By Ritayan Chatterjee, P. K. Mukhopadhyay, Surajit Biswas, Dinabandhu Ghosh, Sandeep Agarwal

An Indian magnetite ore from the Nagaland region was characterized by powder X-ray diffraction, spectroscopies (ultraviolet-visible and Raman), high temperature magnetization and thermal analysis. A Rietveld refinement of the diffraction data revealed that the principal phase present in the sample is magnetite with partial substitution of Fe with Mg (mainly) and Cr, leading to the chemical formula of MgCr0.2Fe1.8O4. The UV-visible spectra of the sample in MeCN solution showed three distinct peaks. The lower region bands are due to metal-oxygen charge transitions and the other band is for d-d transition of iron. Raman spectral study at room temperature gave four characteristics bands of magnetite. The sample underwent a magnetic transition at high temperature and the thermomagnetization curve shows hysteresis during cooling cycle which indicates the possibility of first order structural transition at high temperature. The thermal property of the concentrate was studied by differential scanning calorimetric technique.

Mar 1, 2018

By Mingmei Zhu, Xin Qiu, Xiaofei Dou, Yu Wang, Tiancheng Lin, Bing Xie

In this study, the slag forming route of the single-slag steel melting when smelting medium phosphorus hot metal was investigated. The CaO-SiO2-FeO-MgO-MnO-P2O5 as hexahydric slag system was adopted in the converter. The effect of slag composition on liquidus was calculated by FactSage, the isogram of phosphorus distribution ratio was calculated by using the regular ion solution model, combining these two tasks, the theoretical slag forming route was obtained. Through experiments, the actual melting point ofthe corresponding components on theoretical slag forming route was obtained, in this way, the theoretical slag forming route was confirmed. Then, the theoretical slag forming route was applied to industrial test in a 210t BOF. After using the new slag formating route, the dephosphorization ratio was increased 3.6% while the auxiliary materials consumption was reduced, and the cost of steelmaking was reduced.

Jan 1, 2015

By Mariana M. Arantes, F. R. Valenzuela-Díaz, Olgun Guven, Vijay K. Rangari, Julyana Santana, Esperidiana Moura

Nowadays, the development of polymeric materials reinforced with residues of vegetal fibers is becoming popular for application in different segments, from the automotive to the civil construction and furniture industry. Vegetal fiber residues may be used as reinforcement of the recycled polymer materials, for instance, to produce foams to packaging or to thermal and acoustic isolation for green building application. This work is focused on the development and characterization of recycled-HDPE/EVA foam reinforced with fiber residues from babassu coconut epicarp. Firstly, composites based on recycled-HDPE/EVA blend reinforced with babassu coconut fiber were obtained by melting extrusion process. The composites were then extruded in a special single screw for foaming. The foam samples were submitted to mechanical tests, density measurement, DSC, TG, and FE-SEM analysis.

Mar 1, 2018

By Masanori Harata

A fundamental study was conducted on a new process for producing scandium (Sc) metal or aluminum-scandium (Al-Sc) alloy by the calciothermic reduction of scandium oxide (Sc2O3). In this study, aluminum (Al) and calcium chloride (CaCl2) were used as the collector metal and flux for the reduction, respectively. A mixture of Sc2O3, Al, and CaCl2 in a tantalum crucible was placed inside a stainless steel reaction container, and the feed mixture was reacted with calcium (Ca) vapor at 1273 K for 6 h. After the reduction experiment, the reaction product (CaO), CaCl2 flux, and excess Ca reductant were removed from the obtained alloy sample by leaching with an aqueous solution. The formation of Al3Sc in the Al matrix phase of the alloy was confirmed by X-ray diffraction (XRD) and electron microprobe analysis (EPMA). This result indicates that Sc2O3 was successfully reduced to metallic Sc and alloyed in situ to form liquid Al-Sc alloy during the reduction. When Al was not used in the reduction experiment, a complex oxide (CaSc2O4) was formed, and the reduction was incomplete. This study demonstrates that the Al-Sc alloy can be directly produced by calciothermic reduction using CaCl2 flux and Al collector metal.

Jan 1, 2006

The merging of flash smelting with spray converting in one single furnace is proposed as a continuous copper making process. The proposed process is expected to produce blister copper, clean slag and gas with high sulfur dioxide concentration. Some high grade matte is an intermediate product recycled within the proposed furnace, spray-atomized and converted. The thermodynamic equilibria of the simultaneous oxidations which take place during copper smelting and converting are discussed in order to establish the gradient of oxygen potential along the furnace required for smooth operation. The proposed process is a dynamic system designed to reach equilibrium only close to the slag skimming end of the furnace. The process feasibility is based on the predesigned significant difference between the rates of converting reactions in a finely dispersed system and the rates of deconverting reactions between immiscible liquid phases of restricted interface area. The converting of small stationary droplets of matte, in a silica saturated system, was studied in the laboratory for extremely short oxidation times (10 to 120 seconds). These experiments led to some interesting observations on reaction mechanisms and kinetic trends. The droplet size and the matte grade affected very strongly the oxidation rate and the proportion of the different products obtained.

Jan 1, 1976

By H. Sieber

Multilayer samples of tantalum and aluminum with the composition of Al-25Ta were prepared by cold rolling of elemental foils. The microstructure and phases were characterized by XRD, SEM and TEMISAED and the reactive phase formation was examined by DSC and DTA measurements in multilayer foils rolled for different deformation levels. The rolling procedure yields a decrease of the Ta particle size in the Al matrix and also results in the formation of a multilayer structure with a thickness of the elemental foils down to 200 nm in average. No phase formation is observed during the cold rolling procedure. While XRD and DSC measurements show no phase formation up to the melting of aluminum for samples rolled up to 40 F&R (fold and rolling) passes, in samples rolled for 50 or more F&R passes a first phase formation reaction yield an interfacial layer of TaAl3. Contrary to former studies in the investigated cold rolled Al- 25Ta multilayers the reaction starts at temperatures as low as about 340°C. The first stages of the reaction are associated with two exothermic maxima, that increase in amplitude and shift to lower temperatures with increasing number of F&R passes. At higher temperature the TaA13 reaction layer thickens very sluggishly and yields a third exothermic maxima at about 600°C. Isothermal DSC scans show the reaction is not finished for samples containing elemental particles larger than 1 pm after annealing at 550°C for 5h. In all the investigated samples no Al- Ta phase other than Tad3 was observed to grow for heat treatments up to 800°C. Multilayer samples heated up to 1400°C show a morphology consisting of small AITa2 particles embedded in a single phase TaA13 matrix. The multilayer microstructure and reaction product morphology are characterized by SEM and TEM investigations in cross-section and plan view geometry.

Jan 1, 1998

By K. C. Chou

The surface effect is one of fundamental topics in physical chemistry that has been studied over decades. However, its effect has been neglected in metallurgy researches and industry applications in the past years. With the progress of science and technology in metallurgy, the consideration of surface effect to the metallurgical processes has been paid more and more attention. In this report, it is shown that, how this factor affects the physicochemical properties of metallurgical processes and how to derive some new and more correct theoretical formulae for its application. Besides, some new technique related to the application of this factor in the experiment has also been developed for both fundamental research and industry applications. It is hoped that these progresses will promote some new developments both in fundamental and industrial applications for metallurgy processes.

Mar 1, 2017

By K. Morsi, S. K. Kassegne, A. El-Desouky, K. S. Moon

"Current Activated Tip-based Sintering (CATS) is a new process for the powder-based fabrication of macro, micro and possibly nano-scale features and shapes. This new and unique process enables selective sintering of powders by localizing electrically activated sintering conditions through a stationary or moving electrically conducting tip. We present preliminary experimental results on the effect of tip size in the CA TS process as well as the effect of initial powder particle size on the sintering behavior of nickel powder.IntroductionSpark Plasma Sintering (SPS) has been the center of attention of numerous researchers due its noticeable advantages over conventional sintering techniques such as rapid heating rates, lower sintering temperature and shorter holding times. Research on SPS has been applied on a wide variety of materials such as pure metals [ 1], ceramics [2], composites [3], nano-materials [ 4], biomaterials [ 5], shape memory alloys [ 6] and many other material systems. However, it has been mostly limited to bulk materials with simple shapes with a few exceptions ofresearch efforts where the effect of electric current was combined with metal forming processes such as spark plasma extrusion [7,8] and electric rolling of powders[9]. In this paper a novel process (Current-Activated Tip-Based Sintering (CATS)) is discussed where electric current and pressure are applied simultaneously through a small conducting tip (stationary or moving) over a conducting powder compact. This process has the potential advantages of sintering complex geometries with minimum energy requirements as unconventionally high current densities can be achieved due to the small contact area between the tip and the powder compact. Furthermore, by controlling the tip size, it can be possible to sinter features on the macro-, micro- and even nanoscales."

Jan 1, 2011

By Niander A. Cerqueira, Afonso G. Azevedo, Mairyanne S. Souza, Victor B. Souza, Victor T. Bartolazzi, Igor W. D. C. Pereira, Rondinelli C. Ribeiro

The common glass machining process used in the market of Brazil’s civil construction generates tons of waste through the folder of that waste disposal out by the water used during machining. After drying the product is intended for landfill representing a great environmental liabilities since these deposited glass waste in the environment have a decomposition time greater than four thousand years due to its high chemical and mechanical resistance. Aiming to give a destination that addresses this waste disposal problem in the environment, much has been studied in an attempt to incorporate them into the mix cement to partially replace the sand. In this work it was decided to carry out specific studies using common traits comparing the stroke with sand with a dash with partial replacement of 30% of the sand for the glass machining residue was analyzed resistance compressive resulting in a potential good product.

Mar 1, 2017

By Leiv Kolbeinsen, Stian Seim, In-ho Jung

"The current work presents new experimental data in the iron-unsaturated region of the FeTiO3-Ti2O3-TiO2 slag system. The samples are prepared by melting pure reactants in a high frequency induction furnace that employs a cold crucible. A similar experimental set-up has been described in literature and proven suitable to investigate high titania slags. The FeO content of the samples range from 3.7 to 21.8 wt% and the Ti2O3 content range from 3.6 to 30.1 wt%. The liquidus temperatures of the samples are measured in-situ by a spectropyrometer and range from 1450 to 1645 °C.In addition, an improved thermodynamic database for the FeO-Ti2O3-TiO2 system has been developed. Ternary parameters have been included and optimized to fit previously published experimental data. This optimization minimizes the discrepancy between experimental data and thermodynamic calculations as previously discussed in literature. New liquidus projection plots are proposed for the FeO-Ti2O3-TiO2 and the FeTiO3-Ti2O3-TiO2 systems.IntroductionIlmenite (FeTiOs) smelting is a relatively small industry world-wide. However, a reasonable focus on the process has been applied in Norway due to the location of one such smelter in Tyssedal, which is located in the western part of Norway. The process is essentially carbothermal reduction, where most of the iron in the ilmenite is reduced to its metallic state, and the titanium oxide is concentrated in the slag product. The metallic iron is sold as a high purity pig iron and finds applications in cast products. The slag concentrate is further processed for the production of TiOvpigment and/or titanium metal. This further processing can be performed through different routes according to the purity of the slag concentrate."

Jan 1, 2012

By J. M. Figueiredo, A. R. Silva, M. C. Coelho, R. M. Guedes

"With the continuous depletion of conventional sources of non ferrous metals, low grade complex sulphide deposits have been regarded as an alternative source of supply of zinc, copper, lead and also silver and gold. In spite of very important efforts in research in this domain it is still a long way to go in order to achieve reliable technological solutions both in ore dressing and metallurgical treatments which enable these complex materials to be regarded as commodities. The RLE process to treat bulk concentrates such as those obtained from portuguese ores, under development at LNETI and QUIMIGAL premises, combines experienced unit operations and innovative configurations and is an effective contribution for the future use of these materials. The results of three years of experimental work and main conclusions on the overall feasibility of the process are presented.IntroductionIn spite of the very well-known problems associated to the development of complex sulphide deposits, the economical importance of the enormous reserves of these materials, widespread all over the world, is so evident that its future use as source of supply of basic and precious metals and other minor elements is almost unavoidable.Critical steps in that direction are mainly concerned with favourable economical conditions and sound metallurgical practice for the treatment of nonferrous metals concentrates, which are nowadays still considered as non-conventional raw materials.Since Portugal is one of the countries where these orebodies occur more extensively, Portuguese authorities have dedicated since the beginning of the seventies, a big effort on finding economical and reliable processes for the recovery of copper, lead, zinc and also gold and silver, and for this purpose, several alternatives on ore dressing and metallurgical processing were studied, however without full sucess.Five years ago LNETI, a research laboratory, and QUIMIGAL, a chemical company, both state owned, decided to launch a research programme for the development of a metallurgical process for the treatment of NFM concentrates, which received financial support from NATO under its programme ""Science for Stability""."

Jan 1, 1988

By Florian Kongoli

"Lime ferrite" slag with limited silica content has proven to be a valuable choice in the modem processes of copper smelting and converting due to several advantages that this slag offers compared to classical silicate slags. Nevertheless the liquidus surface of this slag has been experimentally measured only at low oxygen potentials such as in equilibrium with iron or near it and in air. Although most of the smelting and converting processes that use this slag occur at intermediate oxygen potentials, the liquidus surface of this slag is not known at these conditions and the effect of oxygen potential and silica has not been correctly understood. This has brought some confusion in literature as well as in the industrial practice. In this work the liquidus surface of the calcium ferrite slags has been quantified by the means of a new thermophysicochemical model and a new type of liquidus surface diagrams which are very convenient for any industrial process that uses calcium ferrite slags. These diagrams can be easily used to select the lowest liquidus temperature of calcium ferrite slags at a minimum cost and can help design several fluxing strategies in copper smelting and converting processes. The effect of the oxygen potential and silica is also quantified and important industrially related conclusions are drawn.

Jan 1, 2003

By P. Louis

Gécamines is the world largest cobalt producer with about 60 % of the Western World production. During the last ten years, its annual production varied from 5,400 to 14,600 t/year. The actual cobalt production capacity of Gécarnines is 18,000 t/year and could be increased in the near future if necessary. Cobalt is presently produced at the Shituru plant by an old in-pulp electrolysis process and in Luilu, by electrolysis of a clear weakly acidic solution. The Shituru Cobalt quality is lower than the Luilu one. For that reason, part of the Shituru Cobalt is fire refined and cast into granules. Large efforts have been succesfully accomplished to improve the cobalt quality. This has been made possible by a better knowledge of the purification processes and of the electrolysis parameters.

Jan 1, 1988

By Florian Kongoli

"Lime ferrite" slag with limited silica content has proven to be a valuable choice in the modem processes of copper smelting and converting due to several advantages that this slag offers compared to classical silicate slags. Nevertheless the liquidus surface of this slag has been experimentally measured only at low oxygen potentials such as in equilibrium with iron or hear it and in air. Although most of the smelting and converting processes that use this slag occur at intermediate oxygen potentials, the liquidus surface of this slag is not known at these conditions and the effect of oxygen potential and silica has not been correctly understood. This has brought some confusion in literature as well as in the industrial practice. In this work the liquidus surface of the calcium ferrite slags has been quantified by the means of a new thermophysicochemical model and a new type of liquidus surface diagrams which are very convenient for any industrial process that uses calcium ferrite slags. These diagrams can be easily used to select the lowest liquidus temperature of calcium ferrite slags at a minimum cost and can help design several fluxing strategies in copper smelting and converting processes. The effect of the oxygen potential and silica is also quantified and important industrially related conclusions are drawn.

Jan 1, 2003

By Khalid Hattar, Alexander McGinnis, Buchheitm Thomas, Paul Kotula, Luke Brewer

"Understanding the effects of extensive radiation damage in structural metals provides necessary insight for predicting the performance of those metals considered for application in the extreme radiation environment. Predicting mechanical performance after long term radiation exposure is of great importance to extending the life of current nuclear reactors and for developing future materials for the next generation of reactors. A combination of finite element modeling, nanoindentation, and TEM characterization were used to rapidly determine the microstructure and mechanical properties influences of ion irradiation on a standard 3 l 6L stainless steel sample. The results of this study found that ion irradiation and small scale mechanical property testing can be used to characterize extensive levels of radiation damage structure, only when significant consideration is given to ion irradiation depth, surface roughness and polishing condition, the irradiation temperature, and many other experimental parameters.IntroductionFor either the success of next generation nuclear reactors or the extension of current nuclear reactors significantly beyond their designed lifetimes, research is needed into the degradation of the microstructure and mechanical properties governing the performance of the reactor alloys exposed to extreme environments. Although the exact dose and temperature of these nuclear reactor plans may vary, the cladding and other structural components will be exposed to greater dose and at elevated temperatures. To acco=odate these severe exposures, established cladding materials are being testing to longer exposure and new alloy compositions are being considered. [1-3] For neutron test facilities to reach 100 dpa level, exposure times often span several years, significantly limiting the down-select process of potential new materials for extreme radiation environments. Ion irradiation has been used as a technique to provide a look at the effect of irradiation damage on materials in a significantly shorter time frame. Previous work using proton irradiation provides a deep, broad, and relatively uniform defect profile compared to heavy ion irradiation; however, using this type of radiation still requires weeks to months to reach the 100 dpa level. [4] In this research, we investigated the feasibility of using heavy ion (nickel) irradiation and small scale mechanical testing to provide in a few days a first order screening technique for potential alloys that are being considered for advanced testing."

Jan 1, 2012

By Min Chen, Lei Xu

Sintering behavior and performance of high alumina refractory based on the ternary subsystem MgAl2O4-CaAl4O7-CaAl12O19 were investigated using ZrO2 as an additive up to 8 wt.% by solid state reaction sintering. It was found that the added ZrO2 could dissolve in the CA6 grains in the form of a solid solution, which enhanced the isotropic growth of CA6 grains and then improved the sintering. As a result, the densification process was improved and areas with enrichment of ZrO2 showed a more compact structure. With further increase of ZrO2 addition, tetragonal ZrO2 were found to locate in the grain boundaries for exceeding the solid solubility limit, which enhanced the thermal shock resistance, indicating that addition of ZrO2 exhibited a positive effect on sintering behavior and performance of this refractory. In addition, it is considered that the optimal amount of ZrO2 addition was about 4% considering the performance together with the cost.

Jan 1, 2015

By Raymond F. Dalton

Despite the ready availability of numerous zinc sources, the process of solvent extraction- electrowinning (SX-EW) has as yet found little favour in the zinc industry. It is suggested that this is largely due to the previous lack of availability of suitable selective reagents having the particular features required to enable them to fit in to a solvent extraction-electrowinning based process for zinc, particularly with regard to strength and selectivity for zinc over iron. This paper describes work on the development of new selective extractants for the recovery of zinc from both sulfate and chloride aqueous solutions and suggests how they might be integrated into new zinc processes.

Jan 1, 1994

By James M. Lockwood

"Eureka Technology has developed and patented a technology for the recycling of EAFD. Through this process all constituents of the material become salable commodities or are returned to the steel making process. In transforming the EAFD ""waste"" stream into a ""process"" stream the Steelmaker eliminates potential liabilities and the uncertain future of current processes while further reinforcing its role as a recycler. This is a cost-effective and energy efficient technology that combines hydrometallurgic and electrolytic processes resulting in the recovery of salable metals. For instance, unlike pyrometallurgic processes, zinc is recovered in metallic form and no elements are volatilized. This on-site operation also eliminates expensive transportation costs. In summary this technology reduces the cost of dealing with EAFD by recycling material currently being landfilled.IntroductionWorld crude steel production reached a new record level in 2007 - 1.34 billion tons of which 31% was produced by EAF steel makers [1]. This resulted in the generation of over 6 million tons of EAFD. This steel byproduct contains significant amounts of lead, cadmium and other hazardous metals. In the United States the Environmental Protection Agency (EPA) has designated EAFD a hazardous waste (EPA waste code K061). With over 50% of steel production in the US coming from EAF steel making this byproduct represents the single largest source of solid hazardous waste generated."

Jan 1, 2008

By Hongbo Zhu, Jinhui Peng, Linqing Dai

"To optimize the process variables for making direct reduced iron (DRI) by microwave heating, the reduction temperature, reduction time and the ratio of coal to material were studied with the central composite design (CCD) and their interactions on the Metallization rate were also investigated. The predictive polynomial quadratic equations model was analyzed by ANOVA. Optimal conditions of making DRI can be concluded as follows: 28 min at 1139?, the ratio of coal to material is 20.95%. Under these conditions, the metallization rate is up to 97.06%.1. IntroductionThere are some technical problems in making direct reduced iron (DRI) or sponge iron using iron ore concentrates containing coal and lime. In reduction of the iron ore concentrates containing coal with microwave heating, the strength of pellets needn’t to be considered. It reduces the costs and improve quality of materials, but also eliminates the need for pellet preparation process, simplifying the process and achieving a cleaner production.Microwave energy is a clean energy, and has characteristic of selective heating. The speed of heating is also fast. It researched by Chen Jin that when the mole mass of C: O is 0.627 and the microwave power is 15KW, it only spends 15min from 15? to 1021.6? with 1 kg iron ore containing coal with microwave heating [1]. There are many factors affecting metallization rate. In order to find a suitable condition for reduction process, it is necessary to design a series of suitable experiments.Response surface methodology (RSM) is one of the relevant multivariate techniques which can deal with multivariant experimental design strategy, statistical modeling and process optimization [2–5]. It is used to examine the relationship between one or more response variables and a set of quantitative experimental variables or factors. This method is often employed after the identification of the vital controllable factors to find the factor settings that optimize the response. Designs of this type are usually chosen when a curvature in the response surface is suspected. The process optimization of the microwave reduced iron ore was seldom reported in literature. Hence the present work intends to assess the effects of variables such as reduction time, reduction temperature and the ratio of coal to identify the optimum conditions using a central composite design (CCD). The characteristic of product was assessed using scanning electron microscope (SEM)."

Jan 1, 2011

By Zhijing Zhang

Long-term thermal stability of ionic liquids is essential for reliable performance of ionic liquids in any engineering applications. TGA studies were carried out on a series of ionic liquids with different cations and anions such as 1-butyl-3-methylimidazolium chloride ([C4mim]Cl), 1-hexyl-3-methylimidazolium chloride ([C6mim]Cl), 1-hexyl-3¬methylimidazolium tetrafluoborate ([C6mim]BF4), 1-hexyl-3-methylimidazolium hexafluorophosphate ([C6mim]PF6), 1-octyl-3-methylimidazolium hexafluorophosphate ([Csmim]PF6), and 1-butyl-3-methylimidazolium bis(trifluromethanesulflonyl)imide ([C4mim][Tf2N]). The short-term thermal stability of ionic liquids was evaluated by measuring the onset temperature of decomposition of ionic liquids, and the long-term thermal stability of ionic liquids was also evaluated by weight loss of ionic liquids over a long period of time at various temperatures. The experimental results showed that the long-term thermal stability of ionic liquids decreased with increasing temperature and was significantly lower than the onset temperature of decomposition of ionic liquids.

Jan 1, 2002