By Fanke Meng

Electrolyzing oxides of titanium, aluminum and niobium could prepare high-Nb bearing TiAl alloy (Ti-45Al-9Nb) at 1500°C. The chosen electrolysis voltage is 3.5V, which is lower than reducing voltage (~4.7V) of electrolyte CaF2, but higher than that of titanium, aluminum and niobium oxides. The investigation shows that compared with traditional methods, this method for preparing high-Nb bearing TiAl alloy is of many advantages such as few steps, friendly environment, low energy consumption, low cost and high current efficiency.

Jan 1, 2009

By Y. F. Liang

Fe-6.5wt.%Si alloy has excellent soft magnetic properties compared with conventional silicon steel. It is very brittle at room temperature due to appearance of ordered phases, like B2 and DO3. In this paper, we investigate the effect of ordering on cold workability of this alloy. Methods of rapid quenching and hot rolling were utilized. It is found that rapid quenching and proper heat treatment of the hot rolled sheet could decrease the degree of order due to the very high solidification rate and high cooling rate. The rapid quenched sheet and hot rolled sheet after proper heat treatment could be cold rolled without crack. Microstructure, phase ordering, micro hardness, and cold rolling properties were investigated by Optical Microscope, X-ray Diffraction, Micro Hardness Indenter and Four-high Mill.

Jan 1, 2009

By Zhao-cheng Liu

Iron oxide red pigment powders of high quality were synthesized from pyrite cinders. Iron ox-ide red pigment powders were synthesized by hydrothermal method from the precursor of Fe(OH)3 and Fe(OH)2 colloid, which were obtained after ammonia solution reacted with acidic leaching solution produced by the reaction of pyrite cinders with sulfuric acid. Effects of reaction concentration, reaction temperature, reaction time, pH value and n(Fe2+)/n(Fe3+) on main properties of oxide iron red were studied by experiments. The prepared particles were characterized by means of X-ray diffraction (XRD) and scanning electron microscope(SEM). The results revealed that the synthesized iron oxide red particles were _-Fe2O3 and pseudocubic with particle size of 0.50~0.75µm. Furthermore, the quality of iron oxide red pigment powders reached the first grade of national standard (GB1863-89 ).

Jan 1, 2009

By Oluwatosin A. Aladejebi, Apsara S. Jayasekara, Raymond J. Longbottom, Mark Reid, Marc in het Panhuis, Brian J. Monaghan

The coke analogue is a new research tool that has been developed to quantify and characterize the effect minerals in coke have on coke reactivity. The analogue material is made from a number of different carbon or carbon containing materials and minerals to in part replicate real industrial coke’s reactivity behavior. Elucidation of the effects of minerals on coke reactivity has proved difficult due to the complex and heterogeneous nature of industrial coke and the potential non-additive effects of minerals on coke reactivity. The coke analogue addresses this complexity and heterogeneity through control of its mineralogy, mineral size and mineral dispersion through the analogue, porosity and carbon structures. Initial studies using the analogue were focused on coke dissolution kinetics in liquid iron but recent work has focused in characterization of its porosity, carbon structure and rate of reaction.

Jan 1, 2014

By Linli Wu

During the measurement of contact angle, a misty band was observed near the substrate. Hsien-Nan Ho and Shinn-Tyan Wu thought this was because the oxygen atoms on the interface migrate to the droplet surface to form an oxide band near the substrate. But from our experiments misty band appeared before the drop reach to the substrate. Theoretically speaking, the oxygen partial was the same everywhere in the vacuum furnace. So there was no condition to provide enough oxygen forming oxide. This appearance would be explained more reasonably with the optics principle. Most reflected light would be absorbed by the substrate and the light cannot reach the observation area, so the misty band formed.

Jan 1, 2006

By Qingzhu Li

The brewing industry byproduct, spent grain (SG), was evaluated for its ability to adsorb Ag(I) from aqueous solutions. Ag(I) adsorption was dependent on solution pH, contact time, adsorbent dose, initial Ag(I) concentration and temperature. The kinetic data were well described by pseudo-second-order kinetic model, indicating that chemical adsorption was the rate-controlling step. The equilibrium data followed Freundlich isotherm rather than Langmuir isotherm, suggesting heterogenity of the adsorption sites on spent grain. Ag(I) desorbed from Ag(I)-loaded spent grain was also evaluated in this study. HCl, NaOH, Na2S2O3 and ultrapure water were chosen as eluants and desorbed Ag(I)-loaded spent grain for 30min, Ag(I)-loaded spent grain desorbed in 0.1M Na2S2O3 exhibited higher elution efficiency as compared with other eluants. The results indicated that application of spent grain for adsorption and recovery of silver from aqueous solutions was feasible.

Jan 1, 2009

By C. E. M. Meskers

Electronic and Electric Equipment contains a range of components made of a wide variation of metals, plastics and other substances. Up to 60 elements can be found in complex electronic equipment: base metals, precious metals and special metals in circuit boards and batteries. Because of its amount WEEE represents a considerable metal resource with a higher special and precious metal content than found in ores. The Umicore integrated smelter and refinery recovers and supplies back to the market 17 different metals from EEE. Pre-treated materials enter state of the art, material and energy efficient metallurgical processes for environmentally sound recovery of metals and treatment of off gasses and hazardous substances. The organics in the feed function as reducing agent and alternative energy source during smelting for precious metal recovery. Lithium-ion batteries are treated using a dedicated process. As a result the environmental footprint of metals produced from EEE is much smaller than primary production.

Jan 1, 2009

Gas-liquid contacting in the packed bed is a common operation in metallurgical reactors. Research has shown that, unlike wetting flow, non-wetting liquid flows in the form of discrete droplets or rivulets. Thus, modeling of the liquid phase as a continuum is in contradiction to the observations. Also, for the non-wetting case, continuum models have failed to describe liquid flow path when the liquid source is a point source. The aim of the current work is to put forward a combined Lagrangian-Eulerian approach to model the liquid and gas flow in the packed bed. Liquid is assumed discrete and modeled using a force balance approach. Gas is assumed to be interpenetrating continua and modeled using k-emodel for turbulent flow. Structured packing is assumed and x- ray imaging technique is used to visualize liquid flow lines in the bed. Simulation results for liquid flow path compared with the experiments.

Jan 1, 2006

By Qing Bo

In this study, the cobalt oxide precursor was prepared in open-style reactor in the condition of high reactant concentration, and then the precursor was decomposed to obtain the cobalt oxides (Co3O4). The effects of some factors on the cobalt precipitation, the particle size and size distribution, and the micro-morphology were addressed. The factors studied include cobalt concentration, initial pH of solution, temperature and time for the reaction, the charge amount of urea, and the temperature for decomposition. It is determined that the precursor particle is in the chemical composition of Co2(OH)3Cl with fine crystalline. By calcinations under proper conditions, the mono-dispersed cobalt oxide particles were prepared with fine crystalline, about 2 µ m in particle size and regular shape in morphology.

Jan 1, 2006

By Bowen Li

Andalusite is an excellent raw material for refractory applications due to its high aluminum oxide content and phase transformation to mullite at high temperature. Granular andalusite in particle sizes of about 1 to 2 mm was traditionally utilized for the manufacturing of refractory brick. However, if powder andalusite in micron particle size is utilized in high-alumina refractory products, reinforcement on the refractory brick can be obtained and the sintering temperature can be decreased. The phase transformation of powder andalusite plays a key role for the difference.

Jan 1, 2006

By Ram Avtar

High tensile thick plates (>80mm, weight ~3000 Kg) of medium carbon low alloy steel, when heat treated, manifested higher percentage of crystalline area (>20%) in fractured surface. Such problem was not encountered in thinner plates. The genesis of higher crystallinity in fracture was examined. It was observed that the thicker plate undergone slower rate (Average 0.9oC/Sec.) from soaking temperature to Ms temperature) of cooling after austenising during oil quenching and thereby quenched microstructure had upper bainites. During tempering of as quenched bainite, additional precipitation took place at the lath boundaries of bainite. This led to weakening of grain boundaries and aided easy crack propagation during fracture and resulted in formation of higher percentage of crystalline area in fractured surface. Enhancement in cooling rate (Average 1.8oC/Sec. from soaking temperature to Ms temperature) of austenised plate by switching over from oil quenching to water quenching practice resulted in complete transformation of austenite into martensite and produced ductile fracture (zero Crystallinity). Plates conformed improvement in mechanical properties between 2-5%.

Jan 1, 2009

By Chuanlin Fan

The process of flotation separation and recycling of spent potlining (SPL) was described. On the basis of the laboratory investigations, the effects of influencing factors in froth flotation process, such as grain size, flotation agent dosage, pH value, pulp density, and dissolved components concentration, etc, were carefully studied. And the influence on environment of the process was also discussed. It was found that flotation separation can be used as an environment-friendly method for treatment of SPL residue. Carbon and other compounds (include cryolite, sodium fluoride, calcium fluoride and diaoyudaonite, etc.) from SPL were separated and recycled as flotation products respectively.

Jan 1, 2009

By Olga Frank-Kamenetskaya

The experimental results of study of atmospheric corrosion processes on Saint-Petersburg bronze monuments surface, received in situ and by means of simulating experiments, have been discussed. Influence of the time factor on corrosion film (patina) mineral composition has been analyzed. Direct dependence between patina mineral composition and environmental conditions has been proved. The sequence of patina phases crystallization has been established. Effect of the chemical composition and heterogeneity of artistic bronze and also monument surface structure on the rate of corrosion process has been regarded. The time variations of mass of the crystallized in the hydrochloric acid vapor phases have been investigated. The kinetic laws of their development at the initial stage of formation, indicating simple (non chain) reactions, have been revealed.

Jan 1, 2006

A three?stages countercurrent fluidized bed prototipe reactor to neutralize the SO2from smelter gases has been developed. For gases with 8 vol-%SO2, at 800°C and for 4 h mean reaction time of the limestone, the capture of SO2 is 99%, with off gases with 0.07 vol-%. For 2 vol-%SO2, the total capture of SO2 can be obtained at 750°C and 4 h reaction time. The calcine obtained contain a blend of unreacted limestone and calcium sulphatewith minor amounts of residual lime.

Jan 1, 2006

By Gábor Csicsovszki

We have developed a novel method - at the laboratory scale - comprising an ion-exchange separation and a membrane-electrolysis step for the purpose of zero-waste regeneration of spent HCl pickling liquors originating from hot-dip galvanizing of common steels. It is aimed at the parallel regeneration of HCl and iron. Experiments revealed that iron can be electrodeposited at high current efficiencies by maintaining the following conditions: 0.04-0.08 M HCl, 500-1000 A/m2, 20°C and stationary electrolyte in a conventional cell. Zinc in the solution did not disturb the deposition of iron, however it contaminated the product and it poisons the anion-exchange membrane required to tackle acidity during electrolysis. For a preliminary separation, anion-exchange tests were carried out to produce pure iron solutions. Beyond the equilibrium studies, column experiments were carried out showing that low flow rates of the loading solution and the ~1.5 M HCl eluent are essential for separation.

Jan 1, 2006

By Taegong Ryu

Nanosized tungsten powder was synthesized by the hydrogen reduction of ammonium paratungstate (APT) in thermal plasma. The effects of operating conditions on the product composition and particle size were investigated. The particle size of synthesized W powder was less than 30 nm in all cases tested. The sintering behavior of the synthesized powder (25 nm average size) was then investigated and compared with those of commercial W powder of 500 nm average size and W powder of 23 nm average size produced by milling the commercial powder. The sintering was done at 1400oC with various holding times. The hardness of the resulting compact from the synthesized W powder (315 VHN) was similar to that from the milled W powder (309 VHN), but the plasma-synthesized powder had a much lower tendency to form cracks. The compacts of both nanopowders were significantly harder than that of the commercial powder (192 VHN).

Jan 1, 2009

By Z. Sun

Magnetic fields have been used for inclusions removal from melt and preparation of materials with gradient compositions. Fundamental in these applications is that the induced magnetic forces on the particles/melt can enhance migration and change the interaction behavior. In the present paper, migration and interaction behavior of electrical-insulating particles in a conductive melt under strong magnetic field are theoretically analyzed. It is found that the migration can be considerably enhanced for micrometer sized particles by applying a strong magnetic field. In addition, two forces are involved in the interaction between two particles: the interparticle magnetic dipole-dipole attractive force due to magnetization and the repulsive force induced by flow of the melt. This theoretical analysis renders a better understanding of recent experimental results. Additionally, a new method by using strong magnetic field can be proposed to control the particle size distribution for the preparation of metal-matrix composites.

Jan 1, 2009

By Wilson Acchar

The accelerated growth of urbanization processes and current environmental concerns brought to light the existing enormous quantity of construction and demolition waste (C&DW). Considering the frequent lack of adequate landfill areas available for the disposal of these materials, their use in the manufacture of ceramic products has been attracting a growing interest from researchers and is becoming common practice, with the consequent relief in public administration concerns for the C&DW appropriate management. This work describes the study of clay-based products added with C&DW collected directly from the construction industry. Samples containing up to 50 wt.% C&DW were uniaxially pressed and sintered in air in an electric furnace (950-1150 °C, 1 hour). Sintered test pieces were characterized by X-ray diffraction, apparent density, open porosity and flexural strength. The results showed that up to 50 wt.% C&DW can be added to the clay material, with no degradation in the final product properties.

Jan 1, 2009

By Fathi Habashi

While it is commonly known that the precious metals and to some extent copper occur in the native state, it is less known that mercury, iron, nickel, and cobalt do occur also in the native state; the last three (Fe, Ni, and Co) usually occur together in form of an alloy. The particle size varies greatly from less than 10 microns (gold and mercury) to about 400 tons boulders (copper).

Jan 1, 1993

By Chang-Dong Li

Cadmium ingot and nickel powder were prepared by high-temperature distillation, solvent extraction and liquid phase reducing method with spent Cd-Ni batteries as raw material. The impacts of the temperature in the distilling stage, the concentration of H2SO4 in the leaching stage, the pH value in the extracting stage and the dosage of hydrazine in the reducing stage were discussed respectively. The as- prepared samples were characterized by the means of X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic absorption spectrometry (AAS) and inductively coupled plasma-atomic emission spectrometry (ICP-AES). The results showed that the recovering efficiencies of Cd and Ni reach 99.5% and 99.3%, and the purities of Cd ingot and nickel powder were higher than 99.90% and 99.80%, respectively.

Jan 1, 2009