Search Documents

By Donghai Li, Cheng Pan, Xuewei Lv, Mei Liu, Enguang Guo

"Phosphorite is the main raw material for the production of phosphorus in chemical industry. More attentions have been drawn to the phosphorite concentrate beneficiated from low-grade phosphorite due to the decrease of high-grade phosphorite. For another, the agglomeration process is necessary for the phosphorite concentrate after beneficiation process. The mineralogy and sintering process of the phosphorite from Leshan, China were studied in this work. The result shows that the main phases in the phosphorite are fluorapatite (Ca3(P04)3F), hydroxylapatite (Cas(P04)3(0H)), quartz (Si02) and dolomite (CaMg(C03)2). The yield of the sinter increases with increasing the carbon dosage to 7%, and then decreases when it continuously increases. Similar regularities were found for the strength and the content of P20s of the sinter. The best strength of the sinter as well as its P205 content were discovered when the carbon dosage is 7%. Fluorapatite ((Ca5(P04)3)F) is the main phase in the sinter while fuggerite (Ca2MgSiz01) is the main binder phase.IntroductionPhosphorus is an important foundation industrial raw material of national defense industry, food industry and chemical industry, where it is used to produce red phosphorus, phosphonium hydroxide, phosphorus pentasulfide and phosphoric anhydride[l-2]."

Jan 1, 2013

By J. M. Skeaff

As much as 100% of the gold and 67% of the silver in a sulphur-bearing hydrometallurgical leach residue have been transferred to copper metal at copper smelting temperatures by dissolving the partially calcined residue in an iron-bearing slag maintained in equilibrium with the liquid copper metal and matte phases. The precious metals can then be recovered by conventional refining techniques. Copper can be recycled at least four times without any detrimental effects on gold and silver transfers and recoveries. Apparent copper recovery in the .process can be over 100% because of the copper content of the residue. Based on slag analys.es, the overal1 recovery of gold in the copper metal and matte phases varies from 94% to 100% under all conditions investigated. On the? same basis, silver recovery varies .from 9S% ?to 99% under optimum conditions, but is only 4S% to 73% under other, less attractive conditions. Unaccounted for silver losses of' about 30% make it difficult to determine the major factors affecting ?silver transfer and recovery. A method for implementing the technology on a commercial scale at a Canadian copper/zinc smelter has been proposed. A preliminary economic assessment and comparison of the proposed pyrometallurgical process with conventional cyanidation indicates that either process is economically attractive for recovering gold and silver from leach residues. Although the capital costs are higher, the pyrometallurgical process is simpler, has higher recoveries, lower operating costs and no .potential environmental problems related to cyanide disposal.

Jan 1, 1989

By Markus A. Reuter

In this paper various hybrid modelling architectures are proposed for the modelling and metallurgical control of pyrometallurgical reactors. Discussed are architectures in which data reconciliation is combined by thermochemical, neural net and dynamic modelling to improve the models. At the same time the data reconciliation models can act as soft-sensors for estimating unmeasurable data. Cases that are discussed are (i) the modelling of a submerged arc furnace for the production of thermal phosphorous, (ii) the processing of Sn-Pb-Zn flue dust (originating from secondary copper) in a hearth furnace, (iii) modelling of a steel converter, and (iv) dynamic modelling of a flash smelter.

Jan 1, 2001

By S. Eckert, G. Gerbeth, K. Timmel, B. Willers, T. Wondrak, N. Shevchenko, M. Röder

The quality of the produced steel in the continuous casting process is significantly governed by the melt flow in the mold. However, direct flow measurements in liquid metals are still rather scarce. In order to investigate these flow phenomena, three experimental facilities operating with low melting liquid metals were installed at Helmholtz-Zentrum Dresden-Rossendorf (HZDR). The melt flow in the models is measured by the Ultrasonic Doppler Velocimetry (UDV) or the Contactless Inductive Flow Tomography (CIFT), multi-phase flows can be visualized by X-ray imaging. The obtained measurement results are primarily used for validation of numerical models. In this paper we will investigate the fluid flow in the mold and the behavior of the surface of the liquid metal using flow measurements by UDV and surface profile measurement by a laser scanner, respectively. Strong fluctuations and deviations of the free surface were observed in case of a static magnetic field

Jan 1, 2016

By Yuanbo Zhang, Zhixiong You, Zijian Su, Bingbing Liu, Guanghui Li, Guang Yang, Tao Jiang

Sodium stannate is widely used in the electroplating and tin alloy industry. But the traditional processes for sodium stannate production are characterized by long flowsheet, high production cost and strict requirement for the equipments, etc. In this study, a novel process for sodium stannate preparation from cassiterite concentrate and sodium carbonate via roasting in CO/CO2 mixed gas then followed by leaching was developed. The effects of roasting parameters on the Sn leaching efficiency were conducted. A Sn leaching efficiency of 77.2% was obtained under the optimal conditions. Sodium stannate (Na2SnO3·3H2O) with a purity of 95.8% was produced by the new process, which is better than that specified for the industrial first-grade product.

Jan 1, 2014

By R. Padilla

A thermogravimetric study has been conducted to follow the decomposition and volatilization of arsenic from enargite concentrate in nitrogen and slightly oxidizing atmospheres. Temperature has a large effect on the rate of volatilization of arsenic. Fractional volatilization of arsenic as high as 98% were obtained in less than 60 min at 650°C in nitrogen atmosphere, while in slightly oxidizing atmosphere the same volatilization could be achieved in 30 min. It was found that arsenic volatilizes as sulfide in nitrogen atmosphere and as 4xture of sulfide and oxide in atmospheres containing 1% oxygen. By using the pore blocking and the first order kinetic models, apparent activation energies of 213 and 200 kJ/mol for the temperature range of 780 - 900 K and 205 and 184 kJ/mol for the temperature range of 900 - 985 K were determined for enargite and copper concentrate, respectively.

Jan 1, 1997

By Wenjie Zhu

Chromite ore processing residue (COPR) is a hazardous waste containing high concentration of chromium. We describe here a pioneer trial of detoxification of COPR in column reactor with an indigenous chromate reducing bacterium Leucobacter sp. Ch1, which showed high chromate reducing ability at high pH. Under the optimum conditions, at 30°C and pH 10.0, pH of leachate decreased from 10.3 to 8.3, and Cr(VI) concentration in solution decreased to zero mg L-1, and 76.4% of Cr(VI) was removed from COPR samples. The leaching toxicity of detoxified residue was 1.1 mg L-1 that was lower than national standard of China.

Jan 1, 2008

By Cesar Garban

The samples of the washings are characterized of the ore for physical, chemical and metalurgical properties for representivity. the optimum values are determined for the recuperation of gold of the washings of the gold ore from the zone El Callao, Venezuela by acidic solutions of thiourea of the following parameters: Ph , contact time, composition of the liquid mixture, ratio of solid to liquid, grade of liberation, in an apparatus designed for contacting solid powder of the mineral with liquid solution of thiourea mantained in suspension by bubles of compressed air. The experimental results showed that the velocity of lixivation in primier time of (20) minutes is rapid and practically 2/3 part of the reaction is completed. For experimental design of parameters, the optimum conditions of recuperation of gold determind in this experimental investigation are:

Jan 1, 1999

By T. H. Jeffers

The U.S. Bureau of Mines' Salt Lake City Research Center. has developed porous polymeric beads containing immobilized non-living biological materials for extracting metal contaminants? from wastewater&. Immobilized biological materials include peat moss, algae, biological polymers, and other materials that demonstrate high .affinities for heavy metals. The beads, designated as BIO-FIX beads, have distinct advantages over traditional methods of utilizing biological materials in that they have excellent handling characteristics . and can be used in conventional processing equipment or low-maintenance systems.. Toxic metals such as copper, cadmium, zinc, lead, and mercury are several of the many heavy metals effectively removed from mine wastewater& using B'IO"FIX beads. Continuous cyclic testing indicated that the beads continued to produce treated effluents which met National Drinking Water Standards (NDIJS) after 175 loading-elution cycles, Adsorbed metals were removed from the beads using dilute ?mineral .acids. In many cases" the extracted metals were further concentrated to enable processors to reclaim the metals, thus minimizing the generation of a hazardous sludge. Tests indicated that use of the beads in a low-maintenance system was particularly effective for treating remote acid mine drainage waters? and small toxic seeps from hardrock mining districts ..

Jan 1, 1991

By C. F. Feng, L. Froyen

"In-situ processes have emerged as new and promising techniques for metal matrix composite fabrication. They offer significant technical and economic advantages over conventional processing. One of the in-situ processing routes that have been used is reactive free sintering of a mixture of powder reactants. However, materials synthesised via this route are always porous because of density differences between reactants and products. An example are the porous Al/(TiB2+Ah03) MMCs obtained by heating powder mixtures of Al+ Ti02+B with Ti02 and B in stoichiometric ratios for forming TiB2• In this study, porous Al/(TiB2+Ah03) composites were further processed by hot-pressing at temperatures above 600°C. This processing cycle was designed so that the composites could be densified. Furthermore, the reaction kinetics of the in-situ processing are studied by means of DSC analysis measured at different heating rates. The activation energies of the three intermediate steps that are involved in the reactive processing for preparing AV(TiB2+Alz03) MMCs are determined to be 923 kJ/mole, 241 kJ/mole and 235 kJ/mole respectively.XRD proved that the hot-pressed products consist of Al, TiB2 and Al203- Properties of the products are assessed by microstructural characterisation (LOM, SEM and EDS), microhardness, Young's modulus and bending tests. The results show that good microstructures, elastic properties and strengths, as well as acceptable ductilities were achieved. For the composition 79.74wt% Al-15.95wt% Ti0z-4.31wt% B, after the reactive free-sintering and hot-pressing cycles, Young's modulus is 105 GPa, bending strength is 509 MPa and maximum strain is 5.0%; for composition 88.73wt% Al-8.87wt% Ti0z-2.40wt% B, they are 89 GPa, 311 MPa and 8.2% respectively. It can be seen that the properties of products can be tailored by adjusting the relative amounts of reactants in green samples. Furthermore, for comparison reasons, Al and a binary system Al-Ti02 were identically processed as the ternary systems. Their microstructures and properties were studied."

Jan 1, 1998

By Samson Adeosun, Sanmbo Balogun, David Esezobor

"Iron and steel making processes give rise to large amounts of usable and unusable materials, the latter generally being termed wastes. It is sometimes difficult to distinguish between re-usable by-products and wastes which cannot be sold or land-filled. Much depends on circumstances such as the local market for the material. This can itself vary from time to time with by-products which cannot be used or sold becoming wastes and vice versa. This paper defines the concept of “waste-free technology”, discusses its development in the steel industry and highlights the benefits of the technology to the manufacturing sector and the environment. The paper also articulates how the “waste-free” technology could be applied in the proposed Ajaokuta integrated steel plant in Nigeria.IntroductionIn the past, nature was considered an inexhaustible store. Its resources were consequently exploited and waste products therefrom were discarded. Today, attitudes have not changed appreciably even as raw materials cost rise by the year to pose a series of socio-economic problems, which, among others, may include the rational and optimum utilization of resources, environmental protection and reduction of waste formation. Consequently, industrialists now face unexpected regulatory pressure in areas of pollution prevention, waste minimization and hazardous waste disposal.Iron and steel making processes give rise to significant amounts of usable and un-usable materials, the latter generally being termed waste. It is sometimes difficult to distinguish between re-usable by-products and wastes which cannot be sold or land-filled. Much depends on circumstances such as the local market for the material. This can itself vary from time to time with by-products which cannot be used or sold becoming wastes and vice versa. In this paper, the term waste refers to those materials that are either irrationally utilized or, land-filled and part of the byproducts that are not utilized. It includes that part of used materials which is not incorporated into the products manufactured during a process stage and which in contrast to reuseable materials, is considered not suitable for any further use, owing to technical or economic factors. In general, these materials are inorganic and parts of them are either utilized or passed to the other processes; the other part should be disposed of using well-established waste disposal practices to avoid any environmental threat.Thus, creative methods must be developed to modify the manufacturing processes to reduce emissions and process wastes by fully utilizing all resources. One method of eliminating the negative effect of waste formation is the use of purification and cleaning structures (pollution control system, PCS). These are, however, quite expensive."

Jan 1, 2008

By W. K. Connor, O&apos

The U.S. Bureau of Mines, in cooperation with the Idaho National Engineering Laboratory (INEL), conducted over 30 hours of melting tests to vitrify simulated low-level radioactive wastes from the INEL Radioactive Waste Management Complex (RWMC). Five separate waste compositions were investigated, each consisting of noncontarninated soil from the RWMC and surrogate materials used to simulate the actual buried wastes. The RWMC soil and five waste compositions were melted in a 50-lb, single-phase electric arc furnace with a water-cooled shell. These tests were conducted to determine melting parameters in preparation for a large-scale melting campaign to be conducted in the Bureau's 1-metric ton (mt), water-cooled-wall, 3-phase electric arc fumace. Bulk chemical composition was determined for each of the feed materials and for the slag, metal, fume solids, and offgas furnace products, and distributions were calculated for the key elements. The material balance for the furnace operation indicates that from 63 to 84 pct of the feed reported to the slag. Cerium, used as the surrogate for the radionuclides in the wastes, demonstrated an extremely strong affinity for the slag product. Although slag temperatures as low as 1250° C were recorded when melting the RWMC soil, temperatures in excess of 1600° C were necessary to achieve the fluidity required for a successful slag tap.

Jan 1, 1994

By Fuxing Yin, Akira Sato, Yoshiaki Ohsawa, Kohji Kawaharai

"INCRAMUTE alloy (nominally 45Mn-53Cu-2Al wt. %) has a specific damping capacity as high as 0.4, through a solid-solution and aging treatment. The damping behavior of the alloy is highly temperature-dependent and shows a peak near room temperature. The inadequate strength in the high damping condition restrains the practical application of the alloy, as structural components. Ferromagnetic MnB particles are dispersed in the alloy during induction remelting the matrix alloy in an argon atmosphere. Surface modification of the MnB particles by mechanical alloying (MA) and suitable control of the addition process cause a homogeneous distribution of MnB particles in the alloy. In the composite containing 2 wt. % MnB particles, temperature dependence of damping capacity is improved, and higher damping capacity is still retained in the temperatures over 60 °C. Meanwhile, the Young's modulus and tensile strength were also increased by about 20%. The roles of the MnB particles in improving both damping behavior and mechanical properties were also discussed.IntroductionMany viscoelastic materials, such as rubbers, polymers and plastics, have the superior ability to damp vibration and noise. However, in the applications as structural materials the high damping capacities of materials are pursued upon the satisfactory mechanical properties, especially those at elevated temperatures. Damping alloys are finding more and more applications in structures where noise and vibration ·should be ·eliminated. Specific damping capacity (SDC), defined as the ratio of the energy dissipated to the maximum vibration energy stored per cycle, is usually used to evaluate the damping capacity of alloys. INCRAMUTE damping alloy, developed by the International Copper Research Association, Inc., has a nominal composition of 45Mn-53Cu-2Al in weight percent. The high damping· microstructure of this alloy is obtained through the solution treatment at 820 °C followed by a water quench and aging at 400°C for 10 hours followed by cooling to room temperature [1]. With the heat treatment, a SDC peak ·vs. temperature of as high as 0.4 was observed in the alloy at the strain amplitude of about 10-3 while a tensile strength of about 500MPa was sustained."

Jan 1, 2000

By Baokuan Li, Fang Wang

"Comparing with the single electrode in electroslag remelting processes, two series-connected electrodes have the advantage of little inductance, lower power consumption and higher melting rate, which was widely used to produce superalloys and specialty steels. Detailed understanding of the electromagnetic field distribution is essential for both improving ingot quality and saving electric energy. In the present work, a 3D finite element model was developed for the magnetic field, electromagnetic force, current density and Joule heating field of electro slag remelting processes (electrode, slag and ingot) with two series-connected electrodes using Maxwell equation, Lorentz law and Joule law. The results show that the maximum current distribute occur at the middle of electrode, due to the interaction of selfinduced and mutual-induced of two series-connected electrode; associated magnetic flux density on the inner side of electrode increase and the outer decrease; The maximum joule heating is at the interface of slag and electrode. The parameter study shows that if the current frequency is greater than 35Hz, the current density in inner electrode tend to linear distribution; with the increasing of original current, The maximum current density near the wall in electrode will increase linearly; with the increasing of electrode innnersion depth and decrease of slag cap thickness and the maximum of the joule heat in slag will increase.IntroductionElectroslag remelting processes(ESR) are widely used to produce superalloys and specialty steels [l-3l_Two pair, four pair or six pair electrodes in electroslag remelting processes is common in casting large scale ingot, which has the advantage of little inductance, lower power consumption and higher melting rate, comparing to singe electrode. They have the same essence with two electrodes in ESR.Compared to the single electrode ofESR, the other electrode is added which can decrease the reactive resistance and power consumption in the two electrodes of ESR. It is a complicated metallurgy process with a series physical and chemistry phenomenon from the molten of steel to the solidification of ingot [4-71_ These physical and chemistry phenomenon originated the effect of alternating current of high intensity. The rule of the alternating current of high intensity which revealed the law of physical and chemistry phenomenon in ESR is the precondition of improving ingot quality and saving electric energy. Jihe Wei and Yongli Ren[S-9lstudied the distribution of electromagnetic field in single electrode ofESR with Maxwell equation and relative electromagnetic theory. It had the limitation that take the electrode and mold as infinite conductivity. A detail analysis of Electromagnetic fields in ESR had been conducted by Patel A D [JO-llJ using general stream-function formulation. It is difficult to extend to three dimensions which could not be used widely. Daniel V [lZJ and Kharicha A [BJ only analysis the current density associated magnetic flux density field and temperature field without the whole irlformation of electromagnetic field. Maopeng Geng [l4J considered the current density and temperature field of the real and fake electrodes in ESR without skin effect. As to the complication of the two electrodes of ESR, it is rarely reported the electromagnetic field and Joule heating field of the two electrodes in ESR. The rule of effect of electromagnetic and modification of numerical simulation should be studied in depth."

Jan 1, 2011

By Sungdon Kim, Chuljoo Kim, Joonsoo Kim, Hosung Yoon

"This study was performed to establish the optimum leaching condition through the experiments for the oxidized roasting followed by leaching of fluorocarbonate rare earth mineral (bastnasite) using sulfuric acid, and to establish the optimum condition for the recovery of cerium by ion- sieve method from the leached solution of bastnasite. The optimum conditions for the sulfuric acid leaching by the oxidizing roasting of bastnasite concentrates are that the roasting temperature is 550 -600 °C, the roasting time is 2 hrs, the concentration of sulfuric acid is 6N, the leaching temperature is S0°C and the leaching time is 3 hrs. At this time, the leaching yield of total rare earth oxides in the leaching of bastnasite concentrates is about 91%. When cerium is recovered by ion-sieve method from the solution obtained by the sulfuric acid leaching of the roasted bastnasite, the optimum conditions are that the TREO(total rare earth oxide) of leached solution is below 70 g/l, the flow rate of leached solution is 9.6 ml/min and the ratio of height to diameter of resin packed in column is above 9. In these conditions, the recovery of cerium of yield 85% and purity 96% is possible.IntroductionThe rare earths are generally called to Lanthanides, which are totally 17 elements including Scandium of atomic number 21 and Yttrium of atomic number 39 in addition to 1 S elements from Lanthanum of atomic number 57 to Lutetium of atomic number 71. Since the separation to each element is very difficult because of their similar chemical properties, the rare earths were used as the mixed rare earths and the mischmetal without separating to each element. However, the high purity rare earths are recently produced commercially to each element so that they are used as the materials for high tech. industry such as electric and electronic materials, catalysts, optical materials, special alloy and 8Uperconductive materials, and their consumption is rapidly increasing. Therefore, the purpose of this study is firstly to prepare leached solution by using the series of process of the oxidation-roasting and leaching by sulfuric acid. Next, second purpose is the separation and recovery of cerium by ion-sieve method."

Jan 1, 1998

By Zhenbo Zhao

The processes and equipment for INLRFH (Isothermal Normalizing by Utilizing the Residual Forged Heat) of alloy carburizing steel products are presented. It is shown that four key parameters: namely (I) cooling rate before isothermal normalizing, (IT) the lowest cooling temperature before isothermal normalizing, (111) isothermal normalizing temperature and (IV) isothermal normalizing time, should be controlled. The prediction and calculation of these parameters can be achieved on the basis of components treated and the technical requirements of the steel parts by an on-line expert system. The cost-reductions due to the energy savings resulting from implementing this system for automotive parts heat-treatment are most promising.

Jan 1, 1999

By Luis W. Pommier

Large quantities of sea sludge containing halogenated organic compounds, such as PCB, oils and metals like arsenic and lead have accumulated throughout the years at the bottom of sea channels and harbors and are obstructing navigation and creating environmental problems which need to be resolved. A sludge from a California port would be dredged by suction pumps, it would be processed in a plant which would be built either on firm soil or on floating platforms. The sludge shows contents of up to 1 ppm of PCB, 15 % oil and 10 ppm of arsenic, which generates a very fetid odor. Bench scale work indicates that most of the contamination concentrates on the solid phase, in fact, only minor amounts of oil report to the sea water and can be readily removed by physical means. After separation of the sea water from the solids of the sludge by decantation, it is possible to solubilize the PCB, the oil and the metals into an organic solvent leaving a non-hazardous soil for disposal near the harbor. The PCB is dehalogenated during the solubilization process leaving a liquor solution containing the oil and metals. The oil is extracted leaving an aqueous solution containing the arsenic. Further process extracts the arsenic from this solution rendering the liquid non-hazardous. Transportation and disposal of the sludge is impractical. There are hundreds of thousands of tons of hazardous soils accumulated in each harbor, which would fill the hazardous waste disposal sites available and it would be, prohibitively expensive to do so. It is not possible to compare the costs of decontamination with a competitive method. If it were, the proposed process would be less expensive than transportation and disposal and it has the advantage of removing the liabilities from the Responsible party. After a full scale continuous pilot project is run to decontaminate a small, 500 cubic yards accumulation of this type of sludge in a California harbor, a full scale environmental project would be initiated. The decontamination of one million tons of sludge would be completed in five years.

Jan 1, 1995

By Yuhsuke Mizukami

Crude high Cr containing steel such as tool steel, heat-resistant steel or stainless steel is produced by dissolution of high carbon ferro-chromium into molten crude steel. In the refining process, decarburization is performed at the first stage, and deoxidation is followed in the next stage. Therefore, the equilibrium relation between dissolved Cr and 0 in molten Fe-Cr alloy after decarburization is very important when yield of deoxidizer is considered for the ovemll control and optimization of the process. It is well known that the yield of deoxidizer does strongly depend on the kinds of refractories of furnace in the secondary refining process. In the present work, the equilibrium relation between dissolved Cr and O in molten Fe-Cr alloy has been measured in a Cr2O3, MgO or Al2O3 crucible at steelmaking temperature. O contents at given Fe-Cr components have been lower in order of Cr2O3, Al2O3 and MgO crucible. The present results have been discussed based on the activities of the constituents in pure solid Cr2O3, and FeO-Cr2O3, MgO Cr2O3 and (AI,Cr)2O3 solid solutions.

Jan 1, 2003

By D. Lambert

Process modeling for large deformation metal forming processes has been developed into a very successful tool in commercial applications during the last two decades. DEFOR.MTM is a well-known metal forming process simulation program used by many industrial and research institutions. Recent developments include the ability to model multiple deforming body behavior during multi-pass pack rolling and microstructure prediction during multi-pass shape rolling. This paper summarizes how DEFOR.MTM can be applied to a number of rolling processes and briefly describes preliminary work carried out using the ALE technique. Keywords: Simulation, Rolling, Pack, Shape, Microstructure, FEM, ALE, Tantalum

Jan 1, 2003

By Yuanbo Zhang, Huanpeng Mi, Guanghui Li, Binjun Liang, Zhiwei Peng, Tao Jiang

Ludwigite ore has not yet been utilized on an industrial scale due to its complex mineralogy and fine mineral dissemination. In this study, sodium salts were employed to enhance the separation of iron and boron by reductive roasting-magnetic separation. It was found that the separation of iron and boron as well as the iron grade and recovery were significantly improved b y the addition of Na2SO4 or Na2CO3. Under the reduction temperature of 1050 °C, reduction time of 60 min and magnetic intensity of 0.1T. Compared with the inexistence of sodium salts, the iron grade and recovery of the magnetic concentrate increased from 83.3% and 88.6% to 93.2% and 95.1%, respectively, by adding 6% Na2CO3. The XRD and microstructure analyses indicated that the iron oxides were transformed into metallic iron and the average metallic iron grains were grown to over 40μm which was beneficial for separation of metallic iron from gangue.

Jan 1, 2016