By R. K. Dann, L. W. Roberts, R. B. Benson

The mechanical properties of 300-series stainless steels were investigated in both high-pressure hydrogen and helium environments at ambient temperatures. An auslenitic steel which is unstable with respect to formation of strain-induced a (bee) and € (hcp) mar-tensile is embrittled when plastically strained in a hydrogen environment. A stable austenitic steel is not embriltled when tested under the same conditions. The presence of hydrogen causes embrittlement at the mar-lensitic structure and a definite change in the general fracture mode from a ductile to a quasicleavage type. The embrittled martensitic facets are surrounded by a more ductile type fracture which suggests that the presence of hydrogen initiates microcracks at the martensitic structure. If a steel is unstable with respecl to fortnation of strain induced martensile, plastic deformation in a hydrogen environment will produce rapid embrittlement of a notched specimen in comparison to an unnotched one. FERRITIC and martensitic steels can be embrittled by hydrogen that has been introduced into the alloys, either by thermal or cathodic charging prior to testing.1-5 However, conflicting reports exist as to whether austenitic steels that are stable or unstable with respect to formation of strain-induced martensite can be embrittled by hydrogen.8-12 A recent investigation has shown that cathodically-charged thin foils of a stable austenitic steel can be embrittled.13 An earlier investigation of a thermally charged 18-10 stainless steel revealed a significant decrease in the ductility only at the lowest test temperature of -78°C, although strain-induced bee martensite was shown to be present in one specimen tested at ambient temperatures.' When martensitic steels are tested in a hydrogen atmosphere, they are embrittled.'4-'7 It has been observed in this Laboratory that 304L steel, which is unstable with respect to formation of strain induced martensite, forms surface cracks when plastically strained in a high-pressure hydrogen environment. Work in progress elsewhere concurrent with this investigation has also established that 304L is embrittled when tested in a high-pressure hydrogen atmosphere." The objective of this investigation was to study the effect of a high-pressure hydrogen environment on the tensile properties of a stainless steel that contained strain-induced martensite (304L) and one that did not (310). EXPERIMENTAL TECHNIQUES Notched and unnotched cylindrical specimens were machined from 304L* and 310 rods that were heat- treated at 1000°C in argon for 1 hr followed by a water quench. The chemical analyses of these steels are given in Table I. The unnotched specimens had a reduced section diameter of 0.184 & 0.001 in., a gage length of 0.7 in., and were threaded with a 0.5-in.-diam. thread on each end. The notched specimens had a reduced section diameter of 0.260 * 0.001 in. and a 0.75-in. gage length, with a 30 pct 60 deg v-notch at the center. The notch had a maximum root radius of 0.002 in. The tensile bars were fractured in a hydrogen or helium atmosphere of 104 psi at ambient temperatures. The system used for mechanically testing the specimens is to be described in detail elsewhere.19 Several specimens of each type were tested in air using an Instron testing machine. The same yield strength and ultimate tensile strength were obtained in 104 psi helium with the above system as with the conventional testing machine. Magnetic analysis was employed to determine that there was a (bee) martensite in plastically deformed 304L and that it was not present in plastically deformed 310. The magnetic technique depended on allowing the material being studied to serve as the core between a primary and secondary coil. Thus, any change in the amount of magnetic material present between the annealed and plastically deformed steels will be indicated by corresponding changes in the induced voltage in the secondary circuit." The ratio of the output signal of a nonmagnetic stainless steel to a completely magnetic maraging steel was 2000 to I. Several unnotched 304L bars tested in hydrogen were analyzed for hydrogen by vacuum fusion analysis. There was an increase in the hydrogen content to approximately 2 ppm for the specimens tested in hydrogen, as compared to less than 1 ppm for the as-received material. Several thin sections cut from notched areas of 304L specimens tested in hydrogen and containing the fracture surface contained approximately 1.5 ppm H. The accuracy of these determinations was estimated to be ± 50 pct.

Jan 1, 1969

By A. J. Fenn

Long experience with underground mining inspired the unusual idea of using an underground crusher-conveyor system as a substitute for surface haulage at the Cananea open-pit copper mine in Sonora, Mexico. Now implemented and working well, the system has born out the expectations of its originator, Cia. Minera de Cananea S.A. de C.V., that it would effect substantial cuts in the high cost of haulage. The Cananea deposit is a large, low-grade orebody above the mined-out Colorada pipe which was once one of the largest high-grade underground deposits in the district. Present facilities at the pit consist of: (1) A large open-pit mine capable of moving 80,000 tons of material per day with a shovel-truck, underground crusher and belt conveyor haulage system. (2) A 25,000-tpd concentrator equipped for four stages of crushing, rod mill-ball mill grinding with cyclone classification, and flotation in conventional machines. (3) A dump leaching process producing 1 million lb of copper per month in a tin-can scrap precipitation plant. (4) A two-reverberatory, six-converter smelter which can make 140 tons of blister copper per day. (5) A well-integrated contingent of supporting departments running the gauntlet from housing to power generation.

Jan 3, 1969

By Kun Li, Alex Simkovich

The rate of dissolution of alumina in carbon-saturated liquid iron has been studied experimentally in a system where alumina was in the form of a cylindrical rod immersed in an iron bath contained in a graphite crucible. Data obtained consisted of the concentrations of aluminum in the melt as a function of time. In the case of static experiments, the data are shown to agree with theoretical prdictions based on the diffusion of aluminum.. The rate of dissolution was greatly increased by the rotation of the alumina rod. It is concluded that the diffusion of aluminum from the alumina/metal interface is the rate-controlling step. In the past, thermodynamic investigations of systems encountered in ferrous process metallurgy have received widespread attention. More recently, considerable work has been devoted to the study of kinetics associated with these systems in an effort to determine their rate controlling mechanisms. The alumina-iron system is of great importance in ferrous metallurgy. Yet information concerning kinetics of reaction in this system is seriously limited. The present study was made in order to establish the rate-controlling step for dissolution of solid alumina in liquid iron. LITERATURE REVIEW A number of papers concerning dissolution of solid metals in liquid metals have been reported in the literat~re. Generally, for these simple systems, dissolution is controlled by mass transfer of the dissolving species. Complex systems involving dissolution of solid metal carbides and oxides in liquid metals and slags have been studied to a much lesser extent. Skolnick5,6 reported on the reaction between liquid cobalt and poly-crystalline cylinders of tungsten carbide, in which the cylinders were dissolved while being rotated about their longitudinal axes at various speeds and temperatures. As a result of unexpected preferential grain boundary attack by the liquid cobalt, large errors in the measured dissolution rates occurred because of loss of tungsten carbide grains to the liquid cobalt. Nevertheless, it was possible to establish that the liquid Co-W carbide reaction was not controlled by mass transfer. In a similar approach, cooper7 was able to show that artificial sapphire rods, (alumina single crystals) dissolving in lime-alumina-silica slags obeyed a mechanism of mass transfer control. Here, again, the rods were rotated at various speeds and temperatures, and the process was followed as a function of these variables. Forster and Knacke8 took a practical approach to reaction between slags and refractories. By blowing argon through refractory cylinders of silica, silli-manite, or dolomite and directing the gas to rise along the slag-refractory interface, it was possible to increase the rate of mass transfer. Although the method was admittedly crude, it nevertheless permitted an evaluation of the relative stabilities of refractories with respect to slag attack. Data were interpreted on the basis of mass transfer control. EXPERIMENTAL TECHNIQUE Apparatus. An illustration of the apparatus used in this study is shown in Fig. 1. The furnace consisted of a Morganite recrystallized alumina tube wound with a molybdenum coil. A secondary molybdenum heater was mounted around the upper half of the primary coil to aid in controlling the thermal gradient within the furnace. The primary heater tube was 3 in. in ID and 30 in. long. A reducing mixture of 95 pct N and 5 pct H was maintained around the heating elements. Thermal insulation was provided by alumina powder. The chamber within the primary combustion tube contained a boron nitride block near the top to assist in controlling the thermal gradient to the furnace and also to provide a bearing surface for the rotating graphite shaft. The outside diameter of the graphite shaft was $ in. A separate threaded graphite specimen holder was screwed into the end of the shaft. The holder contained a tapered hole drilled into the end to guide the oxide specimens as they were pressed into it for mounting. Additional guidance for the rotating graphite shaft was furnished by a water-cooled bronze bushing attached to the top of the furnace. A steel clamp was fastened to the upper end of the graphite shaft and rested on a thrust bearing; the shaft and clamp were driven by a dc motor through a set of gears. Two O-rings located immediately above the bronze bushing maintained a gas-tight seal about the graphite shaft. The lower half of the alumina tube housed the crucible and charge, which were placed on a 3/4-in. diam movable alumina support tube. With this arrangement, charges could be inserted into or removed from the furnace while the hot zone was maintained at or above 1000°C. To control the temperature of the furnace, the thermocouple was mounted inside the support tube and in contact with the crucible bottom. Stray electric fields in the furnace were of sufficient intensity to cause erratic indications by the thermocouple. By enclosing the thermocouple protection tube in a molybdenum sheath and grounding this shield, the problem was eliminated. Output of the thermocouple went to an automatic continuous balance controller. Procedure. A typical run was as follows. First, electrolytic iron was premelted in graphite crucibles and cast into graphite molds with the same configura-

Jan 1, 1970

By John Sullivan

Resources for Freedom, a report by the President's Materials Policy Commission, commonly termed either the Paley report, after its chairman, or the PMPC report, was issued in June 1952. The data collecting and assembly work for its preparation were done in 1951. The statistical base in most cases was 1950. It reviewed our economy and predicted what it will be in 1975.* The bases for the predictions were given. Consideration was given not only to statistical data and trends but also to technological changes taking place and likely to take place in the ensuing 25 years that will affect our economy. The supply of raw materials was studied and predictions made as to the availability of supply and the sources in 1975. One of the industries covered was iron and steel. For the most part the report did not attempt to provide a curve showing annual growth for any industry or commodity. It contrasted 1950 with the probable status in 1975. Interpolation between these dates is difficult and the Commission did not intend that it be used for short interim intervals. It is possible in 1958 to show the actual changes from 1950. The magnitude of the changes illustrates the agreement with some interpolation of the Paley report. Statistical comparisons can be general only because the Commission did not postulate a linear change. A study of the iron and steel industry will show if the general predictions have been realized or if gross errors were made. This paper is concerned with such an analysis. It is concerned with the production and consumption of crude, not fabricated products. It attempts to bring various facets of technical and statistical information on the industry up to date.

Jan 8, 1959

By Clarence Wright

THE average lead and zinc content of the ores mined and milled in the Joplin district is low as compared with that of other lead and zinc deposits throughout the United States. Because of this fact and of the high grade of the concentrates, the ratio of concentration is unusually high. Most of the operating companies have aimed to produce as high a grade of concentrate as possible in order to obtain the highest price for their product. They have done this at the sacrifice of the percentage of zinc recovered. The average percentage of zinc recovery is from 60 to 70 per cent. For percentage of recoveries from actual mill tests, see tables. The concentration is commonly effected by crushing the ore to h-in. (12.7 mm.) size and subjecting it to a roughing and cleaning over two or more large Cooley jigs, of the Harz type, the finer sands being treated on the usual types of sand and slime tables. The treatment of slimes by flotation is being tested at several of the larger mills. COARSE CONCENTRATION When the ore. has been hoisted from the mine it is dumped onto a chute leading to a grizzly made of iron bars, usually heavy rails, spaced 4 to -5 in. (101 to 127 mm.) apart. The oversize is caught on the grizzly, the mineralized pieces are broken with sledge hammers so as to pass through, and the boulders that are practically barren are sorted out by hand and trammed to the waste-rock pile. The proportion of waste rock thus sorted out varies from a fraction of 1 per cent to 15 per cent., depending on the nature of the rock.

Jan 10, 1917

By B. Hyatt, E. Klokholm

The reesistivity of Cu-Pd alloys of 9.6 to 29 pct Pd alloys was measured after plastic deformzation in tension. For all compositions a continzting decrease in resistivity with increasing plastic strain was observed. By comparison with the results of Damask on a brass ad Cu3Au, it was deduced that these anonzalous decreases in resistivity are due to the decrease in short-vunge order caused by cold work. An anomalous decrease in the resistivity of cold-worked CU-Pd alloys was first reported by Jaumot and Sawatzky.' They observed decreases in the electrical resistivity when disordered Cu-Pd alloys drawing at room temperature. Recently, a similar anomaly was reported by Aarts and Houston-Mac-Mi1lan2 in Ag-Pd alloys containing 10 to 45 pct Pd. The plastic deformation in this case was produced by tensile strain at liquid-nitrogen temperatures. For AE-Pd alloys the relative resistivity change becomes positive for tensile strains of about 20 pct.

Jan 1, 1960

By D. H. Baldwin, R. E. Reed-Hill

Six compositions of polycrystalline ZY-0 alloys, containing up to 4.2 at. pct 0, were tested in tension between 77° and 600° K. The data obtained from each of the compositions corresponded closely to a rela-ion between yield stress and absolute temperature of the form In s/so = BT, where oo is the yield stress extrapolated to zero degrees and B is a constant. In agreement with others who have observed this relationship, it is shown that the activation energy may be expressed as Ho In so/s. In the present specimens Ho is approximately 18,000 cal per mole and is apparently independent of temperature and composition inside the limits of the investigation. It is also demonstrated that this form of activation energy cowesponds to a strain rate sensitivity parameter RT/Ho. Oxygen was also noted to have an effect upon the operative deformation mechanisms. With increasing oxygen concentration there was an increased tendency to observe both nonbasal slip and cross-slip phenomena. Oxygen does not seriously inhibit twinning more than it does slip. Twins were observed in all specimens tested. It is becoming increasingly evident that interstitial atoms in solid solution are able to interact strongly with mobile dislocations. Stein, Low, and seybolt,&apos; have shown that, if the carbon concentration in bcc iron is lowered below the solubility limit, its flow stress temperature dependence is markedly reduced. This suggests that carbon atoms in interstitial solid solution may be responsible for the pronounced temperature dependence of the flow stress normally observed in iron. This view has recently been challenged by Leslie and sober2 who observed a strong flow stress temperature dependence in iron to which a trace of titanium had been added in order to remove carbon atoms from solution. Since the interstitial concentration must be reduced below approximately 1 ppm in order to produce a pronounced effect on the flow stress temperature dependence,&apos; studies of the effect of interstitials on the flow stress in iron necessarily involve serious experimental difficulties in alloy preparation. There are other metals, however, in which strong effects of interstitial solutes upon both the flow stress and its temperature dependence are observed. Of particular significance is zirconium which, according to Domagala and Mcpherson, 3 is capable of dissolving 28.6 at. pct O. The O-Zr alloy system is an almost ideal system for studying the interaction of interstitial atoms with deformation modes since it is possible to form alloys capable of study over an extensive range of compositions. Mills has made such a study using single crystals oriented primarily for single prismatic slip4 and has found an effect of oxygen concentration on the flow stress temperature dependence analogous to that observed in iron due to carbon by Stein, Low, and Seybolt. The present paper is specifically concerned with the effect of oxygen on deformation in polycrystalline zirconium. Although plastic flow in this type of specimen is much more complex than that reported for the single-crystal work, and involves both slip (on several different types of planes) and mechanical twinning, the results of this investigation are in general agreement with the single-crystal observations concerning the effect of oxygen on the temperature dependence of the flow stress. In addition, they also demonstrate that oxygen affects the acting deformation systems. This is in contrast to single-crystal results4 that showed only single slip on a prism plane. EXPERIMENTAL PROCEDURE Material. High-purity hot-rolled zirconium strip, 0.2 in. thick by 4 in. wide, of 0.10-mm average grain diameter, was used for forming alloys. It was obtained from the Carborundum Metals Co., Akron, N.Y., whose analysis indicated the major impurities were, in wt ppm: Hf, 540, C, 145; Fe, 100; and 0, <80. The plate texture was similar to a wire texture, with basal planes generally parallel to the rolling direction and basal poles randomly distributed about the rolling direction. The heat treatments described below did not appreciably alter the basic texture. specimen Preparation. Small threaded-end tensile specimens were machined from the plate with axes perpendicular to the rolling direction. These transverse specimens had gage sections 1 in. long by 0.060 in. in diam. The small gage section diameter was dictated by the fact that the alloys were formed by dif-

Jan 1, 1969

By Arthur F. TQggQrt

THE approximate status of education in ore dressing in 1871 is reflected by Rossiter W. Raymond in an article written at that time presenting the curricula and descriptions of the laboratories at the various mining schools in the United States. For the most part, the curricula in which ore dressing was taught were for mining engineering. They comprised courses in geology, mining, and pyrometallurgy about equal in point or credit weights; a short course in ore dressing, and a somewhat longer course in assaying; and courses in surveying, hydraulics, power, and strength of materials-all superimposed on a broad foundation of physics, chemistry, and mathematics. Some curricula contained a fair content of the humanities. Then, as now, the emphasis on fundamentals was greater in the older colleges and universities. The report on the Columbia School of Mines, then relatively young, emphasized that a large percentage of its students were college graduates. As technical and scientific knowledge grew, first metallurgy and then geology were set up as separate curricula. So far as curriculum designation is con-

Jan 1, 1947

By R. Shuttleworth, R. Smith

A Knudsen effusion tnethod I~as been used lo measure the vapor pressure of pure iron in the temperature range 1000° to 1500°C. Neutron-irradiated , natural iron was used and the Mn&apos;~proclzdced by the (n, p) reaction removed by evaporation at high temperature. The results can be represented by the equation: where pM - 1.088 x 107 atm and T, = 20,890°K. A value of 100.2 kcal per g- atom was obtained for AH;. THE vapor pressure of pure iron in the temperature range 1000" to 1500°C has been measured. Radioactive iron and a Knudsen cell technique were used and the Mn&apos; produced by an (n, p) reaction removed by evaporation at high temperature. From the variation of vapor pressure with temperature values of the enthalpy and entropy of solid iron have been found. Previous workers2 used a Lang-muir method and measurements were made over a smaller temperature range than that in this work. EXPERIMENTAL The apparatus used was similar to that of Pyle and Shuttleworth, and McLellan and Shuttle worth. However, because of the higher temperatures the Knudsen cell was machined from tungsten bar and the flanged furnace tube was beryllia. Heating was by passing a high current (70 amp at 7 v for 1500°K) through a strip of tantalum foil laid across the top of the cell and through a turn of molybdenum wire around the furnace tube. This method of heating ensured that the top of the cell was slightly hotter than the base and prevented condensation and re-evaporation from the orifice. The temperature was measured by means of a pt/Pt 13 pct Rh thermocouple spot-welded to the base of the crucible. To ensure accurate temperature measurement the iron was in the form of a thin disc (0.75 cm diam by 0.075 cm) which lay on the base of the cell. The high-purity iron was irradiated in the Harwell pile for a week at a neutron flux of 1.2 X 10" neutrons per sq cm per sec. The isotopes fe&apos;~ and Fe" are produced by (n! y) reactions but only Fe", half-life 45.1 days, is a emitter; Mn which is also a y emitter, half-life 300 days, is produced simultaneously by an (n,p) reaction.&apos; Immediately after irradiation of natural iron the ratio of ~e" to Mn y activity was 100:l. However, manganese is very much more volatile than iron and almost all the y activity of the condensate is due to Mn&apos;~. Thus it was essential to eliminate all the manganeses before any measurement of the vapor pressure of iron was made and this was done by preliminary heating for 20 hr at 1400°C. For each determination the iron was dissolved from the target with acid and the y activity compared to a known weight of iron. By means of a y-ray spectrometer the y-activity measurements were made at the 1.09-mev peak of the 17e5&apos; spectrum where the background was of the order of 3 cpm. Despite the low specific activity of ~e" a mass of 10- " g of iron could be determined corresponding to a vapor pressure of about l0-&apos;&apos; atm. RESULTS The vapor pressures were calculated from the equation: Where m is the mass of iron effusing in a time t through an orifice of area a2, r is the radius of the target, Z is the distance from the orifice to the

Jan 1, 1965

By R. E. Ogilvie, J. I. Goldstein

The a and y solubility limits in the Fe-Ni phase diagram have been redetermined at temperatures above 500°C. Both a diffusion-couple and a quench and anneal technique were used. The solubility limits were measured with an electron-probe micro-analyzer. The nickel concentration at the phase boundary is increased below 700°C and the a solid-solubility range is much larger than had been previously measured. The solubility limits are also extrapolated to 300°C. It is suggested that the solubility of nickel in a FeNi reaches a maximum in the temperature interval 400o to 500°C. THE equilibrium diagram has been of great use in the field of meteoritics, where the phase relations between kamacite (a) and taenite (?) in metallic meteorites can be described by means of the Fe-Ni diagram. The study of metallic meteorites by electron-probe microanalysis has cast some doubt on the accuracy of the presently available Fe-Ni diagrams.1, 2 Recent thermodynamic studies of the Fe-Ni system also suggest that the diagram may be in error.3 For these reasons the high-temperature (800o to 500°C) part of the diagram was redetermined. INTRODUCTION The currently accepted Fe-Ni diagram is that of Owen and Liu.4 Above 910°C, there is a region of complete solid solubility, ? (fee). Below 910°C, the a (bee) phase is stable in pure iron. The effect of increasing amounts of nickel is to stabilize the y phase. The phases that form when Fe-Ni alloys are heated or cooled bear little relation to the equilibrium diagram. If an alloy is cooled from the y state and held at a temperature within the a + y field, no evidence has been found for the occurrence of the y - a transformation.5 If the alloy is cooled to low enough temperatures the y phase breaks down into a supersaturated bee phase called a2. In fact, in alloys over 27 pet Ni the y phase is retained at room temperature.6 The a, phase has the same composition as the original y. The temperature at which a2 forms, the M, temperature, has been determined experimentally.&apos; A state of equilibrium can be approached by cooling below M, to form a2 and then reheating the alloy into the two-phase region of the diagram. The y phase will then begin to precipitate out of the a2 phase and grow. The growth of the phase, however, is quite slow. Using the interdiffusion coefficients -Da of Goldstein et al.,8 it is estimated that it takes about 1 year to grow a 10-µ-wide region of ? at 700°C in a 5 pet Ni alloy. Owen and Liu4 used the technique just described to form the equilibrium phases. The phases present were determined by means of X-ray analysis. The accuracy of their diagram depends on the number of alloys available near the phase boundary at a given temperature. In this study two different techniques were used to determine the a/a + ? and ?/a + ? solubility limits. The inherent accuracy of both techniques was greatly improved over that used by previous investigators because the phase-boundary compositions were measured with an electron-probe microanalyzer. PROCEDURE The two methods used to determine the Fe-Ni diagram are the diffusion couple (D.C.) and the quench-and-anneal (Q.+A.) techniques. In the first method, diffusion couples whose diffusion path goes through a two-phase region of the phase diagram were used. A description of the technique used for making the diffusion couples has been described in a previous paper.&apos; After the diffusion treatment a discontinuity in the resultant concentration vs distance profile was measured. The nickel concentrations in the a and ? phases at the interface of the discontinuity are the solubility limits of the a and ? phases in the phase diagram at the diffusion temperature. If the interface com-

Jan 1, 1965

By F. N. Rhines, B. H. Alexander

MUCH attention has been directed to the effects of grain size upon the properties of alloys, but there has been scant study either of the conditions that determine the pattern and dimensions of den-drites in metal systems, or of the influence of their shape and size upon the overall properties of cast-ings. The aim of the research that is about to be described has been to investigate the effect of vari-ous factors upon the mode of formation of dendrites in alloys by measurements of the distance between adjacent dendrite arms (dendrite spacing). Early investigators, including Grignonl and Tschernoff,2 showed that a metal dendrite is com-posed of a tree-like system of stalks and branches arranged in a simple geometrical pattern. North-cott and Thomas3 demonstrated that, in the face-centered cubic solid solutions of copper-base, these stalks and side arms all lie in (100) directions in the crystal. Several investigators, including Sauveur and Chou,0 Sauveur and Reed,&apos; and Martin and Mar-tina have reported that the addition to steel of alloy-ing elements, such as nickel, chromium, and molybdenum, not only makes the dendrites easier to reveal by etching, but makes them coarser. The latter authors8 proposed that the coarsening of the dendrites is roughly proportional to the increase in the temperature range of freezing, caused by adding the alloying elements. Sauveur and Chou6 showed, in addition, that the dendrites are coarsened by a decreased rate of cooling of the casting. Measurement of Dendrite Arm Spacing Among the physical conditions that could be ex-pected to have an influence upon the dendrite arm spacing, that appears in a cast metal, are: composi-tion, rate of freezing, crystal structure, and type of constitution. The relationships obtaining between these variables and the dendrite dimensions have been examined, in the present research, by measur- ing the arm spacing in a wide variety of alloys, listed in tables II through VI. Alloy compositions are recorded in the tables by showing the symbol of the major metal followed by the percentage and symbol of the alloying agent; thus, "Al-10Ag" is an aluminum-base alloy containing 10 pct of silver. Although none of the alloys were analyzed, an im-pression of their degree of purity may be obtained from that of their component metals given in table I. Five hundred grams of each alloy was made by melting in small clay-graphite crucibles in an elec-tric muffle furnace. After alloying the temperature was adjusted to 50" to 75°C above the liquidus and the melts were poured into cast iron molds, at room temperature, the molds having a wall thickness of 1 in. and a cavity 11/2 in. sq in cross-section. Each ingot, thus cast, was sectioned at mid-height and the sectioned surface was polished and etched for metallographic examination. Dendrite spacing meas-urements were made at three positions, namely, ad-jacent to the mold wall, midway between the wall and the center of the ingot, and at the center (desig-nated e, m, and c respectively, in the tables). A typical series of microstructures is presented in fig. 1. For each measurement, the average was taken of the dendrite spacing of several grains covering a zone about 2 mm wide. Only those grains which had a major dendrite axis nearly in the plane of polish were selected in order to eliminate corrections for orientation differences from grain to grain. Although the dendrite spacings were measured to the nearest thousandth of a millimeter, the values listed in the tables are thought to be significant only to the nearest hundredth of a millimeter. The larg-est difference in readings found, when various ob-servers rated the same specimens, was 0.012 mm; the largest difference between corresponding meas-urements upon duplicate specimens was 0.027 mm.

Jan 1, 1951

By Frederick M. Becket, Russell Franks

In a recent article,l which described the softening effect of columbium in plain high-chromium steels, the authors stated that their investigations had shown columbium to be also a particularly valuable inhibitor of intergranular corrosion in steels of the 18 per cent chromium, 8 per cent nickel type. It is the purpose of the present paper to record some of the results obtained through the introduction of columbium to the austenitic chromium-nickel steels. The damaging effects of this type of corrosion have become so widely known as to restrict considerably the applications of the steels under consideration, and therefore there is little question of the importance of the goal to be attained. Numerous contributions concerning the susceptibility of the austenitic chromium-nickel steels to intergranular corrosion have appeared during the past few years, and among others who have dealt constructively with the subject are such well-known authors as Strauss and Houdremont of Germany, Hatfield of England, and Bain in the United States. Different theories have been propounded as to the cause of intergranular corrosion, and various remedial measures have been proposed, the majority of which involve the use of addition agents. Titanium is the addition agent at present most generally employed, as suggested by Houdremont and modified as described by Bain, Aborn and Rutherford. Little has been published on the effects of holding these steels for long periods at the relatively lower temperatures in the presence of corroding media, and the effects have mot been fully realized by producer and consumer.

Jan 1, 1934

By J. Chipman, N. J. Grant, H. L. Bishop, H. N. Lander

Data of several studies on the equilibrium between molten iron and open hearth-type slags have been combined to determine some of the chemical reactions involved in steel-making. Effects of slag composition and temperature on the iron oxide activity, distribution of sulfur between slag and metal, and the carbon content of the metal are discussed. Also, an overall reaction for the equilibrium between sulfur and oxygen is presented. DURING the past 15 years, a number of significant equilibrium studies have been carried out between liquid iron and simple basic and acid slags in an effort to throw light on the chemical reactions involved in steelmaking. This paper is a summary of the experimental reports on investigations which have been conducted at the Massachusetts Institute of Technology, and of related work in other laboratories. The investigations summarized in this paper include the works of Fetters and Chipman1 and Taylor and Chipman,&apos; which dealt with simple slags that are similar to those found in the open hearth. The sulfur determinations of the slag-metal tests of Fetters and Chipman as reported by Grant and Chip-man" are included. Also, the investigations by Win-kler and Chipman&apos; and Grant and ChipmanQ f more complex slag systems are included in this summary. The experimental procedure is described in detail in each of these papers and will not be discussed. Since the previous reports have been somewhat independent, it is desirable to review and combine the data of the various investigations to determine, as accurately as possible, the reactions in the slag-metal systems of the open hearth. It is the object of this report to present the combined data in such a way as to enhance their utility and applicability. Oxidizing Power of Slags of the System (CaO+MgO)-Si0,-FeO in Equilibrium with Carbon-Free lron The slags selected to determine the iron oxide activity in equilibrium with pure liquid iron were those containing less than 2 pct each of P,O,, MnO, or A1,0, on a weight percentage basis. The method used to calculate activities of iron oxide in liquid slags was that developed by Taylor and Chipman.&apos; The solubility of oxygen in molten carbon-free iron under pure iron oxide slags can be expressed by the following eauation —6320 log (pctO)-------------— + 2.734 [1] where T is the absolute temperature. The oxygen solubility values as determined from Eq. 1 were used throughout this study to calculate the iron oxide activity. The iron oxide activities of slags of various iron oxide contents are plotted in Fig. 1 as a function of the basicity, which is defined as the ratio (pct CaO + pct MgO)/pct SiO,, and are based on molecular percentage values of the components. The percent (FeO), is the total iron content in the slag calculated to FeO. Fig. 1 shows that as the basicity increases at constant mol pct (FeO),, the iron oxide activity increases rapidly and reaches a plateau which extends on the basicity scale from about 1.3 to 2.3; the iron oxide activity then decreases rapidly until a basicity of about 3.0 is reached, where it tends to level off. The solid portions of the curves represent the experimental data of Fetters and Chipman and Win-kler and Chipman. Their experimental heats were made in magnesia crucibles, and hence the slags were saturated with magnesia. The broken lines on the left represent the experimental data of Taylor and Chipman, who used a rotating crucible. In general, these slags contained less than 3 pct MgO. The absence of data for slags containing less than about 40 mol pct (FeO), and basicity ratios greater than about 2.5 made it necessary to calculate curves using ionic concepts of slags. The broken lines on the right, which disregard the solubility limits of di and tricalcium silicate and lime, were obtained by following the treatment of Flood and Grjotheim,"

Jan 1, 1957

By M. M. Fine

THE problem of producing a uniform, medium-fine sand for glass-furnace feed has been of interest to the glass-container industry for many years. In the present investigation of the problem, conducted by the Bureau of Mines in cooperation with the Owens-Illinois Glass Co., Alton, Ill., a satisfactory method of producing such sand was developed. The investigation involved continuous-grinding studies of glass sand with flint and porcelain pebbles, steel balls and rods, and a simultaneous study of classification. The most satisfactory procedure consisted of grinding in a pebble or ball mill followed by a double classification: hydraulic classification to separate the oversize for return to the grinding unit and mechanical classification to remove fines and impurities from the ground sand. The proper application of this flowsheet usually yielded a graded sand containing less iron than the feed even when grinding was done in a steel-lined ball mill. The amount of sand ground into the so-called "dusting" sizes was, in all cases, less than 10 pct. Experiments were made which showed that this very fine sand could be beneficiated to a usable material. Background The advantages in utilizing a uniform, medium-fine sand as a feed for glass furnaces has motivated a considerable amount of research on the ,problem of producing such sand by glass producers and others. For the glass producer, the faster melting rate of such a graded sand offers the possibilities of reduced fuel costs and increased furnace capacity. In addition, there is the likelihood of improving the quality of the melt and thereby reducing the number of seeds (air bubbles) and stones (unrnelted grains) in the finished ware. Although the melting rate of a glass batch depends on other factors in addition to the grain size of the sand, there is experimental evidence to show that grain size influences the melting rate considerably. Potts, Brookover, and Burch&apos; found that when the raw materials (sand, soda ash, and limestone) were always matched in- size, there was a great decrease in the melting time as the grain size of the materials was decreased. They found, too, that when the grain sizes of the soda ash and Limestone were held constant at 40 to 60 mesh, the minimum melting time occurred when 40 to 60 mesh sand was used. The increase in melting time with decrease in grain size beyond 40 to 60 mesh was due, they postulated, to accelerated demixing or separation of batch during melting as the grain size of the sand decreased in relation to the grain size of the other materials. An earlier investigatora found that the highest rate of melting and purifying ordinary glass was obtained when medium-size sand (0.385 to 0.120 mm, correspondingly roughly to 40 to 120 mesh) was used. Although batches containing smaller-size sand were found to fuse more rapidly, the time required to remove air bubbles from such melts actually increased the total duration of the process. Coarsegrained sand, it was stated, increased greatly the times of both melting and purifying. Although the laboratory data are difficult to confirm on a plant scale, observations by the Owens-Illinois Glass Co. indicate a higher furnace capacity of better-quality ware when a medium-fine sand is used in the batch. During the recent war, the glass producer was inclined to overlook a considerable variation in raw materials in the interest of higher production. For instance, table I shows the wide range in the amounts of various screen fractions in sand supplied by one producer to the Terre Haute plant of Owens-Illinois. The sand, from the northern Illinois St. Peter sandstone, represented material used by that plant over a period of a few years during the war. Since the war, the glass industry has insisted on

Jan 1, 1951

By M. M. Fine

THE problem of producing a uniform, medium-fine sand for glass-furnace feed has been of interest to the glass-container industry for many years. In the present investigation of the problem, conducted by the Bureau of Mines in cooperation with the Owens-Illinois Glass Co., Alton, Ill., a satisfactory method of producing such sand was developed. The investigation involved continuous-grinding studies of glass sand with flint and porcelain pebbles, steel balls and rods, and a simultaneous study of classification. The most satisfactory procedure consisted of grinding in a pebble or ball mill followed by a double classification: hydraulic classification to separate the oversize for return to the grinding unit and mechanical classification to remove fines and impurities from the ground sand. The proper application of this flowsheet usually yielded a graded sand containing less iron than the feed even when grinding was done in a steel-lined ball mill. The amount of sand ground into the so-called "dusting" sizes was, in all cases, less than 10 pct. Experiments were made which showed that this very fine sand could be beneficiated to a usable material. Background The advantages in utilizing a uniform, medium-fine sand as a feed for glass furnaces has motivated a considerable amount of research on the ,problem of producing such sand by glass producers and others. For the glass producer, the faster melting rate of such a graded sand offers the possibilities of reduced fuel costs and increased furnace capacity. In addition, there is the likelihood of improving the quality of the melt and thereby reducing the number of seeds (air bubbles) and stones (unrnelted grains) in the finished ware. Although the melting rate of a glass batch depends on other factors in addition to the grain size of the sand, there is experimental evidence to show that grain size influences the melting rate considerably. Potts, Brookover, and Burch&apos; found that when the raw materials (sand, soda ash, and limestone) were always matched in- size, there was a great decrease in the melting time as the grain size of the materials was decreased. They found, too, that when the grain sizes of the soda ash and Limestone were held constant at 40 to 60 mesh, the minimum melting time occurred when 40 to 60 mesh sand was used. The increase in melting time with decrease in grain size beyond 40 to 60 mesh was due, they postulated, to accelerated demixing or separation of batch during melting as the grain size of the sand decreased in relation to the grain size of the other materials. An earlier investigatora found that the highest rate of melting and purifying ordinary glass was obtained when medium-size sand (0.385 to 0.120 mm, correspondingly roughly to 40 to 120 mesh) was used. Although batches containing smaller-size sand were found to fuse more rapidly, the time required to remove air bubbles from such melts actually increased the total duration of the process. Coarsegrained sand, it was stated, increased greatly the times of both melting and purifying. Although the laboratory data are difficult to confirm on a plant scale, observations by the Owens-Illinois Glass Co. indicate a higher furnace capacity of better-quality ware when a medium-fine sand is used in the batch. During the recent war, the glass producer was inclined to overlook a considerable variation in raw materials in the interest of higher production. For instance, table I shows the wide range in the amounts of various screen fractions in sand supplied by one producer to the Terre Haute plant of Owens-Illinois. The sand, from the northern Illinois St. Peter sandstone, represented material used by that plant over a period of a few years during the war. Since the war, the glass industry has insisted on

Jan 1, 1951

By George Macready

TRINIDAD, British West Indies, is an island near the north coast of South America, situated between latitudes 10° and 11° N:, and. opposite the numerous outlets of the Orinoco River Delta. It is separated from Venezuela by the Gulf of Paria (salt, water) and straits over 5 mi. (8 km.) wide. The area of the island is approximately 1750 sq. mi. (453,- . 250 hectares) and the population is approximately 400,000. The climate is tropical with an annual rainfall of from 45 to 60 in. (114 to 152 cm.). The oil fields consist of several units, or fields, located in the southern half of the island. Approximately 90 per cent. of the total production has been yielded by fields situated within 7 mi: (11.3 km.) of the famous asphalt lake and on the southwest peninsula. The most important producing fields, or units, are the following, which are shown on the accompanying map: Brighton, or Pitch Lake Field, operated by the Trinidad Lake Petroleum Co., Ltd., is situated beside the famous Pitch Lake; it, even encroaches on the lake. Vessigny Field, operated by the Trinidad Lake Petroleum Co., Ltd., is situated 2 mi. (3.2 km.) south of Pitch Lake. Lot One Field, operated by the Petroleum Development Co., Ltd., the United British Oilfields of Trinidad, Ltd., and Stollmeyer, Ltd., is situated 3 mi. south of Pitch Lake upon Lot One of Morne 1&apos;Enfer Forest Reserve and adjoining properties. Parry Lands Field, operated by the United British Oilfields of Trinidad, Ltd., and the Petroleum Development Co., Ltd., is situated 3;2 mi. south of Pitch Lake on Lot Three of Morne l&apos;Enfer Forest Reserve and adjoining properties. Point Fortin Field, operated by the United British Oilfields of Trinidad, Ltd., is situated at Point Fortin, 6 mi. southwest of Pitch Lake. Fyzabad Field, operated by Trinidad Leaseholds, Ltd., is situated several miles southwest of Fyzabad Village and 6 mi. south-southeast of Pitch Lake. Barracpore Field, operated by Trinidad Leaseholds, Ltd., is situated several miles south of. San Fernando and 15 mi. (24.14 km.) east of Pitch Lake.

Jan 9, 1920

By R. F. Mehl

Jan 1, 1961

By Erland Johnson

BRINE was discovered at Avery Island, La., in 1790, but it was not until 1862 that rock salt was found about 13 ft below surface-the first discovery of rock salt on the continent. Maximum elevation of the island is 152 ft and elevation at the shaft 31 ft. The mining level is 530 ft below elevation at the shaft and the shallowest salt about 12 ft below surface. A shaft was sunk in 1869 when the mining operation started. In 1898 the present shaft was sunk, and the mine has been operated by International Salt Co. ever since.

Jan 6, 1957

By C. W. Arnold, H. L. Stone, D. L. Luffel

The purpose of this research is to determine (I) the efficiency of small banks of enriched gar driven by methane in displacing oil from a porous medium and (2) the effects of variation in bank size and composition of that efficiency. Most of the experiments were conducted in a sand-packed tube 20-ft long and 1/2-in. in diameter. The hydrocarbon system generally used was methane, butane and decane at 2,500 psia and 160°F. The results of these experiments indicate that, in the regions contacted by the gas, a small bank of an oil-miscible gas driven by methane can displace all of the oil in a piston-like manner. If the enriched gas is of such composition as to remain immiscible with the oil, displacement of oil is less efficient than for the miscible case, and the gas bank travels through the sand with a velocity less than that of the driving gas. These data along with theories discussed imply that smaller banks and less total gas are required when the enriched gas and oil are miscible. INTRODUCTION Widespread application of enriched-gas drive to the recovery of oil rests upon a key factor — the use of limited quantities, or "banks", of enriched gas. At the present time, the value of liquefied petroleum gas or other enriching agents discourages their use in a continuous injection technique, or even in a large bank, except in a few isolated reservoirs. If small banks of enriched gas driven by methane were as effective in displacing oil as is continuous injection, the enriched-gas drive process might be applied to a larger number of reservoirs. Previous research on the mechanics of the enriched-gas drive process reported by Stone and Crurnpl and by Kehn, Pyndus and Gaskell has utilized continuous injection of enriched gas. This work has shown that two types of displacements occur. With gases containing sufficient intermediates. the oil is displaced misciblv and complete recovery is obtained from the regions swept. When gases are used which contain insufficient intermediate hydrocarbon for miscible displacement, oil is displaced immiscibly. In the latter type, selective solution of the intermediate hydrocarbons causes a swelling and reduction in viscosity of the oil and leads to an increased recovery over that obtained by dry-gas (methane) drive. The size of the enriched-gas bank necessary for efficient displacement of oil is determined by those factors which cause deterioration of the bank. A differentiation may be made between those factors which operate on a microscopic scale and those which act on a macroscopic scale. On the smaller scale, the enriched gas mixes in the direction of flow by diffusion and convection with the fluids immediately preceding and following it. On the larger scale, the gas may by-pass the oil by flowing through permeable streaks, by overriding the oil because of density difference, or by fingering because of unfavorable viscosity ratios. In such cases, the enriching material tends to mix with the oil both laterally and in the direction of flow. The increase in effective area available for diffusion and dispersion of the enriching components leads to a faster degradation of the bank and a need for a larger bank than is necessary for those cases in which no by-passing occurs. The effects of such macroscopic factors in the deterioration of enriched-gas banks have been reported in a separate paper by Blackwell, Terry and Rayne. The present study was confined to the factors which operate on the smaller scale, in particular to the behavior of banks of enriched gas in sands uniformly swept by the gas. Experiments were designed to answer the following questions. 1. Can small banks of enriched gas driven by methane be used to secure oil recoveries comparable to those obtained by continuous injection of enriched gas? 2. What is the optimum bank size (the minimum bank size necessary to obtain a recovery comparable to that obtained by continuous injection of the same enriched gas)? 3. How many total pore volumes of gas must be injected to obtain the maximum recovery when the optimum bank size is used? 4. What is the effect of varying the number of enriching components in a gas bank? This report describes the experimental investigations and discusses the results in terms of their significance to reservoir behavior.

By J. L. Gregg

A STUDY of copper and silver base alloys was made with the object of finding, if possible, useful alloys subject to dispersion hardening. These studies led to the discovery of several alloys showing considerable dispersion hardening, the most important of which, the alloys of copper with iron, nickel, cobalt and chromium silicides, have since been very ably reported by M. G. Corson.1 This paper is offered as a few notes covering alloys other than those described by Corson and some further data on the silicide alloys.

Jan 1, 1929