By H. J. Denning, M. W. Brabbins, A. K. Isaac

The quality of a coalface floor is the essential element that enables powered supports to generate their designed loads in control of coalface strata. The paper introduces a technique for the appraisal of coalface foundation stability. A criterion of support efficiency, viz., the support pressure increase/strata convergence, is included in case study data obtained from investigations in the South Wales Coalfield, U.K.

Jan 1, 1984

By R. G. McQueen, E. G. Zukas

THE production of isotropic fine-grained ingot iron would be most useful since physical measurements associated with the elastic properties of iron are influenced by the size and orientation of the individual grains. This can be accomplished at present for small samples by established metallurgical procedures, but for large samples (in excess of 2 in. diam by 1 in. thick) it is virtually impossible to produce reasonably small uniform grains with random orientation. Such pieces can, however, be produced by impulsive loading followed by a suitable recrystallization treatment. The shock loading system employed is diagrammed in Fig. l. Here the 3/8-in. iron plate is accelerated by the plane-wave initiated high explosive charge through a 1 5/8-in. air space. Collision of this plate and the specimen of interest generates a shock wave in excess of 300 kbars which passes through the specimen. For this type of work it is not necessary to use machined parts: for example, the ingot iron pieces are saw cut from the billet so that they can be inserted in short sections of iron pipe. The recovered specimens are less distorted, however, if the air gap between the iron sample and pipe is filled with Woods metal. The dimensional changes resulting from this type of loading technique are minor, usually less than a 10 pct reduction in thickness. Compressive yield

Jan 1, 1962

By T. A. Read, M. S. Wechsler, D. S. Lieberman

IN the formation of martensite in steel, it has been observed that the habit plane does not change continuously as the alloy content is varied. Instead, it appears that discrete habits correspond to certain ranges of composition. Greninger and Troiano' found that in low-, medium-, and high-carbon steels, the habits are approximately (1l1), (225), and (259), respectively.* The work of Mehl and Van Winkle2 indicated that the change from the (225) to the (259) habit is fundamentally a consequence of the lower transformation temperature rather than the higher carbon content. Also, Otte and Read3 observed that the habit plane orientation for a chrome-carbon steel scattered within a cone of semivertex angle of 5 deg, which was outside of the experimental error in the determination of the habit plane. These observations suggest the importance of investigating what factors in the crystallography of the formation of martensite account for the several types of habit and the inherent scatter in the precise orientation of the habit plane. A theoretical treatment of the austenite-martensite transformation has been given,4 which considers the total transformation distortion to be composed

Jan 1, 1961

By H. R. Thresh, A. F. Crawley, D. W. G. White

The densities of liquid tin, lead, and Sn-Pb alloys have been measured over a range of temperature above the liquidus. In all cases, data can be adequately represented by an equation of the type p = a + bT. For pure tin, the values of a and b are, respectively, 7.139 and 7.125 x 10-4, and for pure lead, 11.060 and 12.220 x 10-4. At constant temperature, molar volumes in the Sn-Pb system vary linearly with composition. DURING the course of a long-term program at the Department of Energy, Mines and Resources, Ottawa, Canada, the densities of liquid tin, lead, and Pb-Sn alloys were studied. The work reported herein draws on two sets of results independently achieved by Thresh, on the one hand, and by Crawley and White, on the other. EXPERIMENT The method and apparatus were originated by Thresh and have been described in detail in Mines Branch reports.172 In operation, the 14 cu cm graphite pycnometer is put in the furnace as shown in Fig. 1 after a machined charge has been placed inside the pycnometer and the lid screwed down. The dimensions of the charge are such that, upon melting, a small excess of liquid metal is discharged through the capillary hole to displace the weighted float above. When the pycnometer has been equilibrated at the experimental temperature, the

Jan 1, 1969

By D. Turnbull, A. M. Turkalo

It is well known that if copper that has been severely cold-worked by rolling (70-98 pct) is heated to high temperatures a small number of large grains are formed at the expense of the fine grained structure that appears upon primary recrystallization. Dahl and Pawlek,' Cook and Mac-Quarie,2 Ward,3 and Boas and Bowles4 have studied this phenomenon in copper. It has been reported as taking place with measurable velocities in the temperature range 700-1080". Boas and Bowles have reported that the time necessary for the transformation is of the order of days at 700°C. According to Ward3 the number of secondary grains which appear in OFHC copper decrease with increasing perfection of cubical alignment after primary recrystallization; also the perfection of cubical alignment increases with decreasing grain size prior to the final reduction. In this investigation two heats, A and B, of especially high purity copper (99.999 pct) supplied by the American Smelting and Refining Co., were used. The behavior of samples prepared from the two heats was qualitatively very similar providing that the grain sizes established prior to the final reduction were about the same. We observed that in specimens prepared from bars which were relatively coarse grained prior to final reduction secondary recrystallization took place at a rapid rate at temperatures as low as 500°C. This is about 200-300°C lower than the temperature necessary to obtain fairly rapid transformation in OFHC copper. A 0.22 in. thick rectangular bar of lot B was cold-reduced 60 pct by straight rolling and given a penultimate annealing treatment at 250°C. Following this it was cold-reduced 90 pct and heated to various temperatures in the range 450-1040°C. The specimens were about 8 mils thick

Jan 1, 1950

By Ronald K. Linde

Metastable Ag-Cu solid solutions at two compositions beyond the maximum limits of solubility obtainable by quenching from the solid state were obtained by rapid quenching from the liquid state. The process of transformation of the metastable solid solutions into the equilibrium phases was studied by means of X-ray diffraction intensity measurements and electrical-resistance measurements; metallographic examination was also performed. Results are compared with those for an alloy quenched from the solid state at a composition which exists as a solid solution at elevated temperatures. Activation energies for the trans-formation were computed to be 33,600 * 2500 and 33,100 * 2000 cal per g mole for the 60.1 and 75.0 at. pct Ag;Cu compositions, respectively THE kinetics of precipitation in supersaturated solid solutions obtained by quenching from high temperature has been thoroughly studied in many alloys, and detailed investigations of the early stages of nucleation and subsequent growth of the equilibrium phases have been carried out. All of these studies have been made on alloys quenched from the solid state, however, and it is the purpose of this paper to present some of the results on the kinetics of transformation of metastable solid solutions in Ag-Cu binary alloys whose compositions lie outside of the solid-state limits of solubility. Limits of solubility in the solid state can be increased by rapid quenching from the liquid state. This was first demonstrated by Falkenhagen and Hofmann, who obtained appreciable increases in solubility limits of the elements of the first transition series in aluminum by rapid cooling of liquid alloys through contact with a copper mold maintained at liquid nitrogen temperature.' The same basic idea of cooling a liquid alloy by conduction onto a substrate rather than by convection of a gas or liquid (conventional quenching) has been recently revived and extended to very high rates of cooling by Duwez and his collaborators. The new technique was first applied to Ag-Cu alloys because the existence of a eutectic in this system is not predicted by the Hume-Rothery rules of alloy phase formation. Rapid quenching from the liquid state resulted in metastable solid solutions at all concentrations. The kinetics of decomposition of these metastable solid solutions containing 60.1 at. pct Ag;Cu (eutectic composition) and 75.0 at. pct Ag;Cu is the subject of the present paper. EXPERIMENTAL TECHNIQUES Alloys were made in 10- to 20-g heats using silver of purity 99.99 pet and copper of purity >99.999 pct. Components were weighed accurately to 0.1 mg and melted by induction heating in an alumina crucible under an atmosphere of hydrogen. Weight losses amounted to less than 0.02 ~ct in all cases. Rapid cooling from the liquid state was achieved in an apparatus of the type described by Pietrokowsky. 3 In this technique a freely falling drop of molten alloy is caught between a stationary anvil and a fast moving piston, both anvil and piston being lined with copper. The resulting foils were approximately circular (about 2 cm in diam) and from about 50 to 150 u in thickness, depending on the pressure driving the piston. Metallographic samples were prepared for polishing by edge-mounting foils in Quickmount. The mostef-fective etching procedure was found to be: 10 parts NH4OH (concentrated), 1 part H2O2 (30 pct), 5 parts H2O, swab for 5 to 10 sec. The transformation of the metastable alloys to equilibrium was followed by X-ray diffraction and electrical-resistivity measurements. The peak intensity and the integrated intensity of suitable Bragg reflections of the metastable and stable solid solutions were studied with a Norelco dif-fractometer, using nickel-filtered copper KO radiation. The peaks were step-scanned at intervals of 0.05 deg. Using either a Kelvin bridge or a null circuit with a Leeds and Northrup K-2 potentiometer, the changes in electrical resistance due to phase transformation were measured for specimens cut into strips about 20 mm long and 4 mm wide. All resistivity measurements were carried out at liquid-nitrogen temperature. The isothermal heat treatment was accomplished by sealing the samples in argon-filled aluminum containers with stainless-steel O-rings. Containers were then suspended in wax baths with temperatures in the

Jan 1, 1967

By W. P. Sykes

IN CONNECTION with a study of tungsten steels, Honda and Murakami1 reported an investigation of the system iron-tungsten. This report included a tentative equilibrium diagram, photomicrographs of various alloys in the series, and qualitative measurements of hardness and magnetic properties. The present investigation originally had as its object the study of the hardness and tensile properties of a series of carbon-free iron-tungsten alloys. But, as the work progressed it became evident that the system possessed other features of interest, so the scope of the investigation was enlarged. MATERIALS The iron powder used in preparing the alloys was obtained as follows: Iron oxalate was precipitated from a ferrous-sulfate solution by the addition of a solution of oxalic acid. This oxalate, after thorough washing, was ignited to iron oxide, which after reduction in hydrogen at about 1000° C. yielded iron powder containing but about 0.2 per cent. iron oxide and about 0.005 percent. carbon. Tungsten metal in the form of powder, such as is used in the manufacture of filaments for incandescent lamps, was the other constituent. This material analyzed 99.8 per cent. tungsten and contained no carbon, The metal powders, in the desired proportions, were mixed by tumbling and formed, under pressure of 20 tons per sq. in., into rods 3/8 by 3/8 by 10 in. To form the alloys without contamination, sections of the pressed rods were placed on alundum slabs and heated in an alundum tube wound with a tungsten resistor and packed in heat-insulating material. While the resistor was heated, a stream of hydrogen was continually passed through both the tube and the case containing it. The tungsten winding on the tube, as well as the material heated within the tube, was thus protected from oxidation. Such a furnace will operate constantly

Jan 2, 1926

By WALTER S.

(New York Meeting, February, 1912,) THE earliest example of attempting to form finely-divided materials into larger masses for better adaptation to commercial use was probably the briquetting of peat and lignite-waste at Paris by the use of a clay binder. It was from this attempt that our word briquette has arisen (Fr. la brique), the formed masses being shaped similar to ordinary bricks. This term does not, however, lend itself to the many shapes of such formed material as are now being produced, as few of them aside from some of the European brown-coal products bear any resemblance to the shape of that well-known article. The term "agglomeration " has therefore been chosen as more accurately descriptive of the products now being manufactured, this term including the molding as well as the sintering. With the increasing prices of fuel and ores and the greater demand for economy in the operation of industrial plants, more ,attention has been paid in recent years to the utilization of waste products and low-grade ores and fuels. Much of the waste has been occasioned by the inability to utilize finely ,divided ores and fuels in the furnaces because they could not be kept there, or else because they clogged up the furnace-shaft so that gases could not be forced through under ordinary conditions of operation. As a result, all such fines were thrown on the dump. Again, with the exhaustion of the richer deposits of ores, concentration of lower-grade ores becomes a necessity, and most concentrates are produced in a finely-divided condition. Aside from these considerations, there is also the economy in the cost of operating the plant; a furnace running on agglomerated material will have a much greater output than one working on fines. In one instance the charge of an iron blast-furnace was changed from fine concentrates to briquettes and the output was increased four-fold; better results could have been obtained had facilities been at hand for taking care of the increased output.

May 1, 1912

By L. L. Melton, D. L. Lord, B. W. Hulsey

A mathematical model d1.20p/4L = A(8v)8 derived from the Blasius equation is proposed to be applicable to turbulent flow through straight cylindrical pipe for time-independent fluids which produce a diameter family of straight parallel lines on a log (dp/4L) vs log (8v/d) plot or stress-flow diagram. Such a correlation should permit scale-up with data taken from one pipe diameter for Newtonian, inelastic non-Newtonian and viscoelastic fluids, such as dilute polymer fracturing fluids, which produce considerable frictional pressure reductions. The Newtonian diameter exponent value 1.20 is shown to be empirically valid for turbulent non-Newtonian flow by application of numerical analysis methods. Multiple regression analysis is applied to a logarithmic linearization of the proposed model. An improved data fit results from further linearization achieved by taking linear terms from a generalized Taylor's series expansion about the multiple regression coefficients. Extensive experimental data obtained in five pipe diameters with water, sodium carboxymethyl-celIulose solutions, guar gum solutions, bentonite clay suspensions and calcium carbonate slurries are presented. Except for calcium carbonate slurries, which were investigated rather than time-dependent cement slurries, the fluids studied contain drilling or fracturing fluid additives. The behavior exhibited by these fluids is considered typical of most fluids encountered in drilling, cementing and fracturing operations. INTRODUCTION Considerable difficulties have been encountered in predicting turbulent flow pressure drops produced by non-Newtonian fluids flowing through straight cylindrical pipe. Correlations previously presented require extensive experimental data which represent several pipe diameters and a wide flow rate range to estimate the necessary scale-up parameters.l-7 One must implement either elaborate experimental apparatus or spend considerable time and effort to gather these data. Presented here is a correlation method which should minimize the experimental effort and data analysis normally required by utilizing flow data taken with only one pipe diameter. Turbulent flow data (up-stream and down-stream pressure and volumetric flow rates) were collected for five pipe diameters through operation of a small pipeline system having an electronic data acquisition and digitizing system. A mathematical model derived from the Blasius equation was utilized to describe the functional relationship between pressure drop and the two independent variables, diameter and average flow velocity. A correlation, which should produce a valid single-pipe scale-up, resulted from a computer-implemented statistical and numerical data analysis for several time-independent non-Newtonian fluids.

By D. T. Farnham

The shale used at the Renton plant of the Denny-Renton Clay and Coal Co. for the manufacture of vitrified paving brick occurs in a hill rising from 200 to 300 ft. above the level of the valley in which the plant is situated.

Jan 1, 1915

By N. S. Stoloff, R. G. Davis

It is concluded from an X-ray stztdy that the formation of the hcp Mg3Cd superlattice is a nuclea-tion and growth reaction. A two-phase, ordered-plus-disordered, region is observed between 153" nnd 141"C. A maximum in the flow stress is observed both at temperature and in quenched specimens within the two-phase region. The peak arises fro112 the extra energy required to create antiphase boundary upon cutting the ordered regions. Hardening during isothermal annealing in Mg3Cd has been shown to be similar to the domain hardening in Cu3Au-type alloys in that up to the maximum the structure is ordered domains growing into a short range ordered matrix. The hardening is due to a combination of short range order strengthening and the strengthening produced when antiphase boundary has to be created. In a recent study1 of the effect of long-range order upon the mechanical properties and deformation modes of hcp Mg3Cd a comparison was made be- tween quenched (disordered) and slow-cooled (fully ordered) specimens. The most striking observations were that the disordered alloy yields at a much higher stress than the ordered alloy, and that there is a change in slip mode from primarily (_0001) ba_sal slip in the disordered state to (0001), {1010}, {1122}, and {l011} slip in the ordered state. The main purpose of the present work is to extend these observations to determine whether MgsCd exhibits a peak in flow stress at an intermediate degree of order, or at a critical domain size, as do other orderedstems. However, disagreement exists about the Mg3Cd order transformation with respect to: 1) the location of the critical temperature for order, 165°C or 153"~,' and 2) how the degree of order varies with temperature. Welber et a1.5 concluded from specific heat measurements that the formation of Mg3Cd is a second-order reaction with the degree of order a continuous function of temperature, while Moore and Raynor concluded that it is neither a first-order reaction, with the degree of order a discontinuous function of temperature, nor a second-order reaction. Consequently it was considered necessary to undertake an X-ray investigation into the change in degree of order and structure in the

Jan 1, 1964

By Horace Pops, J. F. Libsch

THE discovery of SAP alloys (sintered aluminum powders) by lrmannl has stimulated investigations in other alloy systems.23 Not only do such alloys have good room-temperature properties, but they maintain high strength after prolonged service at elevated temperatures. In addition, they show high structural stability, including unusually high recrystallization temperatures. These characteristics are secured by dispersion hardening. For this investigation, Zn-ZnO alloys were selected. Practically, the fact that commercially pure zinc recrystallizes near room temperature prohibits strengthening and hardening by cold deformation and therefore limits the application of zinc where mechanical strength is important. Similarly, the poor

Jan 1, 1961

By P. L. Lavery

A numerical method to derive approximate solutions for stress intensity factors for rectilinearly anisotropic bodies without resolving to complex variable approach is presented. The method is based on the assumption that the crack opening profile can be simulated by a simple curve such as an elliptic function and a relationship is found for the stress intensity factor in terms of near tip displacements. An example solution is derived for a transversely isotropic body and the results are verified with Westergaard's stress function approach. The proposed model has a great potential for the applications to fracture mechanics of anisotropic rock materials.

Jan 1, 1984

By C. W. Tomlinson

The analyses which have been made by the writer according to the method described below were made as part of Professor Withey's investigation of the concrete aggregates1 of Wisconsin, in the hope of throwing light on the extent and nature of the influence of the mineral-ogical constitution of aggregates upon the properties of the concrete and mortar made from them. This method was found most satisfactory after four weeks of experiment and modification. It attains an accuracy quite sufficient for the purpose of the analysis, and is fairly rapid. mineralogical analyses may be thus made at a cost considerably less than that of chemical analyses of a similar degree of completeness. The results obtained by this method should not vary in any item by more than 1 per cent. of the total weight of the sample, and may be made very much better than this by the exercise of greater care in the microscopic counting (see below). The accuracy of the hand sorting is of course dependent upon the experience and carefulness of the analyst. After a month's practice, the writer was enabled to turn out these analyses at the rate of four in 33 hr. of working time. It was found most economical to handle four samples at once. The samples analyzed weighed from 290 to 340 g. each. The same method could be applied to larger or to smaller samples, within reasonable limits. The following list covers the necessary apparatus and equipment: 1 good balance capable of weighing accurately to tenths (or, better, hun- dredths) of a gram, and of handling quantities up to 200 g. in weight. 1 Westphal balance, registering densities to two or three decimal places. 1 Meker or Bunsen burner, and gas supply. 1 nest of sieves, 10, 20, 40, and 100 meshes to the inch.

Jan 1, 1916

By C. W. Tomlinson

INTRODUCTORY THE analyses which have been made by the writer according to the method described below were made as part of Professor Withey's investigation of the concrete aggregates' of Wisconsin, in the hope of throwing light on the extent and nature of the influence of the mineralogical constitution of aggregates upon the properties of the concrete, and mortar made from them. This method was found most satisfactory after four weeks of experiment and modification. It attains an accuracy quite sufficient for the purpose of the analysis, and is fairly rapid. Mineralogical analyses may be thus made at a cost considerably less than that of chemical analyses of a similar degree of completeness. The results obtained by this method should not vary in any item by more than 1 per cent. of the total weight of the sample, and may be made very much better than this by the exercise of greater care in the microscopic counting (see below). The accuracy of the hand sorting 'is of course dependent upon the experience and carefulness of the analyst. . After a month's practice, the writer was enabled to turn out these analyses at the rate of four in 33 hr. of working time. It was found most economical to handle four samples at once. The samples analyzed weighed froth 290 to 340 g. each. The same method could be applied to larger or to smaller samples, within reason able limits. The following list covers the necessary apparatus and equipment: 1 good balance capable of weighing accurately to tenths (or, better, hundredths) of a gram, and of handling quantities up to 200 g. in weight. 1 Westphal balance, registering densities to two or three decimal places. 1 Meker or Bunsen burner, and gas supply. 1 nest of sieves, 10, 20, 40, and 100 meshes to the inch.

Jan 5, 1915

By H. C. Heard

INTRODUCTION As the world's population expands and nations struggle to better their relative position and standard of living, increased emphasis is being directed to the exploration and production of mineral resources, to the mitigation of natural hazards such as earthquakes and volcanic eruptions, and to geotechnical engineering projects such as high-level nuclear waste disposal, underground military facilities, and transportation tunnels. Several topics are common to all of these endeavors. One is the characterization of the rock mass in situ, including the definition of the initial environment (e.g., temperature, stress, etc.). A second is, depending upon the use of the underground or the desired result, the manner in which the boundary conditions or the environment are to be changed by man. Next, the physicochemical behavior of the rock mass must be measured, or inferred with uncertainty limits placed on this behavior, over the appropriate range of environmental conditions (e.g., temperature, chemistry, etc.) for the application proposed. And last, an appropriate, validated predictive model must be applied to estimate the rock mass response to the perturbation. In the period preceding about 1955, only relatively simple testing of soils and rocks was commonplace, partly because the environment (depth) to which these data were applied was not so extreme as it is at present and partly because less precise predictions of material response were acceptable. Only limited and relatively simple test data seemed to be needed to guide the engineering. At the present time and certainly in the future, as we extend our interaction with the earth's crust to greater depths and impose more extreme perturbations on it, we need a larger body of data, deter- mined under much more complex conditions, in order to make the required predictions. The present societal problem of high-level radioactive waste disposal is a case in point. We in the rock

Jan 1, 1982

By Henry M. Howe

In my original paper, Piping and Segregation in Steel Ingots, I pointed out1 among other things that, in view of the slighter stretching (virtual expansion) of the crust, and greater opportunity for sagging, there should be less piping in broad than in narrow ingots, and less in slowly-cooled ingots, e.g., those cast in pre-heated sand molds, than in those which cool quickly, e.g., those cast in iron molds. A. A. Stevenson said that neither of these predictions agreed with his own experience. In particular, in a picture which he showed of a wide and of a narrow ingot cast from the same ladleful of steel: the wide ingot had certainly piped much more deeply than the narrow one. At the time I did not see the explanation of these discrepancies, but further reflection makes it evident. One of the most important elements in determining the depth of the pipe is the degree of " top-lag," that is, the degree to which the solidification of the top of the ingot lags behind that of the bottom. Through this lagging the steel of the upper part of the ingot is able to run down and fill the pipe below as fast as it forms. To the importance of this lagging I called attention in my original paper.' Sand us. Iron Molds.—If we compare two like ingots, one cast in an iron and the other in a sand mold, we see that the top-lag is much greater in the former than in the latter, because in the former the lower part of the ingot is cooling off fast while the metal is running into the upper part. It is perhaps easier to look at this as a case of the solidification of the hot-

Jan 1, 1910

By F. O. Garrabrant

Power is furnished to the Climax Molybdenum Co. by the Public Service Co. of Colorado over two 100,000-volt lines to a bank of three 3333-kva. transformers 100/13.8 kv. These transformers are so designed that with the addition of forced cooling their capacity may be increased 331/3 Per cent at 12,000-ft. altitude. Under present conditions, these transformers are operated at 140 per cent of their rating with forced air cooling. On the secondary side of this bank there is a 15-kv., 1200-amp. Westinghouse oil circuit breaker provided with automatic reclosing relays allowing three successive short circuits before lockout. From this breaker 13.8-kv. power is transmitted to a central switching station (Fig. I) where all circuits radiate to the different operations of the property. Each circuit is protected by a 23-kv., 600-amp. oil circuit breaker with by-pass and isolating disconnecting switches.

Jan 1, 1947

By B. L. Averba

THE determination of retained austenite by X-ray diffraction uses the following relationship:"" Pa = constant . RVaA (8) [1] where: P is the diffracted power from phase a; R, the calculated intensity factor; A, the absorption correction; 8, the diffraction angle; and Va, the irradiated volume of phase a For a flat sample making a glancing angle + with the incident beam the absorption correction is calculated as: * 1 sin (28 - 4) A .= 1 [2] µ sin, (28 — 4) + sin 4 where µ is the linear absorption coefficient. Beu3 has proposed that the computed absorption correction be combined with the constant and that the experimental observation of the absorption correction used in the original method be eliminated. This procedure is permissible only if: 1—There is no preferred orientation in the sample, and 2—The geometric requirements have been met precisely. If these conditions are not met the validity of the determination is questionable. Unfortunately the necessary conditions must be tested experimentally for each determination, and this is done most easily by observing whether the apparent absorption has the form of Eq. 2. In practice it may be convenient to plot P/R vs the parameter sin (2? — )[sin (28 — +) + sin +] to obtain straight lines for the ap- parent absorption correction. Deviations from straight lines indicate either that the sample has not been positioned correctly or that the relative intensities are incorrect. Geiger counter spectrometer methods also have been used successfully for retained austenite determinations. In the usual spectrometer arrangement the sample makes equal angles with the incident and diffracted beams (8 = ); thus the absorption correction is simply 1/2µ and independent of 8. The retained austenite is then easily calculated from integrated intensity measurements on austenite and martensite lines. If the austenite content is not too low and if excessive fluorescence is not encountered it is possible to use filtered radiation and a recording spectrometer. The integrated intensities are then proportional to the areas of the diffraction peaks. For lower austenite contents the following technique was used: A bent quartz monochromator and a Geiger counter spectrometer are employed. The monochromatic radiation is focused on the front slit, and the counter slit is made broad enough to include the entire line. A series of readings are taken in the vicinity of the diffraction peak. The highest reading includes the diffraction line plus background. The background is obtained from the average of several readings on each side of the peak. The integrated intensity is obtained by subtraction. CrK, and FeKa have been used for such determinations. This technique has been found to be as sensitive and as accurate as the photographic methods. In the spectrometer methods the ratio austenite/ martensite may be obtained from readings on austenite and martensite lines and the application of Eq. 1. It is also possible to use external standards and to obtain the austenite contents from measurements on the austenite lines alone. The small correction for carbides then becomes unnecessary. The best standards are probably samples with known

Jan 1, 1954

By Kenzo Ikeda

The Kosaka smelter is situated in the extreme northern end of Hondo (the main island of Japan) 15 mi. east of Odate, on the government railroad, to which it is connected by a private railway. It contains ten blast furnaces having a maximum daily capacity of 1600 short tons of ore, conducting a slow pyritic smelting entirely without coke or limestone, and with a charge carrying over 50 per cent. of briquetted and agglomerated fines. The matte (35 per cent. Cu) is blown in two basic-lined barrel converters, the blister copper (98.8 per cent. Cu) being cast at once into anodes. The adjoining refinery contains 600 tanks with a maximum capacity of 1300 tons of cathodes per month, the byproducts being gold, silver, and bismuth. At present, working at about half capacity, the whole plant consumes 2000 kw. of hydro-electric power, and employs 850 men and women. The ores are derived from two principal sources: The relatively new Hanaoka mine, 20 mi. from the smelter, yielding copper pyrites by underground mining, and the old Kosaka open-cut mine, 1 1/2 mi. from the smelter, yielding three different ores: (a) kuromono, a compact finegrained mixture of barite (32 per cent.), zinc blende, galena, and pyrite, the whole carrying about 2.5 per cent. Cu; (6) cupriferous pyrites with 2.4 per cent. Cu; (c) siliceous ore with 2 per cent. Cu. The Hanaoka ore now constitutes approximately one-half of the charge, almost replacing the Kosaka kuromono which was the ore chiefly smelted until 1913.'

Jan 1, 1923