By Haotian Xue

A new process to extracted antimony directly from stibnite concentrate by reductive sulfur-fixation smelting in sodium molten salt has been presented. The influences of sodium salt content and composition, ferric oxide addition, temperature and time was investigated, respectively. The optimum conditions was determined as follows: W????: ??concentrate=40%, W??alt: ????concentrate =88.75%, WFe2O3 :Wconcentrate =55.13%, W??aCl: ????alt=40%, 1123K, 1h. Under above-mentioned optimum conditions, the average direct recovery ratio of antimony can reach 91.48%, and the main chemical composition of obtained crude antimony is Sb 94.31%, Fe 4.436%, Pb 0.502%, Au 0.0236%. In comparison to traditional antimony pyrometallurgical process, the smelting temperature of present process is reduced from 1423~1473K to 1123~1173K. During the smelting operation, SO2 emision can be avoided completely due to sulfur-fixation as FeS. Furthermore , S0 can be obtained when the molten slag is handled by water leaching with conditions of 323K, L/S=5/1, 2h.

Jan 1, 2014

By Dirk Verhulst

The Altair process employs digestion of ilmenite ore in concentrated hydrochloric acid, solvent extraction to concentrate Ti in a purified stream and spray hydrolysis to produce a TiO2 hydrate, followed by final calcining and milling. HCl gas is regenerated by pressure-swing distillation and reinjected in the leaching solution. All chloride streams are recycled. Chromium compounds generally remain in the residue. Solvent extraction provides flexibility for the removal of naturally occurring radioactive elements (NORMs) present in some ilmenites. The process was previously tested at a 5 t/day feed scale. Recent work at pilot scale (40 liter reactor) led to further improvements. Recovery of Ti in solution is now at least 90% with ilmenite ores, while crystallization at lower temperature lowers the amount of Fe in solution to about 5 g/l and improves solvent extraction, which is now conducted in columns. Higher Ti and lower Fe concentrations in the SX eluate improve the economics. A new formula for pigment production via spray hydrolysis produces a pigmentary base with a narrow particle size distribution.

Jan 1, 2003

By Enrico Cerilli, Bryan Salt

Xstrata Nickel’s Sudbury Smelter has systematically developed its converting aisle from a single stage to a counter current multi stage converting process. This has required the development of two unique converters; the Slag Cleaning Vessel (SCV) and the Slag Make Converter (SMC). This has resulted in a unique three stage converting process that enables treatment of secondary materials and producing a slag that can be discharged without further treatment. The paper will also discuss future changes currently being considered to further improve environmental, plant hygiene and productivity performance.

Jan 1, 2009

By Jamil M. Khalifeh, Shadia J. Ikhmayies, Bothina A. Hamad

"We computed the optical properties of the cubic niobium nitride (o-NbN) compound using the full potential linearized augmented plane wave (FL-LAPW) method within density functional theory (DFT). The complex dielectric function and optical constants, such as optical absorption coefficient, refractive index, extinction coefficient, energy-loss spectrum, and reflectivity, are all calculated and compared with experimental results. The behavior of the computed quantities is similar to that obtained experimentally, but the optical positions are shifted to lower energies. This shift was related to the strong interband transitions, which are located at energies higher than 5 eV for NbN- as they are for IV B transition-metal mononitrides- and they appear in the computed spectra and not in the experimental spectra. These interband transitions simply shift the position of the reflectivity edge or the screened plasma frequency to the longer wavelength side.IntroductionIn recent years, NbN, as a transition metal nitride, has become a very popular material due to its high hardness, melting point, wear resistance, chemical inertness and temperature stability, which makes it suitable for use as emission cathodes in microelectronics and sensors, optical films and micro-mechanics etc [l]. Niobium nitride has long been known as highly polymorphic material, for which several crystalline structures have been reported in the literature [2]. These structures include the well known super-conducting rock-salt (Fm-3m, or Bl) structure (o-NbN), the hexagonal structure with space group p63/mmc and prototype Fe2N (18fuN), the hexagonalstructure with space group p63/mmc and prototype NiAs ~-NbN) and others.There has been a lot of computational studies for the structural and electronic properties ofNbN [3, 4-7], but according to our knowledge there is not any computational work that has been devoted to study the optical properties of this transition metal compound. At the same time a number of authors had performed experimental work in this direction. For example, Xin-kang et. al [l] studied the microstructure and optical properties of magnetron sputtered NbN thin films. Torche et. al [8] studied the composition, structure, electrical and optical properties of nonstoichiometric niobium nitrides. Newport et. al [9] investigated the reflection and transmission spectra of cubic niobium nitride films, and Tanabe et. al [10] had investigated the optical parameters and reflectivity of reactively sputtered NbN thin films by using in situ ellipsometry."

Jan 1, 2013

By D. C. Cupertino

Oxime based solvent extraction provides the user with a selective concentration process for copper prior to electrowinning. The selectivity required is largely for copper(II) over iron(III) and this is achieved by the preferential formation of the square planar copper-oxime complex in the organic phase. The copper/iron selectivity of oximes can however, be altered by modifiers or other types of oximes and may be enhanced in the presence of certain esters. Whilst the oxime based SX processes is important for operations leaching copper from laterite ores, the high selectivity will also be significant in processing streams arising from other leaching regimes which are currently under development, for example leaching of sulfide mineral ores. This paper presents some initial results using Molecular Modelling techniques to further our understanding of the nature of the copper/iron-oxime complexation processes together with some plant studies undertaken at a number of different mine sites investigating selectivity, and other properties, for some modified reagents. Some studies of the interfacial properties of the these systems are reported to explain in part the practical observations.

Jan 1, 1999

By Jian Li, S. Penttilä, P. Liu, W. Zheng, C. Bibby

"The materials selection for Gen IV supercritical water reactor in-core components faces major challenges due to severe operating condition. The current Canadian pressure-tube supercritical water (SCW) concept design requires core outlet temperature of 650 °C at 25 MPa with peak cladding temperature reaching as high as 850 °C. Aside from oilier challenges, there is currently very limited data on candidate stainless steels' corrosion resistance under this operating condition. Austenite stainless steels that include 316L, 304H, AL6XN and 3 l0S that cover a wide range of Cr contents are promising candidates for either direct in core applications or as base coating materials. However, their corrosion resistance has not been tested systematically under this stringent condition. In this study, these types of stainless steels are tested, and their corrosion resistances are compared.IntroductionThe Canadian pressure-tube supercritical water (SCW) concept will operate at a core outlet temperature of 650 °C at a pressure of 25 MPa, with potential peak cladding temperature reaching as high as 850 °C. High-temperature corrosion resistance is one of the key design requirements for fuel cladding components. As summarized by Allen [1 ], most testing to date has been carried out at temperatures below 730 °C. To date, SCW corrosion data above 600 °C is very limited. Even at relatively low temperature exposure to SCW (e.g. 500 °C), F/M steels develop a thick oxide layer rapidly, while some austenitic stainless steels develop thinner surface oxide. Ni based alloys appear to form very thin surface oxide, however pitting was observed in the vicinity of intermetallic precipitates [2-5]. Dissolution of major alloying components from all of these alloys could also pose significant problems for downstream piping [6]. Kaneda et al. [7] suggested some modified stainless steels provide better SCW general corrosion resistance, with no sign of SCC under the slow-strain rate test.Cho [8] suggested that as the Cr content increase, general corrosion resistance improved at 510 °C and 25 MPa. However, similar to Cho's work, most of the SCW corrosion resistance assessments were based on weight change measurement. This can be unreliable due to potential exfoliation of thick oxide film. Besides, there have been no systematic SCW corrosion resistance tests for candidate stainless steels under higher temperatures. SCW corrosion rate increase dramatically for alloys tested at 600 °C [1]. It is also important to understand the role of major alloying elements under this stringent operating condition, not only for fuel cladding components' materials selection, but also for coating materials development."

Jan 1, 2013

By T. Feldmann

Despite the ubiquity of applications for germanium, there is a lack of practically useful solubility data in acidic solutions. Previous studies were done at ambient temperature and only for commonly used acids (H2SO4, HCl). Hence, an investigation of the solubility of GeO2 in different acids was undertaken. Several inorganic and organic acids were studied in the concentration range of 1–11 mol/L and at 23, 40, and 60 °C. In the case of H2SO4 and HCl previous data was confirmed. Lower acidity resulted in a higher solubility for Ge at all tested temperatures. Tests done at 40 and 60 °C and low to moderate acidity levels, gave slightly increased solubility values at higher temperatures compared to 23 °C. This wasn’t the case at higher acidity levels, i.e., the solubility curves at different temperatures converge at high acidity. Lastly, a relationship of water activity and GeO2 solubility in different acid media was established.

By Aichun Dou

Au-Sb alloy sample in which the total amount of Cu and Ni is below 25% (wt. %). In practice, Cu and Ni were difficult to be dissolved in sulphuric acid solution by oxidative leaching under the atmospheric pressure conditions, because of the lower concentration of Cu and Ni in the sample. In this paper, pressure oxidation leaching in sulphuric acid system (POLS) followed by hydrochloric acid leaching (HAL) was employed to remove impurities in the Au-Sb alloy. The effects of variables in POLS on leaching ratios of different metals were investigated in detail. Under the optimal conditions: the concentration of H2SO4 is 1.5 mol/L, liquid-solid ratio is 7:1, the amount of oxidizer is 1.2 times of the theoretical amount, leaching time is 4h and leaching temperature is 427K, the leaching ratios of copper and nickel reached up to 99%, antimony, lead and silver were not dissolved in dilute sulphuric acid solution. The residue from POLS was then treated with hydrochloric acid solution in fixed conditions, the leaching ratio of antimony reached over 92%, the grade of gold in the ultima residue was enriched up to 66%.

Jan 1, 2016

By T. Lezhava

A new reactor model with rotating cathodes has been developed where various forms (dendrite, spongy) of metal depositions and their uninterrupted removal are accomplished by the realization of high current densities and low energy consumption. At the same time in contrast with the existing methods a high quality metal powder may be obtained from concentrated electrolytes without any specific organic or inorganic additives, which allows raising the intensity of the process. The reactor can be used for electrowinning of metals with low adhesive capacity (Pb, Ag, Cu, Zn, Ni, Co, etc.) and the powders. The obtained products may be utilized in general metallurgy as well as in powder metallurgy.

Jan 1, 2006

By G. Haesebroek

In L969 Metallurgie Hoboken-Overpelt started an industrial plant for the separation of iron and zinc from a concentrated CoCL2 solution. Iron and zinc are extracted in column contactors by a solvent containing 12 vol % of tertiary amines in xylene. The extracted metals are stripped from the pregnant organic phase by precipitation with a NaOH solution at pH LL. In this paper an overview is given of the industrial process. In order to overcome some drawbacks of this process (low flash point of the diluent, reagent consumption, batchwise stripping) an alternative solvent extraction process has been examined. In this alternative process, iron and zinc are extracted with an or¬ganic phase containing 50 vol % of TBP in Escaid 110. The pregnant solvent is stripped with water in conventional mixer settlers. Despite the ability of this process to overcome most of the inconveniences due to the use of tertiary amines, it suffers from the poor stability of TBP in concentrated chloride solutions, resulting in unavoidable and inacceptable precipitation phenomena in the stripping section.

Jan 1, 1988

By Thomas Gliick, Jianming Lu, David Dreisinger

"The recovery of manganese from the Boleo project of Baja Mining is via an acid oxidation and acid reduction process in seawater. Manganese as manganese dioxide is leached into solution as manganese sulphate with the addition of sulphur dioxide gas as a reductant and then precipitated as a manganese carbonate. The use of the manganese carbonate intermediate to produce electrolytic manganese metal (EMM) has been extensively studied. The manganese carbonate can be used in place of natural (MnC03) or reduced ores (MnO) of manganese as a feed to the EMM plant. Manganese carbonate can be dissolved in spent electrolyte from manganese plating, followed by purification using ammonium sulphide precipitation of minor elements and then electrowinning in a selenium free process. The results of small cell testing of manganese electrowinning are reported.IntroductionThe Boleo Project of Baja Mining is a greenfields development currently under construction approximately 5 km north of the town of Santa Rosalia, Baja California Sur, Mexico. The Boleo property is held by the Mexican company, Minera y Metalurgica del Boleo S.A. de C. V. (MMB). MMB is owned 70% by Baja Mining Corp. and 30% by a consortium of Korean companies consisting of KORES - Korea Resources Corporation, LS Nikko Copper, Hyundai Hysco, SK Networks and lljin Copper.The Boleo deposit has Measured and Indicated resources of264.7 million tonnes grading 1.50% copper equivalent (CuEq) & Inferred resources of 159.9 million tonnes grading 1.15% CuEq. The calculation of copper equivalent is based on a combination of metal prices and predicted metallurgical recoveries (Table I). The metallurgical recoveries have been confined by extensive bench and pilot plant testing. Proven and probable reserves are available at Boleo to provide for more than a 30 year mine life. Initially, 25 years of mine life and 23 years of process plant operation have been scheduled in the February 2010 Technical Report Update (www.sedar.com)"

Jan 1, 2012

By Shigem Kuramoto

Pure copper is known to exhibit intermediate temperature embrittlement when it is deformed at a slow strain rate, and a small addition of zinc suppresses this embrittlement. In the present study, the relation between zinc addition and hydrogen behavior was taken into account since the impurity hydrogen is believed to deteriorate the ductility at intermediate temperatures. Pure copper and Cu-l mass % Zn alloy specimens are prepared by melting in argon and in vacuum, so that a comparison can be made between the specimens with normal hydrogen content and those with' less hydrogen content. Tensile tests are performed at temperatures ranging from room temperature to 600 "C, and hydrogen behavior is analyzed using a newly developed testing machine that can detect gas evolution from the specimens during deformation and fracture in ultra high vacuum. The small addition of zinc to pure copper decreases hydrogen content, leading to the improved ductility at intermediate temperatures. In addition, the samples of both pure copper and Cu-1%Zn melted in vacuum exhibited higher ductility at intermediate temperatures than those melted in argon atmosphere, which is attributed to reduced hydrogen content.

Jan 1, 1998

By R. Rajiv Srivastava

Brine leaching of a TSL processed zinc-plant residue (ZPR), containing 83.3% anglesite, has been investigated for lead recovery. A prior treatment of ZPR in acid solution did not show any significant effect of acid concentration in zinc dissolution. The study reveals that the solubility limits of PbCl2 is as an important factor with respect to the brine concentration and pulp density in lixiviant. The dissociated sulfate ions hinder the formation of PbCl2 on prolong leaching (above 60 min), while exhibiting the reverse solubility of lead as PbSO4. A 3-step leaching process could yield >92% leaching efficiency when the parameters were maintained as: 10% pulp density in a 250 g/L NaCl solution, 80 °C temperature, and 60 min time. This leaves the insoluble ferrite, sulfides and oxy-sulfates of zinc and lead in the final residue as revealed by the XRD characterization.

By Hiroshi Nakazawa

An acid mine drainage in abandoned Horobetsu mine in Hokkaido, Japan, contains arsenic and iron ions; total arsenic ca.10ppm, As(III) ca. 8.5ppm, total iron 379ppm, ferrous iron 266ppm, pH1.8. Arsenic occurs mostly as arsenite (As (III)) or arsenate (As (V)) in natural water. As(III) is more difficult to be remove than As(V), and it is necessary to oxidize As(III) to As(V) for effective removal. 5mL of the mine drainage or its filtrate through the membrane filter (pore size 0.45m) were added to arsenite solutions (pH1.8) with the concentration of 5ppm. After the incubation of 30 days, As(III) was oxidized completely with the addition of the mine drainage while the oxidation did not occur with the addition of filtrate, indicating the microbial oxidation of As(III). In this paper, we have investigated the microbial oxidation of As(III) in acid water below pH2.0.

Jan 1, 2006

By Rolando Campos

The CODELCO-CHILE Teniente Converter Technology, is presently being applied in four Chilean smelters (Caletones, Chuquicamata, Potrerillos and ENAMI-Ventanas). A Teniente Converter is due to be used at ENAMI-Hernan Videla Lira (Paipote) smelter in the near future. Also, a Teniente Converter is to be installed as part of a retrofit project for Nkana smelter of Zambia Consolidated Copper Mines Ltd. (ZCCM). The charge to be treated through this smelter will consist of a blend of concentrate arisings from the various concentrators within the ZCCM group. The present status on the application of the Teniente Converter Technology at Caletones smelter as well as its projected performance when used at Nkana smelter, are presented in this paper. The design operational basis, autogenous smelting throughputs, concentrate to matte ratios and benefits due to the use of technical oxygen, are presented and analysed.

Jan 1, 1992

By Jinqian Zhao, Jiarong Li, Shizhong Liu

"Creep cavitation of in single crystal (SX) superalloy was investigated. The constant load creep tests, in single crystal superalloys DD6, were conducted at the conditions of 800°C/700MPa, 850°C/550MPa and 900°C/450MPa, respectively. It was found that there were square facets on the stress fracture surface, and microscopic cavities in the ruptured specimens in the vicinity of the fracture surface. Both the square facets on the fracture surface and microscopic cavities in the section of the ruptured specimens show the morphology of the same thing at the different views, namely creep cavities, which are take the form of flatten cuboid. In fact, creep cavities are the longitudinally tensiled creep cracks slowly growing during the stress tensiling. The factors of creep cracks nucleation and growth conditions include: (a) enough high temperature to activate diffusion (b) casting pores as nucleation origination (c) high strains and strain rates. Eventually, the instantaneous fracture mechanism of creep specimen is cleavage fracture.IntroductionFor the materials used in elevated temperature service, creep behavior has to be accounted for. It is well recognized that creep rupture in polycrystalline materials at high temperature occurs principally by the nucleation and growth of microscopic cavities at grain boundaries, followed by microscopic cavities linkage to form micro- and eventually macro-intergranular cracks[l,2]. Without the usual grain boundaries, SX superalloys have superior capabilities at high temperatures to polycrystalline superalloys, and have become an established feature of gas turbine technology where they are commonly employed in the manufacture of high performance blades[3]. A considerable amount of work has been done over the past tens of years, and many models for nucleation and growth of creep cavities have been proposed, however, those are mainly for polycrystalline materials.In order to improve creep resistance that single crystal superalloys, in which grain boundaries are removed, have been developed. Because there don't exist grain boundaries in SX superalloy, the mechanism of nucleation and growth of creep cavities must be different from that in polycrystalline materials.Understanding the formation and characteristics of creep cavitation is crucial to model the lives of single crystal superalloys.M. Marchionni and L.G. Zhao et al. found that there were square facets on the stress fracture surface [4,5]. Roger C. Reed pointed out creep cavities lie in the necked region[6]. In this paper, the effects on the formation of creep cavities are discussed, as well as the morphology of creep cavities and fracture mechanism of SX superalloys."

Jan 1, 2013

By M. A. Verhaege, Stanislav S. Naboychenko, Vladimir I. Skorohodov, Olga Yu. Goriaeva

A new technology for the processing of secondary raw materials containing precious and Platinum Group Metals (PGMs) has been designed at the Laboratory of Heavy Metals at USTU. The technology is based on hydrometallurgical processing of the materials followed by sorption separation of the PGMs from the leach solution. Different versions of the technology can be realised depending on the type of processed material but the fundamentals are similar. Some parts of the technology can easily be integrated into existing flowsheets. The stage of sorption removal of platinum and palladium was tested on the site of the Joint Stock Company (JSC) "Uralelectromed" on pilot plant scale. A process was developed to obtain fine gold, silver, platinum and palladium. No waste is produced because all solutions are recycled. There are no gas emissions. Selective sorption of platinum and palladium from silver-containing solutions is possible even if the concentration ratio of silver to PGMs is one thousand to one. Sorption behaviour of the PGMs as a function of the bulk metal concentrations was studied. Recovery of 90-95% of platinum and 70-80% of palladium is possible.

Jan 1, 2000

By P. Chris Pistorius

"Ilmenite smelting involves partial reduction of iron oxide from a slag consisting mainly of T1O2, T12O3 and FeO, yielding as products iron (with approximately 2% carbon) and titanium slag. Slag purity requirements preclude any fluxing additions, and the aggressive nature of the slag necessitates a furnace freeze lining. Large departures from thermal and chemical equilibrium hold in the smelter, with possible implications for process stability. The slag is approximately 150K. hotter than the metal, which means that the metal temperature is below the slag melting point; this difference in temperature has been shown to lead to formation of a solid TisOs-rich layer between the slag and metal. Recent equilibrium measurements have confirmed that the slag and metal are not in chemical equilibrium either, with significantly more reducing conditions in the metal than in the slag. After solidification, the pseudobrookite slag structure is metastable below approximately 1400K, and may transform upon slight oxidation.IntroductionThe natural mineral ilmenite is the main source of titanium, which is mainly used to produce Ti02-based pigments. Ilmenite has the ideal formula FeTiC>3, but natural minerals can be partially oxidized (to contain some Fe3+), and typically contain MnO and MgO as well, together with associated silicate minerals. Smelting is one of the methods to upgrade ilmenite for subsequent T1O2 pigment production; smelting involves partial reduction of FeO to form metallic iron as a byproduct and titanium slag as the main product. Reduction is typically controlled to yield a slag which contains around 10% FeO, 85% (Ti02+Tij03) and 5% impurity oxides (mainly MnO, AI2O3 and S1O2). An example of a typical average slag composition from reduction of South African ilmenite is shown in Table I. As this indicates, a significant side reaction is reduction of some T1O2 to T12O3. The relative extents of reduction of FeO to Fe and of Ti02 to T12O3 are such that the slag stoichiometry is close to that of the pseudobrookite phase [1]. Pseudobrookite has the structure AB2O5 (where ""A"" and ""B"" are different cation sites); the phase which makes up the bulk of solidified titanium slag has the AB2O5 structure and stoichiometry [2], and can be viewed as a solid solution of FeTi20s, T13O5, ÌçÔÀ2è5, MgTi20s, AI2T1O5 and C^TiOs [1]. This solid-solution phase is referred to as ""pseudobrookite"" or ""M3O5"" in this paper."

Jan 1, 2012

By Meyer Steinberg

"Some early experiences of a Cooper Union Chemical Engineer on the Manhattan project and his latest studies on CO2 Greenhouse Gas Mitigation Technologies are presented. Mitigating Global Greenhouse effect while maintaining a fossil fuel economy, requires improving the efficiency of conversion and utilization of fossil fuels, use of high hydrogen content fossil fuels, decarbonization of fossil fuels and sequestration of carbon and CO2 applied to all energy consuming sectors of the economy including electric power generation, materials production, transportation and industrial domestic heating. Decarbonization means removal of carbon as C or CO2 either before or after fossil fuel utilization and sequestration means long term disposal of C or CO2. The review will cover the principles of removal and recovery from power plant, stacks, the oceanographic and geological disposal of CO2 and the conversion of CO2 to gaseous and liquid transportation fuels. The global economic aspects of CO2 mitigation technologies are touched upon.IntroductionThis is an odyssey of a chemical engineer. My career started with the production of U235 at the Gaseous Diffusion Plant in Oak Ridge, Tennessee and the production of PU-239 metal at Los Alamos on the Manhattan Project. After 40 years at Brookhaven National Laboratory, I wound up performing studies on CO2 mitigation technologies. The following is a power point presentation on the subject of global warmingThe DOE is proposing to increase its sequestration development program in order to maintain the utilization of our vast resources in coal both for power and for transportation fuel production. Congress is considering steps to promote energy efficiency in attempts to solve not only the CO2 problem, but also the prime problem of energy supply. We will be promoting increases in energy efficiency as time goes on."

Jan 1, 2008

By F. G. Caballero, J. L. Gonzalez-Carrasco, S. Barrius, H. Carreon, M. Lieblich

"The grit blasting is a low-cost technique successfully used to enhance mechanical fixation of the implants through increasing their roughness. As a result of the severe plastic surface deformation, it produces subsurface effects such as grain refinement, hardening and compressive residual stresses which are generally evaluated with destructive techniques. In this research work, non-contacting and contacting thermoelectric power measurements are performed in blasted 316L VM and Ti-6AI-4V specimens using Ah03 and Zr02 particles which yield a coarse and a fine rough surface, respectively. This study correlates the microstructural changes induced by the grit blasting treatment and the limitations and advantages of each of the nondestructive thermoelectric techniques based on the Seebeck effect used to evaluate these biomaterials.IntroductionIt is well known that surface properties play an important role in metallic materials used in bio-medical applications. Since the biological response is correlated directly with surface properties it is comprehensible the intense activity in superficial modification by physics or chemistry methods in this field. Grit blasting, one of the most popular surface modification of metallic biomaterials, enhances the mechanical fixation of the implant through the increase in roughness [1-3]. Roughening is developed by bombarding the surface with a high-velocity jet of ceramic particles, being the final roughness a function of the processing parameters (pressure, distance, time, ... ) and blasting particles (nature, shape, size). As the plastically deformed surface layer tries to expand relatively to the intact interior of the specimen, residual compressive stress gradients develops perpendicular to the surface at shallow depths with a maximum value at a depth in the range of 5 to 60 µm. This surface treatment also may cause subtle variations in the subsurface material properties, such as increased hardness and grain size refinement, which are consequences of the significant plastic deformation through cold work. Blasted affected zones may extend to a depth of up to about 200 µm. The subsurface hardening and the near-surface compressive stress gradient playa beneficial role by retarding fatigue crack nucleation and further growth, ultimately extending the fatigue life of the metallic part [4]. In this work, two non-destructive thermoelectric techniques (NDTT), the non-contacting and contacting thermoelectric power measurements were used to analyze the subsurface induced changes on blasted Ti-6AI-4V and 316L VM specimens using Al2O3 and Zr02 particles. Detailed information on the microstructural induced effects and subsurface mechanical properties were published elsewhere [5-8]. Here the nondestructive evaluation of the involved microstructural changes is used to assess the global subsurface damage. Advantages of using nondestructive techniques during manufacturing are envisaged."

Jan 1, 2012