By Fuqiang Zheng, Shuai Wang, Ting Duan, Yufeng Guo, Tao Jiang, Andrew Yakovlevich Travyanov

Organic compound binder can effectively enhance the strength of green pellet and reduce the addition amount of binder during pelletizing. However, compared with traditional bentonite binder pellet, the compressive strength of the preheated and roasted pellets significantly declined. It is of significance to resolve this problem for the application of organic compound binder. In this paper, magnetite concentrate was used as raw material, carboxymethyl cellulose (CMC)- bentonite compound was used as binder, characteristics of preheated and roasted pellets and the effects of additives on that were systematically studied, The results show that sodium acetate can effectively improve the characteristics of the finished compound binder pellets. The compressive strength of the preheated and roasted pellets were increased by 52/N·p-1 and 342/N·p-1 respectively when the addition amount of sodium acetate is 2.2%wt of compound binder. Moreover, sodium acetate has no adverse effect on pelletizing process and drying characteristics of green balls.

Jan 1, 2015

By Jincheng Hu, Honggang Zhong, Qijie Zhai, Congsen Wu, Cheng Zhang, Jingzheng Ye

"The influence of cooling intensity on the solidification structure and ferrite phase content of a new duplex stainless steel (DSS) was investigated by using a thermal simulation setup for continuous casting. The results showed that the characteristics of the solidification structure were similar to their industrial scale manufactured slabs, including chill zone, colunmar zone and equiaxed zone. And austenite morphologies were mainly primary and secondary Widmanstatten sideplates as well as intragranular Widmanstatten plates. In addition, it revealed that the ferrite content increased with an increasing distance from the chill surface and decreased at colunmar to equiaxed transition (CET) position, then the value remained relatively stable at equiaxed zone. Furthermore, the ferrite content presented the same trend with the cooling intensity ranging from 100 mL/min to 2000 mL/min with the values just varying in a slight range.IntroductionThe duplex stainless steel (DSS) is the kind of steel that ferrite phase and austenite phase occupy about 50% respectively, or the content of the fewer phase has to be more than 30% [l]. The success of modem duplex stainless steels is to a large degree due to their higher strength than austenitic stainless steels, higher toughness than ferritic stainless steels, good weldability and high resistance to stress corrosion cracking as well [2,3]. The cost of stainless steel production continues to soar in recent years due to the increasingly higher price of Cr. In order to decrease the production cost, a new type of duplex stainless steel was developed by Bao steel [4]. This newly developed duplex stainless steel had low Cr content compared with 2205 DSS, and was expected to be applied into automobile industry. However, this type of steel was still in the initial stage of development, and the influence of continuous casting process on its solidification process and structure was still unclear, which needed to be studied further. Several works published in literature presented the effect of continuous casting conditions on duplex stainless steel (DSS) 2205, 2304 [5,6]. It was discussed that the cooling intensity in the chill-side had little efficient influence on the phase transformation. In this paper, the effect of cooling intensity on the solidification structure and ferrite volume fraction of this DSS at a given cooling rate was investigated."

Jan 1, 2014

By J. Y. Aubut

The modernization of the CCR Refinery to permanent cathode technology is presently underway. The 360,000 mt/y refinery is being retrofitted to accept the Kidd process. Part of this modernization includes the installation of Kidd stripping machines, and the total replacement of the materials handling equipment. It also involves the reinforcement of building structures to accept the new equipment and the ability to operate in different modes. The future equipment will interface with some existing apparatus, which is being retained for future operations. The whole operation will be automated and will allow product traceability for quality purposes. This retrofit poses important challenges given the size and scope of the modernization project and because it is being undertaken concurrently with normal plant operations.

Jan 1, 1999

By Alexandre Chagnes

The extraction properties of two synthesized cationic exchangers, i.e. bis (1,3-dibutoxypropan-2-yl) phosphoric acid (BiDiBoPP) and bis(1,3-diisobutoxypropan- 2-yl) phosphoric acid (IPA), have been studied for the liquid-liquid extraction of Co(II), Ni(II) and Mn(II) contained in 1 M HCl. A comparison of the extraction properties of these extractants diluted in kerosene with Cyanex® 272 shows BiDiBoPP and IPA extract advantageously at lower pH than Cyanex® 272 and a better Co(II)-Mn(II) separation is achieved using BiDiBoPP or IPA than with Cyanex® 272.

By Hongmin Zhu, Kai Huang, Shuqiang Jiao

"Garlic peel was used as the raw material to synthesize the biosorbent for the selective recovery of precious metals from the acid chloride solution. Garlic peel is rich in carboxyl-, amino- and thiol-groups, has the potential of exhibiting high affinity to Au(III) when appropriate chemical modification process was employed. Here in the present study, the biosorbent was prepared by cross-linking garlic peel particles with concentrated sulfuric acid. Adsorption tests for mixing different metal ions such as Au(III), Fe(III), Cu(II), Ni(II) and Zn(II) from various concentrations of hydrochloric acid media indicated that Au(III) was selectively adsorbed on the cross-linked garlic peel gel over the other coexisting base metal ions investigated. The crosslinking mechanism and selective adsorption of Au(III) were also investigated briefly.IntroductionPrecious metals are quite popularly applied in the modern industries such as jewelry, electronics and electrical devices, catalysts in chemical industry, etc. While their high values, limited deposit and quite large demand in industry makes its recovery from the industrial wastes, typically e-wastes, quite necessary. Actually, many techniques have been developed to recycle and recover the precious metals from various industrial wastes effectively in last decades, but the cleaning and ecofriendly processes are still seriously scarce [1]. Taking into account of the typical recovery processes using cyanide lixiviant in the alkaline media, or aqua regia, followed by the further recovery process using activated carbon adsorption or cementation with zinc, iron or aluminum plate or powder, though they both are quite effective recovery processes, if considering the special requirements on safety and ecofriendliness for the modern hydrometallurgical processes, various improved or novel extraction processes are greatly demanded [2]. Recently, the biosorption technology applied to the recover precious metals in the hydrometallurgical process has become a concern [3,4]. Inoue’s research group made great progress in the recovery of precious metals such as gold, palladium and platinum from the e-wastes such as spent mobile phone by using biosorption from the hydrochloric acid media [5,6]. This new hydrometallurgical process exhibits the prominent advantages of being cost-effective for its short process, easy operation and near-zero emission. In the above recycling process for e-wastes treatment, the preparation of biosorbents is the key and backbone of the whole recovery process. For this purpose, they developed a series of suitable sorbents for precious metals recovery by using the tanning-based or cellulose-based biomass such as persimmon peel, grape peel, orange juicing residue, waste cotton, waste paper through the crosslinking process with concentrated sulfuric acid and relative chemical modification processes [7-10]. In the present study, we also applied this technique to prepare the biosorbent of precious metal uptaking by using garlic peels as the raw materials, and investigated the adsorption properties of such-obtained gel in the hydrochloric acid media."

Jan 1, 2012

By R. M. Donovan

This paper documents the efforts to improve quality and production at the Amarillo Copper Refinery. It summarizes the change in attitudes, work procedures, equipment maintenance, instrumentation, and the ever changing market. The Amarillo Copper Refinery is dedicated to the ASARCO Management System, ISO-9002 and continuous improvement.

Jan 1, 1999

By Sung Jin Han

Magnesia-based refractory is generally used in an electric arc furnace (EAF) due to its relatively high corrosion resistance and strength at high temperatures. However, the magnesia refractory is attacked by EAF slag and thus the lining life continuously decreases. Thus, it is significant to identify the interfacial reaction between magnesia refractory and FeO-rich EAF slags. In the present study, the influence of FeO-rich slag on the corrosion behavior of MgO refractory was evaluated. The (Fe,Mg)Oss layer was observed at the slag-refractory interface and its thickness increased with increasing content of FeO in the slag. The specific reaction phenomena and formation behavior of (Fe,Mg)Oss layer were evaluated by thermochemical computing program, FactsageTM7.0.

By S. S. Bogomolov

The relationship between the magnetic properties and micro- structures of Pr-Fe alloys rapidly quenched by melt-spinning and highly undercooled by containerless processing in the Cambridge drop-tube was studied. The maximum measured coercivity, Hc, of as-cast samples was 4450 Oe for Pr-2 wt.%Fe. However, rapid quenching or melt undercooling decreases coercivity for hypo- eutectic alloys (<10 wt.%Fe) and increases Hc for hyper-eutectic systems.

Jan 1, 1992

By Oleg B. Girin, Yuliya O. Proshenko

"Several approaches to electrolytic synthesis of new types of composite coatings with improved properties were devised using the authors' findings on development of texture, substructure and structural state in metal electrocrystallization. Addressed are texturally composite coatings having improved resistance to wear and corrosion; substructurally composite coatings having improved hardness and corrosion resistance; phase-change constitutionally composite coatings having improved corrosion resistance, reflectance, hardness and resistance to wear; structure-change constitutionally composite coatings having improved electric and magnetic properties; restricted-substructure composite coatings having improved resistance to abrasive-impact wear; and modified-substructure composite coatings having improved strength and plasticity.IntroductionIn recent years, some trends in the formation behavior of crystal texture, crystal substructure and structural state of electroplates were revealed and effects of texture, substructure and structural type on electroplate properties were discovered (1-3). Our interest was in using these findings and effects to develop some ways of synthesizing new types of composite electrolyte coatings having enhanced properties."

Jan 1, 1998

By T. V. Jayaraman

Fe-Ga alloys, with compositions around 27.5 at % Ga, can be heat treated to obtain ? (ordered bcc), DO19 (ordered hexagonal), and L12 (ordered fcc) ordered structures. Our earlier work using polycrystalline samples had shown that magnetostriction is strongly influenced by ordering in this alloy. Here more detailed study of the correlation between ordering and magnetostriction using single crystals of Fe 27.5 at. % Ga alloys is reported. Single crystals of Fe 27.5 at % Ga were grown using Bridgman single crystal growth technique. X-ray and electron diffraction were used to study the ordering in this alloy. Magnetostriction measurements were carried out at no load conditions. Elastic constants were measured using Resonant Ultrasound Spectroscopy.

Jan 1, 2006

By Toshihide Ito, Jie Liu, Takashi Nishiyama

"Human society evolved from an agricultural to industrial and, subsequently, to a service society. As the resource requirements for each stage of this development differ, trends of metal and energy consumption are related to shifts in society. The increase pattern of supplemental energy is similar to that of mineral production throughout the world. Low positive and stable long-term increasing occurred before 1950, whereas they increased quickly after 1950, especially between 1950 and 1973. A substantial decline in· the growth of energy and mineral production began in 1973 and lasted until the early 1980s. Production of energy resources has recently begun to increase again at a high growth rate in the world. Observing the consumption trends of energy and key metals, it is clarified that increasing patterns can be thought in three stages.IntroductionHuman society evolved from an agricultural to industrial and, subsequently, to a service society. As the resource requirements for each stage of this development differ, trends of metal and energy consumption are related to shifts in society [1-3]. Humphreys [4] described that both the non-ferrous metal consumption and the construction material consumption showed a similar trend dropping markedly in the UK over the period 1960-1992. On the other hand, per GDP (Gross Domestic Product) consumption, that is, the intensity of use of construction materials has declined sharply over the past 30 years, more so than the intensity of metal use in the USA [5]. Nishiyama [6] observed that increase pattern of supplemental energy is similar to that of mineral production throughout the world."

Jan 1, 2000

By Han Ilhan

This paper discusses and describes aspects of a cost effective and safe tailings impoundment selection. In light of the current low metal prices and recent tailings embankment failures around the world, it is becoming extremely more important to develop tailings impoundment design that balance cost efficiency with safety. The paper will present critical design components associated with a tailings impoundment which need to be addressed during the planning phase. Procedures for identifying various tailings impoundment alternatives, and evaluation and selection of alternatives are presented.

Jan 1, 1999

By Xiaojie Gao, Shufeng Yang, Jingshe Li, Chengsong Liu

In the blast furnace process, the dust entrained in the blast furnace gas enters into the down-comer, flows through the gravity dust separator (to eliminate coarse particles) and then is collected in a bag-house. The powder collected by the baghouse is called bag dust, while both fractions are called blast furnace dust whose main components are C and Fe. The dust also contains small amounts of nonferrous metals such as Zn and Pb, which have some value. Also, due to the small particle size and low density the dust is easily suspended in air and so can endanger human health. Therefore it is necessary to develop a process to both treat the dust to recover the metal values and to dispose of the residue – preferably by recycling to the blast furnace itself via the sinter strand. These objectives will result in good economic, environmental and social benefits [1].

Jan 1, 2014

By R. Padilla, M. C. Ruiz

Arsenic, antimony and bismuth are commonly found in copper concentrates usually as the minerals enargite, stibnite and bismuthinite, respectively. Concentrates having high levels of arsenic and antimony must be pretreated before smelting. Roasting is the preferred method for removing these toxic impurities from concentrates; However, the removal of As, Sb and Bi in oxidizing roasting by volatilization may not be complete due to the slow reaction rates at 500- 700 °C. Oxidizing/volatilization data were obtained from pure mineral mixtures and from arsenic rich copper concentrate. The reaction mechanism for the volatilization of arsenic and antimony were discussed. Near 100% As and over 95% Sb volatilized in the oxidation of a mixture of pure minerals at 700 °C, 1% oxygen, while over 95% As, and 35% Sb volatilized at 600 °C in 1% oxygen atmosphere when using a copper concentrate containing 3.51% As, 0.14% Sb, and 0.01% Bi. Bismuth did not volatilize.

Jan 1, 2015

By Alan James Parker

Chalcopyrite can be converted to pure copper by the following five steps. An exothermic sulfation roast of chalcopyrite; leaching of cupric sulfate from the calcine with dilute acid; precipitation of Chevreul&apos;s salt and or other copper sulfites with ammonium sulfite or precipitation of crude copper by autoclaving ammonium sulfite and cupric sulfate at 150°C; dissolution of Chevreul&apos;s salt, or the crude copper, as cuprous sulfate, using acidic cupric sulfate in an acetonitrile-water solution as oxidant; precipitation of pure copper by thermal disproportionation of the cuprous sulfate solution. Acetonitrile and acidic cupric sulfate solution recycle. Advantages over conventional processes include lower cost, lower energy consumption as waste heat, sulfur removal as ammonium sulfate or gypsum, rather than as sulfur dioxide and rapid throughput. The net reaction is: 2 CuFeS2 + 4H20 + 15/2 02 + 8 NH3?2Cu + 4 (NR4)2 SO4 + Fe2O3

Jan 1, 1976

By T. Taniguchi

The existing Mitsubishi Process line at Naoshima Smelter and Refinery has been operating successfully since 1991, and its present production capacity is 270,000tpy of copper. Furnace relining works have been carried out every two years to coincide with the compulsory bi-yearly boiler inspection, but the next target is to extend the furnace refractory life to four years, while still undergoing the mandatory boiler inspection every two years. Although the damage of hearth bricks beneath lances in the Smelting furnace was a matter of concern, it was reduced by controlling gas velocity and evening solid distribution to each lance. The life of bath level bricks in the Converting furnace was also a concern, but four-years continuous use of the bricks was achieved in the course of the last two campaigns. Several other improvements were also carried out to the cooling systems during the shutdown in 2005 to ensure longer campaign life. This paper summarizes recent improvements implemented to enhance the advantages of the Mitsubishi Process.

Jan 1, 2006

By Emilia Visileanu, Eftalea Carpus

"Ecological economic policy shall be understood as the sum of political, economical and environmental measurements aimed at the entire economy dematerialization and the dematerialization shall be ""imposed"" since the designing stage of goods and services"". European textile and clothing industry with a long leading tradition in terms of innovation, fashion and creativity, continues to be one of Europe's major industrial sectors. Textile industry affects the environment by high consumption of water, energy and chemicals, as well as by the large amount of waste it generates as a result of using a large number of chemicals and technological processes.Textile waste prevention, reduction and ecological exploitation require the implementation of new management and education tools.Introduction“Europe must learn from the experience of global economic and financial crisis ""- this was the conclusion of the European Commission that has elaborated a ten-year strategy designed to reinvigorate the economy and make possible a growth which is ""intelligent, sustainable and favorable to inclusion"", by a better coordination of national and European policies.Adapting infrastructure and logistics that encourage the marketing of ""sustainable"", ""fair traded"" and ""green"" products as well as other special „green” products will facilitate the movement towards dematerialization and eco-efficiency among producers."

Jan 1, 2012

By Leonard J. Friedman

There have been considerable changes in systems, equipment design and materials used in the modern Sulfuric Acid process. Many of these will shape the metallurgical sulfuric acid plant for the year 2000 and beyond. Advances have come from all over the world, and include new scrubbing area designs, catalyst contacting devices, silicon stainless alloys for unlined acid systems, energy recovery from acid heat, stainless converters and heat exchangers, etc. This paper describes each of the process "advances" and presents a review and analysis indicating advantages, operating experience and limitations.

Jan 1, 1988

By K. P. V. Lei

The U.S. Bureau of Mines investigated a hydrothermal sulfidation procedure to recover lead and silver from plumbojarosite. The plumbojarosite, generated during pressure-oxidative leaching of zinc concentrate in a commercial operation, contained, in percent, 25.4 pb, 18.8 Fe, 1.4 Zn, 29.5 SO,2-, 3.2 s?, 13.4 total sulfur, and 7.4 oz/ton Ag. The sulfidation was conducted in an autoclave and converted the plumbojarosite to amorphous iron oxide and liberated the lead and silver as sulfides. The best operating conditions were using 50 9 of plumbojarosite and 7 pct s? (2.04 9 S? added) in 500 mL of 2.0 mol/L NH3, 150? C, and 1 h. The sulfidation product contained, in percent, 37 Pb, 28 Fe, 6 S2-, 2 SO,2-, and 11.2 oz/st Ag. Ferric chloride leaching extracted 98 pct Pb and 97 pct Ag from the sulfidation product.

Jan 1, 1990

By Yuanbo Zhang, Yongbin Yang, Guanghui Li, Zhengwei Yu, Yufeng Guo, Tao Jiang, Xiaohui Fan, Youming Hu

"Composite agglomeration process (CAP), as an innovative method for preparing blast furnace burden, was developed and has been put into operation in China. CAP is different from traditional agglomeration processes of iron-bearing materials involving sintering and pelletizing. Compared to the traditional agglomeration processes, CAP is characterized by several strengths such as permission of diverse iron-bearing materials in production, obvious improvement of permeability in the feed bed, decreasing the fuel consumption and remarkably increasing the productivity of sintering machine. Furthermore, the use of the composite agglomerates prepared with CAP is capable of obviating the negative effects caused by the differences in quality of sinter and pellets on the operation of blast furnaces. This paper mainly presents an overview of the principle and applications of CAP.Development Background and Principle of CAPhe traditional agglomeration processes including sintering and pelletizing have been the two predominant methods for preparing ironmaking burden from iron-bearing materials. Sintering is a way for agglomeration by heating the coarser fine ores (general granularity 0~10mm). The mechanical strength of irregular porous sinter is obtained by the solidification of molten phase at high temperature process. It has been shown that the production of high basicity sinter (R=1.8~2.2) is characterized by low energy consumption and high efficiency compared to low basicity sintering. Meantime, the finished high basicity sinter is characterized by good mechanical strength and metallurgical performance. Pelletizing is another way for agglomeration by firing wet green pellets, which are balled from the fine grained iron ores or concentrates. Based on the differences of chemical compositions, the finished pellets can be divided into acidic oxidized pellets, fluxed pellets, magnesium-bearing pellets, and so on. The acidic oxidized pellets are the dominant products of modern pelletizing."

Jan 1, 2012