By R. I. Jaffee, H. R. Ogden, D. J. Maykuth

Phase diagrams for the Ti-W and Ti-Ta systems were determined. The Ti-W system is characterized by a wide, two-phase region of ß plus tungsten which is derived from a peritectic reaction between the liquid and tungsten solid solutions. The ß field terminates in a eutectoid reaction between a titanium and tungsten terminal solid solution. Tantalum and ß titanium form a complete series of solid solutions. Other features of this system are the extensive a-ß field at low temperatures and an appreciable solubility of tantalum in a titanium. BOTH tungsten and tantalum were first thought to form ß-isomorphous systems with titanium as a result of early work' using powder-metallurgical techniques. Later work2 on arc-melted Ti-Ta alloys, made using a commercial titanium base, showed that, in the range of 0 to 10 pct, tantalum was soluble in ß titanium and that the a solubility extended to between 2 and 5 pct Ta at 790 °C. The present investigation covered the entire alloy range in both systems and was chiefly concerned with high-purity alloys at the titanium-rich end. The constitution of titanium-rich alloys made with a commercial titanium base was reported by Holla-day, Kura, and Jackson.3, 4 As will be shown in detail later, the early prediction of a isomorphism was true for the case of the Ti-Ta system, but not for the Ti-W system. The results of this investigation will be presented first. The experimental methods used are described in the Appendix. Ti-W System The entire Ti-W phase diagram is shown in Fig. 1. Details of the titanium-rich side are shown in Fig. 2. The chief features of the system are a ß eutectoid and a high-temperature peritectic between liquid and tungsten solid solution. Melting Range: Examination of cast structures of low and medium-tungsten-content ingots showed cored ß phase as the primary constituent. Fig. 3a illustrates a typical cast structure for alloys in the range of 20 to 30 pct W. From 30 to 72 pct W, coring was very severe. Alloys containing 72 through 88 pct W, however, showed definite evidence of a peritectic reaction between the liquid and a terminal solid solution of titanium in tungsten. Fig. 3b shows the cast structure for an 80 pct W alloy. A 95 pct W alloy, shown in Fig. 4, consisted primarily of primary tungsten solid solution plus a small quantity of ß probably rejected during cooling. Incipient-melting experiments located the peritectic temperature between 1850" and 1900°C and indicated that the reacting phases are liquid containing about 25 pct W and tungsten terminal solid solution containing about 8 pct Ti. Figs. 5 and 6

Jan 1, 1954

By I. R. Taylor

Vanadium has recently joined the growing list of mineral commodities being exploited by surface mining methods. Union Carbide Corp. controls several vanadium deposits in central Arkansas near the city of Hot Springs in Garland County and the community of Magnet in Hot Spring County (Fig. 1). Two open pit mines, located approximately five miles southeast of the city of Hot Springs in the Wilson Springs area, have been developed for production during the past two years. Adjacent to the mining area the company has recently completed a 1,600-ton-per-day (tpd) processing plant to treat the Wilson Springs and Magnet Cove ores (Fig. 2). Although this operation constitutes the largest vanadium mining project in the United States, the open pit mines are of moderate size. A number of small to medium-sized surface mines will be developed during the life of the operation. This chapter describes the methods and practices used to bring these recently discovered vanadium deposits into production. PRELIMINARY EXPLORATION The vanadium potential of the deposits near Hot Springs and Magnet Cove was first investigated by Union Carbide Corp. in 1960. These areas have long been of interest for their varied mineral content and were previously explored by government agencies and private interests for titanium, columbium, molybdenum, and uranium. No sustained operations resulted from this early work, although the rutile deposits of Magnet Cove were worked intermittently between 1911 and 1944.l Significant vanadium concentrations were reported in a U.S. Bureau of Mines publication describing the investigation of a titanium prospect

Jan 1, 1969

By C. W. Mueller, P. H. Robinson

A technique was developed for depositing single -crystal films of silicon on single-crystal sapphire substrates via the pyrolytic decomposition of SiH4/H2 mixtures. Electron diffraction and X-ray Laue reflection examinations of these films revealed single-crystal patterns. These films were characterized by measuring conductivity type, thickness, resistivity, and Hall mobility. Chemical etching, dislocation staining, and electron-microscopy examination have indicated the presence of low-angle grain boundaries and microtwinning in the silicon films. The role of the sapphire substrate with respect to its quality, orientation, surface finish, and thermal and chemical treatment was investigated. Hall mobility as a function of sapphire orientation was measured. A mobility equal to 88 pct of bulk silicon mobility was attained. Insulated-gate field-effect transistors which have a transconductance of 4000 pmho at 6 ma were fabricated using these films. THE technology of the fabrication of microelectronic circuits with active and passive components directly on a single wafer of semiconductor material has attained a high degree of perfection during the last few years. One inherent difficulty with the single-wafer approach has been undesirable coupling between components arising from the common base material. Several techniques have been developed for minimizing this coupling and obtaining good electrical isolation between components; however, these result in extra capacitance being added to the circuit. The extraneous capacitance of the connecting leads, resistors, and capacitors degrade circuit performance and limit the high-frequency operation of these circuits. Recently there has been considerable interestl-3 in the deposition of silicon films upon insulating substrates. The use of silicon as the semiconductor allows the subsequent utilization of the large amount of technology which has been developed for silicon for the fabrication of good active components. A sapphire substrate supplies an excellent insulating material which at the same time gives a thermal-conductivity improvement of an order of magnitude over glass-type substrates. This paper will describe the results obtained for the deposition of single-crystal silicon layers upon single-crystal sapphire substrates as well as the characterization of these films. I) APPARATUS The 'system used for the growth of silicon films on sapphire substrates by means of the pyrolysis of SiH4/H2 mixtures is shown in Fig. 1. The all-quartz reaction chamber is water-cooled and includes a quartz optical-flat window for use in conjunction with a 5 kw, 2.5 Mc per sec constant-temperature controlled rf generator. The temperature sensor for the rf generator is a thermopile which is focused through the quartz optical flat onto the susceptor surface. With this system the rf generator will hold the temperature of the susceptor to about +0.3°C at 1200°C. The susceptor is supported on a quartz sled inclined to the gas flow to increase the uniformity of the deposition. The water jacket surrounding the reaction chamber is used to keep the quartz wall temperature low enough to limit the decomposition of the silane to the rf-heated susceptor which contains the sapphire substrates. This eliminates the reaction of silicon with the hot quartz to form SiO which deposits out on the apparatus walls, thus obscuring vision, and interferes with the optical measurements of the temperature as well as with the growth process itself. Provision is also made for "n"- and 'p"-type doping by using mixtures of either phosphine or diborane in hydrogen which are added to the silane during the growth process. The hydrogen used is the purest commercially available tank hydrogen further purified by use of a palladium diffuser. The susceptors which were used include 1) spectro-scopically pure graphite, 2) high-purity molybdenum, 3) high-resistivity silicon using a low-resistivity insert to facilitate coupling to the rf generator, 4) silicon carbide-coated graphite. The latter two susceptor materials produced silicon films on sapphire substrates with more reproducible resistivities. Prior to silicon deposition all connecting lines as well as the reaction chamber are thoroughly flushed with argon and then hydrogen. After the hydrogen flow is set, the growth temperature is adjusted to 11009 to 1150°C, and when thermal equilibrium is reached the silane flow is started. The flow rate of the hydrogen must be fast enough so that turbulent flow occurs in the size of reaction tube used, otherwise a streaked nonuniform silicon deposit occurs. After the deposition

Jan 1, 1967

By G. L. Oldright

THE development of the reverberatory furnace for smelting copper ores up to 1912 was described by E. P. Mathewson1 with details concerning the great changes in dimensions of the furnace. Hayward2 tabulated similar data, giving developments up to about 1924, in his revision of Hofman's Metallurgy of Copper. DEVELOPMENT OF PRESENT SMELTING PRACTICE Dimensions of Furnace Very great changes were made in the dimensions of the smelting hearths of the furnaces in the period from about 1800 to 1906, the length increasing from about 11 to 116 ft., and the width from 8 to 19 ft. During this time the tonnage smelted increased from about 9 to 250 tons per 24 hr., and the tons of charge smelted per ton of coal increased from 0.77 to 4.3. Dr. Mathewson3 noted no great difference in the "fuel ratio" (i. e., the amount of charge smelted per ton of coal) as the furnace at Anaconda was increased in length by stages from 85 to 116 ft. (The percentage of copper in the slag, however, was lowered from 0.42 to 0.36 per cent. The other components of the slag were not given.) Lump coal fired on grates was the fuel used during this period. The practice in operating the furnaces over such a length of time naturally varied considerably, and there were differences in composition and nature of the charge, yet it may be considered that the improvements made were due largely to increases in the size of the furnace used. Doubt-less some credit should be given to improvements in operating technique, like changes in the methods of firing the lump coal. However, the greater part of the advance was probably due to factors influencing the

Jan 1, 1928

By E. S. Leaver

The authors of the paper above mentioned have sent the following statement to correct erroneous com-ments and implications in their article with the re-quest that it be published: "In the above mentioned article the reference to Bendelari jigs is used in the generic sense as applying to the mechanically driven diaphragm jigs. No attempt was made to dif-ferentiate between the various machines as installed on different dredges. The Natomas Company use a jig of their own manufacture. The Yuba Company installed the Placer jig as manufactured by the Pan American Engineer-ing Company. "The Pan American Engineering Company also manufactures the Crangle jig under their own name. This is a diaphragm jig in which the pulsations are produced by intermittent flow of water through the patent Crangle Valve and it has no driving mechanism."

Jan 1, 1937

By D. K. Sarin

The sub-level caving mining method has been applied in base metal mines in Canada under a wide range of ore body and wall rock conditions. This method has been used for primary, as well as secondary mining of both small and large ore bodies of varying ore values. Early experiences of almost all operations were somewhat disappointing. This paper details the initial problems encountered, the design changes made and solutions evolved. Additional experience and the development of operating skills, have helped the method gain acceptance as a viable method for the mining conditions to which it has been adopted.

Jan 1, 1981

By F. C. Miller

THE metallurgical fuel of Colorado, Utah, and New Mexico has been a very tardy member in the caravan of western industrial progress. The history of western coke has naturally been closely related to the development of the metallurgy of iron and steel and the precious metals, in the State of Colorado. It was at Leadville, with a population of 300 in 1877, that the Sentinel was published by Richard S. Allen. The Sentinel gave very full accounts of the various mineral discoveries at the new town of Leadville, which found their, way to the more widely circulated journals of the East, and attracted the attention of many people. At the close of 1878, a census showed a total of 5040 persons. The first smelter was established in 1877, at Malta, two miles from Leadville, by A. R. Meyer, but was not successful. It was succeeded by the Harrison Reduction Works, in 1878. The La Plata began with one furnace in June, 1878, and in 1879 had four furnaces in active operation. These furnaces used charcoal for fuel, and, because of hot tops, suffered a tremendous loss in lead and silver. This difficulty was overcome by the erection of 50 single-bank 10-ft. beehive ovens at Crested Butte, Colo., in 1880. The slack coal sent to these ovens was very pure, and yielded a coke carrying as little as 4.5 per cent. ash. Among the pioneers in the Leadville district were Grant, Eddy, James, Billings, Eiler, and Dickson. To these men the West owes the present expansion of its mining industry, and the erection of metallurgical processes for the treatment of precious metals.

Jan 8, 1918

By R. F. Ashton, D. S. Thompson

In reporting results of precipitation hardening experiments, it is customary to include such conditions as solution heat-treatment temperature, specimen size, and quench medium as well as the aging time and temperature. One portion of thermal history that is often overlooked is the effect of the heating rate employed to achieve the aging temperature. It is the intent of this note to demonstrate the importance of the rate of heating to aging temperatures. This work was carried out on the aluminum alloy 7075 aged at 162oC, a temperature commonly used to obtain stress corrosion resistant tempers. A 2 in. thick plate of 7075 was quenched into 24°C water after solution heat-treatment for 2 hr at 470°C. Approximately 13 in. around the periphery of the plate was discarded to minimize quench rate variations, and the remainder was divided into 0.5 by 1.8 by 2.0 in. blocks which were held at room temperature, 24oC, for 4 days. This aging, or incubation period, at room temperature allowed a copious supply of GP-zones to form. Blocks were then heated at various rates to 162oC using the practices shown in Table I. Both single- and two-step aging practices were employed for each heating rate. The single step consisted of heating directly to temperature at the indicated rate while the two-stage practice included an interruption of heating for 7 hr at 107°C. In the case of the two-stage 100°C per min heating rate experiment, the specimens were returned to room temperature after 7 hr at 107°C where they were held for 16 hr be-fore finally heating at this rate to 162°C. This devia-tion in practice is not considered to be significant. Blocks were removed after various times at 162oC, and aging curves were determined from duplicate R. F. ASHTON and D. S. THOMPSON,Member AIME, are Senior Scientists, Metallurgical Research Division, Reynolds Metals Company, Richmond. Va. Manuscript submitted December 2. 1968. IMD Table I. Aging Practices Two-step Single-Step Heating Rate* Aging Aging Heating Method oC per Min A B Programmed Air Oven 0.23 * 0.01 C D Programmed Air Oven 0.93 ? 0.03 E F Air Oven at Temp -10 G H Oil Bath at Temp ˜100 *Heating rate was measured with a thermocouple at the center of a specimen. An average value between the starting temperature and 3°C below the aging temperature is reported for practices E-H. PRACTICES 70 — A B C E and G 50 - 2 4 6 810 20 40 60 HRS.AT 162°C Fig. 1—The influence of processing variables on 7075 aging curves. Fig. 2—7075 aged according to practice H (single-step aged, fast heating rate) for 3 hr. Magnification 100,000 times.

Jan 1, 1970

By W. C. Leslie

The textures of cold-rolled and of annealed iron are compared with those of an iron-0.8 pct copper alloy in which the amount of precipitation after cold rolling was controlled. Previously published pole figures -for cold-rolled and for annealed iron are confirmed. The effects of precipztatiotz after cold rolling are to retain the cold-rolled texture after annealing, to inhibit the formation of the usual allnealing texture, and to produce elongated recrys-tallized ferrite grains. It is suggested that the inhibition of new textures by precipitation after cold rolling is a general phenomenon. A great deal of attention has been paid to the development of texture during the secondary or tertiary recrystallization of ferritic alloys, but very little work seems to have been done on the control of texture during primary recrystallization. If such control were attained, it might be possible to simplify the processing of oriented materials or to change the characteristics of current cold-rolled and an-nealed products. From previous experience, it seemed likely that texture could be controlled by recrystallizing a supersaturated solid solution. Green, Liebmann, and Yoshidal found that the formation of preferred orientation in aluminum (40 deg rotation about <111> relative to the deformed matrix) was inhibited when iron was retained in supersaturated solid solution in the strained aluminum. The authors attributed this inhibition to iron atoms in solid solution. There is, however, an alternative explanation. Green et al, took a highly supersaturated solution of iron in strained aluminum and heated it to an unspecified temperature for recrystallization. It is probable that precipitation occurred prior to and during recrystallization, and it is proposed that the inhibiting agent is this precipitate, rather than the iron atoms in solid solution. It is important to note that precipitation before cold work is ineffective; the effective precipitate is that formed after cold working and either before or during recrystallization. The location and distribution of the precipitate are critical. Precipitation in such a manner has been found to have profound effects upon kinetics of recrystallization and the microstruc-ture of the recrystallized alloys.2-4 It would be surprising, indeed, if this were accomplished with no change in texture. Because of the relative simplicity of the system, and because of previous experience,4-7 it was decided to determine the effect of precipitation on texture in an alloy of iron and copper. Bush and Lindsay5 found an unspecified change in texture in cold-rolled and annealed low-carbon rimmed steel sheets when the copper content exceeded 0.1 pct. MATERIALS In earlier work, the rate of recrystallization of a low-carbon steel was greatly decreased by 0.80 pct copper, and, after the proper treatment, the recrystallized ferrite grains were greatly elongated.4 Accordingly, it was decided to investigate the effect of precipitation on texture at this level of copper content. The iron and the iron-copper alloy were made from high-quality electrolytic iron and OFHC copper, vacuum-melted in MgO crucibles, cast, hot-rolled to 0.2 in., then machined to 0.150 in. The compositions are given in Table I. The plates were heated to 925°C and brine quenched, twice. This produced a ferrite grain size of ASTM 0 in the iron and ASTM 1 in the Fe-Cu alloy. Disk specimens were cut from the heat-treated plates, repeatedly polished and etched, then used to determine (110) and (200) pole figures by reflection. Despite the complication of large grain size, these pole figures strongly indicated a random texture. PROCEDURES The copper content in solid solution in ferrite before cold rolling and recrystallization, and hence, the amount that could precipitate during the recrys-tallization anneal, was controlled at three levels by heat treatment. The specimens as quenched from 925° C were presumed to have all the copper, 0.80 pct, in solid solution. Other samples of the quenched alloy were aged 5 hr at 700°C to retain about 0.5 pct Cu in solid solution.6 A third set of quenched specimens was reheated to 700°C, then slowly cooled in steps, to reduce the amount of copper in solid solution to a very low level. All specimens were cold-rolled 90 pct, from 0.150 to 0.015 in. thick. The rolling was done in one direction only, i.e., the strip was not reversed between passes, with a jig on the table of the mill to keep the short specimens at 90 deg to the rolls. The rolls were 5 in. in diameter and speed was 35 ft. per min. Machine oil was used as a lubricant. In a supersaturated alloy, the maximum effect of the copper precipitate on microstructure and on recrystallization can be developed by a treatment at 500°C, after cold rolling and before recrystallization.&apos;

Jan 1, 1962

By L. Stone, H. Margolin

The Ti-C-N and Ti-C-O systems were investigated in the temperature range from 500° to 1400°C and in the composition range up to 2 pct C and 5 pct N or 0. Characteristic isothermal sections at 800°, 900°, 1000°, and 1300°C are presented. The Ti-N-0 system was studied in the temperature range from 900&apos; to 1400°C with alloys containing up to 6 pct total alloying content. Characteristic isothermal sections at 1000° and 140O°C are presented. Melting-point data for all three systems are also included. THIS paper reports on one of a series of investi-gations which have been conducted on the phase diagrams resulting from interstitial alloying with iodide titanium. The other investigations involved delineation of the binary systems with carbon,&apos; nitrogen and boron,h and oxygen. The Ti-0 binary system has also been investigated by Bumps et al.&apos; In varying degrees, each of these interstitial elements has been shown to stabilize the low temperature a modification of titanium1-5 and each forms a face-centered cubic TiX compound (henceforth designated 6). In addition, the Ti-N and Ti-0 systems reveal a low temperature tetragonal phase (6) formed by a peritectoid reaction between a and TiX Experimental Procedure The development of experimental techniques for the study of titanium alloy systems has, to a large extent, become standardized. In this investigation, the equipment and procedures described in detail by Cadoff and Nielsenl have been used. Arc Melting: In general, binary alloys with carbon, nitrogen, and oxygen, prepared in the composition range of interest in this investigation, show negligible composition changes during arc melting. However, the possibility of the formation of some gaseous combination of alloying elements such as CO, CN, or NO during the preparation of these ternary alloys was considered. Calculations showed that the evolution of only 0.05 gram of such a gas would be detectable as a pressure change in the closed system used during preparation of these alloys. Such pressure changes were not observed. Consequently, nominal compositions have been used in plotting the data. The compositions of the materials used in the preparation of the alloys are shown in Table I. After melting for 3 to 5 min at 275 to 350 amp, the alloys were checked for homogeneity by microstruc-tural examination. Alloys containing up to 1 pct C were homogeneous in the presence of less than 3 pct N or 0. At higher alloying contents, some inhomo-geneities in the carbon distribution became evident. Alteration of the melting procedure toward longer times and higher currents did not improve the homogeneity of these alloys. Ti-N-0 alloys were homogeneous in the range to about 3 or 4 pct total alloying addition. Beyond this, almost all of the specimens showed as-cast microstructures consisting only of the phase. Consequently, inhomogene-ities could not be detected by examination of micro-structures. Ten alloys from each of the systems were analyzed for two of the elements present (oxygen being omitted in all cases and titanium being omitted in the Ti-C-N alloys). In all cases the analyses were found not to be sufficiently precise to serve as criteria for the total composition of these alloys. On the basis of phase distribution in heat-treated alloys, however, it appears that carbon is distributed throughout the alloys most uniformly, with oxygen and nitrogen following in that order. Heat Treatment: Specimens for heat treatment were wrapped in titanium sheet before sealing in the argon-filled quartz capsules. Heat-treatment times varied from 100 hr at 800°C to 0.5 hr at 1400 °C. After heat treatment the specimens were quenched by breaking the capsule in water. With the exception of alloys in the low composition region, heat treatment did not have an appreciable effect on the as-cast microstructures. Metallography: Following heat treatment, the specimens were prepared for metallographic examination by grinding on emery paper and electrolytic polishing. For the majority of the specimens a 10-sec etch with Remington "A" agent (25 pct HNO3, 25 pct Hf, and 50 pct glycerin) adequately

Jan 1, 1954

By Clarence W. Balke

Small buttons of fused tantalum have been produced by are fusion in a vacuum, by drawing an arc between sticks of pressed tantalum and a tantalum-faced water-cooled copper block. However, ingots of appreciable size can be produced only by the heat-treatment of bars pressed from powder. The following outline covering the production of finished bars of tantalum by the methods of powder metallurgy is also used for the production of columbium, taking into account the difference in the melting points of these two metals. Pressing the Powder With possibly a few exceptions, a pressing operation is one of the essential steps in the practice of powder metallurgy. In fact, the author&apos;s experience with a number of high-melting-point metals and with numerous types of hard carbide compositions has led him to believe that this operation is often one of the most important in the entire process, and frequently one of the most difficult to carry out in a satisfactory manner. Defects due to improper pressing can readily lead to a defective finished product. It is the author&apos;s opinion that rarely is a bar or other article pressed from metal powder in such a way that all parts of the piece are uniformly pressed. The nearest approach to uniformity of pressing is possibly attained when the powder is contained in a flexible receptacle, such as rubber, and is pressed under a liquid by hydrostatic pressure. However, this method is not generally applicable. Hydraulic pressing in steel dies where one or two punches are forced into the die must usually be resorted to. As the pressure in such a die is built up, the powder begins to cling to the walls of the die with a tenacity dependent upon the nature of the powder, and this results in a bridging action, so that the layers of powder adjacent to the moving punch are pressed more heavily than those further removed in the mass. Frequently, as the pressure is carried higher, there may be a mass slippage of the powder upon itself, with the result that slip cracks are formed within the pressed

Jan 1, 1938

By Clarence W. Balke

Small buttons of fused tantalum have been produced by are fusion in a vacuum, by drawing an arc between sticks of pressed tantalum and a tantalum-faced water-cooled copper block. However, ingots of appreciable size can be produced only by the heat-treatment of bars pressed from powder. The following outline covering the production of finished bars of tantalum by the methods of powder metallurgy is also used for the production of columbium, taking into account the difference in the melting points of these two metals. Pressing the Powder With possibly a few exceptions, a pressing operation is one of the essential steps in the practice of powder metallurgy. In fact, the author&apos;s experience with a number of high-melting-point metals and with numerous types of hard carbide compositions has led him to believe that this operation is often one of the most important in the entire process, and frequently one of the most difficult to carry out in a satisfactory manner. Defects due to improper pressing can readily lead to a defective finished product. It is the author&apos;s opinion that rarely is a bar or other article pressed from metal powder in such a way that all parts of the piece are uniformly pressed. The nearest approach to uniformity of pressing is possibly attained when the powder is contained in a flexible receptacle, such as rubber, and is pressed under a liquid by hydrostatic pressure. However, this method is not generally applicable. Hydraulic pressing in steel dies where one or two punches are forced into the die must usually be resorted to. As the pressure in such a die is built up, the powder begins to cling to the walls of the die with a tenacity dependent upon the nature of the powder, and this results in a bridging action, so that the layers of powder adjacent to the moving punch are pressed more heavily than those further removed in the mass. Frequently, as the pressure is carried higher, there may be a mass slippage of the powder upon itself, with the result that slip cracks are formed within the pressed

Jan 1, 1938

By Halbert Powers Gillette

In every chemical reaction heat is either developed or absorbed, and this plus or minus heat of formation is as definite in quantity as the weights of the reacting elements. In this paper I shall show that each chemical element and each chemical radical has its own definite heat-valency,—a fact which, so far as I know, has hitherto escaped the attention of investigators, but, I feel sure, will be admitted after the demonstration here given, and may lead to some practical conclusions of value. When Berthelotys " law of maximum work " was found to have so many inexplicable exceptions, the pendulum of a scientific theory swung away from a recognition of the truth underlying that proposition; and this reaction went so far that not only has thermal chemistry been relatively neglected by recent investigators, but it is not uncommon now to find textbooks on physical chemistry which practically ignore all that Thomsen, Berthelot and others have done. To this temporary tendency of thought I attribute the failure to recognize the principles herein announced and explained. Not long ago, while studying tables of the formation-heat of various salts, I noticed that in this respect all potassium salts in solution differ from the corresponding sodium salts by 9.3 cal.1 I found also that similar differences exist between other salts, not only when the basic radical is varied, while the acid radical remains constant, but also when the acid radical is the variable. Thus chlorine salts in solution differ from bromine salts in this respect by 10.9 cal. Upon further study, I found that Thomsen had noted similar constant differences, but, so far as I can ascertain, he appears to have attached no great significance thereto.

Jan 1, 1904

By Walter Snelling

IN the course of some experiments more than five years ago, made for a totally different purpose than the investigation of the oil used, I placed a small quantity of a transparent yellow lubricating oil in a bomb-like vessel and heated it to a relatively high temperature. At the end of the experiment I removed the oil from the vessel and was amazed to find that instead of bearing any resemblance to the oil which I had put in, it now had the appearance of ordinary crude oil. The green color by reflected light and the rich red-brown by transmitted light were so unmistakable as to at once lead to further investigation. I subjected the material to fractional distillation, and the surprise which I &apos;experienced at the appearance of the oil, changed to amazement when I found that it yielded, on distillation, 15 per cent. of gasoline and 30 per cent. of burning oil, and that its constitution resembled crude oil quite as much as did its appearance. Furthermore, the gasoline and kerosene distillates which it yielded were of a clear water-white color, entirely without treatment with acid or alkali, and were entirely free from the odor familiar in "cracked" petroleum distillates. The result of this experiment was quite too remarkable to be credited without further confirmation, and I at once filled the vessel with some of the same oil that I had used before, and again heated to about the same temperature that I had previously used, and for the same period of time. Upon opening the vessel and removing the contents I found, not the material resembling crude oil that I had obtained before, but apparently only the same oil that I had put in, somewhat darkened in color, but nevertheless far different in appearance from the material obtained in the previous experiment.

Jan 4, 1915

By Edward J. Ryan, E. A. Peretti

iV preliminary X-ray and metallographic survey of the ternary system Bi-In-Te revealed that the following isopleths could form quasibinary systems: InTe-Bi, InTe-InBi, InTe-BizTe3, and InzTe3-Bi2Te3. The nature of the InTe-Bi phase diagram was established by Bologna and Peretti.&apos; This article presents the results of an investigation of the InTe-InBi system by thermal analysis, X-ray methods, and metallographic examination. The bismuth and tellurium were bought from the American Smelting and Refining Co. The tellurium had the following spectrographic analysis: 0.0001 pct Mg, 0.0001 pct Si, 0.0001 pct Fe, 0.0002 pct Al, and 99.999+ pct Te (by difference). The bismuth assayed: 0.0001 pct Mg, 0.0001 pct Pb, 0.0001 pct Fe, 0.0001 pct Cu, and 99.999+ pct Bi (by difference). The indium was obtained from the Indium Corp. of America and contained 0.002 pct Cu, 0.006 pct Pb, 0.01 pct Sn, 0.01 pct Zn, and 99.97+pct In. The alloys were made by melting the required proPortions of InTe and in evacuated, sealed quartz

Jan 1, 1967

By A. Keith Brewer

RECENT advances in the fields of chemistry, biology, and metallurgy have confronted the analytical chemist with an entirely new set of problems. Development of plastics and synthetics has brought about a need, not only for adequate methods for their analysis but also for the various raw materials entering into their manufacture. The remarkable advance made in biochemical and agricultural research resulting from the use of isotopes as tracers or "tagged atoms" has established the necessity for the development of methods for the concentration of natural isotopes and for a means for their analysis. Similarly the advent of new and complex alloys calls for accurate analytical methods. Fortunately the analytical chemist has been able to meet some of these new demands by adapting to his purposes an instrument which has long been the most exclusive toy of the physicists. Solubility and the chemical properties of the atoms, which have always served as the basis for chemical analysis, do not enter into this new technique. Instead, momentum, defined as mass times velocity, is utilized as the means for the separation of atoms or mass groups.

Jan 1, 1946

By F. J. Zuiderweg, G. G. Bemer

Results of a study aimed at assessing kinetics and mechanisms of the batch agglomeration process in suspension are discussed. A recently developed light backscatter technique which enables the increase of average particle size from 1 to 5000 µm to be followed, was used to determine agglomeration kinetics. Growth curves and agglomerate size distributions were obtained in a stirred vessel for various model systems and operating conditions. Four distinct growth regimes were identified, i. e. the flocculation regime, the zero-growth regime, the fast growth regime, and the equilibrium regime. Further, it was observed that large differences in the occurrence and duration of these regimes resulted from small variations in parameters, such as size distribution of the initial particles and the binding-liquid to solid ratio. Mechanisms that determine the occurrence of the relevant regimes are discussed. The growth process was described in terms of population balance equations. In this way, the growth rate, the equilibrium agglomerate size distribution, and the evolution of the agglomerate size distribution were generated. The agreement with experimental results is satisfactory.

Jan 1, 1980

By H. C. Lukens, E. V. Potter

The volume of hydrogen released from electrolytic manganese at various temperatures and pressures was determined in a previous investigation1 as part of a study to determine the most practical procedure for removing the hydrogen from electrolytic manganese metal. No attempt was made to determine the absolute volume of gas in the metal at any temperature and pressure; the volume of gas released showed only the variation in solubility with temperature and pressure. The results were very similar to those obtained by Sieverts and Moritz.² Both sets of data show a minimum solubility between 500&apos; and 700°C., but they differ in certain respects; on cooling from 500°C., our results showed an increase in solubility of about 7 C.C. as compared with an increase of 34 C.C. per 100 grams shown by Sieverts. Furthermore, the transition temperatures, as indicated by sharp breaks in the solubility curves, did not agree well with Sieverts&apos; data. This information was of secondary importance in the earlier investigations, and the solubility at low temperatures and the transition temperatures were subject to considerable error. Therefore, a subsequent investigation, reported in this paper, was made to measure the absolute solubility at temperatures from room temperature through the melting point and make more accurate observations of the transition temperatures. Apparatus and Method The apparatus and method were essentially the same as those described in the previous work,&apos; as shown in Fig. I. At high temperatures, the small tube containing the thermocouple in the sample container A frequently broke off, so for some of this work the thermocouple was placed outside the sample container and protected by a quartz tube of about the same wall thickness as the sample container. No significant difference was found in the transition temperatures obtained in the two ways. The automatic temperature controller was used in these tests in the regions where there was little change in solubility with temperature. In the neighborhood of the transition points a continuously variable autotransformer was used instead of the automatic controller, and the power input to the furnace was adjusted so that the temperature increased or decreased at a very slow, uniform rate through the transition range. This procedure was followed because the temperature oscillations produced by the controller were too great compared with the transition range, and the transi- . tion points determined under such conditions were less accurate. Absolute Solubility Procedure ad Results The absolute solubility of hydrogen in manganese could be determined most

Jan 1, 1947

By E. V. Potter, H. C. Lukens

The volume of hydrogen released from electrolytic manganese at various temperatures and pressures was determined in a previous investigation1 as part of a study to determine the most practical procedure for removing the hydrogen from electrolytic manganese metal. No attempt was made to determine the absolute volume of gas in the metal at any temperature and pressure; the volume of gas released showed only the variation in solubility with temperature and pressure. The results were very similar to those obtained by Sieverts and Moritz.² Both sets of data show a minimum solubility between 500&apos; and 700°C., but they differ in certain respects; on cooling from 500°C., our results showed an increase in solubility of about 7 C.C. as compared with an increase of 34 C.C. per 100 grams shown by Sieverts. Furthermore, the transition temperatures, as indicated by sharp breaks in the solubility curves, did not agree well with Sieverts&apos; data. This information was of secondary importance in the earlier investigations, and the solubility at low temperatures and the transition temperatures were subject to considerable error. Therefore, a subsequent investigation, reported in this paper, was made to measure the absolute solubility at temperatures from room temperature through the melting point and make more accurate observations of the transition temperatures. Apparatus and Method The apparatus and method were essentially the same as those described in the previous work,&apos; as shown in Fig. I. At high temperatures, the small tube containing the thermocouple in the sample container A frequently broke off, so for some of this work the thermocouple was placed outside the sample container and protected by a quartz tube of about the same wall thickness as the sample container. No significant difference was found in the transition temperatures obtained in the two ways. The automatic temperature controller was used in these tests in the regions where there was little change in solubility with temperature. In the neighborhood of the transition points a continuously variable autotransformer was used instead of the automatic controller, and the power input to the furnace was adjusted so that the temperature increased or decreased at a very slow, uniform rate through the transition range. This procedure was followed because the temperature oscillations produced by the controller were too great compared with the transition range, and the transi- . tion points determined under such conditions were less accurate. Absolute Solubility Procedure ad Results The absolute solubility of hydrogen in manganese could be determined most

Jan 1, 1947

By D. L. Albright, R. W. Kraft

A technique is described whereby the study of crystal perfection through the use of conventional X-ray rockite curves is extended to three dimerzsions. Specinzens of unidirectionally solidified eutec-tic alloy which consist of a nearly perfect parallel arrangement of alternating Platelets of Al and CuAl2, but which contain lamellar faults have been analyzed by this technique in conjunction with X-ray microscopy. Analysis of the data has shown that some rotational symmetry about the growth direction occurs, that small groups of lamellae between faults diffract as a unit, and that the misorientation caused by a fault is on the order of a degree of arc. A eutectic-grain can be defined as that portion of a eutectic specimen in which the crystallographic orientation of each phase AND the microscopic or met-allographic orientation of the phase particles have fixed angular relationships one to another. Eutectic-grains of the A1-CuA12 eutectic, which is a normal lamellar eutectic, have been grown by unidirectional solidification and identified as such.1-3 To a first approximation, a eutectic-grain in this system consists of two interpenetrating single crystals which are related to each other and to the lamellae themselves as follows:

Jan 1, 1962