By Denise Crocce Romano Espinosa

The recycling of waste of electric and electronic equipment (WEEE) is one of the main modern challenges. Among the variety of WEEE, batteries can be set apart due to their composition and their growing demand along with portable devices. The objective of this work is to characterize the thermal behavior of a sample of mixed types of batteries using a thermobalance (TGA). The results of tests showed that Cd evaporated up to 800ºC, Zn evaporation occurred mainly above 900ºC and manganese oxides were pre-reduced to MnO at temperatures above 900ºC.

Jan 1, 2009

By Masaru Imaizumi, Hiroyuki Nomura, Mitsuharu Takita

"Cast iron possesses many superior characteristics caused from precipitated graphite structure, for example, castability, wear resistance, solid lubrication, damping capacity. But the more graphite hyper-eutectic cast iron contains, the lower its mechanical strength becomes, because graphite gives a negative effect to strength of cast iron. In addition, primary graphite tends to segregate during solidification, so uniform materials are difficult to be produced.In this study, authors introduced semi-solid processing in developing new and high quality cast iron. A series of semi-solid processing experiments were carried out to clarify the effect of stirring condition; solidification temperature and etc. on microstructures and characteristics of cast iron. In particular much attention is paid to the appearance of ternary eutectic zone at the final stage of solidification. As the results advanced hyper-eutectic cast iron was obtained with high quality of both the mechanical strength and wear resistance. As for the mechanical strength, 300MPa and 0.60% are obtained as the tensile strength and the elongation values, respectively, under the controlled stirring condition. This indicates that semi-solid processed hyper-eutectic cast iron is used prospectively without spheroidization.IntroductionCast iron has various good properties such as wear resistance, solid lubrication, damping capacity and machinability. The characteristics of cast iron are mainly decided by graphite structure, namely graphite shape and its distribution in the matrix. Mechanical strength of cast iron is large in the case of small quantity of graphite particles which are precipitated uniformly, however, it becomes small in the case of large quantity of graphite precipitated flakily."

Jan 1, 2000

By Yong Kuk Park

The horizontal cold chamber die casting process can produce a wide range of near-net shape, non-ferrous castings with small dimensional variation, excellent surface finish and very complex geometries. However, top quality die castings can be achieved only when optimal performance of the cold chamber and plunger is maintained during the molten metal injection phase of the process. Cold chambers (shot sleeves) are known to deteriorate fast and sometimes fail catastrophically because of poor design. Catastrophic fracture and wear due to deformation are leading causes to degrade quality, increase downtime and thereby decrease productivity and profitability. Therefore, a systematic approach to minimize irregular and adverse conditions which prevent an intended injection profile, is highly desirable. To eliminate them, design criteria for shot sleeves were developed using analytical tools and available experimental data. The correlation between design and mechanical failures of shot sleeves was shown by the data obtained from the die casting industry. Also, the relationship between die casting process parameters and deterioration/ failure mechanisms were carefully evaluated.

Jan 1, 1996

By Hongyang Cao

The iron constituents selectively separated from the modified copper slags by magnetic separation and flotation.were studied. The results of magnetic separation for modified copper smelting slags show that the grinding size, current intensity and dispersant agent had great influence on grade, and recovery ratio of TFe in preparation concentrate; The results of flotation for magnetic concentrate show that the positive flotation of sodium oleate negatively upgrade the grade of magnetic concentrate, but the reverse flotation of lauryl amine and soluble starch are effective. The grade of TFe can reach 54% and the recovery ratio can reach about 90% in magnetic concentrate, when the grinding size is 45.8µm and the current intensity is 2.5A. The optimal effect is obtained by using lauryl amine as collector and soluble starch as depressant to reverse flotate magnetic concentrate, and the grade of TFe is upgraded 2.37%.

Jan 1, 2009

By S. Viswanathan, A. S. Sabau

"Dimensional changes between a pattern die and its corresponding investment casting part occur as a result of complex phenomena such as thermal expansion/contraction and hot deformation (elastic, plastic, and creep) during the processing of the pattern material (wax), mold material (shell) and solidifying alloy. Determining the pattern tooling dimensions is crucial to the dimensional control of the investment casting process. To date, computational methodologies have not been applied to the prediction of dimensional changes in investment castings.This paper deals with the evaluation of wax pattern dimensions, which is one important factor in determining pattern tooling dimensions in investment casting. Cerita 29-51, an industrial wax, is considered in this study. The wax pattern dimensions are determined by considering its thermo physical and thermomechanical properties, restraint of geometrical features by the metal die, and process parameters such as dwell time, platen temperature, injection pressure, and injection temperature.IntroductionThe investment casting process involves making a disposable wax pattern by injecting wax into a metal mold, building a ceramic shell mold around the wax pattern by the application of a series of ceramic coatings to the wax pattern, dewaxing the ceramic shell mold, and casting the alloy into the shell mold. Dimensional changes between the pattern tooling and its corresponding cast part occur as a result of thermal expansion, shrinkage, hot deformation, and creep of the pattern .material (wax), mold material (shell), and solidifying alloy during the processing [1]."

Jan 1, 2001

By Xuan Li

Aluminum slag is generated when aluminum metals are recycled through a smelting process in the presence of salt. There are small amounts of aluminum metals trapped in the aluminum slag. This research aims at evaluating the use of aluminum slag as an expansion agent for the production of lightweight concrete by taking advantage of the residual aluminum metals in the slag. The research identified key elements of producing lightweight concrete products through utilizing various mixture components including sodium hydroxide (NaOH), lime (CaO), cement, and gypsum. The volumetric expansion rate was investigated and the density and strength of the products were determined. The results show that aluminum slag can be utilized for the production of lightweight concrete products.

Jan 1, 2010

By Jilai Xue

Experiments with various industrial cathodes ranging from 35 wt.% to 100 wt.% graphitic and fully graphitized carbons were carried out in a laboratory aluminum electrolysis cell. Sodium and cryolite bath penetration into the cathode samples was measured by XRD and SEM-EDS analysis. For a higher cryolite ratio in the bath, the cathodes with lower graphitic carbons exhibited more sodium penetration than the fully graphitized. The increased graphitization in the cathode materials can reduce Na, NaF and Na3AlF6 penetration. SEM-EDS inspection reveals that the sodium and fluorides penetration within the cathode samples has different patterns for varying graphitization of the carbon materials. XRD quantitative analysis indicates that there is a large percentage of Na3AlF6 in the penetrated bath. The results can provide useful information for quality evaluation of the industrial cathode products.

Jan 1, 2010

By E. I. Gedgagov, A. V. Tarasov, V. M. Paretsky, A. D. Besser

"Hydrometallurgical technology and equipment have been developed in the Gintsvetmet Institute (Moscow, Russia) for processing of rhenium-containing alloys waste to produce commercial- grade metal products with recovery of all valuable components. The technology is based on waste treatment with hydrofluoric acid with subsequent decomposition with nitric acid at pH = 1 to 1.5 to ensure maximum degree of rhenium conversion to the liquid phase of pulp. Some experimental lots of ammonium rhenate and ammonium molybdate were produced at a pilot plant. The following main techno-economic performance values have been achieved when processing grinding residues (balance-based tests were conducted with a lot of SP-2 alloy waste) to produce ammonium rhenate of high purity, as well as tantalum-niobium, nickel-cobalt and tungsten-molybdenum concentrates: rhenium recovery of 92.3% into a commercial product from grinding waste; production cost of 170-210 US Dollars per 1 kg of rhenium in commercial-grade ammonium perrhenate taking into account its recovery; tantalum and niobium recovery of 75- 77% into bulk concentrate; nickel and cobalt recovery of 88-89% into a mixed concentrate; tungsten and molybdenum recovery of 88% to 91% into concentrate. Introduction During the recent years the use of rhenium has been increasing at a fast pace worldwide [1]. The growing prices for this refractory metal are an essential factor encouraging collection and processing of rhenium-containing wastes. Double-component waste, such as molybdenum- rhenium or tungsten-rhenium alloys can be readily decomposed and the process of rhenium recovery does not cause, therefore, any difficulties. The main separation of metals takes place at the stage of waste digestion with acid, because molybdenum and especially tungsten remain in precipitate in the form of hydrated oxides and rhenium reports in the liquid phase, from which it can be easily extracted by solid ion-exchange or solvent extraction techniques. However, most of rhenium is contained in super-alloy waste [2]. Such waste has different contents of valuable components, such as tantalum, niobium, molybdenum, tungsten, cobalt, nickel, chromium and other metals. The basis of all such super-alloy waste is nickel. Refractory metals in the super- alloy composition are in the form of metallized target-oriented eutectics, and due to this reason hydrometallurgical decomposition of such alloys is a difficult technological task."

Jan 1, 2008

By Ram Avtar

High tensile thick plates (>80mm, weight ~3000 Kg) of medium carbon low alloy steel, when heat treated, manifested higher percentage of crystalline area (>20%) in fractured surface. Such problem was not encountered in thinner plates. The genesis of higher crystallinity in fracture was examined. It was observed that the thicker plate undergone slower rate (Average 0.9oC/Sec.) from soaking temperature to Ms temperature) of cooling after austenising during oil quenching and thereby quenched microstructure had upper bainites. During tempering of as quenched bainite, additional precipitation took place at the lath boundaries of bainite. This led to weakening of grain boundaries and aided easy crack propagation during fracture and resulted in formation of higher percentage of crystalline area in fractured surface. Enhancement in cooling rate (Average 1.8oC/Sec. from soaking temperature to Ms temperature) of austenised plate by switching over from oil quenching to water quenching practice resulted in complete transformation of austenite into martensite and produced ductile fracture (zero Crystallinity). Plates conformed improvement in mechanical properties between 2-5%.

Jan 1, 2009

By Yuanbo Zhang

Zinc leach residues produced by hydrometallurgical zinc plants contain many valuable elements (zinc, iron, lead, gallium, indium silver, etc), while they have not been utilized effectively hitherto. In this paper, a new process of flotation-reduction roasting-magnetic separation to recover these valuable elements from zinc leach residues is developed on a basis of mineralogy investigations of them. The results show that silver concentrate with grade of 4321.6 g/t and recovery of 80.69% have been obtained, using 1750 g/t Na2S as conditioner, 750 g/t ammonium dibutyl dithiophosphate and SN-9 (assistant collector) as combined collector and 100 g/t terpenic oil as frother, if zinc leach residues with 523 g/t silver are floated at pH = 5.0. When the flotation tailings are subjected to reduction roasting at 1100? for 2 h, the volatilizations of zinc, lead and indium are over 96%. After roasted products are treated by wet-grinding and magnetic separation, the grade of gallium and gallium in the concentrates achieved respectively reaches 1805 g/t and 1536g/t, and the recovery of them is high to 94.67% and 93.20%, respectively.

Jan 1, 2006

By Wenming Wang

Recycling of retired cadmium telluride (CdTe) photovoltaic (PV) modules has attracted attention due to new European environmental regulations. Recycling tellurium from CdTe PV modules is becoming more important because of the low availability of this metal. We investigated several treatment paths for reclaiming tellurium from solutions obtained from leaching fragments of CdTe PV modules. Our experiments showed that conventional soda ash neutralization/hydrolysis methods recovered only 50~60% of tellurium. However, by appropriately combining neutralization and sulfide precipitation, almost all the tellurium present in the leaching solution was precipitated and recovered; the concentration of tellurium in the processed solution was reduced from 900-1000 mg/L to less than 1 mg/L, yielding a tellurium recovery greater than 99%. This method can be incorporated in the scheme of recycling spent CdTe PV modules and manufacturing wastes. It may be also an alternative to the current operations for removing tellurium from copper anode slime leaching solutions.

Jan 1, 2006

By Alex Del Castillo

The mineral processing industry has followed the development of database control systems, and various systems have been installed in existing and new plants. The goal is to improve product quality, raise productivity and lower production costs. Improvements in different units for mineral .processing .have been applied. This has led to increasing information for the operators. To support the operators and for an easy overview of the process, a complete concept for an integrated process-control system is required. This paper describes the plant-wide [process control system for the Collahuasi copper project located in northern Chile. The total investment for the project was $1,700,000,000 and included a port area and two copper processing plants, an oxide plant with a cathode production of 50 tons per year and a sulfide plant with a concentrate production of 330 kilotons per year. The main characteristics of the plant-wide process control system include a 200- kilometer long redundant control network and a 24-kilometer long redundant serial network providing coverage for the entire plant. The plants are located around 4,700 meters above sea level, serial communication lids allow the integration of over 2,700 SCADA data units, and the system handles over 7,500 physical signals plus the SCADA data integration. The main equipment consists of 39 different sized controllers, 16 operator stations, 5 engineering stations, 2 information management systems and 4 X- terminals. The project management, control configuration, factory acceptance test, system integration test, training, commissioning and start-up were carried out in close cooperation with the customer. The result was completely satisfactory for the customer.

Jan 1, 1999

By Anish Kumar

Keywords: Ultrasonic velocity, Poisson?s ratio, Elastic constants A new correlation has been established between two independent elastic properties, ultrasonic shear wave velocity and Poisson?s ratio, in a wide variety of isotropic solid materials, such as pure metals, ceramics, polymers and intermetallics. It has been shown for the first time that Poisson?s ratio decreases with increase in elastic moduli, E & G and ultrasonic velocities. This new correlation between two independent elastic constants may lead to the reduction in independent elastic constants for isotropic solid materials from two to one, at least for a given alloy system with different microstructural conditions.

Jan 1, 2005

By D. R. Kreuzer

The sulfide smelting industry is striving for up-scaling their operations by increasing the throughput and efficiencies of the furnaces. The physical phenomena related to refractory materials prevailing in smelters and furnaces are highly complex. The refractory materials are exposed to fairly high temperatures, thermo-mechanical stresses, penetration of pores, erosion and chemical corrosion. The application of numerical simulation tools is needed for the refractory engineering task to consider those phenomena and to evaluate the impact of operational regimes on the refractory design and finally on the integrity of the furnaces. The work discusses case studies of simulations addressing problems and questions related to the refractory design process. Practical simulation approaches which employ simplified models are introduced as the engineering process demands results in a reasonable time.

By Larry M. Southwick

There is much ongoing work in research and development of new processes for the recovery and recycling of met.a.ls and other materials from various waste and scrap streams. Commercialization of such new technologies requires the bringing together and successful execution of a considerable effort involving a variety of activities. These include process conceptualization, research and development, detailed design and construction, and then plant startup and operation. Processes evolve through all of these steps by engineering due diligence, making objective and critical analyses of results, and troubleshooting processing steps to, hopefully, arrive at a sequence that has the best chance to succeed operationally and economically. After a summary review of the above steps, several processes will be described in more detail that provide mostly successful examples of the above procedures. Finally, some observations will be made on areas that will become critical in the near future to the success of new processes for wastes and residues.

Jan 1, 2000

By James W. Reeves

DuPont was the titanium metal pioneer who put the greatest effort into both R&D and commercial sponge and powder metallurgy production. This was concentrated in the period 1945 through 1963. The commercial results were development of the chloride process for TiCl4 using ilmenite, development and improvement of the Kroll process, development of a modified Hunter process to make titanium powder and commercial development of a direct powder process. The powder metallurgical process failed because of the inability to meet powder chloride specifications. All this work remained a trade secret until published in NMAB -392 by Mahla in 1983. There were other processes explored by DuPont, both improved sponge and powder processes. Much of this work has been continued by others but none, as of yet, resulting in new improved titanium metal capacity.

Jan 1, 2001

By Pengfu Tan

A thermodynamic model of KIVCET lead smelting process has been developed. The model has the capability to predict the distribution behaviors of Pb, Zn, Fe, S, O, As, and heat balance in KIVCET direct lead smelting furnace. The compositions of lead bullion, matte, slag and gaseous phases, and heat balance are calculated. The effect of the ratio between oxygen and feed on the chemistry of the smelt and heat balance of the coke checker has been simulated and discussed. The thermodynamic model also helps to understand the tapping issue of the lead bullion. In this paper, some applications of this model in the industry have been presented.

Jan 1, 2006

By C. J. Parradies

During injection into a die, semi-solid metal alloys exhibit a shear-rate, history-dependent flow response. Simulating the injection of a thixotropic material requires that empirically determined boundary conditions and viscosity are specified as a function of both temperature and shear rate history. Experiments were performed using an industrial die casting machine that was instrumented with sensors to measure the pressure and temperature during the injection of a semi-solid aluminum alloy through a tube. This benchmark experiment was used to develop a simulation of the die casting process that could then be applied to more complex die geometries. The results of the experiments were analyzed using the exact, steady state solution for a power law fluid and simulations accounting for slipping at the boundary between the semi-solid metal and the die. Results indicated that the no-slip condition cannot be used to simulate the velocity boundary condition, because the measured pressure is much lower than that predicted by the models. An estimated apparent slip coefficient was introduced to account for the reduced pressure. During some of the experiments, a sudden drop in the measured pressured, prior to decreasing the ram velocity, coincided with observations of segregation in the form of concentric rings visible on the polished surface of cross-sections cut from material remaining in the tube.

Jan 1, 1997

By Zhigang Liang

Investigation into the mixing of 150t ladle furnace by two-nozzle jetting was performed by a water model simulation of 1:4. The effects of nozzle arrangements including separation angle, radial position and asymmetry as well as tracer adding position on the mixing time were studied. The most favorable mixing is achieved when the two nozzles are symmetrically arranged at half radii in the ladle, with 45o separation angle. The empirical relationship between the mixing time and stirring power intensity has been established for two-nozzle jetting based on the present experimental results. In addition, the swelling above bath surface is also investigated with two-nozzle jetting.

Jan 1, 2009

By Dongok Kim

Regardless of the advantages of the Friction Stir Process (FSP), for age-hardened aluminum alloys, the mechanical properties such as hardness in the stir zone decreased after FSP due to the growth or dissolution of strengthening precipitates. Here, as a new technique, FSP was introduced to alloy copper nanopowders in Al7075 T651. Mechanical properties of copper nanopowder- alloyed Al7075 T651 together with micro and nanostructures were compared with those of as-FSPed Al7075 T651 using SEM, TEM, and Vickers hardness testing to understand structure-property relationships. It was observed that Vickers hardness of the stir zone in copper nanopowder alloyed Al7075 T651 increased by 20% compared to that of the heat affected zone, while the as-FSPed samples did not show a noticeable increase in hardness in the same zone. Xray mapping showed traces of copper nanopowder after the process. TEM is being used to verify if there was CuAl2 formed in the copper alloyed sample.

Jan 1, 2006