By N. E. Idenyi

The effects of compositions and firing temperatures on the physico-mechanical properties of blended Nsu fireclay and Nkalaha redbrick clay have been investigated. The clay samples were compounded according to the following ratios: 10:90, 20:80, 30:70, 40:60 50:50, 60:40, 70:30, 80:20 and 90:10 in the order Nsu: Nkalaha respectively, and test samples made and fired at 9000C, 10000C 11000C and 12000C. The properties tested for were the modulus of rupture, porosity, shrinkage, apparent density, water absorption and bulk density. From the results obtained, it is inferred that the blends have a maximum service temperature of 11000C, with the 30: 70 blend presenting the best characteristics. A conclusion is drawn to the effect that the blend could be adapted for the production of ceramic earthenware, electrical porcelain pin insulators, cement manufacture and for refractory linings where temperature requirements are less severe.

Jan 1, 2006

By Qingyun Huang, Junyi Xiang, Xuewei Lv, Chenguang Bai

The extraction of vanadium from mechanically activated converter slag was studied in dilute sulfuric acid solution. The effects of roasting and leaching parameters were investigated. The results show that Ca/V mole ratio, roasting temperature, leaching temperature, liquid-solid ratio, and particle size all have significant effects on vanadium leaching efficiency from calcification-roasted converter slag.

Mar 1, 2017

By E. G. Noble

The potential for using heterotrophic microorganisms to solubilize manganese from low-grade domestic ores is being assessed at the Reno Research. center, U.S. Bureau of Mines. More than 90 pct of the manganese has been extracted from a variety of oxide ores in shake-flask tests using molasses as a source of .. nutrients for the microorganisms. It has also been demonstrated that high recoveries of manganese can be obtained from a domestic wad ore using column bioleaching. 'l'he isolation and identification of organisms responsible for manganese extraction is discussed, as are the mechanisms responsible for manganese solubilization.

Jan 1, 1991

By Luciano R. G. Santos

Keywords: biosorption, cadmium, copper, biomass, spent zeolite. The majority of the industrial activities produce some kind of solid wastes. In this work two industrial residues (spent zeolite and wood sawdust) were chemically modified to increase their heavy metals sorption capacities. Manilkara longifolia (a Brazilian plant known as parajú) sawdust was first treated with NaOH and modified with different citric acid concentrations (0.6-1.2 mol/L) at 120°C, for 90 min. Infrared spectroscopy confirmed the presence of carboxylate groups in the wood structure as result of their mixing. Similarly, spent zeolites were also submitted to a chemical treatment (NaOH) to remove carbon deposited during oil cracking and to recover its sorption capacity. Batch experiments carried out at ambient temperature showed that both materials present sorption capacity for copper and cadmium comparable to weak acid ion exchange resins. A maximum of 78 mg-Cd/g and 59.7 mg-Cu/g as well as 29.9 mg-Cd/g and 14.6 mg-Cu/g were observed for the sawdust and the zeolite, respectively. The results were modeled according to the Freundlich and Langmuir equilibrium isotherms and compared with results of other studies.

Jan 1, 2005

By Luciano B. Oliveira, Angela O. Costa, Sergio N. Monteiro, Luis Guilherme C. Marques

"Biofuels are gaining a relevant role in today’s world not only as a solution for the decreasing petroleum reserves but mainly as a positive contribution to the efforts in global warming mitigation. In Brazil, since 1975, the replacement of gasoline by ethanol started a so-called PROALCHOOOL program, which is now being complemented with the replacement of petroleum diesel by biodiesel. This biodiesel program was officially created in 2005 with mandatory goals, supported by legislation, of 2% addition in 2008 and 5% addition in 2013 into all commercialized regular diesel. In this work, a critical analysis of the Brazilian biodiesel program is presented. The technical aspects related to the different raw materials, including wastes, available for biodiesel conversion as well as the economical conditions associated with production costs and market logistic are discussed. The environmental benefits associated with the retention of greenhouse gases are also discussed.IntroductionToday the commonly accepted fact that the petroleum world reserves are probably passing through a maximum and start declining in terms of the total amount that can be extracted by existing technologies is motivating significant changes in our society. The continuous increase in the price of gasoline and other liquid fuels is an immediate worrisome and visible consequence. However, more than an economical problem, our civilization is already facing the effects of global warming, due to CO2 emission from burning fossil fuels, mainly from coal and petroleum. It is now realized that a large scale solution for these problems demands the prompt substitution of non-renewable fossil fuels by others that, in addition of being renewable, have a relatively lower contribution to the greenhouse gases."

Jan 1, 2008

By J. K. Brimacombe

Since the Peirce-Smith converter was introduced to the non-ferrous industry in the early part of this century, there has been a paucity of research on process-engineering aspects of the reactor such as gas injection. This paper reviews studies conducted at UBC over the last decade on gas discharge dynamics, high-pressure injection, bath slopping, oxygen/bath reaction kinetics and out-of-stack heat transfer within the converter. The ultimate objectives of this work have been to extend refractory life and to increase converter productivity.

Jan 1, 1985

By Jyothi Rajesh Kumar, Jin-Young Lee

21st century is electronic revolution in human lives as well as energy is one of the most significant tasks. Rare earth elements (REEs) occupy a key role in daily life as well as high-tech industrial applications. REEs are one of the energy critical elements; for sustainable growth, it depends on multiple extraction and separation technologies including solvent extraction and ionic liquid-based extraction methods.

Mar 1, 2017

By C. S. Ek

As a continuation of previous work, further tests have been carried out to recover silver from the residues obtained in a zinc jarosite process. Selective flotation has been performed with different reagents, and ?cleaning steps have been introduced to upgrade the silver concentrate. Leaching of crude residues, as well as flotation tailings, has been carried out with cyanide and thiourea. Finally, the different beneficiation methods are compared, and the industrial aspects? of their application are reviewed.

Jan 1, 1990

By He De-wen

The municipal solid waste is a by-product of the daily life of urban residents. The quantity and ingredients of municipal solid waste has exceeded the current management and disposal ability, which has done a great harm to municipal environment and sanitation quality and threatened people?s health. On the basic of analysis on the amounts and main elements of municipal solid waste of Changsha City, the sanitation landfill, incineration, composting, reclamation and utilization technology of household waste were compared specifically in this paper. Based on the concrete conditions of Changsha City, the paper has proposed a disposal proposal combined with reclamation and landfill of municipal solid waste of Changsha City, and the environmental benefit, social benefit and economical benefit of the prepared processing routes were also analyzed in the paper.

Jan 1, 2009

By Li Zhang

Air was blown into the molten slag as oxygen resource during the dynamic oxidation. It was found that the oxidation is not only in favour of Ti components into perovskite phase, but also the increase of slag temperature and decrease of slag viscosity during the dynamic oxidation promote the precipitation and growth of perovskite phase, average crystal size of perovskite phase is 48 µm. The experimental result realizes the selective enrichment of Ti components and coarsening of perovskite phase, perovskite phase can be separated by mineral dressing method.

Jan 1, 2009

By Jing-she Li, Hai-yan Tang, Cheng-song Liu, Wei Liu

"In order to effectively utilize cheap and low quality iron ores, a hematite ore in a certain steel plant in Xinjiang was researched on to obtain ""iron increase and silicon reduction"" by ore dressing operation experiment and the performance indexes of the hematite ore were optimized. Based on the fundamental characteristics and high-temperature properties of the concentrate after ore dressing and other five kinds of iron ores which were co=only used in this steel plant, ore matching principles were proposed and a sintering ore blending optimization model was established. Finally, sinter pot test was carried out to verify the validity and practicability of the sintering ore blending optimization model which was aimed at giving consideration to the sintering indexes and the cost.IntroductionIn recent years, the price of imported iron ore with high quality is always at a high level, while iron ore self-sufficient rate in China is less than 50%. Enormous market demand and high dependence of domestic enterprises on imported iron ore makes the price of it hardly return to rational. In order to get rid of the situation of long-term meager profit and even deficit, more and more iron and steel enterprises in China transit their focus of reducing production cost to the utilization and development of relatively cheap but low-grade iron ore resources at home[l-4l_ However, besides the disadvantages of low iron grade, high content of impurities and complex embedded properties, the high-temperature properties of iron ore often go beyond the suitable ranges for producing sinter with high quality. Thus directly utilization of this kind of iron ore without ore dressing process would probably affect the metallurgical performance and indexes of sinter ore.Previous research and production practice have shown that traditional iron ore matching in sintering mainly focus on the reasonable collocation of properties of iron ores with low quality and high quality, but pay less attention to ore dressing process of low quality iron ores and matching them with high quality iron ores. Actually, compare with directly utilization, iron ores with low quality after ore dressing have higher suitability for matching with high quality ones which is beneficial to reduce the consumption of iron ores with high quality and control the production cost of sintering [5-s1."

Jan 1, 2014

By Muammer Kaya

The purpose of this review is to raise awareness about e-waste problem in the World. Whether generated at our home or our office, e-waste is most rapidly growing waste problem in the world. Even though there are conventional disposal methods (such as landfill and incineration) for e-waste, these methods have both economic and environmental disadvantages; recycling is a new waste management option which diverts end-of-life (EOL) electrical and electronic equipment (EEE) from landfill and incineration [1, 2]. Successful diversion strategy must be based on economic sustainability, technical feasibility and social support [3]. Recycling infrastructure includes transportation, collection, recovery and resale establishments. The first part of this paper describes the e-waste facts, how big is the e-waste problem and existing recycling programmes and collecting methods in the USA and EU; second part, describes various methods available to recover valuable materials (glass, plastic and metals (Pb, Cu, Al, Steel, Ni, Au, Pd, Cu etc)) in e-waste for a safe and environmental friendly disposal

Jan 1, 2009

By Xiaowen Liu

The thermal decomposition of diaspore was investigated by thermogravimetry (TG),differential scanning calorimetry (DSC), X-ray power diffraction(XRD),infrared (IR)spectrain this paper. The thermal decomposition mechanism of diaspore was discussed according to Coat-Redfer equation. It was found that the decomposition of diaspore was carried out at 500?,and the peak temperature was 530?. The electrovalent balance of diaspore was destroyed. The previous crystal structure was changed. a- Al2O3 was obtained after thermal decomposition. The activation energy is 287KJ/mol.

Jan 1, 2006

By J. Y. Hwang

The relationship between coal characterization and physical cleaning has not been well understood due to the complex nature of coal. Therefore, it is difficult to apply the results of coal characterization to predict and evaluate the performance of a physical separation (e.g. flotation). Eight U.S. bituminous coals were analyzed and studied petrographically in conjunction with washability and flotation tests. The results show that grindability correlates to ash and fixed carbon contents; liberation determined directly by petrographic techniques is close to liberation determined indirectly by washability; and an ideal separation efficiency can be determined by measuring the inertinite content and the washability separation efficiency using a heavy liquid with a density of 1.4. The ideal separation efficiency was attained for most coals by packed column flotation. The ideal separation efficiency can be used for comparing process technologies and process parameters.

Jan 1, 1988

By S. Yin, A. Bogno, H. Henein, P. Natzke

Impulse Atomization (IA) (a single fluid atomization technique) was used to rapidly solidify Al- 4.5wt%Cu and Al-4.5wt%Cu-0.4wt%Sc under argon atmosphere. In addition to the IA-generated droplets, the same technique was used to produce strips by Spray Deposition (SD) of the same alloys on a copper substrate with and without oil coating. The rapid solidification microstructures were analyzed using Scanning Electron Microscopy (SEM). From the SEM images, the amount of eutectic and the secondary dendrite arm spacing (SDAS) were measured. These SDAS results lead to the estimation of cooling rate. The eutectic fraction coupled with the metastable extension of the solidus and liquidus lines of Al-Cu (Sc) phase diagram lead to the estimation of primary and eutectic undercoolings. A comparison of the solidification path of the droplets and the strips was done as well as the analysis of the effects of scandium.

Jan 1, 2015

By Yunnen Chen

This work concerns the removal of zinc(II) and COD by means of sawdust obtained as a by-product from locally used wood. The zinc(II) and COD removal study has been carried out batchwise where the influence of physico-chemical key parameters such as tree species, pH value of solution, temperature and contacting time and dosage of adsorbent have been considered. The maximum percent removal was attained at pH 9 all for Zn(II) and COD after about 60 min. The adsorbent can be effectively desorption using 0.1 M HCl. The experimental results showed that ion exchange maybe the major adsorption mechanisms for binding the divalent metal ions to the sawdust. Sawdust was a potential adsorbent for the removal of Zn(II) from the effluent of electroplating industry.

Jan 1, 2009

By Xiang-dong XING, Zhen-yang wang, Xing-le LIU, Jian-Liang Zhang

Experiments were carried out by adding CaF2 as catalyst in a Ar atmosphere to study the isothermal reduction kinetics of vanadium titano-magnetite carbon composite pellets under high temperature in the range from1473 to 1673K. By analyzing reduction mechanism, it was found that the rate controlling step was gas diffusion, and the activation energy was 178.39kJ•mol-1 without adding any catalysts. Adding CaF2 of 3% to vanadium titano-magnetite carbon composite pellets can decrease the apparent activation energy of reduction, and the decrease extent was 14.95kJ•mol-1. In addition, temperature is an important factor influencing on reaction rate.

Jan 1, 2015

By Giacobbe Braccio, Alessandro Blasi, Assunta Romanelli, Massimo Morgana, Corradino Sposato

The solvent extraction technique is the only industrial way used to separate and purificate yttrium from other rare earths. In order to improve this process several extractants have been tested during last years. In this work, the behavior of sec-octylphenoxy acetic acid (CA-12) in Yttrium recovery from high concentrated heavy rare earth mixture was investigated. Sodium hydroxide solution was used in order to presaponify organic phase composed by CA-12 and Tributyl phosphate (TBP) diluted in kerosene. In the investigated condition, TBP confirmed its role of phase modifier not significantly altering the extraction behavior of CA-12. The CA-12-TBP system showed a high affinity in extraction for lighter rare earths such as Sm, Eu, and Gd, leaving yttrium in aqueous phase. Using a feed concentration (P [RE]) of 1 M, organic mixture is capable to extract around the 70% of metals in a single extraction test showing this extraction sequence Y < Lu < Yb < Tm < Er < Ho < Dy < Tb < Gd < Eu < Sm. Moreover for [CA-12] = 1.79 M and [RE] = 2 M the instability of extraction system occurs.

Mar 1, 2017

By David Arana

The use of gas-water dispersion of a molten material flow onto a vibrating surface is developed as a process to minimize water pumping requirements, minimize the risks of explosions, and minimize the post solidification dewatering and fines handling equipment requirements. The process uses existing vibration transport technologies and common plant utilities. Plant trials using the smaller footprint and the progressive molten particle cooling time have yielded encouraging results. The results are analyzed and reported.

Jan 1, 2006

By Pengfu Tan

In order to understand and control the formation of dioxins and furans in iron ore sinter plants and to possibly avoid expensive end-of-pipe removal stages, thermodynamic calculations on the stability of PCDD/Fs have been combined with sinter process modeling by means of kinetic simulations and computational fluid dynamics. Three thermodynamic databases of PCDD/Fs, derived using the Group Additivity approach and two computational molecular modeling methods, MNDO and PM3, respectively, combined with the SGTE database have been used to model the PCDDIF formation and the PCDD/F isomer distributions in iron ore sintering. The results show very similar conditions for the PCDD/F formation using the different databases. Concerning the isomer distributions of toxic PCDD/Fs, the calculated data derived from the MNDO method showed optimum agreement with measured values from industrial furnaces. The thermodynamic calculations also proved that the isomer distributions found in combustion processes are equilibrium values, while the concentration ratio of PCDDs and PCDFs in the wind boxes does not represent an equilibrium state. A CFD model of iron ore sintering was developed including the kinetics of 15 relevant chemical reactions with the aim of describing the temperature fields and the gas flow patterns in the sintering bed. On the basis of these information and experimental observations reported in the literature possible pathways for the PCDD/F formation in sinter plants have been identified: PCDD/Fs are formed in the critical temperature region of 250 to 450 °C below the combustion zone, are then carried downwards with the gas and condensed close to the bottom of the sinter bed. Transported to the discharge end with the solid mixture, they are again released into the gas phase when the flame front approaches the bottom. PCDD/Fs are also formed in the last wind boxes when the hot off-gases cool down and reach the critical temperature range. Consequently, methods to reduce the dioxin formation reactions are proposed including inhibitor addition to the sinter feed and off-gas quenching.

Jan 1, 2003