By V. Sheikhzadeh, M. Saghaeian, R. Hejazi, A. Abazarpoor

The research aimed to compare the chemical analysis (K, Na, Cl) of Iranian concentrate plants, which are the main source of materials corrosion in the pelletizing plants. Cl alongside alkaline elements (especially K) may cause corrosion and plug in the grate plates and other involved equipment. Therefore, it is tried in the processing plants to remove impurities from the concentrate to prevent potential problems in pelletizing and iron/steel making processes. Part of these impurities are existed in the nature of ores and others are sourced in the processing water. Various samples from the largest Iranian concentrate plants including Chadormalu, Gol-e-Gohar, Jalal-Abad and Sechahun were prepared to investigate the possibility of alkaline problems for each samples. The amount of Cl, K and Na of Chadormalu sample was obviously low and therefore no alkaline problem is expected. The Cl content of Gol-e-Gohar sample was high (980 ppm) while amount of K was less (0.008 Wt. %). Due to low content of K, most of Cl will release as Cl2 or HCl and so problems caused by KCl plugging would not be a problem. The amount of Cl in Sechahun case was nearly same as Jalal-Abad (400-600 ppm), higher than Chadormalu and less than Gol-e-Gohar samples. However, the K content was higher than all samples (0.04 Wt. %). Therefore, the amount of evaporated K would be 2-4 times more than other samples. Since the amount of Cl and K is simultaneously higher than usual iron ores, therefore alkaline problems may be a serious prevention factor for the continuous operation of this plant. In order to solve this problem some counter-measures is suggested and discussed including cleaning system, partial dust enriched with KCl removal and variation in the materials type of involved equipment.

Jan 1, 2018

By D. Govender

Theoretical flotation models suggest that there is a positive relationship between bubble-particle collision rates and turbulent kinetic energy dissipation. Fine particle flotation performance is generally enhanced by increased collision frequency and hence higher energy dissipation. Contrarily, increased turbulence in the rotor-stator region is related to higher detachment frequency of the coarser size range. Therefore, the optimal modes of recovery for the ?fine? and ?coarse? size classes are diametrically opposed. Industrial applications have previously confirmed that applying greater power to flotation slurries yields significant improvements in fine particle recovery. However, recovery of the coarser size class favors a different flotation environment. An improvement in the kinetics of the fine and coarse size classes, provided there is no adverse metallurgical influence on the intermediate size ranges, is obviously beneficial to the overall recovery response. Managing the local turbulent kinetic energy dissipation, and hence the power imparted to the slurry, offers the benefit of targeting the particle size ranges exhibiting slower kinetics. FLSmidth recently introduced the practical implementation of this concept. In principle, it decouples flotation regimes where fine and coarse particles exhibit preferential recovery. In the case of naturally aspirated machines (Wemco®), it is referred to as Hybrid Energy Flotation? and incorporates at least three phases: ? Standard flotation machines (standard energy input, rpm, rotor size/type) at the beginning of the row, where flotation is typically froth phase limited and operational, and set-up parameters have a limited influence on the recovery. ? Higher-powered flotation machines (high rpm, high power rotor size/type) at the end of the row to improve fine particle recovery. ? Lower-powered flotation machines (low rpm, low power rotor size/type) to enhance coarse particle recovery. In evaluating the effect of turbulent kinetic energy on flotation performance, the spatial distribution and its effect on size denominated recovery needs to be evaluated. The mean energy dissipation rate is a measure of the bulk energy input, but CFD-based models offer a more introspective view of flotation sub-processes. A CFD-based flotation model is used to highlight the effect of turbulent dissipation energy on attachment and detachment rates. Preferential collection zones for ?fine? and ?coarse? particles are predicted for both forced air and naturally aspirated machines. Keywords: CFD-based model, attachment, detachment, energy dissipation, hybrid energy flotation?, forced air, naturally aspirated

Sep 1, 2012

By A. Prokopiev

The biological stage of reclamation is the third final stage in remediation the damaged mining terrains, which is carried out following the completion of the mining technical stage. The biological stage of reclamation is carried out through restoration of the vegetation layer. The biological reclamation includes all activities related to the introduction into the terrain of vegetation, microorganisms, insects, and animals, with the acceleration of the succession and creating conditions for a sustainable ecosystem close to the natural one. It comprises of all anti erosion and other activities such as the preparation of the land for growing agricultural crops, sowing grass seeds, planting seedlings, amelioration of the soil and further care for the vegetation until its final place on the land. Mineral and organic-mineral ameliorants for biological reclamation were studied. The basic mineral ameliorant is Bulgarian natural zeolites. The zeolitic-rich tuff samples provided from Golobradovo deposit was characterized by their chemical and mineralogical composition and ion exchange properties and X ray analysis. The average content of clinoptilolite was found to be more than 80%. The materials had ion exchange capacity (NH4+) varying from 100 to 110 meq/100g. Chemical modifications of natural clinoptilolites were made in order to form active phases of nitrogen, phosphorus, potassium, and microelements. Slow-acting mineral ameliorant was developed. Organic-zeolite substrate for biological reclamation was developed. This new product is a mechanical mixture of organo-matter and modified zeolites. Agro-chemical parameters of new ameliorants were determined. The substrates including studied overburden dump soil and mineral or organo-mineral ameliorants are produced. The grass growth test was performed. Keywords: biological reclamation, ameliorants, damaged mining terrains

Sep 1, 2012

By H. Sarvamangala

Selective separation of alumina, silica, calcite and apatite from hematite was achieved through microbiologically induced flotation and flocculation in presence of bacteria (B.subtilis) and that of hematite from apatite after interaction with yeast (Saccharomyces cerevisiae). Bacterial and yeast metabolites containing extracellular proteins were characterized from mineral-grown cell free extract. Bacteria and yeast can adhere to mineral surfaces and influence subsequent separation of the minerals. Bacteria functioned as a stronger depressant for hematite, while yeast cells depressed apatite at neutral pH. Selective affinity of the bacterial and yeast cells towards the mineral surface was observed through adsorption studies. Extracellular proteins (EP) were isolated from B.subtilis and yeast. The protein profile of the EP of bacterial and yeast cells grown in presence and absence of minerals was studied. This study has demonstrated the utility and amenability of microbially-induced mineral beneficiation of iron ores through bacterial and yeast cells and their metabolic by products.

Sep 1, 2012

By Zhu Yangge, Zheng Guibing, Hu Xiaoxing

"Because of the similar crystal structure and surface properties, it is very difficult to realize the efficient separation of magnesite and dolomite by flotation, which is the main reason restricting the utilization of magnesite resources with dolomite symbiotic. To deal with a magnesite resources with high content of calcium impurity in northwest China, a novel decalcification technology by combining flotation with leaching is proposed in this paper. In flotation process, a novel flotation collector with good efficiency and low temperature resistance was developed, and the depression effect of sodium hexametaphosphate was investigated. In leaching process, the leaching rate difference of calcium and magnesium was observed. By industrial test, from the magnesite ore with MgO content of 43.96%,the grade and recovery of obtained concentrate ( calculated by MgO) are 47.28% and 67.68% respectively, at the same time, CaO content decreases from 3.91% to 0.30%, which means that more than 95% of CaO impurity is removed.INTRODUCTIONMagnesite is one of the main raw materials for the production of refractory materials, and it is widely used in metallurgy, chemicals, ceramic, construction and other industries. China is the most important supplier of highquality magnesite resources, accounting for about 60-70% of the world's identified supply of magnesite products is provide by China (Jewell, 2014). In recent years, high-quality magnesite ores can be directly used are going to run out in China, and the utilization of magnesite resources with high impurity content have drawn more attention.The main purpose of purification for magnesite is to remove SiO2 and CaO impurities which affects the strength of the refractory material. Flotation is the commonly used method to remove impurities in magnesite ore. Reverse flotation with cationic collector is usually adopted to remove silicon containing impurities, and a great deal of literature has been reported (Santana A. N. and Peres A. E. C., 2001; Wang and Sun, 2008; Zhu et al, 2014; Wu et al, 2015; Ivan B. et al, 2017). But when the major gangue component is dolomite, it is very difficult to realize the efficient separation due to the similar crystal structure and surface properties between magnesite and dolomite. To solve this problem, researches have studied the surface properties of magnesite and dolomite, such as wettability, electrical property, solubility and solution chemistry (Nermin and Nurgul, 2006; Nermin 2006; Ozbek and Abali, 1999; Lacin et al, 2005; Bayrak et al, 2006; Bakan et al, 2006; Chen G. and Tao D., 2004), but the commonly studied direct flotation using oleic acid as collector is still hard to receive an ideal effect."

Jan 1, 2018

By Chen Jianhua, Shen Zhenchang, Zhang Ming, Chen Feifei

"With flotation cells scale-up, the performance of flotation cells is increasingly variated for short-coming and dead zones existing. The residence time distribution which shows the movement of tracers can assess the unexpected flows such as short circuit and dead zone in a flotation cell. In this paper, the residence time distribution of pilot flotation cell is investigated with CFD simulation. Based on the theoretical model, the short-coming probability and dead zone probability are quantitative. The ideal average residence time is similar with the actual average residence time. The mixing effect of the flotation cell approaches the ideal continuous stirred tank reactor. The operating parameters such as speed and feed velocity have complicated influence on residence time distribution. The research would be helpful to understanding flow in flotation cell and improving performances of flotation cell.INTRODUCTIONFroth flotation is a method which purifies minerals according to difference of physical and chemical surface characters of different mineral particles (Shen, Z., Chen J, 2012). Flotation cell is a key equipment for froth flotation method. The flotation cell performances have great influences on flotation index.It is difficult to evaluate flotation cell how to improve flotation procedure to complexity.The main flotation cell performances are aeration volume, air dispersion, solid suspension and residence time distribution, etc (Shen, Z., Lu, S., 2008). Residence time distribution is an important fluid hydrodynamics which could reveal the flow of pulp, mixing of particles and air bubbles. In the flotation cell, the ideal average residence time of pulp could obtain easily. But the fluid differential units would be different flow paths. The residence time of the fluid differential units is variation and would be longer or less than the average residence time. The residence time distribution would reveal the mixing effect and predict the not ideal flow in the flotation cell such as shorting cutting, dead zone, etc. As we know, the shorting cutting and dead zone would be decreased the real flotation time and it is disadvantage to better flotation effect, especially for large flotation cell. It is impossible to eliminate the not ideal flow totally. It is very important to reveal and decrease the shorting cutting and dead zone probability in the flotation cell."

Jan 1, 2018

By Chen Jianhua, Shen Zhenchang, Zhang Ming, Chen Feifei

"With flotation cells scale-up, the performance of flotation cells is increasingly variated for short-coming and dead zones existing. The residence time distribution which shows the movement of tracers can assess the unexpected flows such as short circuit and dead zone in a flotation cell. In this paper, the residence time distribution of pilot flotation cell is investigated with CFD simulation. Based on the theoretical model, the short-coming probability and dead zone probability are quantitative. The ideal average residence time is similar with the actual average residence time. The mixing effect of the flotation cell approaches the ideal continuous stirred tank reactor. The operating parameters such as speed and feed velocity have complicated influence on residence time distribution. The research would be helpful to understanding flow in flotation cell and improving performances of flotation cell.INTRODUCTION Froth flotation is a method which purifies minerals according to difference of physical and chemical surface characters of different mineral particles (Shen, Z., Chen J, 2012). Flotation cell is a key equipment for froth flotation method. The flotation cell performances have great influences on flotation index.It is difficult to evaluate flotation cell how to improve flotation procedure to complexity. The main flotation cell performances are aeration volume, air dispersion, solid suspension and residence time distribution, etc (Shen, Z., Lu, S., 2008). Residence time distribution is an important fluid hydrodynamics which could reveal the flow of pulp, mixing of particles and air bubbles. In the flotation cell, the ideal average residence time of pulp could obtain easily. But the fluid differential units would be different flow paths. The residence time of the fluid differential units is variation and would be longer or less than the average residence time. The residence time distribution would reveal the mixing effect and predict the not ideal flow in the flotation cell such as shorting cutting, dead zone, etc. As we know, the shorting cutting and dead zone would be decreased the real flotation time and it is disadvantage to better flotation effect, especially for large flotation cell. It is impossible to eliminate the not ideal flow totally. It is very important to reveal and decrease the shorting cutting and dead zone probability in the flotation cell."

Jan 1, 2018

By V. A. Chanturiya

The application of High-Power Nanosecond Electromagnetic Pulses (HPEMP) irradiation in dressing of resistant gold- containing ores appears attractive as this technique provides for a significant increase in precious metal recovery (30-80% for gold and 20-50% for silver), therewith helping reduce both energy consumption and the cost of products. The prospects for applying pulsed power technologies in the mineral processing in order to increase the contrast between the flotation properties of raw minerals dictate the need to perform special studies of the effect of HPEMP on the structural state, phase composition, and physical and chemical properties of surfaces of sulfide minerals as the main carriers of precious metals. This study deals with plausible mechanisms of the micro- and nanophases formation on the surfaces of sulfide minerals under the effect of high-power nanosecond electromagnetic pulses (HPEMP) with high electric field strength ~107 V/m. This paper discusses reasons for the changing of flotation behavior of natural pyrite and arsenopyrite during the pulsed-power treatment. It was concluded that HPEMP treatment may be regarded as a tool to change the surface composition and sorption ability of collector (xanthate) onto mineral surface, and, therefore, it allows to control the hydrophobic-hydrophilic surface balance. Single mineral flotation tests have been shown the significant increasing of the pyrite recovery while the arsenopyrite was depressed. The results of gold containing pyrite (pyrrhotite)-arsenopyrite ore flotation in batch approve the decreasing of arsenic recovery in sulfide concentrate. Keywords: pyrite, arsenopyrite, high power nanosecond pulses, activation, selective flotation

Sep 1, 2012

By S. Z. Khan, Veerendra Singh, Y. Rama Murthy, S. Prasad, Sunil Kumar Tripathy, Gajanan Kapure

"In this study, a low-grade ferruginous low-grade chromite ore was subjected to reduction roasting by using conventional heating as well as microwave heating. Sukinda chromite ore deposit contains majorly iron-bearing minerals as gangue phase. The magnetic susceptibility of these minerals enhances effectively after reduction roasting. Alteration of crystalline structure and magnetic property of these metals enables separation of low-grade ore by using magnetic separation. Conventional roasting studies by varying the temperature, time of reduction and reductant dosage were changed for low-grade ferruginous chromite ore. Similarly, microwave power, retention/exposure time and reductant dosage varied for reduction roasting studies under microwave environment. It is found that low-grade ferruginous chromite ore can be upgraded by reduction roasting and 61.2% Cr2O3 was recovered with a chromium-to-iron ratio of 1.93 from feed chromium-to-iron ratio of 1. Microwave reduction roasting studies resulted in upgradation of chromium-to-iron ratio to 1.73 with a recovery of 21% Cr2O3.INTRODUCTION The chromite ore occurs as a spinel containing oxides of chromium, iron, magnesium and aluminium. Most of the Indian chromite deposits are of ferruginous (rich in iron content) which indicates the abundance of ferruginous gangue minerals along with chromite. The primary use of chromite ore is towards the production of ferrochrome alloys. Chromite ores with less than 40% Cr2O3 and the chromium-to-iron ratio (Cr-to-Fe ratio) <1.8 is considered to be unsuitable for the smelting process (Tripathy et al. 2012, Tripathy et al. 2012a). A considerable amount of low-grade chromite ore and overburden excavated during chromite mining is getting accumulated every year, causing a threat to the environment. Its disposal poses a significant challenge and, hence, the beneficiation of low-grade chromite ore and its utilisation has been attracting a lot of attention. Different physical method of beneficiation methods is generally employed for the improvement of the Cr-to-Fe ratio (Tripathy et al. 2012, Murthy et al. 2011, Tripathy et al. 2012a, Tripathy et al. 2013, Tripathy et al. 2016, Tripathy et al. 2017, Tripathy et al. 2017a). It is observed that the enrichment of the chromite ore is carried out by using gravity and in some places by magnetic separation. However, the enrichment of Cr-to-Fe ratio from low-grade ferruginous chromite ore is difficult by using the above-mentioned beneficiation methods due to the presence of near gravity and near-magnetic susceptibility minerals along with chromite. However, an alternative beneficiation method is needed to explore for the beneficiation of such mineral deposits. Reduction roasting followed by magnetic separation is an alternative option for the separation of these types of ores which is widely reported for the iron and manganese ore (Li, et al., 2010; Chun, et al., 2014, Rath et al., 2018). These processes are majorly focussed on differentiating the magnetic susceptibility between minerals and subsequent separation by using magnetic field. The main advantage of such method is dry process option along with the pre-processed product for the costly smelting process. Also, the roasting of minerals in a microwave environment is also an active research topic in the recent time. So, the amenability of the separation feature of the roasting process by using conventional heating as well as microwave heating can be can be studied for the low grade ferruginous chromite ores."

Jan 1, 2018

By Nicolás Luis, Qi Liu, Gonzalo Montes-Atenas

"The prediction of froth flotation performance is still an unresolved topic. Classic industrial models based on particle size, elemental and mineralogical information provides recovery results with deviations that may become significant. One possible reason for this deviation may be the fact that the current liberation analysis provided by electron microscope based techniques does not take into account the outmost surface layer composition of liberated particles. In order to complete the description provided by the liberation analysis, other spectroscopy techniques measuring the extreme surface of the minerals can be tested. For instance, X-ray Photoelectron Spectroscopy (XPS) is a technique which measures the first tens of nanometers providing elemental composition over the particle surface and allows resolving the elemental associations present at the surface sample. However, this information needs to be statistically robust, reproducible and most importantly representative of what is occurring in the process. The aim of this research work is to develop a statistical model based on particle population to evaluate the feasibility of turning the XPS technique into a metallurgical tool. The model consists of classic statistical population arranged in a bed of heterogeneous particles with a known grade and mineral liberation. The simulations showed that the XPS results statistically followed a well-defined pattern. The statistical results were confronted with pilot plant results obtained from a rougher bank when processing a copper sulfide ore from a Chilean mine site. It was observed that the probability function distribution was in agreement with the experimental data. Further analysis on how the XPS results provide valuable information improve the computation of froth flotation recoveries is also discussed."

Jan 1, 2014

By Stephen J. Harker, John Knights, Randolph A. Pax, Glen A. Stewart

"Mineral samples were obtained from different stages of a mineral processing circuit used to extract the copper and gold rich mineralogical phases. The aim of this work is to characterise the quality of the samples at different stages of processing. The samples were taken of the head grade, tailings, cyclone overflow and the final concentrate.Characterisation of the samples was determined using Cu-Ka X-ray powder diffraction and Fe57 Mossbauer spectroscopy. These measurements will be presented and discussed in terms of the enrichment of the ore, showing the removal of magnetite and quartz through the processing, the final concentrate being rich in chalcopyrite and pyrite. This data also shows the utility of Mossbauer spectroscopy to provide mineralogical phase information directly.Mossbauer spectroscopy is a tool to determine the material phases of a sample. It is a nuclear based technique which measures the amount of attenuation of a narrow Doppler shifted source energy as it passes through a sample. The attenuation depends on the amount of resonantly absorbing material in the nuclear radiation path from the source to the detector. Synchronous detection of the doppler shifting velocity and the nuclear radiation count gives a Mossbauer spectrum. By convention, the energy axis of the Mossbauer spectrum is displayed in units of velocity.Figure 1 shows Mossbauer spectra obtained for a sequence of samples throughout a processing plant. These spectra show the removal of magnetite and the concentration of chalcopyrite and pyrite. Optical microscopy results indicated a significant component of bornite not witnessed with Mossbauer spectroscopy. Closer examination showed that optical microscopy assays over estimate the bornite component."

Jan 1, 2003

By Sudhir Srivastava

India hosts a wide range of globally significant mineral resources, including four fuel minerals; 11 metallic minerals; 22 minor minerals and 52 non-metallic minerals. The country ranks among world?s top five nations for its commodity reserves of coal and iron ore. Interestingly, only small part of country&apos;s landmass has been explored that provides opportunity for future substantial mineral discoveries. India plans to double infrastructure investments to US$ 1trillion. Despite the challenges in infrastructure project implementation, mining sector remains a key driver of demand growth for commodities in the years to come with a good prospect to grow in future.

Sep 1, 2012

By K. D. Mehta

Copper concentrate containing complex sulphides of Cu-Ni with 14.13% Cu and 10.04% Ni besides impurities such as 0.33% Co and 0.71% Mo, is not acceptable to the copper smelters due to the smelting problems. Selective bioleaching of nickel from the concentrate can be considered an an option to make it suitable for copper smelter. Effect of elemental sulphur and pyrite on the bioleaching of Ni and Co has been investigated using a mixed culture of Acidithiobacillus ferrooxidans (A.f.) and Acidithiobacillus thiooxidans (A.t.). Parameters such as pH, temperature, particles, size etc. were optimised to understand the role of additives in the bioleaching. With 2% S at 308K, 2.0 pH, 5% pulp density and 200µm size particles while shaking at 100 rpm, 79% Ni, 41% Co and 5% Cu were bioleached as compared to the leaching of 81% Ni and 45% Co in presence of 10 wt% pyrite in 60 days; 27% Ni, 24% Co and 4% Cu were recovered in sterile experiment. The selective dissolution of nickel and cobalt as compared to copper may be explained by galvanic interaction between chalcopyrite: pentlandite / pyrrhotite. Bioleaching was facilitated by strong oxidizing conditions due to higher Fe3+/Fe2+ ratio/redox potential (ESCE) as a result of improved interaction of minerals through biooxidation of sulphur and accelerated galvanic interaction by pyrite. The mechanism of selective leaching of Ni and Co was established by XRD phase identification.

Sep 1, 2012

By Mingfei He, Yude Gao

"The leaching kinetics was studied during leaching of indium-bearing zinc oxide to recover indium. The effects of temperature, sulfuric acidity, particle size, stirring rate on dissolution rate of indium were investigated. Results showed that the leaching process was controlled by chemical reaction at the condition of low sulfuric acid concentration. While the acidity increased to 1.8 mol/L, the leaching process was transformed into an internal diffusion controlling model . The corresponding value of reaction orders under low acidity and high acidity were 1.194, 0.156, respectively. Further calculation results indicated that the leaching reaction activation energy was only 10.97kJ/mol under the condition of high acid. The leaching rate constant was inversely proportional to the square of particle size, while the effect of stirring rate on leaching process was insignificant. The leaching process can be enhanced by increasing the temperature and acid concentration, as well as the decrease of particle size. And a final kinetics eqution was proposed. KEYWORDS Indium, extration, leaching kinetics, zinc oxide INTRODUCTION Indium[1,2] plays an important role in many aspects of living and industrial production owning to its special physical and chemical properties. The reserve of indium is rare on the earth, and most of indium is distributed in some other minerals[3]. Some researchers [4,5] have proposed that indium mainly substitutes for the lattice of other minerals by isomorphous. Therefore, the extraction of indium should take into account of the production technologies of those minerals to comprehensively recover the valuable metals."

Jan 1, 2018

By E. Vahidi

In this study, a hydrometallurgical treatment involving solvent extraction of zinc using D2EHPA (di-2-ethylhexyl phosphoric acid) has been investigated to recover zinc from an industrial zinc leach residue. The residue was leached with sulfuric acid producing leach liquor which was subjected to solvent extraction for enrichment of zinc and removal of impurities. Operating variables for the zinc extraction process, such as pH of the mixed solution (0.5~5.0), concentration of D2EHPA (5%~40%, w/w), temperature (25~60°?C), A/O volumetric phase ratio (1/2~4/1), concentration of tri-butyl phosphate (TBP) as modifier (3%~7%, w/w), concentration of NaR2RSOR4R in aqueous phase (0.05M, 0.1M, 0.2M) were also studied. Practically all zinc was extracted from the aqueous solution at pH 2.5 with 20% w/w D2EHPA in kerosene. At this operating condition, zinc could be extracted at one theoretical stage at A/O phase ratio of 1/1, as calculated by the McCabe-Thiele method.

Jan 1, 2014

By A. Kuriwada

Dolomite is a mineral, which consists of CaCO3 and MgCO3. In this work, a series of experiments were carried out in order to adsorb boron from a boron-containing solution using a calcinated dolomite sample, and then to desorb it from the loaded adsorbent. A particular modification on the surface of dolomite was observed when it was thermally treated at certain temperature, ranging from 750 oC to 1050 oC; in turn, it is the specific surface was increased. In other words, the experimental results suggested that the calcinated dolomite exhibited a high adsorption capacity for boron, indicating its effectiveness in effectively adsorbing boron from drinking water or wastewater.

Sep 1, 2012

By Y. D. Gao

A new technique has been developed for comprehensively recovering tantalum niobium tungsten ore by adoption of stage grinding, stage separation, combination of flotation and gravity separation, gravity separation for coarse particles, flotation for fine ones, combination of ore-dressing and hydrometallurgy. The new type and high efficiency combinative collector mainly composed of benzyl hydroxamic acid is firstly used to treat tantalum niobium and tungsten slime, besides the new type equipment for gravitational separation ?YTF-C shaking table for fine particles is adopted to treat flotation rough concentrate, hence having notably enhanced both recovery and concentrate grade of fine tantalum niobium and tungsten minerals. The commercial test obtains the tantalum concentrate assaying Ta2O5 31.98% with recovery 43.44% and tungsten product assaying WO3 89.40% with recovery 76.02%. The developed technique provides a reliable approach and an effective way for comprehensive utilization of lean fine complex refractory tantalum niobium tungsten ore resource.

Jan 1, 2014

By Masoud Askari, Ahmad Rafizadeh, Shahamat Rostami, Mohammad Qaredaqi

Gole - Gohar Iron ore mines located in Sirjan, Southeast of Iran, have more than 1 billion Iron ore deposit and this area comprises 45 % of Iran Iron reservoirs. The aim of Wet tailing processing line is recovering Hematite ore from wet tailing of Gole - Gohar iron ore processing plant. The Investigations of Hematite recovery plant showed that the recovery of Iron ore to concentrate in Wet Tailing Processing (WTP) line is very lower than that has been predicted, sampling, and designing of the process parameters are not accurate and designed magnetic field intensity is not reasonable for the recovery of Iron in form of Hematite in this line feed. Applying of MIMS in WTP separator and changes in circuit caused in overwhelming increase of Fe recovery, from 11 to 40%. Although recovery of WTP line was improved, but low recovery of this processing line and high content of Hematite ore in WTP tailing, made applying Wet High Intensity Magnetic separators unavoidable. Two kinds of WHIMS have tested for processing of WTP line tailing. Results showed that traditional Jones separator with grooved plate matrix, is more suitable to achieve a better quality of concentrate compared to Slon® separator.

Jan 1, 2014

By A. Saramak

"The paper focuses on problems of atmospheric pollution by the dusts, produced during the course of crushing and grinding processes, and the main objective of investigative programme is an assessment of emission of particulate pollutants for following crushing devices operated in plant scale: impactors, cone and jaw crushers. All crushers operate in aggregate production plants in Poland. In the first stage of investigations there were determined dust emission levels and supporting characteristics for all crushers under investigation. Then there were introduced indices that allow for comparative analysis in terms of dust emission, for devices with different energy consumptions and comminution ratio. It appeared that crushers with high the overall dust emission do not always achieved unfavorable dust emission per comminution ratio or energy consumption. The introduced indices proved their usefulness, because they helped to carry out a comparative analysis among crushers, operating under different technological conditions. It is also easier to assess environmental impact of individual crushing devices, under analysis. Results of investigations also show that environmental impact of different types of crushers is diverse and it is difficult to compare dust emissions of various types of crushers without taking into account technological aspects (like throughput, comminution ratio, energy consumption, and others) of their operations.INTRODUCTION Mineral processing of raw material is a complex process, involving in general operations of size reductions and separation. Depending on the type of specific raw material, the technological circuit may include operations of comminution and size classification. This is a typical circuit for aggregate production. In ore treatment industry the process in much more complicated and include also a metallurgical treatment of ore concentrate – the final product from processing plant stage.In general, regardless the type of raw material, operations of size reduction are present in each technological circuit of mineral processing. Operations of crushing and grinding are an integral part of processing technology, because they play a crucial role in effective treatment of mineral raw materials (Gawenda 2013). Their duty is to liberate the useful minerals from the gangue in ore treatment industry, or to produce the material with the required particle size in case of aggregate processing. Crushing and grinding operations are of a high negative impact on environment and humans. They consume great amounts of energy, what indirectly contributes to higher emission of carbon dioxide CO2. Apart from energy, crushing and grinding device consume significant amount of steel and other metals and alloys due to high wear of working parts and grinding media. This is also of negative environmental impact due to emissions of additional amounts of CO2 in production of steel and other metals required as spare parts for comminution devices."

Jan 1, 2018

By A. F. Usov

A potential of electric pulse disintegration in benification used for primary deposits ores containing precious metals is shown. Of special significance is that PGM and gold grains, being highly plastic, are easily liberated and are not smeared on the disintegrated rock fragments surface. It al-lows gravity separation, which is less expensive and more efficient, to be used instead of chemical processing, which is expensive and environmentally faulty.

Jan 1, 2014