Search Documents

By G. Kyle Green

Zirconium chlorinator residues contain an array of rare earths, scandium, unreacted coke, and radioactive thorium and radium. Because of the radioactivity, the residues must be disposed in special waste containment facilities. As these sites become more congested, and with stricter environmental regulations, disposal of large volumes of wastes may become more difficult. To reduce the mass of disposed material, the U.S. Bureau of Mines (USBM) developed technology to recover rare earths, thorium and radium, and unreacted coke from these residues. This technology employs an HCl leach to solubilize over 99% of the scandium and thorium, and over 90% of the rare earths. The leach liquor is processed through several solvent extraction stages to selectively recover scandium, thorium, and rare earths. The leach residue is further leached with an organic acid to solubilize radium, thus allowing unreacted coke to be recycled to the chlorinator. The thorium and radium waste products, which comprise only 2.1% of the original residue mass, can then be sent to the radioactive waste facility.

Jan 1, 1995

By Shenghui Guo, Ying Lei, Wei Li, Jinhui Peng, Libo Zhang, Yu Li

"Abstract: In this work, low temperature carbothermic reduction of Panzhihua low grade ilmenite after ball milling were investigated. The ball milling of ilmenite and graphite were processed in a ball mill. The milling process can attenuate the particle of ilmenite, and the ilmenite characteristic peak were broadened and weakened. The reduction temperature and behaviors are studied on the thermo gravimetric apparatus; lower temperature and higher reaction rate were obtained for the reduction of ilmenite with graphite after milled. The reduction temperature and times of ilmenite decreased to 1000-1025°C and 40-60min via milled for 4 or 8h; Low down the reduction temperature can eliminate the solution of Mg2+ and FeTi03 in a certain degree; the reduced ilmenite has an obvious loose structure, can favored the subsequent procedure such as leaching.1 IntroductionThere is about 9.66 billion tons of Vanadic Titan-magnetite deposited in Panzhihua, China. In this reserve, there is about 8.73x108 t ofTi02, Accounting for 90.54% of the Chinese reserves, and 35.17% of the international reserves and ranking first in the world. [JJ Titanium mineral deposits major classified into Rock type and Placer type. Rock type is the igneous mineral, which have great content of FeO (Relative to Fe20 3) and gangue. The rock textures are compact and almost are complex ore. Rock type Titanium mineral major are ilmenite and titan magnetite ore, difficult to separate the metal ore and gangue. l.21 Thus, the Ti02 grade of Rock type ilmenite much lower than the Placer type (Table land 11). Panzhihua ilmenite are the typical Rock-type, due to the higher contents of MgO, CaO and Si02 and the complex mineralogy in ilmenite in Panzhihua region, making its direct reduction progressively more difficult. Mechanical activation, usually carried out by energetic milling or ball milling, was reported to significantly decreased the reduction temperature and accelerate the reaction rate of reduction of ilmenite with carbon, silicon and Magnesium. f3·(>J It reported that the process temperature were decreased to 600-1000°C and the annealing time were reduced to 30-120min after milled for 50-400 h. Shorter milling time involved was imported for else procedure such as direct leaching. 171 Hardly any research had referred to the carbothermic reduction reactivity of ilmeite milled for a short time as 1-1 Oh. In the present work, the aim is to investigate the reactivity and reaction temperature of carbothermic reduction of Panzhihua ilmenite. The Phase composition and micro morphology of samples are characterized."

Jan 1, 2011

By Tianzu Yang, Weifeng Liu, Lin Chen, Wei Chen, DUCHAO ZHANG, HUI XIAO

Carbonaceous refractory materials are widely accepted in many reducing smelting processes such as iron and ferroalloys. Oxidizing processes such as copper concentrate smelting traditionally use magnesia and/or alumina/silica refractory materials. The main objection to the use of carbon-based refractories as the exposed working lining in oxidizing applications is the potential for free oxygen to react with the carbon at high temperature, which could rapidly degrade the refractory lining. In 2013, Outotec and GrafTech conducted joint trials of a thermally conductive, carbonaceous lining for smelting copper concentrates in the Outotec® pilot-scale top-submerged-lance (TSL) furnace in Dandenong, Australia. This testwork had two equally important goals; to demonstrate the ability of carbon refractories to withstand oxidizing process conditions, while ensuring that neither furnace operating conditions nor process stability were negatively affected by the refractory material. The paper discusses the input parameters of the trials, key observations during the testwork program, and the results and conclusions from both process and refractory design standpoints.

Jan 1, 2016

By Akira Nishikawa

During the twentieth century, the copper smelting industry achieved dramatic expansion corresponding to the vast growth of global economy. This was largely due to innovations in pyro-metallurgical processes, such as autogenous smelting and continuous smelting and converting technologies. However, as copper production capacity increased, its impact on the environment also could not be ignored, and thus with increasing global environmental awareness, many smelting operations either had to renew or rebuild their facilities. In addition to these changes, in places like Japan and Europe, with scarce primary resources, the treatment and recovery of metals from a variety of items such as car shredder dust, used electrical appliances and electronic devices, on top of scraps traditionally treated, is having a profound effect on the reduction of waste and the preservation of primary resources. Thus compared to the days when copper smelting focused on the environmental control in order to break with "Smoke Stack Industry", copper smelting today is making an important contribution to the sustainable development of human society.

Jan 1, 2003

By Elders. Wilfred A.

Petrological and geochemical methods, the utility of which has long been established in the mining industry, are proving useful and cost-effective in elucidating the thermal evolution of active geothermal fields. In return, they yield insights into sulfide-silicate equilibria, mass and energy transfer in convecting hydrothermal systems, and the genesis of hydrothermal ore bodies. Within the Plio-Pleistocene sediments of the delta of the Colorado River, in the Salton Trough, several active geothermal systems are known. Temperatures vary from 100-365°C, at less than 2 km depth, and salinities vary from 3,000 to 280,000 ppm, total dissolved solids. The hydrothermal alteration causes marked induration of the sediments, producing greenschist facies metamorphic minerals, including hydrothermal ore minerals. Subsurface authigenic minerals show strong correlation with increasing temperature. A typical sequence in sandstones is (below 150°=C) montmoril-lonite-kaolinite, (above 180°C) chlorite + illite, (above 225°C) calc-alumino-silicates, (above 325°C) biotite. There is a transition from porosity-dominated\to fracture-dominated permeability in the hottest and deepest geothermal reservoirs. This regular series of minerals provides a practical tool during exploration drilling. From drill cuttings, we can make predictions on reservoir temperatures, useful in making decisions on well completion. Other types of geothermometry we have employed include light stable isotopes, fluid inclusions and vitrinite reflectance measurements. A combination of these techniques not only improves our temperature predictions, but together with fission tack annealing studies, permits us to model the dynamics of temperature change and fluid flow in these geothermal reservoirs.

Jan 1, 1981

By Akira Nishikawa

During the twentieth century the copper smelting industry achieved dramatic expansion corresponding to the vast growth of global economy. This was largely due to innovations in pyro-metallurgical processes, such as autogenous smelting and continuous smelting and converting technologies. However, as copper production capacity increased, its impact on the environment also could not be ignored, and thus with increasing global environmental awareness, many smelting operations either had to renew or rebuild their facilities. In addition to these changes, in places like Japan and Europe, with scarce primary resources, the treatment and recovery of metals from a variety of items such as car shredder dust, used electrical appliances and electronic devices, on top of scraps traditionally treated, is having a profound effect on the reduction of waste and the preservation of primary resources. Thus compared to the days when copper smelting focused on the environmental control in order to break with "Smoke Stack Industry", copper smelting today is making an important contribution to the sustainable development of human society.

Jan 1, 2003

By S. K. Varma, Miriam Regalado, Daniel Salas, Erica Corral, Erika Esquivel

"Age hardenable 2014 aluminum alloys and composites containing 0.10 and 0.15 volume fractions of alumina particles (VFAP) have been solutionized at 540 and 550°C for up to 20 hours. The solutionized samples, heat treated for 5 and 20 hours, have been subjected to room temperature rolling until cracking develops. The work hardening curves have been compared to determine the effect of solutionizing time on the rolling characteristics from both hardness and the microstructural evolution points of view. Solutionizing at two different temperatures results in differences in the extent to which the composites can be rolled until fracture. The microstructural characterization by TEM has been performed to understand the room temperature rolling behavior.IntroductionThe effect of solutionizing on the age hardening response of 6061 and 2014 aluminum alloys and composites reinforced with 0.10, 0.15 and 0.20 volume fractions of alumina particles (VFAP) have been reported in the literature [1-4]. A comparison of the monolith and composites indicates that particles promote the aging process through differences in the microstructures in solutionized condition. The first effect of solutionizing is to produce a grain growth process which follows a grain growth law (square of grain diameter as a function of solutionizing time). It appears that it is possible for vacancies to be emitted during grain growth period as they try to minimize the total grain boundary surface area by increasing their diameter. This may be common to both the monolith and the composites. However, the second effect must be exclusively considered for the composites. The particles generate dislocations during the solutionizing process due to the differences in the values of the coefficient of thermal expansion (CTE) between the particles and aluminum base metal. It has been determined [1] that the dislocation density increases with increase in solutionizing time in the composites of 6061 aluminum alloys reinforced with 0.10, 0.15 and 0.20 VFAP. The improved bonding between particles and matrix can give rise to additional generation of dislocations due to curvature effects [1] with the result that the dislocation density continues to increase with increase in solutionizing time even after the CTE effect is considered to have been stabilized."

Jan 1, 1998

By Andrew Campbell, Michael Reed

"WorleyParsons has used Discrete Event Simulation methods in conjunction with more traditional process models to assess the performance of copper smelting operations. This work was performed to determine the plant capacities and suitability of proposed debottlenecking options including accounting for the planned and unplanned (breakdowns) shutdowns in the various parts of the plant and supply chain. This paper outlines the methods used along with demonstrating the benefits of selecting a feasible option and minimizing capital and operating costs.IntroductionTraditionally for de bottlenecking studies of smelters and other process plants, a mass balance is performed based on continuous operating rates and expected operating hours. Smelters have several points of failure that will restrict, if not take the entire plant offline. By using a more detailed model, validated against plant experience, bottlenecks can be demonstrated and strategies to remove them to increase plant availability and economic.The modeling simulates the plant performance in real time, and by performing enough simulation the expected long run performance of the plant can be estimated. The models have been built using ExtendSim which is a powerful Discrete Event Simulation software package that is ideally suited to the batch and semi-batch processes and events that occur within smelter operating environments. The value of performing this work is that the operational performance of the plant can be assessed ensuring production targets are met, without using excessive capital outlay."

Jan 1, 2013

By Lijuan Li, Zheng Lu, Xin Xia, Qijie Zhai, Qingchun Li

"Pulsed current and pulsed magnetic field have been applied to the bainite transformation of Cr5 steel. Three groups of experiments were conducted. In the first group, ordinary resistance furnace was used for heat treatment. The Cr5 specimens were rapidly heated up to austenitization temperature 940 °C, held for 20 min, air cooled to bainite transformation temperature 350 °C, held for 10, 20, or 40 min and then air cooled to room temperature. The second and the third group shared the same temperature-time curve with that of the first group, but their heat resources came from the Joule heat produced by pulsed current. 1.5 T pulsed magnetic field was exerted on the third group specimens when they were held at 350 °C, but the second group specimens did not undergo the treatment of magnetic field. It was found that both pulsed current and pulsed magnetic field obviously retarded the bainite transformation. The phenomena were discussed in terms ofliterature results.IntroductionApplying pulsed current and pulsed magnetic field technology are very pronnsmg ways to change the microstructure of materials by affecting the phase transformation process. People had found that pulsed current dramatically influences the behaviors of materials, for example, electromigration effect [l], the solidification of metals and alloys [2, 3], electroplasticity [4, 5], crystallization of amorphous alloys [6], healing of metal materials [7] and so on. As to pulsed magnetic field technology, a lot of effort had been spent on grain refinement in solidification of metals [8, 9], recrystallization of cold-worked metals and alloys [10] and Fe-based alloys solid-state phase transformation [11, 12]. Though application of pulsed current and pulsed magnetic field technology have proliferated in recent years, investigation on their effects on solid/solid phase transformation, especially bainite transformation, is lacking. The aim of this paper is to show the effects of pulsed current treatment (C-T) and the combined treatment of pulsed current and pulsed magnetic field (CM-T) on bainite transformation of commercial Cr5 steel"

Jan 1, 2014

By Wantae Kim, Furnia Saito, Qiwu Zhang

"A novel mechanochemical processing technique for the preparation of zeolites from kaolinite in NaOH solution was investigated. Dry and wet mechanochemical treatments combined by subsequent moderate heat treatment could accelerate the synthetic reaction for zeolites from kaolinite. This stimulating process produced zeolite-A and zeolite-X from activated kaolinite at extremely lower reaction temperature than conventionally applied for zeolites production. Conversion to zeolite-A and zeolite-X was strongly dependent on the activated state of kaolinite. Wet mechanochemical treatment modified the chemical composition of activated solids. Rapid dissolution of AIO species rather than SiO ones in the reactant solution was accelerated by wet milling together with NaOH that promoted the formation of zeolite-X of high specific surface area.IntroductionZeolites are a family of hydrated alumina-silicate minerals contains alkali and alkaline earth metals. They have a framework structure that encloses inter-connected cavities occupied by large metal cations and water molecules. Zeolites are characterized for their ability toward ion exchange and reversible dehydration. Properties of them are exploited through commercial productions of particular structural and chemical features. Zeolites are used as commercial uses for catalysis for FCC (fluidized catalytic cracking) of petroleum refining, drying reagents of gases and liquids, and selective adsorbent for pollution control [1-3]. In such purposes, artificially synthesized zeolites are employed, although natural ones are associated with hydrothermal and hot spring alteration of volcanic materials. Commercially, a hydrothermal process has been used for the preparation of zeolite synthesis. This preparation method gives zeolites of high chemical homogeneity and purity, however, this wet-chemistry-based processing is significantly influenced by reaction temperature, pH, concentration, and composition of starting substances [4]."

Jan 1, 2000

By R. Padilla

In most of the Chilean copper and gold concentrates, arsenic is present mainly as enargite, Cu3AsS4, which at the conventional roasting or smelting temperatures decomposes liberating arsenic as gaseous compounds. The objective of this investigation was to study the decomposition reaction of enargite in an inert atmosphere in the range of 500 °C - 750°C. The results obtained indicated that the decomposition begins at about 525 °C. Two distinct regions in the temperature dependence of the decomposition rate were observed: a low temperature region between 525 °C to 650°C and a high temperature region between 650 °C to 725 °C. The X-ray diffraction analysis suggests that the decomposition of enargite occurs through the formation of intermediate tenantite, according to the following sequential reactions: 4Cu3AsS4(s) ? Cu12 As4S13(s)+ 3/2S2(g) Cu12 AS4S13(s) ? 6Cu2S(s) + 2As2S3(g) + 1/2S2(g) The decomposition kinetics was analyzed by using the model for a topochemical reaction of spherical particles: 1-(1-X) 1/3 = kt, which represented well the data. Apparent activation energies of 113 kJ/mol and 60.5 kJ/mol were found for the low and high temperature regions, respectively.

Jan 1, 1999

By F. K. Letowski

Leaching in froth is a particular case of a three phase (liquid-solid-gaseous) process which combines flotation with leaching by using a reactive gaseous reagent as a flotation carrier and a leaching solution as the reactive liquid medium to fonn the foam (froth) in' which the solid particles are suspended. Some physico-chemical and engineering aspects of leaching in froth are discussed and illustrated by its application for cleaning the mineral graphite. Leaching of the graphite concentrate containing 4L4% of the elemental carbon and 3.16% of the sulphidic 'sulphur was canied out in the froth fonned by: (a) a concentrated chloride solution, with a small addition of nitric acid, in the foam state; (b) a mixture of gaseous O2, NO., and H20 encapsulated in the foam; and (c) notable particles of graphite suspended in the foam. The laboratory experiments werecanied out in a "flotation column"-type reactor ala temperature from 80 to !08°C and under total pressure of 100 to 200kPa. In the 3-stage leaching-flotation process, the non-flotable fraction of particles was separated three times from the notable fraction. The concentration of carbon and elemental sulphur in the final flotable fraction was 96% C and 0.38% S respectively. The expected advantages and possible application in hydrometallurgy are suggested.

Jan 1, 1995

By R. G. Reddy

The effect of solid particles on viscosity behavior of Na2O-O-B2O3-SiO2 melts of composition XSio2/XNa2o =0.5 and in the temperature range of 900- 1150 K was studied. Samples were analyzed by X-ray diffraction and optical microscopy. The results showed that a crystalline phase (NaBO2) was formed and its amount increases with decrease in X,, from 0.50 to 0.25. The experimental viscosity values were compared with the predicted values using our viscosity model developed earlier. At low temperatures, for low content of B2O3 , the experimental values exhibits a large deviation from the predicted values. It was concluded that the deviation was due to the formation of solid particles in the molten slags. The existence of these solid particles increased the viscosity values significantly. A new viscosity model was developed to include the effect of solid particles.

Jan 1, 1993

By Sadi Medina

As it is characteristic from Custom Smelters, ENAMl Las Ventanas Smelter has to deal with different qualities and quantities of mining products from about 70 suppliers, that contain a variety of impurities that would be harmful for copper production. In order to increase the smelting capacity, an oxygen plant has been running since September of 1990. Moreover, to improve the environmental conditions, a new sulphuric acid plant started up to neutralize the metallurgycal off-gases from the Teniente Converter and partially from the Peirce-Smith converters. Based on the on-line operation among the reverberatory furnace and the Teniente Converter using oxygen enriched air to produce high grade matte, most of the volatilizing impurities, mainly arsenic, are collected as discarding compounds in the gas cleaning system of the acid plant. This paper describes the continuous performance of the Teniente Converter with acid plant, the results attained, the operation problems and how they were solved. The impurities distribution achieved in this process is also included.

Jan 1, 1993

By N. Kanari

The kinetics of oxychlorination of MgO by C12+02 was studied in the temperature range of 850 °C - 1025 °C, using thermogravimetric analysis. The effects of C12/02 ratio, gas velocity, temperature and partial pressure of reactive gases on the reaction rate were investigated. The oxychlorination process was characterized by an apparent activation energy of about 214 kJ/mol. The reaction orders with respect to C12+02, C12 and 02 at 950 °C were about 0.65, 0.98, and -0.37, respectively. Some data about oxychlorination kinetics of MgO, Cr2O3, and MgCr2O4 contained in chromite were compared. Efficiency of using oxychlorination for the removal of iron oxides contained in magnesia was demonstrated.

Jan 1, 1999

By Nobuaki Sato, Tetsuo Fukasawa, Akira Kirishima

To apply the fluoride volatility process for the treatment of fuel debris formed in the damaged nuclear reactors, study on the fluorination behavior of main constituents, such as fuel and cladding is essential. The mixture of uranium and zirconium oxides is formed under severe conditions such as high temperature and oxidizing atmospheres. In this paper, fluorination and volatilization behavior of uranium and zirconium oxides have been studied by TG-DTA method in the presence of fluorine. From the TG-DTA result of UO2 in F2 atmosphere, the weight gradually increased up to 7% at 350 oC followed by rapid weight decrease with exothermic peak showing the vaporization of uranium as UF6. ZrO2 showed similar fluorination behavior to that of UO2. However, fluorination of UO2-ZrO2 seemed to be suppressed with increasing ZrO2 amount. This may be caused by the formation of solid solution.

Jan 1, 2016

By Y. Maeda

Non-ferrous smelting furnaces generally lnstal1 a gas cooling system for treatment of waste gas containing S02. From the point of view of corrosion resistance and recovery of waste heat, the high pressure boiler system Is the best way to cool gas, however this system requires high Initial investment and relatively higher operating costs. Because the feasibility of this boiler system greatly depends on the smelting process and scale, other lower temperature systems, e.g. water-cooled Jacket system, are more suitable If the smelting process does not produce enough steam nor generate enough electricity to compensate operating cost. In addition, the water-cooled Jacket system Is simple in structure and easy to operate. For those reasons, it is applied widely. A new smelting furnace. was planned tin our factory and It was necessary to install waste gas cooling equipment. In our case, a water-cooled Jacket system was mo11e feasible because of the low gas volume and high dust content. H was also expected to operate without maintenance for ten years. On the other hand, some leakage problems with the water-cool1ed Jacket had been experienced In the past. That is because S02 in the waste gas changed into sulfuric acid which corroded the Jacket material, As the first step, several data from actual usage were reviewed to throw light on the corrosion process, and an appropriate procedure to determine the operating temperature of cooling water was obtained. For the basis of this study, a water-cooled Jacket system was newly designed and tested for three months in a pilot plant. After this system's performance was confirmed, It was installed In a new furnace as a commercial pl.ant. After one year of operation, the initial thickness of carbon steel Jacket remains almost the same.

Jan 1, 1992

By A. K. Kyllo

A study has been carried out on the dusts from Hudson Bay Mining and Smelting's Flin Flon copper smelter. The aim of the work was to determine the mechanisms of dust formation and the deportment of the various constituents. The work concentrated on the copper converters, but the electrostatic precipitators and baghouse also clean the reverberatory furnace off gas, so some mixing will have occurred. The dust composition was found to vary with distance from the furnace, and to be made up of three major components: solidified droplets, unreacted flux, and condensed particles. The solidified droplets were formed from material ejected from the converter during blowing, while the flux was blown out of the converters immediately after charging. The condensed particles contained the majority of the lead and zinc, as well as the volatile impurities. There was also a significant soluble content of the dusts, increasing with distance from the furnace. The condensed material may be separated from the remainder by a simple washing and sizing technique.

Jan 1, 1996

By Pekka Hanniala

The Outokumpu Flash Smelting process today is the most feasible method for copper matte smelting. The economic feasibility of the process has always been one of the main decision making criteria in smelter projects. Thus, today about 50 % of the world primary copper production utilizes Outokumpu Flash Smelting Technology. However, in the future, environmental criteria will have stronger and stronger impact on decision making. Flash Smelting technology offers the best pollution control features of any process. today. It is foreseen that, in the near future, the global trend will be that all the smelters must decrease their emissions at an accelerating rate, compelling the smelters to make increasingly larger investments on environmental protection. In most of smelters ?today, Peirce-Smith converting and transfer of the molten material in ladles are the number one pollution source. The key today for copper converting and minimizing emissions is the Kennecott-Outokumpu Flash Converting process, which has proven to be the most effective converting method in terms of pollution control and, production efficiency including capital and operational costs. Outokumpu Flash Smelting technology is applicable also for small to medium scale smelters but the most interesting area is the upper capacity limit for smelting in one line, which has not yet been reached. We predict that by the year 2000 to 2005, there will be at least one smelter which produces 500,000 tonnes of Cu per year based on one Flash Smelting and Flash. Converting unit. The current state-of-the-art of the Outokumpu Flash Smelting - Flash Converting process is presented in this paper as well as some new options for copper production to be utilized in the near future but which are available already today.

Jan 1, 1998

By Eliezer Martinez-Jimenez, Gretchen T. Lapidus

"Electro-assisted reduction is an effective pretreatment to render chalcopyrite less refractory towards oxidative leaching. In this process, chalcopyrite is selectively converted to chalcocite or copper metal in an electrolytic cell under ambient conditions, while ferrous ion is leached into solution. However, the reaction velocity is hampered by the formation of a ferrous sulfide passivating layer on the solid surface, especially at elevated solid to liquid ratios. In the present work, several strategies for overcoming this problem were evaluated. On one hand, specific ligands for ferrous ion were added in order to increase its solubility and, on the other, an anode material which promotes the oxidation of the sulfide ion was chosen. Leaching tests showed citric acid to be an effective ligand for both ferrous and ferric ions and, in combination with a lead-silver anode, significantly increased the kinetics of chalcopyrite reduction and subsequent copper leaching.IntroductionAttempts to oxidize chalcopyrite at a rapid rate in aqueous solutions, below their normal boiling point, have met with difficulties because of passivation by some of its own components. An alternative line of research explores reductive pretreatment, transforming the chalcopyrite into less refractory copper phases, which can later be oxidized. A recompilation of these efforts up until 2000 was published by Dreisinger and Abed [1]. However, this practice usually requires large excesses of reducing agents, such as copper, lead, aluminum or iron, and in this last case at near-boiling temperatures, in highly"

Jan 1, 2012