By C. F. Smart

The heat treatment of the bronze composed of 88 per cent. copper, 10 per cent. tin, and 2 per cent. zinc, has been investigated by H. S. and J. G. S. Primrose,' and also by the U. S. Bureau of Standards.2 The results obtained by H. S. and J. G. S. Primrose on dry-sand castings subjected to reheating followed by air cooling, or by quenching in water, are shown in Figs. 1 and 2. The values for tensile strength have been converted from tons per square inch to pounds per square inch. Figs. 3 and 4, have been plotted from values obtained by the Bureau of Standards on material of the same composition and treatment. Both investigations show that the ductility of the cast bronze is improved by heating to 700' C. and cooling in air, the strength not being impaired by this treatment. They are not in agreement, howevcr, as to the effect of quenching, Messrs. Primrose reporting a decrease, and the Bureau of Standards an increase, in both strength and ductility when the cast bronze is heated to 600' or 700' C. and quenched. The present investigation was undertaken to study the effect of annealing followed by different rates of cooling, and, in particular, the

Jan 1, 1921

By R. J. Evans, A. G. Revesz

Silicon films have been grown by chemical reaction on (111) silicon substrates. The surfaces were examined by various microscopic and interfero-metric methods. Surface structures are classified into two groups depending on whether the angles between the bounding planes and the (111) surface are small (<3 deg) or large (> I0 deg). A layer-gvowth mechanism is postulated to explain the topography and the influence of growth parameters. Growth proceeds by lateral expansion of the (111) layers in (211) directions, thereby forming steps. The step edges are perpendicular to the direction of expansion and are thus along (110) directions. Step bunching md surface nucleation both play an important role in modifying the flow pattern and in the step regeneration. These are influenced ver?) much by impurities, especially oxygen. Although the growth is a result of a surface-controlled ga: reaction, it is very similar to growth from an impure solution. OVERGROWTH ("epitaxial growth") of silicon is important and widely used. During the past years several investigators have observed various topographical features or so-called faults on the grown films. A study of the surface morphology gives some insight into the growth mechanism. I) EXPERIMENTAL Silicon films have been grown on silicon substrates by a method described by Theuerer.&apos; Silicon is formed by reduction of SiCl, in hydrogen. The rate of incidence of SiC1, was varied between 5 x 10"6 and 2 x 10&apos;4 moles min-&apos; cm-&apos;. The mole fraction of Sic4 in the Hz-SiCL mixture was about 5 x X Both the rate of incidence and the mole fraction were calculated on the assumption that the Hz bubbling through the SiC1, reached equilibrium saturation. Assuming uniform velocity distribution, the linear velocity of the gas in the reactor tube was estimated to be 2 cm sec-l. The temperature of deposition was varied between 1070" and 1260°C. Chemically polished p-type silicon wafers of 20 to 100 ohm cm resistivity were used as substrates. These were within 1/2 deg of a (111) orientation. The thickness of the grown n-type film was determined by two methods: a) measurement of the depth of the p-n junction taking into account the junction shift due to diffusion, b) measurement of the traces of stacking-fault tetrahedra on the (111) plane.&apos; The agreement between the two methods was better than 20 pct. The rate of growth varied between 0.2 and 4.0 pmin-&apos;. The formed films were examined by reflection and light-section microscopy, and by multiple-beam interferometry. Phase-contrast illumination revealed height differences of about 30A. For measuring heights greater than 1 p a light-section microscope3 was used. The resolution by multipke-beam interferometry4 was between 50 and 100A. Crystallographic directions on the surface were determined by X-ray and from the orientation of etch pits and stacking faults as revealed by Dash etch (I part HI?, 3 parts HNOJ, and 12 parts CH3COOH). Some specimens have been investigated by electron microscopy. Platinum-shadowing and carbon-replica techniques were used to show the fine topography and reflection diffraction to determine the structure of the grown layers. 11) RESULTS The topographical features can be classified into three groups. he first group is comprised of fine ridges (striations). The second group consists of structures, which are bounded by planes making angles of less than 3 deg with the (111) surface. They are, therefore, vicinal planes. Structures which closely resemble growth or etch pyramids from the third group would normally be bounded by perfect low-index crystallographic planes. In this case they are deformed. The angles between the bounding planes and the (111) surface are generally larger than 10 deg. The fine ridges are present, even on the smoothest surfaces, as shown in Fig. 1. They are along a (110) direction. The height differences could not be resolved with interferometric techniques. The basic characteristic structures of the second group are depressions and hillocks. These are bounded by three planes, two of them with larger slopes than the third one. The edges between the planes, as projected to the (111) surface, point in (211) directions. Various habits of these structures are shown

Jan 1, 1964

By R. C. Hassinger, D. V. von Rosenberg

Transverse dispersion has received considerably less treatment in the literature than has longitudinal dispersion. Different methods for determining transverse dispersion coefficients have been used in different investigations, and the results obtained have not been consistent enough to permit accurate generalizations as to the effect of various physical parameters on the magnitude of these coefficients. A numerical solution to the differential equation describing transverse dispersion in the absence of longitudinal dispersion was obtained to enable one to calculate the dispersion coefficient from experimental results. The more general dispersion equation including longitudinal dispersion also was solved numerically to give quantitative limits of a dimensionless group within which the assumption of negligible longitudinal dispersion is justified. Possible experimental procedures were examined, and one utilizing a cylindrical packed column was chosen for the determination of transverse dispersion coefficients. Values of these coefficients were determined for a system of two miscible organic fluids of equal density and viscosity, for two sizes of packing material over a wide range of flow rates in the laminar regime. The dispersion coefficient was found to decrease, for a constant value of the product of packing size and interstitial velocity, as the size of the packing material particles increased. INTRODUCTION Longitudinal dispersion has received extensive treatment in the literature, and consequently is better understood than its orthogonal counterpart, transverse dispersion. Many mathematical models of dispersion processes assume that transverse dispersion is rapid enough to damp out any radial** concentration gradients and therefore may be neglected. Laboratory and production results, however, indicate that this is a poor assumption.l,2 Various experimental procedures for determining transverse dispersion coefficients have been used in previous investigations, but the results have generally been expressed by similar correlations. The transverse dispersion coefficients obtained, however, have often varied considerably for given values of the correlation parameters. We feel that further experimental determinations of transverse dispersion coefficients will help alleviate some of the inconsistencies in these empirical correlations. One assumption implicit in all previous investigations is that of negligible longitudinal dispersion in the experimental system. An attempt to justify this assumption often is made using intuitive reasoning, but it is apparent that this reasoning must break down as the condition of zero flow rate is approached. A mathematical examination of the equations describing the system yields physical limits outside of which the assumption of negligible longitudinal dispersion is invalid. BACKGROUND In a porous medium, the "effective molecular diffusivity" De is less than the molecular diffusivity D measured in the absence of a porous medium, due to the tortuous path which a diffusing molecule must travel. Various authors3-5 have reported values of the ratio De/D in the range of 0.6 to 0.7. When there is fluid flow within the porous medium, mass transfer occurs by convective dispersion as well as by molecular diffusion. These are separate phenomena and can be treated as such on a microscopic scale. However, the mathematical complexity is such that only extremely simple geometries could be considered, and the results hardly would be applicable to the complex geometries existent in actual porous media. A more

Jan 1, 1969

By P. D. Merica, J. R. Freeman, R. G. Waltenberg

Contents Page Constitution of Commercial Aluminum.................. 4 Solubility of CuAl2 in Aluminum at Different Temperatures........ 9 Effect of Magnesium on Solubility of CuA12 in Aluminum ......... 15 Solubility of Mg4Al8 in Aluminum at Different Temperatures........ 15 Solubility of Metals and Metal Compounds in Aluminum.......... 20 Summary and Conclusions......................20 Aluminum and its alloys have been the subject of much investigation1 during recent years, in the course of which the principal features of the constitution of most of the binary alloy systems with aluminum have been determined. Except in the case of a few metals—silicon, bismuth, cadmium, lead, zinc, and tin—an aluminum-rich compound is formed in each binary system, which forms a eutectic with the aluminum or its solid solution with this compound: Thus such compounds as FeAla, CuA12, Mg4Al3, and NiAls are formed, which are found in aluminum-rich alloys of their respective series as eutectics with the aluminum solid solution. These compounds are, in all cases, hard and brittle and their presence affects profoundly the physical properties of the alloys in which they occur. Within the zinc-aluminum system a compound, Al2Zn,, is formed that decomposes at lower temperatures. Silicon and tin each form a simple eutectiferous series with aluminum; bismuth, lead, and cadmium are only partly miscible in the liquid state with it. The extent of the solubility in aluminum, in solid solution, of these compounds or of the elements themselves, in the case of those series in which compounds are not formed, is of the greatest importance in

Jan 1, 1921

By C. F. Smart

THE heat treatment of the bronze composed of 88 per cent. copper, 10 per cent. tin, and 2 per cent. zinc, has been investigated by H. S. and J. G. S. Primrose,1 and also by the U. S. Bureau of Standards.2 The results obtained by H. S. and J. G. S. Primrose on dry-sand castings subjected to reheating followed by air cooling, or by quenching in water, are shown in Figs. 1 and 2. The values for tensile strength have been FIG. 1.-EFFECT OF QUENCHING ON DRY SAND CASTINGS (H. S. AND J. G. S. PRIMROSE.) converted from tons per square inch to pounds per square inch. Figs. 3and 4, have been plotted from values obtained by the Bureau of Standards on material of the same composition and treatment. Both investigations show that the ductility of the cast bronze is improved by heating to 700° C. and cooling in air, the strength not being impaired by this treatment. They are not in agreement, however, as to the effect of quenching, Messrs. Primrose reporting a decrease, and the Bureau of Standards an increase, in both strength and ductility when the cast bronze is heated to 600° or 700° C. and quenched.

Jan 9, 1919

By Howbert Van Dyne

THE Presidio mine of The American Metal Co. is situated in the "Big Bend" region, some 45 miles over state highway south of Marfa, a station on the Southern Pacific R.R. It lies 20 miles by road north of the Mexican border, in semidesert surroundings typical of this general section of the United States and the adjoining part of Mexico. All supplies are hauled in by truck from Marfa under contract. The concentrates and precipitates produced by the mill are carried by the same trucks to Marfa, from whence they are shipped, respectively, to the El Paso and Selby plants.

Jan 1, 1930

By D. E. Norquist, J. E. Moeller

The results of wear on marked balls, 4, 31/2, 3, and 2 in. diam are given. All balls were forged steel of practically the same chemical analysis and hardness. The results indicate that balls in a given mill for a given length of time will have equal diameter losses, regardless of size.

Jan 1, 1950

By W. Rostoker, R. P. Elliott, B. W. Levincer

Phase equilibria in the Ti-Cr-Mo system have been investigated for alloys containing 100 to 40 pct Ti in the temperature range 550° to 1300°C. Five experimental isothermal sections and a surface of incipient melting are presented in addition to a summary projection of the space. Seven vertical sections have been constructed from the isothermal sections. A STUDY of the system Ti-Cr-Mo was undertaken as part of a program sponsored by Watertown Arsenal toward the development of titanium-base phase equilibrium diagrams of potential technical importance to alloy development. The scope of the investigation included the composition range contained by the titanium corner and the line of 64 pct Ti (all compositions are by weight) and the temperature range 550" to 1100°C. A surface of incipient melting was constructed from measurements on a large number of alloys. The system Ti-Cr has been established.&apos;-? The phase diagram is characterized by a wide miscibility field of the solid solution at elevated temperatures and a eutectoid reaction of the type: (15 pct Cr) + TiCr, (685C). The a solid solution has a very limited capacity for solution of chromium (< 0.5 pct Cr). The intermediate phase TiCr2 has at best a very narrow composition range. It has been shown that two allotropic modifications of this phase exist. However, this behavior does not appear to be perceptibly reflected in the form of phase boundaries of the type + TiCr,. In the system Ti-Mo,9-10 the phase is stabilized to successively lower temperatures with increasing molybdenum content. There are no known intermediate phases. The a solid solution is limited to less than 0.5 pct Mo. Because of the very extensive range of the phase, the ternary system was ideally suited to the determination of the phase boundaries by the parametric method of Andersen and Jette." A parametric surface was constructed to provide the necessary basis for the application of this method. Preparation and Treatment of Alloys More than 60 alloy compositions were prepared for the study of this system. Alloy buttons of 10 grams were arc-melted in a nonconsumable electrode furnace using inert atmosphere protection and a water-cooled copper crucible. The construction and operation of this type of melting unit have been adequately described elsewhere.&apos;&apos; To insure complete solution of alloy additions, the buttons were remelted alternately on top or bottom as many as five times. This was accomplished by a suitable mechanism for "flipping" over the ingots. Iodide titanium (99.97 pct Ti) was used as the alloy base. An especially high quality chromium (99.9 pct Cr) was obtained from the National Research Corp. Molybdenum sheet (0.005 in.) of 99.9 pct purity was used.

Jan 1, 1954

By W. E. Dunn

CHLORINATION of titanium ores and slags is the source of TiCl,4 intermediate between ore and metal. A number of chlorinators are operating in the United States using a wide diversity of ores. These chlorinators vary in design to accommodate the ore source, but all use chlorine and carbon.

Jan 1, 1961

By I. S. Levy, J. L. Brimhall, B. Mastel

Specimens of&apos; Hastelloy X-280, a low-cobalt version of the solid-solution- hardened nickel-base alloy Hastelloy X, were given a series of thermomechanical treatttzents. They were then Lensile-tested at room temperature and 1350°F. The Microstructures of the specimens tested at 1350°F were studied by electron Microscopy. Microscopy showed that dislocation tangling, caused by the cold working, mas still in evidence after aging-for 24 hr to temperatures as high as 1550oF. (Cr, Mo)23 C6, (Fe, Mo)6 C&apos;. as well us an unidentifiable phase precipitale due to the combination of the thermomechanical treatments and subsequent tensile strain. The room -temperature and 1350°F tensile properties show a general increase ill strength and decreccse in ductility with increusing cold-work level. This is due to the dislocation taangling-. PerLurbatiot~s to this general trend occur- due to solid-solution weakening at the higher cold-work levels as a direct result of the preciplitation reactions. THE requirements for corrosion resistance and high-temperature strength place nickel-base alloys among the more promising materials for advanced nuclear reactor applications. However, when these alloys are irradiated at service temperatures, they generally suffer severe embrittlement&apos;" and reduction in rupture life.3 Certain experimental treatments resulted in improvements in the tensile and stress-rupture properties of Hastelloy X-280, a solution-hardened nickel-base alloy.&apos; To provide a basis for understanding these improvements, unirradiated tensile specimens were examined by electron microscopy. The results are reported in this paper. EXPERIMENTAL DETAILS Material. Hastelloy X-280, a low-cobalt version of Hastelloy X, is a member of the solution-hardened class of nickel-base alloys. The Hastelloy X-280 was obtained from 4- and 1-in: thick plates in the mill -annealed condition. Table I gives the chemical composition of the material as reported by the National Spectrographic Laboratories. ~x~erimental Treatments. Plates of suitable size, 12 by 3 by 1 in., or by + in., were cut under a water jet from the stock material and examined ultrasonic -ally for homogeneity of grain size and absence of voids. The acceptable plates were solution-treated at 2150°Ffor 1 hr and air-cooled. These plates were then reduced in thickness by cold rolling 0, 10, 15: or 20 pct along the original rolling direction. The plates were machined into buttonhead tensile specimens with a gage diameter of 0.125 in., with a gage length of 1.125 in., and with their tensile axes parallel to the rolling direction. The specimens were examined for quality of finish with a penetrant dye, ultra son ically checked for voids, and finally given a dimensional tolerance check with an optical comparator. The acceptable specimens were aged for 24 hr at either 1000" or 1500 F and air-cooled. These specimens were then held at 540°F in a water loop for approximately 18 days to qualify as controls for similar specimens irradiated under the same conditions of time, temperature, water chemistry, and flow rate. Table U summarizes the treatments. These treatments were investigated to establish whether prior precipitation and stabilization of carbide phases at strain sites within the matrix could reduce the amount of carbides available for precipitation at grain boundaries during service. Tensile-Test Conditions. Specimens were tested to fracture at room temperature or 1350 F in air on an Instron tensile-testing machine at a crosshead speed of 0.05 in. per min. The time for the furnace to reach equilibrium at 1350°F was approximately 30 min; soak time prior to testing was 15 min; and test duration was approximately 5 min.

Jan 1, 1968

By Olin M. Hart

Uranium ores occur in the Lower Cretaceous Inyan Kara group of heterogeneously stratified fluvial and fluvial-marine sandstones in the Black Hills of western South Dakota and northeastern Wyoming. There are three principal mining districts, each in the ancestral and present drainage area of a major river partially responsible for stripping the region to its present topographic form. Primary minerals in the deposits are coffinite and uraninite with minor amounts of paramontroseite and haggite. The ore minerals coat sand grains and fill interstices of complexly cross-stratified sandstone along solution fronts similar to "roll" type deposits of the other districts. Minerals of oxidized deposits are typically carnotite and tyuyamunite with different proportions of secondary vanadium accessory minerals. Ground water was the transporting medium and deposition of primary uranium and vanadium minerals occurred in reducing environments produced and controlled by physio-chemical characteristics of the sedimentary rocks.

Jan 1, 1968

By Guy N. Bjorge

HOMESTAKE&apos;S mining methods today are of necessity controlled to a considerable extent by that which has been done in the past. This may be shown by the fact that our two main operating shafts now, the B. & M. and Ellison, were begun in 1878 and 1896 respectively, so that-the loca-tions of shafts, locations of all the drifts on the upper levels, and a great deal of sloping was done before any of us now connected with the mine had anything to do- with it. Anything that I may say is not to be construed as criticism of those who have gone before for it would be a sad commentary indeed on us if we had not learned something from their experience. The levels down to the 1100 in the Homestake mine are spaced at 100-ft. intervals, and below that at 150-ft. intervals. The general plan of develop-

Jan 1, 1934

By L. S. Darken

A quadratic formalism is developed lor the representation of the excess free energy, and of the activity coefficients of each component of a ternary system in the vicinity of a single component selected as solvent. This formalism, in contrast to the e formalism, is thermodynamically consistent at .finite concentrations. Numerous specific systems are used as illustrations, with cross checks where possible; these systems are Fe-C-X systems in the vicinity of 1600°C and include practically all those for which reliable data are available. It is shown that this formalism is usually quite adequate to rebresent available data up to a solute concentration of 20 to 30 at. pet. It is hoped that the formalism here presented may prove useful for the treatment and tabulation of data on ternary and multi-component solutions. SINCE, as discussed in a prior paper,&apos; we do not as yet have an adequate basic understanding of the nature of binary metallic solutions, we cannot hope to be in better position for ternary and multicomponent systems. However, the accumulation of thermodynamic data on ternary and multicomponent metallic solutions has led to an urgent need for a rational formalism for the presentation and use of such data. Notable attempts to represent the isothermal isobaric thermodynamics of ternary solutions were made by Benedict et 01.&apos; and by Wohl.3 These attempts were directed toward developing an analytic expression adequate to encompass the entire ternary triangle, primarily for organic systems; they generally involve the power-series approach, which has been shown&apos; to be inappropriate, in general, even for binary metallic systems. On the other hand, interest in the thermodynamics of ternary and multicomponent metallic solutions has tended to focus either on general thermodynamic relations4-10 over wide compositional ranges, or on cases where one or more components have been at rather low concentration. This latter approach has been followed by Wagner,= by chipman,11 and by Alcock and Richardson,12 and more recently in many publications by the same and other authors. It has already been shown&apos; that the thermodynamic behavior of binary metallic systems is, in general, relatively simple only in the terminal regions. Hence, it would appear that any approach, at this time, to a simple formalism for ternary and multicomponent systems must, a fortiori, be limited to the vicinity of the major component or solvent. The present treatment is aimed to be useful for a given solvent with moderate solute concentrations ranging up to 20 or 25 at. pet and in exceptional cases to considerably higher concentrations. In order to achieve even this modest objective, it is necessary that any appropriate formalism have built into it 1) a thermodynamic consistency (at least within the desired degree of approximation), and 2) an approach at infinite dilution to Raoult&apos;s law for the solvent and to Henry&apos;s law for each solute. Let us first formulate the condition of thermodynamic consistency for a ternary system. Under isothermal isobaric conditions, we may write for the molal value G of any extensive function dG - C1 dN1 + G2 dN2 + G3 dN3 [l] where the G&apos;s are the corresponding partial molal quantities and the N&apos;s are the atom fractions. Taking component 1 as the solvent, this relation may be rewritten in terms of the independent variables N2 and N3

Jan 1, 1968

By F. Weinberg, E. H. McLaren

Dilute binary alloys have been solidified under controlled thermal conditions, and solute distributions, temperatures during freezing and melting, and the position and morphology of the solid-liquid interfaces have been examined. Binary Zn, Sn, and Pb based alloys were investigated with solute additions of AgU°, AU°, Sb&apos;24, TlZo4, snH3, and Zns5. Approximately 150 cc of metal was used in each ingot. Appreciable solute segregation occurred in most of the ingots, depending on the solute concentrations, distribution coefficients. and freezing conditions of the alloys. Measurements were made of the general solute distribution by sectioning layers of material from the ingot circumference and counting the activity of each layer. Local segregation was detected by autoradiographic techniques. Freezing and melting curves for the same alloys were obtained by precision resistance thermometry. These curves are related to the corresponding measured solute distribution curves and those calculated from theoretical expressions. The position and morphology of solid-liquid interfaces during freezing were determined by both decanting and quenching techniques. The results indicate the manner in which freezing and remelting occurred under the conditions investigated. If an isomorphous dilute binary alloy is solidified or melted under equilibrium conditions, the concentration of solute in both solid and liquid would be uniform at all stages in the freezing process. The solute concentrations during freezing could be determined from the phase diagram of the alloy, and the freezing curves would have an alloy slope defined by the solidus and liquidus points. In practice, however, solidification under equilibrium conditions rarely, if ever, occurs, primarily because of low rates of diffusion in the solid and incomplete mixing in the liquid. As a result, the solute distribution and the shape of the freezing and melting curves obtained in a given system depends on a number of factors. These include, in addition to the extent of diffusion and mixing, the initial solute distribution and concentration, the distribution coefficient, the rate of freezing or melting, supercooling of the liquid, the morphology of the solid-liquid interface, and the effect of annealing. The purpose of the present investigation was to determine, experimentally, actual solute distributions and thermal curves for a series of dilute binary alloys, using tracer techniques to determine the solute distributions and precision resistance thermometry for the temperature measurements. In addition, observations were made of the positions and morphologies of the solid-liquid interfaces during freezing and remelting. The distribution of solute in a dilute alloy, assuming complete mixing in the liquid, and negligible diffusion in the solid, is given by1 where Co is the mean solute concentration of the alloy, C, is the solute concentration in the solidg is the fraction of the ingot solidified, and ko is the equilibrium solute distribution coefficient (assumed to be independent of concentration for dilute alloys). For the case of partial mixing, ko can be replaced by an effective distribution coefficient k. If solute transport in the liquid is assumed to be entirely due to diffusion, with negligible diffusion in the solid, then the solute distribution in the solid is given by Tiller et a1.&apos; as where R is the rate of advance of the solid-liquid interface, D is the solute diffusion coefficient in the liquid, and x is the position of the interface from the start of freezing. The temperature at the interface TI is related to the solute concentration of the solid at the interface C, by the expression where Tm is the freezing temperature of the pure solvent and ml is the slope of the liquidus for the binary alloy being considered. Accordingly, by relating TL to the actual temperatures measured in the present experiments, solute distributions can be deduced from the temperature measurements. Using the above expressions, the measured solute distribution of a given alloy may be compared to the theoretical distributions, as well as to the distribution calculated from the observed freezing curve. EXPERIMENTAL The solvent materials used in making up the binary alloys were C. P. New Jersey zinc (99.999 pct), Vulcan Extra Pure Tin (99.999 pet), and Tadanac lead (99.998 pct). The solute elements were of 99.99 pct purity or better, and were activated in the

Jan 1, 1963

By M. D. Arnold, P. B. Crawford, P. C. Hall

An experimental study has been made to determine the optimum flooding pressures for four different oils. The oil formation volume factors ranged from 1.08 to 2.13, and solution gas-oil ratios ranged from about 200 cu ft/bbl to 2,250 cu ft/bbl. Viscosities ranged from 0.38 to 0.95 cp at the respective bubble points of the fluids and from 0.7 to 20 cp at atmospheric pressure. Water floods were conducted at various pressure levels from run to run. The recovery as a function of flooding pressure was found to be different for each fluid, with optimum gas saturations ranging from 7 up to 35 per cent. The data indicate that substantially higher recoveries may be obtained if water floods are conducted at an optimum pressure and that this optimum pressure is a function of fluid properties. The same core was used for all tests, and the reproduction of saturations for various runs indicates that wettability in the predominantly water-wet core did not change. INTRODUCTION A paper was presented by Bass and Crawford&apos; which described an experimental study of the effects of flooding pressure and rate on oil recovery by water flooding. This work was conducted using high-pressure models operated in a manner similar to that of an actual reservoir, with gas saturations being obtained by a solution-gas-drive mechanism. They found that the greatest oil recovery was obtained for the system studied by flooding in the presence of a 5 to 7 per cent gas saturation. Another experimental study simulating field conditions was presented by Richardson and Perkins.&apos; They used an unconsolidated sand pack containing kerosene-natural gas fluid and interstitial water. They flooded at various pressures and flooding rates. For their system it was found that the recovery was independent of the pressure level at which the water flood was performed. Kyte, et al," found that oil recovery by water flooding was increased as the free gas saturation at waterflood initiation was increased. However, after the initial gas saturation was increased above 15 per cent, the increase in oil recovery tended to level off. All of their runs were made at the same pressure using a light oil saturated with helium. The desired gas saturation was obtained by injecting helium into the core. Dyes&apos; made calculations which showed that an optimum gas saturation of 12 to 14 per cent may result in an increase in oil recovery of 7 to 12 per cent over that obtained by flooding at the bubble-point pressure. Others have also found that the presence of a free gas saturation may increase the waterflood oil recovery. In each case shrinkage was small and changes in fluid properties with respect to pressure were small. A careful review of the literature reveals that at the present time there is a wide difference of opinion on the factors affecting waterflood recoveries. This diversity of opinion is probably due to the fact that very little research has been done which has taken into account the many variables existing in an actual field being water flooded. Since the literature contains little information on high-pressure waterflooding studies using various types of reservoir fluids, it was believed appropriate that such a study should be made. EQUIPMENT AND PROCEDURE All tests were made using the same consolidated sandstone core. Torpedo sandstone was used to turn a cylindrical core 13.5-in. long and with a 2.92-in. average diameter. The core had a porosity of 28 per cent and a permeability to brine of 146 md. This brine was made up by adding 20,000-ppm sodium chloride and 30,000-ppm sodium nitrite to distilled water. This was used as connate water and flooding water. No fresh water was ever brought in contact with the core, as tests showed the sandstone contained argillaceous material which swelled in the presence of fresh water and plugged the stone. The core was sealed in a section of 6-in. N-80 tubing with Woods metal filling the annulus. The core was mounted horizontally; an injection well was placed in the center of one end and a production well in the center of the other. Pressure control was maintained by placing a back-pressure regulator (upstream control) on the producing well. The "live" oil was stored in a separate bottle and water was injected into this bottle to displace the oil for saturating the core using a two-cylinder standard-proportioning pump. This same pump was used for water flooding the core at a constant rate. This system was enclosed in water jackets and the temperature was automatically main-

By W. T. Olsen, R. Ulcer

WHEN a liquid alloy freezes, the solid first formed usually differs widely in chemical composition from that last formed, so that there is segregation in the alloy as cast. For example in the copper-nickel system (fig. 1) the first solid formed from a liquid containing 55 atomic pct Cu may contain as little as 38 pct Cu, while the last must contain well over 55 pct. Three factors may act to decrease segregation from the maximum possible. 1. Diffusion in the cooling solid tends to make the phase homogeneous, decreasing segregation. This may be important at slow rates of cooling. 2. Segregation is impossible without diffusion in the liquid. At extremely rapid rates of cooling there may not be enough time to allow maximum segregation. 3. Supercooling delays nucleation to temperatures well below the liquidus thereby decreasing segregation. Hence the first nucleus in the copper-nickel system may contain well over 38 pct Cu. At sufficient supercooling the first nucleus may form below the solidus, in which case there is no reason to expect any segregation whatever. From these considerations, we could predict that at sufficiently low rates of cooling the alloy would be unsegregated because of factor 1 and at sufficiently high rates of cooling there should also be no segregation because of factors 2 and 3. Considerable segregation should occur only at intermediate rates of cooling. We have demonstrated experimentally that segregation can be completely suppressed by rapid rates of cooling. For the alloys studied, however, these rates are too great to be attained in any commercial practice. An alloy of 55 atomic pct Cu, 45 atomic pct Ni was frozen by cooling at varying rates. The degree of segregation in the solid was determined by X-ray diffraction photographs. Slow rates were obtained by slowly cooling the furnace containing the liquid alloy; fast rates by pouring or ejecting droplets of the alloy into water or iced sodium hydroxide solutions. The cooling rate of the droplets can be cal-culated from their dimensions by assuming reason- able values of thermal conductivity.&apos; The experi-ments were repeated with an alloy of 16.5 pct Cu and 83.5 pct Au. A single experiment also showed a 50 atomic pct Bi-Sb alloy had no segregation at the most rapid quench. The position of back-reflection X-ray diffraction lines is a highly sensitive function of the lattice constant, which in turn depends on the chemical composition of the phase. A phase of varying composition will give broad diffraction lines. By measuring the edges of these lines and making suitable corrections for intrinsic line width, it is possible to determine the range of lattice constants represented. These can be converted to chemical compositions from a lattice constant vs. composition curve. Results are shown in table I. In the copper-nickel system the greatest segregation is found at the slowest cooling rates, where the lowest percentage of copper theoretically possible is found. In the copper-gold system, on the other hand, the degree of segregation is decidedly less at the slowest rates of cooling, being greatest at 11,100°C per sec. At no rate is the theoretically lowest percentage of copper (12 pct) found. At the rates of cooling found in sand and die castings the degree of segregation is large and depends little on the rate of cooling. Acknowledgment Most of the material in this paper is abstracted from a thesis presented by William T. Olsen, Jr. in 1948 in partial fulfillment of the requirements for the degree of Master of Science at the University of California.

Jan 1, 1951

By CHARLES F. DEISS

The total pipe-line runs of petroleum in Indiana during 1945 were 4,114,000 bbl., a decline of nearly 17 per cent below the estimated 4,950,000 bbl. produced in 1944. Drilling activity during the year was centered in Posey and Gibson Counties, where seven new pools were discovered in the state. Four of the pools are in Posey County-Crunk, Farmersville, Jeffries and St. Wendells East-and the other three are in Gibson County-Johnson West, Lysle and Mt. Carmel East.

Jan 1, 1946

By Thomas Egleston

All industrial establishments whose operations depend upon chemical reactions use gases. In the simplest case the oxygen of the atmosphere, heated or not, as the case may be, is used, and in other cases, gases which are produced by a special apparatus of more or less complex composition. The manufacturer depends, for the success of his operations, entirely upon having these gases arrive at the right time, in the proper proportions, at the required temperature. It often requires but a slight variation in their composition to make a given process a success or a failure. In most cases the gas used is formed from fuel, and according as variations in its composition are produced by alterations in the manner of charging the grate, not only different, but often directly opposite, results are obtained. The great industrial question of the present time, and one upon which the prosperity of the world depends, is how to get the greatest amount of useful effect from fuel, whether the caloric is used directly or is transformed into horse-power. In almost all industrial pursuits this translates itself into the question of how to construct a fireplace and its adjuncts in such a way that the heat of the flame and of the products of combustion shall be made to produce a maximum effect. Unfortunately, until very recently, except by comparison, there was no means of ascertaining whether the loss of useful effect was 80, 40, or 20 per cent. of the total amount of fuel employed. It seems now strange that there should have been furnaces so constructed as to produce 20 per cent. of carbonic acid in the fireplace, but this has been proved by analysis to have been true. It does seem incredible that, notwithstanding the immense number and variety of furnaces used for different processes, and the great difference in kind, quality, and quantity of fuels consumed, there should formerly have been used for them all, the same stereotyped fireplace, varied only in its dimensions of height, length, and breadth. It is true that, with a good fireman, excellent effects may be, and have been, produced, but the manufacture is here, as in many other cases, dependent on the intelligence of the workman, a very uncertain reliance for capital to rest upon. The workman, unless he receives a prime for fuel saved, or is fined for excessive use of it, may be said

By T. Prof. Egleston

ALL industrial establishments whose operations depend upon chemical reactions use gases. In the simplest case the oxygen of the atmosphere, heated or not, as the case may be, is used, and in other cases, gases which are produced by a special apparatus of more or less complex composition. The manufacturer depends, for the success of his operations, entirely upon having these gases arrive at the right time, in the proper proportions, at the required temperature. It often requires but a slight variation in their composition to make a given process a success or a failure. In most cases the gas used is formed from fuel, and according as variations in its composition are produced by alterations in the manner of charging the grate, not only different, but often directly opposite, results are obtained. The great industrial question of the present time, and one upon which the prosperity of the world depends, is how to get the greatest amount of useful effect from fuel, whether the caloric is used directly or is transformed into horse-power. In almost all industrial pursuits this translates itself into the question of how to construct a fireplace and its adjuncts in such a way that the heat of the flame and of the products of combustion shall be made to produce a maximum effect. Unfortunately, until very recently, except by comparison, there was no means of ascertaining whether the loss of useful effect was 80, 40, or 20 per cent. of the total amount of fuel employed. It seems now strange that there should have been furnaces so constructed as to produce 20 per cent. of carbonic acid in the fireplace, but this has been proved by analysis to have been true. It does seem incredible that, notwithstanding the immense number and variety of furnaces used for different processes, and the great difference in kind, quality, and quantity of fuels consumed, there should formerly have been used for them all, the same stereotyped fireplace, varied only in its dimensions of height, length, and breadth. It is true that, with a good fireman, excellent effects may be, and have been, produced, but the manufacture is here, as in many other cases, dependent on the intelligence of the workman, a very uncertain reliance for capital to rest upon. The workman, unless he receives a prime for fuel saved, or is fined for excessive use of it, may be said

Jan 1, 1874

By Peter F. Weiss

INTRODUCTION Austro-American Magnesite Co. of Radenthein, Carinthia, Austria, is a wholly owned subsidiary of General Refractories Company, Bala Cynwyd, USA, and has been incorporated since 1908. The raw material basis is the magnesite mine on Millstatt Alp, located in the mountains near Radenthein at an altitude of 1500 m above sea level. The mined crude magnesite is crushed in a surface crushing plant to minus 35 mm and consequently hauled to the processing plant in the valley by means of a cable conveyor of 7.5 km length. The annual production of 350,000 mt is accomplished with 20 supervisors and 122 workers (of those 60 are in the mine). The labor requirement for block caving is 0.2 man hr/mt, corresponding to an output of 40 mt/man/ shift. GEOLOGY The rock in this area mainly consists of crystalline type schist. There are mostly coarse crystalline garnet mica schists with varying mineral concentrations, and to a lesser degree, some deposits of amphibolite and marble. This petrographically rather homogeneous rock is divided into numerous different tectonic units (covers and scales). The magnesite deposit itself is a foreign body that also has been tectonically inserted. The ore body has a length of 600 m, is 450 m deep, and has a thickness of 60 m on average, varying substantially however, The contact with the accessory rock is very precise. The deposit 1 = ore body, 2 = previous open pit, 3 = caved in area, 4 = block under excavation, 5 = land slide consists of coarse crystalline magnesite in excess of 90 per cent. The few impurities consist of dolomite and talc. The lower part of the deposit is inclined parallel with the schists at approx. 40 degrees. In profile it can be seen, however, that the upper part of the deposit has been tilted over. This is a result of a post-glacial land slide reaching from the bottom of the valley at 1400 m above sea level to the peak of the mountain at 2100 m above sea level. Due to this land slide, with horizontal movements of up to 100 meters, as well as older tectonic events, the rock was crushed to a vast extent. Through mining, the land slide was reactivated; about 40 million cubic meters of rock slowly flow downhill almost like a plasticized mass. Near the surface, the rock is completely crushed and resembles a glacier rupture zone. This renders the originally impermeable rock completely water permeable so that practically all of the annual quantity of 1000 to 1100 mm of precipitation permeates the rock and flows down into the mine. The carbonate rock turns into the preferred aquifer. From 1700 to 2600 cubic meters of water have to be pumped from the mine daily. On one hand, additional problems are caused by the water in the mine, on the other hand we have learned to make use of the down- hill pressure forces to improve the crushing process during block caving. The boundary of the downhill shearing zone moves downward as mining goes deeper.

Jan 1, 1981