By Aiyuan Ma, Kun Yang, Weiheng Chen, Jinhui Peng, Shiwei Li, Feng Xie, Libo Zhang

In this thesis, a new process of recovering zinc sulfide ores was developed. The novel synthetic coordination leaching process mainly included two steps: microwave assisted phase reconstruction and compound coordination leaching. By applying various techniques, such as chemical composition analysis, X-ray diffractometry (XRD) and Raman spectroscopy, it could be concluded that sulfide phases would directly oxidized to zinc oxides under the 500 ºC microwave roasting and adding 30% Na2O2. What’s more, zinc leaching rate reached to 61.16% within 2 hours. Compared to the current technologies, this procedure had the advantage of avoiding SO2 emission, high leaching efficiency, simple process, manipulate easily, and low cost, which could be expected tremendous application potentials.

Jan 1, 2016

By Melvin H. Miles

"Considerable research has been conducted on the anodic oxidation of methanol in fuel cells. The electrochemical reduction of carbon dioxide in aqueous solutions to form methanol is the same reaction in reverse, i.e. CO2 + 6 H+ + 6 e- ? CH3OH + H2O. The same catalysts and conditions may operate for both reaction directions. This carbon dioxide reduction reaction, however, must be able to compete with the electrochemical reduction of water to form hydrogen gas. Thermodynamically, the reduction of CO2 to form CH3OH is slightly more favorable than the reduction of water. The use of nearly neutral electrolytes rather than acidic electrolytes makes the reduction of CO2 kinetically more favorable. The thermodynamics of various reaction steps are presented. Similarities exist with the electrochemical reduction of CO2 and the green-plant photosynthesis process that converts CO2 to carbohydrates.IntroductionVirtually all of the oxygen in the earth’s atmosphere is of biological origin having been generated by green-plant photosynthesis from water and carbon dioxide [1]. The net reaction can be represented byCO2 + H2O ? O2 + [CH2O] (carbohydrates, etc.) (1)Chlorophyll and enzymes promote this reaction, and the energy required comes from sunlight. The actual photosynthesis process is a complex multistage reaction and requires 469 kJ mol-1 of energy supplied by the sun. Isotope tracer experiments using 18O have shown that both the oxygen atoms in the O2 molecule originate from H2O, whereas oxygen atoms in the carbohydrates come from CO2 [1]. The total amount of water on the earth is split by photosynthesis and reconstituted by respiration and combustion once every 2 million years or so. The photosynthetically generated oxygen gas temporarily enters the atmosphere and is recycled about once every 2000 years [1]. The carbon dioxide is partly recycled in the atmosphere and oceans after an average residence time of 300 years and is partly fixed by precipitation of CaCO3 and other carbonate minerals [1]."

Jan 1, 2008

By S. S. Babu, T. Hong, T. DebRoy, S. A. David

"Oxide inclusions form in welds because of deoxidation reactions in the weld pool. These inclusions control the weld microstructure development. Thermodynamic and kinetic calculation of oxidation reaction can describe inclusion characteristics such as number density, size, and composition. Experimental work has shown that fluid-flow velocity gradients in the weld pool can accelerate inclusion growth by collision and coalescence. Moreover, fluid flow in welds can transport inclusions to different temperature regions that may lead to repeated dissolution and growth of inclusions. These phenomena are being studied with the help of computational coupled heat transfer, fluid-flow, thermodynamic, and kinetic models. The results show that the inclusion formation in steel welds can be described as a function of the welding processes, process parameters, and steel composition.IntroductionThe relationship between inclusions and formation of a high-toughness phase, namely acicular ferrite in low-alloy steel welds, is well known (1-4). Past research has focused on maximizing acicular ferrite amount in welds by controlling welding processes, process variables, and welding consumable parameters. Research has shown that there is a complex interaction between inclusion characteristics, prior austenite grain size, and weld metal hardenability. In a low-alloy steel weld, the small addition of titanium lead to a change in the inclusion composition and resulted in a transition in the microstructure from bainitic to acicular ferrite [see Fig. I]. This in turn lead to the best combination of strength and toughness. This paper describes the inclusion formation in low-alloy steel welds."

Jan 1, 1999

By Rolando Campos

In August 1993, the operation of Refimet Chile's copper custom smelter commenced at La Negra, near Antofagasta in northern Chile. Design smelter throughput corresponded to 235 000 tonnes of concentrate, calcines and copper cements arising from suppliers in the north of the country to produce 90 000 t/y of blister copper. Refimet had initially gained experienced in building and operating leaching, roasting and a blast furnace facility at Rungue, near Santiago, followed by Roasting at La Negra. The initial smelter project was based on conventional reverb- smelting and Peirce-Smith converting and the majority of equipment was 'purchased second-hand and rehabilitated or modified. After only 3 years in production, the treatment capacity was significantly improved by introduction of technical improvements to the original plant operating scheme. Recently, the plant was further expanded to an annual smelting capacity in excess of 400 000 t/y feed, corresponding to around 160 000 t/y copper production. This expansion, referred to as Phase 2, was achieved by modification of the reverb to oxy-fuel firing, addition of a further (second-hand) acid plant, fire refining and anode casting facilities. Parallel development of concentrate injection into enlarged converters-also took place. Following successful commissioning of Phase 2 expansion, initial engineering studies for a third expansion phase have been completed. This aims to use leading technology based on bath smelting of bone-dry concentrates in a Continuous Reactor. This paper provides an overview of the relatively short plant history, its development and improvements together with operating indices achieved.

Jan 1, 1998

By Liyuan Chai, Bing Peng, Ji Peng, Di Yu

"Electric arc furnace (EAF) stainless steel dust has been classified as a hazardous waste by various government regulatory agencies as it releases heavy metals to environment. The solidification of EAF dust is to stabilize the hazardous components to the amorphous silica-alumina-based clays. The process of solidification is investigated and the softening temperatures of dust and additive clay mixtures are measured for economical thermal treatment. The results indicate that the mixture of dust and local clay with the ratio of 1:1 has the lowest softening temperature 1100 °C and it could pass the toxicity characteristics leaching procedure (TCLP) test for the environmental regulatory limits after thermally treated at softening temperature for 15 min. Major phases of thermal solidification product clinker are CaAl2Si2O8, (Fe, Cr)2O3, (Fe, Mg)(Cr, Al)2O4 and Al6Si2O13.IntroductionThe yield of stainless steels in China arrived to 10 million tons in 2006 and more than 0.2 million tons of stainless steel dust are produced annually. Approximately 1-2 wt.% of scrap charged to an electric arc furnace (EAF) enters the off-gases and then is converted into the dust and reported to the bag-house. The disposal or landfill of the dust becomes a serious environmental problem in China due to the increased production of stainless steels in recent years. The dust contains elements such as chromium (Cr), nickel (Ni), lead (Pb), zinc (Zn), cadmium (Cd) and their solubility in leaching media exceeds the environmental regulatory limits [1]. Even though easily feasible for low-grade MgO, it is not appropriate to stabilize the heavy metals from the heavily contaminated soils after the dust landfill [2]. Several dust treatment technologies have been developed and they can be divided into two types. One is to recover the metals from the dust [3, 4] and another is to stabilize hazardous components present in the dust [5, 6]. Recycling of the dust generated in EAF is a remediation option for cleaner production. Direct recycling of EAF stainless steel dust was developed to recover the metal value from the dust and protect the environment [7], but it was only suitable for the dust with high contents of Ni, Cr and Fe. As for the dust with low valuable metal content, thermal solidification is an appropriate choice for the dust treatment."

Jan 1, 2012

By Masayoshi Matswnoto

The Kosaka Smelter and Refinery produces copper and lead, and has a history of more than 100 years as a metallurgical department of Dowa?s Kosaka Mine. The Smelter treats complex sulfide concentrates which are difficult to smelt. Valuable metals are recovered using various processes developed by Kosaka Smelter and Refinery. Effluent waters from the smelter contain large quantities of heavy metals. This paper describes how Kosaka Smelter and Refinery recovers valuable metals from various effluent waters and handles overall waste waters in order to meet strict environmental standards.

Jan 1, 1993

By Markus Aspiala, Fiseha Tesfaye, Pekka Taskinen

In this paper, the standard thermodynamic properties of Ag3Sb and Ag6Sb intermetallic compounds have been studied by the solid state EMF-method, using Ag+ ion conducting β- alumina and AgI. The intermetallic compounds were synthesized from pure substances in evacuated silica ampoules and their formation were confirmed by the SEM-EDS analyses. The EMF measurements were made on electrochemical cells of the type [Ag | β-alumina | Ag-Sb] and [Ag | AgI | Ag-Sb]. The usage of β-alumina electrolyte, in this study, enabled thermodynamic measurements of the Ag-Sb-intermetallic compounds above 710 K, hitherto unreported. Based on the new experimental data, thermodynamic properties of the Ag-Sb-intermetallic compounds have been determined. The obtained experimental values have been compared with the available literature data.

Jan 1, 2015

By Anna Wasilkowska

The study concentrates on the effects exerted by microstructure, deformation history and uniaxial stress conditions (temperature, stress state, strain rate) on the mechanical properties offerritic TRIP-aided steels for automotive applications. In low-alloyed TRIP-steels it is quite difficult to separate the effect of the austenite to martensite phase transformation from the influence of the ferritic matrix contributing to the yield stress and uniform elongation. Investigation of transformation kinetics of retained austenite as a function of the deformation temperature show that using the parameter k to characterize the retained austenite stability allows to identify regious of different temperature sensitivity separated by a transition temperature of 10±5°C. The observed low strain-rate sensitivity of the flow stress is an intrinsic property of the ferritix matrix and points to defomtation governed by slip. The ultimate tensile strength is much stronger affected by temperature than the yield stress. The influence of the temperature on the elongation is complex, because of the heating of the specimens by 60-l20°C at moderate and high strain rates. The increase of the total strain can be understood in terms of thermal softening of the ferrite. On the other hand, the steep increase of the stress during dynamic testing is an effect of accommodated elastic and plastic strains in the matrix. The strain- hardening exponent is dependent on the conditions imposed during testing. The martensite transfomtation rate is lower and the critical stress for martensite nucleation is much higher under compression compared to tensile loading. In secondary tensile tests, the yield stress increases steeply, and the ultimate tensile strength and the total elongation depend linearly on the amount of pre-straining. The results confirm that in the range of 8=10-4 s-l the TRIP-effect governs room temperature plasticity. Keywords: TRIP-steels, mechanical properties, strain rate sensitivity, temperature sensitivity, austenite stability

Jan 1, 2003

By M. J. Walker

The lead .smelter at Cominco's operations at Trail, B.C. has been undergoing. a modernization program since 1986. In that year a contract agreement was reached with German-based Lurgi GmbH which allows Cominco to construct and operate a lead smelter using Lurgi's QSL process. Cominco Engineering Services Ltd. (CESL), a subsidiary of Cominco Ltd., was contracted to provide project management, engineering, procurement and construction management? services for the project. The new smelter replaces the existing sinter-blast furnace plant ?and will have a capacity of up to 1601000 tonnes per year of refined lead. This new smelting proc.ess results in significant operating cost reductions and major environmental .improvements. Start-up of the new plant is scheduled for the fall of 1989. The metallurgy and the operating parameters, important to the design of the new smelter, are described together with projected deportments of lead, zinc, silver and minor metals. A plant description, will be given for the following major areas that make up the modernization project: the pressure filter operation for the preparation of ,zinc leach residues feed material, the QSL reactor and boiler itself, together with its feed system and process gas treatment, and the drossing plant with a new continuous drossing furnace and oxygen softening and thallium removal. Slag from the QSL reactor will be treated in existing slag furnaces until a subsequent second phase of the modernization is completed in the 1990s.

Jan 1, 1990

By M. Z. Quadir, M. A. Islam, P. J. Hazell, G. J. Appleby-Thomas, J. P. Escobedo

The mechanical response of closed-cell aluminium metallic foams subjected to low and high strain-rate loading has been investigated. A set of quasi-static and dynamic (shock) compressive tests have been conducted on closed-cell aluminium foams (CYMAT) with densities of 0.50 and 0.30 g/cc. Post-mortem characterization via optical microscopy and electron backscatter diffraction (EBSD) was performed on pristine and deformed specimens to elucidate the dominant deformation mechanisms in these materials. The combination of these techniques allowed for the assessment of critical deformation parameters such as changes in cell geometry and morphology, as well as microstructural evolution and deformation of the aluminium cellular network. These findings aim to aid in the design and development of optimized material structures for impact and blast protection.

Jan 1, 2015

By Hua-qing Li

Electromagnetic stirring process effectively improves the casting quality of metals. In this paper, the physical simulation experiment, in which the molten copper is displaced by mercury, was designed. The factory test parameters were determined according the simulated data. The flow behavior of the mercury to be stirred as well as the relations between the microstructure of plate blanks and the current parameters were analyzed. With an appropriate electromagnetic stirring, the inverse segregation of tin for C51900 alloy plant blank reduces from 15 % ~ 30 % to about 5 %, and the proportion of equiaxed grain rises to larger than 30%.

Jan 1, 2009

By D. D. Harbuck

The U.S. Bureau of Mines recently identified a significant new source of scandium in an Oklahoma tantalum waste residue (approximately 0.24 pct Sc). Because scandium is a strategic and critical metal which the Department of Defense has classified for special consideration, the Bureau is researching methods of recovering scandium and associated metals from this and other process residues. A variety of operating parameters were evaluated to determine the best technique for recovering scandium. Testing showed that by sulfating the residue at temperatures as low as 150' C for reaction times as short as 0.5 hr, over 94 pct of the scandium converted to a water soluble form. Solvent extraction using DEHPA selectively recovered 100 pct of the scandium from the water leach solution.

Jan 1, 1992

By M. F. Chambers

Neodymium metal was electrowon from a molten-chloride electrolyte at 650° C using a molten-metal cathode. A 50 mol pct NdC13-50 mol pct KC1 mixture served as the electrolyte. Binary metal alloys of 'Mg with Zn and Mg with Cd were used as molten cathodes. Under the best conditions, current efficiencies were 90 pct with a Mg-Zn cathode and 80 pct with a Mg-Cd cathode. Vacuum distillation was performed at 1,100° C for 30 min under a vacuum of 10-3 to separate the cathode metals from the neodymium. Neodymium metal of 99.9+ pct purity was recovered from the Mg-Cd alloy cathode. Almost 2 pct zinc remained in the neodymium recovered from the Mg-Zn alloy.

Jan 1, 1989

By S. W. Ip

Over the years, the importance of surface and interfacial phenomena has been neglected by the copper-nickel industry. As a result, little data on the surface and interfacial tension of the Ni matte and slag system are available in the literature. In view of the scarcity of information in this area, the surface tensions of the Ni-Fe-S system together with the Ni-Fe-S and fayalite type slag system were measured using the sessile drop technique. Drop images were obtained by X-ray radiography. For the Ni-Fe-S system, the results showed that the surface tension of the matte increases with matte grade. The surface tension behavior with changing matte grade showed a slight negative deviation from ideality. This indicated that FeS is slightly surface active in the nickel matte system. Results also indicated that small increase in sulphur content in the matte can decrease the surface tension quite significantly. The measured surface tension of the Ni-Cu-S system showed a linear relationship with the Cu2S content in the matte. The surface tension decreased with Cu2S content. Interfacial tension measurements showed a similar trend. That is, interfacial tension increased with increasing matte grade. The presence of MgO (-1.5%) and A12O3 (-6%) in the slag does not affect the interfacial tension value. Effects of matte surface tension on phenomena such as entrainment of matte in slag and infiltration of matte into refractory pores are discussed. The calculated flotation coefficients indicated that flotation of nickel mattes cannot be avoided by changing the matte grade. Filming of matte on bubbles can occur below a matte grade of about 19% Ni3S2. As for infiltration, refractory bricks containing high Cr2O3 will be easily wetted by matte regardless of matte grade. Therefore, bricks containing high Cr2O3 can easily be infiltrated by liquid matte.

Jan 1, 1993

By R. Luo, R. V. Kumar

"The co-deposition of cobalt and nickel as a binary alloy has been studied by both cyclic voltammetry and long-period controlled-potential electrolysis. Cyclic voltammetry experiments showed that the cathodic current density for the mixed Co-Ni (Co-Ni=1:3) electrolyte is noticeably higher than that obtained on electrolyte containing single CO2+ or Ni2+ (II) salt of the same ionic strength. The onset potential observed for the mixed salts electrolyte was also less cathodic (negative) than that for the single metal salts, respectively. The effects of a number of operational and compositional parameters on the co-deposition of cobalt and nickel were studied. The parameters under investigation include cathode (deposition) potential, temperature, CI-/Sol ratio in the electrolyte, the amount of additives such as H3B03, and acidity of the electrolyte.Optimum operational conditions were established for the deposition of cobalt and nickel binary alloy. These results are discussed with respect to feasibility of reclaiming cobalt, nickel and chromium from mixed superalloy scraps by melt-refining (under nitrogen and/or ammonia), followed by electrorerining of cast anode for co-depositing Co/Ni and thermal decomposition of chromium nitride for recovering chromium metal."

Jan 1, 1997

By Matthew John M. Krane, Christopher J. Vreeman, J. David Schloz

"A continuum mixture model of the direct chill casting process is used to model the transport phenomena and solidification behavior in the Direct Chill casting of an Al - 6 wt% Cu billet using Wagstaffs AirslipTM process. The model, which includes the transport of free-floating solid particles, can simulate the effect of a grain refiner on macrosegregation and fluid flow. Numerical predictions of sump profiles and composition and temperature fields are presented. Two 45 cm diameter billets were cast under production conditions with and without grain refiner. Temperature and composition measurements and sump profiles are compared to the numerical results. The comparison shows excellent agreement for the grain refined case. It is believed that an incorrect model assumption prevents good agreement in the non-grain refined billet. IntroductionDirect chill casting is a semi-continuous process in which molten aluminum enters the top of a water-cooled mold, is cooled, and forms a solid ingot drawn out below (Figure l(b)). The molten aluminum begins to solidify due to the cooling effect of the mold wall. As the ingot is withdrawn from the bottom of the mold, water jets impinge on the surface, directly cooling the billet and forming a solid layer around a liquid melt, commonly referred to as the sump.A particular defect that occurs in a wide range of casting processes, including the direct chill (DC) casting of aluminum alloys, is macrosegregation, the uncontrolled redistribution of alloying elements on the scale of the ingot during solidification. Macrosegregation in DC cast ingots can produce non-uniform mechanical properties [l], which affects the behavior of the metal during downstream forming and heat treat operations."

Jan 1, 2001

By G. C. Yao

Iron and silicon impurities can form needle and branch shape intermetallie compounds in molten aluminum when there is no manganese. It is difficult to separate them from molten aluminum by electromagnetic separation. The Fe-Si-AI and Fe-Al intermetallic compounds were transformed into Mn-Fe-Si-Al and Mn-Fe-Al compounds by the addition of manganese into molten aluminum. In molten aluminum the morphology of these intermetallic compound particles is lumpish and spherical. Migration resistance of these impurity particles is small, which is beneficial to separation. FeSiMnA4 and FeMnAI6 are paramagnetic. These impurity particles can be moved by magnetic force and can be separated from the molten aluminum.

Jan 1, 2003

By D. Lambert

Process modeling for large deformation metal forming processes has been developed into a very successful tool in commercial applications during the last two decades. DEFOR.MTM is a well-known metal forming process simulation program used by many industrial and research institutions. Recent developments include the ability to model multiple deforming body behavior during multi-pass pack rolling and microstructure prediction during multi-pass shape rolling. This paper summarizes how DEFOR.MTM can be applied to a number of rolling processes and briefly describes preliminary work carried out using the ALE technique. Keywords: Simulation, Rolling, Pack, Shape, Microstructure, FEM, ALE, Tantalum

Jan 1, 2003

By Terry Gerritsen

Electrode control systems regulate power by physically positioning electrodes. Due to the size and weight of the electrodes, this is a slow process where power fluctuations of less than a few seconds are not fully corrected. Nickel laterite AC furnaces operating in high voltage, shielded arc mode typically incur frequent power variations of approximately +I- 20% around the power set point. To provide enhanced power control, Hatch has recently supplied, at commercial scale, a thyristor-switched reactance system called an SPLC. The SPLC incorporates predictive control software to operate furnaces at the maximum transformer rating by reducing the large power swings experienced without the SPLC. The resulting higher average power enables higher production, without increasing transformer or power plant capacity. A 60 MW production version of the SPLC has been commissioned on Falconbridge Dominicans's laterite nickel furnace, yielding excellent results with a 3 to I reduction in power fluctuations. Keywords: SPLC, AC Power Supply, Electric Furnace

Jan 1, 2004

By Valery Kaplan

Sulfur emission in the form of SO2 in flue gases is one of the most serious atmospheric pollutants associated with coal combustion and non-ferrous metals production. The carbonate eutectic method for removing SO2 from flue gases at 723–923 K was initially proposed in the 1970s but despite its great efficiency (SO2 concentration in the flue gas after purification reached 0.003 volume %), it could not be implemented by industry due to the complexity of the carbonate melt regeneration stage. Earlier we proposed a method suited to coal-firing power stations where the melt was regenerated using CO as a reducing agent. However, most metallurgical plants do not use coal and therefore lack a large source of CO. Here we propose a method for removing sulfur from the carbonate eutectic melt by purging it with natural gas or a natural gas/air mixture, which are available in the vast majority of metallurgical plants. This reaction leads to the reduction of sulfate to H2S gas that leaves the melt. The experiments we conducted show that nearly complete sulfur removal from the melt is possible at 823 K and that the reaction rate is sufficiently high for a large scale process. One can foresee that this carbonate melt-based SO2 removal technique may become a practical and economically attractive method for limiting sulfur emission to the atmosphere from non-ferrous metallurgical processing plants.