Search Documents

By T. P. Floridis

It was deemed desirable to obtain an understanding of the vacuum desulfurization process. McKechnie1 has reported that the sulfur content of nickel- and cobalt-base alloys is reduced in vacuo. Keverian and Taylor2 have observed that vacuum melting causes desulfurization of iron-carbon-silicon alloys. Garnyk and samarin3 have desulfurized transformer steel by vacuum treatment. Experiments were conducted in order to investigate the desulfurization of liquid iron under reduced pressures, and to establish the effect of some alloying elements, and various crucible materials. A vacuum-induction furnace of 50-lb capacity was used. The charge was Armco iron. Silicon was added as 90 pct ferrosilicon, carbon as electrode graphite, and aluminum as high-purity aluminum metal. Magnesia and silica crucibles were used, their inside diameters were 5 1/2 and 5 3/8 in., respectively. The temperature was measured with an optical pyrometer and it was held at 1600 1 15°C. Samples were withdrawn with quartz tubes of 6 mm ID, without disturbing the furnace atmosphere. Pressures were measured with an alphatron gage. The experimental results are shown in Fig. 1. They indicate that: 1) Sulfur can be removed from liquid iron alloys by vacuum treatment; 2) The desulfurization is enhanced by the presence of silicon, carbon, and aluminum, all these elements increase the activity of sulfur dissolved in liquid iron;4 3) The pronounced effect of silicon indicates that probably a volatile silicon sulfide is formed, Alcock and Richardson5 have observed a similar phenomenon; 4) The same rate of desulfurization was obtained when the metal was contained in either magnesia or silica crucibles. Dr. J. Keverian has contributed many discussions and recommendations. M. S. Sutliff has helped in conducting the heats. The permission of General Electric Co. for this publication is gratefully acknowledged.

Jan 1, 1960

By W. H. McCormick, H. J. Benecki

CONSIDERING that a typical modern drilling machine strikes approximately 2000 blows per min and may develop a force of 30 to 200 ft-lb, de- pending upon size of the drill used, the importance of uniform stress distribution in this type of drilling becomes obvious. If the rod were perfectly symmetrical, and if it did not rotate, the problem would be relatively simple, however, the necessary forging, machining and heat treating operations prevent attaining this state of perfection. Take the modern hollow drill rod. The blow is transmitted not from the striking end of the rod directly through to the point of impact of the bit in the rock, but rather through a somewhat complex tool. To add further problems, this entire assembly is rotated immediately after the impacting blow. Rather than attempt to discuss the magnitude and distribution of stresses, it is desired to present a few things that will minimize unusual stress concentration and produce a rod in which the stress distribution will approach the theoretical ideal.

Jan 3, 1954

By John M. Campbell, W. E. Portman

A series of correlating charts have been prepared to enable the field engineer to predict the amount of stock tank fluid produced by stabilization of first stage separator fluid. The charts shown are particularly convenient for estimating the relative effect of temperature and pressure in economic studies. Further work is planned to investigate the factors affecting stage separation' yo supplement this preliminary work. The direct correlation of separation variables is dictated as a convenience to eliminate the trial and error calculation necessary when using the standard flash vaporization equations. These are obtained by a material balance using the equilibrium vaporization ratio K, and have appeared in the following, or similar. form many times in the literature. where La = mols of any component n in the separator liquid Ko — equilibrium vaporization ratio for any component at separator pressure and temperature Fa = mols of any component n in the feed Vn = mols of any component n in the vapor V = total mols of separator vapor These equations may of course be effectively and accurately solved by use of digital and analog computers. However, these are not usually readily available in field offices and the need often arises for fast results during routine operational problems. Consequently, many methods have been devised in an attempt to simplify the basic calculation.2-14 The methods proposed are generally satisfactory, but do not eliminate trial and error methods and the necessity of subsequent calculations to obtain the answer in volume terms. The purpose of this work. therefore, was to develop accurate charts that would give the result directly in gallons. When using stage separation the recoveries would be lower than those shown, for stabilization usually gives about 95 + per cent recovery on the potential stock tank components in the separator liquid. The recoveries are shown in terms of a 14 psi Reid Vapor Pressure product which has a true vapor pressure of 14.7 psia at 98°F. Consequently, this product represents a stable stock tank liquid under normal storage conditions. To estimate natural gasoline re- coveries by stabilization the volume shown may be multiplied by 1.20 for 18 Ib RVP natural gasoline and 1.36 for 26 lb RVP natural gasoline. PROCEDURE The five analyses shown in Table 1 were chosen since they were representative of wellstream compositions often found and had almost the same propanes plus liquid content, expressed in gallons per 1,000 std. cu ft of wellstream. The distribution of the components though is widely variant. A temperature range of 0-100°F. and a pressure range of 200 to 1,250 psia was chosen inasmuch as most separations fall within these limits The K values used were modified values of those originally published by Katz and Hachmuth.' In the range chosen these have generally given good results when predicting fluid recoveries. The choice was somewhat arbitrary, for the authors' personal experience has shown that

Jan 1, 1957

By A. S. Yue

It was deemed desirable to obtain an understanding of the vacuum desulfurization process. McKechnie1 has reported that the sulfur content of nickel- and cobalt-base alloys is reduced in vacuo. Keverian and Taylor2 have observed that vacuum melting causes desulfurization of iron-carbon-silicon alloys. Garnyk and samarin3 have desulfurized transformer steel by vacuum treatment. Experiments were conducted in order to investigate the desulfurization of liquid iron under reduced pressures, and to establish the effect of some alloying elements, and various crucible materials. A vacuum-induction furnace of 50-lb capacity was used. The charge was Armco iron. Silicon was added as 90 pct ferrosilicon, carbon as electrode graphite, and aluminum as high-purity aluminum metal. Magnesia and silica crucibles were used, their inside diameters were 5 1/2 and 5 3/8 in., respectively. The temperature was measured with an optical pyrometer and it was held at 1600 1 15°C. Samples were withdrawn with quartz tubes of 6 mm ID, without disturbing the furnace atmosphere. Pressures were measured with an alphatron gage. The experimental results are shown in Fig. 1. They indicate that: 1) Sulfur can be removed from liquid iron alloys by vacuum treatment; 2) The desulfurization is enhanced by the presence of silicon, carbon, and aluminum, all these elements increase the activity of sulfur dissolved in liquid iron;4 3) The pronounced effect of silicon indicates that probably a volatile silicon sulfide is formed, Alcock and Richardson5 have observed a similar phenomenon; 4) The same rate of desulfurization was obtained when the metal was contained in either magnesia or silica crucibles. Dr. J. Keverian has contributed many discussions and recommendations. M. S. Sutliff has helped in conducting the heats. The permission of General Electric Co. for this publication is gratefully acknowledged.

Jan 1, 1960

By Douglas Bunting

In the anthracite fields of Pennsylvania, mine fires occur with more or less regularity and their existence is an ever-present hazard in coal mining. In all probability 90 per cent. of the mine fires can be ascribed directly or indirectly to the ordinary miner's open lamp. Other causes may be smoking, electrical installations, gas explosions, gas feeders, and the communication of fire to the outcrops from ash dumps, culm banks, timber and brush fires. Fires in pump rooms, engine rooms, and barns have been largely eliminated as a result of the Act of Assembly, approved June 15, 1911, which provides that all inside buildings, including engine rooms, pump rooms, barns, etc., shall be constructed of incombustible materials. Smoking of pipes, cigars, and cigarettes should be prohibited in the mines and too much care cannot be exercised in preventing fires by enforcing all rules designed for that purpose. Mine fires that involve underground fighting are invariably dangerous, and all fires, irrespective of the method pursued in extinguishing them, involve property loss and expense. Each fire generally presents a more or less original problem, dependent on the particular conditions. Generally mine fires may be divided into two classes: Those occurring in inaccessible workings and those occurring in accessible workings. The methods pursued in extinguishing or controlling mine fires are as follows: (I) direct attack, (2) smothering by sealing, (3) flushing with silt or other solids, (4) flooding with water, (5) cutting off, (6) surrounding with incombustible materials, (7) digging out by stripping from the surface. Most fires arc extinguished in their incipiency by direct attack and failure to extinguish by this method is due to late discovery, lack of water, and facilities for fighting, or improper procedure in the initial attack. Should the method first pursued be unsuccessful, careful consideration should be given in determining next the method to be adopted; then the work should be carried on as rapidly as possible and under the supervision of the most competent persons. Materials and supplies should be furnished without delay and in sufficient quantities for the work to be accomplished.

Jan 1, 1922

By Dick Whittington, W. R. Taylor

GENERAL In mid-1974, a representative of ARCO Petroleum Company walked into our Austin offices and asked for a permit for ARCO's first Clay West Mine site. This was the first in situ uranium mining permit issued in the United States. That initial permit, issued in January 1975, was for three acres. The four years since have been characterized by growth and change. Today there are 16 permits approved for approximately 1,540 production acres issued to five companies at eight sites in four counties. There are approximately seven additional permit applications being processed or on the verge of being submitted for an estimated 2,000 additional acres of production. As a rough gauge of the financial scope of this activity, at the typical 40 production wells per acre and an estimated $2,000/well, operators hale installed or committed $122 million for production wells. This does not account for the exploration and development wells installed to delineate the ore or the cost of processing facilities for extracting the uranium. HISTORY OF URANIUM MINING IN TEXAS Information I have concerning early in situ uranium mining activities is "sketchy" but the apparent first on-site test of in situ uranium mining was conducted between 1967 and 1971 at the Dueterstat site, north of Yorktown in Gonzales County, by City Service. Others ran tests at the Bruni site in Webb County and the Burns and Clay West sites in Live Oak County in the mid-70's. During this period, Texas Water Quality Board personnel in the central and district offices maintained a general surveillance of these various test activities. Regulation of in situ uranium mining was formalized with the issuance of a permit in January 1975 with the advent of ARCO's initial production scale (3 acre) effort in the Clay West area at the Moser mine site. Since 1975, the accelerating rate of mining and exploration activity is noticeable. There were 16 exploratory rigs operating early in 1977. This year, the rig count is averaging 46--a 287% increase. HISTORY OF LEGISLATION Paralleling this mining activity was state and federal legislation which subjected in situ mining to environmental regulation. The following is a brief chronology of the legislation that is directly or indirectly related to uranium mining. As most of you know, disposal wells are an integral part of most in situ uranium mines operating in Texas. They are used both during production and during aquifer restoration following production. The wells are regulated by the Texas Injection Well Act, enacted in 1961 by the Texas Legislature. In 1967, the Water Quality Act established the Texas Water Quality Board, and provided for the regulation of water quality by the so-called permit system. In 1969, the Solid Waste Act was enacted by the Texas Legislature. The legislation provides for control of wastes from manufacturing, mining, and agriculture. This Act regulated uranium surface mining activities until 1975 when the Texas Surface and Mining Reclamation Act placed responsibility with the Railroad Commission for uranium open-pit mining and surface mining of coal and lignite. In 1972, the Federal Water Pollution Control Act (Public Law 92-500) was passed. This legislation forms the legal base for the NPDES (National Pollutant Discharge Elimination System) and the subsequent point source effluent guidelines and standards. The November 6, 1975 issue of the Federal Register published interim final rules for Best Practical Treatment levels for effluent discharges from ore mining and dressing operations. Litigation was immediately initiated by eleven companies against these proposed rules, and they are currently being reconsidered for reissuance in 1979. In 1974, the Federal Safe Drinking Water Act (Public Law 93-523) was enacted. A part of this legislation is the Underground Injection Congrol Program. The regulations implementing this program have undergone various public hearings and it is expected that they will be published in the Federal Register before the end of 1978. In 1975, the Texas Surface Mining and Reclamation Act (Senate Bill 55), providing for the Railroad Commission's authority to require reclamation of surface mines, was passed. In 1977, an amendment to Senate Bill 55 was introduced that proposed to place regulation of in situ mining of coal, lignite, and

Jan 1, 1979

By S. C. Langdon, Henry S. Rawdon

The following note describing the behavior of copper under rather unusual conditions is offered for its suggestiveness rather than as a complete study of the question. The examinations described were made because of a request for information concerning the embrittlement of copper when heated in a molten salt bath (sodium chloride) for the purpose of cleaning, as well as softening it. It is well known that metals may be rendered very brittle by electrolytic action in aqueous solutions, in all probability by the action of nascent hydrogen, and it was suspected that perhaps the embrittlement of the copper by means of the molten salt was produced in a somewhat similar manner. It was found that the copper was in contact with iron (or steel) while immersed in the molten salt, through the occasional use of an iron stirring rod, iron forceps for handling the pieces, and an iron pot for containing the fused salt. In the electrochemical potential series iron and copper stand some distance apart, copper being electronegative to the iron. Assuming that the two metals bear 2 similar relation to each other, when immersed in a bath of molten salt, as they do in an aqueous solution, they would be expected to form a galvanic couple, the copper being the cathode. By this means the copper might be embrittled, as often happens in aqueous solutions, by the action of the liberated hydrogen. In this case, however, the embrittlement must be attributed to some other agent than hydrogen. TO demonstrate how copper may be embrittled under these conditions, two small rods, one of copper and the other of mild steel, approximately 3/8 in. (9.5 mm.) in diameter, were immersed in a bath of sodium chloride that had been heated somewhat above its fusion point (melting point of sodium chloride is 801" C.) and an electromotive force of approximately 6 volts from a storage battery was impressed upon the system. The copper was made the cathode and the action was continued for several minutes. When removed from the bath, cooled, and tested for brittleness by bending the specimen back and forth, while clamped firmly at one end in a vise, the copper rod was found to be very brittle, as compared with a rod of the same length of the untreated copper tested

Jan 1, 1921

By T. P. Chen, F. W. Bowdish

Studies made with a captive bubble apparatus on the sulfidization and collection by amyl xanthate of true chrysocolla specimens have defined the ranges of pH value and sulfide concentration which permit contact between the bubble and the mineral surface. Titanium compounds were the most effective of the materials found to activate the sulfidization of chrysocolla. With titanium activation, the contact angles and the ranges of pH value and sulfide wncentration giving bubble contact were all increased. Chrysocolla ores were concentrated by flotation. Chrysocolla ores occur at many localities in grade and quantity sufficient to make mining and millin feasible, but no satisfactory method of concentratio has been found. Although chrysocolla may be leached with acid, only those ores without acid-consuming gangue may be leached economically. Because of its potential importance, a study of the conditions nece sary for flotation of chrysocolla has been carried ou The literature contains a few references to flotation of chrysocolla. Two methods were developed by the U. S. Bureau of Mines.1,2 The first consisted of a fatty acid soap and a high xanthate as collectors of chrysocolla from a synthetic ore, while the second involved the use of hydrogen sulfide and xanthate. Ludt and DeWitt3 demonstrated the difference in adsorptive powers of chrysocolla and quartz for bas triphenyl methane dyes and suggested the use of butyl, hexyl or octyl-substituted malachite green as collector. Jackel4 emphasized the effects of combin tions of reagents such as Aerofloat 31, pine oil, and Reagents 404 and 425 with sodium sulfide and zinc hydrosulfite as conditioning agents. Although he reported recoveries of 89% from a synthetic ore and 98% from a natural ore containing azurite, malachite, chalcopyrite and chrysocolla, careful application of Jackel's method to chrysocolla from Tyrone, N.M., failed to give a high recovery. MATERIALS AND TECHNIQUE Samples from Inspiration, Ariz., and Tyrone and Magdalena, N. M., were used for experimentation and verified as true chrysocolla by leaching tests, specific gravity tests and X-ray diffraction. Chrysocolla does not dissolve at pH 4, although malachite and azurite do. Chrysocolla is about half as dense as the copper carbonates. X-ray diffraction analyses by the powder camera method confirmed the samples as true chrysocolla. A captive bubble apparatus, which cast an enlarged image of the air bubble and the mineral surface upon a screen, was used to check on the character of the surfaces. The specimens were prepared by grinding a flat surface on a glass plate using fine abrasive; then they were washed and kept in distilled water until they were to be treated with reagents. Before each reagent treatment, the specimen was carefully checked for cleanliness in the captive bubble apparatus. It was assumed that the surface was clean if, after fine grinding and washing of the specimen, the bubble would not stick. Specimens were handled with glass forceps, and precautions were taken to avoid contamination of the mineral surfaces. Contact angle measurements were carefully made several times on each treated specimen to obtain reliable average values. EFFECT OF pH VALUE AND SODIUM SULFIDE CONCENTRATION In each experiment, a specimen with a freshly ground surface was immersed for 10 min in a solution of sodium sulfide, washed and immersed for 15 min in a solution containing 30 mg per 1 of potassium amyl xanthate. The specimen was then washed again in distilled water and tested for contact angle in the captive bubble apparatus while submerged in distilled water. In this series of experiments, the pH of the sulfidizing solution was varied from 3 to 7, and the concentration of sodium sulfide, containing 60% Na2S, was varied from 50 to 650 mg per 1. Many combinations of pH value and sulfide concentration resulted in no contact between the bubble and the surface, but over a limited range of conditions, contact angles varying from 24ºto 52ºwere obtained. The data in Fig. 1 show sulfidization conditions that lead to bubble contact and those that do not. The region of contact is surprisingly small, which may indicate why flotation of chrysocolla involving sulfidization has proven so difficult in practice. Several features of the system are illustrated in Fig. 1. In the region between pH values of 4 and 6 with sodium sulfide concentrations below about 350

Jan 1, 1963

By W. M. Johns

The geological mapping of Lincoln and Flathead Counties was a five-year project undertaken by the Montana Bureau of Mines and Geology. This paper, written by the Project Geologist of the survey, is primarily concerned with the stratigraphy of the Belt rocks encountered in mapping. Lincoln and Flathead Counties of northwestern Montana are underlain by sedimentary rocks of the Belt Series of Precambrian age. In only a very small part of the area, near Libby and Troy, have economic mineral deposits been worked with any success. Most of the area has been inadequately mapped as to geology. The region is crossed by the Great Northern Railway and served by the Pacific Power and Light Co.; officials of these two companies believed that with better geologic maps, prospecting might be stimulated and lead to the discovery of mineral resources that would contribute to new economic development within the area. A cooperative mapping agreement was proposed jointly by the two companies to the Montana Bureau of Mines and Geology in May 1958, and thus was born the Kootenai-Flathead five-year project. The dual objectives of this project are: 1) the possible location of mineral deposits of economic value, and 2) the ''stimulation of prospecting exploration" by others. This was to be achieved by geologic mapping of some 6800 sq miles and by establishing a field office in Kalispell where prospectors could come to have their rocks and minerals identified and receive geological advice on their problems. This writer has finished four field seasons as Project Geologist and thus became familiar with the Belt section in the Libby, Yaak River, Ural, Thompson Lakes, Pleasant Valley, and Stryker quadrangles (see Fig. 1). Progress on the project is given in annual reports issued by the Bureau.* This *Montana Bureau of Mines and Geology, Bulletins 12 (1959), 17 (1960), and 23 (1961). paper is concerned essentially with the stratigraphy of the Belt rocks so far encountered in mapping. PREVIOUS WORK IN THE AREA Willis28 made the first study of the stratigraphy and structure in the Lewis and Livingston Ranges of Glacier Park just east of the project area. In 1904, Daly made a study of the Belt rocks of the 49th parallel, using the names from bottom up, Creston, Kitchener, Moyie, and Gateway, for rocks ranging in age from that of Prichard to that of basal Missoula group. Walcott26 studied the Belt rocks exposed in the Mission Range (see Fig. 1) and other areas to the south of the area under discussion. Calkins and McDonald made a reconnaissance of northern Idaho and northwestern Montana in 1905. Calkins was the first to use Walcott's term 'Ravalli' as a group name for the strata equivalent to the Burke, Revett, and St. Regis formations (see Table I). Clapp worked on the Belt of western Montana (including Lincoln and Flathead Counties) throughout his lifetime. The Fentons9 studied the Belt of Glacier Park and

Jan 1, 1962

PUBLIC hearings began before the Committee for Reciprocity Information on May 24, 1950, for the purpose of unearthing data and opinion that will be helpful in the forthcoming reciprocal tariff and other trade-barrier negotiations at Torquay, England, on September 28th of this year. The conference this fall will constitute the "third round" of tariff negotiations under the General Agreement on Tariffs and Trade concluded at Geneva in 1947. The United States plans to negotiate with 17 other countries on possible tariff modifications on various articles all the way from baby carriages and bottle caps to lead and zinc-bearing ores. On May 31, June 1 and June 2, spokesmen appeared before the Committee for Reciprocity Information on behalf of the domestic lead and zinc mining industries. Producers of these metals protested the inclusion of paragraphs 391 (lead-bearing ores, dust and mattes), 392 (lead bullion, lead in pigs and bars, and scrap lead), 393 (zinc-bearing ores of all kinds), and 394 (zinc in blocks, pigs or slabs, and zinc dust) of the Tariff Act of 1930, as amended in the list of articles to be considered for possible tariff concessions at Torquay. It was pointed out that although operating costs have more than doubled since 1939 tariffs on these metals were actually higher in that year than at present. This, coupled with the detrimental effects of the recent series of devaluations, has sounded the death knell for a substantial number of domestic lead and zinc mines-a most undesirable development in the face of the ominous international situation, according to these spokesmen. It was urged that higher rather than lower tariff rates are needed on these metals. The opinion was expressed that it was inconsistent to foster a high living standard in our western areas and then, once it is attained, to undermine that condition by minimizing the protection that was partly responsible for it. The main theme of some arguments implied that although every effort should be made to close the "dollar gap" abroad, serious consideration must be given the methods employed lest our national security position be jeopardized in the process. The House Committee on Foreign Affairs completed hearings on H. J. Res. 236, to provide for United States membership and participation in the International Trade Organization. Hearings began on April 19th and ran for over five weeks. Many witnesses from industry and government presented voluminous testimony, which will not be available for public distribution for several weeks. However, it is no secret that the most controversial provisions of the Draft Charter of the ITO are: (1) Article 17 (Chapter IV on Commercial Policy) which would obligate members to negotiate for the reduction of tariffs and the elimination of trade preferences; (2) Article 20 which would prohibit the use of quantitative restrictions for protective purposes; (3) Article 16 which promulgates rules to implement the principle of non-discrimination in international trade; and (4) provisions permitting the use of protective measures for promoting economic development, particularly in backward areas, even though such provisions are inconsistent with those of the three articles cited above. United States membership in the International Trade Organization is essential to the successful operation of that body in view of this country's position as the economic giant in the present international trade pattern. Many countries are reluctant to take any action toward the ratification of the charter until it is known what course America will pursue. However desirable or undesirable the ideal of free multilateral trade may be it is unlikely that this Government's participation in the ITO will materialize soon. Advices in Washington indicate that H. J. Res. 236 will not be enacted during the present session of Congress. The legislative pattern designed to secure Congressional approval of the ITO is similar to that of the St. Lawrence Seaway project. The Seaway project was pending in treaty form for several years before the Foreign Relations Committee of the Senate and when the Administration decided to incorporate this project into bill form it was found that, while it passed the House promptly, the Senate decided to pigeonhole it because of the obvious intent to circumvent the constitutional prerogative of the Senate to advise and consent to the ratification of treaties. The ITO bill may be slated for a similar fate. It is deemed essential by western Senators and Congressmen that the present session of Congress enact some form of mining legislation before its adjournment, now set for July 31st. These legislators from prominent ore-producing states do not desire to return to their home areas in the fall emptyhanded. Aside from that, it is entirely superfluous to reiterate the necessity for maintaining a healthy domestic mining industry as a bulwark against a sharp rise in the temperature of the "cold war". Now that S. 2105 has failed a new bill is taking shape in the Senate Interior and Insular Affairs Committee. It is similar in language to H. R. 8221 (to encourage the conservation and development of the mineral resources of the United States) reported by the House Public Lands Committee on May 3, 1950, but so far has failed to receive approval of the House Committee on Rules. There are some qualified observers in high circles in Washington as well as in the mining industry who favor a tax incentive program to stimulate investment in mining enterprises, as opposed to a conservation and exploration program. The Bureau of Mines and the Treasury Department have undertaken a joint study to determine the need for modification of the tax laws as they apply to mining. The study is scheduled for completion before the end of the year, and appears to be supplementary to the investigation initiated by the National Minerals Advisory Council which culminated in the submittal of recommendations to the Secretary of the Interior in December 1949. The "cold war" is largely responsible for the increased demand for metals. Stock-pile purchases and heavy industrial demand due to military needs distort markets and disrupt normal price trends. Such activity has an unhealthy influence on metal production, luring some producers into a state of dependency on the continuation of this condition. When stock-pile objectives are met sometime in the future purchases must then come to a halt unless international "fireworks" are touched off. It can only be hoped that technological improvements and further mechanization of mines coupled with the stimulus of a rising population will offset the anticipated drop in industrial demand and cessation of stockpile purchases when the international crisis abates.

Jan 7, 1950

By Roy C. Kirkman

It is with great pleasure that I read Mr. Howard M. Wells article in the December 1978 issue of MINING ENGINEERING entitled: "Optimization of Mining Engineering Design in Mineral Valuation." Mr. Wells very adequately presents the case and point that there are a great number of variables which must be analyzed during an economic evaluation of an FUND RESOURCE, such as copper or uranium.

Jan 4, 1979

By John G. Baragwanath

THE September issue of the Engineering and Mining Journal carried an item regarding the Cercapuquio Mining Co. which was mentioned as a large producer of lead, zinc, and cadmium, situated near Huancayo, Peru. The paragraph caught my eye because I had not heard of the property in thirty years and I recollect all too well the circumstances of its accouchement. In 1916 1 was making my headquarters in the town of Huancayo, then the terminus of the Central Railway of Peru, and was examining mines and prospects in that general area for Cerro de Pasco. In the course of my work I became acquainted with an engaging and energetic "practical" miner named Balarin, a Dalmatian living in Huan¬cayo, and made numerous trips in his excellent company. One day Balarin came to the down-at-heels hostelry where I stopped and told me that a Cholo prospector, a character by the name of Jose, had just reached town and claimed to have made a discovery in a little known locality called Cercapuquio. Lead-silver, Balarin said, and showed me a sample of galena about the size of his fist. "Fine," I remarked. "When do we leave?"

Jan 1, 1947

By R. W. Gurry

WHEN a steel in the austenitic state, with all its carbon in solution, is maintained, at constant temperature, in contact with a gas that removes the carbon from the surface, vet without otherwise altering the composition of the steel, the change in weight of the specimen, after any period of exposure, is a direct measure of the amount of carbon it has then lost. The purpose of the present paper is to show how, by application of established mathematical reasoning based on the fundamental diffusion law and on certain postulates, this loss of weight yields a complete picture of the distribution of carbon throughout a specimen of regular shape after any period of exposure, with all the accuracy required in any practical occurrence of decarburization. Precisely the same is true for the gain in weight during the reverse process of carburization, or for the gradual gain or loss of any element, so long as the steel comprises only a single phase at temperature, provided always that the experimental conditions conform to the postulates. The change in carbon content from surface to center of the specimen is always continuous, when everything is in solution, even though under the microscope the decarburized zone (or carburized rim) may appear to be sharply defined. The experimental procedure is described and some typical results are presented, which are then interpreted by application of the diffusion law. EXPERIMENTAL PROCEDURE Initially an endeavor was made to follow the gain of weight during the process of carburization in a hydrogen-toluene atmosphere, but it was soon found that the specimen became coated with graphite, which could not be removed without some loss of metal; therefore it was decided to continue carburization until the steel was saturated throughout, to remove all graphite from the surface of the specimen, and then to follow the loss of weight during decarburization in a moist hydrogen atmosphere at the same temperature as that used for carburizing. The carburizing procedure has been described in an earlier paper;1 it suffices to state here that the carburization lasted about 140 hr. at 760°C. (1760°F.) and 44 hr. at 1110°C. (2030°F.), these periods being long enough-on the basis of the calculations presented later-to ensure that the specimen was about 9.99 per cent saturated at each temperature. The speci¬men was a cylinder about 3.8 cm. long and 0.475 cm. in diameter; the materials were carbonyl iron, a commercial low-metalloid iron, and a steel with 3.6 per cent nickel and the usual proportion of other elements. The fully [carburized] specimen, after cooling at the top of the furnace tube, was placed in a lathe and sandpapered to remove all graphite; then the diameter was measured with a micrometer caliper, and the initial weighing (corresponding to complete saturation) was made. By means of a

Jan 1, 1942

By F. J. Haller

IN 1943, we found, in the new Mather operation, a very unusual and disappointing condition in the footwall rock where all of our main haulageways were to be located. With the exception of a few hundred feet out of the thousands then planned and since driven, all of the openings require support. In general, the ground is not particularly heavy, at least by our standards, but it must be supported and the back carefully covered. Also, our operations require rather wide plat openings (16 to 18 ft) and rather flat curves at the turn-outs, all of which adds to the problem. When this completely unforeseen condition was discovered, ordinary timbering was the only answer, because of the impossibility of obtaining adequate steel supplies in time due to war shortages. Then by the time steel supplies were obtained and a practice developed, we found ourselves with between four and five miles of main haulage drifts and plat openings of a permanent nature, all of which were supported by hardwood timber, some of which had already rotted to an unsafe degree. Also, our drifting program was adding some two miles per year to the above figure. F. J. HALLER, Member AIME, is Superintendent, Mather Mine, Cleveland-Cliffs Iron Co., Ishpeming, Mich. AIME Columbus Meeting, September 1949. TP 2840 A. Discussion (2 copies) may be sent to Transactions AIME before May 31, 1950. Manuscript received Aug. 22, 1949. Revision received Jan. 17, 1950. To give all of the details of our experiments, studies, and experiences would fill a large book, but we were satisfied that our organization had done an excellent job, starting from scratch. You can appreciate our surprise when we discovered that we had added very little to an existing record. Attention was called to a footnote in a copy of "Carnegie Pocket Companion" year 1923. The note read: "Full information as to uses of H-Beams is given in pamphlet entitled 'Steel Mine Timbers.' " A search of our Engineering Library brought to light a pamphlet printed in 1911 showing extensive use of steel for this purpose. Except for welding in place of riveting, we have added very little to the designs in that book. We have, however, developed an experience which proves, at least to our own satisfaction, that steel mine supports pay off under the proper conditions. We are now convinced, in spite of the relatively high initial cost of materials, that steel sets, because of comparatively low installation cost, are actually cheaper than either treated or untreated wood sets, if they are properly designed and adapted. Several Sections in Use: Convenience guided our first experiments in steel sets, since for a number of years, we had used the 4-in. WF, 10 lb per ft section in 10-ft lengths as safety forepoles along with wood forepoles. This section replaced the 40-lb rail which had formerly been used for the purpose. Having the 4-in. WF sections on hand, it was natural that our first experiments in steel sets involved their use. Later, the rolling of the 10-lb section was discontinued in favor of the much stronger 13-lb section, which is now standard for both legs and caps in areas of no particular weight, but which, none the less, require permanent support. Our experiments involved the use of the 10- and 13-lb sections as legs and 6- and 8-in. I beams, 16 and 23 lb per ft, respectively, as caps. Experience soon indicated that, if the ground were heavy enough, and the opening wide enough to require a cap stronger than 13-lb, the 8-in, 23-lb should be used, eliminating the 6-in. I beam. We now know that the 8-in. WF section of the same weight, which we propose to use in the future, is considerably stronger for the amount of money involved. Comparative Strengths: Tables I to IV giving strengths of several species of timbers as compared with the structural sections that we now use have been prepared in accordance with accepted practice. Experience indicates that failure due to compression perpendicular to the grain of the wood does not destroy the effectiveness of a wood set frequently enough to be a practical factor. Therefore, no table of these values is included.

Jan 1, 1951

By F. J. Haller

IN 1943, we found, in the new Mather operation, a very unusual and disappointing condition in the footwall rock where all of our main haulageways were to be located. With the exception of a few hundred feet out of the thousands then planned and since driven, all of the openings require support. In general, the ground is not particularly heavy, at least by our standards, but it must be supported and the back carefully covered. Also, our operations require rather wide plat openings (16 to 18 ft) and rather flat curves at the turn-outs, all of which adds to the problem. When this completely unforeseen condition was discovered, ordinary timbering was the only answer, because of the impossibility of obtaining adequate steel supplies in time due to war shortages. Then by the time steel supplies were obtained and a practice developed, we found ourselves with between four and five miles of main haulage drifts and plat openings of a permanent nature, all of which were supported by hardwood timber, some of which had already rotted to an unsafe degree. Also, our drifting program was adding some two miles per year to the above figure. F. J. HALLER, Member AIME, is Superintendent, Mather Mine, Cleveland-Cliffs Iron Co., Ishpeming, Mich. AIME Columbus Meeting, September 1949. TP 2840 A. Discussion (2 copies) may be sent to Transactions AIME before May 31, 1950. Manuscript received Aug. 22, 1949. Revision received Jan. 17, 1950. To give all of the details of our experiments, studies, and experiences would fill a large book, but we were satisfied that our organization had done an excellent job, starting from scratch. You can appreciate our surprise when we discovered that we had added very little to an existing record. Attention was called to a footnote in a copy of "Carnegie Pocket Companion" year 1923. The note read: "Full information as to uses of H-Beams is given in pamphlet entitled 'Steel Mine Timbers.' " A search of our Engineering Library brought to light a pamphlet printed in 1911 showing extensive use of steel for this purpose. Except for welding in place of riveting, we have added very little to the designs in that book. We have, however, developed an experience which proves, at least to our own satisfaction, that steel mine supports pay off under the proper conditions. We are now convinced, in spite of the relatively high initial cost of materials, that steel sets, because of comparatively low installation cost, are actually cheaper than either treated or untreated wood sets, if they are properly designed and adapted. Several Sections in Use: Convenience guided our first experiments in steel sets, since for a number of years, we had used the 4-in. WF, 10 lb per ft section in 10-ft lengths as safety forepoles along with wood forepoles. This section replaced the 40-lb rail which had formerly been used for the purpose. Having the 4-in. WF sections on hand, it was natural that our first experiments in steel sets involved their use. Later, the rolling of the 10-lb section was discontinued in favor of the much stronger 13-lb section, which is now standard for both legs and caps in areas of no particular weight, but which, none the less, require permanent support. Our experiments involved the use of the 10- and 13-lb sections as legs and 6- and 8-in. I beams, 16 and 23 lb per ft, respectively, as caps. Experience soon indicated that, if the ground were heavy enough, and the opening wide enough to require a cap stronger than 13-lb, the 8-in, 23-lb should be used, eliminating the 6-in. I beam. We now know that the 8-in. WF section of the same weight, which we propose to use in the future, is considerably stronger for the amount of money involved. Comparative Strengths: Tables I to IV giving strengths of several species of timbers as compared with the structural sections that we now use have been prepared in accordance with accepted practice. Experience indicates that failure due to compression perpendicular to the grain of the wood does not destroy the effectiveness of a wood set frequently enough to be a practical factor. Therefore, no table of these values is included.

Jan 1, 1951

By Kenneth K. Humphreys, J. W. Leonard, T. S. Spicer

INTRODUCTION Reasons for Thermal Drying The continuing increase in the percentage of - '/4 in. ( -6.3 mm) coal produced as a result of the increased use of mechanical mining methods has, over the years, tended to shift considerable portions of the work of producing salable coal to the fine coal cleaning section of the preparation

Jan 1, 1979

Preliminary plans of this meeting, together with a most interesting series of papers that have been received or promised, were published in the May Bulletin. The plans are being carried out enthusiastically and hospitably by the Colorado members and all indications point to an interesting and valuable meeting.

Jan 6, 1918

By J. J. Gilman

THEORIES of fracture in metals have been based primarily on the dependence of fracture strength on grain size. This dependence was first observed by Masing and Polanyi.l These workers, as well as 0rowan12 and Davidenkov and Wittman,' thought the grain size could be equated with the crack size in the Griffith condition for crack propagation.4 In this way they could account for the observed proportionality between fracture stress and the reciprocal square root of the grain size. The chief results of recent investigations of the fracture strength of polycrystals are summarized in Fig. 1. Low for iron,5 Petch for iron,' Greenwood and Quarrel for zinc, Petch and Zein for zinc,' and Hauser, Landon, and Dorn for magnesium'' have all found that the fracture stress of a polycrystal is proportional to the reciprocal square root of the grain size. Also, they find that, for large grain sizes, the fracture stress lies near the extrapolation of the yield-stress curve determined at small grain sizes; where measurable plastic strain precedes fracture. Low9 has gone a step further and shown that, in Range 1, the fracture stress in tension is almost identical to the yield stress in compression for a given grain size. Homes and Gouzou, 10 and Low also have shown that, in Range 2 of Fig. 1, microcracks form when the yield stress is reached, but they do not cause failure until the stress reaches a much higher value. The fact that yielding always precedes fracture suggests that fracture is induced by plastic flow. A mechanism by which this might occur was first proposed by Zener.11 He pointed out that blocked dislocations would cause stress concentrations which might cause fracture. The blocking would be caused by grain boundaries. This idea has been developed by Eshelby, Frank, and Nabarro,12 by Koehler,13 and by Stroh.14 By means of etchpits blocked dislocations have been observed in brass by Jacquet,15 in zinc by Gilman,16 and in lithium fluoride by Gilman and johnston. The blocked-dislocation theory and the experiments that bear on it have been summarized by Mott.18 One of the strong points of the blocked-dislocation theory is that it can explain the grain-size dependence of the fracture stress in a natural way. However, Low9 has pointed out that the theory is not satisfying when it is considered quantitatively. Gilman10 also has criticized the theory and presented an alternative interpretation of the relation between fracture stress and grain size. Since the blocked-dislocation theory is not the only theory that can explain in the grain-size effect, it is necessary to find other evidence either to support or deny it. In this investigation the following points were studied: 1) If blocked dislocations normally cause fracture, then the fracture stress ought to be very high in the absence of plastic glide. Is it? 2) If dislocations must be blocked in order for metals to fracture, then certain types of grain

Jan 1, 1959

By P. Rama Rao, D. H. Sastry, T. R. Anantharaman

Deformation (a) and twin (a') stacking-fault densities in cold - wor ked filings of fcc silver alloys containing 2, 4, and 6 wt pct Sb have been estimated from Debye-Scherrer peak shifts and asymmetries, respectively. Evidence has been obtained for a possible strain-induced transformation in a two-phase alloy containing 9.0 zut pct Sb. Using Fourier analysis of X-ray line profiles, the effective particle sizes and root mean square strains have been determined for the three fcc alloys in the cold-worked condition. The values of the compound fault probability 0.5a + a') evaluated from peak shifts and asymmetries are in reasonable apeement with those derived from peak broadening. COLD work of fcc metals may produce both deformation and twin (also called growth) stacking faults, which can be detected and quantitatively estimated by X-ray diffraction techniques.' In addition to peak broadening, deformation faults produce a shift in peak positions and twin faults an asymmetry of the Debye-Scherrer reflections. Besides stacking faults, a reduction in the size of coherently diffracting domains and distortion within these also broaden the powder reflections of deformed fcc metals and alloys. Fourier analysis' of peak shapes provides quantitative infor- mation about the effective domain sizes, lattice strains, and also the compound fault probability (1.5a + a'), where a and a' represent deformation-and growth-fault density, respectively. The Paterson method2 for determination of a from peak shifts, the warren3 or wagner4 method for evaluation of a' from peak asymmetries, and the Fourier analysis for quantitative estimates of all the contributory causes of peak broadening have, in the course of the last decade, been extensively applied to obtain data for a number of deformed fcc metals and alloys. One of the useful results of earlier measurements of a in several solid solutions is a correlation between a and the solute valence as well as electron concentration per atom (p) in alloy systems based on a particular solvent. The work of Smallman and westmacott5 on Cu-Zn, Cu-A1, and Cu-Sn, of Foley, Cahn, and ~aynor' on Cu-Si and Cu-Ge, and of Rama Rao and Anantharaman7 on Cu-Si and Cu-Sb has revealed a common trend in the increase of a with p and also a with valency of the solute. Cahn and Davies' and Ad-ler and wagnerg have observed similar trends for silver alloys containing cadmium, indium, and tin. Data on a for silver alloys with a pentavalent solute element are not, however, available. It is primarily to fill this need that the present investigation on Ag-Sb alloys was undertaken. Utilizing the Patersonand Warren methods, values of a and a', respectively, have been determined in three silver alloys containing 2, 4, and 6 wt pct Sb. By Fourier analysis of the broadening of Debye-Scherrer peaks, effective particle sizes, lattice strains, and the compound fault probability (1.5a +a') have also been evaluated.

Jan 1, 1967

By K. A. Gschneidner, O. D. McMasters, T. J. O’Keefe

X-ray diffraction, differential thermal, ad rnetallo-graphic methods were used to establish the Dy-Pb Phase diagram. Lead additions lower the 1377°C transformation temperature of dysprosium to 1360°C leading to an inverted peritectic reaction. The 327°C melting point of lead is lowered by dysprosium additions to about 326°C yielding a eutectic reaction. A second eutectic reaction occurs at 13.3 at. pct Pb and 1200°C. The dysprosium-richest intermetallic compound DysPb3 melts congruently at 1695°C and crystallizes in the hexagonal Mn5Si3 (D8,) type structure. The peritectic decomposition temperatures for the remaining compounds are Dy5Pb, at 1555C, DyPb2 at 955C, and DyPb3 at 880°C. A fifth compound near the DyPb stoichiometry exists over a 310°C temperature range decomposing at 1130°C by means of an inverted peritectic reaction and melting incongruently at 1440°C. The crystal structures of the compounds are discussed. A systematic study of the rare earth-lead alloy systems is underway in an effort to supply information concerning the alloying behavior of the rare earth metals. The Dy-Pb phase diagram is the fourth system to be investigated in this study. The Yb-Pb,1 Y-Pb,2 and Eu-Pb 3 diagrams have been published recently. Utilization of the rare earth series of metals as a research tool in this manner should yield a better understanding of alloy formation. EXPERIMENTAL PROCEDURE Materials. The lead used in this investigation was obtained from Cominco Products, Inc., and was specified to be 99.99 pct pure. The dysprosium was prepared in this Laboratory by the calcium reduction of the fluoride followed by distillation of the dysprosium. The major impurities in the dysprosium in ppm are: A1 (<40), Ca (400), Er (<50), Gd (<200), Ho (<200), Mg (<50), Si (30), Ta (400), Tb (<100), Y (<50), 0 (651, H (15), N (not detected), F (430), C (35). Alloy Preparation. Most of the alloys were prepared by melting weighed amounts of dysprosium and lead in sealed tantalum crucibles. The tantalum crucibles were sealed by are-welding in a He-Ar atmosphere welding chamber. Thus the alloys are in contact with He-Ar at about 1 atm pressure. Homogenization was achieved by holding them in the liquid state for about 1 hr, cooling, inverting the crucibles, remelting, and repeating the process at least twice. Since these alloys were prepared in sealed tantalum crucibles, chemical analysis for final composition was thought to be unnecessary. No detectable reaction of these alloys with the tantalum crucible was observed by metallographic examination. Metallographic evidence was also used to confirm the homogeneity of some of the alloys prepared in this manner. The compositions of a few alloys, which were prepared by nonconsum-able are-melting, were corrected for the small weight losses involved by assuming that the weight loss is due to vaporization of lead. The specimens obtained from the alloy samples were prepared under a dry-argon atmosphere because they were rapidly attacked by air and moisture. Thermal Analysis. Differential thermal analysis methods were used to determine the liquidus curves and reaction horizontals of the system. Both Pt vs Pt + 13 pct Rh and W + 5 pct Re vs W + 26 pct Re thermocouples were used to measure the temperature. An X- Y recorder was used to record the specimen temperature and differential electromotive force between the specimen and molybdenum standard. The arrest temperatures were measured potentiometri-cally. The accuracy limits (* values) associated with the reaction temperatures obtained by this method were estimated on the basis of both the reproducibility of the particular temperature value and the accuracy of the thermocouple at a given temperature. Liquidus temperatures were obtained from cooling arrest data while both heating and cooling arrest data were used to establish the horizontals of the diagram. Heat treatments during the thermal analyses of the alloys between 40 and 70 at. pct Pb were necessary in order to approach equilibrium conditions. The samples were held at temperatures between the various peritectic horizontals for l to 2 hr before the thermal analyses were continued. The entire range of compositions was investigated at the expense of a minimum amount of materials by adding appropriate amounts of lead to master alloys. More than sixty alloys were analyzed by this differential thermal method and for each alloy the results given herein are taken from two or three heating and cooling cycles. X-Ray and Metallographic Methods. Slice specimens for metallography and powder specimens for X-ray diffraction were prepared from rod-shaped samples which had been melted in sealed 0.62 5-cm-diam tantalum crucibles. The specimens were heat-treated in sealed tantalum crucibles which were protected by sealing them in argon-filled quartz ampules. Quenching was accomplished by breaking the ampules in ice water after heat treatment. X-ray powder specimens were sealed in 0.3-mm-diam glass capillaries under a dry-argon atmosphere. Copper, iron, and chromium radiation were used to obtain the powder patterns for these alloys. More than 150 powder patterns were obtained for specimens of various compositions and heat treatments. Included in these were several patterns for specimens which had purposely been oxidized. Patterns from specimens which had been accidentally exposed

Jan 1, 1969