By Ferid Kromer

Geography: The Tagtepe district of the Vilayet of Eskigehir is about 20 miles northeast of the city of Eskigehir (approximately midway between Ankara and Istanbul) in western Anatolia. The area is a mountainous one, the highest peak being Tagtepe Mountain (5200 ft) which is approximately in the center of the district. The mountains drop off to the deep valley of the Sakarya River on the north and to the plain of Eskigehir on the south. FERID KROMER, Junior Member AZME, is a Consulting Mining Engineer and General Manager, Bagtag Turk Maadin Ltd., Istanbul, Turkey. New York Meeting, February 1950. TP 2629 H. Discussion of this paper (2 copies) may be sent to Transactions AIME before Feb. 28, 1950. Manuscript received Dec. 29, 1948. For the most part, the watershed is on the northern side of the mountain barrier, draining into the Sakarya River, which in turn empties into the Black Sea midway between Zonguldak and the mouth of the Bosphorus. The approximate area covered by the Tagtepe district is shown in fig. 1. Transportation to shipping points is available via the Istanbul-Ankara railroad. The station on this line nearest the mining district is Alpikoy station, about 20 miles by road southwest of Tagtepe Mountain. Interior roads within the district are poor. Being of dirt, the winter rains and snows render them almost impassable for trucks from about the middle of December until the end of March, thus presenting a considerable transportation problem. However, the roads from the Bagoren and Tagtepe chromite mines to the railroad shipping point at Alpikoy station have recently been repaired and will be maintained for all-weather truck transportation. Detailed climatic data are not available. However, in general the spring, summer, and early autumn months are dry, and good weather may be expected from May until early November. Then the winter rains commence, and heavy snow is usual during January and February. Geology: The mountainous structure of Tagtepe belongs to basic rocks of serpentine (Variscan Orogeny) which is in contact with Paleozoic schists at west, and an Oligocene outcrop of red clays in Margi-Sepetci region (see fig. 1) at southeast. The northwest and southwest borders of Tagtepe district are, respectively, surrounded by Paleozoic schists and pebbly gray and yellow Neogene clays. More recent formations of alluviums overlay the plain of Eskigehir. Dark basic rocks of trachytes with hornblende are visible on Turkmenbaba Mountain, at the west of Tagtepe. Mineral Occurrences: Chromite: the most important mineral found in any quantity in the Tagtepe district. The alignment of the deposits of chromite is in general along the line Bagoren-Tagtepe (see fig. 1). The first mines in the area were those of Tagtepe and Bagoren, which were developed over 20 years ago with Swedish capital. Other deposits of chromite, more recently discovered and so far of less importance, are being worked at Kurucor, Komurcu, Gelinmezari, and Lacin (see fig. 1). Deposits average generally between 46 and 48 pct chromic oxide, with the exception of the Bagoren mine which averages 44 pct. However, a new lode, very recently plotted, in the Tagtepe mine averages 50 pct Cr,O,, 4.6 pct SOz, and 7 pct FeO. Geological character of the chromite occurrences in the Tagtepe mine may be considered typical of most chromite lodes in this area. The indications are that the formations of ore lenses are developed by the segregation of chromite crystals intruded into the serpentinized rock, and exposed later to tectonic movement within the zone of crystallization. All lenticular masses are more or less regular in shape and follow each other in southeast-northwest direction and dip generally 70" NE. Ore lenses do not seem to persist in depth, average depth of two lenses is 60 ft below surface. Three lodes .have been mined as open-pit. The average dimensions of individual lenses are as follows: pitch length, 100 ft; breadth, 27 ft; and width, 20 ft. The lenses and their enclosing rocks are broken by parallel fractures in approximately east-west direction. These joints are filled, except in one lode, with cementing material, which gives to the ore a

Jan 1, 1951

By Terkel Rosenqvist

J. Chipman (Massachusetts Institute of Technology, Cambridge, Mass.)—The fact that the experimental work has been applied to copper rather than iron and that the paper is presented to the Iron and Steel Division, I regard as rather significant. It shows the unity of metallurgy and the fallacy of trying to cut it up by metals. This result for the solubility of sulphur in molten copper correlates with Professor Schuhmann's finding that the published data on the other side of the copper-sulphur miscibility gap are also in error. I should like to ask the author to say a little bit more about the sulphur capacity of the slag. T. Rosenqvist (author's reply)-—I hope that Dr. Chipman will find the derivation of the expression for sulphur capacity more clearly explained in the printed version of the paper than in the oral discussion at the meeting. I feel that this quantity, which actually is the ratio of two activities, can be measured more easily than the individual activities. Even if the ratio CaO/CaS is chosen as the standard state, the expression can be used for any slag, even for slags completely free of lime, and it represents a way to put the desulphurizing power of all slag constituents into one bag. Some doubt has been expressed as to whether oxygen ions really exist in calcium oxide and in molten slags. From a thermodynamic view point that question is of minor importance. The term oxygen ion activity, or any activity for that matter, is defined rigorously by the equation: activity = exp p/RT, where p is the change in free energy connected with the transfer of one mol of ions from the standard state into the slag. Whatever happens to the ion in the slag is of no concern to the thermodynamicist. Regardless of whether the ion is "free" in the slag or not, or whether it is present in a very small amount, its activity can always be expressed, and for a thermo- dynamic calculation that is all we need. However, ionic activities will only be of some real value if they are simple functions of the slag composition, or can be measured easily. Concerning the real nature of the oxygen in the slag, my feeling is that the oxygen atom has a rather multiplex nature depending on how strongly it is tied by covalent forces or polarized by the other atoms or ions present. The oxides of iron, cobalt, and nickel differ from calcium oxide and blast furnace slags as to the amount of free electrons that can give rise to electronic conductivity. In slags we know that the conductivity is mostly ionic. The fact that reversible emf's can be obtained with oxygen electrodes in certain salt melts, indicates a significant amount of oxygen ions in these melts. But extended work, e.g. polaragraphic studies and measurements of transference number; are needed to obtain quantitative information about the real structure of the slags. D. E. Babcock (Republic Steel Corp., Youngstown, Ohio)—-With reference to the ion, it might be well to remember Dr. Moses Gomberg. All of his life he had no use for the ionization theory and he contributed greatly to the field of chemistry on the assumption there was no such thing as ions. I do not think we have to worry about whether the oxygen is ionic or not. I think one thing specifically should be brought to your attention and this I think is one of the important contributions of Dr. Rosenqvist. He pointed out what we know as oxygen potentials or what is described as oxygen potentials. I have used this concept for a long period of time and I want to state that if this concept is properly applied, it vitiates much of what we have in the literature, or makes our usual ideas regarding oxidation seem primitive. That one thing is more valuable than almost all the rest of the discussion as a fundamental basis on which to build a reasonable in-

Jan 1, 1952

By Ferid Kromer

Geography: The Tagtepe district of the Vilayet of Eskigehir is about 20 miles northeast of the city of Eskigehir (approximately midway between Ankara and Istanbul) in western Anatolia. The area is a mountainous one, the highest peak being Tagtepe Mountain (5200 ft) which is approximately in the center of the district. The mountains drop off to the deep valley of the Sakarya River on the north and to the plain of Eskigehir on the south. FERID KROMER, Junior Member AZME, is a Consulting Mining Engineer and General Manager, Bagtag Turk Maadin Ltd., Istanbul, Turkey. New York Meeting, February 1950. TP 2629 H. Discussion of this paper (2 copies) may be sent to Transactions AIME before Feb. 28, 1950. Manuscript received Dec. 29, 1948. For the most part, the watershed is on the northern side of the mountain barrier, draining into the Sakarya River, which in turn empties into the Black Sea midway between Zonguldak and the mouth of the Bosphorus. The approximate area covered by the Tagtepe district is shown in fig. 1. Transportation to shipping points is available via the Istanbul-Ankara railroad. The station on this line nearest the mining district is Alpikoy station, about 20 miles by road southwest of Tagtepe Mountain. Interior roads within the district are poor. Being of dirt, the winter rains and snows render them almost impassable for trucks from about the middle of December until the end of March, thus presenting a considerable transportation problem. However, the roads from the Bagoren and Tagtepe chromite mines to the railroad shipping point at Alpikoy station have recently been repaired and will be maintained for all-weather truck transportation. Detailed climatic data are not available. However, in general the spring, summer, and early autumn months are dry, and good weather may be expected from May until early November. Then the winter rains commence, and heavy snow is usual during January and February. Geology: The mountainous structure of Tagtepe belongs to basic rocks of serpentine (Variscan Orogeny) which is in contact with Paleozoic schists at west, and an Oligocene outcrop of red clays in Margi-Sepetci region (see fig. 1) at southeast. The northwest and southwest borders of Tagtepe district are, respectively, surrounded by Paleozoic schists and pebbly gray and yellow Neogene clays. More recent formations of alluviums overlay the plain of Eskigehir. Dark basic rocks of trachytes with hornblende are visible on Turkmenbaba Mountain, at the west of Tagtepe. Mineral Occurrences: Chromite: the most important mineral found in any quantity in the Tagtepe district. The alignment of the deposits of chromite is in general along the line Bagoren-Tagtepe (see fig. 1). The first mines in the area were those of Tagtepe and Bagoren, which were developed over 20 years ago with Swedish capital. Other deposits of chromite, more recently discovered and so far of less importance, are being worked at Kurucor, Komurcu, Gelinmezari, and Lacin (see fig. 1). Deposits average generally between 46 and 48 pct chromic oxide, with the exception of the Bagoren mine which averages 44 pct. However, a new lode, very recently plotted, in the Tagtepe mine averages 50 pct Cr,O,, 4.6 pct SOz, and 7 pct FeO. Geological character of the chromite occurrences in the Tagtepe mine may be considered typical of most chromite lodes in this area. The indications are that the formations of ore lenses are developed by the segregation of chromite crystals intruded into the serpentinized rock, and exposed later to tectonic movement within the zone of crystallization. All lenticular masses are more or less regular in shape and follow each other in southeast-northwest direction and dip generally 70" NE. Ore lenses do not seem to persist in depth, average depth of two lenses is 60 ft below surface. Three lodes .have been mined as open-pit. The average dimensions of individual lenses are as follows: pitch length, 100 ft; breadth, 27 ft; and width, 20 ft. The lenses and their enclosing rocks are broken by parallel fractures in approximately east-west direction. These joints are filled, except in one lode, with cementing material, which gives to the ore a

Jan 1, 1951

By J. M. Karpinski, R. O. Tervo

A method and equipment have been developed for measuring the impact strength of grains of brittle materials. It is shown that brittle materials develop a characteristic particle size distribution when fractured by impact. A simple mathematical model has been found to describe this distribution, and one of the parameters of the model has been designated the r value. The r value is directly proportional to impact energy and, for fixed impact energy, it becomes a useful criterion of grain strength. Data are presented on the variation of the r value as a function of sample history, initial size, energy input and number of impacts. The results are interpreted in terms of the flaw theory of brittle fracture. The view is now widely held that brittle materials comprise a strong matrix, throughout which flaws or points of weakness are scattered at random. Failure always starts at one or more of these imperfections, and planes of fracture are established by the geometry of the flaw distribution. This view has been developed extensively by Weibull 1,2 and experiments of a confirmatory nature have been reported.3,4 Thus the process of fracture or size reduction of brittle materials can be regarded as a process of elimination or creation of flaws, and the concept of strength is intimately connected with the size and history of the specimen tested. One consequence of the point of view described above is that brittle materials will fracture to yield similar size distributions, although the impact energy to produce a given amount of fracture may vary greatly from one material to another. Generally speaking, experimental investigations of brittle fracture in solids have been confined to two extreme experimental situations. On one hand, we have tests on single specimens of well-defined, but artificial, geometry and, on the other, empirical data have been obtained on the feed-product relation in a variety of mills. The first situation necessitates specimen preparation, which in the case of brittle materials is equivalent to a priori size reduction, while the second one suffers from the disadvantage that little knowledge is gained about individual fracture events. Also, the statistical significance of single specimen tests may be questioned. Our approach lies somewhere between these two extremes. We test a large population of sized specimens and yet subject each specimen to a single fracture event. In 1956 G.H. Fetterley of Norton Co., Chippawa, Ont., made the empirical observation that product size distributions obtained from impacting sized grits can be described by the following equation where R is the proportion by weight of the grain that remains on a screen having an opening x on a side, x, is a parameter having the dimensions of length, and r is a number. This equation has since been derived on a theoretical basis by Gaudin and Meloy.5 They identify x, with the initial size of the test piece and r with the number of flaws per unit length. As will be shown below, our experiments indicate that both x, and r are functions of energy and hence they should more properly be called the effective initial size and the effective number of flaws respectively. Also, our empirical data give us no basis for assuming that r represents the effective number of flaws per unit length, rather than per unit volume. METHOD AND MATERIALS The impact test machine has been designed to feed specimens, essentially one at a time, into an evacuated chamber, where they fall freely and are struck with random orientation by one or the other of a pair of flat steel vanes. The vanes are mounted at opposite ends of a steel bar, which rotates at a closely controlled angular velocity about a vertical axis. Fig. 1 shows the flat circular vacuum chamber with the cover removed, and the horizontal steel bar with the steel vanes at the ends. The cylindrical pot in which the grains are collected after impact appears at the left. Fig. 2 shows the equipment assembled for a test. The vacuum chamber occupies the central position with the variable speed drive below the table surface, the vacuum pump at the extreme left

Jan 1, 1964

By Alex Boozenny

The results of potential measurements between 1) a titaniurn electrode in NaCl-TiCl, melts and a graphite-cizlorine reference electrode and 2) a titanium electrode in NaC1-Nu "melts and a graphite-chlorine reference electrode show that the following relationship expresses the equilibrium relationship between the TiCl, and the dissolved metallic sodium concentrations, expressed in mole fraction units, in dilute NaCl welts at 850°C. The results of potential measurenments between a graphite electrode in NaCl-TiCl, melts that were saturated with TiCl, and a graphite-chlorine reference electrode, when combined with the standard free energy data given in literature, gave the following expression for the equilibrium relationship between the TiCl, and TiCl, concentrations, expressed in mole fraction units, in dilute NaCl melts at 850°C. These relationships are for melts in equilibrium with pure titanium. In impure systems, less sodiurn and more TiCI, can be copresent with a given concentration of TiCl,. AFTER 10 years of existence, the titanium metal industry still relies on the original Kroll and the sodium reduction processes for the only important means of converting titanium-bearing ores to titanium metal via production of titanium tetrachloride as an intermediate. Through years of modification and development these two processes have evolved to a point where any further major economic advances in the field of titanium metal production must be achieved through implementation of processes which are distinct departures from simple magnesium or sodium reduction of titanium tetrachloride. Concurrently with the refinement of the Kroll and sodium reduction processes, industries and government have sponsored research and development in the field of producing titanium by electrolysis of oxides,' carbides,' and halides3'4 in fused salt media. However, the incomplete understanding of the physical chemistry of fused salt systems has in many cases hindered the development of promising new titanium production processes to the point where they will have a clear advantage over the processes presently employed. Fortunately the volume of information on fused salt physical and electrochemistry is increasing at an accelerating pace. The first approaches tbward investigating the electrochemical behavior of fused salt systems have been the measurements of equilibrium potentials of metals immersed in melts containing their halides.' Some work on the kinetics of fused salt electrochemical processes has been reported.'09" Some descriptions of the structural composition of fused salt systems are also available. The work described herein is a continuation of the study of metal electrode potentials in fused salts. Specifically, this contribution to the growing store of fused salt chemistry information presents a description of the equilibrium relationships between the concentrations of titanium dichloride, titanium trichloride, and metallic sodium in fused sodium chloride. The investigation of the titanium dichloride-titanium trichloride equilibrium relationships is not completely new. Kellog and Krye and Melgren and opie15 have presented the results of chemical analysis of salts containing titanium chlorides. Flengas and lngrahaml' have published the results of an investigation of these equilibrium relationships obtained by measurement of electrode potentials in a fused NaCl-KC1 mixture. The investigation described herein differed from that of Flengas and Ingraham principally in the use of straight NaCl as the solvent in place of the more costly and more difficult to purify mixture. This investigation was conducted in three parts. First, the equilibrium potentials of titanium in sodium chloride containing known concentrations of titanium dichloride were measured. A graphite-chlorine electrode was employed as reference. Second, the equilibrium potentials of titanium immersed in sodium chloride containing known concentrations of elemental sodium were measured. Third, the equilibrium potentials of graphite immersed in titanium tetrachloride-saturated sodium chloride containing known concentrations of titanium trichloride were measured. The results of these three related investigations are presented in the above order. The results are combined with the thermodynamic properties of titanium chlorides and sodium chloride, obtained from literature, to give the titanium dichloride-titanium trichloride-elemental sodium equilibrium concentration relationships. In the test, whenever a melt contains titanium chlorides in predominantly divalent form, the melt

Jan 1, 1962

By G. R. Belton, Y. K. Rao

A galvanic cell, using liquid MgCl2 or MgC12-CaC12 mixtures as the electrolyte, has been used to determine activities in Mg-A1 liquid alloys between 700' and 880°C. The incovporation of a chlorine electrode in the cell also allowed measurements to be made of the standard free energy of formation of MgCl2(l). The results are shown to be in good agreement with thermo-chetrlical values from the literature, and this is taken as evidence that the small, known solubility of magnesium in iMgCl2 introduces no significant error in galcanic cell measurements. Within experimental error, the activity coefficients and relative partial molar enthalpies at 800°C are shown to be represented by the following "subregular" solution equations: logy~~ =-0.68(1 -xMgj3 log yAL =-1.02(1 - XMf + 0.68(1 - XMf H.M = -4400(1 - %)3 / cal Mg 7Ag' HZ =-6600(1 - xA1)' + 4400(1 - XMf cal SCHNEIDER and toll' have used a transpiration technique to measure the vapor pressures of magnesium over Mg-A1 alloys between 544" and 594°C. amsstad,' however, has since suggested that the extrapolation to zero flow rate, used by these authors in interpreting their apparent pressure vs flow rate data, gives unreliable results. Rogers, Tomlinson, and Richardson,3 in interpreting the results of solution equilibria between Mg-A1 alloys and liquid MgC12, also considered the measurements of Schneider and Stoll to be unreliable and preferred to derive activities for the alloys from the earlier boiling point determinations of ~eit~ebel~ and the partial molar heats recommended by Kubaschewski and ~atterall.~ These latter heats were based substantially on the early calorimetric work of Kawa-kami but, unfortunately, his work on other systems has sometimes been found to be inaccurate.7 Rogers et al., in the above-mentioned paper,3 tentatively concluded that the most likely species responsible for the limited solubility (0.3 mole pct at 800°C) of magnesium in MgC12 were Mg° (neutral) and Mg2++. Two more recent studies8,9 have supported Mg2++ as the soluble species. In the present study, activities in Mg-A1 alloys have been determined by means of a galvanic cell involving liquid MgCl2 or MgC12CaCl, mixtures as the electrolyte. Since the reactive nature of magnesium precluded simple Faraday yield experiments, a chlorine electrode was incorporated in the cell in order that the performance of the cell could be checked by measurements of the heat and free energy of formation of MgC12. This procedure was considered necessary since it has been suggested1' that the solubility of a metal in a molten salt might introduce electronic conductivity; also, previous determinations of the standard electrode potential for MgC12 differed by as much as 70 mv11-13 EXPERIMENTAL Materials. Analyses of the materials used in preparing the alloys and the electrolyte mixtures are presented in Table I. The alloys were prepared by induction melting weighed amounts of the metals in a graphite crucible held under an argon atmosphere. Pure anhydrous magnesium chloride was prepared by heating the mixture MgCl, . 6H20 +NH4C1(1:1) to 650°C, followed by melting under dry argon. The melting point of the dry MgC12 was found by differential thermal analysis to be 714.8oC, which compares well with the accepted value of 714C.14 This agreement was taken to be an indication of the high purity of the dried salt. Table I. Compositions of Materials, wt pn Impurity Mg Al MgCI2 CaCI, Ba - - 0.005 Ca - - 0.010 Cu 0.02 0.02 Fe - 0.10 0.001 0.010 Pb 0.01 - 0.001 0.005 Mn 0.15 0.001 Si - 0.10 Sr - - 0.005 MBSO* - 0.040 ARGON TUNGSTEN CHLORINE LEAD—411 11 II ALUMINA 'A I / ave GRAPHITE on irA~_ ( ^"l ROD MAGNESIUM S>ILICA~^ /, OR ALLOY-. I /A] ___________ -«^- _ ELECTROLYTE I y FRITTED DISCS Fig. l—Arrangement of chlorine and metal electrodes in electrolytic cell.

Jan 1, 1970

By Eugene A. Thiers, William V. Morris

INTRODUCTION Direct reduction processes reduce the various commercial forms of iron oxide (pellets, concentrate, fines, etc.) to metallic iron at temperatures lower than that of molten iron. Thus, this technology includes practically, all iron reduction processes other than blast furnaces and electric pig iron furnaces (whose output in terms of world production is negligible). The product of these processes which is known as direct reduced iron (DRI), or sponge iron, is primarily used as a source of metallic iron in steel-making operations. Interest in DRI, which has been significant since the early 1960s, increased significantly in recent years with the rapid growth of DRI installed capacity throughout the world. The importance of the subject for the Circum-Pacific region stems directly from the influence that DRI has on iron ore consumption and on future steel development for this region. Although there is widespread agreement that electric furnaces will continue to increase their share of global steel output, and especially so in the countries of the Pacific Steel community, some doubts exist about future scrap supplies being adequate to support growth at past rates. The authors believe that such doubts are soundly based. As this paper points out, the total supply of all metallics used in electric furnaces may not be adequate to support the extrapolated rapid growth in electric furnace steel production. This paper seeks to provide perspective on the global and Circum-Pacific prospects for DRI in light of recent energy price developments and the current recession. In this regard, the demand for DRI within the context of recent evolutionary patterns in steel-making, the outlook of DRI supply in terms of prevailing production costs, and the prospects of new technology are discussed. THE DEMAND FOR DRI Although several reports published in the last 10 years predict high rates of growth in DRI, the subject remains a controversial one. Significant growth has indeed occurred, but not to the extent anticipated in the studies summarized in Table 1. The substantial difference between previous expectations and present reality can be ascribed primarily to: (1) lower growth in steel production than formerly anticipated; (2) numerous cancellations of DRI facilities that were previously announced; and (3) a fundamental and probably irreversible change in the economics of DRI production. Note that DRI capacity at the end of 1980 was about 16 million tonnes, a significantly lower figure than any of the projections above. In addition, DRI production was only about half of capacity, reflecting the abnormally low rates of capacity utilization in this industry. [ ] Before examining the current outlook in steel, it is pertinent to note that the market for DRI is usually different in the industrialized countries of the West from that in developing countries. In the former, the available infrastructure and industry's diversification extends DRI's potential markets to numerous steelmaking, foundry, and other industrial applications, although competition from scrap and other forms of metallic iron is constant. Scrap is generally available in these countries and, therefore, DRI competes with it in electric furnace steelmaking, basic oxygen steelmaking (as a coolant), cupola foundry operations, or as an additive in the metallic charge for open hearth and blast furnaces. On the other hand, DRI in developing countries is often allocated exclusively to domestic electric furnace steelmaking or, when capacity exceeds domestic captive requirements, to export. Notwithstanding quality considerations, DRI is being and is likely to continue to be used predominantly as a source of metallics in iron and steel-making. Other uses of DRI, such as in copper cementation represent a marginal market in terms of overall tonnage and can be ignored at this point. Therefore, DRI demand is-determined by the overall availability of metallic scrap in its various forms--a function of steel production and its probable evolution. The Global Steel Outlook Given the present recession, an objective appraisal of the long-term outlook for steel is particularly difficult. On the one hand, historical trends and, especially, the inertial forces associated with such a basic industry as steel must be recognized; such trends suggest that the current stagnation with

Jan 1, 1982

By O. W. Simmons, L. W. Eastwood, C. M. Craighead

H. Schwartzbart and W. F. Brown, Jr.—The authors have divided the effects of recovery on the true stress-true strain curve into two types; metarecovery, which effects only the first part of the curve or the yield strength, and orthorecovery, which effects the flow stress at any strain. Both of these are said to be true recovery effects, involve no recrystallization, and are explained by the removal of two different types of imperfections caused by work hardening. However, there seems to be some question as to whether the data are sufficiently conclusive to exclude, as an explanation of the authors' results, a mechanism based on the relief of residual stresses between the grains or slip bands and recrystallization. It appears that metarecovery could be interpreted in the same fashion as a customary interpretation of the Bausch-inger effect. The balanced system of internal stresses which exists between grains in a strained specimen due to varying orientation and, hence, yield strengths, of the different grains is responsible for a reduced yield strength in compression following pre-tension, and, similarly, for an elevated yield strength in tension following pre-tension. If the specimen is now heated so that the internal stresses are relieved by creep, then the yield strength in tension following tension will have been reduced and in compression following tension will have been raised. There seems to be a very strong case for the lack of recrystallization in the aluminum investigated by the authors, if one defines recrystallization as the presence of visually detectable new grains or accepts the X-ray evidence as conclusive. One must remember, however, that the appearance of spots on the back-reflection X-ray patterns cannot be taken as the time when recrystallization first started. The areas of recrystallized strain-free material must first have grown to a size large enough to give distinct spots on the patterns and this may take some time. Averbachl7 in an investigation of brass has shown that recrystallization can be detected by extinction measurements at temperatures lower than those based on hardness or X-ray line width determinations. It can be seen from fig. 10 that the rate of recrystallization is extremely low over a considerable time period at the onset of the process. Observations on the rate at which small amounts of recrystallization effect the flow stress would have given further insight as to whether undetectably small amounts of recrystallization might have been responsible for orthorecovery. Also, the question arises as to whether the effects observed in fig. 6 for various times and temperatures could not have been obtained if the time at 212°F were sufficiently long. In addition, the argument that the curve in fig. 10 is not sigmoidal seems weak in view of the scattering of the points. It is conceivable that an accurate determination of the curve for the first 100 hr would exhibit a relationship other than the one drawn. There is one point we would like to raise about the condition of the starting material. The authors annealed their material at 750°F for 15 min to remove the effects of any previous work hardening or machining strains. Reference to the work by Anderson and Mehl shows that this treatment may not have completely recrystallized the aluminum, so that the starting material may have had some strained areas. Higher temperatures or longer times may have been required to remove the effects of any small strains. We would like to mention some results of tests being conducted at the Lewis laboratory of the National Advisory Committee for Aeronautics in an investigation of the Bauschinger effect in relation to fatigue. Tests were performed on annealed electrolytic copper and several annealed brasses. Specimens were pre-strained 1 pct in tension and then tested in compression or tension with and without intermediate stress-relieving annealing treatments at 500°F for various times. Specimens heated at 500°F for 10 1/2 hr showed an elevation of the flow curve in compression and an approximately equal lowering of the flow curve in tension when compared with the curves for the un-heat treated specimens. After approximately 0.8 pct strain, all flow stresses coincided and were equal to the flow stress of the virgin material at this strain. This behavior is consistent with the metarecovery observed for aluminum by the authors and for which a residual stress model can be used. On the other hand, increas-

Jan 1, 1951

By Joseph E. Pogue

THAT the domestic consumption of gasoline displays a marked seasonal variation, with a low in the winter and a high in the summer, is well known. It is logical to expect that the nature of the variation has itself been undergoing a change as a result of improvement in roads, general employment of closed cars; and growth of mass haulage; but so far as I am aware the change in seasonal variation has never been investigated and measured. It is the purpose of this paper to present the method and results of such an investigation undertaken as a contribution to the technique of planning operating schedules now so prominent in connection with the functioning of the industry under a Federal quota system. For the method employed I am in-debted to the suggestions and help of Frederick R. Macaulay', who kindly looked over the work sheets; and credit is due Barnabas Bryan, Jr., for assisting in the computations and the graphic work. Ideas for the approach to the problem were also derived from an article by Aryness Joy, and Woodulief Thomas of the Division of Research and Statistics of the Federal Reserve Board*-.

Jan 1, 1934

By A. A. Brant

In this presentation, concepts of the formation and evolution of the universe, the earth, and the cyclic civilizations of man are broadly outlined. The 5 billion or more years of the universe and the 4% billion years of the earth are contrasted to the 5000 years of modern society and the 100 years of objective scientific breakthrough. THE UNIVERSE Let us start back as far as possible, to the beginnings of this universe, some 5 billion or more years ago. This is a time interval that can be crudely underestimated by the moon-earth tidal friction effects that have increased the length of the day by about 1/1000 second per century — from a 5 to 7 hour day to its present 24 — and have moved the moon away at 5 inches per year to its present 240,000 miles. The oldest stony meteorites from interplanetary space give an age dating of some 4.6 billion years, approximating the time of formation of our earth. Further, certain stars pulsate, the period of pulsation being related to their absolute brightness. Measuring apparent brightness and comparing, gives the distance away. Thus Hubble and Shapley of Harvard, from 1925 on, were able to show that the universe reached as far as our telescopes could scan. The Doppler shift of the hydrogen red lines could only mean that the nebulae, or galaxies, were moving away away at velocities increasing with their distances, by 180 km/sec velocity increase for every million light year's distance. In short, the universe is expanding like an exploded bomb. Comparing the velocity increase per million light year's distance again indicates a zero time of some 5 billion years' Thus it appears that this universe had a finite beginning. Physical measurements and present theories permit some picture of our universe's birth. We know since Einstein that many forms of energy are equivalent, e.g., mass, and electromagnetic radiation, aspects of which are heat and light. Now with expansion, radiation density or equivalent mass decreases as a length factor to the 4th power, while mass as matter decreases at a length factor cubed. The temperature in outer space is now perhaps 100° absolute and the radiation mass equivalent is but 1/1000 the rarefied interstellar gas densities. Decompressing the universe to a starting point, however, raises temperature more rapidly than mass density, and results in a high radiation mass energy fraction, which since it is proportional to temperature to the 4th power suggests a zero point temperature of several billion degrees, brighter than any sun. "Let there be light and there was light," according to Genesis 1-3. Now what further initial conditions must there be to explain the relative abundance of the elements in the universe, which by spectral analyses of the earth's crust, stony meteorites, and the sun and stars is surprisingly uniform throughout. Some 55% of all cosmic matter is hydrogen, some 44% is helium and only 1% is made up of all the heavier elements in much the same proportions as on earth. These latter decrease logarithmically in abundance up to atomic weight 100, then level out. This consistent abundance distribution of elements in the universe may be generally explained by taking at Time Zero a hot neutron gas of density about 10-3 grams per cc, at a temperature of several billion degrees Centigrade, with a high radiation energy fraction. Generally neutrons break down into positrons and electrons within about ten minutes, but at the initial high temperature and radiation pressure would recom-bine. However, with rapid expansion and decrease of temperature and pressure, the neutron disintegration would run uncompensated and aggregation would result from neutrons and protons uniting in different degrees of complexity. The total calculated element aggregation time would be about one hour while the temperature still remained above one billion degrees. The element abundances formed would depend on density of the nuclear gas, simplicity of the atom formed, and the neutron capture cross section. Thus a higher density

Jan 1, 1964

By F. H. Buttner, H. Udin, J. Wulff

Using a modified Udin, Shaler, and Wulff technique, the surface tension of gold Udin, purified helium was found to be 1400 ± 65 dynes per cm for the temperature range 1017° to 1042°C. IN the original Udin, Shaler, and Wulff technique for measuring the surface tension of copper: variously weighted wires were allowed to extend or contract in a copper cell held at elevated temperatures in vacuum. By plotting stress vs. strain for a wire array in one test, the stress at zero strain is obtained. This is the point where the contractile forces resulting from surface tension are balanced by the applied load, according to the expression: y = e=o r [1] where y is the surface tension in dynes per cm; a,,,, the stress at zero strain in dynes per cm; and T, the radius of the wire in cm. The assumption that the wires deform viscously permits the drawing of a straight line through the points on the stress-strain plot. Justification of the assumption has received further experimental support recently.'-' The presence of grain boundaries in the wires requires a correction to the original expression used." Thus: y = d4=T [l- (dl) (ar)Y1 [2] where, n/l is the number of grain boundaries per unit length, and a, the ratio of grain boundary tension to free surface tension. Alexander, Kuczynski, and Dawson in studying the creep of gold wire in vacuum were unable to obtain reproducible values of the surface tension of gold. In plotting stress vs. strain for progressively longer times, they found that the stress at zero strain drifted with time from positive stress values to negative values. Similarly, for the surface tension of silver, reproducible values were obtained only when a purified helium atmosphere was substituted.' Evidently the evaporation rate of silver in vacuum is too high at the temperatures employed to obtain solid-gas equilibrium even in a similar metal enclosure. Thus reproducibility of results is lost. Experimental Procedure The experimental procedure was much the same as that originally developed by Udin, Shaler, and Wulff with a few modifications and improvements. For greater accuracy in strain measurements, knots gave way to cut gage marks as shown in Fig. 1. These were made with a hand-driven lathe in which razor blades serv'ed as cutting tools. Also a more precise cathetometer with a screw accurate to 0.00015 cm was used. The tests were conducted in an atmosphere of purified .helium rather than in vacuum in order to avoid possible evaporation difficulties. Five mil wire of high purity gold (99.98 pct) was used. After cutting in the gage marks, each wire of a series of about 12 was differently loaded by welding a gold ball to one end. This was done by dipping the end of the wire in a cooling gold droplet, previously melted on a charcoal block with a No. 2 acetylene torch. The other end of the wire was strung through a hole in a gold lid and twisted over the edge to hold the wires fixed and in suspension from the lid. The lid and mounted wires were then dipped in pure ethyl alcohol to dissolve any skin oils and dirt on the surface of the wires due to handling. Finally the lid was put in place on an alundum crucible lined with gold so that the wires hung freely within the gold-lined chamber. This whole assembly was next heated in a quartz nichrome wound tube furnace and heated for a few minutes at 600°C to soften the wires. After this anneal the wires were easily straightened with tweezers. The wire assembly was finally annealed 10" to 25°C above the subsequent test temperature for 2 hr. This treatment allowed the grains to grow to equilibrium size and shape. After the anneal, the lid was mounted in front of the cathetometer. The gage length was measured by sighting the 40 power microscope on the upper lip of the lower gage mark for the first reading, then traveling up to the lower lip of the upper gage mark for the final reading. This procedure was repeated four times to give an average gage length value. In this manner the annealed gage length and the final gage length could be measured to determine the strains. During all measurements, grain counts were made.

Jan 1, 1952

By C. E. Lundin, D. T. Klodt

The binary alloy systems, Y-Ti, Y-Zr, and Y-Hf, have been investigated throughout their entire composition regions. There is no compound formation in any of the systems, and each system is characterized by a single eutectic reaction. The eutectic compositions and temperatures are as follows: A eutectoid reaction pct Y and 870°C occurs in the Y-Ti system, whereas a peritectoid reaction,: pct Y and 880°C occurs in the Y-Zr system. Peri-tectic-type reactions at temperatures above the eutectic levels are postulated for the yttrium and hafnium transfovmations. The development of the technology of yttrium has been given considerable attention during the past few years, and studies of binary phase equilibria have, of course, taken a prominent position in this development. In many respects yttrium, in the third group of metals of the periodic table, is similar to the adjacent group of metals, titanium, zirconium, and hafnium, and the knowledge of the phase relationships of yttrium with these metals is basic to their technology. MATERIALS AND EXPERIMENTAL PROCEDURES Materials. The metals for this investigation were supplied by the General Electric Co., Aircraft Nuclear Propulsion Department. The yttrium was in the form of an arc-melted ingot, and the other metals were in the form of high-purity, iodide-Process crystal bar. Table I lists the purities of these materials. Alloy Preparation. Melting was done by conventional techniques in a nonconsumable electrode arc furnace in an atmosphere of purified argon. Melting conditions for each binary system were the same. Each alloy button was inverted and remelted several times to assure homogeneity. Accurate weights of the charges and resultant alloy buttons were obtained to indicate deviations from intended compositions. No chemical analyses were obtained since melting weight losses were consistently in the range of 0.1 to 0.2 pct of the total weight. 10- or 20-g buttons for each 5.0 wt pct composition increment were melted to survey the three individual alloy systems. Additional alloys differing in composition by 1.0 or 0.1 wt pct increments were also melted to study selected regions of the systems. Metallograpllic Techniques. Standard metallo-graphic techniques were followed for mounting and rough grinding. Preliminary polishing was accomplished using 6-u diamond paste as an abrasive on a Metcloth Lap. Final polishing was done on a Microcloth-covered wheel using 1-u diamond abrasive paste. Purified kerosene was used as a lubricant for both polishing stages. • sothermal- Annealing. Alloys were sectioned for as-cast structlure examinations and then homogenized in preparation for isothermal-annealing treatments. Homo{:enization was accomplished by cold pressing the alloy buttons followed by 72-hr anneals at 1100c. The alloys were encapsulated in Vycor or quartz for the homogenization treatments or for isothermal anneals. Resistance-wound or resistance-element tube furnaces were used for the annealing treatments. The homogenized alloy buttons were cold rolled until cracking occurred or until a -in. specimen thickness was obtained. Small -in. square) specimens for the isothermal anneals were then sawed from the alloys. Each specimen was wrapped in tantalum foil before being sealed in the capsule. Temperatures during the anneals were controlled The time at temperature necessary to equilibrate the structures during the anneals was determined for each alloy system by holding triplicate specimens of alloys at a constant temperature for three different periotls. The specimens were quenched and examined microscopically to determine the number and amounts of phases present in the micro-structure as a function of time. Melting Studies. Eutectic temperatures of the three alloy systems were established from the results of incipient-melting studies conducted on as-cast alloys. Specimens to be melted were suspended on a tungsten wire inside a graphite cylinder placed in a glass vacuum chamber. An optical pyrometer was used to follow the temperature of the specimen as it was inductively heated in a high vacuum. The temperatures were corrected for emissivity losses by standardizing the pyrometer with known-melting-point metals. Accuracy of the temperature measurements is estimated to be + 10°C. The melting point of the yttrium was determined to be 1550°C by this technique. The invariant-temperature levels were also checked by an anneal-quench technique. This technique consists of annealing a series of

Jan 1, 1962

By Ikuya Takase

INTRODUCTION Since the occurrence of the first oil crisis, coun-tries of the world, especially oil-importing countries have made sustained and vigorous efforts to lessen the dependency on oil as a source of energy supply. The adoption of "Principles of Coal Policy" by the IEA Ministerial Governing Board Meeting in May, 1979 was the first formal action taken by major energy consuming countries. At the Venice Summit in June, 1980, it was agreed that production and use of coal should be doubled over the next ten years. In fact, the world coal use in 1980 showed around a 10 percent increase over the previous year. Recently, we have seen an indication that the balance of oil supply and demand in the short term have eased. But I believe that it remains vital that we continue to encourage the development and introduction of alternative energy sources. Because, from the medium and long range viewpoint the recovery of the worldwide economy will lead us to increased oil requirements and thus we will be faced with the cyclical, structural tightening situation between the supply and demand of oil. Moreover, we are still convinced that the constraint of the supply capabilities of the Middle-East nations may be increasing in the long-term, since there still remains political uncertainties among these nations. Consequently, above all, coal is viewed as an alternative energy resource available for immediate expansion of use and is given as high a priority as nuclear power. In Japan, we regard coal as the most reliable alternative energy resource to replace oil. According to the "Alternative Energy Supply Targets" approved by the Cabinet in November, 1980, the level of coal imports is estimated to approximately double by 1990, while our domestic coal production will remain nearly at the same level. The transition from oil to coal is found in the recent import levels of coal---73 mil¬lion tons in 1980, a 23 percent increase over the 59 million tons imported in 1979. There was an upsurge in steaming coal imports, reflecting the transition in feedstocks---7.2 million tons in 1980, four times over the previous year's amount. Henceforth, from the medium to long range view, the demand for coal, especially that of steaming coal is forecast to continue to grow. The timely expansion of supply capabilities is our utmost concern and should be one of the most significant goals of our comprehensive policy. The Overseas Coal Investigative Committee, a privately organized advisory panel to the Director-General of the Natural Resources and Energy Agency of the Ministry of International Trade and Industry (MITI), investigated means to secure a stable supply of overseas coal. The panel presented its interim proposals in August, 1981, recommending the diversification of coal import sources, extensive use of low rank coal, as well as enhanced international cooperation between coal producing and importing countries. THE CONTENTS OF THE COMMITTEE'S REPORT Four Points for Major Consideration In order to ensure a stable supply of overseas coal, Japan needs adequate policy measures consistent with the characteristics of coal resources and environmental requirements, giving consideration to Japan's status and the role she is expected to play in the areas. From the above, great importance should be attached to the following four points: All the components of the "Coal Chain" (Namely, the development of mine sites, construction of railroads, port loading facilities, coal shipping vessels, port receiving facilities, including coal centers and international transport facilities etc.) should be reviewed and reformed with steps taken to assure efficiency consistent with the entire coal chain system. The complete formation of a coal chain system requires such lengthy lead times and huge amounts of investment that necessary measures should be undertaken well in advance utilizing long-range projections of future demands and various economic surveys. Policy planning should be conducted taking into account of harmonizing stability and economics of the supply structure. For ensuring the long-term stability and expansion of the coal trade, international cooperation on a bilateral and multi-national basis should be encouraged. Mutual understanding and close relationships are essential to facilitate the formation of the supply system and to promote the extensive use of coal. Direction and Problems Related to Supply Stability Expansion of Supply Capabilities. World coal imports in 1979 amounted to 229 million tons, of which Japan's share amounted to 59 million tons, or one fourth of the entire amount. The imports of European and Asian countries accounted for 83 million tons and 7 million tons respectively. According to the examination of the Investigative Committee, Japan's coal requirement is estimated to be between 140-150 million tons by 1990, nearly the same level as announced in the Provisional Long-Term Energy Supply and Demand Outlook in 1979. This fore¬cast is-to be revised in April, 1982. Japan's demand is expected to be met through fiscal 1985; however, by 1990, the supply is estimated to fall short of demand, particulary, in the field of steaming coal. For the expansion of supply capability, first, mine development should be accelerated. The proposed

Jan 1, 1982

By D. H. Desy, L. C. Fincher

The magnesium-rich end of the Mg-Ti phase diagram was investigated. The liquidus, solidus, and solvus boundaries to 1 pct Ti were established. All alloys were prepared by saturating molten magnesium with titanium in a consumable titanium crucible under inert gas maintained at 230 psig. The liquidus of the Mg- Ti system was determined by analysis of dip samples taken from 700° to 1300°C under equilibrium conditions in a pressurized inert atmosphere furnace and by analysis of small ingots rapidly poured and quenched from 1400° to 1500°C. The solubility of titanium in magnesium ranged from 0.018 wt pet Ti at 700°C (0.012 wt pet at 650°C by extrapolation) to 1.035 wt pet Ti at 1500°C. The solidus for compositions ranging from 0.03 to 1.00 wt pet Ti was determined to be 650° ± 1°C by thermal analysis. The titanium solid solubility values ranged from 0.08 wt pet at 350°C to 0.19 wt pet by extrapolation to 650°C. The freezing reaction is peritectic. No intermetallic compounds were found in the system; the phase in equilibrium with molten magnesium saturated with titanium was found to be titanium with magnesium in solid solution. Solid titanium will dissolve at least 1.32 wt pct Mg. PREVIOUS investigations of the Mg-Ti system have shown considerable disagreement on the solubility of titanium in liquid magnesium. Furthermore, the solid solubility of titanium in magnesium has not been well established. Liquidus curves for previous work and for the present investigation are shown in Fig. 1. Aust and Pidgeon1 used a dip-sampling method on molten magnesium held in equilibrium with solid titanium under a protective atmosphere to determine the solubility and found that it ranged from 0.0025 wt pet Ti at 651°C to 0.015 wt pet Ti at 850°C. Eisenreich2 introduced titanium into molten magnesium by means of TiCL4 adsorbed on BaCl2. Ingots were then cast at various temperatures. Making the assumption that only the titanium dissolved in magnesium at the time of casting was soluble in H2SO4, Eisenreich determined the solubility of titanium in molten magnesium to range from 0.003 wt pet at 655°C to 0.115 wt pet at 800°C. Eisenreich also determined the solid solubility of titanium in magnesium to be 0.015 wt pet at room temperature and 0.045 wt pet at 500°C. Since the solid solubility just below the freezing temperature for the bulk of the alloy was much larger than the liquid solubility just above the freezing temperature, Eisenreich concluded that the freezing reaction was peritectic. Obinata et al.3 equilibrated molten magnesium with titanium in hermetically sealed titanium containers which were then furnace-cooled. The titanium content of the magnesium was then determined and found to range from 0.170 wt pet at 700°C to 0.85 wt pet at 1200°C. No intermetallic compound was found in the system. The Armour Research Foundation4 determined two points on the solvus by electrical resistivity methods: 0.00057 wt pet at 200°C and 0.0008 wt pet at 300°C. At higher temperatures, data were meaningless with no trends observable. The authors of this report believed that the lack of significant data at the higher temperatures was due to variations in specimen geometry, although there was no positive evidence to verify this supposition. The present investigation was undertaken to clarify the uncertainty in both the liquidus and solvus of the magnesium-rich end of the Mg-Ti system. EQUIPMENT AND MATERIALS The equipment used in this investigation, with some modifications, was essentially that used by Crosby and Fowler5 in their determination of part of the Mg-Zr phase diagram. The equipment, as modified for this work, is shown in Fig. 2. It consists of a sealed furnace chamber which can be pressurized with inert gas so that melts can be made above the boiling point of magnesium at atmospheric pressure. Melts are made by induction heating in a titanium crucible which, after diffusion of sufficient magnesium into the walls of the crucible to saturate the titanium at the sampling temperature, comprises the solid phase in equilibrium with the molten magnesium. Dip samples may be taken with the sampling tube, or the entire furnace may be tilted so that ingots may be poured into a mold in the side chamber. The principal difference from the earlier apparatus is in the thermocouple, which in the present equipment is enclosed in a protection tube and immersed directly in the melt. The tips of both the thermocouple protection tube and the sampling tube, which dip into the melt, are made of high-purity titanium. The 4 1/2-in.-long titanium tip of the sampling tube is threaded into a steel tube, O in Fig. 2, which extends through the top of the furnace. To determine whether the temperature at the tip of

Jan 1, 1969

By W. M. Baldwin, C. R. Johns

Cobalt is reported1,2 to scale in accordance with the Pilling and Bed-worth3 parabolic law: where w = weight increase per unit surface area K = constant l = time The reported values of the parabolic oxidation constant, K, in the temperature range 600 to 1100°C follow an Arrhenius type of equation as inspection of Fig 1 shows. According to Valensi's theory5 on the scaling of metals where multiple-layered scales (for example, MeX, MeX2, and others) are possible, this fact could be construed as indicating that a single oxide only is formed on cobalt in this temperature range. Since the single straight line extends above 920°C where only CoO is stable in air (see Fig 2) it might be inferred that this is the only oxide formed on scaling. Arkharov and Voroshilova10 have studied the scales formed when cobalt is heated in air in the temperature range 385 to 800°C and report that CoO is indeed found in the scale but that CoO4 is also found as an overlay and in increasing amounts in the lower temperature ranges. No quantitative data regarding the relative proportions of the two oxides were reported. Again in the light of Valensi's theory this would indicate that the straight line in Fig 1 would be expected to undergo an inflection at some point in the temperature range 385 to 800°C. Chauvenet2 has studied the oxidation rates of CoO to Co3O4 and has found this reaction to proceed parabolically with time but reports parabolic scaling rates which are considerably (about ten times) larger than the scaling rates of cobalt metal itself. This is difficult to explain in terms of Valensi's theory although a full discussion of the possible discrepancy cannot be made in view of the lack of sufficient data. These points made an investigation of the scaling behavior of cobalt in air an attractive study. Discussion of Results Relatively large (approximately 95 sq cm of surface area) samples of 0.020 in. thick electrolytic cobalt strip,* sanded with 2/0 paper, were heated in air in a cyclone type furnace. The samples were weighed before and after the scaling treatment. The weight increases so observed obeyed the Pilling and Bedworth parabolic law at all temperatures studied. The parabolic scaling constants when plotted on a logarithmic scale as a function of absolute temperature are reproduced

Jan 1, 1950

Discussion of the paper of CHARLES H. MACDOWELL, presented at the New York meeting, February, 1915, and printed in Bulletin No. 98, February, 1915, pp. 103 to 114. GEORGE S. RICE, Pittsburgh, Pa.-I am especially interested in the mining side of this important question. In 1911, when in Europe investigating mining matters, giving special attention to subsidence clue to mining, for there is a very big problem of that kind, as many of you know, in the Pennsylvania anthracite region, I visited Stassfurt, which is one of the chief centers of potash mining, and which was pointed out as the place to see surface subsidence. We found the town much askewsome of the streets having sunk from 15 to 30 ft., leaving many ancient buildings pitching at various angles. One old church, 500 or 600 years old, has been sunk about 20 ft., cracking it badly. I understand that this condition came about because in early mining clays they were careless about leaving proper supports and used no filling or packing. The Stassfurt mines work along a buried anticline the sides of which pitch at 45° on the average. Through this careless mining they had a break of the hanging wall which let in water from the overlying marls and sands. The water rapidly dissolved the salts in the pillars, and spreading through the entire chain of mines, caused their complete loss, with serious trouble for the old city. They had to start new mines some distance away, and take care to prevent roof caves. The packing system is of interest. They were driving large rooms into the rock-salt foot wall and using the rock salt as dry filling. The application of hydraulic filling, using a saturated solution, was under contemplation at some plant nearby. Whether 6r not the plan was carried out I do not know. I was reminded of the plan by Mr. MacDowell's remarking on the use of a saturated salt solution in the core drilling. His reference to the apparent breakdown of the potash syndicate raises an interesting question. We have had the German system of syndicates pointed out as perhaps one means of solving our troubles in the soft-coal mining industry due to overproduction. It seems to have worked out admirably in the case of the Westphalian coal-mining syndicate and also in the syndicate of Upper Silesia; but apparently the syndicate plan did not work in the potash industry. .

Jan 5, 1915

By R. P. Olsen, A. K. Schellinger

Molten silicate salts, the important industrial byproducts termed "slags," are known to be electrolytic conductors at furnace temperatures. This property is due to their partial dissociation into ions with the ion kind and size being closely related to the slag composition. Ionic conductance, in liquids, is a function of the viscosity, which in turn is a function of the temperature. It could be anticipated, therefore, that a semi-log plot of conductivity vs. reciprocal absolute temperature might yield a straight line, in the case of molten silicates and salts. As liquids, the viscosity of these slags should follow the Shepard1 relationship: log viscosity = A/T + B Then, if the resistance of the molten slag is directly proportional to the viscosity: log Rs = A/T + B Resistance measurements of molten halide salts,2 and silicate salts34 by various investigators have, indeed, shown this straight line relationship between resistance and temperature. A further relationship between the conductivity versus the degree of ioni-zation, the size of the ions, and the slag composition is, also, to be expected. Large ions, and fewer ions, would move more slowly in a potential field and could not carry as much current as smaller, more numerous, and mobile, ions. Conductivity, therefore, would be smaller in the presence of such large ions and higher slag viscosities. The conductivity-composition relationship is of considerable interest in the case of the industrial slags produced in iron blast furnaces, and non-ferrous smelting furnaces. These slags usually approximate three component systems with several minor components as impurities. At least one of the major components is commonly purchased for the sole purpose of rendering the slag less viscous at a reasonable furnace temperature. Should the conductivity be related rather directly to the concentration of such a purchased slag component (that is, CaO) instrumental measurement and control at the furnace might be possible. Modern tele-metric control methods in aqueous chemical process industries are often based on the property of conductivity of solutions, and its variation with composition. Investigators3 of the phenomenon of electrical conductivity in molten blast furnace slags have established that these systems show lines of equal conductivity on their ternary diagrams at one temperature level. These isocon-ductivity lines form closed contours on the diagrams, and at times, minimum areas occur at which these contours are essentially closed down to a point. The conductivity reading at such a point, at one temperature , would, of course, locate one on the diagram, and give the slag composition. Research in this field is understandably scanty. The reactive nature of

Jan 1, 1950

GEORGE F. COMSTOCK (author's reply to discussion*).-Mr. Thum's description of the effects of butt welding and spot welding on the micro-structure of steel are interesting and timely. The speed with which the changes noted by Mr. Thum must take place is indeed remarkable, but the writer has noted a similar very rapid diffusion of carbide in annealing a t a rather high temperature certain samples of soft sheet steel containing massive cementite segregated on a small scale. The massive cementite in such steel can be dissolved and distributed very quickly if the proper temperature is attained. Mr. Thum's explanation of the structure he found in the spot welds seems entirely reasonable, but the mystery of the decarburized material in the butt weld is one that might well be the subject of further research. The possibility of decarburization by air ,might perhaps be worthy of a little more consideration than he gives it, for the oxides formed would be gaseous on account of the presence of carbon, and hence not visible in the microscope, and the effect of the pressure might be to squeeze the carbon oxides, which would normally form blow-holes, out of the metal or possibly into such small volumes as not to be noticed The removal of carbon by liquation and squeezing into the fin would be an effect similar to the "bleeding" of a steel ingot that is rolled while the center is still liquid, giving a soft low-carbon interior in the finished section while the segregate was removed in cropping the pipe. This effect in Mr. Thum's butt welds could, however, only be obtained if the weld was heated to near the melting point of the steel, and if the carbon was considerably segregated in the bars at the start, for the first effect of the high temperature would be to promote diffusion rather than the contrary segregation and Equation. It is gratifying to learn from Dr. Ruder's remarks that his researches have resulted in no disagreement with the few points brought out by the writer's experiments. In addition to the three forms in which nitrogen may occur in iron that he mentions, it would seem that a fourth form is often found; This is apparently a eutectoid, like pearlite, and sometimes almost as coarse as the massive cementite seen in soft steel sheets that have been annealed for a long time. One of the things needed in the metallographic study of steel is an etching reagent that will distinguish definitely between nitride in this form and the more common pearlite or cementite.

Jan 6, 1919

By Edward H. Robie

SEPTEMBER usually being a fine month for motoring, we set out with our better half at the end of August in our Studebaker for points West. A combined business trip and vacation. The first night found us 392 miles away, at the Statler Hotel in Buffalo, and the next morning we revisited Niagara Falls for the first time in some forty years. The cataracts were as impressive as ever and certainly worth a day of any vacationist's time, instead of the half hour we could spare before going on to Chicago. The Centennial of Engineering, the hundredth anniversary of the founding of the ASCE, no doubt attracted the greatest gathering of engineers in history but still the attendance was disappointing to most of the forty or fifty societies that participated. Perhaps the time-the two weeks following Labor Day-was unfavorable. Few could afford to spend ten days away from home and business at that time of the year. Fall meetings of the AIME normally attract far more than the 300 that registered in Chicago. The technical program, however, was excellent, especially that arranged by the Minerals Beneficiation and Industrial Minerals Divs. The mineral industry papers of a more general nature that were presented as a part of the Centennial program on Monday and Tuesday of the following week were of high quality and offered by top names but had a meager audience. Undoubtedly the celebration brought engineers and engineering to the attention of millions of people. The pageant at the Museum of Science and Industry proved continuously interesting, showing the progress of engineering following the first use of fire. The show continued for many weeks. A special stamp was issued by the Government, which engineers might well use on their Christmas cards or other mail this year. After six days in Chicago we set out north, first visiting Fairbanks Morse in Beloit and Allis-Chalmers in Milwaukee. Will Mitchell's Basic Industries Research Laboratory is doing interesting work and being installed in more comfortable quarters. The next day at Ishpeming, C. W. Allen arranged for luncheon with a local group of AIME members and we then looked over the new surface plant of the Mather B mine, a model of modern functional design. Then on to a small dinner meeting at Calumet following cocktails at Endicott Lovell's attractive summer home on the lake at Point Mills. The new Memorial Union Bldg. at Houghton, where we were domiciled for the night through the courtesy of Roy Drier, is a beautiful modern addition to the college, a model of its kind.

Jan 1, 1952

By W. L. Phillips

Stress-strain data are reported for sodium chloride, lithium fluoride, and magnesium oxide tested in compression at diffevent strain rates in the telrlperature range from 70° to 873°K. Quantitative equations are given for the stvain-rate dependence of the critical resolved shear stress and the initial rate of work havdening. The properties so determined are compared with results previously reported for metals. ALTHOUGH the effects of strain rate and temperature on the stress-strain characteristics of metals have been extensively investigated1,2 these effects have not been studied in detail in ionic crystals. In the only previous investigations on the effect of strain rate on the deformation of ionic crystals. Gilman and gohnston3 and Hulse and pask4 have shown that the yield stress of lithium fluoride and magnesium oxide at room temperature is proportional to the ninth or tenth root of the strain rate. CRYSTAL PREPARATION Lithium fluoride, sodium chloride. and magnesium oxide single crystals were purchased from the Har-shaw Chemical Co. The compression fixture and sample preparation have been described in detail previously.5 The detectable impurities in MgO were eight parts in 105 of Fe and six parts in 105 of Si; in LiF, six parts in 105 of Mg; and in NaC1, two parts in 105 of Fe and four parts in 10&apos; of Mg. The cleaved samples measured - 0.1 in. by 0.1 in. by 0.3 in. Prior to testing all samples were annealed at -0.8 of their melting point and cooled to room tempera- ture at 50 C per hr.&apos; Samples were strained at rates (<) of 0.1, 0.01, 0.002, and 0.0002 in. per in. per min. EXPERIMENTAL RESULTS Fig. 1 is a plot of the critical resolved shear stress a,. (extrapolation of slope of easy glide region to zero strain) of sodium chloride, lithium fluoride, and magnesium oxide tested at different strain rates as a function of temperature. In all crystals at all strain rates a, decreases with increasing temperature according to an equation of the type397 where uo is a stress constant, K is a constant, and T is the absolute temperature. The points in Fig. 1 are the average of six tests. It is evident that there is a break in the log 0,- temperature plots at a characteristic temperature T,. The constant K of Eq. [I] is dependent on strain rate, Fig. 2. The relationship

Jan 1, 1962