By Albert Sauveur

IT is not without some hesitation, and even misgiving, that I venture into a discussion of the now classical Roberts-Austen Roozeboom diagram, lest I too fail, like so many other writers, in giving a satisfactory and logical explanation of these interesting curves. Roozeboom's original diagram is reproduced in Fig. 1. The generally accepted meaning of the various curves has been so often described before this Institute that it will suffice to recall it briefly before passing to my own interpretation of the changes involved.

Nov 1, 1906

By J. E. Steiner, J. M. Hodge, M. A. Orehoski

Ingots of four steels (1045, 1080, Ni-Mo-V, and Ni-Cr-Mo-V) were cast at pressures varying from about 1 to 760 mm of mercury, so as to obtain a range of hydrogen contents in each steel. The susceptibility of these steels to flaking was evaluated by cooling hot-rolled blooms at a range of cooling rates, varying from water quenching to slag cooling, and studying the occurrence of flaking as a function of cooling rate. The steels exhibited differences in susceptibility to flaking, and a tlzreshold value for hydrogen content for each steel was found, below which the susceptibility was very low and above which the susceptibility increased markedly with increasing hydrogen content. Mechanical property evaluations, metallogvaplzic exantinations, and X-my diffraction determinations o,t retained austenite were made on samples from the blooms. A mechanism of flaking which is consistent with the observed behaviors, the effects of hvdrogen content, and the differences in susceptibility among the steels investigated is postulated, based on the results of mechanical property evaluations and metallographic and X-ray diffraction studies. ThE important role of hydrogen as a factor in the occurrence of "flakes" or "hair-line cracks" in steel has now been established by many investigations. These have included investigations by steel producers and forging manufacturers, to whom the prevention of flaking is a very real and serious problem, and many research studies aimed primarily at establishing the mechanism of this behavior Several investigators3 have reported that steels cast at reduced pressures (absolute pressures of about 1 mm) not only are low in hydrogen content but are essentially insensitive to the formation of flakes. These investigations have shown that a general relationship exists between hydrogen content and susceptibility to flaking. The difficulty of obtaining suitable samples of steels of a given composition with the desired range of hydrogen contents, particularly in the relatively large sections in which flaking most commonly occurs, has been the principal obstacle to quantitative evaluations of these relationships. Steels with intermediate hydrogen contents between 1 ppm, and the 4ppm or higher of air-cast steels are generally not available in commercially produced steels. Laboratory procedures, in which the hydrogen is introduced into solid steel samples by heating in a hydrogen atmosphere under pressure, generally involve a limitation in the size of the sample which can be treated, and thus are not representative of the behaviors in large sections. The availability of a facility at the South Chicago Works of U.S. Steel, in which several ingots could be cast from a single heat of steel at total air pressures ranging from 0.25 to 760 mm of Hg, has made it possible to overcome this obstacle and to obtain ingots of a given steel covering the intermediate range of hydrogen contents desired. These ingots, furthermore, are of a size suitable for the production of product with section sizes large enough to be representative of the products in which flaking most commonly occurs in commercial production. In these experiments, this facility was used to study the relationships between hydrogen content and the susceptibility to flaking of four steels, two plain carbon steels at 0.45 and 0.80 pct C and two low-carbon alloy steels representing a medium and a rather high hardenability level. These flaking studies were supplemented by evaluations of mechanical properties and by metallographic studies on samples from the blooms, in order to obtain pertinent information on the factors other than hydrogen content which influence the susceptibilities of these steels to flaking. Based on the results of these tests, a mechanism for the initiation and propagation of the flaking cracks, which is consistent with the observed behaviors, is postulated. MATERIALS AND EXPERIMENTAL WORK Steelmaking and Conversion. To provide material for the investigation, five 29- by 35-in., hot-topped, big-end-up ingots were cast from each of four 80-ton, basic electric-furnace heats of four different steels (a 1045 steel, a 1080 steel, a Ni-Mo-V steel, and a Ni-Cr-Mo-V steel). A double-slag practice was used on all steels and the two plain carbon steels were Si-A1 deoxidized with an addition of 2 lb of A1 per ton, while the Ni-Mo-V and Ni-Cr-Mo-V steels were deoxidized only with silicon and

Jan 1, 1964

By Frank J. Tolonen, Nicholas H. Manderfield, Paul Jasberg

EARLY in the study of the low grade iron formations of Michigan, wide variations in their structure and texture became evident. Because of these variations no simple method of concentration is possible, and those portions of the formations that can be exploited profitably under a given stage of metallurgical progress and existing economic conditions must be searched for carefully. Both structure and texture of the formations have an important bearing on their amenability to beneficiation. By structure is meant the banding planes of easy fracture, the porosity, and the degree of leaching. Texture, which includes grain sizes, shapes, and degree of interlocking, determines the amount of grinding necessary to liberate the mineral grains. Structure determines the liberation of portions richer in one mineral. Structure and texture may be termed the gross features of the formation

Jan 11, 1957

By A. W. Peake, F. O. Prior

Considering the great advance in the development and application of electricity, it is not strange that eventually a big field for its use has been found in oil-field operations. So far as is known, the first electric drive in oil-field operations was in the Russian field of Baku in 1900. The first application in this country was made by the South Penn Oil Co. near Folsom, West Va. in 1903. In 1916, electric power was first used in the Burma fields of India for drilling and pumping. Between 1916 and 1922, The Empire Gas & Fuel Co. made the first large electrical installation in the Mid-Continent fields. But although the first application was made 27 years ago, it is only within the last 10 years that oil companies have begun to look upon its use with much favor. Within the last few years, there has been a steady increase in the use of electricity in the oil fields. The first application of electricity for oil-field operations in Wyoming was in the Lander field in 1919; the second was in 1924 in Salt Creek; and the third, and last to date, was made by the Continental Oil Co. in the Big Muddy field during 1926. Lander Field The electrification of oil-field operations in Wyoming was initiated by J. W. Steele, superintendent of the Producers & Refiners Oil Corpn., in the Lander field in 1919. At that time, 32 wells were being pumped from five band-wheel powers, with oil engines as the prime movers. Eight barrels of fuel oil were used for power per day and at the price of 90 c. per bbl. the fuel bill was $36 per day. It was decided to try a 15 to 35-hp. oil-field motor on one of these powers. Electric power was generated with steam at the old Wind River refinery station. This test was so successful that in 1920 all five powers were equipped with 15 to 35-hp. oil-field motors, the power being obtained from the Sinks Canyon hydroelectric station. Four of these powers pumped wells at an average depth of 1450 ft., and the fifth pumped wells at an average of 2100 ft. In 1920, the average production per day from the 32 wells was 325 bbl. The power bill on the

Jan 1, 1928

By C. G. Rhodes, D. Kramer

The kinetics of precipitation of transient a phase during the transformation in U-16 wt pct Mo between 400° and 550°C were studied using quantitative metallography and electrica1 resistiuity measurements. The volume percent of a phase goes through a maximum in time, corresponding to a critical degree of progress of y' formation. prior to its re-solution after prolonged annealing. The fastest rate of a precipitation oc-cuvs at 500°C with a concomittant lowest peak of 9.5 vol pct a. At 450°C, 14 vol pct a, greatest fov any temperature, was observed after 24 hr witlz an associated slowest rate of formation. a precipitation at 400°C ceases after approximately 160 hr and the amount of a present remains unchanged after long times at temperature; no y' was observed metallographically at this temperature. IN the U-Mo system at 16 wt pct Mo, an ordering reaction takes place below 600°C, see Fig. 1, whereupon the random bcc solid solution, y, transforms to the ordered bct phase, y'."2 The new unit cell is constructed of three old unit cells somewhat distorted. While attempting to study the kinetics of this transformation it was observed that an unexpected phase was precipitating out early during the transformation anneal reaching appreciable amounts before disappearing after long times. The y' appeared in the presence of this new phase and after long times constituted the whole sample. Owing to the high optical activity of this unexpected phase under polarized light, it was suspected to be the a phase. Subsequent X-ray powder pictures confirmed this belief. The kinetics of a phase formation and disappearance is the subject of this paper. EXPERIMENTAL PROCEDURE A) Alloy Preparation. Alloys for this study were prepared by vacuum induction melting normal reactor grade uranium and 99.5 wt pct Mo pellets in thoria crucibles. Two ingots were prepared, and sections of the top and bottom of each ingot were chemically analyzed for uranium and molybdenum content. The results of the analyses appear in Table I. B) Metallography. Samples of 16M were wrapped in tantalum foil, sealed in evacuated (5 X 10"6 mm of Hg) quartz capisules, and annealed at 1110"C prior to being transferred directly to the transformation temperature. They were examined metallographically after increasing times to determine the progress of the transformation at 400°, 450°, 500°, and 550°C. The samples were prepared for metallographic examination by mechanical polishing with diamond paste and electrolytic polishing with a solution of glacial acetic acid and chromic acid. Since the y' phase is tetragonal, its presence can be detected by viewing the sample in polarized light. To increase the contrast between y' plates, the samples were electro-etched in a 10 pct oxalic acid solution. To reveal a phase in bright field (it can be seen in polarized light in the "as-polished" state), the samples were electro-etched in a solution of citric acid and nitric acid. To determine the vol pct a phase, a variation of the one dimensional systematic point count method as described by Hilliard and cahn3 was used. The

Jan 1, 1962

By D. J. Carney, E. Van Meter, J. J. Oravec

A study was made of combustion-air temperatures and factors affecting air temperatures in the open-hearth regenerative systems. Air-temperature surveys in the regenerative system revealed marked thermal gradients in the air above the checkers. The design of the fantail-uptake region plays a prominent part in increasing the heat recovery of the regenerative system. THE efficiency of the open-hearth regenerative system is one of the most important factors affecting open-hearth performance. Until recently, this factor has not received the attention in the literature given to many other items affecting performance, such as the type of charge, speed of charging, and the mechanical equipment of the open hearth. J. S. Marsh' emphasized the importance of the flame temperature and its dependence upon the combustion-air temperature. By means of measured air temperatures in open-hearth furnaces, data were presented which showed a remarkable degree of correlation between production rate and combustion-air temperature. This correlation was extremely good in view of the numerous factors, other than air temperature, which affect open-hearth production rates. In Marsh's work, a 100°F increase in air temperature reduced the heat time by approximately 45 min. Realizing the importance of combustion-air temperature, it is desirable to know which factors control the regenerative efficiency of the open-hearth furnace. B. M. Larsen recently discussed this subject.' The present paper illustrates a few of the more important items that affect regenerative efficiency and combustion-air temperature. In the latter part of 1951, a study of open-hearth combustion-air temperatures was begun at the South Works of the United States Steel Corp. In the initial work at open-hearth shop X, which produces low carbon steel products, temperatures were measured in the uptake in a manner similar to that used by Marsh' and the results obtained were very similar to the Bethlehem data. When it was decided to expand the study of combustion-air temperatures, open-hearth shop Y was selected because of the greater variety of furnace-design features, types of steel produced, and firing rates used. With the use of aspirating thermocouples, continuous gas analyzers, thermocouple and optical pyrometers, a study was made of: 1—effect of combustion-air temperature on open-hearth production rate, 2—thermal gradients present in various zones of the regenerative system, 3—effect of furnace-design variations on air temperature and heat recovery, 4-—effect of furnace-operating variables on heat recovery, and 5—variation in heat recovery with furnace age during the normal furnace campaign. Data collected on individual heats at 15 min intervals included air-flow rate, firing rate, checker temperature, combustion-air temperature, and furnace pressure. These data were collected on approximately 230 heats of steel. In addition, information was obtained at random on air infiltration and combustion-gas compositions. The data gathered have shown the desirability of closer control of open-hearth firing practices, a need for reducing air infiltration in the uptake zones, and a need for further study of design of checkers and of uptake-fantail areas. Equipment Air is practically a nonradiating medium. Consequently, in the measurement of air temperatures, the principle of heat conduction must be used rather than heat radiation. For this reason, aspirating-type thermocouple pyrometers normally are used to measure air temperatures. With these devices, air

Jan 1, 1956

By R. J. Wagner, F. F. Craig, H. G. Riley, J. D. Griffith

Peripheral water injection has been underway in the Sholem Alechem Fault Block "A" Unit, Stephens County, Okla., since 1955. In the engineering planning of the flood, it was recognized that maintenance of pressure in the large, dry gas caps was vitally necessary to prevent the loss of an estimated 27 million bbl of oil through saturation of the gas caps by the oil banks moving updip on the peripheral flood pattern. The development of an abundant, low-cost water supply and the rising cost of makeup-gas purchases indicated that gas-cap control by water injection was desirable from an economic standpoint, provided an eflective water barrier could be placed without premature water breakthrough into downdip oil producers. A laboratory model scaled to the existing reservoir conditions was comtructed to evaluate the feasibility of gas-cap water injection. Model studies indicated that (I) water injected at the edge of the gar-oil contact would form a continuous barrier between the oil and gas zones, and (2) water would advance uniformly downdip without segregation due to gravity effects provided a specified, minimum water-injection rate was maintained. The model test results also indicated that it was not necessary to fill the gas cap completely with water. Water injection at the edge of one of the gas caps was initiated in March, 1958, to field test gas-cap water injection. Water breakthrough occurred at a downstruc-ture producing well in April, 1959, after approximately 2.5 million bbl of water had been injected into the gas cap. This was the volume calculated to be required to form the barrier between the oil zone and gas cap. This performance indicates that prevention of oil encroachment into dry gas caps in a peripheral water flood by water injection at the gas-oil contact appears practical and that the model studies provided a valid prediction of field performance. INTRODUCTION The Sholem Alechem Fault Block "A" Sims Sand Unit was one of the fist major waterflood projects in Oklahoma to utilize a peripheral injection pattern. Design of control measures to minimize oil encroachment into the large crestal gas caps was one of the greatest single problems during engineering planning of this flood. Engineering studies indicated that saturation of the gas caps with oil displaced by the peripheral water flood could result in a loss of about 27 million bbl of oil, or over one-half the estimated waterflood recovery. This estimate was based on a residual oil saturation after water flooding of 35 per cent pore volume, compared to the negligible oil saturation initially in the gas caps. The Sholem Alechem Springer field, located in Stephens County, Okla., is an elongated anticline with structural dips varying from 400 to 1,000 ft/mile. The structure contains numerous faults, some of which are sealing. The portion of the field considered in this paper is Fault Block "A", which is the largest of the five major fault segments in the field. A map of the unit is shown on Fig. 1. The unit is bounded on the east and west by major sealing faults, on the north by a water-oil contact and to the south by a deterioration of sand development. Two domes, each having gas caps, exist in the unit and are separated by a north-south fault as shown in Fig. 1. The sands being flooded are the Sims sand members of the Springer series of early Pennsylvanian age. The Sims sands average over 100 ft in thickness in Fault Block "A" and have a porosity of approximately 19 per cent. Core permeabilities average 160 md, with interstitial water saturation of about 23 per cent pore volume. Three different zones can be correlated over most of the area. However, they are commingled in most of the producing wells. The two upper zones, designated as First and Second Sims, are the most important. Both the First and Second Sims have gas caps in the east dome, while only the First Sims has a gas cap in the west dome. These gas caps, whose limits are also shown on Fig. 1, initially occupied nearly 11 per cent of the total reservoir volume. The major concern of this paper is the control of the two gas caps in the First Sims sand. Fig. 2 is a cross section, to scale, across the east dome of this formation. Notable features are the relatively shallow dip, the deterioration of the First Sims sand on the south side of the gas cap and the water-oil contact on the northern edge. The formation dip at the gas-oil contact in this cross section is approximately 5".

By Thomas T. Read

The cost of labor turnover in industry is so large as to justify the adoption of almost any means to bring about its reduction. Intensive study has shown that faulty methods of hiring and discharging men is the most important factor in labor turnover. Complete control over hiring and discharging by the foreman is a relic of outgrown industrial conditions; centralized hiring permits this work to be put on a scientific basis and also does away with many serious evils that cannot, otherwise be reached. Centralized hiring does not impair the authority of the foreman; he hires his men from the employment office and discharges them back to it, instead of from and to the street. The employment manager, being a direct representative of the employer, tends to restore the former relation of direct intercourse between employee and employer that was helpful in avoiding friction between them. Being a specialist,, he is able to bring special knowledge and skill to bear upon the task of selling employment in his concern to desirable workmen; he is also able to give the foreign workman the special attention he requires. Employment managers have been used for the past few years by a number of large organizations, a few of which are engaged in the mining and rnetallurgical industries. They have invariably reduced labor turnover, in some cases to as little as one-tenth of what it had been. So great a reduction is due in part to other changes made in the light of the data made available by scientific study of the labor problem. In my former paper on personnel work' I advocated the more general use of the employment manager in mining and metallurgical enterprises as a means of reducing labor turnover. The form of organization recommended seems not be to understood by all, and I have requested the privilege of explaining it at greater length, since it is perhaps the most important factor of all in personnel work, and has a vital influence on the cost sheet of every industrial enterprise.

Jan 1, 1918

By John McCaslin

ONE of the most common technical terms in the U. S. today is automation-a word not listed in the 1946 dictionary. The influence of automation on the national economy has been tremendous. It has even been the subject of congressional investigations. Automation, writes Aronson, substitutes mechanical, hydraulic, pneumatic, electric, and electronic devices for human effort and decision? Automatic devices and instruments are used extensively in some industries, but many others have yet to take full advantage of these great discoveries. The petroleum industry has been a leader in using automatic controls-some refineries are almost completely controlled by automatic devices. The field of geophysics is entirely dependent on instruments and has progressed at almost exactly the same rate as improvements in instrumentation. In metallurgy and mineral dressing use of instrumentation is increasing very rapidly. Mining engineers throughout the country are beginning to think in terms of instruments and controls.

Jan 3, 1958

By C. N. J. Wagner, E. N. Aqua

The bee alloys of the terminal solid solution of rhenium in niobium were investigated by X-ray diffraclion methods. The analysis of the broadening of the powder pattern peaks from the niobium-rich alloys, cold-worked by filing, showed evidence for faulting on (211) planes. The alloys with larger rhenium concentrations were brittle, and fractured when filed. The analysis of the shapes of the diffraction profiles from powders produced by hammering with steel plates) of these brittle alloys indicated that the broadening was due predominantly to platelets bounded by clibe planes. This result was consistent with the Laue patterns from single-cleazlage facets which showed evidence for clearage fracture on {100} planes. The influence of faulting on the mechanical properties of face-centered cubic (fcc) metals and alloys, i.e., how faulting affects the various dislocation configurations in fcc metals, is well-known.' The important question is whether or not faulting occurs in body-centered cubic (bcc) metals and alloys, and, furthermore, if faulting does occur, to what extent it affects the mechanical properties. Theoretical calculations indicate that the stacking-fault energy is rather high in most bcc metals.2 The results of sev-eral studies using transmission electron microscopy have indicated that faults are present in well-annealed and lightly deformed bcc metals and alloys, such as tungsten,3 vanadium,4 and Mo-Re alloys.5,6 These faults, as have been observed, may be stabilized by the presence of interstitial (C,N,O) atom segregation to the extended dislocations. In addition, there is considerable X-ray diffraction evidence for faulting in bee metals,7-8 using the same techniques that were successful for the study of faulting in fee metals and alloys.7 This X-ray diffraction method is currently the only technique applicable for the investigation of faulting in metals with high stacking fault energies, i.e., when severe amounts of deformation are required to produce sufficient amounts of faulting to be detectable by X-rays. The thinned films of heavily deformed metals will become opaque in the electron microscope due to the high dislocation densities present. In a previous investigation of faulting8 in bee metals of group Vb and VIb, the authors observed that niobium was ductile when filed at room temperature, and showed the highest density of faults on the (112) family of planes. A niobium-base alloy system was therefore chosen to study the effect of alloying on the occurrence of faults in a bcc alloy. There is a large range of terminal solid solubility of rhenium in the alloys of the bee refractory metals. All of the Group VIb-rhenium alloys, i.e., Cr-Re, Mo-Re, and W-Re, exhibit solid solution hardening without loss of ductility.9 In fact, the ductility reaches a maximum for alloys with compositions near to the limits of solubility. This enhanced ductility has been attributed to the lowering of the stacking-fault energy in the alloy; i.e., the increased amounts of twinning provide an additional mode of deformation, resulting in the observed high ductility.' Because of this demonstrated effect of rhenium in bee alloys, it was decided to study a series of alloys of Nb-Re. Using the same X-ray diffraction methods as described in the previous investigation,' one is able to identify the possible causes of broadening of the powder pattern peaks, e.q., particle size, microstrains, stacking faults, and/or twin faults. The separation of these various contributions to the measured peak shape is accomplished by the Warren-Averbach analysis.7 I) EXPERIMENTAL PROCEDURE A series of seven bee solid solution alloys containing from 2.5 to 21.5 at. pct Re (remainder niobium) were prepared at the General Electric Research Laboratory. Buttons, weighing 25 g, were alloyed from electron-beam-melted niobium chips and random rhenium sheet by arc melting in a water-cooled copper crucible, under an argon atmosphere. The buttons were inverted and completely remelted to promote homogenization. The nominal alloy compositions are listed in Table I. Samples of the cold-worked alloys were obtained by filing to produce a powder for the X-ray study. Alloys too brittle to be filed were hammered with steel plates. The resultant filings or brittle impactings were screened through 150-mesh classifiers and compacted to the required shape for the diffractometer holder. The X-ray diffraction peaks were automatically recorded by fixed time counting at uniform 28 intervals, or by continuous registration with a ratemeter. In all cases, the (110)-(220) and (200)-(400) pairs of peaks and the (211), (310), (222), and (321) reflections were measured on a GE-XRD5 diffractometer using CuKa radiation with nickel filter or MoKct radiation and a LiF monochromator in the diffracted beam. The first part of the data reduction, completed with the aid of a series of programmed computations,10 was the analytical resolution of the Kol component of the diffraction profile. Subsequent computations were then made with reference only to the resolved Kol peak shape. These included the measurement of the

Jan 1, 1967

By W. Spencer Hutchinson

The experiments described in this paper were undertaken primarily for the purpose of measuring the quality of work done in screening and sorting in American concentrating-mills for Prof. Richards' work on Ore-Dressiag. For this purpose a series of samples of screened and sorted products was obtained from four different mills, and a plan was devised for sizing these products, and for tabular and graphic representation of the results. The results, together with discussions as to their significance, so far as they serve to interpret the quality of mill-work, have already been published in the above-mentioned work, and it is not the purpose of this paper to duplicate the work, except so far as is necessary to explain and illustrate methods and appliances. The sizing of coarse products was clone by sifting on screens of sheet-metal with round punched holes. These holes ranged in size from 64 mm. to 0.5 mm. in diameter. Below the smaller limit, punched metal, suitable for this work, was not obtainable, and the sizing was carried on by sifting on woven wire-sieves. The finest woven wire-cloth obtainable gave a hole 0.073 mm. square, and the finest silk bolting-cloth pave a pentagonal hole with an average diameter of 0.069 mm. Even these very fine screens served no useful purpose in sifting certain of the very fine classifier-products, of which all, or nearly all, passed through the finest screen. A new adaptation of a method of settling and decantation with water in beakers was therefore worked out, and by this means the sizing mas carried down to grains of a diameter as small as 0.012 mm. Description of Apparatus and Manipu1ntion.—Sieves of sheet-metal with round punched holes were used as far as practicable, chiefly because, as already explained, the primary object of the experiments was to test mill-work, and the mills had all used

Jan 1, 1905

By Donald H. McLaughlin

THE primary function of the mining engineer is to find mineral deposits and fuels in the accessible rocks of the earth and to recover them for the vast needs of our complicated civilization. On him has been placed the responsibility for the exploitation of the nation's and world's mineral resources. The degree to which the minerals of the earth have been utilized serves to an extent as a measure of man's material advancement, as well as an index of the relative strength of nations. The natural endowment of lands, varies greatly, but the intellectual energy of a people is revealed by the way in which they take advantage of their heritage of minerals or reach out to less developed regions by exporting their engineering skill as well as capital to secure the raw materials they need.

Jan 2, 1953

By John D. Sullivan, Edwin J. Rogers, Chester R. Austin

THE problem of making a building unit combining the necessary physical and mechanical properties and good thermal insulation has been foremost in the minds of architects and ceramic and construction engineers for many years. This paper presents the results of studies on thermally expanding shales or clays to produce light-weight cellular products suitable for making building units. An expanded clay block suitable for building purposes should be large enough so that substantial savings may be effected in labor costs in laying the wall. The permeability should be low and it should have sufficiently good "dry-wall" characteristics to permit exposing the exterior surface to the elements, and to permit plastering directly the inside wall surface. The thermal conductivity should be low and the mechanical properties should be adequate. Obviously, a unit possessing satisfactory qualities for constructing an outside wall would be satisfactory for interior walls and for back-up purposes. The results of studies on bloating various shales or clays† and the properties of the expanded products are reported. In another paper1 basic factors involved in bloating of clays are discussed. Manufacturers of ceramic products, particularly structural clay, may encounter bloating of the ware during burning, and precautions must be followed to avoid this phenomenon. About 1927 the C. F. Burgess Laboratories, Madison, Wis., while carrying on an investigation for the American Face Brick Research Corporation, conceived the idea of intentionally bloating clay while holding it in a restrained condition, with the hope of producing a unitary cellular mass. Work was carried on until about 1931, when studies were terminated because of business conditions. These studies were continued later by The Western Brick Co., Danville, Ill., which developed a process of "inwardly expansive bloating." The major purpose of the latter investigation was to produce back-up tile to compete with concrete blocks made from Haydite or cinder aggregate. Haydite is a light-weight aggregate formed by heating certain clays or shales rapidly in a rotary kiln. While the investigations at the C. F. Burgess Laboratories or at Western Brick Co. were not carried far enough to lead to the commercial production of material for the construction of walls, particularly outside walls, they showed that certain clays could be thermally expanded and that it was possible to produce a material of low permeability with a large percentage of the total voids or cells closed. Commencing in 1939, the Ozark Chemical Co. sponsored a research program at Battelle Memorial Institute for the purpose of determining whether it is technically feasible to make thermally expanded building units, and specifically to get answers to the following questions:

Jan 1, 1942

By P. L. Menaul, P. P. Spafford

This paper discusses the most dangerous form of corrosion encountered in condensate-well oil production, the discovery of the agent causing this corrosion and the remedial chemical treatment proved effective by field use. The injection of ammonium hydroxide, even as little as one quart per day, has proved effective in preventing gas-condensate well corrosion. The injection of "Bone oil" is applied to wells producing brines containing calcium and magnesium salts. Introduction The severe corrosion of equipment in high pressure gas condensate wells has been a problem for several years and numerous papers have been presented on the subject. The term "gas condensate" or "distillate well" is applied to a distinct variety of hydrocarbon producing well, the characteristics of these wells being high bottom-hole (formation) pressures and temperatures and high gas production. These wells usually produce about 40 gal of water per million cubic feet of gas and the gas contains from 0.1 pct to 2 pct carbon dioxide. In the operation of this type of well, the operators soon noted severe internal corrosion of the pipe carrying the production. In some instances the dl tubing has been found to be corroded to perforation in eight months. The high well head pressures of 2500 to 8000 psi makes any weakening of the well equipment by corrosion extremely hazardous. Bursting of the well equipment results in very expensive repair operations and may result in the loss of valuable production, loss of the costly well, or even loss of life. In November 1944, a gas-condensate well in a Gulf Coast field producing from 9500 ft showed a tubing leak. The well was "killed" by filling it with mud through the tubing, and then the tubing was pulled. Corrosion was found to have caused several perforations in the tubing, Fig I. While the mud was being circulated to kill the well, a high pressure jet from the corroded hole in the tubing perforated the casing and damaged the well to the extent that the cost of repairs amounted to $75,000. In November 1944, another gas-con-densate well in a Gulf Coast field producing from 11,400 ft showed tubing failure. This well had been producing an average of 2,500,000 cu ft of gas daily for two years. In the workover of this well, it was found that a hole one inch in diameter had corroded through the tubing and that corrosion had reduced the wall of the tubing to less than half the standard thickness over large areas of the interior of the tubing. It was found that corrosion had also caused two leaks in the casing. After four months spent in an attempted workover failed to make the well safe for further production, the well was plugged and abandoned at a total loss of $300,000,00.

Jan 1, 1948

By P. L. Menaul, P. P. Spafford

This paper discusses the most dangerous form of corrosion encountered in condensate-well oil production, the discovery of the agent causing this corrosion and the remedial chemical treatment proved effective by field use. The injection of ammonium hydroxide, even as little as one quart per day, has proved effective in preventing gas-condensate well corrosion. The injection of "Bone oil" is applied to wells producing brines containing calcium and magnesium salts. Introduction The severe corrosion of equipment in high pressure gas condensate wells has been a problem for several years and numerous papers have been presented on the subject. The term "gas condensate" or "distillate well" is applied to a distinct variety of hydrocarbon producing well, the characteristics of these wells being high bottom-hole (formation) pressures and temperatures and high gas production. These wells usually produce about 40 gal of water per million cubic feet of gas and the gas contains from 0.1 pct to 2 pct carbon dioxide. In the operation of this type of well, the operators soon noted severe internal corrosion of the pipe carrying the production. In some instances the dl tubing has been found to be corroded to perforation in eight months. The high well head pressures of 2500 to 8000 psi makes any weakening of the well equipment by corrosion extremely hazardous. Bursting of the well equipment results in very expensive repair operations and may result in the loss of valuable production, loss of the costly well, or even loss of life. In November 1944, a gas-condensate well in a Gulf Coast field producing from 9500 ft showed a tubing leak. The well was "killed" by filling it with mud through the tubing, and then the tubing was pulled. Corrosion was found to have caused several perforations in the tubing, Fig I. While the mud was being circulated to kill the well, a high pressure jet from the corroded hole in the tubing perforated the casing and damaged the well to the extent that the cost of repairs amounted to $75,000. In November 1944, another gas-con-densate well in a Gulf Coast field producing from 11,400 ft showed tubing failure. This well had been producing an average of 2,500,000 cu ft of gas daily for two years. In the workover of this well, it was found that a hole one inch in diameter had corroded through the tubing and that corrosion had reduced the wall of the tubing to less than half the standard thickness over large areas of the interior of the tubing. It was found that corrosion had also caused two leaks in the casing. After four months spent in an attempted workover failed to make the well safe for further production, the well was plugged and abandoned at a total loss of $300,000,00.

Jan 1, 1948

A shrinkage stope is an overhand stope in which the broken ore accumulates until the stope is completed to, or near, the level above. As broken ore generally occupies at least 60 per cent. more space than ore in place, about a third of this must be drawn out as the stope advances to leave a working space under the back. The ore remaining supports the miners and gives temporary support to walls, and is all withdrawn when the stope is finished. The shrinkage-stope method is applicable to steep-dipping deposits of strong ore with strong walls. It may be applied to narrow or wide veins, and is simple and cheap. Five examples, which include important and varied types of deposits, are given: namely, Kennecott, Homestake, Jarbidge district, Mogollon district, and Cripple Creek district.

Jan 1, 1925

By J. M. W. Mackenzie, M. H. Buckenam

Flotation experiments using stearic, oleic, linoleic, linolenic, and ricinoleic acids and naturally occuring products rich in these acids as collectors for calcite are described. The results confirm the validity of the rule of Hukki and Vartiainen relating the collecting power and unsaturation of the C18 acids. Reasons for this relationship are discussed and a close relationship between mineral depression and critical micelle concentration is reported. It has long been recognized that the unsaturated fatty acids are in general superior flotation collectors to their saturated homologues. Whereas earlier workers concentrated on saturated and monoethe-noid acids, recent investigations have centered on oleic, linoleic, linolenic, and the substituted mono-ethenoid acid: ricinoleic. From studies of the collecting properties of palmitic, oleic, linoleic, and linolenic acids on ilmenite, rutile, hematite, and magnetite, Hukki and Vartiai-nenl concluded that the collecting power of fatty acids increased with unsaturation of the hydrocarbon chain. Sun, Snow, and Purcel12 investigated the collecting properties of unsaturated fatty acids as collectors for phosphate ores and concluded that the collecting power increased with increasing unsaturation of the hydrocarbon chain up to two double bonds and that further unsaturation decreased the collecting power. More recently Sun3 studied the collecting power of the C18 fatty acids stearic, oleic, linoleic, and linolenic on 37 minerals. The results of these experiments with a few exceptions showed that the collecting power of the acids increased in the order stearic, oleic, linoleic, and linolenic. The relative collecting powers of linoleic and linolenic acids were in many cases altered by the cleanliness of the mineral surface prior to flotation. Sun concluded that linolenic acid may become oxidized by atmospheric oxygen during flotation, a reaction which would reduce its effectiveness as a collector. This deduction is supported by Gaudin and Cole4 who concluded that oleic and linoleic acids do not undergo appreciable oxidation of the double bonds during flotation but that the linolenic acid double bonds are measurably affected. The most complete investigation on the influence of hydrocarbon chain unsaturation on the collecting properties of fatty acids is that of Kivalo and Lehm~svaara.~ These workers using linolenic acid of a higher purity than Hukki and Vartiainen showed that this acid was superior to oleic and linoleic acids as a collector for magnetite. They also found that ricinoleic acid was a more effective collector for this mineral than the other acids investigated, an observation particularly apparent at high collector concentrations. Seeking to explain the superiority of the unsaturated acids these authors considered the effects of critical micelle concentration, surface activity, hydrolysis, and cross sectional area of the hydrocarbon chain in relation to unsaturation. Using what, according to the results of Caviere are erroneous surface tensions of the soap solutions of these acids, they concluded that the surface activity decreases and the critical micelle concentration increases with increasing unsaturation. In view of the data of Cavier, whose results show that surface activity of these soaps increases with unsaturation, the deductions of Kivalo and Lehmusvaara are open to criticism. The degree of hydrolysis of the soap solutions as measured by Kivalo and Lehmusvaara decreases as the unsaturation of the fatty acid increases, a result which helps to explain the superiority of unsaturated acids as collectors. In view of the superiority of unsaturated acids as collectors for many minerals, attention has been directed towards the utilization of fatty acid raw materials such as tall oils and linseed oils which contain considerable quantities of these acids. This paper describes test work to determine the effect of unsaturation of the hydrocarbon chain on the collecting properties of fatty acids on calcite, and includes comparable test work using natural products rich in unsaturated acids. TEST WORK Reagents: The pure fatty acids used were oleic, linoleic, and linolenic. Of these, oleic was supplied by British Drug Houses Ltd. and the others were produced by the Hormel Inst. When not in use these

Jan 1, 1961

THE paper on "Specific Efficiency of the Blast Furnace" by Richard Franchot, which was pub-lished in the September issue of MINING AND METALLURGY, was presented for discussion at the Pitts-burgh meeting. The session opened with a discussion among S. P. Kinney, Mr. Franchot, and J. N. Reese as to the methods and results in sampling for cyanides in the blast furnace. This is covered in detail in writ-ten discussion below. T. T. Read objected to the use of the term specific efficiency as likely to be confusing. The blast furnace has to perform the function of reducing Fe, 03 to Fe as well as that of fusing the metal and, since the reduc-tion of Fe, 0? involves a CO equilibrium, it seems mis-leading to calculate efficiency on the basis of burning the , all carbon to CO? since it is not possible. Mr. Franchot replied that he used the term in the sense defined by Richards in his "Metallurgical Calculations;" but a subsequent search failed to reveal the term in Richards, who says (page 245, 1st edition): The practical conclusion is that a blast furnace generates in itself not much over 40 per cent of the calorific power of the fuel used, and rejects nearly 60 per cent; by using part of the waste gases to heat the blast, however, some of this rejected heat, to an amount representing net 5 to 10 per cent of the calorific power of the fuel used, is returned to and injected bodily into the furnace, thus rendering available for the purpose of running the furnace about 50 per cent of the calorific power of the fuel as a maximum. The efficiency with which the furnace applies this 50 per cent usefully to the objects of the reducing and smelting is another question for investigation.

Jan 2, 1927

By J. H. Nead

The experiments herein described were undertaken with a view to investigating thoroughly the influence of carbon on the tensile and impact physical properties of carbon steel. The original comprehensive plan included investigation of a series of steels with varying carbon contents over a wide range of heat treatments. These were to be studied as to their static tensile qualities, and also their resistance to shock as measured by the Charpy impact bending test. A thorough metallographic examination was likewise included in the schedule. The Charpy tests and the metallographic examination have not been completed to date, and are accordingly withheld for another report. All heat treatments, however, have been made, and the static tensile tests have been completed. A description of the procedure of the experiment and the results thus far obtained are therefore reported herein. Conclusions No attempt is made to draw general conclusions from these experiments, but the curves and the data are submitted as being of general importance and wide applicability. Composition of Materials An attempt was made to secure steels increasing in carbon by increments of 0.1 per cent. from 0.1 per cent. up to 0.8 per cent., and from that composition to 1.6 per cent. by increments of 0.2 per cent. Actually, however, steels of the composition given in Table I were procured, and as the carbon contents were arranged sufficiently well so that satisfactory curves could be drawn showing the relation between carbon content and other properties, these steels were used in the experiments.

Jan 1, 1916

By H. Tabachnick, N. Hedley

The extraction of gold and silver from ores with alkaline cyanide solutions is well known. Cyanide solutions are also good solvents for many base metal minerals, particularly most of the copper minerals. Leaver and Woolf,1 who determined the solubilities of copper minerals in 0.10 pct sodium cyanide solution, showed that malachite, cuprite, chalcocite, and bornite are readily soluble in cyanide; least soluble are chalcopyrite and chrysocolla. The Mining Chemicals Laboratory of American Cyanamid Co. has studied the possibilities of using cyanide solutions for leaching base metals. In this article the authors present the results of their experiments with cyanide leaching to reduce the copper content of a zinc concentrate from 0.050 pct to the desired specification of less than 0.02 pct. Zinc Ore Sample: The sample of commercial zinc ore used in this investigation to produce zinc concentrates was ball mill feed ranging from 1/2 in. to fines. The ore was crushed to —10 mesh and riffled into 600-g charges for zinc flotation. Analysis revealed 4.54 pct Zn and 0.005 pct Cu. Examined microscopically, the ore consisted essentially of cream-colored sphalerite and carbonate gangue. It contained a small amount of pyrite, partly tarnished. The only copper mineral identified was chalcopyrite, mostly smaller than 20µ, some of which occurred as attachments on sphalerite. Flotation Procedure: Batches of zinc concentrates were made as required according to the following general procedure. A 600-g charge of —10 mesh ore was ground for 4 min at 60 pct solids in a laboratory steel rod mill. Screen sizing showed it to be all —35 mesh with 42 pct —200 mesh. The pulp was transferred to a Fagergren laboratory flotation machine, diluted to 25 pct solids and conditioned for 5 min with 0.6 lb per ton CuSO4, . -5H2O. It was then conditioned with 0.10 lb per ton Sodium Aerofloat promoter and floated for 5 min with pine oil as frother and creosote as froth stiff-ener. The pH during flotation was 8.5. A typical analysis of zinc concentrate subjected to leaching is 44.41 pct Zn and 0.051 pct Cu. The ratio of concentration was close to 10 to 1. Leaching Procedure: Aero Brand cyanide, technical calcium cyanide analyzing 49.5 pet NaCN equivalent, was used for all cyanide leaching tests. For each test three rougher concentrates floated as described were combined (total weight close to 180 g) and the water content adjusted to 150 ml. The percent solids in the pulp was thus 55. After a weighed amount of cyanide flakes had been added, the pulp was agitated on rolls for a given period, then filtered and washed. Filtrate and washed concentrate were assayed for copper content. The procedure for ammonia leaching was similar to the cyanide process. A series of tests was run in which the effects of ammonia as a solvent for copper in the zinc rougher concentrate were investigated. In each test 180 g of zinc rougher concentrate was leached with 150 ml of ammonia solution. Various strengths of ammonia and times of leaching were investigated. The results are shown in Table I. It is apparent that ammonia was a poor solvent for copper in the zinc concentrate; 60 min of agitation with a relatively strong NH:, solution extracted only 2 pct of the copper. CYANIDE LEACHING TESTS Effect of Solution Strength: The solvent effects of 0.125, 0.187, and 0.250 pct NaCN equivalent solutions were compared for leaching periods of 15 min. Residue and filtrate were assayed for copper content. The copper content of the filtrate plus wash was calculated back to the original volume of cyanide solution (150 ml). The effects of cyanide strength are given in Table II, It will be noted that 15 min leaching with 0.25 pct NaCN equivalent solution extracted 74.6 pct of the copper in the zinc concentrate. The leached product assayed 0.013 pct Cu, appreciably below the required specification of 0.020 pct. Effect of Leaching Time: Portions of zinc concentrate were leached with 0.25 pct NaCN equivalent

Jan 1, 1961