By P. D. Frost, H. A. Robinson, J. R. Doig, M. W. Mote

The mechanism of hardening in heat-treatable zirconium alloys was foUNd to be analogous to that for titanium alloys. Zirconium containing a relatively large addition of a ß -stabilizing element such as molybdenum or columbium can be hardened by the following transformation: Lean alloys, having insufficient alloy content to retain ß at room temperature are hardened by the following transformation: Application of these findings in Zr-Mo-Sn and Zr-Nb-Sn alloys produced strengths as high as 190,000 psi with reasonable ductility. PRIOR research on zirconium alloys has been concerned with development of greater strengths and creep resistance by solid-solution hardening or by dispersion hardening. Although solution and aging heat treatments had been applied earlier to zirconium alloys, quenching frequently produced low ductility. The possibility that the ß-to-w transformation, discovered earlier in titanium alloys,' might also occur in zirconium alloys and cause low ductility was considered, and, indeed, was found as predicted2 to be the case. In the earliest experiments, the heat-treatment response of titanium, too, was disappointing. However, by avoiding the formation of the embrittling w phase, it became practical to obtain room-temperature strengths higher than 180,000 psi, with elongation values of 10 pct.3 Based on the present concept of titanium heat treatment, the principal requirement for a heat-treatable zirconium alloy is that it contains a certain minimum amount of one or more ß -stabilizing elements. Only molybdenum, columbium, and tantalum, when present in sufficient amounts, are known to stabilize ß zirconium to room temperature during rapid cooling from the ß field. Tantalum was undesirable because of its high thermal-neutron cross section. Aluminum and tin are effective a stabilizers, but aluminum has been shown to seriously decrease the corrosion resistance of simple zirconium alloys in hot water. Therefore, for the present study, tin was used as the stabilizer addition. The alloys selected for this evaluation are presented in Table 1 along with their analyses and ß-transus temperatures. The analyses indicated that intended compositions were usually realized. EXPERIMENTAL PROCEDURES All of the alloys were melted from sponge zirconium and fabricated to sheet for heat treatment

Jan 1, 1960

By W. David Menzie

An inventory of the mineral resources of a region is a most desirable basis for planning their systematic development. In the absence of appropriate samples upon which to base a reliable estimate of this inventory, investigators have resorted to a number of indirect approaches; the unit regional value concept forms the basis for one such approach. The produced resources of a region are a function of the inventory multiplied by the degree of intensity (some fraction between zero and one) of development of the resources. A convenient means of expressing this amount is to accumulate the weight and value of resource and to prorate the totals over the area represented by the unit sampled; i.e., weight and value per unit area or tonnes/km.2 and U.S. 1967 $/km.2. When this approach is used for the U.S.A., South Africa and Rhodesia the average value of (log.) U.S. 67$/km.2 for the states of the U.S.A. and South Africa are similar ($55,176 U.S.$67/km.2 and $52,538/km.2 respectively); whereas, Rhodesia is relatively underdeveloped (10,301 U.S.67$/km.2). On the other hand if the individual commodities are used as a basis for comparison, the U.S.A. shows the greatest diversity (67 commodities out of a possible total of 75) with South Africa next (50 commodities) and Rhodesia last with only 26 commodities. Since it is known that area and value are not simply related perhaps diversity is directly related to area. Again the kinds of commodities which have contributed the greatest value to the totals differs, with fuels (petroleum, coal and natural gas) predominating in the U.S.A. totals; whereas, South Africa and Rhodesia obtain their greatest contributions from gold, diamonds (S. Africa) coal and asbestos. In each case the greatest value of resources is produced from sedimentary rocks. As a somewhat different kind of example, consider a single resource (petroleum, the most valuable in the U.S.A.) over a large area (number of sampling units) the U.S.A. by state. Furthermore, assume that the model frequency distribution of the amount of petroleum (tonnes/km.2) is log normal. Then the present production fails to match the model first because 17 states (34% out of 50) have not produced petroleum. Of the remaining 33 states, Louisiana has produced the most (15,177 tonnes/km.2) and the frequency histogram is still skew. A spatial analysis of the distribution of the amount of petroleum by state shows that the samples (i.e., states) are not random; the non-producers and producers tend to cluster. It remains to be seen if this is indeed a true representation of the incidence of petroleum or is a function of the exploration philosophy currently in vogue.

Jan 1, 1977

By W. M. Gray

The determination of the state of stress existing at a point in any solid body requires the determination of the six components of the stress tensor relative to a convenient set of axes. One general method of doing this in rock is to make strain or deformation measurements associated with local relief of stress in a number of boreholes penetrating a limited volume in the vicinity of the point at which the stress is to be determined. The stress is assumed to be constant throughout this volume. Leeman1 has described a number of the instruments that have been developed for making deformation or strain measurements in boreholes. Panek2 has described the application of statistical methods to the determination of the average components of ground stress from sets of measurements made in boreholes by means of deformation meters of the type developed by the U.S. Bureau of Mines. In this paper attention is given initially to the strain cell developed for use on the flattened ends of boreholes by the Council for Scientific and Industrial Research (CSIR) , South Africa. The equations required for evaluating the average components of ground stress from measurements made by means of the CSIR strain cell are derived. These equations are similar in form to those applying to measurements made by the borehole deformation meter developed by the U.S. Bureau of Mines. The results of an investigation of the properties of the equations are described. These results are important in the practical use of both the instruments mentioned above and any instrument based on similar principles.

Jan 1, 1968

By C. N. J. Wagner, E. N. Aqua

The bee alloys of the terminal solid solution of rhenium in niobium were investigated by X-ray diffraclion methods. The analysis of the broadening of the powder pattern peaks from the niobium-rich alloys, cold-worked by filing, showed evidence for faulting on (211) planes. The alloys with larger rhenium concentrations were brittle, and fractured when filed. The analysis of the shapes of the diffraction profiles from powders produced by hammering with steel plates) of these brittle alloys indicated that the broadening was due predominantly to platelets bounded by clibe planes. This result was consistent with the Laue patterns from single-cleazlage facets which showed evidence for clearage fracture on {100} planes. The influence of faulting on the mechanical properties of face-centered cubic (fcc) metals and alloys, i.e., how faulting affects the various dislocation configurations in fcc metals, is well-known.' The important question is whether or not faulting occurs in body-centered cubic (bcc) metals and alloys, and, furthermore, if faulting does occur, to what extent it affects the mechanical properties. Theoretical calculations indicate that the stacking-fault energy is rather high in most bcc metals.2 The results of sev-eral studies using transmission electron microscopy have indicated that faults are present in well-annealed and lightly deformed bcc metals and alloys, such as tungsten,3 vanadium,4 and Mo-Re alloys.5,6 These faults, as have been observed, may be stabilized by the presence of interstitial (C,N,O) atom segregation to the extended dislocations. In addition, there is considerable X-ray diffraction evidence for faulting in bee metals,7-8 using the same techniques that were successful for the study of faulting in fee metals and alloys.7 This X-ray diffraction method is currently the only technique applicable for the investigation of faulting in metals with high stacking fault energies, i.e., when severe amounts of deformation are required to produce sufficient amounts of faulting to be detectable by X-rays. The thinned films of heavily deformed metals will become opaque in the electron microscope due to the high dislocation densities present. In a previous investigation of faulting8 in bee metals of group Vb and VIb, the authors observed that niobium was ductile when filed at room temperature, and showed the highest density of faults on the (112) family of planes. A niobium-base alloy system was therefore chosen to study the effect of alloying on the occurrence of faults in a bcc alloy. There is a large range of terminal solid solubility of rhenium in the alloys of the bee refractory metals. All of the Group VIb-rhenium alloys, i.e., Cr-Re, Mo-Re, and W-Re, exhibit solid solution hardening without loss of ductility.9 In fact, the ductility reaches a maximum for alloys with compositions near to the limits of solubility. This enhanced ductility has been attributed to the lowering of the stacking-fault energy in the alloy; i.e., the increased amounts of twinning provide an additional mode of deformation, resulting in the observed high ductility.' Because of this demonstrated effect of rhenium in bee alloys, it was decided to study a series of alloys of Nb-Re. Using the same X-ray diffraction methods as described in the previous investigation,' one is able to identify the possible causes of broadening of the powder pattern peaks, e.q., particle size, microstrains, stacking faults, and/or twin faults. The separation of these various contributions to the measured peak shape is accomplished by the Warren-Averbach analysis.7 I) EXPERIMENTAL PROCEDURE A series of seven bee solid solution alloys containing from 2.5 to 21.5 at. pct Re (remainder niobium) were prepared at the General Electric Research Laboratory. Buttons, weighing 25 g, were alloyed from electron-beam-melted niobium chips and random rhenium sheet by arc melting in a water-cooled copper crucible, under an argon atmosphere. The buttons were inverted and completely remelted to promote homogenization. The nominal alloy compositions are listed in Table I. Samples of the cold-worked alloys were obtained by filing to produce a powder for the X-ray study. Alloys too brittle to be filed were hammered with steel plates. The resultant filings or brittle impactings were screened through 150-mesh classifiers and compacted to the required shape for the diffractometer holder. The X-ray diffraction peaks were automatically recorded by fixed time counting at uniform 28 intervals, or by continuous registration with a ratemeter. In all cases, the (110)-(220) and (200)-(400) pairs of peaks and the (211), (310), (222), and (321) reflections were measured on a GE-XRD5 diffractometer using CuKa radiation with nickel filter or MoKct radiation and a LiF monochromator in the diffracted beam. The first part of the data reduction, completed with the aid of a series of programmed computations,10 was the analytical resolution of the Kol component of the diffraction profile. Subsequent computations were then made with reference only to the resolved Kol peak shape. These included the measurement of the

Jan 1, 1967

By A. G. Weber, K. H. Coats, M. H. Terhune, R. L. Nielsen

Two computer-oriented techniques for simulating the three-dimensional flow behavior of two fluid phases in petroleum reservoirs were developed. Under the first technique the flow equations are solved to model three-dimensional flow in a reservoir. The second technique was developed for modeling flow in three-dimensional media that have sufficiently high permeability in the vertical direction so that vertical flow is not seriously restricted. Since this latter technique is a modified two-dimensional meal analysis, suitably structured three-dimensional reservoirs can be simulated at considerably lower computational expenses than is required using the three-dimensional analysis. A quantitative criterion is provided for determining when vertical communication is good enough to permit use of the modified two-dimensional areal analysis. The equations solved by both techniques treat both fluids as compressible, and, for gas-oil applications, provide for the evolution of dissolved gas. Accounted for are the effects of relative permeability, capillary pressure and gravity in addition to reservoir geomety and rock heterogeneity. Calculations are compared with laboratory waterflood data to indicate the validity of the analyses. Other results were calculated with both techniques which show the equivalence of the two solutions for reservoirs satisfying the vertical communication criterion. INTRODUCTION Obtaining the maximum profits from oil and gas reservoirs during all stages of depletion is the fundamental charge to the reservoir engineering profession. In recent years much quantitative assistance in evaluating field development programs has been provided by computerized techniques for predicting reservoir flow behavior. Because of the spatially distributed and dynamic nature of producing operations, automatic optimization procedures, such as those now in use for planning refining operations, are not now available for planning reservoir development. However, present mathematical simulation techniques do furnish powerful means for making case studies to help in planning primary recovery operations and in selecting and timing supplemental recovery operations. A number of methods have been reported which simulate the flow of one, two or three fluid phases within porous media of one or two effective spatial dimensions>-4 However, applying computer analyses to actual reservoirs have been limited mostly to two-dimensional areal or cross-sectional flow studies for two immiscible reservoir fluids. To obtain a three-dimensional picture of reservoir performance using such two-dimensional techniques, it has been necessary to interpret the calculations by combining somehow the results from essentially independent areal and cross-sectional studies. To the authors' knowledge, the only other three-dimensional computational procedure, in addition to those presented here, was developed by Peaceman and Rachford8 to simulate the behavior of a laboratory waterflood. Two computational techniques which may be used to simulate three-dimensional flow of two fluid phases are described in this paper. The first method, called the "three-dimensional analysis", employs a fully three-dimensional mathematical model that treats simultaneously both the areal and cross-sectional aspects of reservoir flow. The second method, called the vertical equilibrium (VE) analysis", is applicable

By Walter H. Bucher

This symposium is designed to lay the basis for a general discussion of the place of geophysics in the training of geologists. As there is danger that in the ensuing debate individual interests may be given emphasis out of proportion to their place, we shall do well to view the whole field of geological inquiry in order to see the problem in true perspective. The Nature of Geological Inquiry "Basic" and "Complex" Sciences It is convenient to divide all science into two major divisions, the basic and the complex sciences. The basic sciences separate out from reality such entities as "substances" and "movements," describe their behavior in terms of arbitrary units of measurement and derive from them by progressive abstractions concepts and patterns of behavior that exist between them, so-called general "laws" and "properties" of nature. The complex sciences, on the other hand, deal, with little or no abstraction, with those objects of reality that are accessible to man in the atmosphere, the hydrosphere, the lithosphere and the biosphere. Their work comprises two types of inquiry. One is concerned with abstractions to the extent of dealing with types rather than individuals—that is, with such things as plants, animals, protoplasm; clouds, streams, gla- ciers; volcanoes and mountain ranges. It comprises the search for general properties and patterns of behavior or "laws" that characterize the objects and their reactions to each other. These properties and laws apply always, everywhere. They are independent of the stream of time. We may call the results of this sort of inquiry timeless knowledge. The other type of inquiry is concerned with the objects themselves—that is, with this animal and that plant; this river system and that mountain chain; this glacier and that valley. Like all concrete objects in nature, they are subject to change with the passage of time, especially when it is measured in years, centuries, eons. The characteristics by which we recognize them —indeed, their very existence—are dependent on their position at this point in the stream of time. This we may call time-bound kntowledge. The so-called descriptive sciences are all bound to the past of which the objects of their study are the product and through which alone their present properties call be understood. They are historical sciences. This obvious fact is easily overlooked, which leads to serious misunderstanding, as we shall see later. Dynamic Geology With this broad picture in mind, let us now examine the nature of geological inquiry, defining, for the purposes of this discussion, geology as the science of rocks. Air is not a rock; water is. Meteorology and climatology are, correspondingly, gen-

Jan 1, 1946

By Walter H. Bucher

This symposium is designed to lay the basis for a general discussion of the place of geophysics in the training of geologists. As there is danger that in the ensuing debate individual interests may be given emphasis out of proportion to their place, we shall do well to view the whole field of geological inquiry in order to see the problem in true perspective. The Nature of Geological Inquiry "Basic" and "Complex" Sciences It is convenient to divide all science into two major divisions, the basic and the complex sciences. The basic sciences separate out from reality such entities as "substances" and "movements," describe their behavior in terms of arbitrary units of measurement and derive from them by progressive abstractions concepts and patterns of behavior that exist between them, so-called general "laws" and "properties" of nature. The complex sciences, on the other hand, deal, with little or no abstraction, with those objects of reality that are accessible to man in the atmosphere, the hydrosphere, the lithosphere and the biosphere. Their work comprises two types of inquiry. One is concerned with abstractions to the extent of dealing with types rather than individuals—that is, with such things as plants, animals, protoplasm; clouds, streams, gla- ciers; volcanoes and mountain ranges. It comprises the search for general properties and patterns of behavior or "laws" that characterize the objects and their reactions to each other. These properties and laws apply always, everywhere. They are independent of the stream of time. We may call the results of this sort of inquiry timeless knowledge. The other type of inquiry is concerned with the objects themselves—that is, with this animal and that plant; this river system and that mountain chain; this glacier and that valley. Like all concrete objects in nature, they are subject to change with the passage of time, especially when it is measured in years, centuries, eons. The characteristics by which we recognize them —indeed, their very existence—are dependent on their position at this point in the stream of time. This we may call time-bound kntowledge. The so-called descriptive sciences are all bound to the past of which the objects of their study are the product and through which alone their present properties call be understood. They are historical sciences. This obvious fact is easily overlooked, which leads to serious misunderstanding, as we shall see later. Dynamic Geology With this broad picture in mind, let us now examine the nature of geological inquiry, defining, for the purposes of this discussion, geology as the science of rocks. Air is not a rock; water is. Meteorology and climatology are, correspondingly, gen-

Jan 1, 1946

By C. M. Loeb, T. E. Norman

The use of ball, rod and tube mills for grinding ore, cement and other materials has grown so rapidly during the past forty years that the world's annual consumption of ferrous grinding media for these mills is now estimated to be between one half million and one million tons per year. Ferrous grinding balls constitute the major portion of this tonnage. Obviously they represent suficient value to justify thorough studies of the factors governing their performance. The selection of grinding balls is governed principally by: I. Quality (wear resistance, impact resistance, soundness, and the like). 2. Sources of supply and delivered cost. 3. Grinding characteristics or efficiency in the ball mill. This paper deals principally with the quality of ferrous grinding balls. In the study of these factors certain data relative to the fundamental nature of ball wear in ball mills have been obtained. These data are also presented and discussed briefly. The Development of a Suitable Wear Test A study of the fundamental factors governing the quality of grinding balls has been hampered seriously by the fact that a competent test has, in the past, involvetd the purchase of several hundred tons of halls of a specific type which were then run in one or more ball mills for a period ranging from several months' to several years' duration. Often, during the period of test, it became necessary to change operating conditions or the character of the ore fed to the test mill with the result that the rate of ball consumption changed and the test figures became of little value. Under such circumstances, progress in the development of better grinding balls, has been necessarily slow. Economic factors and variations in the quality of balls produced by different sources of supply generally make it necessary for each mill operator to determine for himself the most suitable type of balls for his mills. In our own ball mill grinding operations at Climax, Colo., we were faced with this problem. After we had run a few large scale wear tests at considerable expense we decided to investigate the possibilities of a small scale wear test which would be capable of testing numerous types of balls within a relatively short time. The most important requirement of any test is, of course, that it give results which can be used to predict accurately the wear in full scale operations. It was known that Ellis and his associates1'2 had developed a method of testing grinding balls by small scale tests run at the Ontario Research Foundation. Ellis' method of testing was used as a starting point in our investigations. In the course of our tests a number of modifications of the original method were found to be desirable so that, by an evolutionary procedure, a method of small scale

Jan 1, 1949

By C. M. Loeb, T. E. Norman

The use of ball, rod and tube mills for grinding ore, cement and other materials has grown so rapidly during the past forty years that the world's annual consumption of ferrous grinding media for these mills is now estimated to be between one half million and one million tons per year. Ferrous grinding balls constitute the major portion of this tonnage. Obviously they represent suficient value to justify thorough studies of the factors governing their performance. The selection of grinding balls is governed principally by: I. Quality (wear resistance, impact resistance, soundness, and the like). 2. Sources of supply and delivered cost. 3. Grinding characteristics or efficiency in the ball mill. This paper deals principally with the quality of ferrous grinding balls. In the study of these factors certain data relative to the fundamental nature of ball wear in ball mills have been obtained. These data are also presented and discussed briefly. The Development of a Suitable Wear Test A study of the fundamental factors governing the quality of grinding balls has been hampered seriously by the fact that a competent test has, in the past, involvetd the purchase of several hundred tons of halls of a specific type which were then run in one or more ball mills for a period ranging from several months' to several years' duration. Often, during the period of test, it became necessary to change operating conditions or the character of the ore fed to the test mill with the result that the rate of ball consumption changed and the test figures became of little value. Under such circumstances, progress in the development of better grinding balls, has been necessarily slow. Economic factors and variations in the quality of balls produced by different sources of supply generally make it necessary for each mill operator to determine for himself the most suitable type of balls for his mills. In our own ball mill grinding operations at Climax, Colo., we were faced with this problem. After we had run a few large scale wear tests at considerable expense we decided to investigate the possibilities of a small scale wear test which would be capable of testing numerous types of balls within a relatively short time. The most important requirement of any test is, of course, that it give results which can be used to predict accurately the wear in full scale operations. It was known that Ellis and his associates1'2 had developed a method of testing grinding balls by small scale tests run at the Ontario Research Foundation. Ellis' method of testing was used as a starting point in our investigations. In the course of our tests a number of modifications of the original method were found to be desirable so that, by an evolutionary procedure, a method of small scale

Jan 1, 1949

By Dermot M. Ross-Brown

Introduction Slope angles are one of the major factors affecting the shape of the final pit and the location of the walls Due to differences in geology, the optimum slope angles vary from pit to pit and within different parts of the same pit. Indeed, it is not unusual to have different slope angles for the top and bottom portions of the same cross section. The optimization of these slope angles is a major study in itself and this chapter is intended as a general introduction to the subject. It is not intended to be a comprehensive text for the absolute beginner The objective is to put the various aspects of slope stability analysis into relative perspective by describing the vari¬ous analytical techniques available and indicating when each may be most appropriately used References are made to the many excellent texts and papers on slope stability for the reader who does not have a formal training in soil or rock mechanics. In writing this chapter, an assumption has been made that a tentative mining plan has been drawn up, includ¬ing a preliminary estimate of the slope angles. It has also been assumed that all the necessary field and laboratory data has been collected and reduced to a form suitable for input into the stability analyses.

Jan 1, 1979

SLAG composition, slag constitution, reactions in slag, and reactions between slag and metal-in other words, the physical chemistry of slags-are matters of great importance to the open-hearth operator, whether or not he makes use of any detailed knowledge of them. Although this is a relatively young branch of the science of steel- making, much progress has been made; however, much remains to be learned, and many of the statements that can be made at present are probably--or even certainly-subject to future change. Nevertheless, the physical chemistry of slags is sufficiently developed to provide a reasonably secure basis for real understanding of steelmaking reactions. FUNDAMENTALS OF SLAG CONTROL By way of introduction, some time is spent in this chapter on effecting an easy transition from some of the more "practical" manifestations of slag to discussions couched in the more formal language of physical chemistry. This necessitates a certain amount of repetition, but it is felt that the purpose of the chapter is best served in this way. Reactions in the metal phase have products that find their way into the slag and are important components thereof; they are discussed in detail in the preceding chapter. Some substances distribute themselves Between slag and metal in definite fashion, and others are found only in the slag. Their reactions are a large reason for this chapter. Limitations of Slag Control. The open-hearth process is essentially oxidizing and cannot be otherwise operated. (Oxygen gradients in the furnace, the mechanism of oxygen inflow, and similar subjects are discussed in Chapter XIX.) As shown in the calculations of material and heat balances for the charge (see Chapter XV), from 25 to 50 lb. of oxygen will flow from air or combustion gases into the charge or molten bath during the heat for each ton of liquid steel

Jan 1, 1944

By Shiro Ban-ya, John F. Elliott, John Chipman

The activity of carbon in Fe-C austenite at 1150°C has been determined for concentrations up to about 2.1 pct C using the equilibrium: C + COz = 2CO; equations have been derived expessing the activity as a function of carbon content on the basis of twelve mathematical models. Several of these represent the data satisfactorily. ACCURATE information on the thermodynamic properties of austenite in the binary system Fe-C is needed as a basis for studies of transformation and precipitation in steels of all sorts, alloy as well as plain carbon. The many attempts to approach this problem through statistical thermodynamics require sound and dependable experimental data in order to evaluate the several models which have been suggested. In this paper we are concerned with the experimental determination of the activity-composition relation in austenite at the temperature of its widest range of stability, approximately the eutectic temperature (1153°C). Accurate investigation of the activity of carbon in austenite may be said to have begun with the work of Dunwald and wagner.' A more detailed study was carried out by R. P. smith2 on the two equilibria: More recent work on these two equilibria has been reviewed by Chipman,3 who pointed out the experimental hazards associated with studies of Eq. [I]. Studies of this reaction involve rather small values of the ratio these are susceptible to errors due to traces of moisture in the apparatus according to the reaction: Ellis, Davidson, and Bodsworth4 evaluated K, for their experimental temperatures and used desiccants to control water vapor pressure. While they were able in this way to obtain consistent values for K1 it cannot be said that all of the uncertainties of the method have been overcome. Results by both methods reported by Schurmann, Schmidt, and wagener5 appear to be consistent except at very low carbon content. Reaction [2] was employed in the experimental work reported here. It is to be recognized, however, that it is not applicable to projected studies of certain alloy steel compositions involving stable oxide-formers.

Jan 1, 1970

By Charles C. Russell, Glenn C. South

A primary factor in the selection of coals for making coke at high temperatures is the amount of pressure the coal will exert upon the oven walls when carbonized in modem by-product ovens.l-3 This factor has become increasingly important in recent years because of demands for increased throughput and higher coke yields. As a result of the increasing necessity for assessing coals in regard to their carbonization pressures, more and more research work is being directed toward developing labora-tory-scale tests for predicting carbonization pressures and for showing how blends of coking coals may be modified to eliminate pressures liable to damage coke-oven walls. The specific reasons have never been defined as to why some blends of coking coals develop dangerous carbonization pressures and others do not, therefore specific procedures to eliminate dangerous pressures could not be prescribed. It is true that the major processes occurring during carbonization have been described by many writers,4 and there is a general agreement on the ideas of the changes that occur as coal is transformed into coke. However, there is little evidence relating the processes occurring during carbonization to the pressure developed and the available evidence is very incomplete and often contradictory. This deficiency arises in part from the fact that the fundamental causes of pressure development have not been defined, at least from experimental data, and in turn this is the result of the lack of satisfactory testing equipment for studying the problem. Operating experience has shown several ways of reducing or eliminating dangerous pressures,5 but probably none of these ways is applicable to all blends of coking coals, and such empirical methods often lead to production of inferior coke. They are trial-and-error methods, not designed to remedy specific causes of pressure development. The number of laboratory-scale testing devices designed to estimate the carbonization pressures that result when coals are carbonized in commercial ovens is probably well over a hundred.6 Few of these instruments have remained in use for any length of time, either because the predictions were not sufficiently accurate or, more often, because too many exceptions were found. Often testing devices are operated without any attempt at duplication of conditions in commercial ovens and erroneous and contradictory results are frequently obtained. Therefore, it has seemed desirable to study the properties of coal itself and to determine any relationships between the properties of the coal and the carbonization pressures developed. Relationship between Properties of Coal and Carbonization Pressure Attempts to determine relationships between various properties of coal and carbonization pressures, for the most parti have been indirect because no satisfactory and reliable laboratory testing device has

Jan 1, 1944

By Glenn C. South, Charles C. Russell

A primary factor in the selection of coals for making coke at high temperatures is the amount of pressure the coal will exert upon the oven walls when carbonized in modem by-product ovens.l-3 This factor has become increasingly important in recent years because of demands for increased throughput and higher coke yields. As a result of the increasing necessity for assessing coals in regard to their carbonization pressures, more and more research work is being directed toward developing labora-tory-scale tests for predicting carbonization pressures and for showing how blends of coking coals may be modified to eliminate pressures liable to damage coke-oven walls. The specific reasons have never been defined as to why some blends of coking coals develop dangerous carbonization pressures and others do not, therefore specific procedures to eliminate dangerous pressures could not be prescribed. It is true that the major processes occurring during carbonization have been described by many writers,4 and there is a general agreement on the ideas of the changes that occur as coal is transformed into coke. However, there is little evidence relating the processes occurring during carbonization to the pressure developed and the available evidence is very incomplete and often contradictory. This deficiency arises in part from the fact that the fundamental causes of pressure development have not been defined, at least from experimental data, and in turn this is the result of the lack of satisfactory testing equipment for studying the problem. Operating experience has shown several ways of reducing or eliminating dangerous pressures,5 but probably none of these ways is applicable to all blends of coking coals, and such empirical methods often lead to production of inferior coke. They are trial-and-error methods, not designed to remedy specific causes of pressure development. The number of laboratory-scale testing devices designed to estimate the carbonization pressures that result when coals are carbonized in commercial ovens is probably well over a hundred.6 Few of these instruments have remained in use for any length of time, either because the predictions were not sufficiently accurate or, more often, because too many exceptions were found. Often testing devices are operated without any attempt at duplication of conditions in commercial ovens and erroneous and contradictory results are frequently obtained. Therefore, it has seemed desirable to study the properties of coal itself and to determine any relationships between the properties of the coal and the carbonization pressures developed. Relationship between Properties of Coal and Carbonization Pressure Attempts to determine relationships between various properties of coal and carbonization pressures, for the most parti have been indirect because no satisfactory and reliable laboratory testing device has

Jan 1, 1944

By G. L. F. Powell, L. M. Hogan

Samples of silver and Ag-O alloy, 0.12 wl pet, have been undercooled to a maximum of 250°C by melting in a slag of commercial soda-lime glass. Grain refinement occurred in undercooled silver samples whet the degree of undercooling exceeded a critical value which varied from 153° to 175°C, depending on the melting conditions. In under cooled Ag-0 samples, the grain structure was fine and equiaxed at degrees of undercooling larger than 50oC. The grain refinement in both silver and Ag-0 alloy samples was the result of recrystallization during or immediately following freezing. When the oxygen content was increased, the degree of undercooling at which recrys-tallization occurred decreased. INVESTIGATIONS of the grain structure of strongly undercooled melts of nickel and cobalt1-4 have revealed a change in room-temperature grain size as a function of undercooling. At large degrees of undercooling the grain size was fine, but samples undercooled by smaller amounts exhibited a much coarser grain structure. The reported undercooling at which this grain size transition occurred in nickel varied between 140° and 175'C undercooling. Walker1 attributed this grain size change to an enhanced nuclea-tion rate. Cavitation at a melt-solid interface was con sidered to generate a high-pressure wave. This, in turn, produced nucleation in the liquid as a result of an elevated freezing point increasing the undercooling in the melt. A similar grain size transition was observed in undercooled silver between 133° and 153°C undercooling.5 The grain size transition in undercooled silver was found to be dependent on oxygen con tent. More recently, the authors5 showed that a simila transition occurred in an undercooled Cu-O alloy, =0.08 pet, but not in oxygen-free copper undercooled more than 200°C. The transition was attributed to recrystallization of the solidified grains after freezing; the greater the degree of undercooling, the more complete the recrystallization. In view of this effect of oxygen content on grain size transition, additional undercooling experiments were carried out with silver. This paper reports the results of these studies on silver and Ag-O alloys undercooled more than 50°C EXPERIMENTAL 1) Materials. The silver was supplied by Matthey Garrett Pty., Ltd., as fine granulate, silver mini' mum 99.9 pet, and contained the trace impurities shown in Table I. The silver originated from two different refineries resulting in the difference in impurity content shown in Table I. However, the variation in composition had no discernible effect on the undercooling behavior. Samples of the silver were melted in an open-ended, vertical, cylindrical resistance furnace, wound with Kantha] wire, the temperature of which was adjusted by means of a variable transformer, 2) Melting and Undercooling. Bulk samples of silver were undercooled by preoxidation and removal of oxidized impurities in a glass slag, as previously described,5 but special precautions were necessary to allow comparison between oxygen-free silver and a Ag-O alloy. Samples free of oxygen were prepared by first melting weights of granulate varying from 200 to 400 g in clean vitreous silica crucibles in air for approximately 15 min. A sample was frozen and a complete glass cover formed over the top surface by adding granulated glass rod. The sample was then melted and frozen several times until no oxygen bubbles appeared in the glass slag. Subsequent thermal analysis indicated that the oxygen content was negligible. The glass acted as an efficient barrier to absorption of oxygen from the air. Ag-O alloys were prepared by melting silver in silica crucibles with only a partial cover of glass, so that the top surface of the melt was in contact with air. The silver was held molten in air for several hours at 1000° to 1050°C, in the expectation that the oxygen in solution would reach equilibrium with atmospheric oxygen. At T - 1000°C the equilibrium oxygen content was calculated as 0.12 wt pet O, using Sieverts law and Eq, [l], derived by Mizikar et a!.7 from the data of Sieverts and Hagenacker8 for 1 atm of oxygen:

Jan 1, 1970

By E. A. Breitenbach

A computer program has been developed to afford rapid and complete quantitative log analysis for exploration and production decisions. The computation consists of automatic selection of tops and bottoms of porous intervals from the digitized data, and then point-by-point calculations within each selected interval. Nearly all log types can be analyzed. This paper presents the calculation techniques found to be appticable to machine evaluation and gives examples of their use. INTRODUCTION As the quantitative interpretation of well logs entails repetitive use of charts and equations, it is natural that digital computer programs would be written. A Universal Log Interpretation Computer Program (ULICP) has been developed to afiord rapid and complete analysis for exploration and production decisions. Application of this program enables the log analyst to: (I) apply rapid quantitative log analysis for exploration and production decisions on either a field, a well or on a single zone basis; (2) apply concepts of interpretation requiring detailed numerical analysis; (3) analyze all porous intervals on each log, rather than a few selected zones, and complete the analysis in less time than previously required. Computations are reported for every digitized point in each zone; (4) use empirical techniques applicable to a given area as an integral part of the computation; (5) experiment with the empirical coefficients and exponents in the interpretation equations to find the best possible solution; and (6) automatically plot both the original and computed data to scales analogous to the field prints. The primary utility of a log interpretation program stems from its ability to do an overwhelming amount of work with very little man-power. If a calculation procedure or thought process can be formalized to the extent that step-by-step logic can be written, a computer program can be developed that follows this logic. The major question is one of economics. A feasibility study of the costs for such a program indicates that digital processing is economical primarily as a means of increasing the productivity of the log analyst. In effect, the probability of missing productive intervals in any well, because of a lack of time to do detailed calculations, is greatly reduced. The nucleus of ULICP is programmed to compute large sections of a suite of logs by selecting zones automatically and then performing all pertinent computations on a data point by data point basis within each zone.'.' An entire suite of logs can be processed in this manner with very little manual intervention. Sufficient programming logic is available so that each log analyst can request computations pertinent to his area. These requests are made by simple additions or deletions of information on the input header cards. Hence, the log analyst is always in complete control of the computation process. The evaluation of a suite of logs requires pre-editing, digitization, computation, presentation of results and interpretation. Work by the log analyst is reqilired only in pre-editing and interpretation. Thus, he is allowed more time for comprehensive interpretation, rather than calculation. For continuity, the discussion of ULICP is organized sequentially: pre-editing, digitization, computation and presentation of results. DISCUSSION PRE-EDITING The extent of pre-editing prior to computation is dependent on the format of the original data. For analog prints, it requires inspection, correlation and editing of the logs, plus the entering of required data an special forms. For digitized data such as magnetic tape field recordings, only the special forms are necessary. The process for analog prints will be given here. The inspection and correlation process involves the selection of sections for digitization and the correlation of the traces to a common depth. To decrease the cost of digitization, traces that exhibit large variations in shale formations can be redrawn to a non-zero baseline. The next step is to enter all pertinent data on the input header cards. The header cards presently used for ULICP are presented as Figs. 1 through 6. Cards 1, 2, 3 and 4 (Fig. 1) are defined as the Main Header Cards. They describe the particular well for output identification and give basic information. Cards 5 through 15 (Figs. 2 through 6) are defined as the Block Header Cards. As such, they define the log types and the interpretation parameters for the block of data immediately following. Cards 1 through 10 are required for every computer run. Cards 11 through 14 pertain only to nuclear logs. Card 11 is required if any nuclear log is supplied, and cards 12 through 14 are required only when gamma-ray, density or neutron log data, respectively, are supplied. Card 15 (Fig. 6) must be supplied when cross-plot calculations are required. Either two- or three-component

Jan 1, 1967

By E. M. Wise

THe properties required of gold alloys for jewelry are not well standardized, due in part to problems peculiar to certain branches of the jewelry industry, in part to the individual preference of the fabricator and to his willingness to cope with certain difficulties in manufacture, which arise with the use of certain alloys. General Requirements In general, the properties desired may be classed as follows: 1. Color should conform to the dictates of good taste and smart style. 2. Corrosion resistance and tarnish resistance should he good. This is to a considerable extent determined by the carat. Resistance to such corrosive agents as mercuric chloride as well as certain depi1atories is unreasonable to expect and difficult to meet. 3. Strength and hardness must be adequate to maintain the delicate contours of finely modeled jewelry. 4. Wear resistance must be great enough to resist abnormal wear, such as is encountered by a wedding ring in a lifetime of wear. 5. Ductility must be sufficient to permit the fabrication of drawn shells, tubes and difficult shapes. Material having a yield point of not less than 60,000 lb. per sq. in., an ultimate strength of 100,000 Ib. per sq. in., and an elongation of 40 per cent. is desirable. 6. Melting point should be between 800" and 1200" C. Colored Golds The popular green and yellow golds are based on the gold-silver-copper alloys; in some cases modified by the introduction of zinc to improve the casting properties and to alter the color, and nickel to increase the strength. The properties of the Au-Ag-Cu system have been the subject of a very thorough investigation by Jänecke,l Sterner-Rainer12 and Carter."

Jan 1, 1929

By E. M. Wise

THe properties required of gold alloys for jewelry are not well standardized, due in part to problems peculiar to certain branches of the jewelry industry, in part to the individual preference of the fabricator and to his willingness to cope with certain difficulties in manufacture, which arise with the use of certain alloys. General Requirements In general, the properties desired may be classed as follows: 1. Color should conform to the dictates of good taste and smart style. 2. Corrosion resistance and tarnish resistance should he good. This is to a considerable extent determined by the carat. Resistance to such corrosive agents as mercuric chloride as well as certain depi1atories is unreasonable to expect and difficult to meet. 3. Strength and hardness must be adequate to maintain the delicate contours of finely modeled jewelry. 4. Wear resistance must be great enough to resist abnormal wear, such as is encountered by a wedding ring in a lifetime of wear. 5. Ductility must be sufficient to permit the fabrication of drawn shells, tubes and difficult shapes. Material having a yield point of not less than 60,000 lb. per sq. in., an ultimate strength of 100,000 Ib. per sq. in., and an elongation of 40 per cent. is desirable. 6. Melting point should be between 800" and 1200" C. Colored Golds The popular green and yellow golds are based on the gold-silver-copper alloys; in some cases modified by the introduction of zinc to improve the casting properties and to alter the color, and nickel to increase the strength. The properties of the Au-Ag-Cu system have been the subject of a very thorough investigation by Jänecke,l Sterner-Rainer12 and Carter."

Jan 1, 1929

By J. M. Callow

THE results obtained by pneumatic flotation throughout the country on all classes of ore, and. the tonnage now being treated by this particular method, speak for themselves. Its advantages over the so-called agitation process are now established by facts and data from practice. The comparative efficiency of a rapidly revolving paddle, as a means for aerating an ore pulp, and of a cycloidal or turbine blower for the same purpose, would seem to be so obvious as to leave no room for discussion. Practitioners in this art are to be congratulated on the acquisition of the valuable literary contributions that have recently been made on the theory of. flotation by Messrs. Ralston, Van Arsdale, Taggart and Beach, and others, and the very valuable and able articles, by Messrs. Laist and Wiggin on "Flotation Concentration at Anaconda, Mont.," by, Dr. Rudolf Gahl- on the "History of Flotation at Inspiration," and by David Cole on "The Advent of Flotation in the Morenci District." It is not within the province of this article to attempt an answer to the various issues raised in regard to the theory, or to defend the one advanced by me a year ago. But since discussion usually benefits the profession, a reply will be made to some of the statements made by the last-named writers. COMPARATIVE SENSITIVENESS AND ATTENDANCE Concerning 'the article, "Flotation Concentration at Anaconda, Mont.," by Laist and Wiggin, a little explanation is in order. It should be stated that; with the exception of about 24 days at the end of the testing 'period, the Callow experimental plant at Anaconda was not run under my direction. This perhaps accounts for some of the conclusions drawn on page 562 of the descriptive paper. The conclusion that the use of acid seems to be of considerable advantage, calls, for some comment. While the tests conducted by the Anaconda Copper Co. do show acid to be, of considerable benefit, this is a consequence of using acid sludge as a flotation agent. My belief has always been that the Anaconda

Jan 2, 1917

By E. P. Pfleider

DIAMOND drill research work was initiated at the School of Mines, University of Minnesota, in late 1949. The Drilling Symposium held in Duluth that spring highlighted the problem of high cost and core recovery and the need for controlled testing. An advisory committee made up of informed representatives of both mining companies and drilling companies was formed to suggest and advise on a program of drill research. A Hy-Mac hydraulic drill unit, see Fig. 1, especially designed for experimental testing, was obtained for this work by the School of Mines through the courtesy of the Carboloy Co. It is an extremely flexible unit, capable of exerting a forward thrust of about 1750 lb and turning at speeds from 650 to 2200 rpm. The feed arrangement is so designed that the advance can be set either at a constant rate or permitted to vary at a fixed pressure, see Fig. 2. The

Jan 1, 1952