By M. L. Holzworth, Philip R. Sperry, Paul A. Beck

INTRODUCTION THE basic work of Z. Jeffries1,2,3 has long ago established the main features of grain growth in the presence of a dispersed second phase. Working with sintered specimens of initially fine grained tungsten, to which various amounts of thoria have been added, Jeffries found that grain growth was inhabited, that is, practically prevented, up to a certain annealing temperature. When this temperature, which increased with the thoria content, was exceeded, extremely large grains developed abruptly from the fine grained matrix. Such a "coarsening temperature" was later found by Gross mann13,14 in certain types of steel, while Bain showed" that in other steels grain growth was gradual, without inhibition and abrupt coarsening. Later work16,17,18,19,21 demonstrated the connection between coarsening and aluminum additions. The viewpoint that the direct cause of inhibition and coarsening in aluminum killed steels is a fine dispersion of aluminum oxide21 appears to be held quite generally, although some doubts have been voiced even very recently.20 In steels with Ti additions the titanium carbide phase is considered responsible for the inhibition effects found.20 The coarsening temperature increases, with the titanium content. That coarsening may occur, as a result of certain heat treatments, even in low carbon rimmed sheet steel, was shown by Samuels,22 He also detected coarsening in a steel ingot of similar composition, after giving it the same heat treatment as that used by him for the sheet material, In this instance the identity of the inhibiting phase has not been determined, However, Tangerding found 23 that even the few small carbide particles, which occur in carbonyl iron, have a very marked inhibitive effect. As a result of an oxidizing anneal at 850°C, large grains begin to form at the surface of the carbonyl iron specimen, and gradually grow inward as the subsurface oxidation of the carbide particles progresses and eliminates the obstruction, The carbide particles can be removed also by annealing in hydrogen, with similar results. But if the oxidizing anneal of 10 hr at 850°C in air, is followed by annealing in hydrogen for 75 hr at the same temperature, grain growth is more spectacular; usually the whole specimen is transformed into a single crystal (approx. 1,5 cm X 5 cm). The reversed procedure, that is, hydrogen annealing followed by oxidizing annealing leads to smaller grains. Tangerding arrived at the logical conclusion that there must have been in his specimens some additional obstruction to grain growth resulting from a minor impurity, other than carbon. It seems likely that this obstruction was caused by an oxide formed during the oxidizing anneal and gradually reduced during the subsequent hydrogen-annealing. Other instances of grain growth inhibition of varying severity, associated with a dispersed second phase, have been described by several authors. Notable examples: lead with 0.06 pct Cu or Ni,24 cartridge brass with 0.12 pct Cr,25 or with up to 0.15

Jan 1, 1948

By David B. Brooks

INTRODUCTION Resources are not; they become (Zimmermann 100) . The companion concepts of reserves and resources appear, one way or another, in almost all considerations of mineral supply. Yet, no other concepts in the economics of the mineral industries have occasioned so much confusion. Whereas everyone agrees that in general the terms refer to the amounts of material that-depending upon technology, market conditions, and institutions-will become available for production in the near or more distant future, the apparent agreement disappears when we come to more specific definitions or to application of the definitions. Some definitions emphasize the physical aspects of reserves and resources, while others emphasize the economic. Some treat reserves and resources as fixed quantities, while others regard them as continually varying. Some consider that reserve and resource estimates have validity only for individual deposits, while others insist that they can be measured with sufficient accuracy for regional or national planning. This confusion in concepts that lies at the very heart of mineral economics is both strange and not so strange. It is common in the social sciences to find concepts that have been adopted into scientific jargon from popular usage and given rather special meanings -at the same time that they continue to be widely used without such qualifications. Psychologists have the same trouble with personality and sociologists, with community. Nevertheless, an attempt must be made to straighten out the various meanings of reserves and resources, or at least to clarify the conditions under which different meanings are applicable, before much progress in analysis of mineral problems can be expected. That is the objective of this chapter. Throughout the chapter, an attempt has been made to provide enough references to guide the interested reader to the most pertinent works on the concepts under study. However, even in a review article, it is no longer feasible to provide a comprehensive set of citations; there are simply too many. In many instances the works cited will themselves include the bibliographies needed to complete a literature search; those that are particularly useful in this respect are so noted. Also, because of the limited availability of foreign periodicals, some important works -originating largely in Canada, France, the

Jan 1, 1976

By J. E. Steiner, J. M. Hodge, M. A. Orehoski

Ingots of four steels (1045, 1080, Ni-Mo-V, and Ni-Cr-Mo-V) were cast at pressures varying from about 1 to 760 mm of mercury, so as to obtain a range of hydrogen contents in each steel. The susceptibility of these steels to flaking was evaluated by cooling hot-rolled blooms at a range of cooling rates, varying from water quenching to slag cooling, and studying the occurrence of flaking as a function of cooling rate. The steels exhibited differences in susceptibility to flaking, and a tlzreshold value for hydrogen content for each steel was found, below which the susceptibility was very low and above which the susceptibility increased markedly with increasing hydrogen content. Mechanical property evaluations, metallogvaplzic exantinations, and X-my diffraction determinations o,t retained austenite were made on samples from the blooms. A mechanism of flaking which is consistent with the observed behaviors, the effects of hvdrogen content, and the differences in susceptibility among the steels investigated is postulated, based on the results of mechanical property evaluations and metallographic and X-ray diffraction studies. ThE important role of hydrogen as a factor in the occurrence of "flakes" or "hair-line cracks" in steel has now been established by many investigations. These have included investigations by steel producers and forging manufacturers, to whom the prevention of flaking is a very real and serious problem, and many research studies aimed primarily at establishing the mechanism of this behavior Several investigators3 have reported that steels cast at reduced pressures (absolute pressures of about 1 mm) not only are low in hydrogen content but are essentially insensitive to the formation of flakes. These investigations have shown that a general relationship exists between hydrogen content and susceptibility to flaking. The difficulty of obtaining suitable samples of steels of a given composition with the desired range of hydrogen contents, particularly in the relatively large sections in which flaking most commonly occurs, has been the principal obstacle to quantitative evaluations of these relationships. Steels with intermediate hydrogen contents between 1 ppm, and the 4ppm or higher of air-cast steels are generally not available in commercially produced steels. Laboratory procedures, in which the hydrogen is introduced into solid steel samples by heating in a hydrogen atmosphere under pressure, generally involve a limitation in the size of the sample which can be treated, and thus are not representative of the behaviors in large sections. The availability of a facility at the South Chicago Works of U.S. Steel, in which several ingots could be cast from a single heat of steel at total air pressures ranging from 0.25 to 760 mm of Hg, has made it possible to overcome this obstacle and to obtain ingots of a given steel covering the intermediate range of hydrogen contents desired. These ingots, furthermore, are of a size suitable for the production of product with section sizes large enough to be representative of the products in which flaking most commonly occurs in commercial production. In these experiments, this facility was used to study the relationships between hydrogen content and the susceptibility to flaking of four steels, two plain carbon steels at 0.45 and 0.80 pct C and two low-carbon alloy steels representing a medium and a rather high hardenability level. These flaking studies were supplemented by evaluations of mechanical properties and by metallographic studies on samples from the blooms, in order to obtain pertinent information on the factors other than hydrogen content which influence the susceptibilities of these steels to flaking. Based on the results of these tests, a mechanism for the initiation and propagation of the flaking cracks, which is consistent with the observed behaviors, is postulated. MATERIALS AND EXPERIMENTAL WORK Steelmaking and Conversion. To provide material for the investigation, five 29- by 35-in., hot-topped, big-end-up ingots were cast from each of four 80-ton, basic electric-furnace heats of four different steels (a 1045 steel, a 1080 steel, a Ni-Mo-V steel, and a Ni-Cr-Mo-V steel). A double-slag practice was used on all steels and the two plain carbon steels were Si-A1 deoxidized with an addition of 2 lb of A1 per ton, while the Ni-Mo-V and Ni-Cr-Mo-V steels were deoxidized only with silicon and

Jan 1, 1964

By Frank C. Roberts

Neglecting the hydrogen and hydrocarbons, 1 will assume the following analysis as a fair average composition, by weight, of the waste gases escaping from a coke-burning blast-furnace: CO2............17.25 CO,............25.25 N,.............57.50 100.00 The 25.25 CO requires for combustion 62.6 of air, or 11.398 of oxygen, necessitating the passage of 48.202 nitrogen into the products of combustion. The latter, therefore, have the following composition: CO2,,............ 56.9 N,............105.7 Tile total specific heats of these quantities of the respective gases are 12.31 and 25.79, giving for the combined product, 38.1 approximately. That is, the product of combustion will absorb 38.1

Jan 1, 1889

By Welton J. Crook

Unless present, in considerable praportion, metals of the precious-metal group—other than gold and silver—are not readily detected by the methods of fire assaying usually applied to ores and metallurgical products. Platinum, when present in small quantity, will ordinarily be reported as silver unless special methods of parting are used. Other elements occurring in the gold itself are all fluxed and slagged in the assay operation and if analyses are made on bullions the melting and slagging operations to which the bullion has been subjected may eliminate most of the associated elements. On the other hand, the analysis of precipitate from the cyanide treatment of gold ores may reveal the presence of many unexpected elements, such as tungsten and molybdenum. It is uncertain, however, whether many of the elements present in the precipitate are derived from the ore gangue or from the gold itself. No very general survey of the distribution of metallic elements in gold seems to have been made. Rose and Newman,l in connection with the composition of native gold, say in part as follows: Gold is occasionally found alloyed with copper and sometimes also with iron, bismuth, lead, mercury, tin, antimony, palladium or rhodium. Rhodium gold from Mexico was found to be of the specific gravity 15.5 to 16.8 and contained 34 to 43 per cent of rhodium. The native alloy of palladium, gold, and silver from Porpez contains 85.98 per cent of gold, 9.85 per cent palladium and 4.17 per cent silver. Mal-donitk, from Victoria, contains gold 64.5 per cent, bismuth 35.5 per cent (Louis). Dana2 says that native gold is usually alloyed with silver in varying amounts, and that sometimes it also contains traces of copper and iron. Rare varieties contain palladium, rhodium and bismuth. Other authors, for instance Zeigler3 and Clark,4 give similar information. Most references on the subject agree that ordinary native golds contain, in common, the elements silver, copper and iron. After completion of the work of which this paper is a record, the conclusion is reached that all ordinary native gold probably does contain these elements and, although in certain cases other elements may be found to be present, that it is difficult to

Jan 1, 1943

By Welton J. Crook

Unless present, in considerable praportion, metals of the precious-metal group—other than gold and silver—are not readily detected by the methods of fire assaying usually applied to ores and metallurgical products. Platinum, when present in small quantity, will ordinarily be reported as silver unless special methods of parting are used. Other elements occurring in the gold itself are all fluxed and slagged in the assay operation and if analyses are made on bullions the melting and slagging operations to which the bullion has been subjected may eliminate most of the associated elements. On the other hand, the analysis of precipitate from the cyanide treatment of gold ores may reveal the presence of many unexpected elements, such as tungsten and molybdenum. It is uncertain, however, whether many of the elements present in the precipitate are derived from the ore gangue or from the gold itself. No very general survey of the distribution of metallic elements in gold seems to have been made. Rose and Newman,l in connection with the composition of native gold, say in part as follows: Gold is occasionally found alloyed with copper and sometimes also with iron, bismuth, lead, mercury, tin, antimony, palladium or rhodium. Rhodium gold from Mexico was found to be of the specific gravity 15.5 to 16.8 and contained 34 to 43 per cent of rhodium. The native alloy of palladium, gold, and silver from Porpez contains 85.98 per cent of gold, 9.85 per cent palladium and 4.17 per cent silver. Mal-donitk, from Victoria, contains gold 64.5 per cent, bismuth 35.5 per cent (Louis). Dana2 says that native gold is usually alloyed with silver in varying amounts, and that sometimes it also contains traces of copper and iron. Rare varieties contain palladium, rhodium and bismuth. Other authors, for instance Zeigler3 and Clark,4 give similar information. Most references on the subject agree that ordinary native golds contain, in common, the elements silver, copper and iron. After completion of the work of which this paper is a record, the conclusion is reached that all ordinary native gold probably does contain these elements and, although in certain cases other elements may be found to be present, that it is difficult to

Jan 1, 1943

By F. L. Wolf, G. E. Alderson

The reclaiming of nietallics from slag and sweepings is of vital interest to every brass-foundry man, but the first cost and interest on the investment often make it prohibitive for the small foundry to enjoy the benefits of a complete concentrating unit. However, the cost of such an installation and the cost of operation are often exaggerated to such an extent that foundries dispose of their copper-bearing refuse at a great loss. This paper gives the actual costs and the returns obtained in the reclaiming plant used at the Ohio Brass Co. This plant is divided into two sections—the preliminary treatment and concentrating departments. In the former occur the screening, crushing, and hand-picking operations whereby rnost of the non-valuable and heavy metallic constituents are removed. The concentrating equipment consists of an elevator, bins, jigs, ball-mill, arid table. Preliminary Treatment The preliminary treatment varies, depending on whether the material is slag, foundry-floor sweepings, or brass casting-floor sweepings. Material of the first class is produced from the operation of six Steele-Harvey and six Schwartz furnaces; the second class represents sweepings from an average of thirty-five. molding floors per day: and the last is collected around the sprue cutters and knockout bench. Treatment of Slag The slag, analyzing 30 to 40 per cent. copper, is passed over a 3-mesh yard screen (Tyler standard mesh) stretched on an inclined rectangular frame supported by adjustable legs and equipped with a hopper which directs the undersize into a barrow. The fine product, running about 20 per cent. copper and representing 20 to 25 per cent. of the total slag, goes direct to a storage bin for concentrator frrd. The oversize is charged into a No. 2 Hill cinder crusher, which takes 175 to 200 11,. to a charge and crushes two charges per hour through 'a No. 4 riddle. It

Jan 1, 1921

By F. C. Frischknecht

Most early development and application of electromagnetic prospecting methods took place in Scandinavia, where geological conditions favor their use. In other parts of the world these methods have aroused cycles of interest, but in Scandinavia they have been used continuously and successfully since the 1920's. Electromagnetic methods may be classified into two general groups. One group includes methods in which the source of the electromagnetic field remains stationary while the receivers are moved about to explore the area. The other includes procedures in which the energizing and receiving systems are moved together. Other classifications could be based on the size of the energizing source, the particular components of the electromagnetic field which are measured, or the mode of transporting the equipment. The difference between fixed-source and moving-source methods, however, is of such great fundamental importance that it will be emphasized in this discussion. FIXED-SOURCE METHODS Essentially, a fixed-source method consists of the measurement of electromagnetic fields about the source. The mutual coupling between the source and the earth is constant, but the mutual coupling between the receiver and the earth (unless the earth is homogeneous) and also between the source and the receiver changes at each station. The results are usually normalized by relating the field data to the calculated free space or primary field. Turam and Radio Reference Signal Methods: The turam or two-frame* (see Fig. 1A) is probably * Turam means two-coil. the most common fixed-source method. The energizing source is an insulated cable grounded at both ends or formed into a large rectangular loop. Measurements are taken along a traverse at 5 to 50-meter intervals using two small receiving coils, the lagging coil being placed at the position previously occupied by the leading coil. The complex ratio (i.e., inphase and out-of-phase ratios) of the voltages induced in the two coils is measured. Operating frequency range is about 100 to 800 cps. In a typical turam survey a straight, grounded cable several kilometers long is laid out parallel to the probable strike of the ore deposits or conducting strata being sought. An area extending 1 or 2 km on each side of the cable, and within 1 or 2 km of the ends of the cable, is surveyed. Measurements are made at stations 5 to 25 m apart along traverses perpendicular to the cable. Measurements may be made along lines parallel to the cable to serve as base lines for the traverses or for other special purposes. Commonly the receiving coils are oriented with their planes horizontal so that only the vertical component of the field is measured. If additional information is required, one of the hori- zontal components may also be measured by orienting the coils with their planes vertical. In a modified turam technique developed recently for both ground and airborne measurements (Fig. 1B) the amplitude of the complex voltage induced in a single receiving coil is measured and its phase compared with that of a reference signal transmitted from the energizing system by a radio frequency carrier. Thus the un-normalized field is obtained directly, whereas with the turam method it is obtained by calculation from the ratios. The turam method and its modifications have a greater working depth than the other electromagnetic procedures used in ore prospecting. Under favorable conditions conductors have been located at depths of 200 to 300 m. A modified turam method with one of the electrodes grounded in the upper end of a plunging orebody was used to follow the extension of this body to a depth of 200 m beneath a layer of conducting schists. Straight grounded cables are usually preferred to insulated loops because they are easier to lay out and because they often make the method more sensitive. The greater sensitivity of a grounded cable is a result of ground return currents which may flow in the orebodies in addition to the eddy currents caused by induction from the current in the cable. Anomalies in the vertical field due to eddy currents are characterized by a correspondence between high values for the inphase component and positive out-of-phase components and/or low values for the inphase component and negative out-of-phase components. Also the inphase component may approach zero, but it does not become negative. In very long continuous conductors that are parallel to a grounded cable the effect of ground return currents may far exceed the effect of eddy currents. These ground return currents cause a lack of correspondence between the inphase and out-of-phase components and may cause negative inphase or anti-phase components. It becomes difficult to carry out the measurements and often difficult to interpret the results. Such results immediately suggest the presence of graphitic strata, however, since ore deposits are rarely extensive enough to accumulate sufficient ground return current to cause these results. A cable laid out perpendicular to the strike or an insulated loop is sometimes used in areas where graphitic schists and slates are present. Anomalies are then completely or almost entirely due to eddy currents and are easier to interpret. The measured voltage ratios are normalized by either subtracting or dividing by normal field ratios calculated from free space considerations. The normalized ratios are then plotted as individual profiles. When significant anomalies occur in the ratio measurements, the actual normalized fields are calculated by beginning with a measured or an assumed value for the field at a point near the cable and successively multiplying this value by the normalized ratios. There is a similarity between this process and a numerical integration of the ratio curve. Conversely, in many respects the ratio curve is similar to the first derivative of the field curve.

Jan 1, 1960

By S. Leber, R. F. Hehemann

Diffusion coefficients for the Cb-W system were measured using couples prepared from poly crystalline, commercially pure metals. The diffusion coefficients, measured in the temperature range between 1700° and 2300°C, decreased exponentially as the tungsten concentration was increased from 0 to 50 at. pct, then decreased abruptly at higher concentrations. A decrease of two orders of magnitude was observed over the entin? compositional range. The diffusion coefficients were in the range defined by the self-difiusion coefficients of the individual elements, indicating their general validity. An activation energy of 60,500 cal per mole was measured for the 20 pct W composition. Such low values, when compared with energies over 100,000 cal per mole for the pure constituent elements, indicated that transport mechanisnzs more rapid than volume diffusion were contributing substantially to inter dijfusion. Difference should, therefore, be expected between these data and the intrinsic diffusion coefficients. These differences should be significant in the kinetics of 'transport phenomena in practical systems. CONSIDERABLE attention has been devoted in recent years to the mechanical behavior and other properties of the refractory metals and their alloys. The Cb-W system has been of special interest as a base for the development of more complex compositions of commercial interest. In spite of the importance of mass transport to all aspects of elevated-temperature behavior, and especially to the production of alloys by powder-metallurgy techniques, little attention has been paid to diffusion in the Cb-W system. Results from a previous study of this system1 appeared to be anomalously high. The present investigation is, therefore, an attempt to obtain more accurate diffusion coefficients in this system. Intrinsic diffusion coefficients, of primary importance from the theoretical viewpoint, can only be obtained accurately from studies utilizing compositional gradients approaching zero. However, many practical problems involve diffusion under significant concentration gradients. The diffusion coefficients determined in this investigation were, therefore, obtained from couples prepared from elemental metals. The data obtained should be of value in the analysis of problems such as homogenization during powder-metallurgy alloying or reactions between base and clad in coated structures. In this vein, the investigation was conducted on poly crystalline materials of commercial purity. PROCEDURE Diffusion couples were prepared by sandwiching a columbium sheet between two sheets of tungsten. The composite was welded around all edges, the tungsten forming a protective can for the columbium. The composite was soaked for 4 min at 1600°C in a hydrogen-atmosphere furnace, quickly forged to 40 pct reduction in thickness, and then rapidly cooled to room tempera-

Jan 1, 1967

By H. E. McKinstry

MOVEMENT on a fracture of irregular shape can cause local widening of the fissure and thereby offer freer channelways for circulation of ore-depositing solutions. This influence, coupled with large areas of wall rock available for reacting with ore solutions in brecciated and shattered ground can account for locally active deposition of metals and the resulting ore shoots. Such irregularities in the fracture system may be caused by local variations in the strength of rocks and by pre-existing lines of weakness, especially if these stand at favorable angles to certain components of the fracturing stress. Therefore correct interpretation of the mechanics of fracturing should permit deductions as to structurally favorable places on unexplored portions of the vein system. INTRODUCTION IT has long been recognized that movement on a curved or irregular fault surface is capable of separating the walls in certain portions of the fault, but until very recent years the importance of this mechanism as a factor in localizing ore shoots has escaped proper recognition. A short time ago W. H. Newhouse' presented a careful analytical study of displacements and their corresponding open spaces. For reasons that will be discussed later, it frequently happens that portions of the vein which are favorably oriented are not merely wider but also richer than the average. In many cases the widening with its accompanying richness coincides with very minor changes in the dip or strike of the vein, irregularities that commonly escape notice unless the vein is mapped in detail and a careful geometrical analysis made. While the relationship between the width of the vein and the changes in dip or strike has been recognized as a matter of observation, the irregularities have been accepted as more or less the result of accident. There has been very little effort except in isolated cases to find out the causes of these changes in dip or strike. Yet it is clear that if the causes can be recognized and expressed in terms of geologic structure the geologist will know where to look for repetitions of these favorable conditions either on extensions of the same vein or on adjoining veins. Any lack of understanding of the causes is due to the limitations of our ability to interpret our observations and not to the sheer capriciousness of

Jan 1, 1941

By J. E. Kirby, L. B. Schnitz, H. E. Stamm III

The production history of a gas-cap-drive reservoir was reproduced by calculations, and predictions were made for operations under primary depletion, pressure maintenance by gas injection, and pressure maintenance by water injection. Although the general equations used in this analysis have been available to the industry for a number of years, the procedure has not had extensive use because of the unusually large time requirements for developing numerical results. The use of digital computing equipment for processing the calculation work generally reduced the time usually required for an extensive analysis of this type. Calculation techniques were developed that were equally applicable for solving the gar-cap-drive problem, whether digital computing equipment or desk calculators are used. These techniques are outlined and the procedures are illustrated by the field problem. INTRODUCTION The analysis of a gas-cap-drive res-ervoir requires the simultaneous solution of the volumetric balance1 and displacement2 equations. Equations for the analysis of combination drive reservoirs were presented by Wooddy and Moscrip in a previous paper." These equations permit the evaluation of possible operating processes in order that the optimum method of pro- ducing the reservoir may be determined. Although these equations represent the basic technique known for the detailed analysis of gas-capdrive reservoirs, the calculation processes are quite complex and time consuming; hence, the procedure has not had extensive use. Recently, these equations were satisfactorily applied with the aid of a digital computer to investigate the completion history of a gas-cap-drive reservoir under the following operating methods: primary depletion, depletion under full pressure maintenance by gas injection, and depletion under full pressure maintenance by water injection. The use of digital computing equipment substantially reduced the time necessary for making the computations and permitted a more concise investigation of the reservoir's depletion history than was possible when the desk calculator was used. This more rigorous investigation also permitted a detailed analysis of the calculation procedures necessary in the solution of the gas-cap-drive problem. This paper outlines the procedure of analyzing a gas-cap-drive reservoir and illustrates the process with an actual field problem. CHARACTERISTICS OF THE RESERVOIR ANALYZED Production in the field under consideration is obtained from a Frio formation of Oligocene age at a depth of approximately 5,740 ft sub-sea. The accumulation, which is bounded on the flanks by strand lines, is semirectangular in shape with gentle narrowing toward the base of the structure as shown by the sand limits and completion map in Fig. 1. The reservoir development indicates an oil column of 319 ft that is defined by gas-oil and oil-water contacts. Basic data relative to the characteristics of the formation and the formation fluids are shown in Table 1. The formation exhibits considerable shaliaess and thinning near the oil-water contact indicating that little or no benefit will be received from natural water influx. This is substantiated by the fact that wells completed near the original oil-water contact have not produced water. A sizeable gas cap is present; however, considerable faulting is in evidence, and it is believed that only a limited portion of the gas cap will aid in oil displacement and pressure maintenance. Although the reservoir was in an initial stage of depletion, it was believed that as soon as the equilibrium gas saturation in the oil zone was exceeded and a number of upstructure wells were invaded by the expanding gas cap, the resulting high gas-oil ratio production would rapidly dissipate the natural drive and lead to limited oil recoveries and inefficient reservoir operation. This analysis evaluated the effectiveness of the primary displacement mechanism and

Jan 1, 1958

By C. S. Finney, John Mitchell

The introduction of ovens for the production of metallurgical coke is believed to be due to L. L. Norton who operated an iron foundry in the vicinity of Connellsville, Pa. Persuaded by his foreman, an English immigrant named Nickols from Durham, L. L. Norton put up a 12-ft square oven which produced coke in 1833. The coal used was taken from a local mine at Mounts Creek. The oven seems to have been used in conjunction with the customary method of coking in mounds. It was in the Connellsville district also, in 1841, that two carpenters, Provence McCormick and James Campbell, formed a partnership with John Taylor, a stone mason, for the manufacture and sale of oven coke. The task of the mason was to construct the ovens, while the carpenters were to build the arks by which the coke could be taken by water to the market at Cincinnati. The following account of the enterprise was given by McCormick: "James Campbell and myself heard in some way that I do not now recollect that the manufacturing of coke might be made a good business. Mr. John Taylor, a stone mason, who owned the farm on which the Fayette coke works now stand, and who was mining coal in a small way, was spoken to regarding our enterprise, and proposed a partnership-he to build the ovens and make the coke and Mr. Campbell and myself to build a boat and take the coke to Cincinnati, where we heard there was a good demand. This was in 1841. Mr. Taylor built two ovens. I think they were about 10 feet in diameter. My recollection is that the charge was 80 bushels. The ovens were built in the same style as those now used, but had no iron ring at the top to prevent the brick from falling in when filling the oven with coal, nor had we any iron frames at the mouth where the coke was drawn. The top and mouth had to be repaired when they fell in. In the spring of 1842 enough coke had been made to fill two boats 90 feet long-about 800 bushels each-and we took them to Cincinnati down the Youghiogheny, Monongahela, and Ohio, but when we got there we could not sell. Mr. Campbell, who went with the boats, lay at the landing some two or three weeks, retailing out one boatload and part of the other in small lots at about 8 cents a bushel. Miles Greenwood, a foundryman of that city, offered to take the balance if he would take a small patent flour mill at $125.00 hi pay, which Mr. Campbell did. He had it shipped here. We tried it, but it was no good, and we sold it to a man in the mountains for $30.00, and thus ended our coke business." So successful did the coke subsequently prove to be in use that the three partners were asked to deliver more. Evidently they had had enough of the coke business, however, for they refused to have anything more to do with it. Few ovens were built between 1841 and 1855, and it is reported that in the latter year, "there were only 26 coke ovens along the river above Pittsburgh". Successful coke makers of these years included Mordecai Cochran, Richard Brookius, and Colonel A. M. Hill. It was the use of coke in 1859 in the Clinton furnace erected by Graff, Bennett and Co. in a plant on West Carson Street, Pittsburgh, that brought the real beginning of the coke-iron era in America. Here the successful use of Connellsville coke as a blast-furnace fuel was demonstrated beyond all possible doubt, and from the year 1859 the coking industry expanded tremendously. The era of beehive coke ovens During the latter half of the nineteenth century and the early years of the twentieth, the major percentage of metallurgical coke produced in the United States came from beehive ovens. It was not until 1893 that the first battery of by-product ovens came

Jan 1, 1961

By Charles A. Ashburner

VERY little is known of the economical value of the cod-bells of the State of Texas. The first authentic statement in regard to their occurrence is that contained in the reports of the United States Exploratians for the Pacific Railroad, near the 32d parallel of latitude, published in 1863-55. Professor William P. Biake reports, "that a number of seams of bituininorls coal, varying in thickness from two to four feet, have been opened along the Brazos River, in Young County, about one hundred and fifty miles west of Fort Worth." Dr: Shurunrd also states, " that the claracteristic fossil fornis of the Carbeiferaas Era have been found with this coal, and considers the age of the formation established. Foesils obtained from the carboniteroas limestone remove all doubt of the age of these deposits."† In the spring of 1879, I was called upon by some Eastern capitalisets to make an examination of the Brazos coal-field, in order to obtain the thickness, extent., and value of the coal which could be mined and be'made merchantable fir stearn, heating, and metallurgical purposes. The demand for coal in this section of the country is great, and a fuel which in our Eastern markets might be considered of inferior quality, would here find a ready sale. It must be remernbered that the market value of a coal does not depen'd upon its absoltite purity, but upon its actual value in heat units which it is capable of prodwing. A poor coal which can be cheaply milled near the consuper, is infinitely more remunerative to a mining company than a superior coal whose cost to the consumer is greatly increased by high mining charges and railroad freights. The value of the Texan coals does not depend upon their purity but upon their low first cost and nearness to a market. A glance at a geological map of the United States, will show that the Brazos coal-field is the extreme southwestern extension of what may be called the Missourian, Fourth or Western, bituminous coal

Jan 1, 1881

By Zay Jeffries

IT has been known for a number of years that certain aluminum alloys could be hardened by quenching from a temperature of about 500° C. Immediately after quenching the total increase in hardness is not marked, but the hardness increases gradually so that after about 4 days, it has reached a maximum. The actual increase in hardness probably continues for weeks or even months, but in order to detect the differences after 4 days, it is necessary to make tests at rather long intervals. So far as is known to the authors, Alfred Wilm was the first to discover these properties in aluminum alloys.1 The aluminum-copper alloys are amenable to this treatment and the addition of magnesium makes the heat-treatment effect more pronounced. Until recently heat treatment of aluminum alloys has been confined to the worked alloys in the form of sheet or extruded products. The alloy that has been most used in this connection is known commercially as duralumin and has about the following composition: copper not exceeding, 6 per cent.; magnesium not exceeding, 2 per cent.; manganese not exceeding, 1 per cent.; commercial aluminum,2 balance. A typically good alloy in this range consists of: copper, 4 per cent.; magnesium, 0.5 per cent.; manganese, 1 per cent.; commercial aluminum, balance. This alloy can be rolled into sheets or extruded; and in this condition it can be heated in the ordinary furnace atmosphere to a temperature near 500° C. and quenched in water. After about 4 days it will have the following physical properties: tensile strength 55,000 to 60,000 lb. per sq. in. (3866 to 4218 kg. per sq. cm.); elongation in 2 in., 15 to 20 per cent. No harmful effects of the furnace gases or even the air, if the heating is affected in an electric furnace in an air atmosphere,

Jan 9, 1919

By L. S. Darken

IT has been known for sometime that in an ionic lattice, such as that of Ag2S or FeO, the migration velocity of the anion may differ markedly from that of the cation, the cation being usually the more mobile. It has been shown, for example, that during the formation of silver sulfide tarnish on silver, the tarnish layer grows principally by the motion of silver cations through an essentially stationary silver sulfide lattice. Similarly, the growth of wüstite scale on iron proceeds principally by motion of iron ions, this being accomplished with the aid of vacant iron lattice sites into which the iron may readily move. Likewise investigations of solid solutions of various salts show that there is usually considerable difference in the mobility of the different cations. Measurements of the mobility of various metals in liquid mercury indicate that the various metals move at different rates relative to the mercury. In view of the foregoing it seems reasonable to suppose that when any single phase solution is acted upon by a field, the atoms of different elements respond in different ways; in particular, that the force arising from a particular concentration gradient in a binary alloy would cause the atoms of one component to move with a drift velocity which is in general different from that of the atoms of the other component. The recent experiments of Smigelskas and Kirkendall1 support this viewpoint, since they found, in essence, that during diffusion in alpha brass zinc moves appreciably faster than copper. This was evidenced by the relative motion of inert molybdenum wires. Such a phenomenon is incompatible with the place interchange theory of diffusion proposed by several authors, most recently by Birchenall and Mehl.2 This theory has, however, also been questioned3.4 for other reasons, principally because of the high energy required for direct atomic interchange. The rather large difference between self-diffusivity, as determined by tracer technique, and mutual diffusivity, as determined with the aid of another element at low concentration, might also be interpreted as favoring the above idea; however, Birchenall and Mehl have pointed out that there is another possible interpretation of this difference; this is discussed later. A rather interesting and pertinent observation was made by Schwartz,5 who noticed that tungsten lamp filaments, heated by direct current, commonly fail by necking down in the region at the temperature gradient near the positive end, with a concomitant swelling at the corresponding position near the negative end. He introduces considerable auxiliary evidence to show that this phenomenon is occasioned by the motion of tungsten cations which migrate in the high temperature region from the positive end toward the negative end. The mechanism of this migration is not clearly understood. If, however, this experimental evidence be accepted, we are forced to conclude that alloying elements in the tungsten may migrate by the same or a similar mechanism, whatever it may be, at a greater or lesser rate, thus giving rise

Jan 1, 1948

Flexibility is the keynote in designing modern exploration drills that and mobility. Add to the flexibility of individual drills the wide range of models, and the man looking for a drill has ample choice today. Weight? Choose from models as light as 50 lb or as heavy as 10,000 lb. Hole capacity? From less than 1 in. for smallest core drills to 20 in. or more for auger types. Transportation? The lightest go by packsack (in fact, that is one trade name) ; others are designed to go by Jeep, truck, on skids or are built on light trailers. Power? Select air power, gasoline or diesel engine, electric motor, or use a power take-off from the vehicle on which the drill is mounted. Drill bits offer almost as much variety as the drilling machines themselves. Many drills are suitable for a variety of uses, and often adapt to several types of bits with ease. Some of the types available are: diamond core, diamond reaming, rotary, auger, shot, and special soil sampling tools.

Oct 1, 1955

By V. A. Josendal, J. W. Wilson, B. B. Sandiford

Two radioactive tracers have been tested as a means of determining core saturation in multiphase flow studies. Cesium chloride was tried as a water-phase tracer, but complications in its use in low permeability cores resulted from sorption of cesium by the core or water-wet pads. IodoI3'ben-zene proved very satisfactory as an oil-phase tracer. The synthesis of iodobenzene from the sodium iodide as received from Oak Ridge is simple and direct. The tracer is insoluble in water and there was no evidence of sorption by any of the core materials used. use of the method to determine saturation profiles during capillary and dynamic desaturations and relative permeability measurements on oil-water and oil-gas systems is described. Comparisons of the dynamic and capillary methods of relative permeability determination were made using the tracer to check core saturation and saturation distribution. Other experiments are also described in which mobility of the oil phase at various saturations was measured by displacing labeled oil by flowing inactive oil. Similar experiments were made using water labeled with cesium 134. INTRODUCTION To be fundamentally sound. any laboratory method of determining relative permeability must meet, among others, the following requirements: (1) the core saturation between the pressure taps must be uniform, and (2) there must be uniform pressure difference between the phases in the region between the pressure taps. In practice it may eventually be shown that appreciable departure from either or both of these conditions may be permitted without introducing sensible error. but the magnitude of such error remains to be established. There is need then for methods of saturation determina- tion which will determine the saturation profile in a core as well as the overall average saturation given by the gravimetric or material balance methods usually employed. Methods which have received consideration include resistivity, X-ray absorption, gamma ray absorption, neutron diffraction, and radioactive tracers. The resistivity method has use in the determination of profile, but needs checking by independent means.' The X-ray method has been used successfully, but requires elaborate equipment and calibration.23 4 At present gamma ray absorption is practical only for very large cores. The neutron methodo does not appear adaptable to measurement of saturation variations in short cores since it is a scattering method. Russell, Morgan and Muskat' employed radiovanadium in a study of the mobility of interstitial water. Coomber and Tiratsook used radioiodine as an oil-phase tracer and measured profiles in unconsolidated sand packs. ADVANTAGES OF RADIOACTIVITY METHOD A thorough discussion of the theory of radioactive tracers and the technique of using them to study the movement of fluids in sands is given by Coomber and Tiratsoos and need not be detailed here. The method requires less equipment than the X-ray method; the counting problem is similar, but the generation and regulation of the radiation, which is a major problem in the X-ray method, is not required in the radioactivity method. In the X-ray method it is customary to add up to 20 per cent of absorber, usually an iodine compound, to the phase to be labeled. while in the radioactivity method a mere trace is sufficient. A possible disadvantage of the radioactivity method is that a disproportionate amount of the activity comes from the portion of the core nearest the counter, whereas the X-ray gives a true average saturation in the region traversed by the beam. 011 the other hand, this characteristic of the radioactivity method renders it peculiarly adaptable to study of certain types of radial variations in saturation. As with the X-ray method, a tracer may be added to either the oil or water-phase. An oil-phase tracer is more generally useful. however. since it permits work on oil and gas in the

Jan 1, 1952

By John Hall

THE Fremont test for measuring the energy consumed in breaking a notched bar of steel is not so well known in this country as it deserves to be. The test specimen used in this test is about 3/8 by 1/4 by about 1 1/4 in., notched with a hack saw on the lower side to cause the piece to break at a fixed point. A weight of 10 kg. falling 4 m., and provided with a knife or chisel which strikes the specimen, breaks the test piece by impact. The residual force in the falling weight after it has broken the specimen is recorded by a suitable device, and the difference between the total energy and the residual energy of the weight (in kilogrammeters) is the force consumed in breaking the specimen. An experience of several years with the Fremont testing machine has shown its great value in readily detecting brittleness not revealed by tensile testing or slow bending testing. I this paper it is proposed to discuss (1) the supersensitiveness of the test as applied to cast steel and (2) its value in revealing the effect of heat treatment under certain conditions. .

Jan 7, 1913

By S. L. Hoyt

IN technological studies on steel considerable emphasis has been placed on the identification of the foreign inclusions, testimony of which is adequately given in the metallographic literature covering methods for their identification. The outstanding accomplishment in this field is the scheme devised by Campbell, Comstock and Wohrman for identi-fying various oxides, sulfides, silicates and other constituents by syste-matic etching tests and microscopic examination.1 The time involved in carrying out this procedure has led to attempts to secure quicker methods, or at least to shorten the time required to secure essential information. An example of this is the use of dark field illumination, but when this was tried out by the authors it was found that cavities and pits on the polished surface appeared bright on a dark field and could not be distinguished from small glassy inclusions. Still another means is the Leitz Ultropak, an instrument equipped with optical units for the illumination of the specimen by reflected light to secure an effect similar to dark field illumination. The structures are made visible in exceedingly sharp details by utilizing the inherent properties of the samples, such as refractive index, absorption coefficients and reflection powers. We have had no experience, with the Ultropak, but a recent paper by Benedicks and Löfquist3 describes methods for

Jan 1, 1934

By B. Woyski

MANY writers, in discussing defects caused by oxidation and gassing of bronzes and red brasses advocate substantially the same cure for both. But from its nature, oxidation cannot take place if there is an excess of fuel in the furnace, while the gases absorbed by some alloys are products of incomplete combustion of the fuel. Hence the metal can be either oxidized or gassed, but it is doubtful whether these actions can take place simultaneously. Oxidation can be easily overcome by the use of deoxidizers or it may be avoided by protecting the molten metal with suitable fluxes. Absorption of gases is more difficult to overcome. The regulation of the air and fuel, so as to produce complete combustion, and the protection of the bath by mineral fluxes are the most important factors. Gas expulsion, resulting in gas holes, porosity, unsoundness, and swollen or cauliflower-headed risers, is said to have several causes. One writer' lists the most common causes in the order of their importance, as follows: Superheated metal, dirty or slaggy furnace conditions, using metals low in quality or those previously subjected to bad melting practice, poor grade of fuel, use of newly lined or damp ladles, indiscriminate mixing of scrap or illogical combinations of metal. Superheating the metal usually occurs when the heat is ready to be poured but for some reason must be held in the furnace. In this case, a careful furnace tender tries to avoid overheating the metal by keeping a mild fire; that is, a reducing fire which, unfortunately, results in gassing the metal. A dirty, slaggy furnace may result in gassing the metal by retarding the heating and prolonging the time necessary to bring the metal to the proper temperature, thereby increasing the chances of gassing in uncertain furnace atmosphere.

Jan 5, 1922