By Liu Wei-feng

In this paper, the practice of separating precious metals from base metals in gold-antimony alloy by selective chlorination leaching under controlling potential in China has been introduced in detail. The precious metals and the base metals can be separated completely when the complex gold-antimony alloy is treated by this process. The impurity metals were removed effectively since the leaching efficiencies of copper, nickel and antimony are over 99%, with direct recovery of gold being 99.83% that is about 20% higher than that of the original process and silver, antimony, copper and nickel are also recovered effectively. The gold grade of the resulting crude gold powder can reach to 94%.The new process has been applied in the treatment of gold-antimony alloy for two years, and many former procedures have been cancelled, such as electrolysis, Anode slime leaching by nitric acid, smelting in crucible and blowing in muffle. The new process is more shorten, lower cost and friendly to the circumstance comparing to the original process.

Jan 1, 2008

By P. N. Anyalebechi

The effects of application of steady and pulsed electric current on the cast microstructures of ingots of a 7050 type aluminum alloy have been experimentally investigated over a solidification rate range of 0.1-10 K/s. This involved the application of an electric current of 465-930 mA/cm2 of melt surface area to laboratory-size ingots solidified in a unidirectional manner. Within the ranges of electric current density and solidification rate investigated, the applied electric current reduced the average dendrite, grain, and second-phase particle size. It also made the size distribution of the second-phase particles more uniform. The mechanism for the observed refinement of the cast microstructure by the applied electric current is not well understood. The potential effects of heat-induced local convections, shear stress-induced fragmentation of dendrites, increased temperature gradient due to Joule heating and the thermal and constitutional supercooling engendered by Peltier, Thompson, and Joule heating are discussed.

Jan 1, 2009

By Fei Ruan, Chang Jie, Jieyu Zhang, Jifang Xu, Kuochih Chou

"Viscosity is an important physical parameter of slag in metallurgical processes. Most studies of aluminosilicate and aluminate systems assume that aluminum occurs in tetrahedral coordination. In this case, the O/Al value was utilized to describe the slag structure in terms of the network character of aluminosilicate and aluminate systems. Composition and viscosity data from the literature and the trends were analyzed according to the O/Al value and temperature. It is shown that the O/Al value explains the trends in more than ten systems, containing more than 200 data points. In aluminosilicate system, the trend that viscosity value changed with the O/Al value which implies that alumina works as network modifier such as basic oxides or works as network former. In aluminate system, irrespective of the system and temperature, viscosity decreased steadily when O/Al value increased.IntroductionMetallurgical slags, which are made of oxides and many also contain fluorides, play an important role in metallurgical processes such as iron making, steel making and secondary refining processes. Aluminosilicate slags are applied in a wide range in metallurgical processes. A polymerizing effect of the addition of aluminum and an association of aluminum with low-field strength cations is further supported by the physical variations in aluminosilicate and aluminate systems. The behavior of alumina in silicate melts has been studied by various authors [1-6]. It is generally accepted that Al2O3 is amphoteric [7] because Al3+ ions can behave in profoundly different ways in a silicate melt. When added to a pure silica melt, Al2O3 acted as a network modifier, breaking the bridging oxygen of the pure silica network, thereby decreasing the viscosity in a similar manner to other network modifiers, such as CaO, MgO etc. to form [1/2Ca (AlO4)]4- complexes. However, when added with alkali or alkali-earth metal oxides, some of the Al3+ ions assumed tetrahedral coordination and replaced Si in the liquid network, the missing charge was compensated by Me+ or Me2+ ions. Therefore Al2O3 acted as network former [8, 9]."

Jan 1, 2011

By Christian M. Sagedahl

The stringent environmental regulations for air pollution regarding emission control, along with the need of dry concentrates to feed autogenous smelting processes, are enhancing the development of cleaner technologies. Indirect drying of concentrates by a Kvaemer steam dryer is a technology with promising results, reducing dust entrainment to the exhaust gas stream and leading to smaller dust separation units. The Kvaemer dryers are designed for a very high availability, a high-energy efficiency, low amount and velocity of exhaust gases, no SO2, CO or CO, emissions combined with a wide range of satisfactory operating conditions and low total operational costs.

Jan 1, 1999

By Stephen K. Pave1

Over 1,100 tons per day of Fluid Catalytic Cracking Unit (FCCU) catalyst is used worldwide. During the cracking reaction, catalyst is contaminated by deposited metals including nickel, vanadium, potassium, copper, iron, sodium, etc. To compensate for contaminants, a portion of the circulating catalyst inventory is withdrawn for disposal and fresh catalyst is added. The DEMETR process takes spent FCCU catalyst and removes a portion of the metal contaminants, enabling the refiner to recycle demetallized catalyst, thus reducing the solid waste from the refinery. Through August, 1993, the operation of one unit for one refiner has resulted in the recycling of over 7,500 tons of spent catalyst.

Jan 1, 1994

By D. A. Horne, V. R. Daiga

Certain steel mill wastes contain significant amounts of zinc oxide due to the use of galvanized scrap during the steel making process. Typically electric arc furnace (EAF), and basic oxygen process (BOP) flue dusts contain 20 to 30% zinc oxide and 40 to 50% iron oxides, along with smaller quantities of lead and cadmium. These materials can be recovered from the flue dusts by using a proven rotary hearth furnace (RHF) process. By-products of the recycling operation include a crude zinc oxide fume, which is captured in a baghouse filtering system, and sponge iron that may be recycled into the steel making operation. Crude zinc oxide properties plus the operating experience from two commercial RHF installations utilizing MR&E's DRyIron™ Process will be presented.

Jan 1, 2000

By Saskia Duyvesteyn

Small ion-exchange resin particles provide faster mass transport than conventional-sized beads. Unfortunately, high pressures are needed to pump solutions through columns containing small resin particles. It is preferable to disperse fine resins in the solution being treated. Screens have been used to separate the resin from the solution, but screens do not retain fines created by attrition of the resin particles. We have developed a separation process based on flotation, which relies on the surface characteristics of the resin, instead of size. The resin is conditioned with a surfactant before dispersing it in the solution to be treated; this increases the hydrophobicity of the resin sufficiently for froth flotation, without introducing surfactant directly into the solution. The surfactant adsorbed on the resin surface does not appear to impair the kinetics of metal ion removal. A flowsheet for an effluent treatment process is proposed; other applications are clearly possible.

Jan 1, 1998

By R. D. Irwin, W. M. Mullins, E. A. Medina

"Various stability criteria are introduced and thermo-kinetic models for metallurgical processes are used as concrete examples for evaluation. Kinetic criteria for the process of dynamic recrystallization are proposed. These criteria are compared to the non-equilibrium thermodynamic approaches discussed in the literature. The application of macroscopic stability criteria to materials processing is then discussed.IntroductionThe mechanical behavior of metals at elevated temperature is very well predicted by any of several empirical constitutive relations. Typical is the power-law (or Swift's) form,Equationwhere r-is the stress, y is the strain and m, n , t0, y0 and Q are material constants. This form has been used with some success in the metals processing area [1]. In general, though, all of the empirical constitutive equations are static, failing to account for any dynamical properties of the system they seek to describe.The physics of warm deformation is qualitatively well understood. An example is power-law creep, where the dominant mechanism is assumed to be lattice diffusion limited climb of dislocations, which allows the strain-rate to be determined by the applied stress through"

Jan 1, 1997

By Larry M. Southwick

Considerable process and equipment development and analysis were conducted during design of Freeport Sulfur's laterite nickel facilities in the late 1950's. These covered ore concentration at Moa Bay, Cuba, and concentrate refining at Port Nickel, Louisiana. Both facilities utilized acid pressure leaching and product refining steps that were similar to those later used elsewhere in the laterite processing industry. Unfortunately, developments in Cuba removed the Moa Bay facilities from Freeport control. This deprived the project of a start-up that would have allowed thorough resolution of difficulties and a quicker attainment of production capacity. This meant lost opportunity to positively prove and complete the technology when optimum resources and staff were available. This paper reviews the original rationale of how design was developed via laboratory, bench scale and pilot studies by Freeport Sulfur. Some later operating problems will also be discussed. This case is unusual, but the lessons learned may be instructive in the application of difficult and complicated technologies, as well as the need to understand and retain access to the original development and design activities Keywords: Moa Bay, Freeport Sulfur, Port Nickel, acid pressure leaching, pilot plant, pachuca, Chemical Construction, pressure letdown, cobalt, titanium

Jan 1, 2004

By F. F. Lins

There is a large use of mercury in Brazil by the gold miners in the so called "garimpos" (non registered mining operations), where it is usual to recover the gold contained in the gravity concentrates by amalgamation, which is highly deleterious to environment if not conducted properly. Unfortunately, this is a common practice there. After presenting in brief the modus operandi generally practiced in the garimpos and the environmental problems, this work reviews some of the research conducted in CETEM according to two approaches: (i) replace amalgamation by other processes and (ii) develop technology to treat mercury-contaminated soils and effluents. Conventional processes like froth flotation, to recover gold from gravity concentrates, and centrifuges were considered. Also as alternatives to amalgamation, innovative process like the recovery of gold by coal-oil agglomerates and a technology that is currently under development in our laboratory, called gold-paraffin process, are described in brief, some results presented and their potential use assessed. To reclaim sites already polluted a technology was developed to float mercury selectively from contaminated soils. The potential use of centrifuges to pre-concentrate the mercury is also discussed. The scope for applying the last techniques is to concentrate the pollutants in a small volume of mass which would be suitable for recycling or isolation from the environment. A prospective technology to treat contaminated soils, or mercury concentrates, is the immobilization of mercury by adding inorganics. Concerning the ionic mercury which may be present in effluents, precipitation of the ions and flotation of the precipitates are being studied.

Jan 1, 1994

By Ragnhild E. Aune, Shahid Akhtar, Reza Beheshti

"The potential use of Black Dross (BD) as a raw material for the production of refractories, fluxing agents and glasses is the main motivation of the present study. Heat treatment experiments were carried out in Ar, and under reduced pressure (20 Pa), to evaluate the salt removal efficiency. The chemical composition of the BD after heat treatment was investigated by SEM-EDS and XRD analyses. Based on the present results, it is established that the salt starts to evaporate at ˜1273 K in Ar, and under reduced pressure. The salt removal efficiency in a 20 g sample was found to increase in both cases as a function of time and temperature. Moreover, in Ar the chlorine concentration was lowered to 0.3 wt% after heat treatment at 1523 K for 10 hours. Under reduced pressure, however, 0.2 wt% residual chlorine was obtained after 8 hours at 1473 K.IntroductionIt is believed that aluminum recycling in the near future will become the main route of aluminum production [1]. Black dross (BD) that is produced during this process contains, among other things, high amount of salts like NaCl and KCl [2, 3]. Almost 800,000 tons of BD is annually land filled in United States and this number continues to grow with the increase in aluminum recycling [2]. The BD should be dumped in controlled land field and it is costly procedure [4, 5].The water-soluble compounds in BD react with water or environmental humidity and release chlorides into the water and/or generate toxic gases such as H2, CH4, NH3 and H2 S [6-8]. In the Europe, BD is considered as toxic waste and its disposal as landfill is forbidden [8, 9]. After salt removal, the BD is considered to be non-hazardous and can be buried under ground [10].On the other hand, BD do also contains many relatively valuable compounds that may be changed in to useful materials as a result of further treatment [11, 12]"

Jan 1, 2012

By Hector M. Henao

To provide thermodynamic data for converting nickel matte to liquid nickel at high temperature, an experimental study was conducted on the phase equilibrium between the Ni-S alloy and the FeOX-SiO2, FeOx-CaO, and CaO-A12O3 base slag in a magnesia crucible and the CaO-Al2O3-MgO slag in an alumina crucible. All experiments were carried out at 1773 K under controlled pso2 of 0.1 atm and po2 in a range between 5x10- and 10-5 atm by using CO-CO2-SO2 gas mixtures. The dissolution of nickel in the slag was found to be minimum for the CaO-Al203¬-MgO slag with a molar ratio of NCaO/NA1203=1.7. The solubility of nickel in this slag at p02 of 6x10 atm (just before the precipitation of solid NiO) was 4 mass%. This result suggests that a CaO-A12O3 base slag could be used in converting Ni-S melt to nickel while minimizing nickel losses to the slag.

Jan 1, 2002

By S. Seetharaman

The present paper presents. the concept of micro-models and illustrates the application of the same in the simulations metallurgical processes. Development of micromodels requires access to accurate thermodynamic, thermophysicaland kinetic information for the relevant systems with suitable models to extrapolate the data as functions of temperature and composition. Experimental measurements and modelling of the thermodynamic properties, sulphide capacities and viscosities of oxide melts carried out in the department are presented. The incorporation of these models in process models, with special reference to ladle refining of steel is illustrated. Typical example of micro-modelling of solid-gas reactions is also presented.

Jan 1, 1999

By P. D. Lee

The effect of strontium on porosity formation in aluminum-silicon alloys is not well understood and there is no consensus upon the cause of the effects observed. This paper describes a series of experiments where the effect of adding strontium on pore formation was observed directly with combination of a traditional temperature gradient stage and real time micro-focus radiography. These in situ observations provide a new insight into the effect of strontium on the nucleation and growth kinetics of porosity. The addition of strontium was found to have a minor effect on the growth of the pores in the mushy zone. However, strontium appeared to alter the nucleation and stability of hydrogen bubbles within the melt. The interaction of strontium with titanium-boride grain refiners produced an even stronger change in the nucleation and stability of the bubbles formed.

Jan 1, 2002

By Richard A. Shulkosky

The American Iron and Steel Institute (AlSO, in conjunction with the U.S. Department of Energy (DOE) jointly funded the development of a mechanical properties model for Hot Strip Mills. INTEG process group, inc. validated an enhanced version of the model under a project funded by the AlSI/DOE Technology Roadmap Program (fRP). The Hot Strip Mill Model (HSMM) version 6.0 allows users to easily set-up their mill configuration, simulate a rolling mill schedule and calibrate the model for a variety of grades of steel. Starting from reheat furnace drop out, the model simulates roughing mill stands (reversing and continuous), heat retention equipment (coil box and covers), finishing mill stands (tandem and Steckel mills), the run out table and the mill exit area. The HSMM uses a series of physical models to calculate both the thermo-mechanical and the microstructure evolution of steel being processed in a hot mill to predict its final mechanical properties. The enhanced HSMM was validated using a multitude of samples from several steel companies. Excellent agreement was obtained for tensile strength. The supporting steel companies have utilized the model for a variety of practical applications. Keywords: Process Modeling, Microstructure Evolution, Mechanical Properties

Jan 1, 2003

By Xiaodi Huang, Matthew Andriese, Zheng Zhang, Jiann-Yang Hwang, Zhiwei Peng

"The thermal decomposition and regeneration behaviors of wüstite were investigated by in situ high temperature X-ray diffraction (HT-XRD) under non-isothermal condition at heating rate of 4 K min-1 in vacuum ranging from 294 K to 973 K. Wüstite on heating decomposes to magnetite and iron up to 823 K, above which it exhibits marked tendency to regenerate. Investigation of thermal stability of the reaction system shows that the decomposition proceeds under kinetic reaction control while the regeneration is under thermodynamic control. Kinetics study based on the Coats-Redfern integral approximation method indicates that the decomposition reaction follows a Komatsu-Uemura model-based diffusion-controlled kinetics with activation energy of 32.860 kJ mol-1. The thermodynamics analysis of regeneration reaction demonstrates that wüstite regenerates at lower temperature than stoichiometric ferrous oxide.IntroductionOwing to its importance in preparing various magnetic ceramic/metal nanocompostites or nanocrystals with high values of coercivity for the application as recording media, wüstite (non-stoichiometric ferrous oxide) has been attracting the attention of scientists over a long period [1-6]. The thermal behavior of wüstite was investigated by several researchers and phase transformations due to thermal decomposition and regeneration of wüstite during the heating in a specific temperature range was observed [7-9]. In spite of wüstite being found to dissociate to magnetite and iron at temperatures lower than 848 K and then regenerates at higher temperature, a clear understanding of the reaction mechanisms is clearly lacking [9]."

Jan 1, 2012

By M. C. Furerstenau

Adsorption behavior of various surfactants on sulfide minerals is very much affected by the nature of the surface of the mineral. Since sulfides are naturally meta-stable, oxidation occurs when they are exposed to air, especially in aqueous environments. As a result. oxygen assumes a major role in sulfide flotation. Mechanisms of adsorption of various thiol collectors on sulfide minerals have been reviewed. The electrochemical behavior of various sulfide minerals has also been reviewed. Flotation behavior of galena, chalcocite, sphalerite, pyrite, chalcopyrite and pentlandite has been presented together with the. flotation of copper sulfide- nickel sulfide ore.

Jan 1, 1993

By Devon A. Hannan

Thermodynamic modeling calculations were undertaken for the recovery of mercury from HgTe using a vacuum retort reactor. However, discrepancies were noted in the available thermodynamic data which introduced uncertainty in the model results. Consequently, a series of transpiration experiments were first undertaken on the thermal decomposition of HgTe into an inert carrier gas stream according to the following reaction: HgTe(s) Hg(g) + Te(s) From the measured weight loss of the HgTe samples, the Gibhs free energy change for the above volatilization reaction was determined as a function of temperature. The experimentally determined Gibbs free energy values were found to be approximately 30% larger (more posi-tive) than the values available in databases such as HSC Chemistry. By conducting a second-law analysis on the experimental data, the heat of formation of HgTe at 298.15 K and the en-tropyat 298.15 K were determined, which then formed the basis for a new database for the modeling calculations. The results of this study showed that HgTe was more stable at elevated temperatures than was generally indicated in the literature. The new database is given in a for-mat for direct insertion in HSC Chemistry. Using the new database, modeling calculations were conducted to examine the effects of the re-tort pressure and the molar ratio of purge gas to HgTe on the volatilization of mercury from HgTe. A diagram is presented that shows the minimum temperature for 100% volatilization of mercury from HgTe as a function of retort pressure for different molar ratios of purge gas (N2) to HgTe. For example, it was found that the minimum temperature for 100% volatilization could be decreased by 175 K, at a retort pressure of 0.05 bar, if the molar ratio ofN2 to HgTe is increased from 1.0: 1 to 100.0: I.

Jan 1, 2003

By Thomas Niehoff, Yin Qing, Wei Zhongling, Liu Yongguo, Zhang Deliang, Tang Le

The gold ore of Shandong Gold Mining (Xinhui) was a refractory ore, which contained multi metallic sulfides (ZnS and PbS etc.) and carbonaceous. The gold ore concentrate came into leaching process and thickener and zinc replacement to recover gold. In order to improve gold recovery, the GOLDOX™ hydrometallurgy process was studied in Shandong Gold (Xinhui) by bench scale and 6 month plant scale test supported by Linde Gas. It was shown that the process promoted the leaching kinetics and improved gold recovery. The residue grade reduced 0.22 g/t in average after oxygen was applied. This indicates an operating profit increase 850,000 yuan/a in the plant. It was setting a good example for similar gold mine plant and would promote the oxygen application in Chinese gold mining industry.

Jan 1, 2015

By Gerson de Araújo Filho

This paper shows the use of tires as fuel to be employed into blast furnaces. The tires can substitute coal or even charcoal in the blast furnaces tuyeres. The injection into tuyeres, besides the contribution for energy generation, can also produce gas for iron oxide reduction. The tires, as powder to be injected into blast furnaces, contributes for an environmental use of this waste, which helps to obtain a high value product as well. So, the advantage of using such material is that it is waste and has lower cost for preparation. The obtained results showed that the tires have good combustibility. This one was obtained in a model that simulates the same conditions occurring in the blast furnaces tuyeres; these used raw materiais include tires and mixtures of tires with coal or even with charcoal.

Jan 1, 2006