By Guiqing Zhang, Liansheng Xiao, Zuoying Cao, Li Zeng

A new process of direct solvent extraction of nickel from sulfuric acid leach solutions of low grade and complicated nickel resources using a novel extractant HBL110 was proposed. The basic performance of new organic system was investigated and the continuous pilot plant and the industrial test were conducted. The results indicated that the extractant of HBL110 can be used to directly extract nickel selectively over iron, aluminum, manganese, magnesium, calcium and chromium from sulfuric acid leach solutions. The loaded organic solution can be easily stripped using dilute H2SO4 solutions. Both kinetics of extraction and stripping of nickel were fast. The continuous pilot plant test with the sulfuric acid leach solution of laterite containing 6.22g/L Ni2+, 14.1g/L Fe3+, 0.73g/L Fe2+, 33.9g/L Mg2+, 1.58g/L Al3+, 0.495g/L Ca2+, 0.97g/L Mn2+ and 0.5g/L Cr3+ as feed in mixer-settlers showed that the process had run stably with 98% recovery of nickel. The concentration of nickel in strip liquors reached as high as 50 g/L while the removals of Fe3+, Fe2+, Mg2+, Al3+, Ca2+, Mn2+ and Cr3+ were 98.5%, 91.5%, 99.95%, 99.8%, 99.1%, 98.6% and 99.5%, respectively. The industrial test with the sulfuric acid leach solution of electroplating sludge containing 11.5g/L Ni2+, 2.68g/L Fe3+, 7.54g/L Cr3+, 0.61g/L Mg2+, 2.09g/L Al3+, 0.68g/L Ca2+, 0.022g/L Mn2+ and 0.154g/L SiO2 as feed in mixer-settlers also showed that the process had operated successfully with 99.5% recovery of nickel. The concentration of nickel in strip liquors reached 42.7 g/L while the removals of Fe3+, Cr3+, Mg2+, Al3+, Ca2+, Mn2+ and SiO2 were 99.2%, 99.77%, 99.73%, 99.56%, 99.57%, 98.51% and 98.75%, respectively. The new process exhibited big advantages of short flow sheet, high recovery of nickel, high removal of impurities, low chemical reagent consumption and low cost. Application of this process in industry is expected to make important impact on the extraction of nickel from sulfuric acid leach solutions and to deliver good environmental and economical benefits.

Jan 1, 2016

By A. F. Saavedra, N. E. Richards, C. J. McMinn

"The aluminum industry in general and Reynolds Metals Company in particular have continued to support development work for improvement of the Hall cell design and for alternative processes for the reduction of alumina. The evolution of the Hall cell design will continue into the next century as a result of further development of mathematical models, sophisticated control systems and new materials for cell components. This paper discusses the areas in which the new generation cell advances will differ from the present day design. Additionally, Reynolds Metal s has supported work for the development of a carbo thermic process to reduce alumina. Theoretical work has indicated that this process could possibly have economic advantage over the Hall process. Several complicated furnace configurations have been proposed to provide the conditions for successfully reducing alumina. The results of small pilot scale operation and most promising furnace design are discussed. For comparison, projected capital investment costs and operation costs are discussed. IntroductionThe evolution of the Hall-Heroult process will continue into the next century. This evolution will be influenced by economics, more .restrictive environment and worker protection requirements, and technological development. These factors will also cause changes in the competitive position of alternate processes for aluminum production.Several aluminum producers have made major investments in alternate processes for aluminum production in the past three decades and there is continued support in some companies for improvements in the Hall-Heroult process and for alternate processes. The more visible development work in reduction technology, not aimed at significant process changes, is in the areas of higher amperage cells with bus bar designs to reduce harmful magnetic effects, more advanced and automated feed, voltage and electrolyte composition control, improved energy efficiency and sol id waste disposal . Efforts to bring significant change to the reduction process are being made in development of materials that can function as inert anodes and cathodes. These materials could lead to the development of reduction cells with multiple bipolar electrodes operating on oxide feed and fluoride electrolytes. Development work on new processes was reduced in the last decade by several companies because of economic and technological realities. Reynolds Metals supported work on a carbothermic process to reduce alumina and produce commercial pure aluminum. This work progressed through small pilot plant operation, and resulted in development of furnace designs and operation regimes. This paper reviews how this and other technologies could influence the reduction of alumina beyond the year 2000."

Jan 1, 1988

By B. Madelin

Over the last ten years, Minemet Recherche and Metaleurop have used an approach in order to investigate and improve the operation of its Smelting furnace and its lead blast furnaces. This approach gives importance- to three complementary means of investigation : - Probing campains in the industrial furnace (temperature and gas analysis profiles), - Chemical and physical modeling (coke combustion, sinter reduction modes, flows patterns, ?.) , - Staged mass and heat balances or kinetic model. This allows to define the limits of operation of each blast furnace and to predict the influence of operating parameters on the furnace performances. For the zinc Imperial smelting furnace, the probing results show the existence- of both an Isothermal reserve zone at 1015ºc and a chemical equilibrium between ZnO and gas which makes possible the use of a practical model for heat and material balances. In particular, very good prediction on the influences of operating parameters can be made. On the contrary, for lead blast furnaces, the probing results show that the thermal and chemical equilibria are not reached. Consequently, classical models for staged heat and mass balances are not sufficient. The use of the other means allows then to characterize the specific influences of operating parameters on the thermal instabilities of these furnaces and their allowed limits.

Jan 1, 1990

By R. G. Henley

Mount Isa copper concentrate was combusted in a laminar-flow furnace. The conditions simulated those likely to be encountered in flames in flash smelters of the Outokumpu (air as oxidant) and INCO (oxygen as oxidant) types. The range of conditions studied was as follows: T 400-1400°C, 02 0-100%, SO2 0-95% for residence times up to 0.23 s. The distribution of sulfur, arsenic and lead between the particles and the gas phase was studied. Combustion was very rapid provided the concentrate was adequately dispersed, i.e., no agglomerates. The importance of the latter is discussed. It was possible to oxidize 80% of the sulfur present in the con¬centrate after only 0.1 s reaction time at 1000°C in an atmosphere contain¬ing 8.5% 02 and 12.5% SO2. Best volatilizations (90% of the As, 52% of the Pb) were obtained under localized conditions attained in an air-type flame. Average volatilizations were: air-type flame, As 50%, Pb 32%; oxygen-type flame, As 40%, Pb 30%. The substitution of oxygen for air reduced the arsenic volatilization. The products of combustion were mainly cuprospinel and cuprite; small inclusions of elemental copper were found in some of the particles. At high temperatures, there was a loss of copper due to vaporization of CU( g) CuO kg) (g)

Jan 1, 1983

By R. A. Roberti

Most copper refineries use conventional wheel systems to cast anodes. over a period of time the copper moulds that are used become warped and cracks develop. To control mould warpage, the mould's are either rejected after a certain warpage is reached, or the shape is restored by mechanical means. The cracks, unless they are very severe, are repaired by a peening process. Even with regular maintenance to control warpage and cracks, the moulds have a limited useful life. If warpage and cracks are not controlled, anode quality deteriorates and tankhouse operations are seriously affected. -An intensive study was initiated to develop means of controlling mould warpage which culminated in the d?evelopment of technology to control mould warpage to within ±1. 5 mm, and at the same time effectively contr0l: cracking and significantly increase the mould life-. The warpage control has been achieved by using a unique mould design. Mould cavities are present on both sides of the mould and periodic inverting controls the wa-rpage in the cavities. The mould casting procedure has been developed and all production wheels have been converted to the new mould design. The performance characteristics of these moulds will be detailed. 21

Jan 1, 1987

By Sharif Jahanshahi

Calcium ferrite slags are often associated with Professor Yazawa due to his pioneering work on the thermodynamics of this type of melts. Over the past years CSIRO has invested some effort in studying physico-chemical properties of such melts to fill in some gaps in our knowledge and explore opportunities for application of the understanding developed. These investigations cover thermodynamics, transport properties of calcium ferrite based slags, as well as the kinetics of reactions of such slags with refractories. The present paper provides an overview of some of these studies and highlights some of the interesting behavior of such melts. The oxidation state of copper and arsenic in calcium ferrite based slags are predominantly Cu+ and As3+, respectively, at oxygen potentials below 10.1 atm. The concentration ofCu2+ in such slags becomes significant at oxygen potentials of greater than 10'1 atm at 1300 ?C. The activities of CuOo.s and AsOl.S in calcium ferrite slags show strong deviations from the Raoultian Law, while that of CoO is very close to ideal behaviour with respect to pure solid CoO. Addition of Si02 to calcium ferrite slags can have significant effects on the activities of FeO and Fe2O3 and hence the stability of magnetite phase. Transfer of oxygen in calcium ferrite slags is fast with diffusivity of 2xlO?3 cm2/s at 1350 °C and activation energy of 16 kcal/mol Presence of solid phases, such as magnetite, has pronounced effect on the viscosity of calcium ferrite slags. The observed dependence on solid loading and shear rate indicates deviation from Newtonian behaviour. The interfacial tension between copper mattes and calcium ferrite slags is strongly dependent on the matte grade, with the determined values being much lower than the corresponding ones for interfacial tension between similar mattes and iron silicate slags. MgO, Cr2O3 and MgCr2O4 have low solubility in calcium ferrite slags and their solubility increases with increasing copper oxide content of the slag at 1300 °c. The oxidation state of the slag has strong effects on phase transformation, dissolution rate and disintegration of refractories in calcium ferrite slags. Other key factors with major impact on slag-refractory interactions include viscosity and surface tension of slags as well as the contact angle between slag and refractory material.

Jan 1, 2003

By G. C. Gullo, H. Wabusseg, P. J. Uggowitzer, H. Kaufmann

"The basic concept of New Rheocasting (NRC) is described and the application of wrought alloys with this process is discussed. Practical experiments with the aluminium alloy AIMgSi I are explained. For this alloy the proper NRC - casting temperature was determined by using Thermo Cale - computer software and DT A and the essential processing conditions are shown. In the experiments the melt was taken from an aluminium holding furnace and cast into NRC steel cups. After controlled cooling the resulting slurries were cast into a 4-step die on an UBE HVSC 350 Squeeze Casting machine. The characteristic microstructural values such as grain size and shape factor were measured and compared with classical casting alloys. The influence of the wall thickness of the step part (6 mm, 10 mm and 14 mm) on the microstructure is described. Tensile properties in different heat treatment states are compared with characteristic prope1ties of the same alloys in forged condition. The ew Rheocasting - process CNRC)The NRC process is a recently developed new semi-solid processing method which allows the production of pore-free, pressure tight components.In the NRC process a fu lly liquid, but only slightly superheated melt is taken from a holding furnace and poured into specially designed steel crucibles, which are placed on a carousel next to the Vertical Squeeze Casting machine. In this ,NULL,slurry maker'· globul ar a-Al grains grow, following forced homogeneous nucleation at the cup wall [ 1, 2]. In the few minutes during which the melt is cooled to sem i-so lid processing temperature, a stable ske leton of a-Al phase forms. The resulting slug keeps a cylindrical shape during its slide into the sleeve of the Vertical Squeeze Casting machine, where it is cast into shape."

Jan 1, 2000

By A. M. T. S. Bandara

The solubility of rare earth (RE) salts in aqueous solutions depends on many factors including the type of cations and anions in solution, their concentrations, temperature and the type of solid precipitated. Experiments were conducted using anhydrous La2(SO4)3 and Ce2(SO4)3⋅8H2O as solids and lanthanum(III) perchlorate prepared by dissolving La2O3 in HClO4 solutions as RE-sources. Solutions of H2SO4, H3PO4 and their mixtures in the presence or absence of Na+, Ca2+, Fe(III) or Al(III) as perchlorates served as test solutions. Saturated solutions and precipitated solids were assayed and characterized using standard techniques to show that the La(III) and Ce(III) ions precipitate as hydrated sulphates, phosphates or double salts with sodium, depending upon the solution composition. The change in solubility of RE-salts with solution composition and temperature is the result of the composite effect of changes in solubility products (pKSP) of salts, pKa of acids and other equilibrium constants for ion-association.

By Rui-Qing Li, John G. Peacey, Peter J. Hancock

"Noranda has been investigating a pyrometallurgical process for the direct recovery of zinc from zinc concentrate and zinc and iron containing residues. The process consists of injecting dry zinc concentrate and secondary zinc materials into a molten iron oxysulphide bath, volatilizing metallic zinc into furnace off gas essentially free of sulphur or S02, fixing sulphur contained in the feed materials as iron oxysulphide matte which is disposed, and recovering metallic zinc in an ISP type lead splash condenser. Combustion of petroleum coke with air or oxygen enriched air inside the oxygen containing matte supplies part of the heat, and the products of combustion dilute the zinc-laden gas to a desired level.This paper describes the process concept, thermodynamic background, experimental tests, mass and heat balance calculation for a conceptual flowsheet, environmental stability of the residue and advantages and disadvantages of the process. Experimental tests have successfully proved the process concept and thermodynamic predictions. Direct smelting of zinc concentrate and residues inside an iron oxysulfide bath has a great potential to become a cost effective and flexible zinc smelting process.1. INTRODUCTIONZinc is mainly produced by a roast-leach-electrowinning process route, which accounts for about 80% of the world primary zinc production. This process produces high quality zinc with very high zinc recovery (>95%) but suffers from several major drawbacks such as using high cost electricity as reductant, producing environmentally problematic iron containing leach residue (jarosite or goethite) and the difficulty in treating secondary zinc feed materials containing high impurity levels, such as electric arc furnace dusts from the steel industry, and other complex sources. Also in some areas, markets for sulphuric acid are distant resulting in negative realizations on acid sales.The Imperial Smelting Furnace (ISF) process is the major pyrometallurgical process to treat zinc-lead concentrate. The advantage of this process over the electrolytic zinc process is its flexibility in treating high-lead, bulk concentrates with high recoveries of lead, copper and precious metals. However, this is a two-stage process involving sintering of Zn-Pb concentrates followed by blast furnace reduction. The process requires large amounts of high-quality coke which is a major operation cost, and the sintering process which results in serious environmental problems."

Jan 1, 1996

By V. I. Lakshmanan

Wastes when produced can be reused or recycled prior to disposal. Industries that cause environmental concerns during manufacturing include primary materials and primary metals. Pollution prevention mechanisms to achieve waste reduction require new separation, reclamation, control and process simulation technologies. Substituting recyclables for virgin resources will reduce energy use, water pollution, air pollution, water use and mining wastes. Shrinking landfill space will spur new technologies for waste treatment and recycling. These situations hence offer opportunities for innovative flowsheets with appropriate separation technologies. Development of innovative flowsheets to treat recyclables offer unique opportunities for process/product development, obtain green products and hence market advantage. The paper will illustrate with selected innovative flowsheets to treat recyclables.

Jan 1, 1996

By Adolf Mikula

Lead-tin solders are commonly used in electronic packaging due to their unique combination of electrical, chemical, physical, thermal and mechanical properties. Since it is known that lead and lead containing alloys cause great environmental concern and health hazards it is necessary to replace lead in solder materials. Besides the environmental concerns new technologies in electronic packaging require new and improved solders. In most cases the new solders will consist of ternary or quarternary alloy systems, the main component will be tin or indium and the second element could be bismuth, silver, copper and gold and to improve certain properties a third element will be added. For a third element zinc, nickel, antimony and aluminum can be considered. This report will concentrate on solders containing zinc as an environmental safe element.

Jan 1, 2003

By Mikula Adolf

Lead-tin solders are commonly used in electronic packaging due to their unique combination of electrical, chemical, physical, thermal and mechanical properties. Since it is known that lead and lead containing alloys cause great environmental concern and health hazards it is necessary to replace lead in solder materials. Besides the environmental concerns new technologies in electronic packaging require new and improved solders. In most cases the new solders will consist of temary or quarternary alloy systems, the main component will be tin or indium and the second element could be bismuth. silver, copper and gold and to improve certain properties a third element will be added. For a third element zinc, nickel, antimony and aluminum can be considered. This report will concentrate on solders containing zinc as an environmental safe. element.

Jan 1, 2003

By Bowen Li

Copper vermiculite is a special nanomaterial with excellent antibacterial and antifungal performance. By means of ion exchange, copper vermiculite containing up to 5.8wt% copper was prepared. The chemical and mineralogical characterization of the material was investigated in this study based on the XRD, AAS, TEM and EDS analysis, as well as the calculation of crystalline parameters and crystal chemical formula. Cu2+ and Mg2+ have similar atom radius and same electrovalence. Correspondingly, the structure character of copper vermiculite is very close to that of standard Mg-vermiculite. Most of the CU21 may have occupied the interlayer cationic positions in the form of hydrate in vermiculite. However, some may have entered into octahedral coordinate positions. The values of au and bo of the copper vermiculite crystal cell have no obvious change compared to that of original vermiculite micropowder, but the Co value decreased slightly, which is desirable for the stabilization of the Cu2+ in copper vermiculite.

Jan 1, 2003

By Richard D. Hagni

Microscopic examination of selected, representative, unweathered samples of Birmingham, Alabama, Silurian, sedimentary iron ores has fully revealed the nature of the phosphorous-bearing mineral grains. The grains are composed of carbonate-fluorapatite (collophane), range in size from 1 um to 2.25 mm, and exhibit varied types of intergrowth with hematite. Modal analyses conducted under cathodolumi-nescence have provided quantitative data on the a3undance of each of 15 types of phosphorous-bearing mineral grains and made it possible to assess the potential phosphorous liberation from four types of iron ore. The results indicate that 27% of the total phosphorous contained in the iron ores in the western part of the Birmingham district can be expected to be liberated by fine grinding; 60% for ores in the eastern part of the district.

Jan 1, 1982

By Balladares V. Eduardo

Most of the arsenic contained in copper concentrates is removed in the gas phase during the smelting and converting processes and, according to recent environmental regulations, it is required to fix it in a solid stable form. In this regards, ferric arsenate has been reported as thermal and aqueous stable compound. Therefore, various alternatives for treating gas containing arsenic were considered in this work. From data obtained at laboratory scale on fixation of arsenic using iron oxide, a new process to treat copper concentrates containing arsenic was evaluated. The effect of temperature, oxygen potential and the sample porosity on the fixation of arsenic contained in a gaseous stream was studied, and the iron oxide converted into ferric arsenate was up to 10%. The obtained results suggest a new alternative for gas treatment with an interesting and attractive technical development. The arsenic was retained as ferric arsenate with thermal and aqueous stability, and it allows a safe disposal keeping the environmental restrictions. The kinetics parameters are used to scale up laboratory results to higher processing rates.

Jan 1, 2005

By J. L. Watson

The composite nature of titanomagnetites found on the west coast of the north island of New Zealand is an important parameter in the beneficiation of the black beach sands for export to Japan. To investigate this composite nature, borehole and plant samples from the Waipipi Ironsands Ltd property were subjected to a series of separations in heated Clerici solutions at densities varying from 3.2 to 4.6 g/cc. The resulting density fractons were analyzed magnetically and a set of distribution curves for composite grains proposed. In addition the experi¬mental data was plotted to produce titanomagnetite sand 'washability curves" which illustrate the possible problem areas in beneficiation that may arise due to composite titanomagnetite grains. From this data a set of guidelines are suggested for interpreting the curves in terms of ease of gravity concentration. The composite nature or liberation of titanomagnetite grains is shown to favor high and low grade composites with few intermediate compositions being isolated. The relationships between grain size, borehole depth and liberation are examined and related to beneficiation procedures for the black sand deposit.

Jan 1, 1982

By T. Ueno

Naoshima Smelter & Refinery of Mitsubishi Materials Crop. commissioned a new Mitsubishi continuous copper smelter in May 1991. Process offgas volume of the conventional reverberatory furnace line, one of the previous smelters having been shut down, was very large and thus two acid plants had been operated. It was expected that the offgas volume would be reduced at the new smelter to about a half of the sum of those from previous two 1 smelters and the sulfur dioxide strength would be increased. So various alternatives were studied to minimize the operation cost. And it was decided to utilize both of the plants with minor modifications by diluting the gas either with air or with dilute gases. The acid plants now receive offgases from the new copper smelter, a sintering machine of a lead smelter and a decomposer of waste acid. The paper discusses plant design, operation, improvements and modifications realized in relation with the retrofitting of the copper smelter.

Jan 1, 1992

By E. Oshilna

The Mitsubishi process has many advantages pertaining to economical and environmental matters. These advantages have led to the installations of the Mitsubishi process in constructing new smelters: The Mitsubishi process utilizes highly oxygen enriched blast air and uses a special lime slag in the C?furnace. These characteristics change the . distribution of Impurities from other processes which use P.S. converters, Recently an Increased amount of secondary materials which contain impurities Is being treated at Naoshima Smelter. In order to cope with an Increment of the Impurities load and maintain the cathode quality, many Improvements have been Implemented. This paper discusses the impurities behavior In the Mitsubishi process and describes the measures taken to treat an Increased ?amount of secondary materials:

Jan 1, 1998

By May Nyman

Due to the vast diversity of chemical media in which metal separations are executed, a wide range of ion separation materials are employed, This ,results in an ongoing effort to discover new phases with novel ion exchange properties. We present here the synthesis of a novel class at, thermally and chemically stable microporous, niobate-based materials. Ion exchange studies show these new phases are highly selective for Sr2+ and other bivalent metals.

Jan 1, 1999

By Takahiko Okura

Most non-ferrous raw materials are associated with sulphur. To extract the metals, the sulphur is recovered typically as sulphuric acid or liquid SOz, On the other hand, natural gas may contain over 20% of hydrogen sulphide (HzS) and a huge quantity of elemental sulphur is produced through oil and gas refining processes in the world. A large fraction of the sulphur mined from natural sources is eventually returned to the earth as fertilizers, by-products of desulphurisation and neutralisation processes, or as fugitives to the atmosphere. However, the supply and demand for sulphur are in imbalance. Such situation urges to develop a new smelting process without sulphuric acid production. This paper briefly reviews the global sulphur balance and the technologies for recovering elemental sulphur. The core of this paper is a proposal to convert SO2 gas to elemental sulphur by using organic materials. Some results of thermodynamic calculations and experiments are presented.

Jan 1, 2003