By M. J. Sinnot, J. C. Shyne

Low-frequency mechanical damping measurements were made to investigate internal friction in Fe-A1 alloys. The atomic ordering of the Fe-A1 system strongly influenced the stress-induced ordering internal friction. Magnetoelastic damping was also encounteyed and was shown to be reduced by the application of a static stress. THIS paper describes some damping experiments made on alloys of Fe and Al. Stress-induced ordering internal friction was measured with samples containing from 9.8 to 31.3 at. pct Al. Aluminum is soluble in a-Fe to about 50 at. pct and forms at least two long-range ordered structures, Fe3Al and Feu.' Stress-induced ordering internal friction is known to occur in many substitutional solid solutions, but few measurements of this damping effect have been made with alloy systems that have pronounced ordering tendencies. LeClair and Lomer developed expressions relating the relaxation strength of the damping process to the degree of atomic ordering and predicted that stress-induced ordering internal friction would be zero with complete ordering.' This concept was confirmed experimentally by Lulay and Wert using the system cd-Mg It is also consistent with the weak stress-induced ordering peaks observed in P -brass by Artman and in 16 wt pct Al Fe-Al by bert.' It was expected, therefore that the ordering characteristics of the system Fe-Al would strongly influence the stress-induced ordering internal friction exhibited by the experimental alloys. SAMPLE PREPARATION The alloys used in this investigation were induction melted under vacuum using high-purity melting stock. The iron was electrolytically refined Plastiron 101 which contained 99.85 wt pct Fe. The aluminum was a special 99.95 pct pure grade supplied by Alcoa. The only other raw material was spectrographically pure graphite which was used in small quantities as a deoxidant. The amount of carbon used was slightly in excess of the amount required to completely deoxidize the melt; this resulted in residual carbon contents of 0.01 to 0.02 pct in the finished alloys. The vacuum cast 2 1/2-in. diam ingots were hot rolled to 5/8-in. diam round bars. Portions of these bars were hot swaged and hot drawn to 0.050-in. diam wire. Straight pieces of the hot drawn wire were slowly heated to a temperature of 1300°C in a He atmosphere. After holding for 4 hr, the samples were allowed to cool in the furnace. This annealing treatment resulted in grain growth in the samples, the final grain size being about the same as the wire diameter. The grain boundaries were oriented perpendicularly to the wire axis, giving a bamboo grain structure. The existence of a preferred orientation could not be detected in these coarse grained samples. If the samples had a fiber structure, this probably would have been the same in all samples because of similar processing, thus the influence of crystal orientation on the relaxation strength would have been similar in all samples. The aluminum contents of the alloys are listed in Table I. EQUIPMENT The principle of the torsion pendulum was used for the internal friction measuring device. The

Jan 1, 1961

By C. S. Matthews, H. M. Girner, C. D. Williams, M. J. Edwardson, H. R. Parkison

Quantitative interpretation of electric logs requires knowledge of formation temperature. In this paper, methods are developed for computing changes in formation temperature caused by circulation of mud during drilling operations. The basis of the method is the mathematical solution of the differential equation of heat conduction. The solution of this equation is presented in a series of graphs. These graphs are used to determine formation temperature disturbance at various radii for arbitrary mud circulation histories. Example comparisons with field results show reasonable agreement. It is concluded that, in general, the temperature disturbances caused by circulating mud are small beyond 10 ft from the wellbore but are quite significant near the wellbore. INTRODUCTION Quantitative interpretation of electric logs requires knowledge of the formation temperature in order to establish the resistivity of the formation water with accuracy. To determine the formation temperature, the temperature disturbances produced by circulating drilling mud must be evaluated. -The objective of this investigation was to develop a method for the numerical determination of these temperature disturbances at any distance from the wellbore as a function of time. The first step was to solve the differential equation describing the temperature behavior in the formation during and after mud circulation. This solution was used to calculate a series of curves relating temperature disturbance to shut-in time for various circulating periods. An "exact" method for computing formation temperatures with the use of these temperature-disturbance plots is described, and the results of an application of this method to a well in Montana are presented. Procedures for approximating formation temperatures are also discussed. BASIC EQUATIONS AND ASSUMPTIONS With the assumptions that (1) cylindrical symmetry exists, with the borehole as the axis, (2) heat flow is 1. The formation can be treated as though it is radially infinite and homogeneous in extent, as regards heat flow. 2. The presence of mud cake can be disregarded. 3. The effect of heat generated by bit action is negligible. 4. After mud circulation ceases, the rate of radial heat flow at the wellbore is negligible and is assumed zero for purposes of calculating temperature change with time. These assumptions are believed to be reasonable because of the agreement achieved between calculated and measured borehole temperature in a well, to be discussed later. Further, the agreement at the wellbore indicates that temperatures in the formation were also approximately correct. since it is the formation temperatures that determine wellbore temperature after ceasing circulations SOLUTION OF THE DIFFERENTIAL EQUATION AND ITS APPLICATION The solution of Eq. 2 for the temperature behavior during and after a single period of mud circulation is

By G. G. Sarkar

SHARPNESS of separation and washing efficiency are often confused. The sharpness index indicates the precision of a washing unit; the washing efficiency takes into account not only the unit's precision but also the washability characteristics of raw coal and the near-gravity materials at the effective density of cut. A sound basis for evaluating the sharpness index is essential in comparing the sharpness of separation attained by different cleaning units. Sharpness Index and Related Criteria: Washing plant sharpness of separation has been well represented by Hancock's efficiency chart and Tromp's curve of migrated materials. Some useful coefficients derived from Tromp's curve—the error area, probable error, and imperfection value—have been widely used to measure sharpness of separation. These are defined in a number of papers presented at the first and second International Coal Preparation Colsference held in Paris (1950) and Essen (1954).1-5 In evaluating the performance of a dense medium separator at four different gravities, Yan-cey and Greer6 bserved that even with similar operating conditions and the same size grading of feed, the imperfection value of a washing plant varies through a greater range than the probable error. The present writer also observed the same type of anomalies in comparing the imperfection values of one plant which were determined under almost identical conditions. He therefore devised a graphical method to evaluate a washing unit's sharpness of separation and define it by a single coefficient, which is substantially independent of coal characteristics under normal operation of the unit. Unlike imperfection value, the new coefficient can be expressed on a percentage basis. Coal preparation engineers generally agree that the amount of misplaced material resulting from any separation in a washing plant is almost directly related to the amount of +0.10 sp gr (near-gravity) materials. In actual practice, however, misplacement is not restricted to the 20.10 sp gr range. It will be evident from a study of Tromp curves that this misplacement often extends over unequal specific gravity ranges on the two sides of the actual density of separation. The same condition exists for near-gravity ash distribution and the resultant misplacement of ash units during any separation. But so far as the same unit is concerned, the total misplacements bear a definite ratio to the amount of near-gravity zone materials that is affected by misplacements. This ratio should be constant not only for various densities of separation but also for different qualities of feed coal treated in the same plant. This ratio, multiplied by 100, directly represents the inefficiency of the plant. When the plant inefficiency value is subtracted from 100, the re- ' sult is designated as sharpness index. Evaluating the Sharpness Index: The method of evaluating the sharpness index is explained here with reference to Fig. 1. Fig. 1 is a reproduction of the familiar diagram used by Cerchar of France to represent the inefficiency of a separation in terms of "triangle of errors," which is a measure of organic loss. It will be observed that the characteristic (yield/fractional ash) curve of the raw coal represented by GHAPR

Jan 1, 1958

By Kenneth C. Vincent, A. M. Gaudin

In a study1 of the action of amyl xan-thate on chalcocite in water suspension, it was found that if the xanthate is added in relatively large quantity the xanthate group can be accounted for in three forms: (1) as xanthate ion remaining in water, (2) as benzene-soluble cuprous xanthate on the chalcocite, (3) as a benzene-insoluble coating on the chalcocite. Reduction in the amount of xanthate added leads to disappearance of form I then of form 2. With minute quantities of added xanthate, substantially all the reagent is of the "unleachable" kind. Yet this unleach-able xanthate can be dissolved by pyridine to form a soluble cuprous xanthate complex, and it is sufficient in effectiveness to make chalcocite flotable even if insufficient in quantity to form a complete mono-molecular film on the mineral. In that study it was also found that chalcocite abstracts cuprous xanthate from benzene so1ution, in what may (or may not) be a case of molecular adsorption. It seemed desirable, therefore, to study further the "unleachable" xanthate on the chalcocite, and particularly to ascertain whether it is formed as a result of the benzene leach or is actually formed during the conditioning of chalcocite in aqueous xanthate solution. A 'splendid tool to make such studies has recently been perfected; that is, the use of radioactive spies or tracer atoms. With this tool, it was thought possible to answer the problem stated above, but, unfortunately, this did not prove to be true. Answer to the flotation question was clouded by the existence of rapid and selective diffusion of copper atoms in the solid mineral—a phenomenon that was totally unexpected yet remains interesting and perhaps important. Method of Radioactive Spies The method of radioactive spies is discussed in many places. Two convenient references are the article by Evans2 and the book by pollard and Davidson.3 The method was first developed by van Hevesy and paneth in 1013, when only natural radioactive isotopes were available. These isotopes are few in number, and so the method remained limited in scope. Recently the synthesis of over 350 active isotopes of all the known stable chemical elements4 has opened widely expanded possibilities for the method, A fundamental tenet of the method is that a radioactive atom and a nonradio-active atom are exactly alike until disintegration of the radioactive atom. Then, by its sudden death, the spy reveals its location. The relative abundance of spies at various locations makes it possible to ascertain the relative abundance of the corresponding nonradioactive atoms at the same times and locations. A second fundamental tenet of the method of radioactive tracers is that the radioactivity lies in the nucleus of the atom: transfer of radioactivity from one

Jan 1, 1947

By P. CHARTERIS A.

THE following scanty notes on the Roumanian oil-region may serve as an introduction to more detailed future study and description. The Roumauian oil-belt, follows the outer edge of the sweep of the Carpathian Mountains, and may, in a broad sense, be regarded as a prolongation of the Galician belt. It is distributed over a tract of country from 300 to 400 miles in length, with a width of from 15 to 20 miles, and is believed to cover an area of at least 20,000 hectares (59,420 acres). The Government claims that 16,000 to 17,000 hectares of its land is petroliferous. The primary deposits of petroleum are considered to be in the Padeogene (Oligocene) and the Neogene (the salines of the Miocene) formations. Most of the other repositories, especially those of Muntenie, are only secondary, the petroleum there having been introduced by the orogeneric movements which raised the Carpathian Mountains. The oil-field has been divided by the Roumanian survey into two regions, the Flysch and the Sub-Carpathian, as is shown in the accompanying sketch-map, Fig. 1.(p. 518). So far as is yet, known, practically all the seepages and .productive pits and wells are situated oil anticlinals. Those which outcrop in the Flysch region. (called Paleogene anticlinals), as indicated in the sketch-map, Fig. 1, are : Solontz, Middle Oligocene; Moineshti, Moineshti and Tagu-Ocna-beds of the Eocene.

Jul 1, 1906

By W. R. Hibbard, Ming-Kao Yen

Various rationalizations of preferred orientations in cold worked polycrystalline metals have been based on the operation of at least two three2 five, an indefinite number, and all,6 slip systems of the type occurring in single crystals. Pickus and Mathewson3 suggested that the cold rolling texture in face-centered cubic metals could be rationalized on the basis of two or more operating slip directions symmetrically disposed about the direction of flow in such a manner that the resolved shear stress factor is equal for all operating slip systems and lattice rotations cancel each other. The importance of the direction of flow, the necessity for the operation of slip systems capable of producing the required changes in external dimensions, the maintenance of a common surface between adjacent grains and a symmetrical arrangement of the operating slip systems in order to produce an end orientation which is stable under additional deformation lead to the following rationalization of textures based on the type of slip systems operative in single crystals. The rationalization is intended to explain why certain orientations are suitable for deformational flow without a change in orientation and thus are stable end orientations or ideal texture orientations. It does not attempt to explain how the grains of a randomly oriented polycrystalline aggregate will reach this orientation. The rationalization is based on the following four postulates: 1. The ideal textures for polycrystalline aggregates are the result of reorientations of individual crystals toward the same stable end orientation at which no further reorientation will occur even during additional deformation. Since, in simple slip, the relative orientations of the stress axis and the active slip system determine the change in orientation during slip, it is considered that the orientation of the stress axis with respect to the ideal texture determines what slip systems must be active to retain the stable end orientation. Therefore the stable end orientation should be a symmetrical one around the stress axis with respect to the active slip systems such that lattice rotations resulting from slip will cancel each other and prevent a resultant change in orientation. (Rotational symmetry only—not translation, inversion, nor others—is considered here.) Thus a metal under a pure stress should develop a texture consisting of one or more of the crystallographically symmetrical directions, <100>, <110> or <111> for cubic metals or <0001>, <1010> or <1120> for hexagonal close-packed metals, parallel to the stress axis. 2. Since the active slip direction is the direction of glide during simple slip and thus the direction of maximum shear movement, in the ideal texture the active slip

Jan 1, 1949

By H. G. Schneider

The Smackover oil and gas field lies in Ouachita and Union Counties, Ark., in the south-central part of the state, in T.15 and 16S., R.15, 16, and 17W. It is 10 miles north of El Dorado, the principal business and railroad center in the south-central part of the state, and extends from the town of Smackover in all directions. Productive territory having an aggregate area of nearly 55 sq. mi. has been developed. It extends 6 miles from north to south and 12 miles from east to west. The field may be divided into two parts: the east district, which includes the area east of the town of Smackover, and the west district, which includes the area west of the town of Smackover. In relation to the neighboring productive fields of Arkansas, the Smackover field is 9 miles north of the El Dorado oil and gas field, 8 miles slightly west of north of the East El Dorado oil and gas field, and 16 miles east of the Stephens oil field. Smackover was discovered in May, 1922, when the Oil Operators Tnist drilled well No. 1 on the J. T. Murphy farm, in the southeast quarter of sec. 8, T.16S., R.15W. This well is located almost on the top of the Norphlet dome and was drilled to the Nacatoch sand. It had an initial open flow volume of 30,000,000 cu. ft. of dry gas per day, and a rock pressure of 950 lb. per sq. in. In July, 1922, the V. K. F. Co. completed the first oil well in sec. 29, T.l5S., R.l5W., on the north side of the Norphlet dome, and 3 miles north of the first gas well. This well started the active development of the north and northwest sides of the dome.] The field was extended westwards, when oil was discovered in the Nacatoch sand, during October, 1922, in sec. 4, T.l6S., R.l6W., 51/2 miles west of the original gas well. This opened up the so-called "light oil district," which is located on a structural terrace, for which the name

Jan 1, 1924

By Ray Light, Everett M. White

Numerous articles have been written about the coal miner ; he has been compared with brave men who have gone out to conquer some unknown hazard throughout the ages. Now, however, modern mining is no longer something to be avoided, but a vocation that anyone can be proud of, with remuneration equal to or above that of almost any industry. A concerted effort is being made each day by both the operators of most mines as well as the state and federal inspectors to see that coal mines are as safe or safer than work places in any other industry. However, it is true that mine fires and explosions have occurred in the mining industry since its inception. One of the earliest accurate references to such an occurrence is found in the transactions of the Royal Society of London. In the Colliery Managers&apos; Handbook, 1898, Caleb Pamely writes of an explosion that occurred at Fatfield, England in August 1708, resulting in the deaths of 69 persons. He states: "Three of them, viz, two men and a woman, were blown quite up from the bottom of the shaft, fifty-seven fathoms deep, into the air, to a considerable distance from the mouth of the pit." It is interesting to note that women were employed as miners in England during that period. In the United States, the first record of coal mined was in 1702 by the Jamestown colonists. In 1786, about 20 years after Pittsburgh, PA was first settled, a charter was granted by William Penn to mine coal on the banks of the Monongahela River. Then in 1803, the first important coal company, the Lehigh Coal Co., was established. From this beginning, the mining industry continued to grow in importance and the first state mining law was formulated in 1870. The Pennsylvania state mining law was followed in 1873 by Ohio&apos;s, and in 1876 by Maryland&apos;s. A mine explosion at Avondale, PA in 1869 stimulated state legislatures to formulate these early laws. In 1907 near the town of Fairmont, WV, there were, within three days, two explosions resulting in a total of 597

Jan 1, 1981

By Ming-Kao Yen, W. R. Hibbard

Various rationalizations of preferred orientations in cold worked polycrystalline metals have been based on the operation of at least two three2 five, an indefinite number, and all,6 slip systems of the type occurring in single crystals. Pickus and Mathewson3 suggested that the cold rolling texture in face-centered cubic metals could be rationalized on the basis of two or more operating slip directions symmetrically disposed about the direction of flow in such a manner that the resolved shear stress factor is equal for all operating slip systems and lattice rotations cancel each other. The importance of the direction of flow, the necessity for the operation of slip systems capable of producing the required changes in external dimensions, the maintenance of a common surface between adjacent grains and a symmetrical arrangement of the operating slip systems in order to produce an end orientation which is stable under additional deformation lead to the following rationalization of textures based on the type of slip systems operative in single crystals. The rationalization is intended to explain why certain orientations are suitable for deformational flow without a change in orientation and thus are stable end orientations or ideal texture orientations. It does not attempt to explain how the grains of a randomly oriented polycrystalline aggregate will reach this orientation. The rationalization is based on the following four postulates: 1. The ideal textures for polycrystalline aggregates are the result of reorientations of individual crystals toward the same stable end orientation at which no further reorientation will occur even during additional deformation. Since, in simple slip, the relative orientations of the stress axis and the active slip system determine the change in orientation during slip, it is considered that the orientation of the stress axis with respect to the ideal texture determines what slip systems must be active to retain the stable end orientation. Therefore the stable end orientation should be a symmetrical one around the stress axis with respect to the active slip systems such that lattice rotations resulting from slip will cancel each other and prevent a resultant change in orientation. (Rotational symmetry only—not translation, inversion, nor others—is considered here.) Thus a metal under a pure stress should develop a texture consisting of one or more of the crystallographically symmetrical directions, <100>, <110> or <111> for cubic metals or <0001>, <1010> or <1120> for hexagonal close-packed metals, parallel to the stress axis. 2. Since the active slip direction is the direction of glide during simple slip and thus the direction of maximum shear movement, in the ideal texture the active slip

Jan 1, 1949

By H. R. Peiffer

Composite alloys of silver and alumina are shown to resist flow above the melting point of the continuous matrix. The ability to resist flow depends on the fineness of the dispersion and the oxygen content of the silver. It is believed that the oxygen influences very strongly the bond between the molten silver and the finely divided alumina. RECENT needs for materials with high strength and creep resistance at high temperatures initiated mechanical property studies on dispersed phase materials to near the melting point of the continuous matrix material. Results&apos; of these investigations have shown that certain of these materials do have promise for high-temperature applications. Experiments performed on composite materials of silver and alumina by the author have resulted in the discovery of an interesting effect above the melting point of the silver. In these materials the silver was continuous and the alumina very finely divided (Linde B). It was observed that these materials exhibited strength and resistance to flow above the melting point of the silver matrix. The purpose of this paper will be to describe these properties. METHOD OF PREPARATION The materials were prepared by mixing the proper amount of Linde B alumina and high-purity silver oxide. The alumina content was varied from 5 to 20 wt pct alumina in silver in 5 pct steps. The materials were mixed by blending the constituents in an ordinary food blendor using ethyl alcohol as a vehicle. Enough alcohol was added to the powders to form a mixture with the consistency of a thin mud. After blending for about | hr the material was dried and the silver oxide reduced by heating to 450 OC. The material was then pressed at 25 tsi into a -in. billets 3 in. long. EXPERIMENTAL PROCEDURE The specimens were horizontally supported at either end by knife edge supports of cold-rolled steel. This holder was then placed in a "globar" furnace and a chromel-alumel thermocouple placed very close to the specimen recorded its temperature to within 10°C. Each specimen was heated rapidly to 900°C initially. The specimens were held at temperature approximately 30 min and then the temperature was raised 50 deg. The procedure was repeated until deformation was noted. Photographs were made of the specimens at various temperatures and increments of time using a Polaroid Land camera. RESULTS Fig. 1 shows the 5 pct by weight "Linde B" alumina and silver material after reaching 980 °C. Failure occurred after 15 min at this temperature. There were two points of failure and silver collected at them. No additional flow of the molten silver was noted at any other place. Fig. 2 shows a 20 pct by weight "Linde B" alumina in silver specimen. After 30 min at 1400°C, bowing of this material was observed. Other concentrations of alumina were added to

Jan 1, 1961

By H. W. Hitzrot, R. H. Limons, L. V. Fegan

The testing of a new method for measuring pellet-bed temperatures in the traveling-grate or shaft furnace is presented in this paper. This method, using silver-palladium alloy wires as indicators, overcomes disadvantages existing in the methods based on the use of thermocouples which are costly and time-consuming. The authors have developed and tested a new method for measuring pellet-bed temperatures in the traveling-grate or shaft turnace through the use of silver-palladium alloy wires as indicators. This method overcomes the disadvantages of existing methods, which, based on the use of thermocouples, are generally costly and time-consuming. For example, in the case of the traveling-grate furnace, the installation of an instrumented pellet, together with its attached thermocouples, requires stopping the furnace, with resulting loss of production time. As for temperature measurement in the shaft furnace by the existing method, the movement of the shuttle-car feeder seriously interferes with both the actual insertion and the resulting distribution of continuously fed thermocouples. The authors have overcome these difficulties by using, as temperature indicators, a range of silver-palladium alloy wires that can be easily recovered, after firing at any desired location in a pellet furnace. Silver-palladium wires having specific melting points from 2000°F to 2500°F are enclosed in ceramic capsules. Each capsule is placed in a ni-chrome wire basket filled with a sample of green pellets, the baskets being the means for recovering the capsule after firing. After the encapsulated wires have been exposed to the firing cycle, the alloy wires are examined to determine the maximum temperatures attained by the pellet sample. This method gives accurate, rapid determinations of maximum temperatures attained during pellet induration in either the traveling-grate or shaft furnace The new method has the following advantages over existing methods: 1) it is less expensive; 2) no furnace downtime is required; 3) the testing units can, be made in quantity in advance; 4) measurements can be made in rapid succession at all desired locations; 5) measurements of maximum firing temperatures are more accurate; 6) on the basis of points 4 and 5, the new method gives a more reliable picture of the correlation of pellet quality, petrographic textures and maximum temperatures, thus providing a more effective quality-control tool. A disadvantage of the method is, of course, that the measurements are not continuous and only maximum temperatures are determined. TEST PROGRAM Preparation of Materials: CALIBRATION OF ALLOYS - In the following discussion the term "bead point" (see Fig. 1) refers to the temperature at which each alloy begins to melt and form a bead. Fig. 2 gives the bead point curve for silver-palladium alloys. Before the alloys are used in plant tests, the bead point of each alloy should be determined in the laboratory to verify the alloy compositions. Once a given alloy has been calibrated, it can be

Jan 1, 1965

By AIME AIME

Award of a Gold Medal : to the Institute. The Jury of Awards of the Jamestown Ter-Centennial Exposition has conferred a gold medal, the highest distinction within its power,. on the American Institute of Mining Engineers for the excellence of its publications during the past decade. ; A half-tone photographic reproduction of both sides of the medal is given in the accompanying illustration.

Jan 7, 1908

By R. H. Brown, F. Keller

Because of the extensive use of Alclad 24s alloy sheet in aircraft construction, there is much interest in the metallurgical changes caused by heat-treatment of this product.1, 2 One of these changes is the result of the diffusion of soluble elements from the core into the coating during treatment. This paper deals with the thermal treatments that may influence diffusion and with the practical effects of diffusion on the serviceability of the product. As is well known, Alclad 24s-T sheet has a core of high-strength alloy combined with surface layers of relatively pure aluminum. The microstructure of a cross section of this product is shown by Fig. I. Not only does the relatively high-purity coating have a high resistance to corrosion, and hence serves as a mechanical barrier between the core metal and the corroding environment, but in addition this coating exerts electrochemical protection over areas where the core may be exposed, such as cut edges. In addition, the coating affords electrochemical protection to projecting heads of A17s-T, 17s-T and 24s-T rivets, or attached members made from these alloys. Under some conditions of heat-treatment, however, diffusion of copper into the coating will alter the electrochemical relationship between the coating and the core to the extent that only partial protection will be obtained under some corrosive conditions. The reason for the electrochemical protection lies in the fact that the coating layers of pure aluminum are anodic to the alloy core. The addition of copper to aluminum produces alloys in which the potential is lower than that of the pure metal. Moreover, as the amount of copper in solid solution in 24s alloy is increased, the potential of the alloy becomes more cathodic. When heat-treated at 920°F. and quenched in cold water, 24s-T is about 0.16 volt cathodic to pure aluminum. However, copper will diffuse from the core into the coating, and if it reaches the surface the potential will be altered in a cathodic direction. Thus the potential difference between the core and coating may be less than 0.16 volt, depending uponIthe thickness of the coating, and the time and temperature of heat-treatment. Of the methods available for determining the extent of diffusion of copper from the core into the coating of Alclad 24s-T, two are generally used; namely, the metallo-graphic and the solution potential methods.3 Metallographic Methods Metallographic methods will reveal the progress of diffusion of copper into the coating. For instance, the diffusion zone in the coating intermediate between the coating surface and the core is shown in Fig. I. This photomicrograph is of a polished and etched cross section of 0.040-in. Alclad 24s-T sheet. Diffusion proceeds into the coating more rapidly along the grain boundaries than through the body of the grains. Consequently, the diffusion zone is not of uniform width

Jan 1, 1944

By C. J. Rosa, W. C. Hagel

An attempt is made to determine the diffusion coefficients of oxygen ions in hypostoichiometric zirconium oxide. A phenomenological theory is developed for three-phase, unidirectional volume diffusion of a gaseous species from a planar source. Knowledge about oxygen diffusion in a and ß zirconium and experimentally measured rates of movements of interfaces permit the evaluation of oxygen ion diffusivi-ties in ZrO2-x. The results conform to the relationship: sq cm per sec, for the temperature range of 875" to 1050° C. DIFFUSION coefficients of oxygen ions in stoichio-metric oxides have been studied by many investigators. The obtained results not only supplement the knowledge about the lattice-defect structures of oxides and conduction mechanisms but also provide information of technological importance. Rate processes such as oxide sintering, high-temperature creep deformation, and oxidation of metals and their alloys are directly dependent on diffusion phenomena. Unfortunately, diffusion coefficients obtained from studies on stoichio-metric oxides cannot be treated without restraints when applied to oxidation kinetics, if precise evaluations of oxidation rates are desired. Oxides formed on metals are usually nonstoichiometric and exhibit nonuniform distribution of either cation or anion vacancies across their thicknesses. Debuigne and Lehr1 extended Danckwerts&apos;2 mathematical analyses and furnished a semitheoretical treatment for evaluating oxygen diffusion coefficients in zirconium oxide in terms of weight gain measurements during oxidation of zirconium in the temperature range 400° to 850°C. Their calculations are based on theoretical partitioning3 of the total amount of oxygen between a zirconium and its oxide phase. An inherent discrepancy appears to continue throughout their calculations. The amount of oxygen confined to the oxide phase should be corrected by multiplying the calculated oxide thickness by the inverse of Pilling-Bedworth ratio, if expansion of zirconium dioxide is taken into account. The purpose of the present investigation is to provide a new semitheoretical treatment for evaluating diffusion coefficients of moving species in hypostoichiometric oxide. The analyses are relevant to unidirectional volume diffusion. Although the presented method is quite general, its applicability will be discussed in terms of kinetic measurements from oxidation of zirconium at temperatures above the a/ß transition, for reasons stated in the later part of this paper. EXPERIMENTAL Pure, 99.93 wt pct, zirconium samples of approximately 2 by 1 by 0.35 cm were exposed to oxygen for various times at four temperature levels: 875°, 950°, 1000°, and 1050°C. High-purity, better than 99.9 vol pct oxygen was passed through a cold trap and columns containing anhydrous CaSO4 to remove residual water vapor. Before exposing to oxygen at a pressure of 500 Torr, specimens were subjected to wet abrasion on 200- through 600-grit Sic papers and polished with 1—p diamond dust. Prior to oxidizing, all zirconium samples were vacuum-annealed at 10-6 mm Hg for about 15 min at the test temperature. The temperature variation across the uniform heat zone was ±2°C from the preset value. Final polishing, for phase thicknesses measurements, was performed by using 8- and 1-p diamond dust and followed by vibrator polishing with 0.05-µ ? Al2O3 solution. Measurements of phase thicknesses were made by projection on a metallographic viewing screen. Conventional powder X-ray analyses for the oxide were employed. RESULTS Fig. 1 is an example of the cross section of oxidized zirconium. Designations of phases given below this figure are the same as those used in the three-phase diffusion system represented by Fig. 5 in the following section. Zirconium oxidized for longer exposure times showed two types of oxides: white oxide at the surface and an underlaying layer of gray oxide. X-ray powder patterns of these oxides at room tern-

Jan 1, 1969

By Henry P. Ehrlinger, James C. Bradbury

Tripoli is a naturally occurring, very finely divided form of silica found chiefly in some midwestern and southeastern states and used commercially as fillers and abrasives. Definitions Tripoli is a microcrystalline, finely particulate, more or less friable form of silica that appears to be the product of leaching of siliceous limestone or calcareous chert. The term was originally applied to a deposit near Seneca, MO, that resembled material of that name found near Tripoli In North Africa (Hovey, 1894). The two deposits were subsequently found to have different physical characteristics -the North African tripoli, now called tripolite, is a diatomite, composed of the siliceous skeletons of microscopic marine plants called diatoms; the Missouri tripoli contains no diatom remains. The term tripoli, however, continued to be used for the Missouri material and is now applied in a general way to most silica deposits similar to it in characteristics and geologic origin. In commercial trade tripoli is commonly understood to designate material from the Missouri-Oklahoma field; silica from southern Illinois, the other major producing area, is referred to commercially as amorphous silica. Each term, however, may be used commercially for material, regardless of place of origin, that has the characteristics or uses commonly ascribed to the material from one or the other major producing area. For example, in the commodity price listings, Engineering & Mining Journal routinely lists under Tripoli, prices "f.o.b. Elco, IL" and "f.o.b. Seneca, MO, and Rogers, AR," and under Silica, amorphous, prices "f.o.b. IL," and "f.o.b. bierks, AR." Amorphous silica, the commercial designation given to southern Illinois tripoli, is, like the term tripoli, a misnomer. Mineralogically, the southern Illinois deposits are composed of microcrystalline quartz, and no amorphous material has been detected during X-ray and scanning electron microscope investigations (Leamnson, Thomas, and Ehrlinger, 1969; Thomas et al., 1970; Keller, 1978). Soft silica is another term that has been applied to Illinois and Tennessee tripoli, presumably to distinguish it from the more compact Missouri material. It has also been used in the ceramic trade to distinguish tripoli from "hard" silica, or silica flour, produced by pulverizing silica sand (Heinz, 1937). Rottenstone, produced commercially in Pennsylvania, is similar to tripoli in that a major constituent is finely particulate silica, and its uses are much the same as those of Tripoli-as abrasives and fillers. The origin of rottenstone also is similar to that of tripoli-decomposition of a siliceous sedimentary rock. The parent rock is defined as a siliceous limestone (Gary, McAfee,, and Wolf, 1972; Thrush, 1968) or as shale. Heinz (1937) quotes a brief statement describing the Pennsylvania deposits -"a black impure shaly limestone grading into black shale"-but does not identify the source of the statement. For convenience, rottenstone is included with tripoli in the reporting of production statistics in US Bureau of Mines (USBM) Minerals Yearbooks. Other materials that have been called tripoli include siliceous deposits in San Bernardino County, California (USBM Minerals Yearbooks, 1934-1941) and in Nevada (Chandler, 1960). These, however, differ in composition and/or origin from tripoli and, therefore, should not be identified by the name tripoli.

Jan 1, 1983

By G. W. P. Rengstorff, R. B. Fischer

A study was made of the effect of impurities on the bend ductility of cast molybdenum. High purity molybdenum was repared by re-melting under high vacuum. The ductility of "transverse-grain" specimens indicated that intergranular brittleness decreased with an increase in purity of the metal. THE production of as-cast molybdenum with high ductility at room temperature would make working of the metal easier and increase the usefulness of the as-cast metal. Furthermore, a .knowledge of the factors that influence the ductility of as-cast molybdenum might be applied to the problem of making fusion weldments having satisfactory room-temperature ductility. Individual grains of commercial as-cast molybdenum are slightly ductile at room temperature. However, the presence of carbides at the grain boundaries may cause the metal to fracture in a brittle manner. This behavior has been discussed.&apos; The amount and distribution of the impurities in as-cast molybdenum would be expected, from previous research on the metal, to have considerable influence on its ductility. Some effects of oxygen and carbon on the mechanical behavior of the metal were discussed by Parke and Ham,2 Woodside,3 and Zappfe. Landgraf, and Worden.4 Parke and Ham2 found that, if a sufficient number of molybdenum oxide particles were present at the grain boundaries, the intergranular cohesion was reduced to the extent that arc-melted molybdenum would rupture intergranularly during hot forging. They also found that if the oxygen content was less than 0.003 pct, the cast molybdenum was hot forgeable. It is suspected, however, that forgeable molybdenum may contain a small amount of oxide that could reduce the ductility of the as-cast metal at room temperature. Also, there is the possibility of the unfavorable distribution of other impurities having a detrimental effect on the ductility of cast molybdenum. The results of a study of the influence of purity on the room-temperature ductility of cast molybdenum are presented here. Vacuum Arc-Melting to Produce High Purity Mo One way of determining the effect of impurities on the ductility of molybdenum is to prepare and test metal as free of all impurities as possible. Accordingly, the present investigation was undertaken with this in view. Arc melting in high vacuum (less than 0.1 micron of mercury) was chosen as the method for reducing the impurities below the concentrations occurring in commercial molybdenum. Commercial arc melting of molybdenum is carried out at about 50 microns pressure. During the arc melting, carbon and oxygen in the metal react to form carbon monoxide. By virtue of the vacuum process, the partial pressure of carbon monoxide is maintained at such a low value that the reaction greatly lowers oxygen and carbon contents. An excess of at least 0.03 pct C is used in commercial arc melting to insure that the oxygen content will be below 0.003 pct. The excess carbon remaining after the deoxidation step forms carbides on freezing. Some of the carbides precipitate at the grain boundaries and, as will be shown, have an unfavorable effect on the room-temperature ductility. In the present work, only the small amount of carbon (0.003 pct) contained in the commercial powder-metallurgy molybdenum used for melting stock was present. Partial removal of oxygen from the melt probably occurred as the result of the volatilization of molybdenum oxides, or by distillation of oxygen at the high melting tem-

Jan 1, 1953

By G. W. Healy, W. Craft, D. C. Hilty

By means of a theoretical extension of the Cr-C temperature relation in molten chromium steels to low chromium contents and by a correlation of the ratios of chromium to iron in the slag and metal, a method has been developed for estimating the amount of metallic oxidation during the oxidizing period of a chromium steel heat. Application of this method has indicated that due to temperature limitations metallic oxidation may be excessive for very low carbon steels charged with more than a small amount of chromium. IN the melting and refining of chromium steels the oxidation of carbon to a low level is accompanied by the oxidation of chromium and iron in considerable amounts. For the subsequent recovery of chromium and associated iron from the slag, the amounts of metal oxidized must be known for efficient reduction and control of composition. Further, in order to arrive at an accurate understanding of the process, so that chromium-bearing scrap can be used effectively, information is required on the relation between composition of the charge and weight of metal oxidized to reach the desired carbon content. Crafts and Rassbach1 recently developed an empirical relation between chromium, iron, and manganese oxidized per ton of steel charged, and final carbon content and temperature. This relation did not show any dependence on amount of chromium charged. However, it was felt that such a dependence might be present, so a further analysis of the data was undertaken. Cr-C Relation at Low Chromium Levels Crafts and Rassbach&apos;s results were based on temperatures estimated from the Cr-C relation previously established experimentally by Hilty,2 and on a single temperature observation (immersion thermocouple) on a heat made at low temperature from a charge of carbon steel scrap containing only a small amount of residual chromium. The temperatures estimated from the Cr-C relation were for heats charged with chromium-bearing scrap and which contained substantial amounts of chromium (2 to 10 pct) at the end of the oxidizing period. No data, other than that from the low temperature heat just mentioned, were available for the low and intermediate chromium ranges. In order to extend the range in which temperature may be estimated, the Cr-C relation requires further consideration. The Cr-C relation, expressed as suggests that carbon is zero at zero chromium in the bath. This is obviously absurd, because as chromium approaches zero the carbon content must approach the limit established by the Fe-C-O equilibrium. It is evident, therefore, that the Cr-C relation as defined by Eq. 1 is not valid below some minimum chromium content that may vary with temperature. On the other hand, it is probable that any such limiting chromium content is less than 4 pct at 3200°F, since the experimental data from which the Cr-C relation was derived included several observations at that level with no deviation. In any event, it is apparent that further evaluation of the results presented by Crafts and Rassbach is dependent upon a means for estimating the Cr-C temperature relation in the low chromium region. From the observations of Chen and Chipman9 and thermodynamic data given in Basic Open Hearth Steelmaking,4 the following relation can be calculated for melts containing small amounts of chromium and carbon assuming a carbon monoxide pressure of 1 atm: % Cr -21,250 K&apos; = (%C)2; logK1 == —t— +13.88 [2] Moreover, by plotting Eq. 2 for any given temperature on cartesian coordinates, it can be extrapolated graphically to the limiting carbon content at zero chromium for the specified temperature without serious complications. By means of Eq. 2 and its extrapolation, the Cr-C temperature relations originally established experi-

Jan 1, 1954

By F. Keller, R. H. Brown

Because of the extensive use of Alclad 24s alloy sheet in aircraft construction, there is much interest in the metallurgical changes caused by heat-treatment of this product.1, 2 One of these changes is the result of the diffusion of soluble elements from the core into the coating during treatment. This paper deals with the thermal treatments that may influence diffusion and with the practical effects of diffusion on the serviceability of the product. As is well known, Alclad 24s-T sheet has a core of high-strength alloy combined with surface layers of relatively pure aluminum. The microstructure of a cross section of this product is shown by Fig. I. Not only does the relatively high-purity coating have a high resistance to corrosion, and hence serves as a mechanical barrier between the core metal and the corroding environment, but in addition this coating exerts electrochemical protection over areas where the core may be exposed, such as cut edges. In addition, the coating affords electrochemical protection to projecting heads of A17s-T, 17s-T and 24s-T rivets, or attached members made from these alloys. Under some conditions of heat-treatment, however, diffusion of copper into the coating will alter the electrochemical relationship between the coating and the core to the extent that only partial protection will be obtained under some corrosive conditions. The reason for the electrochemical protection lies in the fact that the coating layers of pure aluminum are anodic to the alloy core. The addition of copper to aluminum produces alloys in which the potential is lower than that of the pure metal. Moreover, as the amount of copper in solid solution in 24s alloy is increased, the potential of the alloy becomes more cathodic. When heat-treated at 920°F. and quenched in cold water, 24s-T is about 0.16 volt cathodic to pure aluminum. However, copper will diffuse from the core into the coating, and if it reaches the surface the potential will be altered in a cathodic direction. Thus the potential difference between the core and coating may be less than 0.16 volt, depending uponIthe thickness of the coating, and the time and temperature of heat-treatment. Of the methods available for determining the extent of diffusion of copper from the core into the coating of Alclad 24s-T, two are generally used; namely, the metallo-graphic and the solution potential methods.3 Metallographic Methods Metallographic methods will reveal the progress of diffusion of copper into the coating. For instance, the diffusion zone in the coating intermediate between the coating surface and the core is shown in Fig. I. This photomicrograph is of a polished and etched cross section of 0.040-in. Alclad 24s-T sheet. Diffusion proceeds into the coating more rapidly along the grain boundaries than through the body of the grains. Consequently, the diffusion zone is not of uniform width

Jan 1, 1944

There were present twelve- Directors, the Secretary and the Assistant Secretary of the Institute, and fifteen guests. A committee of three was appointed to draft a suitable resolution of memorial of the services of Joseph Esrey Johnson, Jr. The committee consists of Joseph W. Richards, Chairman, J. V. N. Dorr and Allen H. Rogers. William R. Walker was elected a Director in place of J. E. Johnson, Jr., and Edwin Ludlow was elected a member of the Executive Committee in his stead. George C. Stone was appointed Chairman of the Committee on Membership in place of Mr. Johnson. The following resolutions were then adopted: RESOLVED, That a special business meeting of the Institute be and the same hereby is appointed to be, held at the office of the Institute, No. 29 West 39th Street, Borough of Manhattan, City of New York, on the 27th day of June, 1919, it 8.30 o&apos;clock in the P. M. to consider and take action upon the proposal to change the name of the Institute to "American Institute of Mining and Metallurgical Engineers, Incor-porated," and the further proposal to extend the corporate purposes of the Institute so that it shall, in addition to its other powers, be empowered to promote the arts and sciences connected with the economic production of the useful minerals and metals, and the welfare of, those employed in these industries, by all lawful means.

Jan 6, 1919

By W. B. Finkeldey, C. H. Mathewson, C. S. Trewin

This paper was prepared upon request as a contribution to a symposium covering the manufacture, properties, and uses of the important non-ferraus metals. In approaching a subject as broad as this, there is a natural desire to build up a comprehensive and finished production which shall constitute a dependable source of information on all questions properly belonging to this branch of metal technology. There are, however, a number of circumstances, apart from the mere routine of labor and thought involved, which operate rather effectively against the possibility of completing such .an ambitious program at the present time. First of all, as far as any public record of results is concerned, the commercial rolling, drawing, and forming of zinc with relation to changes of structure and properties—and this we consider to constitute the clement~ of metal technology—might as well be an unpractised art. We have never seen a published photomicrograph showing the structural characteristics of either hard or soft sheet or strip, although the structure of castings has been frequently described, and other coarse-grained structures resulting from hard-hammering and annealing have been reproduced. Thus, an author in this field must proceed to his task without much assistance from the literature, and the outcome can represent only a personal estimate of principles, facts, or findings, and not a summary or survey of progress in the entire field as determined by varied experience, practice, and settled opinion.

Jan 1, 1921