Search Documents

By W. A. Boyer

MINE hoisting ropes can be loaded to capacity only when the strength of each component is exactly known. Characteristic curves provide this information. When load and rate of acceleration are specified for an individual rope, the characteristic curve assumes a predetermined shape. The factor of safety, is the value drived by dividing the breaking strength of the rope by the total stress on the rope where it goes over the sheave wheel. Total stress is made up of the weight of skip and cage, weight of ore, weight of rope between sheave and rope clevise or attachment, friction load, and acceleration force. Bending stresses are neglected in this discussion, as sheaves and drum di- ameters are assumed to be large enough to reduce these stresses to a negligible value. Fig. 1 gives a family of characteristic curves for 13/8-in. improved plow steel hoisting ropes of 6 x 19 or 6x21 construction with hemp core. The curves will hold for all rope sizes of this specified quality when they are subjected to an acceleration rate of 1.608 ft per sec2. As acceleration rates of most deep shaft hoists are close to this value, this family of curves is presented as a standard. Deviation is slight for other rope sizes. Note that for 0, which is the most important, the deviation is within the width of the line on the graph. In a comparison of values for ropes of 5/8-in. and 21/4-in. diam the deviation ranges from a maximum 1.2 pct at 0 ft to 0.6 of 1 pct at 5000 ft. The value of 5.55 is the same for all ropes at 2500 ft. The tabulated columns to the left of the curves are values of total connected load for each size of rope from 5/8-in. to 21/4-in. diam inclusive. With each of these connected loads the safety factor characteristic curve for the rope will be as indicated.

Jan 1, 1957

By C. Norman Cochran

The pllnse diagvam for the NaF-AlF3 system was used to calcutate an ionic model for the NaF-AlF3 system. Assuming an ideal solution,a series of simultaneous equations expressing equilibria be-tween solid and liquid phases at the euleclic, perilec-tic, and melting points were solved for the activities of the ionic species, the dissociation constants, and the entropies and heats of fusion. The calculations suggest the existence of A13F1415 ions in addition to the F-1+AlF6-3 , and AlF4-4 ions previously proposed by others. The calculaled valnes give better agreement with vapor pressures than the previous model without Al3Fl14-5. Additional possible vefinements of the model are proposed. CRYOSCOPIC1 investigations and density data2 for the NaF-A1F3 system have previously been used to study the dissociation mechanism of Na3A1F6 and to derive equilibrium constants for its dissociation to NaF and NaAlF,. Depending primarily on the heat of fusion assumed for cryolite, the dissociation constants ranged between 0.02 and 0.18 from cryoscopic studies, and from 0.09 at 1273°K to 0.16 at 1363°K from density data. In most cases the values were unable to reproduce satisfactorily the experimental liquidus lines very far on the A1F3 side of the Na3A1Fe composition. This suggested the existence of at least one other ionized compound in the melt besides NaA1F4 in the Na3A1F6-A1F3 side of the system. This is assumed to be liquid Na&13F14 (chiolite), which is already established as a stable solid in phase studies of this system. MODEL FOR THE MELT The melt is assumed to be an ideal solution with ion activities equal to anion fractions. The only cation in the model is sodium so that Temkin and simple anionic activities are identical. Although the compounds are completely ionized to Na' and the respective anion in the melt, molecular rather than ionic notation is used throughout this work. The Na3A1Fe is assumed to dissociate to NaA1F4 and NaF as in the former model, and Na&13F14 to dissociate to Na3A1Fe and NaA1F4. Other valid dissociation equilibria can be written involving these four compounds, but all of these can be obtained by combinations of the two described dissociation reactions and, thus, are automatically considered in these calculations. The model allows for no free AlF3 so that compositions for NAIF3 > 0.5 (mole fraction A1F3 on the NaF-A1F3 basis) cannot be treated. The question of the existence of free AlF3 in the melt will be discussed again later. The constants in the model were evaluated from points along the entire known liquidus line of the NaF-A1F3 system. Previous work employed only the liquidus line or densi- ties near the Na3A1F, composition. The liquidus line compositions used in the solution of the model are from unpublished work by Mr. P. A. Foster, Jr., for compositions between the Na3A1F6 melting point and the Na&13F14-A1F3 eutectic, and from the published works of Grjotheim,1 Phillips,3 and Foster4 for the remainder of the system. The relationships used in solving for the desired dissociation constants and heats and entropies of fusion are listed in Table I, and the points along the liquidus line at which each apply are indicated to the right of the relationships. The mole fractions of each of the separate species in the melt are symbolized by N. Relationships [I] and [2] are the respective dissocia-ation constants, Kl and K2, of Na3AIF6 and Na5A13F14 for this model. For simplicity, these constants will be assumed to be independent of temperature. Relationship [3] follows from the assumption of the ideal solution. The expression relating the values of N to the experimental values of NAIf3, is given in Relationship (41. Relationships [5], [6], and [7] each state the equilibrium between a compound in the melt and its pure solid phase for the portion of the liquidus lines where it precipitates. The heats of melting, AH,, and entropies of melting, AS,, used in [5], [6], and [7] are assumed to be independent of temperature. The compositions and temperatures of all five invariant points (two melting points, two eutectics, and one peritectic) along the liquidus lines from NAIF3 = 0 to NAIF3 = 0.5 were employed in the solution. The eutectic and peritectic compositions were particularly useful because each of these is involved in one more equation than other points along the liquidus lines and thus reduces the number of points required to solve for the constants. Also, their use assures that the inflection points in the derived liquidus line will correspond exactly with those on the experimental liquidus line. The total number of equations is 5k1 — 1, where n is the number of experimental composition points used. The number of unknowns is 4n + 5 (4n- 3 values of N, 3 values each of AH, and AS,, and 2 values of K). Thus, six points must be used in the solution to obtain an equal number of equations and unknowns. The one additional required experimental composition was taken on the liquidus line between the Na3A1Fe melting point and the Na3A1F6-Na5A13F14 peritectic. Previous work indicated this was a difficult portion of the curve to fit. The temperature used for the point was 1161°K, the same as for the NaF-Na3A1Fe eutectic. This choice of temperature gave two points with identical NNa3AIF6 values which simplifies the algebraic solution. The second point at this temperature is denoted 1161°'K. PROCEDURE FOR SOLUTION OF EQUATIONS Values were assumed for NNa,AIF and NNaF at the NaF-Na3A1F6 eutectic at 1161°k. By an iterative procedure, the corresponding values for NNa5A13F14 and NNaAlF4 at 1161°K were determined from 131 and 141. A value was assumed for NNaAlF4 at 1161°'K and

Jan 1, 1968

By W. S. Stahmann, F. W. Bowdish

Previously published experimental data showing that both collectable and non-collectable sulfide films may be formed on chrysocolla were analysed, and chemical mechanisms were proposed for the formation of the films. A special technique was developed by which the quantity of sulfur adsorbed was determined for samples sulfidized under different conditions of pH and soluble sulfide concentration. The data on sulfur adsorption were used together with the expression for the equilibrium constant for the proposed reaction to indicate the validity of the chemical mechanism theory. A recent paper 1 about contact angle studies on chrysocolla reported the effects of pH value and sodium sulfide concentration during sulfidization upon the character of the surfaces produced. In each experiment the surface of a specimen of chrysocolla was prepared by grinding it with fine abrasive and washing it in tap water. The specimen was then placed in the sulfidizing solution for 10 min, rinsed in tap water, treated for 15 min in a solution containing 30 mg of potassium amyl xanthate per liter, rinsed in distilled water, and tested for air adhesion in a contact angle apparatus. The results, when plotted as in Fig. 1, showed an island representing conditions giving air adherent or collectable surfaces surrounded by conditions giving non-collectable surfaces. Particular interest may be attached to the region of non-collectability to the right of and above the island in Fig. 1, and to the boundry curve separating these two regions. It is apparent that at any pH from 4.0 to 6.0, where a collectable surface may be produced, a sufficient increase in the sulfide concentration results in a non-collectable surface. Thus it appears that too much soluble sulfide has a depressing effect upon the mineral, just as it has in sulfide flotation. This paper presents some speculations regarding the chemical mechanisms by which the collectable and non-collectable sulfide films may be formed and reports on a physical-chemical study intended to support these speculations. THEORETICAL CONSIDERATIONS The experimental results presented in the previous paper were analysed in several ways in an attempt to understand better the chemical mechanisms involved. For several points on the boundary to the right of the region of contact in Fig. 1, molar concentrations of H+, OH-, HS-, and S= ions, as well as various ion concentration products, were calculated. Following the reasoning of Wark and Cox, 2,3 no single kind of ions may be credited with causing depression of the surface because none of them have a constant con-

Jan 1, 1968

By Gunnar Thaning, Goran Mathisson

The iron ores mined by LKAB in the north of Sweden have excellent beneficiation properties. This gives LKAB a favorable position as regards the production of low silica pellets for direct reduction. LKAB has concentrated on developing and marketing grades of pellets for the Midrex-Purofer-HyL process group, i. e., such direct reduction processes carried out in a shaft furnace or a static bed using reformed natural gas as a reducing agent. The paper deals with properties and quality demands of iron ore pellets for such processes. Matters such as the effect of the residual magnetite in the fired pellets on the degree of metallization, the amount and composition of the slag phase in the pellets, the mechanism of the disintegration during reduction, the state of swelling of the pellets during the conditions prevailing in these processes, the importance of the porosity, the improvement of the reducibility and lowering of the sticking tendency of the pellets by small additions of suitable additives, and the influence of the pellet size are discussed. A special test procedure for direct reduction pellets has been elaborated by LKAB. Thus, three metallurgical properties are routinely determined separately, namely reducibility, reduction strength, and sticking. The test methods are described. Finally the present and future LKAB pellets for direct reduction are presented with respect to chemical analyses and metallurgical properties.

Jan 1, 1980

By O. Jay Myers

THE war effort has furnished the necessary impetus for better magnesium foundry practice. Four or five years ago, there were but a few formulas in general use for cores and mixtures for magnesium castings. Certain sands, binders, and inhibitors were specified and the proportions of these materials in each mixture were maintained between very narrow limits. As more and more war industries entered the field, much research was carried out and methods and practices were improved. Magnesium founding is still in a state of flux; therefore it is not uncommon to find one foundry spraying inhibitors on its cores, and another foundry using sand mixtures with incorporated protective agents. The basic core or dry-sand mold mixture for magnesium in use today is compounded with sand, core oil or resin binder, cereal, and moisture. Core oil or resin binder are added for baked strength while the cereal binder and moisture are for green strength. The normal mixtures (based on the weight of the sand) contain from 0.5 to 1.5 per cent of both cereal binder and core oil, and the moisture content varies between 1.5 and 5 per cent. The ratio of core oil to cereal binder varies from 60:40 to 40:60, while the correct amount of moisture depends upon the method of coremaking. PROTECTIVE AGENTS In all magnesium practice, protective agents are used in conjunction with the core and molding sands to prevent oxidation of the metal. The use of these inhibitors is not novel, but publications covering this field are not entirely adequate. Beck1 says Magnesium alloys decompose water to form magnesium oxide, hydrogen being liberated in the process (Mg + H20 -+ H21 + MgO). This reaction results in the blackening of the skin and the appearance of areas of porosity on the casting surface, the cavities of which are filled with a grey oxide powder (these are termed `burns'). Although sand cores for magnesium castings are thoroughly dried during the baking cycle, burning will take place on the castings unless the metal is protected properly. This type of burning is more difficult to define than the "water-magnesium" reaction cited by Beck. A possible explanation may lie in the following equation: 2Mg + 02 -s 2MgO Here, the source of the oxygen is not water, but the air in the mold cavity, together with the chemically combined oxygen in the core-binding media. Generally, two methods are used to prevent this reaction from taking place.

Jan 1, 1945

By Felix Wunsch

WHILE the effect of the cold-junction temperature has been known by many, its consideration has been ignored in a number of installations, resulting at tunes in a very considerable error. In fact, the magnitude of this error may amount to over 100° in some cases. While hand-operated correcting devices for portable checking pyrometers may be entirely satisfactory, it is, of course, desirable to have such apparatus en¬ Millivoltmeter Thermocouple Platinum Wire Mercury FIG. 1.-EARLY `METHOD OF AUTOMATICALLY COMPENSATING FOR COLD-JUNCTION TEMPERATURE CHANGES. tirely automatic, when applied to curve-drawing or printing pyrometers, otherwise there is no assurance that the record is correct. Numerous methods for automatically compensating for cold-junction temperature changes of thermocouples have been proposed and used in connection with millivoltmeters. One of the earliest proposed was that shown in Fig. 1. A bare resistance wire was immersed in a column of mercury located near the cold junction of the thermocouple. An increase in temperature near the cold junction resulted in a rise of the mercury column, which short-circuited more of the resistance wire causing an increase in the potential difference across the millivoltmeter, which compensated for the decreased electromotive force of the thermocouple.

Jan 9, 1919

By J. E. Tobey, David R. Mitchell, J. H. Kerrick

DETAILED knowledge of purchase specifications established by coal consumers is essential to the successful design and operation of a coal preparation plant. ANTHRACITE Specifications should be considered by both the consumer and the producer as guide posts outlining a certain path for both to follow. Plants differ, therefore specifications must differ to meet the varied requirements. Specifications are not of themselves a "cureall" or an assurance of complete satisfaction in fuel utilization. Specifications should not be regarded as a license to engage in an orgy of buying any and all coals that may happen to fall within their limits. This would lead to the indiscriminate mixing of coals which may vary in their burning characteristics. Different coals of equal grade tend to be individualistic in their burning characteristics. Rather, specifications should be used to help simplify coal selection, to reduce the actual number of coals used over a given period; in other words, to have a stabilizing influence on coal or customer turnover. In the final analysis, the use of too many coals per year in a plant is costly to both the consumer and the producer. Too many sources usually result in higher operating and maintenance costs for the consumer and higher sales costs for the producer. Finally, the statement included in the report accompanying the comprehensive Coal Selection Charts prepared by the Coal Committee of the National Association of Purchasing Agents, and released in 1938, is significant. This Committee worked diligently for a period of 15 years seeking to find a scientific and reliable method for selecting coals. The two following paragraphs are quoted from its report: More important is the fact that no ready-made classification or set of specifications can possibly replace the judgment and resourcefulness of an experienced combustion engineer or fuel technologist, nor the usual need for full scale plant tests under the exact conditions of use before a final decision is made.

Jan 1, 1950

By E. P. Mathewson

(Butte Meeting, August, 1913.) IN a discussion -of a paper on " The Basic Process as Applied to Copper Smelting," by Percy C. Gilchrist, read before the Society of Chemical Industry, London, Jan. 5, 1S91,1 Prof. W. C. Roberts Austen asked Mr. Gilchrist whether he thought that the substitution of a basic lining for acid lining in the Marshes process would afford anything like the service which it had been shown to render in the metallurgy, of iron. Claude Vautin stated that he had experimented for over two years with basic linings for Bessemer converters for copper mattes at Cobar, but had given up the attempt on the score of cost. Mr. Gilchrist in his reply stated that he did not believe in applying any system of Bessemerizing to copper. About the time of the presentation of the paper mentioned, Herman Keller, Superintendent of the Parrott smelter, in Butte, was experimenting on a large scale with converters lined with magnesite brick. He gave up the idea on account of the cost of linings and because no particular advantage was observed. My belief is that his tuyeres and converters were -too small. A short time; afterward similar experiments were tried at the Great Falls plant of the Boston & Montana Co., said at the Old Works of the Anaconda Copper Mining Co. in Anaconda. These were abandoned on the score of cost and the lack of advantages. The same cause of failure, in my opinion, holds here. The Anaconda Copper Mining Co., however, adopted the magnesite brick lining for its tilting casting machines.

Jan 6, 1913

By Shosei Serata, Bruce Gardner

A system of three new field instruments has been developed to measure, in situ, the three basic classes of geomechanical parameters: material properties, stress state, and creep deformation. The significance of this development is that it represents a successful adaptation of recent computer technology to underground rock mechanics work, opening up new possibilities in underground mining methods. The system was developed to meet the application requirements of the stress control method of mining, a method which is based on the actual geomechanical conditions of the underground, rather than upon conventional linear-elastic, idealizations of ground conditions. These instruments enable in situ measurement not only of elastic, but also post-elastic, yielding, and failure conditions of geological materials, establishing the stress control method on a truly scientific foundation. In order to evaluate the present status of this field instrumentation system, case examples of underground mine openings designed with the stress control method are reviewed and analyzed, in terms of the effectiveness of the three instruments for informing and guiding the site-specific application of stress control design.

Jan 1, 1984

Although the Suggestions to Institute Authors, as revised and amplified over the years to meet changing conditions and experience, have had as their primary objective the guidance of the author who is preparing a paper for record in the TRANSACTIONS, there are in this current version many excellent suggestions for the preparation of any material for publication by the Institute In this connection it should be emphasized that in a sense, and to a degree determined by the editors, the Institute has in its journals "a place for everything," especially a place for the article of practical nature that is of immediate but not necessarily permanent interest Such articles may be referred by the Institute Technical Publications Committee to the editors or submitted directly to them , [Papers (TECHNICAL PUBLICATIONS and TECHNICAL NOTES) authorized for the TRANSACTIONS are, with the discussion, gathered together at the end of the calendar year and with a table of contents and index, bound, according to Branch classification, as volumes of the TRANSACTIONS

Jan 1, 1952

By Samuel E. Doak

The utilization of rotary kilns, of the well-known cement type, for the preparation of iron ores for the blast furnace, has become of considerable economic importance within the past 10 years in certain localities, notably those where the native ores are lean. Such kilns may be used simply for the agglomeration of ores too fine to be charged into the blast furnace (i.e., ores whose, loss in the dust catchers is excessive, and whose fineness is detrimental to the working of the furnace), or for the desulphurization of lump and fine ores the sulphur content of which does not exceed 6 or 7 per cent. The desulphurizing action can be combined with that of agglomeration provided the kiln is sufficiently large. Other processes have been developed for the same purpose, but while I am not able to draw a comparison between them by reason of lack of sufficient data, it is safe to say that the kiln, if properly dimensioned for the character of ore to be treated, will compare favorably in its results, both as to economy and quality of product, with any other process. It is not, however, as well adapted for the treatment of flue dust as is a sintering operation, on account of the large percentage of fine coke contained therein. Any combustible entering the kiln at its feed end renders the process very much more expensive and unsatisfactory on account of the difficulty of controlling the temperature, also because of the rapidity with which long "rings" form, due to the increased heat at the cooler end of the kiln. The greatest value of the kiln at present is in the treatment of pyrites cinder; that is, the residue from pyrites ore after the extraction of the greater part of the sulphur. This cinder, while high in iron content, has too much sulphur remaining in it to be allowed to form a large part of the blast-furnace burden, without further treatment. It will range in metallic iron from 42 per cent., representing a very low-grade cinder from a domestic pyrites, to 64 per cent. of the residue from the best Spanish ore, and the corresponding silica content will vary from the maximum of about 25 per cent. to 11/2 per cent. The residual sulphur depends largely on the type of burner used in the original desulphurization. In general, the leanest original ores retain the greatest amounts of sulphur. In modern practice the percentage of sulphur in the cinder is rarely as great as six, and seldom lower than one and one-half. Average analyses for iron, silica, and sulphur of the cinders that have come under my personal observation are as follows:

Jan 1, 1916

By G. Mempel, D. C. Yang, D. W. Fuerstenau

This paper describes details of the design and operation of a batch tumbling mill which has been used for a number of years in the laboratories at the University of California. In order that the energy expended for grinding can be measured accurately, this specially constructed laboratory mill has sensitive torque measuring apparatus. Torque measurements are given for a variety of conditions with this particular mill. In recent years, there have been numerous and fairly extensive investigations of grinding in tumbling mills reported in the literature. Most of these investigations have been carried out in mills with widely differing dimensions. As a result, comparison of results obtained from various investigations has been virtually impossible. If similar mills were used by different investigators, a considerable step forward would be taken in grinding research. A specially constructed laboratory mill with sensitive torque measuring apparatus has been used for a number of years in the laboratories of the University of California. The purpose of this paper is to describe details of the design and operation of this batch tumbling mill so that other researchers, who might be interested in obtaining data for intercomparison, could construct a similar device for their own research. Furthermore, since torque instrumentation is quite expensive, torque measurements are given for a variety of conditions with this particular mill so that those who may not wish to duplicate torque measuring apparatus can make reasonably accurate torque estimates merely by duplicating the loading conditions. It is not intended in this paper to present theoretical derivations of energy consumption in ball mills. This has been done e1sewhere.l-3 CONSTRUCTION OF THE MILL In order to eliminate rust problems with wet grinding, the mill and grinding media are made of stainless steel. The mill shell was rolled from 1/2-in. steel plate. The inside dimensions are 10-in. diam and 11-1/2-in. length, similar to the mill used by Charles.4 It is equipped with eight lifter bars (1/4-in. in height) whose dimensions are given in Fig. 1. The lifter bars have been bolted into the shell so they can be removed for experiments without lifter bars; however, all data presented here are for the mill with lifters. One end of the mill is fitted with two 1/2-in. diam removable plugs for filling the mill with liquid for wet grinding experiments. The mill is mounted on ball bearing rollers as can be seen in Fig. 2. The pillow block bearings are single-row self-aligning sealed ball bearings with 1-1/4 in. hole diam. The bearings supporting the mill shell are single row sealed ball bearings with

Jan 1, 1968

By Robert L. Grayson, Y. J. Wang, R. Mike Mishra

Prediction of ventilation needs in long range mining projections requires serious consideration when formulating those projections. Predicting the behavior of the ventilation system of an old, complex mine poses an especially provocative problem. Air-flow around and through mined-out areas via bleeder systems, leakage flows through stoppings or other air control devices, and the use of multiple fans all add to the basic complexity of a ventilation system and make predictions of ventilation changes very difficult. Fortunately, the task of making ventilation decisions can be greatly assisted by ventilation surveying and computer simulation. The Nemacolin Mine of Jones and Laughlin Steel Corporation, located in Southwestern Pennsylvania, is one such old mine which used the computerized approach successfully. A mine-wide pressure-quantity survey was used to obtain realistic values for airway resistance factors. These values, together with network topology, formed the basic input for computer simulation. Results from this simulation indicated that air quantities generated at critical airways by the model were generally within a couple of percent of those measured in the actual survey. It was then concluded that the model was acceptable for practical application, and it was used immediately for studying the effects on the ventilation system of changing the blade settings of fans. Additionally, the model was modified to incorporate projected mine development and used to predict future ventilation.

Jan 1, 1982

By W. C. Weslow

AN extended program devoted to the development of a matrix for holding diamonds of a size and. kind not heretofore generally used is being carried on by the Carboloy Company, and this paper describes the part of the development that affects mining and its allied industries. Labora-tory and field work so far has indicated the following: 1. Tungsten carbide and cobalt form the most desirable known matrix material for the holding of diamonds for drilling work. 2. Industrial bort diamonds in sizes and of a class not generally heretofore acceptable and therefore less expensive can be successfully held in this cemented carbide matrix. 3. In exploratory drilling, the combination of bort diamonds, impreg-nated throughout a matrix of tungsten carbide and cobalt, when fabri-cated onto drilling crowns, is an indicated economic substitute for drilling crowns in which the diamonds are set by hand, mechanically or by casting. 4. This impregnated type of drilling crown or bit has definite possi-bilites of revolutionizing the drilling of blast holes, particularly in the harder formations. This will be brought about by the development of high-speed light-weight rotary equipment using an impregnated diamond bit to replace the percussion drill now in general use. (The development of this rotary equipment is well past the laboratory stage at this time.) 5. That the use of a rotary bit is a preventive measure in the fight against silicosis. The development of this product was started by G. F. Taylor at the Research Laboratories of the General Electric Co. It was early recog-nized that it had possibilities in the drilling field and the present product is the result of considerable experimental work with other powdered metals as well as with tungsten carbide and cobalt.

Jan 1, 1940

By Wilbur Stout

IN Ohio, the annual output of coke made from native coals has averaged not more than 70,000 tons, or about enough to run a 200-ton blast furnace. Raw coal locally mined from the Sharon, or No. 1, bed was used for iron smelting in Mahoning furnace at Lowellville, Mahoning Co., as early as 1846. This practice was continued in the Youngstown district until the coal became scarce and the Connellsville coke more popular. At present, the Sharon bed contributes a part of the fuel for the production of ferrosilicon iron at Jackson, Jackson Co. About one-third native coal and two-thirds soft coal are used. In this state, coke, on a commercial basis, was first made in Jefferson County probably about 1861 or 1862. The coals used were the Steubenville Shaft, or Lower Freeport, and the Strip Vein or Middle Kittanning. The practice, however, was discontinued before 1880 because of the competition of superior foreign cokes. Beehive ovens, later built at Leetonia, Columbiana Co., were operated for only a few years; the coal used at this place is the Lower Kittanning or No. 5. In a desultory way, slack from the Pittsburgh coal has been coked at a few places in eastern Ohio, and attempts, either for experimental or for commercial purposes, have been made in other parts of the State. Small quantities of coke were made from the Upper. Freeport coal at Salineville, Columbiana Co., and near Nelsonville, Hocking Co.; the results were poor. Tests were made of the Middle Kittanning coal near Zanesville, Muskingum Co., at Moxahala Furnace, Perry Co., and at Washington Furnace, Lawrence Co.; the cokes were all high in sulfur and ash. Attempts were made to coke the Clarion coal at Vinton Furnace, Vinton Co.; a small battery of molding ovens and a pile of high-sulfur coke yet remain to tell the story. The Pittsburgh coal was coked on a commercial scale at Utley and at Lathrop, Athens Co.; but the operations were not successful and were soon abandoned.

Jan 9, 1919

By Jan M. Mutmansky

Main purpose of the research described is to apply the method of computer simulation to the process of tunneling by rapid excavation methods. Primary attention was focused on the materials handling subsystem because of its potential for improvement from a systems standpoint. A description is given of the computer model and a summary of some applications of the model for improving the rapid excavation process is included.

Jan 1, 1975

By G. A. Parks, C. Kovacs

The xanthate flotation of chrysocolla can be improved by preheating the ore to 500° to 600°C. Addition of water vapor reduces the preheating temperature required. The temperature range of flotation improvement correlates well with the range over which dehydroxylation occurs. This observation is consistent with changes in the structure and properties of the mineral as detected by measurement of solubility, D.T.A., T.G.A., X-ray diffraction, and infrared absorption and with recently proposed explanations of chrysocolla flotation. A brief experiment by one of the authors several years ago showed that exposure of chrysocolla to high temperature water vapor resulted in increased recovery by subsequent xanthate flotation. Recently renewed interest in flotation and thermal properties of chrysocolla1-5 prompted further study of this effect and more detailed reporting.6 This paper explores the response of pure chrysocolla recovery in Hallimond tube flotation tests to the time and temperature of exposure and to changes in the water vapor pressure. Brief attention is paid to the effects of such treatment on accessory minerals. A single experiment with flotation of chrysocolla from an ore is reported. MATERIALS Chysocolla from Inspiration, Gila County, Ariz. was crushed in a porcelain mortar, cleaned of visible and magnetic impurities, and screened to obtain -48 +65 mesh (Tyler) material for flotation test work. The clean material contained 28.5% Cu and was identified as chrysocolla by comparison of X-ray diffraction, D.T.A., and infrared absorption data with that reported for similar materials by others.4,5,7 Samples of malachite and chalcopyrite, prepared in a similar way, were also identified by X-ray diffraction. The sources of these materials are unknown. A sample of chysocolla-bearing oxidized copper ore from Pima, Ariz. was crushed and dry ground for thermal activation and subsequent flotation. PROCEDURES Activation: The apparatus used for exposure of materials to high temperature water vapor is illustrated in Fig. 1. The furnace temperature was controlled to ±5°C Water vapor pressure was controlled by pre-saturating a nitrogen carrier stream with water in an adjustable thermostatted saturator (multiple bubbler). A water manometer and capillary orifice flow meter were used to measure nitrogen flow rates for activation and for subsequent Hallimond tube tests. Gas flow rate and temperature were adjusted prior to introduction of samples. Exposure time was measured from the moment of introduction of the sample to the furnace, hence includes an initial drop below the control temperature. After heating, the samples were removed from the furnace and stored at room temperature in air. Representative samples of activated materials were examined by X-ray diffraction and infrared absorption.

Jan 1, 1967

By S. A. Falconer

Much attention and publicity has been given, during recent years, to grinding, classification, flotation, and thickening. The various technical papers, and symposiums held to discuss these important phases of milling, have contributed to a better understanding of the fundamental principles and operating variables involved. Another important part of milling— to the flotation operator—is a treatment step to which frequently too little attention is given—"conditioning," or the treatment the ground mineral pulp receives before it enters the flotation machines. "Conditioning" is a hackneyed and frequently misused term, commonly employed to describe the pretreatment of surfaces of minerals in ore pulps or mill products prior to froth flotation. In general, such pretreatment is for the purpose of changing the flotation characteristics of these mineral sur- faces to enable them to respond in some desired predetermined manner when subjected to flotation. Taggartl states that the function of conditioning is "either to insure selective collector coating of one mineral species while another species is not; or to take such steps as will compensate for departure therefrom." As 0. C. Ralston has stated? ... we are still faced with the fact that some mineral particles are water-avid, others air-avid, and that by properly modifying them they may be enhanced or diminished in desirable or undesirable avidity. Coatings on minerals must still be assumed to fall into three classes: (1) a coating of immiscible oil, (2) a layer of adsorbed substance, (3) a chemically produced coating. It is submitted that the process of preparing mineral surfaces for subsequent flotation treatment should take into consideration physical as well as chemical means for altering the normal flotation response of the mineral surfaces. A more descriptive word than "conditioning" is needed to designate broadly these procedures. The minerals in many ores cannot be made to respond in a normal manner to usual methods of "conditioning" with selectivity modifying reagents, until they have been cleansed, or interfering slimes and soluble salts have been removed from the ore. Therefore, it appears important to include under the general subject of "conditioning" a discussion of the purposes, methods used, and some of the advantages of these pretreatment steps. This is dealt with under the subject heading " Initial Treatment of Mineral Surfaces and Ore Pulps." Under this broader interpretation, the methods employed for treating mineral surfaces to alter their flotation characteristics may be divided into three general classes: 1. Physical methods.

Jan 1, 1950

By Heinrich A. Kortmann

Specifications on the chemical, physical and metallurgical properties of the blast furnace burden are steadily becoming more stringent, especially in those countries where higher raw material and energy costs can be overcome only by improved technology. This paper describes the test methods for the relative predetermination of the criteria where the effects of temperature, gas composition and physical load in the blast furnace are duly considered. Data are presented to show the correlations between burden material tests and blast furnace results. Possible test methods for the direct reduction process are also discussed.

Jan 1, 1977

By F. W. Gordon

Since the waste gases of the blast-furnace came to be generally utilized in heating the blast and raising steam, the gradual improvement in the economy of fuel, mainly through the nse of higher temperature in the blast, has impoverished the gases. The increased output per unit of measurement of the furnace, and the increased height of the furnace, have markedly increased the resistance to the blast, thus enormously increasing the duty required from the gases. In other words, a gas reduced in heating power by a further dilution of CO, is required to raise the temperature of the blast to 1800' Fahr., where formerly 600' was a good temperature, and at the same time to raise steam enough to drive the air into the furnace at a pressure of from four to eight pounds in coke practice, and from eight to twelve pounds in anthracite practice, and also pump at least double the water formerly used at furnaces. Hence the necessity for the employment of the best scheme for thoroughly consuming these gases with the least dilution of air, and the use of the best device for absorbing the heat prodnced for the purposes above mentioned. In a former paper before this Society the writer called attention to such improvements as had been made by his firm, by which it was claimed 1400' Fahr. could be maintained in the blast by a less consumption of gas than was required to maintain 900' when using pipe-ovens; and it would not be too much to say that 1600' Fahr. might now be written in place of the 1-400. The object of this paper is to give the practice of our firm in the

Jan 1, 1884