By W. C. Ellis

NONFERROUS alloys upon which desirable properties can be conferred by heat treatment are becoming of increasing industrial importance. The alloys of copper with a constituent which has a solubility varying with temperature are materials of this character. Some of the constituents which are effective in producing a change in the mechanical properties of these alloys upon heat treatment are, according to Corson,1 nickel and silicon, iron and silicon, cobalt and silicon, and chromium and silicon. In addition to these elements, Gregg2 states that the combination of beryllium and silicon is effective in producing age-hardening characteristics in copper. The effect of these elements, however, as dispersion-hardening constituents in the copper alpha solid solutions does not seem to have been studied in any considerable detail. This paper deals with the heat treatment and properties of three alpha brasses containing 3 per cent. of nickel plus silicon in the proportion necessary to form the compound nickel silicide, Ni2Si. Some information of a preliminary nature in regard to the hardening by heat treatment of phosphor bronze containing the same percentages of nickel and silicon is included. The method of hardening the alloys, which is effective in increasing the tensile strength and proportional limit, is similar to that used in, the case of duralumin type aluminum alloys. It consists of a quench from a temperature at which the hardening constituent is in solid solution, followed by an aging at a lower temperature to precipitate the dissolved constituent in a dispersed condition. This results in an increased resistance of the alloy to deformation with an attendant improvement in the tensile properties.

Jan 1, 1929

By T. R. Lippard

PURE gypsum may be broken down into its constituents as follows: [ ] Standard specifications (ASTM Designation C22-25) state that a material shall not be considered gypsum if it contains less than 64.5 pct by weight of CaS042H2O. Anhydrite, the second calcium sulphate mineral found in nature, may be broken into its constituents as follows: [ ] PROPERTIES OF GYPSUM AND ANHYDRITE Pure gypsum is colorless to white but various impurities change its color to shades of gray, brown, red, or pink. It has a hardness of 2 in the Mohs scale and can be scratched with the fingernail. The specific gravity of pure gypsum is 2.3 to 2.4, so that rock gypsum, free from moisture, weighs about 145 lb per cu ft. Gypsum crystallizes in the monoclinic system in tabular crystals that exhibit good cleavage

Jan 1, 1949

By K. Huessener

INTRODUCTION THIS paper attempts a survey of the principles involved in the com¬bustion of blast-furnace gas in boilers and stoves. I do not expect to be able to give much information which is actually new, since the laws and methods of calculation pertaining to this problem are contained in a number of handbooks; but, so far as I am aware, they have nowhere been treated exclusively with reference to this one problem of gas economy. The road which I follow is less that of strictly scientific research than that of the practical engineer, faced by operation problems which require a. quick solution by easily accessible means without a prolonged search in scientific handbooks. For this purpose I give a number of tables and diagrams, as well as the results of many years' practical working experience as combustion engineer, which I trust will prove useful to my readers. HISTORICAL Considering the tremendous efforts made during the last 15 years to increase the efficiency of all kinds of power plants, it is highly surprising that until a comparatively very recent period, progress in the economical combustion of blast-furnace gas has been so slow. The explanation generally put forth, that fuel has been so cheap that it was hardly worth while to bother about this economy, will not hold good, for the greatest trouble was taken to improve the combustion of coal and to reduce the consumption of steam. The most plausible explanation appears to be the general impression, held as an accepted fact, that gas, especially hot, uncleaned, blast-furnace gas, was not a good boiler fuel. Many managers of high repute had tried unsuccessfully to improve the conditions of its use, and the dictum went forth that efficiencies of over 60 per cent., particularly with high loads, were impossible. This was the situation not only in the United States, with very cheap fuel, but also in Europe, where fuel prices are twice and three times as high.

Jan 2, 1916

AT A MEETING of the Shareholders of the Russo-Asiatic Cons. Ltd., in London, Oct. 23, 1922, LESLIE URQUHART, chairman of the com- pany made the following statement:* I come now to our recent negotiations with the Soviet Government and to the agreement which has resulted from them. You will remember that the conference at The Hague broke up without having achieved anything very definite. It was not, however, a failure. It elicited from M. Litvinoff an offer which will, I think, come to be regarded as a milestone in the progress of Russia from a ruinous and unpracticable Communism towards a modified form of capitalism. The offer made by M. Litvinoff at The Hague amounted in effect to this: that in return for political recognition on our part the Soviet Government would first acknowl-edge its liability for Russia's national foreign debts, and, secondly, would give the original foreign owners of property in Russia effective compensation. A very great advance that. It showed-and there have been many other signs to confirm it-how real and persistent has been the internal evolution of Russia during the past year from Marxism to the economics of the Western world. I will not now detain you with the reasons why M. Litvinoff's highly promising and significant offer came to nothing. The fact that it had been made and the further fact that The Hague Conference had separated indefinitely were the important things. The first fact seemed to indicate that the Soviet rulers, after all, proved to be people with whom one could do business. The second fact rather emphatically showed that the way to do business with them was not by unwieldy poly-glot conferences of ministers, officials and experts representing a few dozen different governments and a few dozen different sets of national interests. That method had been tried at Genoa. It was tried again at The Hague. Each time it failed, and having failed it left the road clear for a simpler and more direct approach.

Jan 12, 1922

NEW MEMBERS The following list comprises the names of those persons who became members during the period of Mar. 10, 1917, to Apr. 10, 1917. ADKINS, HARVEY S Adkins & Denham, Engineers, Box 291,. Hazard, Ky. ANDERSON, ARTHUR P .... Leaser, Gibson Copper Co., Box 1978, Miami, Ariz. ARNOLD, EDWARD C... Min. Engr., Chief Engr., Federal Lead Co., Flat River, Mo. ASKIN, THOMAS B. H., Ball Mill Expert, Inspiration Cons. Copper Co., Miami, Ariz. BAIN, C. KREMER Butte & Superior Mining Co., Butte, Mont. BAKER, WILLIAM A.,.JR., Vice Pres. & Sales Mgr., The Georges Creek-Parker Coal Co., 306 North Gay St., Baltimore, Md. BOOTH, GEORGE H Mech. Engr., Inspiration Cons. Copper Co., Miami, Ariz. BRIDGMAN, G. TEMPLE, Asst. Consulting Mining Engr., Guggenheim Bros., 120 Broadway, New York, N. Y. BROOKS, CHARLES A Mine Surveyor, Homestake Min. Co., Lead, So. Dak. BUTCHER, FREDERIC E., Secretary, Missouri Metals Corpn., 1945 Railway Exchange Bldg., St. Louis, Mo.

Jan 5, 1917

By M. A. Scheil

Austenitic stainless alloys are susceptible to stress-corrosion cracking which may occur under certain corrosion environments irrespective of their susceptibility to intergranular corrosion. Test samples are described for investigating stress-corrosion susceptibility of alloys for industrial equipment. A laboratory test using a solution of magnesium chloride boiling at 309 F. was found to produce transgranular cracks in several alloys investigated and in types 347 and 316 stainless steel tubing a residual stress of the order of 10,000 psi. was observed to initiate cracking. The susceptibility to stress-corrosion cracking as judged by the boiling magnesium chloride test indicates that alloys may be selected which will withstand a high stress in service Stressed specimens of stainless alloys included in a corrosion testing program will aid in determining the acceptibility of these fabricated alloys, when stressed, to the service conditions.

Jan 1, 1945

By E. A. Gulbransen, J. W. Hickman

IN a previous paper1 the authors have investigated the structure of the oxide films formed on most of the metals that make up the alloys of this study. The metals were studied in order to provide basic information on the structures, both physical and chemical, of the oxide films and to determine how these structures are effected by the temperature, time of oxidation, and surface preparation. It was felt that an understanding of the physical and chemical structure as well as the stability of the oxide film might furnish clues as to the nature of the reaction process and the protective quality of the film. The oxidation of the metals was studied over the temperature range 300° to 700°C. except for copper, where the range selected was 100° to 500°C. The results of these studies were presented in graphical form as existence diagram, of the oxides on a time-temperature scale. For some of the metals the existence diagrams were simple and showed few chemical transitions, but there were numerous cases where the physical state of the oxide surface was a function of time and temperature. In general the physical state of the oxide surface changed with increasing temperature so as to increase the sharpness of the diffraction patterns and to cause orientation effects to be more pronounced. Deviations in lattice parameters from X-ray values were noted. In general these deviations were of positive nature and may be due to solid solution of the metal in the oxide lattice. This effect might be expected in thin oxide films. In a study of the oxidation of alloys containing two or more metals, there may arise the complicating factor of identification of the oxides formed. A thorough understanding of the oxides formed on the pure metals, therefore, was, essential before investigation of the oxidation of alloys. In this paper it is our purpose to present a study of the following problems: I The existence diagrams of various alloys. [2.] The effect of the structure of the [ying] metal on the existence diagram of Iron. 3. The effect of the percentage of chromium on the oxides formed on Fe-Cr alloys. 4. The relationships, if any, between the oxides formed and the protective quality of the oxides. The following alloys are included in this study: alloys of iron with body- centered cubic, face-centered cubic and other metals, 13 Cr-Fe, 18-8 stainless steel, K42B1 Nichrome V, Hipernik, Inconel, Stellite " 21," Refractaloy, Kovar, mild steel, a series of Cr-Fe alloys and a series of Co-Fe alloys. Since many of the commercial alloys in this list contain more than two metals, various complicating factors in the identification of the oxides formed may arise.

Jan 1, 1946

By S. N. Kesten, Richard Murphy, A. H. Land, W. F. James

Introduction—by W. F. James and A. H. Lang This paper describes the geology and present state of development of uranium and thorium deposits in Canada. It is expected that this information will be added to that now being assembled from available American and British data to provide a background for engineers and others who may be called upon in the future to examine or search for radioactive deposits. Some generaliza- tions regarding the Canadian deposits are included, but many of these are necessarily tentative. The information contained in the paper is up to date for the end of 1948. The information contained in this paper has been derived from many sources. Much of it is from the records of the Canadian government-owned Eldorado Mining and Refining (1944) Limited and from examinations of government and private properties made by officers of the Geological Survey of Canada. Some information on privately-owned properties has been quoted from other sources mentioned in the text. The information has been assembled by W. F. James of Eldorado Mining and Refining (1944) Limited and A. H. Lang of the Geological Survey of Canada, who have written the sections for which they are credited. The description of the Eldorado mine is based on reports by Richard Murphy, formerly chief geologist for Eldorado; the report by Mr. Murphy was published previously by the Canadian Institute of Mining and Metallurgy,' to whom the writers are indebted for permission to repub-lish. The section dealing with the geology of and development work in the Goldfields area, where Eldorado has important holdings, is by S. N. Kesten, field geologist for Eldorado. The geological diagram of the Goldfields area (fig. 2) was kindly supplied by A. M. Christie of the Geological Survey of Can-

Jan 1, 1951

By W. F. James, Richard Murphy, S. N. Kesten, A. H. Land

Introduction—by W. F. James and A. H. Lang This paper describes the geology and present state of development of uranium and thorium deposits in Canada. It is expected that this information will be added to that now being assembled from available American and British data to provide a background for engineers and others who may be called upon in the future to examine or search for radioactive deposits. Some generaliza- tions regarding the Canadian deposits are included, but many of these are necessarily tentative. The information contained in the paper is up to date for the end of 1948. The information contained in this paper has been derived from many sources. Much of it is from the records of the Canadian government-owned Eldorado Mining and Refining (1944) Limited and from examinations of government and private properties made by officers of the Geological Survey of Canada. Some information on privately-owned properties has been quoted from other sources mentioned in the text. The information has been assembled by W. F. James of Eldorado Mining and Refining (1944) Limited and A. H. Lang of the Geological Survey of Canada, who have written the sections for which they are credited. The description of the Eldorado mine is based on reports by Richard Murphy, formerly chief geologist for Eldorado; the report by Mr. Murphy was published previously by the Canadian Institute of Mining and Metallurgy,' to whom the writers are indebted for permission to repub-lish. The section dealing with the geology of and development work in the Goldfields area, where Eldorado has important holdings, is by S. N. Kesten, field geologist for Eldorado. The geological diagram of the Goldfields area (fig. 2) was kindly supplied by A. M. Christie of the Geological Survey of Can-

Jan 1, 1951

By J. Steininger

The Hallimond tube flotation of sphalerite and pyrite with sulfhydryl collectors has been found to be inhibited near neutral pH in the presence of copper salts. Alkalimetric titration studies of the reactions between collector and activator indicate that this effect is apparently related to the formation of basic copper collector complexes. The conditions of formation of these compounds and their stability are in good agreement with the depression observed in flotation experiments. The general procedure employed in the flotation of zinc sulfide minerals requires activation of the mineral surface by heavy metal ions, usually copper, which react more easily than zinc with the common short-chain ionic sulfhydryl collectors.' Commercially, zinc flotation is carried out under alkaline conditions (pH 7 to 10.5), but small-scale experiments indicate that zinc sulfide minerals can also be activated and collected under acid conditions. Selectivity, however, becomes poor at low pH and undesirable materials such as pyrite, silicates and carbonates tend to report in the float. Several years ago, Wark and Sutherland~, measured the contact angles of air bubbles on copper-activated sphalerite immersed in various sulfhydryl collector solutions. When represented, as in Fig. 1, on pH-sodium cyanide diagrams, the results are characterized by 'islands' of non-contact near neutral pH and

Jan 1, 1969

By Henry S. Rawdon

The structure of wrought iron as usually described by metallographists and workers in metal in general is that of a fairly pure iron. Impurities, if present, are usually considered as being in solid solution in the crystals of the ferrite matrix or as forming part of the ever present "slag streaks." Attention is herein directed to one type of these dissolved impurities; to the detection of such impurities, particularly in low-grade irons, and to their possible influence on the physical properties of the metal. The attention of the Bureau of Standards was first directed to wrought iron of the peculiar and unusual characteristics to be described later, in material which had failed in service and was submitted for test. The examination was extended to other grades of wrought iron, to see whether such features are of common occurrence in this class of material. MICROSTRUCTURE OF WROUGHT IRON Usual Structure The general microstructure of wrought iron is so well known that a detailed description of it here is needless. There is shown in Fig. 2 the structure of a sample of Swedish iron which illustrates well the matrix of ferrite crystals in which are embedded the slag threads so characteristic of the puddling process and the subsequent working of the material. The usual commercial product contains varying amounts of the impurities commonly associated with iron and steel, i,e,, manganese, phosphorus, silicon, and sulphur together with small amounts of carbon. Of these, the larger part of the phosphorus and some of the silicon present are held in solid solution in the ferrite while most of the remaining impurities, other than carbon, exist in the in closures of slag. Aside from the discontinuities introduced by the slag streaks the ferrite matrix has the microstructure and appearance of a pure metal. No definite orientation of the various crystals or grains is apparent; deep etching of the specimens reveals no intracrystalline features (i.e., within the grains) other than those noted in " pure " metals in general (etching pits).

Jan 1, 1918

By Charles W. Carter, Alfred H. Bell

In 1942, Illinois produced 106,590,000 bbl. of crude oil, or 7.6 per cent of the entire amount produced in the United States. It ranked fifth among the oil- producing states. The production for 1942 declined 20.5 per cent from the previous year's total of 134,139,000 bbl. Tie daily average production for 1942 was approximately 292,000 bbl., or 74,000 bbl; less than the 366,000 daily average for 1941. At the beginning of 1942 the daily production was 367,000 bbl. This production declined steadily to 282,000 for June and to 246,000 for December. This steady decline was caused partly by the reduction in drilling resulting from Federal Conservation Order M-68 and partly by the fact that no major pool was found during the year. Discoveries Forty new fields (Fig. 2, Table 2), 48 extensions (Table 3), and 45 additional producing zones in existing fields (Table 4) Were discovered in 23 counties in Illinois during 1942. Of the 40 new fields, three

Jan 1, 1943

By Alfred H. Bell, Charles W. Carter

In 1942, Illinois produced 106,590,000 bbl. of crude oil, or 7.6 per cent of the entire amount produced in the United States. It ranked fifth among the oil- producing states. The production for 1942 declined 20.5 per cent from the previous year's total of 134,139,000 bbl. Tie daily average production for 1942 was approximately 292,000 bbl., or 74,000 bbl; less than the 366,000 daily average for 1941. At the beginning of 1942 the daily production was 367,000 bbl. This production declined steadily to 282,000 for June and to 246,000 for December. This steady decline was caused partly by the reduction in drilling resulting from Federal Conservation Order M-68 and partly by the fact that no major pool was found during the year. Discoveries Forty new fields (Fig. 2, Table 2), 48 extensions (Table 3), and 45 additional producing zones in existing fields (Table 4) Were discovered in 23 counties in Illinois during 1942. Of the 40 new fields, three

Jan 1, 1943

By Oscar Harder

IT is now just a quarter of a century since Fred W. Taylor§(23) pub-lished his classical paper On the Art of Cutting Metals, describing -his researches in which he, in cooperation with Maunsel White, had developed what is essentially the modern method of heat-treating high-speed steels. Regarding this research, Dr. Sauveur, (22) in his address on Steel Wizards, Past and Present, at the annual banquet of the American Society for Steel Treating in Philadelphia in 1920 said, "The discovery of high-speed steel, or if you prefer, of the treatment imparting high-speed properties to certain steels by Taylor and Maunsel White I am inclined to consider as our one epoch-making contribution to the metallurgy of steel." It was at about that same time (1900) that Taylor exhibited high-speed steels, heat-treated by the improved process, at the World's Exposition in Paris and attracted much attention by showing that the steels would operate at such feeds and speeds that the tips of the tools were visibly red hot. This observation must have started metallurgists to wondering regarding the relative hardness of the various steels at red-heat temperatures. Considerable work has indeed been done in an effort to measure the hardness of high-speed steels and. related materials in the red-heat range, using various methods. . The results, however, have been only partly satisfactory, owing to experimental difficulties. The present investigation had as its immediate inception an address by J. V. Emmons, of the Cleveland Twist Drill Co., to the Columbus Chapter of the American Society for Steel Treating in 1931, in which he deplored the fact that comparatively little was known with regard to the hardness of high-speed steels at elevated temperatures, in spite

Jan 1, 1933

By J. B. Umpleby

PRoduction engineering in 1927 may be characterized by a great. clarification of fundamental conceptions, and many improvements in technique. During the year the profession has received tnarked recogni-tion by the industry and to an extent never before attained has become an integral part of it. History Petroleum production engineering is a new profession. Prior to 1925, when this Institute undertook the work, no forum existed for the open discussion of its technical problems. There was no attempt at a handbook of the subject prior to "Petroleum Production Methods by J. R. Suman, in 1921, and no textbook prior to Petroleum Production Engineering" by L. C. Uren, in 1924. As late as 1926, only six schools and universities offered special courses in petroleum production engineering. Prior to about 1923, engineers engaged by oil companies were used almost exclusively for construction and location work. Two of the leading production engineers in the Mid-Continent field, although with their respective companies more than twelve years, were not definitely assigned to production work until 1924. Both men now head large departments giving almost their entire time to production problems. Because of the newness of the profession, the leading production engineers of today have had their fundamental training in mining, civil, mechanical and electrical courses. Not unlikely this diversified training is in considerable part responsible for the amazing growth of the profession. I believe, however, that recognition is due principally to economic pressure within the industry which has directed attention more and more sharply on costs and efficiency. After all, the justification for the growth and continued development, of the profession is to recover more oil from a given unit of sand at less cost per barrel. In this new profession, it seems to me that greatest progress will result from focusing thought and effort on this single objective, and if I might offer one suggestion to the com-

Jan 1, 1928

By E. F. Loiseau

(Read at the Philadelphia Meeting, February, 1878.) UNTIL June, 1868, it had not been attempted, either in this country or abroad, to manufacture by mechanical means, from anthracite coal-dust, artificial fuel for domestic use. Several attempts had been made to utilize coal-waste by converting it into a fuel for manufacturing purposes, but none of the processes were original, and they were merely applications of the well-known European processes and machinery, slightly modified by American ingenuity and mechanical skill. With one exception all those attempts have been failures. The great difficulty in the application of European processes and machinery has always been the limited production, and the excessive cost of the manufactured product, as compared with the cost of mining and preparing the ordinary anthracite coal for the market. The only serious and intelligent attempt to manufacture, on a large scale, artificial fuel for manufacturing purposes, has been made by the Anthracite Fuel Company, whose works are erected at Fort Ewen, near Rondout, New York. This company, organized under the auspices of the Delaware and Hudson Canal Company, had to go through the usual course of difficulties, breakages, and disappointments, which seems to be the lot of every new industry. Thanks, however, to the energy and perseverance of Mr. L. L. Crounsse, a gentleman of means, from Washington, D. C., the enterprise succeeded, and it is to-day established on a permanent basis. In order to increase the production, and to reduce its cost, the Anthracite Fuel Company was compelled to change most of its plant, and to erect more powerful machinery, producing lumps of a larger size, almost twice the size of the lumps made previously by the same company. This increase in the size of the lumps has been resorted to in Europe as well as in this country, in order to increase

Jan 1, 1878

By E. F. Loiseau

Until June, 1868, it had not been attempted, either in this country or abroad, to manufacture by mechanical means, from anthracite coal-dust, artificial fuel for domestic use. Several attempts had been made to utilize coal-waste by converting it into a fuel for manufacturing purposes, but none of the processes were original, and they were merely applications of the well-known European processes and machinery, slightly modified by American ingenuity and mechanical skill. With one exception all those attempts have been failures. The great difficulty in the application of European processes and machinery has always been the limited production, and the excessive cost of the manufactured product, as compared with the cost of mining and preparing the ordinary anthracite coal for the market. The only serious and intelligent attempt to manufacture, on a large scale, artificial fuel for manufacturing purposes, has been made by the Anthracite Fuel Company, whose works are erected at Fort Ewen, near Rondout, New York. This company, organized under the auspices of the Delaware and Hudson Canal Company, had to go through the usual course of difficulties, breakages, and disappointments, which seems to be the lot of every new industry. Thanks, however, to the energy and perseverance of Mr. L. L. Crounsse, a gentleman of means, from Washington, D. C, the enterprise succeeded, and it is to-day established on a permanent basis. In order to increase the production, and to reduce its cost, the Anthracite Fuel Company was compelled to change most of its •plant, and to erect more powerful machinery, producing lumps of a larger size, almost twice the size of the lumps made previously by the same company. This increase in the size of the lumps has been resorted to in Europe as well as in this country, in order to increase

Jan 1, 1879

By F. S. Pettit

The oxidation of Ni-3 to 25 wt pd Al alloys has been studied in 0. 1 atm of oxygen at temperatures between 900° and 1300°C. These alloys have been found to oxidize by three different mechanisms which depend on the temperature of- oxidation and the alloy composition. Two of the three mechanisms do not permit a continuous layer of Al,0, to be formed on the alloy surface and the oxidation rates are greater than that for pure nickel. The third mechanism results in the formation of an external A1203 scale and lke oxidation rates are about three orders of magnitude smaller than those for pure nickel. The minimum amount of aluminum required for the formation of external scales of A L,0, has been determined. NICKEL-base alloys are currently the main source of materials for use at elevated temperatures in gas turbine engines. These alloys are usually coated to obtain oxidation resistance. Coatings on nickel-base alloys are frequently formed by reaction of the alloy with aluminum whereby alloyed nickel aluminides are formed. The alloyed nickel aluminides provide protection to the nickel base alloy because external scales of A1203 (alumina) are formed during oxidation and mass transport through A120, is slow in comparison to mass transport through most other oxides. In view of the protective properties of A1203, it is important to know how much aluminum is required in these alloys in order to form external scales of AlzO,. The present paper is concerned with the oxidation kinetics and the oxidation mechanisms of Ni-A1 alloys and the minimum amount of aluminum required in these alloys for the formation of external scales of Alz03. THEORETICAL CONSIDERATIONS When a Ni-A1 alloy is heated in oxygen at elevated temperatures, the following reactions can take place on the surface of the alloy where the oxide phases are assumed to be virtually pure: These oxide phases are in the form of nuclei scattered over the surface of the alloy and, in view of their rapid formation, they need not be in equilibrium with the alloy. As the oxidation process continues, equilibrium between the alloy surface and the oxide phases is approached and the stability of the oxide nuclei is determined by the composition of the alloy at the alloy/oxide interface because of the following reactions: 3NiA1204 + 2A1 (alloy) = 4AlzO3 + 3Ni (alloy) [41 4Ni0 + 2Al (alloy) = NiA120, + 3Ni (alloy) [ 5 1 Application of the mass-action law to Eqs. [4J and [5J yields the following equilibrium conditions for these reactions: where aA1 and aNi are the activities of aluminum and nickel, are the standard free energies of formation of NiO, A1203, and NA1204, respectively, R is the gas constant, and T is the absolute temperature. If the composition of the alloy at the alloy/oxide interface is such that (akl/ahi) is greater than the equilibrium values defined by Eqs. [6] and [7], then Reactions (41 and [5] will go to the right as written. Conversely, if the alloy composition is such that the activity ratio (aLl,/aki) at the alloy/oxide interface is less than the equilibrium values, then Reactions [4] and [5] will proceed to the left. The equilibrium activity ratios in Eqs. [6] and 171 can be calculated since values for the standard free energies of formation of the oxide phases are available. Standard free energies of formation for NiO and A1203 have been tabulated by Elliott and ~leiser.' The standard free energy of formation for NiA1204 can be obtained from the data of Tretjakow and Schmalzried.' The results of these calculations are tabulated in Table I. Table I shows that the following inequality is valid over the temperature interval 900" to 1300°C: (Reaction [5]) (Reaction [4]) « 1and therefore the aluminum activity for these compositions can be taken as equal to the square root of the activity ratios (i.e., aNi = 1). If equilibrium is estab-

Jan 1, 1968

By R. B. Haagensen, E. Martinez, V. Kudryk

The sample under investigation contained approximately 16% BaSO, and was 80% -325 mesh. Established methods for floating barite did not produce concentrates of satisfactory grade or barite recovery because of low barite content and the presence of 6% calcite in the feed. By using a new long-chain sulfosuccinamate collector in combination with relatively high concentrations of sodium silicate, a barite concentrate was produced that would be acceptable as an oil-drilling mud using a simple rougher-cleaner circuit. No desliming of the fine-ground feed was necessary. Barite recovery was over 80% and the concentrate produced had a specific gravity higher than 4.3. During the course of the investigation, a procedure was developed to obtain semiquantitative determinations of barite, calcite, quartz, and feldspar in test samples using an infrared spectrophotometer. Samples were also analyzed in a thermobalance for determination of the calcite content. The use of these instruments made it possible to obtain quick mineralogical assays and proved to be of invaluable assistance in guiding the flotation testing.

Jan 1, 1976

Joseph LeConte, Berkeley, Gal.: I have read with some care and with extreme interest the work of Dr. Don, and have 110 hesitancy in expressing my high estimate of its value. We have here an example of laborious work undertaken in the true scientific spirit and by right methods. Loose statements and rash conjectures are here brought to the test of chemical analyses. By such work only may we hope to reach reliable conclusions and finally to solve the complex problems presented by the occurrence of ore-deposits. Such work as this is not only scientific but Is in the highest degree practical; for while a crude and imperfect science, by interfering with the results of approved empirical methods, may be positively hurtful, a more perfect science must eventually become the only sure guide to practice. Such a more perfeet science can only be reached by such work as Dr. Don's. I am sure every member of the Institute will unite with me in the hope that Dr. Don will continue his work, and that his example will incite others to similar work. S. F. Emmons, Washington, D. C.: I desire to bear my humble testimony to the great value of Dr. Don's paper to the science of ore-deposits, the thoroughness and accuracy of his work, and the immense amount of care-taking and tedious labor which it represents. The only regret with regard to it is that it could not have been published in full. No more important paper in its line has ever appeared in the Transactions. Indeed,

Jan 1, 1898