6 wt. % Fe. In the Fe range of 0.1 to 0.6 wt.% studied, a significant improvement on mechanical properties at elevated temperature has been observed due to the precipitation of dispersoids, and the best combination of compression strength and creep resistance at 300°C is obtained in the alloy with an intermediate Fe content (0.3 wt.%) with finest size and highest volume fraction of a-Al(MnFe)Si dispersoids. The superior properties obtained at 300°C makes 3004 alloys more promising for high temperature applications. The relationship between the Fe content and the precipitation of stable dispersoids as well as the materials properties has been discussed.

Jan 1, 2015

By J. I. Carroll, J. A. Walker

"Abstract - Camelback is a small (=200 000 tonnes), moderate grade (5%-7% Zn+Pb), volcanogenic massive sulfide deposit, which occurs within the Nepisiguit Falls Formation of the Ordovician Tetagouche Group. The host rocks are tuffaceous sedimentary rocks (Little Falls member) that overlie quartz-feldspar porphyritic tufflavas (Grand Falls member). The hanging-wall sequence comprises rhyolite of the Flat Landing Brook Formation, overlain by the Forty Mile Brook tholeiitic basalt. A dike of unaltered andesite was intersected beneath the massive sulfides, but was not found in the hanging-wall sequence in the vicinity of the deposit. The stratiform part of the deposit is made up of two, steeply south dipping, subparallel massive lenses that average approximately 4 m in thickness. Each lens is zoned, with an upper part consisting mainly of a pyrite and a basal part containing pyrite, sphalerite, and galena, with Ag values. The Au content in the massive sulfides is low (average = 52 ppb for 271 samples), but tends to be enriched in the massive pyrite near the top of each lens. Oxide facies iron formation is spatially associated with the massive sulfides, and has been traced up to 1800 m along strike. Footwall hydrothermal alteration is typical of VMS systems, and is characterized by depletion in K2O and Na2O, and enrichment in MgO and Fe2O3T with proximity to massive sulfides. The massive lenses are underlain by intensely chloritic, fine-grained, tuffaceous sedimentary rocks containing locally significant sulfide (chalcopyrite > pyrite > pyrrhotite) veins, which are interpreted to represent feeder zone mineralization. Unlike many VMS deposits, there is no evidence of silicification beneath the massive sulfides at the top of the feeder zone. The oxygen isotopic compositions (d18O = -1.5‰ to -0.3‰) of hydrothermal chlorite coupled with sulfur isotopic compositions (d34S ˜ 12‰) of the massive sulfides suggest that seawater was the dominant fluid in the hydrothermal system. Normalized rare earth element diagrams show flat Ce profiles and positive Eu anomalies, indicating that modified seawater was involved in ore formation; i.e., high-temperature (=350ºC), acidic, and reduced prior to entrainment into the hydrothermal cell. Although, seawater was the dominant fluid in the sulfide-forming system, d34S values of stringer zone sulfides (8.5‰) coupled with elevated Sn (400 ppm) in one massive sulfide sample indicate that there was at least some magmatic component in the hydrothermal cell."

Jan 1, 2006

By L. Vinnett, T. Ledezma, F. Contreras, F. Díaz

"Mass balances in secondary grinding are subject to critical constraints mainly because of the unknown load distribution from the SAG mills, the uncertainties in the hydrocyclone split estimations and the lack of flowmeters in the key streams. In this paper, a methodology to support mass balances based on the use of radioactive tracer is presented. This approach was successfully implemented in two secondary grinding circuits of Minera Los Pelambres, which operate with ball mills of 21’ x 33.5’. The method allowed the load distribution of the SAG product (secondary grinding feed) to be determined. This load distribution was used as an input in the mass balance data reconciliation.The effective residence times of solid tracers were obtained in the secondary grinding equipment, where irradiated solid was used as a tracer. The residence times were obtained from the parametric deconvolution between the input and output tracer signals. The model fitting was performed to reconstruct the normalized output tracer concentration. Effective residence times of solid tracers in the ball mills ranged from 1.9 min to 9.5 min. The use of radioactive tracer measurement in grinding circuits is a powerful tool to consolidate mass balance results as well as to characterize grinding mills.INTRODUCTIONGrinding is the last stage of the comminution circuits. At this stage, the ore particles are reduced in size by a combination of impact and abrasion, either dry or wet (Austin & Concha, 1994). The grinding equipment mostly used in industrial operations correspond to horizontal tumbling mills (Wills & Napier- Munn, 2006). Tumbling mills employ steel balls or rods as grinding media. Ball mills, which are a type of tumbling mills, use steel grinding media with greater surface area per mass unit than SAG (semiautogenous grinding) mills or rod mills (primary grinding). Hence, the ball mills are suitable to obtain the particle size required in the next separation stages (Napier-Munn et al., 1996; Wills & Napier-Munn, 2006)."

Jan 1, 2016

By A. H. Lang

"The Cordilleran region of western Canada includes most of British Columbia and the Yukon and pares of Alberta and the Northwest Territories. The western part of this region was for about 50 years the principal mineral producing area of the Dominion. It lost this distinction in 1907 when production from the mines of the Canadian Shield took the lead, but it continues to provide about 15 percent of the total Canadian production. In 1945 the total mineral production of British Columbia and the Yukon was valued at $65,302,900, of which about 80 percent was derived from metals.This paper is intended to serve as an introduction co the more derailed Cordilleran papers. Part I includes a brief synopsis of the complex geology and diverse types of mineralization in the region and Parr II collates the main structural principles exemplified in the derailed papers, and draws some conclusions regarding the application of this information to prospecting."

Jan 1, 1954

?Four-wheel, skid-steer, rover developed for CSA ?U-chassis for payload accommodation ?Passive geometric suspension ?Max speed 13km/hr ?Remote workstation ?275kg payload capacity ?On-board processor, IMU, motor encoders ?5.2kW-h battery capacity

May 1, 2013

By Gonzalo Díaz, Diego Mesa, Willy Kracht

"It is well known that frothers affect the amount of water that is transferred to the froth, which has an effect on both the froth stability and the water recovery. On the other hand, since non-selective recovery by entrainment is directly related to water recovery, it can be said that frothers have an indirect effect on flotation selectivity. Recent research on this subject has shown that the non-selective recovery by entrainment, which is characterized by the entrainment factor, is frother dependent. In other words, the entrainment factor is not unique, but depends on frother type.Having different entrainment factors implies that for the same water recovery, the amount of undesired particles reporting to the concentrate may vary if one changes the frother type, which suggests, as a possible explanation, that it is not only the amount of water in the froth what is affected by frother type, but also the froth structure.The purpose of the current work is to study the effect of frother type on foam structure (two phase froth). A quasi-2D cell operated with a slot sparger was used to study the foam structure in the presence of three different frothers: Methyl Isobutyl Carbinol (MIBC), OrePrep®549, and Octanol at the same gas flow rate and reagent dosage. The foam structure was studied using image analysis, and an algorithm based on textural analysis was developed to classify the foams. The results show that it is possible to classify foams according to the frother used, which proves that frothers have an effect on the foam structure.INTRODUCTIONFrothers are usually dosed paying attention to froth stability, condition that is commonly estimated by sight, according to the operator's criteria and experience. This happens because there is not an established procedure or technique for frother characterization, generating qualitative descriptions such as “powerful” or “selective” frothers, which lack of scientific thoroughness and remain under subjective factors. Nevertheless, several works have been done in this line of research. Moyo et al. (2007) classified frothers based on their water-carrying capacity, proving that this characteristic is related with gas holdup and frother type. Previously, Trahar (1981) had related water recovery and gangue particles recovery, defining the entrainment value (ENT). Nowadays it is known that entrainment affects both hydrophilic and hydrophobic because it is not a selective process. In the last decade some studies (for example the one of Konopacka and Drzymala (2010)) delved into different entrainment behaviours dependent mainly on the flotation type (batch or continuous, agitated or columnar, etc.), but there were no studies on the effect of frother type regarding entrainment, since Rahal et al. (2001) argued that the ENT factor was independent of the frother type and concentration, and froth height."

Jan 1, 2016

By Th. Hassel

The application of magnesium as an absorbable biomaterial demanded the consideration of the alloy composition, the mechanical properties and the corrosion a special adapted material development in terms of the human biological system. Magnesium for technical applications mostly comprised alloying elements up to 10 wt%. Thereby often metals (e.g. rare earth and aluminum) with high toxic potentials are used to optimize the mechanical properties. To minimize toxic reactions during the degradation of a absorbable magnesium alloy, the Mg-Ca system is being selected and investigated because both elements belong to the mineral nutrients. Rods and small tubes are produced by extrusion of gravity die casting billets (Ca-content 0.4 to 4.0wt%). The positive grain fining influence of calcium and its improvement of the corrosion behavior are additional advantages. The microstructure, the mechanical properties and the corrosion attitude are investigated. The results show that an optimal composition of micro alloyed Mg-Ca and ideally processing parameters lead to 16% strain and a tensile strength up to 185MPa. Electrochemical investigations and measurements of the hydrogen production demonstrate the influence of the Ca-content to the corrosion behavior of the investigated alloys.

Jan 1, 2006