By Charles Hart

THE-report of the advisory committee to the U. S. Bureau of Mines, on the use of oxygen in metallurgy, brings to the art of steelmaking a radical change in the method of operation of the many processes of this widely diversified industry. When completed, the improvements suggested by the use of oxygen will be far-reaching and revolutionary. As to its effect upon the iron blast furnace, the use of oxygen should be as important as any of the improvements in the art of iron smelting and should take its place beside the German "Hochofen" which was the first attempt to use a shaft for preheating the stock, and beside the hot-blast stove which heated the blast before entering the furnace. The former initially produced molten iron and the latter made unbelievable economies in fuel consumption. It would seem that a discussion of this paper would be best served by following the conclusions on page 17 of the report and analyzing them seriatim. 1. (a) A decrease in costs, due to higher smelting heats is only attainable by taking full advantage of these heat units. This is affected by, adding additional ore to the burden which in turn increases production and yields a larger tonnage upon which to figure costs. These economies appear in decreased cost per ton of iron for coke and limestone consumed, and a proportionate reduction in all items entering the cost above materials. We can take no exception to these. premises. It is a well-known fact that silicon in the iron and sulfur removed" are the result of hearth temperature, other matters remaining constant. To a practical furnaceman the most satisfactory manner of controlling a furnace is by increasing the burden. It is not necessary, therefore, to consider the question of refractories, for this discussion presupposes that the temperatures in the furnaces will be kept practically where they now stand for making the various grades of iron. The same situation obtains in regard to the height of the furnace, which, as intimated, was one of the great strides forward in this art, and its abandonment at this time, is inconceivable. The shaft prepares the stock so that at each succeeding step we have exactly the proper conditions. All the stock entering the furnace is dried and preheated. The limestone is calcined by sensible heat practically at no cost, for this is sensible heat which otherwise would pass from the top with the gases. Under normal conditions, external calcination has been attempted without tangible results. Under normal average furnace operation, limestone requires about 760 B.t.u. for calcination and the loss of sensible

Jan 11, 1924

By Carl G. Hogberg

During recent months, the acute shortage of steel scrap has necessitated the use of higher percentages of hot metal in the open-hearth charge. With these higher percentages, the sulphur content of hot metal has become an increasingly important factor in the control of the quality of steel. Thus, the blast-furnace operator is faced with a demand not only for more output but for a higher quality of product. More than go per cent of the sulphur charged into the blast furnace is contained in the coke. With the tremendously increased demand, the trend of coke quality has been toward higher sulphur, higher and more variable ash, and poorer physical characteristics. This has been brought about by less selective coal mining, increased production rates in coke plants and resumption of operations of many beehive ovens. In a single month last year, one blast-furnace plant in the Pittsburgh district operated with coke obtained from 52 sources. The effect of variability and quantity of coke ash on blast-furnace operation is well known. The improved results obtained with furnaces operating on coke made from washed coals compared with results on coke made from raw coals is ample proof of the effectiveness of low and uniform ash. Coal-washing plants, however, require a large capital expenditure, and are impractical for most of the large number of small producers, whose operations are confined chiefly to periods of abnormally high demand. Furthermore, not all coals are physically adaptable to washing. Principles 01 Iron Desulphurization in Furnace Although investigations of the blastfurnace process have not clearly revealed the detailed mechanism of iron desulphuri-zation within the furnace, they have been sufficiently extensive to permit a postula tion of the following general principles: 1. Iron, in its travel from furnace top to hearth, continues to pick up sulphur until it has reached tuyere level. The zone of iron desulphurizatioil is relatively narrow, being confined to a vertical distance extending zapproximately from tuyere level to the iron-slag interface in the hearth.' 2. Combustion of coke is confined to spherical zones extending approximately 40 in. from the nose of each tuyere.= Coke ash is released as the coke bums in these combustion areas. 3. With a constant amount of sulphur in the charge, the sulphur content of the metal product is a function of hearth temperature, final slag analysis, slag viscosity, and slag volume. Both hearth temperature and slag analysis affect slag viscosity. For a slag of constant analysis, viscosity always decreases with an increase in temperature;

Jan 1, 1943

By Carl G. Hogberg

During recent months, the acute shortage of steel scrap has necessitated the use of higher percentages of hot metal in the open-hearth charge. With these higher percentages, the sulphur content of hot metal has become an increasingly important factor in the control of the quality of steel. Thus, the blast-furnace operator is faced with a demand not only for more output but for a higher quality of product. More than go per cent of the sulphur charged into the blast furnace is contained in the coke. With the tremendously increased demand, the trend of coke quality has been toward higher sulphur, higher and more variable ash, and poorer physical characteristics. This has been brought about by less selective coal mining, increased production rates in coke plants and resumption of operations of many beehive ovens. In a single month last year, one blast-furnace plant in the Pittsburgh district operated with coke obtained from 52 sources. The effect of variability and quantity of coke ash on blast-furnace operation is well known. The improved results obtained with furnaces operating on coke made from washed coals compared with results on coke made from raw coals is ample proof of the effectiveness of low and uniform ash. Coal-washing plants, however, require a large capital expenditure, and are impractical for most of the large number of small producers, whose operations are confined chiefly to periods of abnormally high demand. Furthermore, not all coals are physically adaptable to washing. Principles 01 Iron Desulphurization in Furnace Although investigations of the blastfurnace process have not clearly revealed the detailed mechanism of iron desulphuri-zation within the furnace, they have been sufficiently extensive to permit a postula tion of the following general principles: 1. Iron, in its travel from furnace top to hearth, continues to pick up sulphur until it has reached tuyere level. The zone of iron desulphurizatioil is relatively narrow, being confined to a vertical distance extending zapproximately from tuyere level to the iron-slag interface in the hearth.' 2. Combustion of coke is confined to spherical zones extending approximately 40 in. from the nose of each tuyere.= Coke ash is released as the coke bums in these combustion areas. 3. With a constant amount of sulphur in the charge, the sulphur content of the metal product is a function of hearth temperature, final slag analysis, slag viscosity, and slag volume. Both hearth temperature and slag analysis affect slag viscosity. For a slag of constant analysis, viscosity always decreases with an increase in temperature;

Jan 1, 1943

By F. Keller, A. H. Geisler

Some of the important changes that take place in the structure of aluminum alloys are largely submicroscopic in character. This is especially true of the changes that accompany age-hardening and recrystallization. Although improved metallographic practices have been helpful in indicating some of these changes indirectly, results are limited by the resolving power of optical microscope lenses. The electron microscope, however, provides a new and important means for investigating the fine structure of metals in a range not possible heretofore. It is anticipated that this microscope will yield new and useful information to metallurgists when suitable techniques are developed to utilize its very high resolving power. Several unique methods have been devised to permit the examination of the structure of opaque samples by the electron microscope. These are all based on the principle of producing a very thin film that represents the prepared surface of the opaque metal sample, which can be examined in the transmission microscope; however, the available methods fall into three categories, depending on the manner in which the film is obtained. With the oxide-film method developed by Mahl3-17 a very thin surface layer of the metallographic sample is converted into oxide by a thermal, chemical or anodic treatment. After removal from the metal sample by one of the special techniques described by Evans,19 this oxide film is examined in the electron microscope, and is found to portray the structure of the original metal surface. Films formed on aluminum,8,17 nickel,7 iron 3,8,9 and a nickel-beryllium alloy" by heating; films formed on iron 8.9 by chemical action; and films formed on aluminum3-16 by anodic oxidation, have been examined. The other two are more recent methods developed principally in this country; they consist in making the thin film in the form of a mold or replica of the surface contour of an etched sample. With the negative replica method the thin film is made directly on the sample; with the positive replica method it is made on a negative reproduction of the sample. With both methods, variations in the contour of the metal sample, caused mainly by etching, produce variations in the thickness of the surface replica. Because of the direct dependence of the amount of scattering of the illuminating electrons upon the thickness of the film penetrated, only the variations in thickness of the replica are responsible for tones in the electron image. Negative replicas are made by forming a thin film of some suitable material directly on the polished and etched metal sample, and derive their name from the fact that after removal from the sample they have the high and low points in the sample reversed, as shown in Fig. I. Nega-

Jan 1, 1944

By E. H. Bunce

CONTINUED progress in zinc metallurgy has been shown during 1933 by the adoption of new methods as well as the modernization of old processes and equipment, and by the initiation of new fields of activity for future advancement. The use of suspension roasting continued to grow as its advantages and adaptability became increasingly, apparent. The process developed by the National Smelting Co., Ltd., several years ago, of completely roasting on large sintering machines with utilization of the gas for acid manufacture has worked so successfully that an additional machine was installed during the year. At both the Swansea and the Avonmouth Works all of the ore for smelting is now roasted on the large sintering machines, thereby completely eliminating the old hearth-roasting furnaces. Work continued on obtaining partial purification of zinc ores from lead and cadmium by close control of conditions on the sintering machine, and in a few instances by chlorine additions to the ore before sintering. Ores so treated were either partially roasted or com-

Jan 1, 1934

By Arthur S. Dwight

THE last decade of the 19th century was a peculiarly interesting one in. the annals of American metallurgy, especially as concerns the lead and copper- smelting industries; and it may be interesting to review briefly one of the outstanding incidents of that period, the development of the mechanical roasting furnace. I shall not pretend, in these reminiscences, to give with absolute accuracy the sequence of events or dates, nor to present a complete history of the period, but shall seek merely to 'sketch a more or less impressionistic picture with some of the underlying facts and causes as the recollection comes back to me and then point out how the present-day practice grew out of those activities. My acquaintance with the developments in Montana was based on occasional visits and general collateral information, but in Colorado I lived through the episode and was of it.

Jan 1, 1921

By W. M. Myers

MINERAL Economics is the most recent profession to be recognized as a separate division of the mineral industries. It has originated from the increasing awareness of the importance of the economic aspects of industries concerned with discovery, extraction, and utilization of minerals. It is concerned with the interrelated fields of economics and technology. The individual trained in economics alone cannot qualify. The curriculum in the School of Mineral Industries at The Pennsylvania State College was approved in May 1946, and enrollment begun in September of that year. Due to the transfer of advanced students from other courses, particularly metallurgy and electrical engineering, it was possible to graduate the first seniors in June 1947. The next class was graduated in February 1948. From experience derived from placing these graduates in industry, and from information supplied by prospective employers, valuable data have been obtained in the organization and operation of the course of study.

Jan 1, 1948

By C. H. Li, R. J. Stokes, T. L. Johnston

Dislocation half-loops, artificially introduced by sprinkling with carborundum, were subjected to stress using three-point loading. The different stages of loop expansion and multiplication were then correlated with the macroscopic stress-deflection curve. Loop expansion started at approximately one-third of the "yield stress," defined here as the motivation stress. Above one-half of the "yield stress" simple multiplication commenced while about two-thirds of the yield stress gross multiplication developed short slip-line segments. These values were not affected by the age of surfaces exposed to both dry and wet air. Slip was not detected on unsprinkled crystals below two-thirds of the "yield stress." Thus the stress to activate intrinsic sources, defined here as the activation stress, was approximately twice the motivation stress. This relationship was independent of the strain rate used. It is concluded that lattice resistance takes the form of a viscous drag rather than a static type of force. THE importance of surface condition and environment as one of the more significant factors controlling the mechanical properties of ionic solids has recently received renewed attention.1-4 In some materials, notably the alkali halides, exposing freshly cleaved specimens to the atmosphere results in a progressive hardening and embrittlement of the crystals. This has been attributed to the surface layer becoming "aged," thereby restricting the motion of dislocations in such a way that pileup and eventually fracture results. It is necessary therefore in studying the mechanical properties of ionic crystals to inquire first into the density and distribution of dislocations in the normal cleaved surface and to understand the role these dislocations play in the onset of plastic flow. Knowledge of the effect of environment on this behavior will then assist in understanding the mechanism of embrittlement on aging. In the work reported here a method is described for studying the initiation of plastic flow from dislocation sources in the surface of magnesium oxide crystals. Preliminary results are described of the influence of surface age on this behavior. EXPERIMENTAL TECHNIQUES The magnesium oxide used in this investigation was obtained from the Norton Co. and had a nominal purity of 99.5.pct. Single-crystal specimens, having dimensions typically 1/4 by 1/8 in. cross section and 1 in. in length, were prepared by cleavage over (100) planes from the parent crystal. They were deformed under three-point loading with 3/4 in. spacing between the two end supports and a constant rate of deflection at the center of 0.001 in. per min. The maximum strain rate therefore was 1.5 X 10-5 sec-1. Reasons for choosing this particular form of loading will become apparent in a later section. In addition, a number of confirmatory type tests have been performed at higher loading rates where the maximum strain rate was increased to 1 x 10-3 sec -1. Following deformation the crystals were etched to reveal the dislocation distribution. In a previous paper5 we described a satisfactory etching solution consisting of 5 parts of saturated ammonium chloride, one part of sulfuric acid, and one part distilled water. Immersion of the crystals for 1/4 hr at room temperature developed reproducible conical etch pits at the points where dislocations emerged through the surface. It should be mentioned that dislocations freshly introduced by room temperature deformation gave sharply pointed etch pits which generally distinguished them from the almost flat-bottomed pits obtained on "grown-in" dislocations. The distinction is obvious in the photomicrograph included in Fig. 5(b). Annealing crystals at 1000°C for 12 hr on the other hand gave sharper etch pits on the grown-in dislocations and the distinction was no lower -possible; a similar observation has been reported for lithium fluoride. We have succeeded furthermore in chemically polishing magnesium-oxide crystals. Boiling in fresh 85 pct ortho-phosphoric acid for only 1 min resulted in a microscopically smooth surface which could again be etched to reexamine the dislocation distribution. This boiling time was sufficient to remove the surface damage introduced by cleavage (see next section). SURFACE DISLOCATION SOURCES There are a number of ways by which dislocations may be introduced into cleaved surfaces to act later

Jan 1, 1960

By Robert M. Weidenhammer

For years before the war, Coal had the reputation of being a sick industry. Currently it is operating at peak production and succeeding pretty well in keeping out of the red. But, says Mr. Weidenhammer, it will have a relapse as soon as the war ends unless (1) working capital can be built up; (2) it gets the support of the people and Congress; and (3) a truly long-range national fuel policy is formulated.

Jan 1, 1943

By R. W. Gurry

WHEN a steel in the austenitic state, with all its carbon in solution, is maintained, at constant temperature, in contact with a gas that removes the carbon from the surface, vet without otherwise altering the composition of the steel, the change in weight of the specimen, after any period of exposure, is a direct measure of the amount of carbon it has then lost. The purpose of the present paper is to show how, by application of established mathematical reasoning based on the fundamental diffusion law and on certain postulates, this loss of weight yields a complete picture of the distribution of carbon throughout a specimen of regular shape after any period of exposure, with all the accuracy required in any practical occurrence of decarburization. Precisely the same is true for the gain in weight during the reverse process of carburization, or for the gradual gain or loss of any element, so long as the steel comprises only a single phase at temperature, provided always that the experimental conditions conform to the postulates. The change in carbon content from surface to center of the specimen is always continuous, when everything is in solution, even though under the microscope the decarburized zone (or carburized rim) may appear to be sharply defined. The experimental procedure is described and some typical results are presented, which are then interpreted by application of the diffusion law. EXPERIMENTAL PROCEDURE Initially an endeavor was made to follow the gain of weight during the process of carburization in a hydrogen-toluene atmosphere, but it was soon found that the specimen became coated with graphite, which could not be removed without some loss of metal; therefore it was decided to continue carburization until the steel was saturated throughout, to remove all graphite from the surface of the specimen, and then to follow the loss of weight during decarburization in a moist hydrogen atmosphere at the same temperature as that used for carburizing. The carburizing procedure has been described in an earlier paper;1 it suffices to state here that the carburization lasted about 140 hr. at 760°C. (1760°F.) and 44 hr. at 1110°C. (2030°F.), these periods being long enough-on the basis of the calculations presented later-to ensure that the specimen was about 9.99 per cent saturated at each temperature. The speci¬men was a cylinder about 3.8 cm. long and 0.475 cm. in diameter; the materials were carbonyl iron, a commercial low-metalloid iron, and a steel with 3.6 per cent nickel and the usual proportion of other elements. The fully [carburized] specimen, after cooling at the top of the furnace tube, was placed in a lathe and sandpapered to remove all graphite; then the diameter was measured with a micrometer caliper, and the initial weighing (corresponding to complete saturation) was made. By means of a

Jan 1, 1942

By NORMAN EBBLEY

NUMEROUS references have been made recently to "Alaska's oil reserves," and in view of the wartime petroleum situation sober thinking demands a dispassionate and scientific study and investigation of these reserves or supposed reserves. The question naturally arises, "Is there actually oil in Alaska, or are the reserves there a supposition?" True, in 1923 President Harding established Naval Petroleum Reserve No. 4 in Alaska, certainly implying that oil was there. This reserve, embracing about 35,000 sq. mi., was set aside on the advice of the Bureau of Engineering of the Navy Department and was based upon the existence of known petroleum seepages at Cape Simpson on the Arctic coast. The Cape Simpson seepages have been known for more than fifty years, but in spite of persistent rumors of other seepages in northern Alaska no definite evidence of their existence has been available.

Jan 1, 1944

By N. G. Johnson

ALL of us are only too familiar with the fact that first the defense program, and finally the war, required vastly increased production from existing sources, and the discovery and development of new sources of minerals and metals. For this vast program, the explosives industry was well prepared. I use the term "well prepared" to cover all the phases of explosives service, which include formulation, design, manufacture, distribution, and application.

Jan 1, 1944

By Edwin Chance

DURING the last decade many conditions have been encountered that have materially increased the cost of the production of coal. As in most cases it has not been practicable to increase the selling price of such coal sufficiently to insure the necessary margin of profit, the mine management has been forced to avail itself of what might be termed unusual means that costs might be held at as low a figure as possible. The so-called efficiency engineer has been called upon, costly power plants have been built and machinery has been installed to replace manual labor wherever possible. Another aid used recently to secure economies through the more intelligent production of coal, is the chemist. As the coal industry, barring the production of byproduct coke, does not at once give evidence of its need of the services of the chemist, the writer will endeavor to point out a few of the services that this branch of the staff has been able to render. The preparation of coal in the past has been carried on entirely upon an empirical basis, that is, the criterion adopted has been an ocular inspection. Unfortunately, the appearance of a coal and especially of an anthracite, has but little relation to its fuel value, and as long as coal is purchased for the heat that 'can be obtained from it by its combustion, the quantity of such heat that is purchased must be one of the principal desiderata in selecting or preparing a coal. Were coals purchased for use as bric-a-brac or for exhibition in museums it might be both wise and just to purchase them upon their appearance. After 4 or 5 years of investigation the fact has been established that coals of very inferior appearance, and I now have special reference to anthracite, might and often did possess heating and burning properties superior to those possessed by, bright coals which in the past had commanded considerable and uniform premiums in the market. This being the case the question arose as to whether the trade could be convinced of this fact. While at first some difficulty was experienced in establishing the quality of such dull coals, still it was found that the real obstacle to the sale of these

Jan 4, 1916

By Ernest O. Kartinen

This report is the accumulation of eight years of experience on only one small phase in the business of oil production. It is not intended as a final report but rather as a progress report dealing with the internal corrosion of oil field dehydrating tanks. The corrosion of dehydrating tanks continues to be a problem in the production of crude oil. The deterioration hy corrosion of these tanks falls into three general classifications: (1) Atmospheric corrosion of exterior areas, (2) corrosion of the underside of deck and the rafters and top area of the upper row of staves in that part of the tank which is known as the vapor space, and (3) corrosion of the bottom and shell areas, and the steam coils which are normally immersed in water and thus exposed to the corrosive action of the water. Atmospheric corrosion is primarily a paint problem, and has been omitted in this discussion. The corrosion in the vapor space, in this company's experience, which has been of great concern only in one area. has also been omitted in this discussion. The third, and most troublesome type of corrosion, and the one with which this report deals, is that which occurs in the water-exposed areas of dehydrating tanks, and, to a lesser degree. in some stock tanks. The operating temperature of these waters varies from 80°F to 160°F and the salt counts run from a few thousand to as high as 25.000 parts per million. Corrosion in these tanks occurs in three forms: (1) pits, (2) ringworm type of attack along the vertical and horizontal bolt seams, and (3) as a general attack, spread over a wide area. Steam Coils In dehydrating tanks, our experience has been that the steam coils are the first to show signs of corrosion, and then the shell and bottom areas. This action is not uniform throughout this company's operations. Some installations have coil troubles with very little tank trouble, and some show just the opposite. But in the majority of cases the coils are the more seriously corroded areas. This may be partly due to the fact that we have tried by periodic application to keep a protective coating on the interior areas of the tanks, and some protection has been afforded by these coatings. Through the years several types of hot and cold coatings have been tried with many various methods of cleaning the steel, ranging from use of cleaning solvents to hot and cold Oakite washes, as well as sandblasting. Although experience has shown that a longer life expectancy of a coating is possible after a very thorough steel cleaning job, it has still been necessary to recoat these tanks at least every two or three years. Until a few years ago, vertical spiral steam coil bundles were installed when the tanks were originally erected. When these coils needed replacement, in some cases within 18 months, it was necessary to remove a couple of shell staves to accomplish this task. This required a down time period of several days and was often very inconvenient to the production operations of the leases. This problem was considered on the basis that the coils were expendable, and thus. to eliminate any unnecessary down time when changing coils, the vertical spiral coils were discarded in favor of horizontal flat coils which could be taken in and out of the tanks by way of the cleanout openings, and put together with unions. This made a fairly easily replaceable and repairable coil. But it was still very much of a nuisance when repairs were necessary. Efforts to increase the useful life of the dehydrating tanks led to the adoption of galvanized tanks at an increased initial cost. The zinc coating was depended upon for protection and no other protective coatings were applied. In July, 1944. during the development of a new lease, a 3-ring 1,500 bbl, black iron water tank was converted into a dehydrating tank with steam coils to handle the new production. This tank was coated inside with a cold, brushed-on coating, for protection against corrosion. After approximately 18 months of service, holes developed in the tank and the steam coils. The tank was emptied and cleaned for repairs. The coils were so badly pitted that it was felt advisable to replace them. Coating Becomes Loose Inspection of the tank showed the protective coating to be still in place but loose, and numerous blisters were in evidence. A closer inspection showed that the interior of this tank was so badly pitted under the coating that any further attempt to use the tank was inadvisable. This tank was therefore discarded and a new galvanized tank ordered and set up at considerable expense and inconvenience. In April, 1946, another dehydrating tank installation was made on an adjoining lease. This installation consisted of a 1,500 bbl. 3-ring galvanized tank with two sets of flat steam coils 12 in. and 24 in. up from the bottom. In September, 1947. seventeen months after installation. salt showed up in the boiler feed water. When the dehydrating tank was opened and cleaned, the steam coils were found to be badly pitted — several holes having penetrated through the wall of the pipe. New coils were installed.

Jan 1, 1950

By AIME AIME

ON Tuesday afternoon, Feb. 17, a large and interested audience gathered in the auditorium of the Engineering Societies building to take part in the gold supply symposium that had been arranged for by the Mining Geology Committee. Waldemar Lindgren presided over the gathering and after brief introductory remarks on the international situation as regards lead, silver and gold, called on John Wellington Finch to present an oral abstract of the paper, "Sources and Trends in Gold Production," by R. J. Grant, director of the Mint, and. J. B. Knaebel. This ' paper reviewed the gold production of the world, by countries, since 1845, from the statistical viewpoint, leaving to the later speakers discussion of the statistics.

Jan 1, 1931

By ALFRED T. BARR

In certain areas of the New Cornelia pit, considerable secondary blasting is necessary to reduce oversized boulders, formed from primary blasting, to pieces which will pass the 41/2-cu yd dippers on the shovels. Some of the boulders are 'dobied, but when time permits they are blockholed and blasted. In most instances one hole drilled to a depth of 2 to 3 ft and blasted with 1/3 to 1/2 of a stick of powder will break a boulder satisfactorily. Blockholing is normally done by using a jackhammer of the 55-lb class, 1-in. round drill steel, and detachable steel bits, 2-in. gauge when new. A bit change is usually made after the completion of each hole. The use of light drilling equipment in blockholing is desirable, both from the standpoint of safety and ease of doing the work, and when it was seen there was a possibility of using a lighter jackhammer through the use of tungsten-carbide bits and at the same time get at least the same drilling efficiency as with the standard equipment, it was decided to test tungsten-carbide bits. The claims for long life of the bits and footage drilled before resharpening gave hopes of eliminating much of the delay time in changing bits which is unavoidable with the use of steel bits. and thus gain in actual drilling time.

Jan 1, 1949

By E. W. Parker

THE anthracite region, from which there is produced annually about 80,000,000 tons, or approximately 15 per cent. of the total coal supply of the United States, has a combined area of a little less than 500 sq. mi. The total area occupied by the bituminous fields (including the sub-bituminous and lignite fields) is in the neighborhood of 400,000 sq. mi., so that 15 per cent. of the total output comes from this small area of only a little more than 0.1 per cent. of the coal-producing territory. of the United States. The productive anthracite area is divided into a series of basins or troughs, roughly parallel, extending. in a northeast-southwest direction through the. Counties

Jan 1, 1921

By AIME AIME

A COMMITTEE of the American Railroad Association, consisting of Samuel Rea, president of the Pennsylvania System, Chairman; F. D. Underwood, president of the Erie Railroad; A. T. Dice, president of the Philadelphia & Reading Railroad; E. J. Pearson, president of the New York, New Haven & Hartford Railroad; and C. H. Markham, president of the Illinois Railroad (who was represented at the meeting by J. F. Porterfield of his system), met at the headquarters of the American Institute of Mining and Metallurgical Engineers, New York, on April 6 to assist in the Coal and Coke Committee's attempt to solve the bituminous coal problem. There was a full discussion of the questions of seasonal freight rates and the purchase by the railroads during the slack months of their winter's supply of coal. As the question of fuel supply for the railroads is in the hands of the Railroad Association, as well as the coal operators, it was vital that it should be represented at this important conference. The situation from the point of view of the mine operators was presented very thoroughly. No seasonal rates were considered necessary for the year 1920, and, as this matter requires considerable thought, it will be given thorough study and worked out in detail at a subsequent meeting.

Jan 1, 1920

By J. F. Kemp

IN submitting an additional contribution to the discussion on ore-deposits in the recent volumes of the Transactions, it is my desire to adhere closely to matters of material importance as affecting the actual processes. Judging from the discussion by Professor Van Hise, and from one or two reviews or other articles by associates of his in geological work, the impression seems to prevail that, in so far as my paper* referred to ,his masterly essay,†I was guilty of misconceptions regarding both the part attributed by him in it to the igneous rocks and the ubiquitous presence of the ground-water. I should regret extremely to be wanting in these particulars or to have misunderstood one for whose great services in this and other branches of geology no one has a higher esteem than myself. I have, however, in the most careful way, and with these points in mind, read his essay again, anti, taking it as a whole, I cannot gain any different impression of relative magnitudes than the one first received. The importance of the igneous phenomena and the restrictive influence of the processes described by " cementation " in their effect upon the ground-water, as set forth in Professor Van Hise's " Discussion " (Trans., xxxi., 292), impress me as being in very marked contrast with the same things in his first essay. If the point seems to anyone of sufficient importance, it can easily be decided by reading the originals. My paper was the result of some years of observation, reading and reflection, and was meant to be an independent contribution, controversial only in some subordinate particulars. In depicting the drama of the deposition of ores, I cannot but feel that Professor Van Rise assigned to the chorus and the scene-shifters some characters which, it seems to me, should

Jan 1, 1913

By J. Chipman, N. J. Grant, H. L. Bishop

In a recent review1 of the iron-oxide activity of simple open-hearth type slags containing lime, magnesia, silica, and iron oxide, it was established that activity values were lacking in the range of slag composition most interesting to open-hearth operators. That is, laboratory experimental results were not available for simple slag compositions having basicity ratios ranging from about 1.5 to 4.0 and iron-oxide concentrations ranging from about 10 to 30 pct. However, in order to estimate iron-oxide activities for the range of slag compositions of interest to open-hearth operators, activity values were calculated using ionic concepts of slags by following the treatment of Flood and Grjotheim.2 A study of these data indicated that the desired slag compositions were probably not obtained due to the limited solubility of the basic constituents lime and magnesia. Thus, it was decided to make additional heats equilibrating molten carbon-free iron with slags containing MnO, P2O5, and A12O3 in percentages commonly found in open-hearth refining slags, and to examine the liquid slag field over a greater composition range than that of the simple slags studied previously. The ranges of the constituents used in the present study are summarized as follows: Metal Pct 0 0.070-0.201 PctMn 0.005-0.142 Slag Pet CaO 24.45-41.90 Pct MgO 3.23- 9.21 Pct MnO 1.13- 9.62 Pct FeO 20.08-48.7 Pet Fe2o3 2.23-10.14 Pct SiO, 3.51-28.50 Pct P2O5 0.23- 3.65 Pct A12O3 0.43- 3.38 The experimental procedure consisted of equilibrating the slag and metal in an induction furnace provided with a carbon-arc slag heater as described previously by Winkler and chipman.3 The data obtained were used to establish both the iron-oxide activity values and the activity coefficients for FeO and MnO in the open-hearth type slags. RESULTS AND DISCUSSION I) Iron-Oxide Activity of Open-Hearth Type Slags—The iron-oxide activities of various iron-oxide contents of the open-hearth type slags, as calculated from the oxygen content of the metal by the method of Taylor and Chipman, 4 are plotted against the molar ratio of bases to acids in Fig. 1. The data represent slag-metal studies carried out in the temperature range 1530" to 1700°C. For the purpose of this study, the constituents CaO, MgO, and MnO are assumed equal on a molar basis in their effect on the iron-oxide activity; and, PO2,5 is calculated as an equivalent to SiO2 and A12O3 on a molar basis. The total iron content of the slag is calculated to FeO and is represented by the symbol (FeO) The points presented in Fig. 1 represent the results of this investigation for iron-oxide slags containing between 1 and 8 mol pct MnO and less than about 2 mol pct each of A12o3 and PO2,5 The curved lines shown in Fig. 1 represent the results of the summary1 of the iron-oxide activities of simple slags of the system (CaO + MgO) - SiOz - (FeO),. The solid portions of the curved lines represent experimental data, and the broken portions represent iron-oxide activities calculated from ionic concepts of slags. The iron-oxide values of the open-hearth type slags of this study are in good agreement with the values of the simple iron-oxide slag system. Only a slight modification is indicated. The results of this study suggest that the line for 20 mol pct (FeO), should be lowered slightly in the basicity range 1.5 to about 3.

Jan 1, 1959