By Steven Wright, Sharif Jahanshahi, Shouyi Sun

"While there is a large industry based on recovering platinum group metals (PGM) from complex sulphide ores containing Cu and Ni, there is little information on the thermodynamics of the matte phase formed on smelting the ore and in particular the behaviour of Pt in the matte.The equilibrium between metallic platinum and industrial mattes was studied in a series of experiments where a small quantity of matte (5g) and platinum foil of 150 µm thickness (0.5 g) were equilibrated in magnesia crucibles at 1400°C under conditions where the oxygen and sulphur partial pressures were controlled.The chemistries of the phases were determined from EDS analysis using a scanning electron microscope. Line scans were initially used to confirm that the foils had attained a uniform composition across their thickness. The composition of the matte was determined from analysis of an area of matte including the small metallic droplets and dendrites.The distribution of Pt in Cu-Fe-Ni mattes (Pt: 1.5 – 3%) and solid Pt alloys (Pt: 54 – 72%) was studied. For a matte of base composition 45%Fe, 11%Ni, 8% Cu, at a base temperature 1400°C, the following behaviour was observed for the Pt distribution ratio:Under the range of sulphur and oxygen pressure of this study (log pO2 from -15 to –12.2, log pS2 from – 4.6 to –2.2), the distribution ratio of Pt between matte and alloy was independent of the sulphur and oxygen pressure, having a value of 0.04.The Pt distribution ratio increased from 0.02 to 0.08 with temperature from 1340 to 1450 oC.For mattes where the proportions of Cu and Ni were kept constant, a slight decreasing trend was shown for the distribution ratio of Pt versus the iron content (37 to 53%) in the matte but was not confirmed because of experimental uncertainty."

Jan 1, 2003

By Vladimir E. Vigdergauz

"Bubble-mineral complexes could be formatted by an attaching of hydrophobic particles to the surface of air bubbles or by an evolution of bubbles from solution onto hydrophobic surfaces. Measurements of contact angles, detachment forces (DF), induction times (IT), evolution pressures (EP) and flotation recoveries (FR) for the studying of minerals wettability at various pH and electrochemical potentials were used. An analysis of the obtained IT results show that a process of bubble attachment to a mineral surface is a rather slow one and it will scarcely be enough for bubble-mineral complex formation under the conditions of real flotation.The ranges of adhesion potentials obtained by DF measurements, Figure 1, correlate with the data of floatability-potential for pyrite. The ranges of adhesion potentials obtained by DF measurements for galena (-1 ÷0.2V) and chalcocite (-0.5÷1.2V) correlate with the potential ranges of floatability for galena (<0.2V) and chalcocite (>-0.4V). An increase of the DF and the cathodic limit of the adhesion potential with increasing length of the hydrocarbon chain were observed. EP-pH curves for sulfides are a mirror-like to the DF-pH curves, Figure 2. Structure of solid-liquid and liquid-gas borders has a determinative importance for formation of bubble-mineral complexes and subsequently flotation results. Under vacuum on the mineral surface there are produced micro bubbles and preferably they will be appeared on the hydrophobic sites. Water structure breaks near a hydrophobic surface facilitate water mass destruction and formation of gaseous phase embryos under decompression in the impeller zone. It simultaneously reduces a probability of produced micro bubbles dissolution as a result of pressure increasing owing to constant fluctuation of liquid densities into impeller zone. Comparison of Taggart’s evaluation of the suction behind blades of the impeller of an agitation-froth machine and ABEP data on galena, Figure, shows that gas evolution will be observed in the range of 1300-2700 revolutions of impeller per minute for hydrophobic and hydrophilic surfaces successively."

Jan 1, 2003

By M. Özer, G. Önal, F. Arslan

"The use of ultrasonic in industrial processes has increased during the last few years. Ultrasonic vibrations are used in sieving, grinding, ore washing, cleaning, and flotation in mineral industry. There are also some attempts for the utilization of ultrasonic treatment in separation and removal of fine particles from gases and liquids. In Kalemaden A.S. (Turkey) four different types of clay mixtures (1. A mixture of clays from Balikesir-Düvertepe and Istanbul-Sile, 2. A mixture of clays from Ukrania and Balikesir-Düvertepe, 3. Sögüt-Kadikelimesi, 4. A mixture of clays from Sögüt and Istanbul-Sile) and kaolin from Balikesir-Düvertepe (Turkey) are concentrated before their use in ceramic production. Dewatering is the important step in those types of concentration plants. Sedimentation of concentrated clay has always been difficult and taken long times due to their nature and having small particle sizes. Flocculants can be used to enhance the sedimentation, but they are not preferred by the ceramic industry since they affect the quality of ceramic products. For this purpose, ultrasonic treatment is used in the sedimentation of clays mentioned above for solving the problems encountered related to the ceramic industry and promising results were obtained.Kaolin sample, subjected to this experimental study, from Balikesir-Düvertepe region of Turkey was brought from the plant as a pulp in containers and throughly mixed with a stirrer before sedimentation experiments. A two liter graduated cylinder and an ultrasonic bath (with 25 kHz frequency and 0.5 KW power) were utilized in the tests. Superfloc A-120 (1% concentration) was used as a flocculant. The settling distance was reported against the settling time during the experiments. Initial and final pulp densities were also determined. The effects of several parameters such as pulp density, flocculant addition, and ultrasonic treatment on the sedimentation of kaolin were investigated and the results are represented in terms of settling distance versus settling time."

Jan 1, 2003

By Felix M. Zhuravlev, Vitalij P. Lyalyuk

"While there is a large industry based on recovering platinum group metals (PGM) from complex sulphide ores containing Cu and Ni, there is little information on the thermodynamics of the matte phase formed on smelting the ore and in particular the behaviour of Pt in the matte.The equilibrium between metallic platinum and industrial mattes was studied in a series of experiments where a small quantity of matte (5g) and platinum foil of 150 µm thickness (0.5 g) were equilibrated in magnesia crucibles at 1400°C under conditions where the oxygen and sulphur partial pressures were controlled.The chemistries of the phases were determined from EDS analysis using a scanning electron microscope. Line scans were initially used to confirm that the foils had attained a uniform composition across their thickness. The composition of the matte was determined from analysis of an area of matte including the small metallic droplets and dendrites.The distribution of Pt in Cu-Fe-Ni mattes (Pt: 1.5 – 3%) and solid Pt alloys (Pt: 54 – 72%) was studied. For a matte of base composition 45%Fe, 11%Ni, 8% Cu, at a base temperature 1400°C, the following behaviour was observed for the Pt distribution ratio:Under the range of sulphur and oxygen pressure of this study (log pO2 from -15 to –12.2, log pS2 from – 4.6 to –2.2), the distribution ratio of Pt between matte and alloy was independent of the sulphur and oxygen pressure, having a value of 0.04.The Pt distribution ratio increased from 0.02 to 0.08 with temperature from 1340 to 1450 oC.For mattes where the proportions of Cu and Ni were kept constant, a slight decreasing trend was shown for the distribution ratio of Pt versus the iron content (37 to 53%) in the matte but was not confirmed because of experimental uncertainty."

Jan 1, 2003

By C. P. Lowes

"The REFLUX™ Classifier (RC™) consists of a fluidized bed housing, with a system of parallel inclined channels above. This system performs a simultaneous gravity separation and desliming of the feed material, utilising the inclined channels in order to retain the relatively fine dense particles. These particles promote the formation of an autogenous dense medium within the fluidized bed. Relatively large, low density particles are displaced from the fluidized bed and conveyed upwards through the inclined channels reporting to the overflow with other finer particles. Given the hydrodynamic role of both the particle size and density in determining the particle transport through a water based suspension, all gravity separators operate over a limited size range. In the case of the REFLUX™ Classifier, efficient separations can be produced across a very broad size range, from nearly 10 mm down to 10 m, however, for a given application the size range is much more limited. This study was concerned with the processing of dense minerals over a broad size range, and the need for multistage processing. Here the overflow from the first stage cascades to the second stage, incorporating coarse gangue rejection. This approach is shown to deliver remarkably high grades and recovery.INTRODUCTION The performance of the REFLUXTM Classifier (RC™) in beneficiating fine coal is well documented (Galvin, 2012). Although the technology can be applied to relatively fine particles below 0.1 mm, or coarser particles below 2.0 mm or even 8.0 mm (Galvin et al., 2010), in each case the technology is applicable to limited particle size ranges. In coal preparation, the most common size range is 0.25 to 2.0 mm, covering an eight-fold range in the particle diameter. Coal has a relatively low density, typically below 1600 kg/m3, with a significant portion below 1400 kg/m3. In water, the buoyant density difference (~ 400 kg/m3) is therefore low compared to that of gangue minerals (1600 kg/m3) by a factor of 4, enhancing the potential for separation. Thus, in coal preparation, the technology can be applied over a commensurately broader size range, typically up to eight-fold."

Jan 1, 2018

By S. Banisi, O. Farshid, M. R. Rozebehi, A. Bahar, A. Arghavani, M. Mahdavi

At the rougher flotation circuit of the Miduk copper concentration plant (Kerman, Iran) five column cells (CISA) with the diameter of 4m and height of 12m using static mixer type (MicrocelTM) spargers have been installed. Based on the initial design, columns should accept a feed rate of 625 t/h with 80% passing size of 90 µm and solids concentration of 28% and produce 88% of the plant concentrate (i.e., 22 t/h) containing 32% copper. Due to mechanical and processing problems this objective was never realized and theses columns were remained out of operation from the commissioning time (2005). A new attempt with the aim of returning these cells into operation started in 2013. The results of an extensive study indicated that spargers plugging due to the entrance of small amount (2 kg) of coarse particles (up to 2.5 cm) because of usual problems at the plant environment was the main reason of columns non functionality. With a change in the recycle pump inlet design to the column, which prevented the entrance of coarse particles to the spargers, the operation of the column significantly improved. It was found that in order to have a stable operation of the columns at the rougher stage the feed rate for each column should be reduced from 125 (design) to 70 t/h. The air superficial rate had to be also reduced from 1.9 (design) to 0.6 cm/s. A period of 10 days of continuous operation showed that the carrying capacity was 0.23 (g/min/cm2) which was significantly lower that of the design value (i.e., 0.58). The gas hold up was found to be lower than 10% beyond which columns started to move to the turbulent state indicated by "boiling" froth. The average life time of spargers was determined to be 20 days which considered to be very short. The average recovery and concentrate grade of these columns were found to be 68% and 32%, respectively. The high wear rates of spargers, unusually high level of maintenance and supervision needed and instability of the operation made the plant managers not to use column cells as the roughers.

Jan 1, 2014

By W. H. Cheung

Nickel (Ni) plays a major role in the production of steel and other major alloys. There are two sources of Ni: laterite and sulphide ores. Global reserves of sulphide ores are being rapidly depleted, while there are enormous reserves of Ni laterite, much of it in Australia. As well as being present in huge amounts, Ni laterites have the advantage of containing cobalt (Co), a valuable mineral. Over the past decade, these factors have been driving the industry to explore the processing of Ni laterite. A route that has been used commercially in processing nickel laterite ore involves the thermal activation of the minerals by pre-reduction followed by ammoniacal leaching (Caron). Although this process has been effective in processing the goethite rich laterite minerals, the higher-grade serpentine-based minerals have been shown to be less susceptible to this process. This has been attributed to the formation of inert olivine phases. In this study, we examined the use of an alternative lixiviant, sulphuric acid, in leaching pre-reduced limonite and weathered saprolite nickel laterite ores. The specific aim of this study was to examine the sulphuric acid leaching of Ni and Co from pre-reduced laterite minerals, and to understand the role of mineral transformations in this metal dissolution. Synchrotron based X-ray diffraction was used to examine the transformation of goethite (FeOOH) to spinels and serpentine mineral ((Mg,Fe)3Si2O5(OH)4) to olivine. Reduction tests were carried out using CO and CO2 reducing gas mixtures and temperatures from 400 °C to 700 °C. The rate of formation and disappearance of specific Bragg peaks during reduction of specific minerals were used to derive an understanding of these solid-state reactions. Laboratory based reduction tests and leaching in sulphuric acid were used to validate the effect of these mineral transformations. The results suggest the versatility of sulphuric acid in leaching nickel from spinels and olivine, which was achieved at the expense of lower selectivity. Cobalt dissolution was found to be dependent on the nature of ferro-cobalt alloy formed during reduction.

Jan 1, 2014

By William Skinner, Ishmael Quaicoe, Jonas Addai-Mensah, Ataollah Nosrati

To date, intractable ore specific operational challenges such as poor heap geotechnical stability, permeability and high acid consumption rates associated with low grade (~1 wt%) nickel (Ni) laterites still makes the adoption of heap leaching processing unattractive. This paper presents some highlights of drum agglomeration, column leaching and characterization studies undertaken to foster the understanding and knowledge of some of the desirable product attributes of -2 mm and -15 mm, low grade saprolitic (SAP) and goethitic (G) Ni laterite feed ores and their blends (SAP/G). For column leaching, 5-40 mm agglomerate beds were continuously irrigated with 200 g/dm3 H2SO4 solution at 8.5 dm3/m2/h rate over 100 days. Ni, Co, Fe, Al and Mn extraction rates, free acid concentration, agglomerate bed slump and structural changes were determined as a function of time. The results show that at equivalent feed masses, except -15 mm G which displayed slower, pseudo-layering based behaviour, all the feeds (single and blends) displayed coalescence controlled agglomeration behaviour at varying binder dosages. Whilst the agglomerate compressive strength of the G ore was markedly higher than that of SAP ore, those of the blends were substantially similar. At fixed column leaching conditions, the Ni/Co extractions and acid consumption were higher for SAP ore whilst the agglomerate bed slump was lower than those for G ore. The bed of agglomerates produced from -2 mm G/-15 mm SAP blend was more stable than that for the -2 mm G/-2 mm SAP blend agglomerate, the latter experiencing blockage within 24 h of acid irrigation due to agglomerates breakdown. The Ni/Co extractions and acid consumption rates obtained for agglomerates of -15 mm G/-2 mm SAP blend were lower than expected based on the ratios of the SAP and G ores within the blend composition. The findings suggest that judicious saprolitic and limonitic ores’ blending could reduce acid consumption rate, improve the agglomerate bed robustness and enhance bed percolation behaviour under prolonged acid irrigation periods during heap leaching of lateritic ores of variable mineralogy.

Jan 1, 2014

By Katarina Theander, Robert J. Pugh

In the flotation process, control of the stability of the froth is extremely critical. In the case where the froth is too stable then mechanical entrainment of particles can occur but in the opposite case, where the froth is too unstable and difficult to skimm-off, then a reduction in recovery can result. In minerals and deinking flotation, commercial fatty acids are used and may act as both both collectors and frothers. However, frequently the fatty acids are mixed with nonionic ethoxylated surfactants to give more effective froth control and increase the flotation performance. It is of interest to note from the surface chemistry literature, that such mixtures may cause synergistic effects in surface activity which may explain changes in bubble size, foaming and carry over of particles. In the present study, we have carried out foaming and drainage experiment with oleic acid and model nonionic surfactants; hexa(ethylene glycol) mono-dodecyl ether, C12E6 and tetra (ethylene glycol) mono-dodecyl ether, C12E4 both in separate and mixed systems. Frothing was carried out in a column, equipped with a series of conductivity electrodes which enabled the water content of the froth to be measured along the length of the column, during various stages of the drainage process. The variation in water content of the froth enabled the process to be characterised by distinct three stages; (a) an entrainment state where the water transfer from the bulk phase to the froth was dominant (b) a steady state when entrainment and drainage are balanced and no water is transferred to or from the froth and (c) the drainage step when drainage predominates and the volume of the bulk phase increases. We also carried out surface tension measurements on the oleic acid/ nonionic systems and related the results to the frothing and drainage performance. From the surface tension data, the adsorption interaction parameter of the mixed systems at the air/solution interface could be calculated and was found to depend on the oleate/ nonionic surfactant ratio. This value was related to the frothing performance and the results indicated a positive interaction parameter for the mixed surfactant systems which could explained the synergistic effects in frothing performance.

Jan 1, 2003

By I. A. Makalin, V. N. Yakovlev, S. V. Imangulov, I. V. Zyryanov

"The presented studies aimed at solving the problem of recovery of low-luminescent diamonds, which are not recovered using X-ray luminescence method of processing of diamond-bearing ore. The purpose of the studies is the determination of possibility and feasibility of recovery of such crystals using dual-energy X-ray transmission separation technology. In preparation for studies methods were developed for testing technical and process parameters of XRT-400 Aliud GmbH (Germany) sorter, manufactured according to design specifications of Yakutniproalmaz Institute, and XRT/D TOMRA Sorting Solutions GmbH (Germany) sorter, designed for processing of -50+5 mm ore, as well as RGS-1M, RGS-2 X-ray sorters, developed by JSC NPP Bourevestnik (St. Petersburg) in cooperation with Yakutniproalmaz Institute, for material size of -6+3 mm. In 2018, in-process tests of RGS-OD-3 X-ray sorter prototype on material size of -3+1 mm are scheduled. Studies to determine the content of low-luminescent diamonds and feasibility of their recovery using XRT-400 and XRT/D sorters at the Processing Plant #3 of Mirny Mining and Processing Division (MPD) were carried out. The results of the studies confirmed presence of such diamonds and possibility of their recovery using the dual-energy X-ray transmission method. In-process tests of RGS-2 X-ray graphic sorter were carried out at the Processing Plant #16 of Nyurba MPD. According to the results of sampling of RGS-2 sorter separation products, the recovery of -6+3 mm sized diamonds from tailings of X-ray luminescence sorters was achieved at the level of 96%, while the diamonds recovery was 98.5% in value terms, the concentrate yield was 0.1%. In-process tests of RGS-1M sorters at final recovery of the grease separation concentrate at the Processing Plant #3 of Mirny Division were carried out. Recovery of low-luminescent -6+2 mm sized diamonds by RGS-1M sorter amounted to 92.4% for single operation, and with the double control operation reached 99%. As a result, -6+2 mm sized base product recovery increased by 0.2%."

Jan 1, 2018

By O. N. Mohanty, S. Mohan Rao, N. D. Rao, T. Mukherjee, P. V. T. Rao

"Chromite ore is an indispensable raw material in the manufacture of ferro-chrome and charge-chrome, which are used for the production of stainless and other alloy steels. The demand for chromite ore is ever increasing because of increasing consumption of these steels. Keeping this in view, Tata Steel is keen to recover values from fines and wastes, and also to produce value added products from their captive chromite mines and its processing plants.Tata Steel has its captive chromite resources at Sukinda, Orissa. They contain two ore types, i.e. (i) Ferruginous and (ii) Siliceous. The generation of off-grade ores is an increasing trend and simultaneously customer quality requirements are becoming ever more stringent. The ferruginous type ore also contains a considerable quantity of in-situ fines (~20% particles below 0.5 mm) that compound the beneficiation problem.In many places, in India and abroad, mined non-marketable off-grade and low grade chromite ores are upgraded by using either simple classification techniques like screw classification, hydrosizing, hydrocycloning or conventional gravity concentration processes such as Heavy media separation, Jigging, Spiraling, Tabling etc.At Tata Steel, the ferruginous type ores are treated in Chrome Ore Beneficiation (COB) Plant that comprises: a crushing and grinding circuit; a classification circuit using hydrocyclones; and a beneficiation circuit using 4 stage spirals in the coarse circuit (-0.5+0.1 mm) and 3 stage spirals & tables in the fine circuit (-0.1+0.038 mm). In this process, 3 types of tailings are being generated and together analyses about 17 % Cr2O3, which is high. From the present operation the chromite recovery is around 70% and could not produce coarse concentrates (+0.5 mm size). Whereas the siliceous type ore is treated in the Lumpy Ore Processing (LOP) plant, consisting of crushing-washing & classification-hand sorting operations, to produce marketable grade lumpy ore and –10 mm de-slimed fines. These fines are intermittently treated in the COB plant. The higher silica content (greater than 1%) and low Cr/Fe ratio (less than 2.8) are the problems with these concentrates."

Jan 1, 2003

By Sanggono Adisasmito

"The quality of the higher education in Indonesia is being improved by implementing a program financed by the World Bank under a project named QUE (Quality for Undergraduate Education). The investments are provided to selected study programs through a competitive selection process. The grant finances staff development, the purchase of equipments, textbooks, consumables, technical assistance, and incentives for outstanding faculties such as teaching grants, project grants, lecture note awards, and educational policy studies. These additional investments are provided to produce chemical engineering graduates that will compete beyond the national market.Chemical Engineering Department of Institut Teknologi Bandung in Indonesia has been selected to receive the QUE grant beginning the year 2000 and ending the year 2004. The department is actively involved in the mineral processing issues, particularly in the aspects of energy supply and the environmental protection. The activities are distributed in different laboratories and areas of expertise, such as: thermodynamics and utility systems, process equipment, chemical reaction and catalysis, microbiology and bioprocess engineering, process control, ceramics, as well as polymer and membrane technology. The main objectives of the QUE project are to improve the undergraduate program in the following aspects: Relevance, Academic atmosphere, Institutional management and commitment, Sustainability, as well as Efficiency and productivity, or abbreviated as RAISE. At the end of every fiscal year, the progress of the program is evaluated to measure the effectiveness of the project.The achievement of the QUE project objectives were assessed using performance indicators developed during the program design. There are six indicators to measure the performance of the individual program of study, such as: (1) Admission Test score, (2) average students' Grade Point Average (GPA), (3) average graduates' length of study, (4) graduates' waiting time before getting first job, (5) Test of English as Foreign Language (TOEFL) score, (6) Graduate Record Examination (GRE) score. Essentially, the RAISE evaluation criteria will be used to perform three main functions, such as (1) to measure the achievement through the six quantitative performance indicators, (2) to support the progress of evaluation and reporting throughout the implementation of the program, (3) to provide a universal framework for qualitative evaluation."

Jan 1, 2003

By Vladimir Grujic, Milorad Grujic, Ivan Djurkovic, William Riggs

"In this paper, we have studied efficiency of different chemical structures of frothers on copper ore Majdanpek. The goal was to find out the best suitable chemical structure, which allows good bubble formation, size and interaction, forces on mineral surface. The particle size distribution was between 10 and 100 µm. Our research was oriented on three groups of frothers: alcohols, poly glycol ethers and poly glycols.We also used different collectors based on similar or less similar alcohol group in chemical structure as in frothers, expecting higher stability of air bubble in contact with copper minerals. Minimal potential energy was determinate in the hydrodynamic conditions for different particle sizes. It was founded that it is proportional to air bubble volume on 0.88° and contra proportional to the kinematics viscosity of pulp.Analyzing the results, we find out that poly glycols decreased surface tension the most. Also, it increased amount of coarser particles to the top of pulp. This group is less sensitive to pH value compared to the others too.From the class of frothers with higher efficiency in flotation process, we pointed OrePrep X-75 and X-133 as frothers with expressive frothing characteristic in the alkaline and low alkaline circuits. Special suitability of those frothers for floating copper minerals makes their hetero polar molecules with more than one hydrocarbon radicals connected to one polar group. However, those froters have no nether high or low solubility and are non-ionization. Those froters indicate some small collecting characteristics too. In dispersion systems, those two frothers make two types of bubbles: smaller di < 1.2 mm; V = 0.0008 cm3 and middle di < 16 mm; V = 2.2 cm3 (di – Bubble diameter, V – Bubble volume). Transportation speed of air bubbles it is possible to calculate based on equation: ?s = 27.5 * di 1.4 cm/s. Distribution of free surfaces for chalcopyrite is average 80% in the class –74µm +10µm and 20% in the class -10µm. If we get all class sizes, we find that recovery (R) depends from the time by equation:"

Jan 1, 2003

By Alan Bax, John D. Lewins

"Platinum Australia Limited (“PLA”) is currently undertaking a Feasibility Study into the development of the Panton Platinum Palladium Project located in the Kimberley region of Western Australia. The Panton Intrusive is a layered, differentiated mafic to ultramafic structurally complex body that has undergone numerous folding and faulting events. This has resulted in a southwesterly plunging synclinal structure some 10 kilometres in length and 3 kilometres wide.High grade PGM mineralisation is hosted within a number of stratiform chromitite reefs within the ultramafic sequence. The focus of the Feasibility Study is on the Top Reef which is situated approximately 150 metres below the mafic/ultramafic interface. The average true width of this reef is approximately 1.2 metres and the reef has a defined resource is 10.1 million tonnes at an average grade of 6.1 g/t PGM + Au.The Palladium to Platinum ratio of the Top Reef is approximately 1.15:1 and the reef also contains an average of 0.4 g/t Au and 0.3 g/t other PGM’s. The Panton ore is considered refractory in nature and standard flotation techniques achieve a PGM + Au recovery of less than 65% with a concentrate grade of less than 100 g/t PGM + Au. As part of the Feasibility Study Platinum Australia in conjunction with their major shareholder Lonmin Plc developed a new metallurgical process which has achieved an overall PGM + Au recovery of approximately 80% into a high grade PGM concentrate which is suitable for feeding direct to a PGM refinery.THE PANTON PROCESSThe Panton Process incorporates a two-stage Milling and Flotation circuit with no cleaning stages to produce a low grade, high recovery flotation concentrate. Typically the concentrate mass constitutes 25% of the feed and has a PGM + Au grade of 25 g/t.This low-grade concentrate is subjected to calcination in a rotary kiln or fluid bed at a temperature of approximately 400 0C for a period of 60 minutes. This step is designed to render the platinum minerals soluble in cyanide and both the temperature and the duration of calcination are critical to the efficiency of the leaching process."

Jan 1, 2003

By I. Gombköto

To sustain the growth of industrial production necessitates the increasing of the amount of processed mined raw and secondary materials. As a side effect of raw material production, the amount of tailings material, - coming from mineral processing operations ? increases as well. Using wet technology, these tailing materials are generally transported and stored with the water used for previous operations. This habit could lead to dangerous situations. Enough to remember the disasters had happened to the last decade, safe tailings operations need to remove as much water from the solid as possible. Environmental, technical and economical needs should meet, therefore using a technology combining these specific needs could be necessary. Paste technology was introduced generally into tailings operations at the last ten years, as an answer to the call of the above mentioned challenges, however there are still many questions to answer within the frame of using it. The Institute of Raw Materials Processing and Environmental Process Engineering of the University of Miskolc has been dealing with mechanical process engineering, especially by the support of the EU project TAILSAFE Contract nº EVG1-CT-2002-0066 and the NKFP 3A/068/2004 Hungarian fund extensive research has been carried out about paste technology. Different test methods and materials were applied. Tested tailings materials were as follows: different fly ashes from coal power plants from Pécs ? Hungary, Gyöngyös ? Hungary, Neyvil ? India, different Croatian ashes, hazardous waste incineration plant ashes from Dorog ? Hungary, different kind of sands from Hungary, fine glass sand from Fehérvárcsúrgó ? Hungary, flotation ore processing tailing from Gyöngyösoroszi ? Hungary. Different additives, as gypsum, bentonite and cement were tested as well. The applied test methods were as follows: physical material testing (laser sizer, piknometer, different microscopes), X-ray diffraction analysis, settling columns, the three measuring pipes tube viscometer (16~27 mm pipe diameter), a hydraulic test loop with different pumps (40~53 mm pipe diameter, 0.2~4 m/s average slurry velocity range, 0%~52 % volumetric concentration range), rotational viscometer, Cassagrande yield locus tester and the slump cone test. This paper summarizes and systematizes the results of the aforementioned research as well as reports about the developed paste pipe transport design method based on the fine suspension ? coarse mixture model. The paper also reports about a systematic experimental series with different materials to establish criteria when high concentration suspensions behave like paste.

Jan 1, 2014

By S. Banisi, A. R. Ghasemi, M. Maleki-Moghaddam

Direct observation of the charge shape and its motion in industrial mills are not possible, it is then customary to use transparent end, small-scale mills (i.e., model mills) to determine the charge trajectory directly by visualization methods. Because of a short length of the model mills, the end-wall effects could introduce a significant bias on the observed charge trajectories and shape. The shorter the mill, the stronger the bias. This could be due to some material bridging between the end walls. In this research, the end-wall effects were investigated by gradually increasing the model mill length and analysing the charge trajectory and shape variation at a given operating conditions (i.e., ball filling, mill speed, liner type). The unbiased mill length was assumed to be beyond the mill length where no significant change observed in the charge trajectory and shape. For all tests, the torque of the charge was also measured by a torque sensor. The special design of the model mill with the diameter of 100 cm made possible to increase the mill length in steps of 3.6 cm up to 21.6 cm. Four types of liners, five steel ball fillings (10, 15, 20, 25, 30% v/v) and three mill speeds (55, 70, 85% of critical speed) were tested. The ball sizes ranged from 4 to 12 mm. The results indicated that when the mill length was below 10.8 cm the end walls prevented the charge from free falling. This resulted in lower impact point angles and lower power draws compared with the case of no end-wall effects. When the same experiments were performed using an iron ore instead of balls with the same size range, the impact of end-wall effects was more pronounced. For an increase of 30% in the speed (from 55 to 85%), the torque due the change in the charge shape decreased by 41% (from 3.7 to 2.2 kgf.m) when mill filling was 30%. At the same operating conditions when steel balls used the torque decreased only by 19% (from 9 to 7.2 kgf.m). This was expected due to irregular shapes of the ore particles which facilitated bridging. Three-dimensional DEM simulations also resulted in the similar conclusions.

Jan 1, 2014

By I. V. Makarskii, D. N. Nikitin, L. G. Tarasova

"The extent and nature of the damage to diamonds at processing plant is largely determined by the design features of the equipment, the characteristics of the feed ore and the parameters of the ore disintegration process (change in the rotational speed of the autogenous mills, variations of the water supply to comminution process, choice of the optimum charge, etc.). To monitor the intactness of diamonds, an instrumental method using the X-ray tomography system and colored synthetic indicator diamonds was developed for identifying the process-related damage. The X-ray tomography system consists of a CT-Portable X-ray tomographic scanner, a crystal positioning device and customized software (developed by the Fraunhofer Institute and Aliud GmbH, Germany). The developed method enables improvement of the accuracy of the results, exclusion of the subjectivity of the mineralogical assessment, acceleration of data processing and promptly planning of the activities aimed at reducing the process-related damage to diamonds. KEYWORDS Diamonds, colored indicator diamonds, process-related damage, loss of mass, instrumental method, X-ray tomography system. INTRODUCTION Industrial tests of ore processing technology at the enterprises of ALROSA PJSC are accompanied by assessment of the process-related damage to diamonds. The assessment of the process-related damage to crystals is carried out for prompt elimination of factors contributing to the increase of impact forces in the process flow sheet of ore treatment plant. For this purpose a specially selected parcel of -4.0 + 2.0 mm sized natural indicator diamonds is used. The diamonds are exposed to ionizing radiation in order to turn them green and thus to create a distinctive feature. Colored natural indicator diamonds are described, photographed in several views and introduced into the process flow sheet of the processing plant, then extracted from the process flow, described and photographed again. The comparison of diamonds before and after their passing through the process flow sheet of the plant allows to find evidence of process-related impact on the crystal and to calculate the factor of process-related damage (the number of crystals damaged during liberation and recovery), the loss of crystal weight and the degree of damage to the crystals. The method of colored indicator diamonds is used to select processing methods, equipment or regime which would be the safest for diamonds based on the analysis of the factors of process-related damage. There are limitations of the method, such as:"

Jan 1, 2018

By A. J. Lynch, L. Ergun, M. Oner

"A research program on modelling cement grinding circuits has been in operation at Hacettepe University, Ankara, for four years. It has concentrated so far on tube mill and air separator grinding circuits for cement clinker, with emphasis on plant sampling surveys, including axial sampling inside the tube mills. The methodology is to use plant data to build the models and to supplement this by laboratory data where necessary, for example the determination of breakage functions. The plant data come from comprehensive sampling surveys and so far 33 surveys of clinker grinding circuits have been carried out in 9 plants. The operating conditions have been• mill sizes – 3.2 to 4.8 metres diameter and 8.5 to 15 metres long,• mill feed rates – 46 to 158 tonnes per hour,• air flow through mills – 25000 to 125000 cubic metres per hour,• cement clinker work indexes – 10.3 to 18,• separator sizes – 2. to 3.1 metres diameter,• separator feed rates – 132 to 689 tonnes per hour,• separator speeds – 12.3 to 21 metres per second.The ball mill model is Whiten’s perfect mixing model and the separator model is the Tromp curve with a fish-hook. This paper emphasises on the importance of calculating the breakage rates and the discharge functions with three case studies at five different circuits which were selected for discussion because they show how particular features of circuit operation can be included in the general models. Size distributiongraphs are used to illustrate every aspect of the discussion.In case I the special emphasis on calculating the breakage rates and discharge rates separately is given in a high pressure grinding roll-ball mill-separator circuit. The tonnes of each size fraction in the mill and the calculated values of R/D, D and R are determined. The values of R per mw are also given to allow comparison with mills of other sizes. The circuit allows the comparison of the static type (V Sep) and dynamic type separators (SKS). Comparing the reduced efficiencies shows that the dynamic separator is slightly more efficient than the static one.In case 2 data are given from two compartment tube mills having the same diameter and the motor power but different ball size gradation. The breakage rate particle size variation of the second chamber of two mills indicate that having finer ball size distribution causes higher breakage rate values."

Jan 1, 2003

By Güven Önal, Zeki Dogan, Neset Acarkan

"In general, the processing of glass sand may involve comminution, washing, wet classification and attrition scrubbing. Additional processes may include magnetic separation, flotation and leaching in various combinations.Yaliköy sand dune deposit is located near to Istanbul on the European side by the Black Sea coast. The reserve of deposit is around 70 million tons. Iron content of Yaliköy sand dunes is 0.48 % Fe2O3 and not suitable for glass manufacture. The iron content of glass sand should be less than 0.15 % Fe2O3 for window glass manufacture and 0.05 % Fe2O3 for glassware. In this study, it was aimed to produce glass sand with less than 0.15 % Fe2O3 for window glass and with less than 0.05% Fe2O3 for glassware manufacture from Yaliköy sand dunes. A representative sample with a weight of 200 kg was taken from Yaliköy sand dunes deposit through opening small pits.• Mineralogical studies have shown that iron is present in three forms:• Hematite, limonite, clay and iron silicate minerals such as epidote and garnet occur in free form.• Quartz grains are coated by hematite and limonite.• Iron is also present in the cracks of quartz grains.Free iron minerals such as hematite and limonite and silicate minerals were subjected to magnetic separation and flotation for removal. Iron coatings were tried to be removed by scrubbing and leaching. Iron removal in the cracks of quartz grains was attempted by grinding and leaching.Under optimal conditions, sand concentrate with 0.38 % Fe2O3 was obtained by means of high intensity disc type magnetic separation. Grinding and scrubbing were applied to see the effect of size reduction and attrition at room temperature and 90 ºC, by using non-magnetic fraction. Sand concentrate with 0.13% Fe2O3 was obtained at 90 ºC in this test.Sand sample which was previously ground to minus 0.5 mm and scrubbed, was floated by using sulphonates as collector. After flotation tests, sand Concentrate was obtained with 0.11 % Fe2O3.The optimum iron removal was achieved by H2SO4 leaching at 90 ºC depending on acid concentration and leach duration in static, percolation and agitation leaching. Agitation leaching was done by the use of mixer at 600 rpm, 50% solids and leach duration was 15 minutes."

Jan 1, 2003

By lves Matiolo, Jorge Rubio, Carlos Perez Guerrero, Denise G. Nunes, Fabiano Capponi

The problem (very old) of processing by flotation, the fine (“F”, 38-13 µm) and ultrafines (“UF”, < 13 µm) mineral particles continues to be a major technical challenge in the area of mineral processing. Many different processes have been proposed over the last three decades but, unfortunately, most of them have not found practical applications yet. This paper describes some advances in flotation research in fines (“F”, 38-13 µm) and ultrafines (“UF”, < 13 µm) mineral recovery by two different techniques. Extender flotation (EF) and flotation with bubbles with a wide size distribution-SB of copper sulphide ore fines (1 % Cu) were compared with a “standardised” (STD) mill laboratory procedure. Comparative evaluation was made through concentrate grade and recovery (size by size results included), “true” flotation recoveries and process kinetics. Copper porphyry samples, containing about 1/3 of the mass and about 37 % of the total copper content in the fines and ultrafines fractions were used. In the EF tests diesel-in-water emulsions were used as an extra reagent, added after the collector and frother addition. In SB tests, drawing air through an aspiration nozzle, directly in the pulp, generated bubbles sized about 50-200 µm. Both techniques yielded higher metallurgical efficiencies than the mill standard but better results were obtained with the extender flotation, with emulsified diesel oil (90 gt-1). Concentrate recoveries were of the order of 85-90 % (84 % in standard conditions), 14-17 % Cu grade (15 % Cu in the standard) and 3.5-4.5 min-1 for the Klimpel rate constant (3 min-1 in the standard). Size by size and true flotation results proved that metallurgical and kinetic gains, obtained with the two techniques, might be attributed to fines and ultrafines enhancement. Data obtained are discussed in terms of physical and physicochemical parameters related to aggregation and capture (of particles by bubbles) phenomena and the practical potential of these techniques are envisaged. The following figure shows size-by-size copper recoveries results, after classification of produced concentrates and tailings using micro-sieves. Results clearly show that flotation of the F and UF fractions is highly improved with injection of small bubbles (SB) and with the addition of an extender collector. It is believed that the techniques presented here will establish shortly a new basis for the flotation enhancement of the F and UF, aimed at solving a very old problem. This work is being continued, now at pilot plant scale, and results will be published en the near future.

Jan 1, 2003