By R. Bakish, W. D. Robertson

IN the course of a study of stress corrosion cracking of AuCu,, it was necessary to develop new electropolishing and metallographic etching methods. The techniques are generally useful for Cu-Au alloys, including the AuCu composition in which transformation markings are well delineated. For electropolishing, the only satisfactory electrolyte and procedure that has been found1 has the composition given in Table I. The solution must be vigorously stirred while polishing and the temperature maintained in the range of 55" to 62°C. The electrolyte is very unstable and can be used only for 10 to 15 min after which its color changes and a dark-brown precipitate forms. The polishing time is between 1 and 4 min depending on the initial surface preparation. The use of a hood is recommended to avoid the danger of cyanide gas which may form at one of the electrodes even though the solution is alkaline. The optimum current and voltage conditions for vertical anode and platinum cathode are on the plateau shown in Fig. 1, in which voltage is measured across the cell terminals. At voltages below the plateau, etching of grain boundaries occurs and under some conditions, which have not been clearly defined, octahedral etch figures are observed. For general purpose grain-size determination in polycrystalline alloys, a 3 pct solution of iodine in methyl alcohol is used with excellent results. However, when it is necessary to reveal small orientation differences or concentration gradients in an alloy, the iodine etch is not satisfactory. For this purpose, a highly satisfactory etching procedure was developed during this investigation. It involves the use of the vapor given off by freshly prepared aqua regia. The solution employed is 3HC1 to lHNO, which decomposes in accordance with the reaction HNO, + 3HC1 = NOCl + 2H,O + Cl,. The polished specimen surface is held about 1 to 2 cm above an aqua regia solution for 2 to 10 sec depending on the intensity of the contrast required and the surface is not subsequently washed. The results obtained with a coarse grained cast structure are shown in Fig. 2. Subgrain boundaries in a single crystal and concentration gradients within the boundaries are developed by the same treatment with the results shown in Fig. 3. Obviously, any conclusions regarding structure-dependent properties will be modified by the pronounced heterogeneity, which is not clearly evident when more conventional methods are used. Interesting structural details are also revealed by treatment for 4 hr at 850°C in unpurified tank argon. Fig. 4 shows a pattern characteristic of orientation-dependent oxidation.

Jan 1, 1956

By H. J. French

WITHIN the past few years, particularly because of the rapid growth of the airplane industry during the war, considerable attention has been paid to the manufacture of light-wall cold-drawn seamless and welded steel tubing for structural purposes. While the manufacture of such tubing is not, in itself, a difficult matter, some difficulties have. been encountered in producing the same under specifications requiring definite physical properties. It is the purpose of this paper to describe the methods of manufacture and the properties that may be obtained by such methods for tubing coming within about ½ to 2 in. (12.7 to 50.8 mm.) outside diameter and 10 to 22 Birmingham wire gage (0.134 to 0.028 in. wall thickness). Such tubing is largely used as structural material in the aircraft industry, and it is of the utmost importance that the physical and chemical properties should be known, and also that the various factors entering into the manufacture should be under such control as to allow these properties to be varied and held within definite limits. In general, tubing may be divided into four classes: namely, specialty tubing, such as riveted-sheet or plate, lock jointed, etc.; brazed tubing; welded tubing; and seamless tubing. Welded tubing may be divided into hot product, such as lap welded and butt, welded, and cold product, such as acetylene and electric welded. Seamless tubing may be hot rolled or cold drawn.

Jan 9, 1919

By K. E. Brown, A. R. Hagedorn

A 1,500-ft experimental well was used to study the pressure gradients occurring during continuous, vertical, two-phase flow through 1-in., 1 1/4-in. and 1 1/3-in. nominal size tubing. The test well was equipped with two gas-lijt valves and four Mathak electronic pressure transmitters as well as with instruments to measure the liquid production rate, air injection rate, temperatures and surface pressures. Tests were conducted for widely varying liquid flow, rates, gas-liquid ratios and liquid viscosities. From these data, an accucrate pressure-depth traverse was construcred for each test in each of the three tubing sizes. From the results of these tests, correlations have beer] developed which allow the accurate prediction of flowing pressure gradients for a wide variety of tubing sizes, flow conditions, and liquid properties. Also. the correlations and equations which are developed satisfy the necessary condition that they reduce to the relationships approprate to single-phase flow when the flow rate of either the gas or the liqutid phase becomes zero. All the correlations involve only dimensionless groups. which is a condition usually Sought for in similarity analysis but not always achieved. The correlations developed in this study have been used to calculate pressure gradients for pipes of larger diameter than those upon which the correlations are based. Comparisons of these calcuclaed gradients with experimetally determined gradients for the same flow conditions obtained from the literature indicate that extrapolation to these larger pipe sizes is possible with a degree of accuracy sufficient for engineering calculations. The extent of this extrapolation can only he determined with additional data from larger pipe diameters. INTRODUCTION The accurate prediction of the pressure drop expected to occur during the multiphase flow of fluids in the flow string of a well is a wideiy recognized problem in the petroleum industry. The problem has been brought even more into prominence with the advent of tubingless or slim-hole completions which use small-diameter tubing. Many of the correlations which give reasonably accurale results in the lager tubing sizes are greatly in error when applied to small-diameter conduits. Small-diameter conduits are defined as 1 1/2-in. nominal size tubing or smaller. The study of the pressure gradients which occur during multiphase flow of fluids in pipes is exceedingly complex because of the large number of variables involved. Further difficulties relate to the possibility of numerous flow regimes of widely varying geometry and mechanism and the instabilities of the fluid interfaces involved. Consequently, a solution to the problem by the approach normally used in classical fluid dynamics based on the formulation and solution of the Navier-Stokes equation has not been forthcoming. This is primarily the result of the nonlincarities involved and the difficulty of adequately describing the boundary conditions. As a result of the foregoing, most investigators have chosen semi-empirical or purely empirical approaches in an efford to obtain a practical solution to the problem. Much of the previous work in this area was done in short-tube models in the laboratory. A number of problems arise, however, when attempts are made to extrapolate these laboratory results to oilfield conditions where a much longer tube is encountered. In those few studies where data taken in long tubes were utilized, the data covered only a limited range of the variables, and as a result inaccuracies are introduced when the correlations are extended outside the range of the original data. Also, as a consequence of the limited amount of data available for these studies, the effects of several important variables were overlooked. The problem of predicting the pressure drop which occurs in multiphase flow differs from that of single-phase flow in that another source of pressure loss is introduced, namely, those pressure losses arising from slippage between the phases. This slippage is a result of the difference between the integrated average linear velocities of the two phases, which in turn is due to the physical properties of the fluids involved. In contrast to single-phase flow. the pressure losses in multiphase flow do not always increase with a decrease in the size of the conduit or an increase in production rate. This is attributed to the presence of the gas phase which tends to slip by the liquid phase without actually contributing to its lift. Many investigators have attempted to correlate both the slippage losses and the friction losses by means of a single energy-loss factor analogous to the one used in the single-phase flow problem. In an approach of this type, hourever, many of the important variables, such as

Jan 1, 1966

By M. S. Smani, P. Blazy, J. M. Cases

Investigations on the beneficiation of sedimentary Moroccan phosphate ores are reported in four separate parts. The first discusses electrochemical phenomena at the solid-aqueous solution interface for minerals of the apatite group. In the second part, the electrochemical properties of the calcareous gangue associated with the phosphate ore are investigated. The flotation of calcite and phosphate oölites, using both anionic and cationic collectors, is discussed in the third part. It is shown that selective recovery could be obtained for precise concentrations of collectors and pH ranges. Results of work aimed at optimizing depression of phosphate oölites during inverse flotation of the carbonate gangue with sodium oleate are reported in Part 4.

Jan 1, 1976

By M. L. Fuller

MOST commercial alloys undergo changes in phase composition after casting. This is a natural result of the fact that the alloys are not in a state of phase equilibrium as cast and phase changes will therefore take place, with more or less rapidity, in an attempt to attain equilibrium. The practical aspect of aging in zinc-alloy die castings concerns the changes in physical properties and in dimensions that may accompany aging phase changes. Harmful alterations have been reduced to a minimum and zinc-alloy die castings are being produced today that are so stable with respect to dimensions and physical properties that they are entirely suitable for most practical purposes1. In the first paper2 of this series, and in this paper, aging phase changes of zinc alloy die castings have been investigated and the possible influence of these changes on dimensional changes of the castings has been evalu-ated and compared with the dimensional changes actually experienced. The change of dimensions has been selected for practical comparison in these papers because the effect of phase changes on the dimensions of a casting is directly calculable; from X-ray crystal-analysis data of the phase structure. The die-casting alloys considered contain, in addition to zinc, 4 per cent of aluminum, about 0:03 per cent magnesium, and from 0 to 3 per cent of copper. It was shown in the former paper that the eutectoidal decomposition of the beta aluminum-zinc phase, while intrinsically capable of causing a considerable shrinkage, can have very little effect on the observed shrinkage of die castings because it takes place within a few days of aging, whereas the observed shrinkage continues for five weeks. It was therefore concluded that the other existing phase change,

Jan 1, 1935

By Martin E. Chenevert

The early work of Terzaghi1 showed that the true stress state of a rock can be expressed by the principle of effective stress. This principle states that effective stress is equal to total applied stress minus the pore pressure. Since the introduction of this principle, a great effort has been made to measure the pore pressure of rocks so that the true stress state can be determined. For clean, permeable sandstones, it is usually found that the effective stress principle can easily be applied. Direct measurement of the pore pressure is achieved with a hydraulic pressure device and the effective stress state thereby computed. However, for fine-grained rocks which contain large amounts of clay (referred to herein as shales), pore pressure measurements are usually quite difficult because of the adsorptive forces of the clay platelets, which produce negative internal pressures. No suitable device is known for measuring internal pressures of dry shales; the effective stress approach is therefore not feasible and data are usually presented in another form. As an example, data from compressive strength tests are presented as a function of rock wetness, rather than effective confining stress. The work of Belopoloskii2 and Colback and Wiid3 are examples of such data. It was pointed out by Lambe and Whitman4 that a better way must be found to express the effective stress of argillaceous rocks. The information presented herein is an attempt to fill that need. Various authors have been able to measure moderate negative pore pressures (0-240 psi) within rather wet, argillaceous rocks by means of various pore pressure devices. In 1961 Lambe5 resented information which shows that pore pressures in argillaceous rocks are indeed negative ; he presented values of suction pressure as low as - 14 psi. Likewise,

Jan 1, 1970

By J. L. Gregg

RECENTLY there has been considerable interest in the production and use of, extra hard alloys composed primarily of tungsten and carbon. Dr. Hoyt's recent paper1 gives a good description of these alloys and describes their performance when used as tools. There are a number of these alloys on the market sold under various trade names, and it is the purpose of this paper to describe the results of an investigation of the structure of five of these alloys by means of microscopic and X-ray methods. The samples studied were in the form of small tools or wire-drawing dies, which were either purchased or supplied as samples. They were in some cases not supplied by the original makers but were furnished by the agents in this country, and we wish to call attention to the fact that they may not be truly representative of the materials supplied under the various trade names. No performance data are given and no inference as to the inferiority of one alloy as against any other is made K Schröter2 recently described methods for polishing alloys of this type for microscopic examination and has presented photomicrographs of several alloys. However, he did not identify their constituents or describe methods for their identification.

Jan 1, 1929

By W. A. Foster

NINETY years after the Riddle nickel deposit N was discovered in Oregon in 1864, Hanna Coal & Ore Corp. began mining operations. Until 1954 much prospecting and preliminary development work had been done on the property, but no ore had been shipped other than for metallurgical testing. The deposit is being explored by churn drilling and trenching, and a few test shafts have been put down for the purpose of studying the ore in place, determining volume and moisture factors, and gathering bulk samples for pilot plant and smelter tests. In churn drilling, 6-in. casing is driven down 2 or 3 ft behind the drill bit and bottomed at each 5-ft interval. All the sludge for each cased 5-ft interval is dumped through a splitter and one eighth is saved and analyzed. Drillholes are stopped after going through the ore zone and penetrating fresh peridotite in which the nickel content is less than 0.5 pct.

Jan 8, 1957

By R. E. Ogilvie, J. I. Goldstein, R. E. Hanneman

The interdiffusion coefficients for the Fe-Ni system were determined as a function of composition in both the a and y phases at 1 atm pressure. The inter diffusion coefficients were also determined in the y phase at 40 kbar pressure. The concentration gradients were measured with an electron probe, and the diffusion coefficients were calculated by the Matano analysis. At 1 atm, Ey increases with nickel content up to 65 at. pct Ni. The relationship of Dy with temperature and nickel concentration, up to 50 at. pct Ni, is given by the equation DY-l atm = exp(.0519 CN~ +1.15) MANY of the transformations that occur in the solid state are diffusion-controlled, especially those involving precipitate growth in most metallurgical systems. Multicomponent diffusion is usually expressed in terms of a chemical or an inter diffusion The activation energy Q at 1 atm decreases from pure iron to 60 to 70 at. pct Ni and decreases from pztre nickel to 60 to 70 at. pct Ni. The Kirkendall marker movement indicates that DFe is greater than DNi zcp to about 60 at. pct Ni. Above 60 at. pct Ni, however, DNi becomes peater than DFe The inter diffusion coefficients were also compared with those calculated from self-diffusion data. A comparison between calculated and measured coefficients shows only rough agreement. The effect of 40 kbar pressure is to decrease DyPl atm by an order of magnitude. The activation volumes for high-pressure diffusion are in favorable agreement with theoretical models developed for self-diffusion. coefficient which determines the rate at which material is transferred from the matrix phase to the precipitate and hence determines the growth rate of the precipitate. Since the numerical values of the diffusion coefficients differ widely as a function of the metallic system, temperature, and pressure, the diffusion coefficients must be determined for each particular environmental condition. Of long-standing interest is the growth of the classic Widmanstatten pattern in metallic (Fe-Ni) meteorites. The growth rate of the pattern is controlled by the diffusion coefficients in the Fe-Ni system. Since these coefficients are essential to calculating the growth rate of the pattern, we found it necessary to determine the diffusion coefficients

Jan 1, 1965

By John R. Low

A number of cases of low-temperature, intergranu2ar brittle fracture of metals containing small amounts of certain impurities, have now been identified. Some degree of understanding of this phenomenon exists for the simpler binary systems of a metal and a single impurity, but the profound effects of other impurities and alloying elements in modifying this type of behavior remain unexplained. Current research in this area is reviewed and some of the newer techniques of investigation which should make possible a more quantitative study of the structure and composition of grain boundaries in impure metals are described. To indicate the subject matter of this lecture, we may begin by reviewing the experimental observations concerning low-temperature intergranular brittleness in impure metals, particularly those examples in which the embrittlement appears to result from what has been called "equilibrium grain boundary segregation."' These are the systems in which it has been impossible, at least up to now, to detect the presence of any second phase film at the brittle interfaces. When second phase films are present they are usually readily detectable by fractographic methods, often appearing as epitaxial films in geometric or dendritic patterns. An example is shown in Fig. 1 for the case grain boundary carbides in a sensitized stainless steel which failed by intergranular brittle fracture at 78?k2 In contrast to this type of embrittlement there are numerous examples of low-temperature intergranular embrittlement in which the fractographs are essentially featureless, for example, that of an oxygen-embrittled iron shown in Fig. 2. The only second phase particles visible are the small, widely separated, round oxide particles typical of the bulk material. The fracture surface is extremely smooth and the fracture path appears to follow the intergranular interface without deviation. This type of fractograph also implies that crack propagation has occurred without plastic deformation at the crack tip, since localized slip or twinning ahead of the crack would be expected to distort the interface and be readily visible in the fractograph. Such indications are occasionally seen in these fractographs, but are not characteristic. A second example of this type of fractograph is shown in Fig. 3, which is from a temper-embrittled, carbon-free, Fe-Cr-Ni alloy containing Sb, broken at 1OO?C.3 The similarity to the oxygen embrittled iron case will be apparent. In the case of the temper embrittled Cr-Ni ferrite containing antimony, it is possible to remove the embrittlement by suitable thermal treatment. The grain boundaries may then be examined by thin film transmission in the electron microscope for the material in both the nonembrittled condition and in the embrittled condition. Two boundaries are shown in dark-field transmission in Fig. 4, one in the nonembrittled

Jan 1, 1970

By G. F. Jenkins

ASBESTOS is a general term embracing the fibrous varieties of a number of minerals. Of these, the hydrous magnesium silicate, chrysotile (H4Mg3Si209), a variety of serpentine, is the most abundant and useful to industry. All other types of asbestos belong to the amphibole group of minerals and are classified as: crocidolite, NaFe(SiO3), FeSiO3; anthophyllite, (MgFe)SiO3; amosite, also a ferromagnesium silicate but with iron content higher than that of anthophyllite; tremolite, CaMg3(SiO3)4; and, actinolite, Ca (MgFe)3(SiO3)4. PROPERTIES The commercial value of asbestos depends largely on the physical property that permits it to be readily separated into fine filaments of high tensile strength and flexibility, which, coupled with the fact that it has the quality of incombustibility of a mineral-in distinction to vegetable and animal fibers-makes it of unique usefulness for many purposes. To some extent, the value depends upon the length of the fiber, although extreme length is neither necessary nor desirable for most purposes. Chrysotile occurs as cross-fiber veins, in which the asbestos fibers are approximately' at right angles to the vein walls, with vein width- or fiber length-seldom exceeding 2 or 3 in.; also as slip-fiber, in which the fibers 'lie in the same plane as the vein or on slippage planes. A cleanly broken vein of cross-fiber has a pearly luster and may range from a deep green or brown color to light shades of yellowish green or cream. When of good quality, the fiber filaments forming the vein may be easily drawn away from their neighbors and exhibit a fine silkiness and pure white color. They may be twisted into a thread and when flexed between thumb and fingers are found to be strong and pliable. Chrysotile withstands comparatively high temperatures without breaking down completely or fusing but begins to lose water of crystalliza-

Jan 1, 1949

By W. D. Kruger

Methods for analyzing flooding or cycling projects by means of two-dimensional flow calculations are presented in the literature. The use of these methods allows the determination of optimum operating conditions for such projects and provides information on pattern efficiencies, relative flow rates, pressure distributions and floodout histories. The accuracy of such analyses depends on the basic reservoir data employed, especially the absolute permeability distribution in the reservoir; however, absolute permeability data normally are determined from well flow tests and/or core measurements and are so limited in quantity and quality that they do not adequately describe the reservoir flow properties. A calculation procedure is presented for determining the areal permeability distribution in the reservoir. Use of the procedure allows verification of the basic reservoir data through the matching of past reservoir conditions, thereby providing proper data for reliable predictions of future operations. The calculation procedure is a numerical technique based on a mathematical model of the reservoir and is designed for solution by means of an electronic digital computer. Results from field application of this procedure are presented. Permeability distributions from measured data are compared to those calculated to indicate the need for the analysis. Comparisons of field-measured and calculated pressure distributions are given to establish the validity of the calculation procedure. The conclusions of this paper are (I) use of the calculation provides data that allow a match of past reservoir conditions and thus reliable prediction of future operations; and (2) the procedure should, where applicable, be used to provide adequate reservoir data for use in two-dimensional flow calculations and related reservoir analyses. INTRODUCTION One means of providing more precise engineering control over reservoir operations during all stages of depletion is to develop some type of model to simulate the reservoir, using information developed from the behavior of the prototype to predict the performance of the actual reservoir. The use of mathematical rather than physical models for this purpose has been gaining in importance recently because of the application and availability of electronic computers. Mathematical models avoid instrumentation difficulties and allow easier handling of large-scale problems. At present, analyses employing two-dimensional models are common, and thought is being given to the use of models in three dimensions. The use of multi-dimensional models is necessary to show not only what is occurring in the reservoir, but also where in the reservoir the phenomena of interest are taking place. Methods for analyzing flooding or cycling projects by means of two-dimensional numerical models are presented in the literature. The use of these methods allows the determination of optimum operating conditions for such projects and provides information on pattern efficiencies, relative flow rates, pressure distributions and floodout histories. The applicability of numerical models and the results of using such analyses have been presented through field examples. The references indicated here discuss fully the data necessary to build the mathematical reservoir model and the way the model is used to study or predict the future performance of the reservoir. The accuracy of the analysis of such projects depends on the basic reservoir data employed in the construction of. the model. In order to be sure the model represents the reservoir, it must be used to match some known set of reservoir conditions, i.e., to match past reservoir performance. The accuracy of the model is directly dependent upon the absolute permeability distribution in the reservoir; however, absolute permeability data are normally determined from well flow tests and/or core measurements, and are so limited in quantity and quality that they do not adequately describe the reservoir flow properties. There is always the need for better data and for verification of existing data. The purpose of this paper is to show the use of the mathematical model to match past performance in flooding or cycling projects, the use of numerical techniques to adjust the basic absolute permeability data if necessary so that a match is obtained, and in this way to generate the effective areal permeability distribution of the reservoir. A review of the basic concepts of the numerical model will be given, followed by a discussion of the data-adjusting technique for matching past performance. TWO field examples will be cited to show

By R. E. Lund

Josephtown Smelter employs the St. Joe-developed electrothermic process for producing zinc metal and zinc oxide. The process uses resistance-type electric furnaces. Flow of current through the sintered ore and coke charge develops the energy required for smelting at the reaction sites. To produce zinc metal, the furnace off-Gases bubble through a large "U"-tube filled with molten zinc which condenses the zinc to liquid; the metal is then mechanically cast into slabs. To produce zinc oxide, the furnace vapors burn in air and the resultant powders are collected. The smelter comprises three distinct circuits. One circuit produces American Process zinc oxide and high grade metal; another circuit produces tailor-made alloys of controlled lead and cadmium content; the third circuit produces prime western zinc metal and feedstock which is refined into special High grade metal and French Process zinc oxide. The roasting circuit utilizes multiple-hearth furnaces for deleading the zinc concentrates; fluid bed and suspension roasters are employed for desulfurization. Sintering produces a hard, porous furnace feed. The flexible smelting process is adaptable to consuming various kinds of secondary material. Extensive residue treatment accomplishes high overall zinc recovery. Smelter by-products include sulfuric acid, cadmium, and mercury.

Jan 1, 1970

By M. J. Bradley, P. H. Dike

THE art of melting nonferrous metals, in smelting, casting, and in compounding of alloys, is highly dependent on a knowledge of the temperature of the metal. This knowledge may reside in the experience and judgment of the melter, or it may be based on measurement by suitable instruments. It-is our purpose to discuss briefly the instruments available for such measurements, and more at length the present, practice in molten metals, without recommendation. In the limits of time and space allotted, we can do little more than mention the available methods of measurement that are directly applicable in this field. In the 1939 edition of the Metals Handbook, issued by the American Society for Metals, pages 285-310, there is a more extensive discussion of pyrometry than can be attempted here, which should be referred to for details we must omit. For reasons that will appear, thermoelectric pyrometry will constitute the major portion of our discussion of the subject, only limited attention being given to radiation or optical pyrometry. METHODS OF MEASUREMENT THERMOELECTRIC PYROMETRY A thermocouple consists of two dissimilar wires, or a wire inside a tube of a dissimilar material, joined together at one end, which is placed in the region or medium where the temperature is to be measured, while the other ends are connected through suitable lead wires to a voltage-measuring device, which may be a millivoltmeter or a potentiometer. An electromotive force is generated in the circuit, which is proportional to the difference in temperature between the hot junction and the junctions of the lead wires to the measuring instrument. If this latter temperature is maintained constant, the e.m.f. measured varies only with the temperature of the hot junction. Every thermoelectric pyrometer is calibrated for a particular cold-junction temperature such as 0°F., 32°F. or 75°F., but usually it is more practical to compensate instrumentally over the probable range of cold-junction temperatures than to maintain the junction at the particular temperature for which the instrument was calibrated. Thermocouple Materials Only a very few pairs of metals are in frequent use for pyrometric measurements. The most generally used are iron-constantan for temperatures up to 1500°F. in oxidizing and up to 1800°F. in reducing atmospheres and chromel-alumel, which may be used in oxidizing atmospheres at temperatures up to 2400°F. for intermittent service. The accuracy of the latter deteriorates rapidly at temperatures above 2200°F. Platinum vs. platinum-rhodium thermocouples may be used up to a temperature of 3000°F , but they are easily contaminated by slow absorption of

Jan 1, 1946

By E. C. Bohlen, H. l. Burghoff

THE work reported in this paper was carried out to supplement the existing information concerning directional properties and recrystallization textures of annealed brass sheet and strip. These characteristics are of direct interest when the forming and drawing properties of such material are being considered. Among those who have made contributions in this field are Bass and Glocker;1 Bauer, Göler and Sachs;2 Phillips and Samans;3 Pratt;4 Price;5 Cook;6 Richards;7 Brick;8 and Brick and Williamson.9 These investigators have found, in general, that in brass strip that shows directional variations in properties, tensile strength has a minimum value and elongation has a maximum value at 45° to the rolling direction. The most pronounced directional properties have been found in material given the greatest reductions in rolling followed by high annealing temperatures. Recrystallization texture of brass has been variously reported as (113)[112], (001)[100], and a combination of (110)[115] and traces of the primary rolling texture, (110)[112]. The directional studies have been very informative, but actual tests appear to have been confined to material in its final condition. Tests at intermediate stages have received little attention although previous history of some materials has been partly considered. Perhaps the most comprehensive investigation was made by Cook,6 who studied the directional properties of 70-30 brass strip for which the final and penultimate, or next to the last, anneals and the final reductions were varied. He found that, for any given combination of penultimate anneal and final reduction, the tendency toward the development of directional properties was reduced as the temperature of the final anneal was decreased. In addition to drawing cups and making tensile tests of the finished material at various angles to the rolling direction, he measured the frequency and the angles of twins in grains for several specimens. Plots of his twin counts showed directionality for the materials that produced eared cups. TEST MATERIALS AND EQUIPMENT For this investigation, one commercial heat of 68-32 brass was cast in the form of bars for cold-rolling, 13 ½ in. wide and 1 ½ in. thick. The analysis was as follows: 68.83 per cent copper, 0.04 per cent lead, 0.01 per cent iron, 31.12 per cent zinc (by difference). The bars were so processed to the final thickness, 0.020 in., as to obtain on this thickness all possible combinations of the variables listed below except those involving the sequence of 84 per cent penultimate reduction and 84 per cent final reduction: I. Penultimate reductions of 37 per cent, 50 per cent and 84 per cent; 2. Penultimate anneals at 800°, 900°, 1050° and 1200°F.; 3. Final reductions of 37 per cent, 50 per cent, 69 per cent and 84 per cent;

Jan 1, 1942

By H. G. Doll

THIS paper discusses a method and apparatus for determining the dip of formations traversed by a drill hole, by means of electrical measurements in the hole. The process consists in recording the Spontaneous Potentials present along three oriented generatrices in the hole. By comparison of the three curves thus obtained, after application of a correction factor to compensate for any deviations of the hole, the dip angle and the dip direction are determined. Excellent accuracy is obtained for dip angles over 10°. Because the method is simple and the apparatus rugged, the measurements are rapid and reliable; consequently, they can be made at all the levels that are of interest at any time after the well has been drilled. Mechanical cores are not needed to evaluate the dips. A convenient, timesaving procedure is to perform the dipmeter survey at the time the electrical log is taken, using for both operations the same cable and truck. Actual examples of results obtained in wells of the Gulf Coast area are given.

Jan 1, 1944

By C. S. Barrett

THE crystal imperfections known as faults in stacking (stacking disorder) are of importance to both fundamental and applied science and are receiving increasing attention. On the theoretical side there have been recent advances in the analysis of diffraction patterns in terms of stacking faults, and on the experimental side it has been found that certain metals develop a faulted structure on cooling through a phase transformation. Beyond this, little is known of what may be called the physical and mechanical metallurgy of faulting, although there has been no lack of discussion and conjecture as to the presence of faults in metals and the effect of faults on mechanical properties and microstructures. In the close-packed metals the nature of faults can be described very simply. Face-centered cubic (FCC) crystals consist of close-packed layers of atoms, (111) planes, stacked above each other in a definite manner. If one layer is designated as the A layer, the next must be a B or a C layer; that is, every atom of the second layer lies not above the atoms of the A layer, but nestles in the hollows between these, using the hollows designated as the B positions, or the equivalent hollows designated as C. If the sequence of layers is ABCABC...., so that layers three spacings apart are directly over each other, the crystal is FCC; if CBACBA ... it is an FCC crystal that is a twin of the former; if ABAB........or BCBC..it is hexagonal close-packed (HCP). A fault is a break in the sequence, such as ABCABABC .. . which has the effect of inserting an HCP lamella into an FCC crystal. Regularly spaced faults spaced two layers apart would convert an FCC crystal entirely to HCP, or an HCP to FCC. A fault in an FCC crystal is also equivalent to creating an FCC twin of minimum thickness; in fact, the entire crystal would be converted to its twin if faults were introduced regularly. (In HCP crystals, however, twinning does not occur on the basal plane and a fault on this plane is not identical with a thin twin). Faults are one of the possible causes for annealing twins,' for the strain markings that are brought out by etching deformed metal,'," for the altered X ray reflecting power of metal at slip bands that is revealed in X ray reflection micrographs,' for the extinction of Kikuchi lines in electron diffraction patterns, and for the hardening of latent slip planes.' Since other explanations of these effects are also available," there has been no direct proof of faults from deformation; yet it has appeared likely that they would occur. Faults resulting from phase transformations in metals, however, have been clearly revealed by diffraction in cobalt" and lithium. It is to be expected that the faulting tendency is greatest

Jan 1, 1951

By J. Brett, S. Friedman

A study of the diffusion of nickel into both fibrous and recrystallized 0.065-in.-diam silica-alumina doped tungsten wire at 1200°C has been conducted. The diffusion profiles were determined by chemical dissolulion of successive circumferential layers and spectro-photometric determination of nickel in the etchant. It was shown that the diffusion of nickel into tungsten is markedly structure-sensitive. No significant amount of nickel could be introduced at 1200°C into tungsten which had first been recrystallized at temperatures of 2300°C, leading to an upper limit estimate for the bulk diffusivity of nickel in tungsten of 10-11 sq cm per sec at 1200°C. However, nickel did diffuse into initially fibrous wires, caused re crystallization, and was alsays present at the advancing recrystallization front. The accumulation of nickel in an initially fibrous region ceases when the recrystallization front arrives. The characteristics of the resulting diffusion profiles are explained in terms of the relation between diffusion processes and micro structural changes. WHILE it is well-known that the presence of nickel and certain other metals causes low-temperature recrystallization of the cold-worked fibrous structure of doped tungsten,''' the character of the phenomenon is not well understood. Recently it was shown that the recrystallization reaction can be induced at low temperatures by the presence of solid nickel on the surface of doped wire, but not by exposure to nickel vapors.3 Once recrystallization was initiated, a continued source of nickel was required for propagation of the recrystallization front. The phenomenon appeared to be a complicated solid-state reaction since, in addition to the change in structure of the tungsten from fibrous to equiaxed grains, diffusion of nickel from the surface into the recrystallized and fibrous structures was occurring with possible chemical reaction between nickel and tungsten at the surface and interaction of nickel with the dopants which ordinarily stabilize the fibrous structure within the wire. The objective of the present work was to study the diffusion of nickel into fibrous and recrystallized tungsten structures in order to clarify the relationship of the diffusion process to nickel-induced recrystallization. Studies of interdiffusion in the Ni-W system4"7 have been principally concerned with the mobility of tungsten in nickel. Information on diffusion of nickel in tungsten is meager, and there seem to be no studies of the mobility of nickel in tungsten which elucidate the structural aspects of the phenomenon. The present experiments were designed to determine the diffusivity of nickel at 1200°C in fibrous tungsten, in large-grained tungsten prerecrystallized at high tem- perature, and in tungsten recrystallized at 1200°C due to the presence of nickel. Although the concentration profiles were determined in these experiments, unexpected changes in boundary conditions or complex diffusion paths complicated the analysis of these profiles so that the interpretation could not be readily expressed in terms of simple diffusivities. EXPERIMENTAL PROCEDURE The experiments were conducted on Sylvania 0.065-in.-diam silica-alumina doped commercial tungsten wire, hereafter designated as ordinary doped wire. A special lot of 0.065-in.-diam silica-alumina doped low-nickel wire was also used. Impurity analyses of the wire are given in Table I. The experimental design is shown in Fig. 1. All heat treatments were conducted in vacuum. Two groups of ordinary doped wire were prepared for diffusion with nickel. One group in the as-received (fibrous) condition was elec-tropolished, nickel-plated, and annealed at 1200°C for 20 and 40 hr, or was exposed to nickel vapor at 1200°C for 20 and 40 hr. The second group was recrystallized to an equiaxed grain structure at 2300°C for 3 hr, electropolished, nickel-plated, or exposed to nickel vapor for anneals at 1200°C for 20 and 40 hr.

Jan 1, 1969

By Rodolfo V. de la Cruz

The in situ deformability of rock masses is determined by relating the applied load to the radial displacements of points on the borehole wall that are outside of the loaded surfaces. The external displacement method includes the steps in which: a) radial displacement sensors are installed to measure the change in length of a diameter of a borehole; b) unidirectional self- equilibrating pair of forces perpendicular to the direction of radial displacement measurements are applied on opposite sectors of the borehole wall, and; c) using elastic theory, the in-situ deformability of the rock mass can be related with the applied loads and measured radial displacements. The displacements outside the loaded surfaces are comparatively smaller in magnitude than displacements inside the loaded surfaces. These displacements, however, are sufficiently large and can be measured precisely by commercially available linear displacement sensors. Loads are applied by a conventional borehole jack. Existing methods for measuring the in situ deformability of rock masses yields unreliable results due to complex boundary stresses, small and varying contact areas, and the existence of fractures. It was shown that in the external displacement method, the effect of boundary pressure distribution and contact area are negligible. Also, since the displacements measured in the external displacement method were due to materials that are deeper inside the rock mass, borehole fractures have less influence on the calculated deformation modulus.

Jan 1, 1982

By R. G. Green, R. L. Dowdell

LEAD POISONING as a result of eating lead pellets deposited in marsh areas is a cause of high mortality among ducks, geese, and other waterfowl ingested lead shot become trapped in the gizzard with gravel and are slowly ground away by the grit. Absorption of lead as it passes through the intestine in a finely divided state produces severe lead poisoning which is usually fatal. Ducks and geese with lead poisoning develop first a typical green diarrhea. Later, paralysis of the wing muscles prevents flight. As the poisoning continues with further grinding of the shot trapped in the gizzard, increasing paralysis reduces the bird to helpless-

Jan 1, 1937