Search Documents

By Bever M. B., Floe Carl F., Hung Liang

Data on the solubility of hydrogen in iron-silicon alloys are of practical interest, as hydrogen causes gas unsoundness and embrittlement in iron and steel and is also a factor in the metallurgy of cast iron. Zapffe and Simsl have recently demonstrated that in deoxidized iron and steel castings gassiness and bleeding are primarily functions of the hydrogen content of the liquid metal. These authors also suggested convincingly that ordinary melting and casting practice provides several sources of hydrogen for absorption by the metal. Norbury and Morgan2 and Boyles3 have shown that dissolved hydrogen affects the graphitization of cast iron. Schneble and Chipman4 included in a study of the effects of superheating on the properties of cast iron an investigation of the part played by hydrogen. Schwartz, Guiler and Barnett5 investigated the significance of hydrogen in the metallurgy of malleable cast iron. A complete interpretation of investigations of this kind calls for equilibrium values of the solubility of hydrogen in the liquid and solid phases. From the theoretical standpoint, the solubility of gases, especially hydrogen, may reveal some aspects of the nature of liquid metallic solutions. This was implied in the early work of Sieverts6 on the effect of alloying additions on the solubility of hydrogen in copper. Recent work by Bever and Floe7 has shown that in liquid copper-tin alloys the solubility of hydrogen changes abruptly at the composition of the intermetallic compound Cu3Sn. It is of considerable interest to determine whether liquid alloys of iron also have compositions at which the solubility of hydrogen exhibits a discontinuous or otherwise unique behavior. Among the various alloys of iron the iron-silicon system is important because of the presence of silicon in various structural alloy steels, transformer sheets, cast irons and special acid-resisting castings. The various grades of ferrosilicon, finally, cover almost the entire remainder of the composition range. Published information on the solubility of hydrogen in iron-silicon alloys is meager. The first values for pure liquid iron were reported in 1910-191 1 sieverts and Krumbhaar8 and by sieverts.9 They found that 100 grams of iron absorbs 28 c.c. of hydrogen at 1550°C and One atmosphere pressure, and 31 C.C. at 1650°C. In 1938 Sieverts, Zapf and Moritz10 published a value of 26.3 C.C. at 1550°C. Data on the solubility of hydrogen in liquid iron-silicon alloys and in liquid silicon are not available. Martin1' investigated

Jan 1, 1947

By Bever M. B., Floe Carl F., Hung Liang

Data on the solubility of hydrogen in iron-silicon alloys are of practical interest, as hydrogen causes gas unsoundness and embrittlement in iron and steel and is also a factor in the metallurgy of cast iron. Zapffe and Simsl have recently demonstrated that in deoxidized iron and steel castings gassiness and bleeding are primarily functions of the hydrogen content of the liquid metal. These authors also suggested convincingly that ordinary melting and casting practice provides several sources of hydrogen for absorption by the metal. Norbury and Morgan2 and Boyles3 have shown that dissolved hydrogen affects the graphitization of cast iron. Schneble and Chipman4 included in a study of the effects of superheating on the properties of cast iron an investigation of the part played by hydrogen. Schwartz, Guiler and Barnett5 investigated the significance of hydrogen in the metallurgy of malleable cast iron. A complete interpretation of investigations of this kind calls for equilibrium values of the solubility of hydrogen in the liquid and solid phases. From the theoretical standpoint, the solubility of gases, especially hydrogen, may reveal some aspects of the nature of liquid metallic solutions. This was implied in the early work of Sieverts6 on the effect of alloying additions on the solubility of hydrogen in copper. Recent work by Bever and Floe7 has shown that in liquid copper-tin alloys the solubility of hydrogen changes abruptly at the composition of the intermetallic compound Cu3Sn. It is of considerable interest to determine whether liquid alloys of iron also have compositions at which the solubility of hydrogen exhibits a discontinuous or otherwise unique behavior. Among the various alloys of iron the iron-silicon system is important because of the presence of silicon in various structural alloy steels, transformer sheets, cast irons and special acid-resisting castings. The various grades of ferrosilicon, finally, cover almost the entire remainder of the composition range. Published information on the solubility of hydrogen in iron-silicon alloys is meager. The first values for pure liquid iron were reported in 1910-191 1 sieverts and Krumbhaar8 and by sieverts.9 They found that 100 grams of iron absorbs 28 c.c. of hydrogen at 1550°C and One atmosphere pressure, and 31 C.C. at 1650°C. In 1938 Sieverts, Zapf and Moritz10 published a value of 26.3 C.C. at 1550°C. Data on the solubility of hydrogen in liquid iron-silicon alloys and in liquid silicon are not available. Martin1' investigated

Jan 1, 1947

By Donald L. Katz

FIFTEEN years ago Dr. Manning published a paper in "Petroleum Development and Technology" on '.Fundamental Research Relating to Petroleum." He tabulated for several industries "the proportion of their present success which can be fairly attributed to the application of information and processes obtained by scientific research," giving petroleum a score of 7 compared to 100 for the electrical and coal-tar industries. Today the petroleum industry as a whole and the producing groups both have raised their score beyond the majority and are climbing toward the top. Present practices are being developed both by fundamental research and the application of the research method in field operation.

Jan 1, 1941

By C. E. Shoenfelt

Wildcat drilling in the Rocky Mountain region did not suffer as large a decline in 1942 as was anticipated. The drilling program laid out by the Government at the beginning of the year stressed wild-catting operations and called for reduction of drilling in proved fields. The increased wildcatting campaign did not yield a great many new discoveries, nor important extensions to old fields. Several interesting wildcat wells were drilled in Colorado in 1942 but no new fields were discovered. The Wilson Creek field was extended and about 400 acres added to its reserves. In Montana two new oil fields and two small gas fields were discovered. The developments in the marketing situation had improved, however, making the prospects especially bright for 1943, as will be shown presently in the section on Montana in this report. In New Mexico eight wells were completed, which constituted discoveries ol either oil or gas but none of these was of major proportions. In Wyoming one new oil field and one new gas field were discovered, and one old oil field and one old gas field were extended. Most important was the disco-very of prolific oil producers in deeper sands in three old oil fields, of which one at least, Elk Basin, probably is of major proportions. Government Action On Dec. 26, 1942, President Roosevelt signed the O'Mahoney bill, calling for a flat 12.5 per cent royalty on lands in the public domain. It is expected that the enactment of this bill will encourage wildcatting in the public land states. Opportunity for a full discussion of the problems of reserves and production was afforded at the hearings conducted on the O'Mahoney bill by the minerals subcommittee of the Senate Committee on Public Lands and the statements submitted at these hearings last fall placed the situation, its causes and the logical remedy, clearly on record. It was established at the hearings that for several years the volume of oil discovered per wildcat well drilled has steadily declined; new fields discovered have not been of major proportions; drilling costs have advanced rapidly; a sharp decline in exploratory drilling took place in 1942, while the proportion of dry holes increased; the inescapable conclusion is that to find new reserves the search for oil must be intensified and much more wildcat drilling ' must be done. To ensure an adequate drilling campaign, the Petroleum Industry War Council, the Interstate Compact Commission and other representative oil organizations have voiced by resolution their opinion that an upward revision of crude prices is necessary to provide an incentive to the prospector to undertake the hazards of wildcat drilling, since statistics prove that only ope in five or six wells drilled results in actual production. Former Price Administrator Henderson rejected the recommendations for price increases and declared himself unalterably opposed to a general price advance, On the ground that such advances would contribute to inflation. Now that Mr. Hender-

Jan 1, 1943

By C. E. Shoenfelt

Wildcat drilling in the Rocky Mountain region did not suffer as large a decline in 1942 as was anticipated. The drilling program laid out by the Government at the beginning of the year stressed wild-catting operations and called for reduction of drilling in proved fields. The increased wildcatting campaign did not yield a great many new discoveries, nor important extensions to old fields. Several interesting wildcat wells were drilled in Colorado in 1942 but no new fields were discovered. The Wilson Creek field was extended and about 400 acres added to its reserves. In Montana two new oil fields and two small gas fields were discovered. The developments in the marketing situation had improved, however, making the prospects especially bright for 1943, as will be shown presently in the section on Montana in this report. In New Mexico eight wells were completed, which constituted discoveries ol either oil or gas but none of these was of major proportions. In Wyoming one new oil field and one new gas field were discovered, and one old oil field and one old gas field were extended. Most important was the disco-very of prolific oil producers in deeper sands in three old oil fields, of which one at least, Elk Basin, probably is of major proportions. Government Action On Dec. 26, 1942, President Roosevelt signed the O'Mahoney bill, calling for a flat 12.5 per cent royalty on lands in the public domain. It is expected that the enactment of this bill will encourage wildcatting in the public land states. Opportunity for a full discussion of the problems of reserves and production was afforded at the hearings conducted on the O'Mahoney bill by the minerals subcommittee of the Senate Committee on Public Lands and the statements submitted at these hearings last fall placed the situation, its causes and the logical remedy, clearly on record. It was established at the hearings that for several years the volume of oil discovered per wildcat well drilled has steadily declined; new fields discovered have not been of major proportions; drilling costs have advanced rapidly; a sharp decline in exploratory drilling took place in 1942, while the proportion of dry holes increased; the inescapable conclusion is that to find new reserves the search for oil must be intensified and much more wildcat drilling ' must be done. To ensure an adequate drilling campaign, the Petroleum Industry War Council, the Interstate Compact Commission and other representative oil organizations have voiced by resolution their opinion that an upward revision of crude prices is necessary to provide an incentive to the prospector to undertake the hazards of wildcat drilling, since statistics prove that only ope in five or six wells drilled results in actual production. Former Price Administrator Henderson rejected the recommendations for price increases and declared himself unalterably opposed to a general price advance, On the ground that such advances would contribute to inflation. Now that Mr. Hender-

Jan 1, 1943

By Charles H. Fulton

(Cleveland Meeting, October, 1912.) I. INTRODUCTION. THERE are comparatively few accurate data on the melting-or the freezing-point temperature of metallurgical slays, or on related physical phenomena, such as fluidity near the melting-point, specific heat, latent heat, etc. With the exception of the work of H. 0. Hoffman,1 and some older work by R. Akerman, P. Gredt, and H. M. Howe, no information is available that is of direct interest to the metallurgist. Hofman's valuable work is the only one that refers to slags produced in the metallurgy of copper and lead. The classic work of J. H. L. Vogt,2 who views slays from the standpoint of physical mixtures (solutions in which the entities are minerals), has opened up a. new field in the study of slags, and has placed the investigation of such properties as melting-temperatures, etc., on a rational basis. The recent work of A. L. Day, E. T. Allen, and W. P. White, of the Carnegie Institution, at Washington, and of European investigators 3 on certain systems of silicate minerals confirms the value of the investigation of silicate series from this standpoint, and it is my aim to apply this method to metallurgical slaws, in order to gain exact data of value in metallurgy. The work recorded in the present paper is the result of an investigation of reverberatory-furnace slags made for a Western smelting company to determine exactly the influence of change in composition, within comparatively narrow limits, on the melting-point. For a general discussion concerning the mineralogical character of slaws and the principles on which this investigation is based, reference should be made to other work,4 for the subject is too large to be stated in this paper, except very briefly in the following outline 1 Trans., xxix., 682 (1899). 2 Die Silikatschmelzlösungen; I. Ueber die Mineralbildung in Silikatschmelzlösungen; II Ueber die Schmelzpunkt-Erniedrigung der Silikatschmelzlösungen (Christiania, 1903-04). 3 Doelter, Handbuch der Mlineralehevu:e (1911) 4 C. H. Fulton, Principles (of Metallurgy. Chapter viii., on Slags, p. 24.5 (1910).

Dec 1, 1912

NEW- MEMBERS The following list comprises the names of those persons who became members during the period Feb. 10, 1917 to Mar. 10, 1917. ANDERSON, .LAWRENCE W., Min. Engr., Boston Mine, Utah Copper Co. Bingham, Utah. AUSTIN, JOHN W., Assayer, Magma Copper Co., P. 0. Box 101, Superior, Ariz. BARNARD, C. W., Treas. and Resident Mgr., Arizona Asbestos Assn., Globe, Ariz. BIERMAN, A. C : Geol., Producers Oil Co., Box 75, Houston, Tex. BOCHERT, W. C., Prof. of Mining, South Dakota State School of Mines, Rapid City, So. Dak. BROOKS, FLOYD R., Shift Boss, Mond Nickel Co., Ltd., Worthington, Ont., Can. BROWN, CECIL J., Draftsman &,Surveyor, Wallaroo SC Moonta Min. & Smelt. Co., Wallaroo, South Australia. BURRAGE, ALBERT C., Vice-Pres., Chile Copper Co., 85 Amos Bldg.; Boston, Mass. BURGESS, JOHN ALBERT Genl. Supt., United Eastern Min. Co., Oatman, Ariz. CARLOCK, JOHN BRUCE, Supt., O'Neall Oil Process Co., - 608 Haas Bldg., Los Angeles, Cal. CARPENTER, BYRON H., Min. Engr., . . Willoughby, Ohio.

Jan 4, 1917

By W. W. Norton

The gradually increasing proportion of sulphide ores which lead smelters of to-day are called upon to handle has caused the roasting problem to become one of ever greater importance. Mines have increased in depth, methods of concentration have improved, competition in the purchase of ores has become more keen and it has been clear that new and modern methods of eliminating sulphur must receive a large share of attention. We may look back a score of years or so and recall the old hand roasters, some of which turned out a finely divided roasted product, and others fashioned with a "fuse-box" wherein the roasted ore was slagged. Then came mechanical furnaces of several types, the Bruckner cylinder, the Brown-O'Harra, the Ropp, and others, all designed to cut out the cumbersome hand labor of the old reverberatories. Roasting costs were thereupon reduced and tonnages stimulated to a gratifying extent. However, it seems to have been early recognized that this very feature of a greater amount of roasted sulphide ore as compared with oxide ore brought with it a train of difficulties at the blast furnaces. The mechanically roasted ore was fine physically, the blast furnaces were choked and the troubles of the smelterman were not at an end. Then the Huntington-Heberlein pot system of roasting appeared upon the scene, and later on the Dwight-Lloyd machines were invented, and inasmuch as both of these processes were designed not only to roast the ore but to agglomerate it as well, it was apparent that distinct steps in advance had been achieved. At the Murray plant, modern up-to-date roasting practice is fully exemplified and there are now in successful operation roasting furnaces or devices of several sorts: namely, Godfrey revolving-hearth furnaces, Wedge multiple-hearth mechanical roasters, Dwight-Lloyd sintering machines, and Huntington-Heberlein pots. Godfrey and Wedge furnaces will properly handle material high in sulphur, say ores with 25, 30, and 35 per cent. of that element; D. & L. machines and H. & H. pots will positively not treat efficiently ores or mixtures containing anywhere near the sulphur content mentioned, but are confined to charges containing in the neighborhood of 15 or 18 per cent. In passing, it may also be explained that, so far as the knowledge of the writer goes, Godfrey and Wedge furnaces do not economically eliminate sulphur to an extent

Jan 1, 1915

By T. S. Blair

I feel a certain sense of responsibility in bringing before you the subject of the direct process in iron manufacture. I am aware that, in such a body as I have now the honor of addressing, there are few who are not already so well informed upon its past history that it would be a weariness to them to listen to anything else than an account of practical success. Yet, to claim that success involves so much that, if I do not make good my claim, I deservedly expose myself to severe criticism. The whole literature of the art, so far as it relates to the direct process, is, up to this time, but a history of failure. It is safe to say that more money, time, and talent have been fruitlessly spent in the pursuit of this object than in all the other unsuccessful efforts in the whole line of iron metallurgy. A distinguished authority in patent law has remarked that " the invention records of the United States and of foreign countries are filled with the waifs and abandoned relics of these abortive struggles." Dr. Percy, whose great work may be taken as an epitome of all that was worth mention, whether useful or curious, in pig-iron metallurgy, up to the date of its publication (1864), after giving elaborate accounts of various attempts at the direct process, condenses his own opinion of all that had been then effected, into a brief but summary comment upon a pamphlet of one of the sanguine inventors who had said: "It is evident that the present mode of working iron

By Francis Lucas

EACH year we gather in this auditorium to honor the memory of a . distinguished American metallurgist and educator. I cannot bring to you reminiscences of Prof. Henry Marion Howe as other lecturers have done. It was not my good fortune to enjoy the privilege of studying and ,working under his direction. As I have reflected on the published works of Professor Howe, it has seemed to me that his mind was trained on the nature of metals and on the mechanism which produced known but unexplained effects. He was interested in controlling and regulating the causes so as to produce specific effects, useful in serving mankind. I recall an afternoon in May, 1925, when, at the invitation of Mrs. Howe, I visited his former home, Green Peace at Bedford Hills, N. Y. The purpose of my visit was to receive at the hands of the widow -an engraving of Professor Howe, a reproduction of a painting from life. Mrs. Howe showed me his study. The walls of this large attractive room, brilliantly illuminated by the spring sunshine, were literally covered with the scrolls of honors and of decorations which had been conferred on Professor Howe by governments, academies, universities, societies and. institutions the world over. As we walked about the room, she pointed out the significance of each honor and recited a few details of each occasion. I sensed the pride with which Mrs. Howe, then in the late autumn of her life, told me of her husbands' achievements, of his struggles, of his disappointments and of his successes. There was a surprisingly familiar note in the recital to which I was listening. I have found the same theme running as a disconnected thread through the written accounts of the lives of most men of science. We then went to the drawing room to chat for a few minutes before I said my farewells. As we seated ourselves, Mrs. Howe turned to me and asked: "Mr. Lucas, what of this great microscope of yours? Cannot it be applied to the study of disease? What a great blessing it would be if it could be directed to relieve the suffering of mankind."

Jan 1, 1931

By William T. Folwell

The Lucky Friday mine east of Mullan, Idaho, is an outstanding example of a property in the Coeur d’Alene district where a small and insignificant- appearing silver-lead-zinc vein at the surface has changed at depth into a large vein of great importance. The Lucky Friday vein has little if any surface expression and above the 1200 level the ore shoots are small and discontinuous. Between the 1200 level and 2450 level, the lowest developed level, the main ore shoot has shown remarkable improvement on each succeeding lower level, and today the mine is one of the major lead-silver producers in the Coeur d'Alene district. History: The Lucky Friday property is on the north side of the South Fork of the Coeur d'Alene River in sections 25, 26 and 35, T. 48 N., R. 5 E., Hunter mining district, Shoshone County, Idaho. This is about one mile east of the town of Mullan, which serves the eastern portion of the Coeur d'Alene district. The southern part of the property is crossed by a branch line of the Northern Pacific Ry. and by U. S. Highway 10. This highway is the principal road crossing the panhandle of Idaho and connects the district with Spokane, Wash., on the west and Missoula, Mont., on the east. The main portal and surface plant of the Lucky Friday mine is at an elevation of 3365 ft, only a short distance above the valley floor and a few hundred feet from U. S. Highway 10, so the mine is readily accessible for year-round operation.

Jan 12, 1958

By Howard Martens, Pol Duwez

XPERIMENTS were performed on a Cr-Fc alloy Econtaining 44.7 pet Cr in order to determine the heat evolved during the transformation of the a solid solution into the s phase, and the change in volume accompanying the transformation. Since previous measurements on the rate of formation of a from s indicated that the reaction was quite fast as soon as the equilibrium temperature of 820°C was exceeded by some 50°, standard thermal analysis experiments were performed on heating specimens of s at the rate of approximately 40°C per sec. A definite thermal arrest was observed at 870"C, Fig. 1. This result indicates that the reverse seaction of into a is exothermic. From the heating curve of Fig. 1, taking 15°C per sec as the heating rate in the neighborhood of the transformation, 2.4 sec as the time for transformation, and assuming that the specific heat of the alloy at 850°C is an average between iron and chromium, namely 9.5 cal per mol per "C, the latent heat of transformation is approximately 342 cal per mol. The order of magnitude of this latent heat was also obtained by comparing the heating curve of Fig. 1 with a similar curve obtained with pure iron under identical experimental conditions. It was found that the length of the thermal arrest for s was about 1.8 times as long as that for iron. Since the latent heat of the a to 7 iron transformation is 203 cal per mol1, 2 the latent heat of it to a would be 365 cal per mol, which is in relatively good agreement with the value determined from the heating curve. For the determination of volume change, thermal expansion curves were recorded using a specimen containing 44.7 pet Cr and completely transformed to cr by previous treatment. The curves were recorded at a rate of heating of about 4°C per min and at approximately 840°C a sharr, increase in length of about 0.08 pet took place. Fig. 2. It is therefore established that the specific volume of a near the transformation temperature is about 0.24 pet smaller than that of a, and consequently, when the s phase forms in an a matrix, it would tend to shrink away from the matrix. Since the s phase is known to be extremely brittle, these results offer an explanation for the microscopic cracks often observed in the a phase under the microscope. The results of this study are in qualitative agreement with previously published data on stainless steel 19-9DLa and on a Cr-Fe alloy containing 45 pet Cr.' The increase in density due to the transformation from n to s given in ref. 4 is 0.90 pet. These measurements, however, were made at room temperature. whereas the presently reported 0.24 pet is the change at the temperature at which the transformation takes place during heating. In the graph of Fig. 2, the percentage change in length that would be observed at room temperature is given by the length X, which is about 0.27 pet. This would correspond to 0.81 pet in volume change. Acknowledgment This work was done at the Jet Propulsion Laboratory, California Institute of Technology, under Contract No. DA-04-495-ORD-18 with the Army Ordnance Corps, Washington, D. C. The authors wish to thank this agency for permission to publish the results of this investigation. References I H. Klinkhardt: Measurements of True Specific Heats at High Temperatures. Annalen der Physik (1927) 84, pp. 167-200. - H. Esser and W. Runghardt: Influence of the Method, of Dctcrmination on the Measured Heat Content of Iron. Archtvo ffur Dct Eisenhiittenwesen 11934) 8, pp. 37-38. J. J. Gilman, P. K. Koh, and 0. Zmeskal. Delta Ferrite Formation and its influence on the Formation of Sigma in a Wrought Heat Resisting Steel. Trans. ASM 1 1949) 11, pp. 1371-1388. 1 J. M. Thomas: Discussion of ref. 3. Trans. ASM (1949) 41, pp. 3 390-1392.

Jan 1, 1957

By Norman J. Sather

LOCATION AND HISTORY The Bunker Hill Mine is situated on the south side of the Coeur d’Alene River in Shoshone County of Northern Idaho near the City of Kellogg. Kellogg, the largest in the Coeur d’Alene District cities, is at an elevation of 2,300 feet and has a population of approximately 7,000 people. It can be reached by air, railway or highway. The history of the Bunker Hill Mine dates back to August 26, 1885, when Noah S . Kellogg found the outcrop of the Bunker Hill ore body on the hillside above the present town of Wardner, Idaho, in Milo Gulch. A small concentrator was erected in 1886. Before the railroad came, the mine output was transported by mule teams to the head of navigation on Coeur d’Alene Lake. After ten years of production, an interest was purchased in the Tacoma Smelter at Tacoma, Washington, to which the entire output was shipped. In 1916 and 1917 a modern lead smelting plant and refinery was erected and in 1927 and 1928, a modern Electrolytic Zinc Reduction Plant was built and put into operation by the Sullivan Mining Company which was 50% owned and now totally owned by The Bunker Hill Company. GEOLOGY AND MINERALOGY The Bunker Hill ore bodies are found in gray and greenish gray quartzite and argillaceous quartzite of Precambrian age and are known as the Revett and St. Regis formations. Most of the ore bodies are found in the St. Regis formation.

Jan 1, 1970

By R. S. French, W. R. Hibbard

FOR tensile deformation, if the stress value is defined by the ratio of the load to the actual area, and the strain value by the natural logarithm of the ratio of the immediate length to the original gauge length of the sample, the resulting data when plotted with logarithmic coordinates result in a linear relation extending from the initial plastic yielding through the maximum load and in some cases, such as for copper and brass, to fracture'.'. The normal form of the curve, therefore, is a parabola, satisfying the following equation: S = Kem [1] where S and e represent true stress and strain, K is a constant, and m is a coefficient evaluating the slope of the curve and designated therefore as the strain hardening coefficient. Hollomon² has reported that this coefficient is a function of the yield strength as effected by grain size in alpha brass, and the carbon content and heat treatment of steel. In the case of steel, the value of the proportionality constant is a function of the carbon content. It was further shown in that paper2 and also by Low and Prater -hat, if the power relation between stress and strain remains valid, the strain hardening coefficient m, is equal to the strain at the maximum or necking load. Thus, an added significant feature is that this coefficient may serve as an index of the capacity for deformation prior to localized necking and subsequent fracture, e.g. drawability. The constant K may be defined as the strength of the material at unit strain. Together the K constant and the m coefficient describe an alloy's physical properties as far as strength and ductility are concerned for a particular yield strength and, in the case of steel, a particular carbon content. The work of Lacy and Gensamer4 gives data on alloy ferrites from which very close estimates of the strength of ternary and higher iron alloys have been made. It was the purpose of this investigation to develop similar data for commercial copper base alpha solid solution alloys. Preparation of Specimens Commercial binary alloys of copper with aluminum, beryllium, cadmium, nickel, silicon, tin and zinc were investigated. In addition, laboratory castings were made of a 1 pct silicon alloy and a 2 pct aluminum alloy to complete these particular series. Two types of copper were used, oxygen free OFHC and tough pitch FC. The analyses of these alloys are shown in table I. Standard ASTM sheet tensile specimens were used to determine the usual physical properties of each alloy and to obtain stress data at strains from 0.0005 to 0.01. Small (1/4 in. x 3 in. x tk.) samples

Jan 1, 1951

By Alexander B. Morris

Studies such as the investigations into the solubility of gases in crude oil under various conditions, which have been carried on during the past three or four years, are very interesting from an academic point of view, but this consideration alone is hardly sufficient to warrant the large contributions from the industry necessary to maintain them. Some definite benefit to the industry as a whole should be forthcoming. The purpose of this paper is to direct the attention of company engineers, and company executives, to some of the ways in which the information gained from these studies can be made directly profitable. This work has two principal economic aspects. One affects the investment budget, and through it the financial requirements of the companies. The other affects operations, and through this course is reflected in current earnings. It will be shown that, as a direct result of the investigations into gas solubility, undertaken in the recent past by various investigators, it is now possible: 1. To determine more accurately the amount of reservoir oil originally present. 2. To obtain closer control on operating conditions, to effect more economical recovery. 3. To predict earlier and more dependably when and how much surface lifting equipment will be needed. 4. To reduce, or entirely avoid the very large investment in gasoline recovery equipment now frequently found necessary. 5. To control the gravity of the pipe-line oil so as to secure the greatest possible revenue from the products of the well. 6. To effect the recovery of a large amount of gasoline now wasted while the practicability of a gasoline recovery system is being decided. 7. To plan operations, by comparison with the history of old properties operated without this new information, so as to avoid the mistakes of ignorance made in the past. These points will be discussed in the following pages, though not necessarily in the order stated. There is so much overlapping of the points themselves, and of the data from which they have been drawn as conclusions, that to treat them in any particular order would require

Jan 1, 1935

By C. J. Fleisch, C. P. Clingerman

THE recent installation of a combination dust catcher, gas washer and precipitator at Carrie blast furnaces of the Homestead Steel Works has given very satisfactory results. The following description of the gas-cleaning installation is based on actual operating experience. When Carrie blast furnace No. 3 was rebuilt the decision was made to fine-clean all the gas produced by the furnace, because the management wanted fine-cleaned gas for fuel in the stoves and boilers. In order to keep the installation cost as low as possible, the gas-cleaning system was streamlined. All by-pass lines and goggle valves for bypass lines were eliminated from the system. A radical departure from the use of 8-in. tubes in the Cottrell-type precipitators was made by using 12-in. diameter tubes in a single compartment, the single compartment being divided into two units by a single partition wall in the top header. THE FURNACE PROPER A few of the characteristic points and dimensions of the furnace proper are: [Hearth diameter 26 ft. o in. Bosh diameter 29 ft. 1 3/4 in. Stock-line diameter 20 ft. o in. Large-bell diameter 114 ft. 8 in. Small-bell diameter 6 ft. 6 in. Height of furnace from center of iron notch to bottom of large bell, closed 94 ft. 4 in. Height of furnace from center of iron notch to main platform 105 ft. o in.] The furnace top is equipped with a McKee revolving distributor, the operation of which is electrically interlocked with the skips, bell hoists, and coke-weighing and charging apparatus through a Freyn automatic charging control. The gas leaves the furnace first through four offtakes, 5 ft. g in. in diameter, then through uptakes that are approximately 85 ft. high, which feed into a single down-comer that is 9 ft. in diameter. DUST CATCHER The primary dust catcher installed (Fig. I) may be described as a single-cone type. The inlet pipe at the top of the dust catcher is g ft. in diameter; it is flared to a conical shape as it extends down inside the dust-catcher shell, which is 35 ft. in diameter, 37 ft. high on the straight side, and has a conical top and bottom. The slope of the bottom is 50° with the horizontal. The cone-shaped pipe inside the dust-catcher shell is 42 ft. high and is 19 ft. 7 in. in diameter at its bottom lip where it releases the gas in-

Jan 1, 1943

By Harold Margolin, W. R. Hibbard, R. W. Fenn, H. P. Moore

Deformation lines, also called etch markings or strain markings, are non-effaceable lines developed in individual grains by etching a metal specimen which has been cold worked sufficiently to cause atomic non-conformity or slight orientation differences within the grains. Etching occurs more rapidly at these lines of high chemical reactivity to produce a result similar to that revealing grain boundaries. Wider etching effects forming bands have been found. They are believed to be bands of deformation lines which form areas of measurably different orientation from the crystal matrix. The crystallite rotations causing these bands have been shown by Barrett2 to contribute to deformation textures. Although deformation lines have been observed in many metals, the amount of deformation requireti for their appearance has been established only in general terms. Mathewson and Phillips3 observed the first appearance of deformation lines in cold-rolled alpha brass at about 20 pct reduction in thickness using the standard ammonium hydroxide hydrogen peroxide etchant. Price and Davidson4 noted defor- mation lines in common high brass after 26.5 pct reduction by cold rolling using the same etchant. Johnson6 observed dark thick forklike lines in 99.99 pct pure copper reduced 31.8 pct. Adcock6 observed deformation lines in 80-20 copper-nickel alloy rolled 50 pct. Samans7 found no deformation lines in alpha brass single crystals cold rolled 9.5 pct but they did appear after 25 pct reduction using ammonium hydroxide and hydrogen peroxide etchant. Barrett and Levenson8 observed deformation bands in drawn polycrystalline iron at very small reductions in area and noted that their initial appearance perhaps depends on grain size and other conditions. They reported deformation bands in a single crystal of iron reduced 6 pct by drawing. Brickg noted that deformation lines in 70-30 brass apparently associated with I I I I ) planes appeared after reductions of from 20-50 pct by cold rolling. Brick and Williamson10 noted that in single crystals of 70-30 alpha brass "as in polycrystalline brass, no deformation markings appeared until reductions exceeded 20 pct." Cook and Richards" reported that in Copper cold rolled less than about 50 Pet few strain markings were apparent but for higher reductions many strain markings appeared transverse to the rolled direction. In a review article Brick and Phillips12 noted that previous studies had not shown deformation lines in cold rolled alpha brass below 20 pet reduction and added that 4

Jan 1, 1949

By H. P. Moore, R. W. Fenn, Harold Margolin, W. R. Hibbard

Deformation lines, also called etch markings or strain markings, are non-effaceable lines developed in individual grains by etching a metal specimen which has been cold worked sufficiently to cause atomic non-conformity or slight orientation differences within the grains. Etching occurs more rapidly at these lines of high chemical reactivity to produce a result similar to that revealing grain boundaries. Wider etching effects forming bands have been found. They are believed to be bands of deformation lines which form areas of measurably different orientation from the crystal matrix. The crystallite rotations causing these bands have been shown by Barrett2 to contribute to deformation textures. Although deformation lines have been observed in many metals, the amount of deformation requireti for their appearance has been established only in general terms. Mathewson and Phillips3 observed the first appearance of deformation lines in cold-rolled alpha brass at about 20 pct reduction in thickness using the standard ammonium hydroxide hydrogen peroxide etchant. Price and Davidson4 noted defor- mation lines in common high brass after 26.5 pct reduction by cold rolling using the same etchant. Johnson6 observed dark thick forklike lines in 99.99 pct pure copper reduced 31.8 pct. Adcock6 observed deformation lines in 80-20 copper-nickel alloy rolled 50 pct. Samans7 found no deformation lines in alpha brass single crystals cold rolled 9.5 pct but they did appear after 25 pct reduction using ammonium hydroxide and hydrogen peroxide etchant. Barrett and Levenson8 observed deformation bands in drawn polycrystalline iron at very small reductions in area and noted that their initial appearance perhaps depends on grain size and other conditions. They reported deformation bands in a single crystal of iron reduced 6 pct by drawing. Brickg noted that deformation lines in 70-30 brass apparently associated with I I I I ) planes appeared after reductions of from 20-50 pct by cold rolling. Brick and Williamson10 noted that in single crystals of 70-30 alpha brass "as in polycrystalline brass, no deformation markings appeared until reductions exceeded 20 pct." Cook and Richards" reported that in Copper cold rolled less than about 50 Pet few strain markings were apparent but for higher reductions many strain markings appeared transverse to the rolled direction. In a review article Brick and Phillips12 noted that previous studies had not shown deformation lines in cold rolled alpha brass below 20 pet reduction and added that 4

Jan 1, 1949

By George Burrell

J. S. HALDANE, M. D., F. R. S., Oxford, England (communication to the Secretary?).-The valuable paper of Messrs. Burrell and Gauger is of special interest to me as, through the courtesy of the management, I had an opportunity of visiting the Portland mine, Cripple Creek, in 1911, in connection with the investigations on acclimatization to high altitudes, carried out on Pike's Peak, near Cripple Creek, by Professors Yandell, Henderson and Schneider, Dr. Douglas and myself.1 The analyses of one or two samples of the vitiated air were entirely confirmatory of those of the authors. A fatal accident owing to two men being lowered down a shaft filled with the gas had occurred in a neighboring mine just before our visit.

Jan 12, 1916

By R. W. Hertzberg, F. D. Lemkey, J. A. Ford

The technique of unidirectional solidification has been applied to the A1-AI3Ni and A1-CuAl2 ezltectic alloy systems; the controlled microstructure of A1-A3Ni consists of parallel A13Ni whiskers emhedded in an aluminum matrix while the Al-CuAl2, system solidifies as parallel alternate lamellae of aluminm and CuAl2. Mechanical tests (tension and flexure) have shown that the particle-matrix interface bond formed during unidirectional solidification allowes for efficient load transfer from the matrix to the reinforcing phase. Strength and fracture characterstics of the alloys were studied as a function of phase orientation; the tensile strength of controlled Al-Al3Ni samples was 43,000 psi (three times greater than that of as-cast specime~s). The strength of the Al-CIA2, cutectic was studied as a function of lamellae-flexure stress-axis orientation using a microbend apparatus. A twofold increase in outer fiber stress was observed as the lamellae were rotated from a position of no reinforcing (perpendicular to the stress axis) to one of maximum reinforcing (parallel to the stress axis), The brittle reinforcing constituent in each alloy (A13Ni and CuAl2) was observed to he the nucleating phase for fracture. It is to be concluded from this investigation that unidirectionally solidified eutectic alloys have a potential use as reinforcing coniposite) materials. In a recent review article, Chadwick1 has described the work of many investigators in the area of controlled solidification of binary eutectic alloys. Thus far, more than twenty eutectic alloys have been unidirectionally solidified to produce structures consisting of two phases in the form of alternating lamellae or as whiskers embedded within a continuous matrix; in either case, the phases are aligned parallel to the growth direction. In particular, Kraft and Albright2 have shown that the Al-CuA1, eutectic alloy exhibits a lamellar microstruc- ture as a result of unidirectional solidification while Lemkey, Hertzberg, and Ford3 have studied the A13Ni whisker-aluminum matrix morphology in the A1-A13Ni system. Whether these alloys could exhibit reinforcing behavior would have to depend upon the strength and volume fraction of the reinforcing phase (AI3Ni and CuA12) and the nature of the bond between the reinforcing phase and the matrix. Hertzberg and Kraft4 have shown that the interface bond between chromium whiskers and a copper matrix in unidirectionally solidified Cu-Cr is particularly good while Lemkey and Kraft5 have reported chromium-whisker tensile strengths in excess of 1,000,000 psi. However, with the chromium volume fraction being less than 2 pct, no reinforcing behavior was displayed by the Cu-Cr alloy.6 In view of the encouraging results concerning the good interfacial bond and high strength of the reinforcing phase in the Cu-Cr system and preliminary mechanical test data reported by Lemkey et al.3 for the A1-A13Ni system, the A1-CuA1, and A1-A13Ni eutectic alloys containing 50 and 10 vol pct, respectively, of the reinforcing phase give promise of possessing mechanical reinforcing behavior. Based on this premise, the objective of the investigation was to study the strength and fracture behavior exhibited by these anisotropic microstructures. EXPERIMENTAL PROCEDURE Controlled Solidification Procedure. An extensive description of the technique of unidirectional solidification has been presented elsewhere.' However, the pertinent details for each eutectic system studied are discussed below. Al-A13Ni System. Several master heats of this alloy were prepared by vacuum-induction melting in an A12O3crucible and casting in SiO2 mold or by induction melting in alumina crucibles under argon. The initial heats were prepared from 99.99 pct A1 and 99.99+ pct Ni, while later heats used 99.999+ pct A1 and 99.99+ pct Ni. Specimens of these master heats were unidirectionally solidified using induction and resistance heating sources and argon atmospheres at growth rates from 1.1 to 28.7 cm per hr. The thermal gradients in the liquid were controlled in the range of 26" to 36°C per cm for these runs. Al-CuA12 System. The master heat and controlled

Jan 1, 1965