Search Documents

By R. N. O'Brien, E. Peters

"It has been discovered that copper concentrates can be leached in strong (40-60%) sulfuric acid with nitric acid, or with oxygen if nitric acid is present as a catalyst. Chalcopyrite is rapidly decomposed at temperatures well below the boiling temperature of the lixiviant (-150 C.) and the resulting copper and ferric salts are precipitated as CuS04.H20 and FeH(S04)z.4H20. Other metal sulfides such as zinc, lead, nickel, etc. are also converted to sulfates that are nearly insoluble. Sulfur is partially converted to elemental and partially to sulfuric acid. Reduction products of nitric acid can be recovered from the distillate with good recovery. Conversion of as-received copper concentrates is largely complete in about 1 hour. Introduction9 molar sulfuric acid is an unusual hydrometallurgical lixiviant: it has a boiling point of about 150 C. and a low solubility for base metal sulfates. Below about 6 molar acid, the boiling point falls below 120 C. and yields much higher sulfate salt solubility, while above 12 or 13 molar acid and at higher temperature sulfuric acid becomes an oxidizing agent, yielding gaseous S02' Thus, sulfuric acid within this range of concentration is capable of acting well above the temperature of boiling water without requiring autoclave conditions, and if typical oxidative leaching conditions are applied to suspended mineral sulfide concentrates, it is possible to obtain a conversion of these sulfides into 'crystalline sulfates. Thereafter, the sulfates can be separated by filtration or by solid - bowl centrifuge and the solution can be recirculated to the reactor vessel. Meanwhile, the solid sulfates can be treated in a typical hydrometallurgical circuit, i.e., dissolved in a return stream that is essentially water, separated from each other by, for example, solvent extraction, and recovered as metals by electrowinning."

Jan 1, 1997

By Jr. Napolitano, Jr. Sanders

"Morphological evolution of a dendritic growth front in a binary alloy is simulated using a cellular automaton approach to establish the feasibility of modeling such growth with a local rule-based scheme. The motivation for this work is derived from the need to predict the development of solidification structures within real components of complex geometry, where significant constraint of the thermal and solutal fields may exist. Such cases present complex boundaries and large domain sizes, which may preclude the effective use of more conventional methods. In this work, a model is presented which couples a two-dimensional alternate-direction-implicit finite-difference diffusion solution with a cellular automaton growth algorithm to simulate morphological evolution in alloys solidifying under directional growth conditions. Temperature, composition, and interface curvature are incorporated into a local growth potential which is used by the automaton, allowing the interface to evolve. Alloy solidification is simulated over a range of experimental conditions, producing various structures. Issues addressed include morphological instability, primary spacing selection, interface curvature, microsegregation, and tip conditions.IntroductionThe development of dendritic structure plays an essential role in alloy solidification. Virtually every microstructural feature, within a cast alloy component, is related to the interface morphology present during solidification. Conventional solidification theory, describing dendrite tip kinetics and mushy zone phenomena, provides a means for estimating overall microstructural parameters for an alloy solidified under steady-state conditions. Microstructural prediction for actual components, which are finite in size and complex in geometry, requires a description of the evolution of the interface morphology under transient conditions and geometrical constraint and an understanding of how the structure propagates through the mold. Any useful simulation tool must be equipped to handle these circumstances within the limits of computational feasibility."

Jan 1, 1998

By Roderick 1. L. Guthrie, Mei Li

"A mathematical model was developed to study the role of orifice shape in the detection of inclusions in LiMCA (Liquid Metal .cleanliness Analyzer) system. The fluid flow field within the ESZ was obtained by solving the Navier-Stokes equations. The trajectories of entrained particles were calculated using the equations for motion of particles. A numerical study of the effect of orifice shape on signal shape generated by inclusions passing through orifice showed that the signals in a parabolic orifice are gaussian in shape, while those in a cylindrical orifice are trapezoidal in shape. This signal shape difference needs to be taken into account when performing particle discrimination. Orifice shape influences also pass-through fraction of inclusions. Finally, a study of the orifice shape on critical conditioning currents suggested that as the polynominal coefficient of the parabolic orifice increases, the critical conditioning current, which is also the maximum operating current, decreases dramatically. These critical conditioning currents also increase as the fluid flow velocity within the ESZ increases. IntroductionThe presence of non-metallic inclusions in metals often leads to impaired mechanical properties such as a reduction in fatigue strength, and to processing problems such as tear-offs in deep drawing and increased breakage rates in wire drawing operations. Similarly, inclusions cause a variety of surface defects in rolled or extruded products.Prior to the development of the LiMCA system (1) at McGill University in the early 1980's, it was not possible to measure inclusions, in situ, in liquid metals. Compared with other techniques, such as sedimentation, filtration and metallography, which require considerable amounts of labor and time, the LiMCA method has the advantage of providing not only information on the volume concentration of inclusions, but also on the size distribution of inclusions immediately and quantitatively."

Jan 1, 2001

By K. Fukushima, K. Baba, H. Kurokawa, M. Yamagiwa

"The Toyo smelter has expanded its anode production capacity from 126,500 to 239,000 t/year by introducing technical oxygen into blast air for flash and converter furnaces and improving smelting facilities. Significant efforts were made in the expansion not to increase the number of workers, which mean development of some automation systems for the copper converters and anode casting wheel. The efforts have resulted in the above-mentioned increase in productivity and a saving of production cost as well as a decrease in the number of workers for the anode casting operation.IntroductionThe Toyo smelter has been performing a highly stable and pollution free operation since its commencement in 1971 (1). Its distinctive features are the on-line control by process computer (2) and the high productivity without trouble. But owing to the so-called oil crisis in 1979, we were faced with a sharp increase in production cost. To decrease the production cost, some measures for saving of energy were planned and carried out, such as conversion from oil to coal in a flash furnace (3), the heat recovery from converter slag and the introduction of technical oxygen in blast air with the intention of energy saving as much as possible.The first increase in production capacity and some savings of production cost were attained in 1982 by the introduction of technical oxygen in blast air for the flash furnace without major modification of the furnace as shown in Table I. The capacity of an oxygen plant is 7,800 Nm3/H as 90% O2 . Part of oxygen from the plant is also supplied to tuyeres of copper converters through an oxygen holding tank with a volume of 830 m3 at 7 kg/cm2-G."

Jan 1, 1989

By Matthew D. Andriese, Jiann-Yang Hwang, Zhiwei Peng

"It has been demonstrated that metallic-bearing minerals are physically liberated from host rock when exposed to microwave (MW) energy. The metallic minerals are iron sulfides and spinel oxide minerals contained in peridotite rock. Experimental evidence has shown ore particles readily couple with MW energy at 2.45 GHz, 1000 W resulting in rapid heating. Thermal stresses are generated by highly absorbing metallic-bearing minerals resulting in cracking and embrittlement of ore particles that assists in crushing and grinding processes. The liberated metallic-bearing minerals are shown to report to coarser size fractions as a result of MW exposure.IntroductionComminution of ore material during beneficiation is a large energy expenditure for the mineral processing industry. Crushing and grinding operations alone consume 50-70% amount of energy used in mineral processing [1]. Size reduction becomes increasingly difficult with decreasing particle size making grinding the most energy-intensive step of comminution. The aim of comminution is to maximize liberation of economically valuable minerals from the host rock [2]. Overall, the less material that needs to be handled, then grinded, to create a useful product for hydro/pyro metallurgical processes will achieve the greatest reduction of energy.Much of the scientific interest for use of microwave (MW) energy in mineral processing has been for improved hydro/pyro metallurgical techniques [3-6]. Early authors have employed MW energy for improved grinding of ore particles but most conclude the energy savings do not justify the energy input [7-9]. The effectiveness of MW assisted grinding is dependent on the ore mineralogy and the absorptive properties of minerals contained within it. Ore containing magnetic minerals should prove successful with MW assisted breakage from highly absorptive properties."

Jan 1, 2012

By D. T. Smith, L. M. Hsiung, J. J. Schmitt, J. W. Golz, R. L. Lankey, H. N. G. Wadley, J. Z. Zhang, B. L. Halpern

"The microstructure and mechanical properties of Al/AI2O 3 metal-oxide nanolaminates fabricated by' a novel Jet Vapor Deposition (JVD) process at substrate temperatures of ~25° and -250°C have been investigated using transmission electron microscopy (TEM) and nanoindentation methods. The thickness of the oxide layer was held constant between 2 and 5 nm, whilst the Al layer thickness was systematically varied from -3 to -50 nm. Continuity of the Al layers was significantly improved when the nanolaminates were deposited at an elevated substrate temperature (-250°C). The yield strength of the nanolamintes with Al layers greater than -25 nm follows a Hall-Petch type relationship, whereas that of the nanolaminates with Al layers less than -25 nm is better predicted by a Koehler-Lehoczky strengthening model. IntroductionAluminum-aluminum oxide (presumably A12O3) nanolaminates have been recently fabricated using a novel Jet Vapor Deposition (ND) process developed and patented by Jet Process Corporation [1-4]. ND uses sonic, high purity helium (He) gas jets to entrain atomically dispersed vapor and deposit films. It is of interest here because it can deposit multilayered structures (laminates) inexpensively at high rates. Materials with a thin, multilayer structure are of interest because they potentially offer novel mechanical and physical properties [5]. Koehler in 1970 used an image force model to investigate the strength of laminated materials and proposed the use of alternating layers of high and low shear modulus metals to produce high strength composite materials [6]. He predicted that dislocations would have to overcome a large repulsive image force in order to move from metal layer B of lower shear modulus (uB) into metal layer A of higher shear modulus (uA)' The image force (F) is given by the relation:"

Jan 1, 1994

By M. Tamura, K. Fujita, K Shinozuka, H. Daimon, H. Esaka

"In-situ observation of unidirectional solidification using transparent substance has been performed to investigate the growth direction of solid phase. Cell or dendrite of which preferred growth direction is not parallel to the heat flow direction was observed with various solidification conditions. Dimensionless growth direction (p) changes from 0 to 1 with increasing growth velocity at a constant temperature gradient. Introducing the dimensionless growth velocity, the relation between p and growth condition could be correlated.IntroductionTransition in macroscopic solidified structure from chill to columnar zone which is found in normal castings takes place via grain selection1). Cast products such as turbine blades are unidirectionally solidified, grain selection plays an important role to choose suitable crystals which have reasonable orientation in the region called ""starter"", which is a very initial part of casting2). Therefore, grain selection is a very important process in the formation of casting structure. The present authors have been studying on the process of grain selection using succinonitrile, which is a transparent organic substance and have found that the growth distance necessary for grain selection depends upon the solidification condition3-5). When the solid/liquid interface is dendritic, the grain selection occurs quickly. On the other hand, when the solid/liquid interface is cellular, it occurs slowly. We supposed that the growth direction of dendrite is different from that of cell when the substance is unidirectionally solidified. Indeed, Kurz and Fisher wrote in their text book that dendrite grows along its preferred growth direction, <100>, regardless of heat flow direction and that cell grows along heat flow direction regardless of its preferred growth direction1). However, there is no quantitative description about the growth direction when the solid/liquid interfacial morphology is cellular. Furthermore, there have been little works6) to study the growth direction of cell and dendrite."

Jan 1, 2000

By Hiroshi Nakajima, Kotobu Nagai, Toshihiro Hanamura

"Low carbon ferritic steel bars with ultra-fine grain structure was developed through a warm rolling for the first time by the present authors. They show better low temperature toughness than conventionally hot-rolled plates. Hence, the brittle fracture surfaces in Charpy tests were examined in terms of the effective grain size of fracture, compared with those of conventional QT steels. The ductile-to-brittle transition temperatures were in good accordance with those for the QT steels if referred to the effective grain size of fracture: · However, the size was a few times that of the ferrite grain. This means the grain refining is not yet fully utilized from the viewpoint of low temperature toughness. The anisotropy of· the impact properties and the annealing effect of highly dislocated structure on the toughness are also discussed in the present paper.IntroductionFor structural materials, both high strength and good toughness are required. Well-known approaches for obtaining better toughness for steels are as follows:1) Grain refining2) Addition of Ni3) Thin plate effect by cracking parallel to the rolling direction prior to crack propagation4) Contribution of metastable austenite.Among them, only the grain refining can raise the strength and improve the toughness. And it is well known that the finer the ferrite grain size, the lower the ductile-to-brittle transition temperature. For example, in the case of 0.11 carbon steel, the transition temperature decreases linearly to in d 1/2 [1 ]. However, these have been told in the regime of coarse grain size that is larger than 10 µm in diameter. There ~as .been no study dealing with the low temperature toughness in the regime of ultra-fine grain size with a diameter in the order of 1 µm."

Jan 1, 2000

By Eiichi Kuzuno, Atsushi Shibayama, Toyohisa Fujita, Kazuo Koike, Toshio Miyazaki, Hitoshi Masuda

"A solid sulfur is more useful to recover and store than a sulfuric acid as a by-product in the zinc hydrometallurgy. In this experiment a zin concentrate (sphalerite) was leached with ferric sulfate at about 373 K for 3 to 6 hours. Zinc was leached more than 95%. After a solid-liquid separation, the leached residue contained solid sulfur was obtained. The particles in the residue were dispersed by lignin and the solid sulfur of approximately 85% was recovered as float product by a flotation with frother in the pH 4. The dried float product was heated at 413K for 2 hours. The pure solid sulfur was recovered. On the other hand in the leached liquid a zinc oxide was ·added and ferrous .iron was oxidized to ferric iron by blowing oxygen. This ferric iron was returned to the zinc leached process after solid-liquid separation.IntroductionZinc concentrate is usually roasted as pretreatment in zinc hydrometallurgy and the produced S02 is changed to sulfuric acid. However, recently in Japan the utilization of sulfuric acid has been limited and it is more costly to store. Instead of producing sulfutic acid the solid sulfur recovery has been examined by direct leaching of zinc_ concentrate in this experiment.In the direct leaching, several kinds of effects have been studied for leaching of sphalerite in ferric sulfate solution. The addition of lignine siilfonate1 • 2) and fine· grinding3) increases the · speed arid leaching fraction of sphalerite. The leaching ratio depends on impurities in sphalerite ores4 • 5). Here, the zinc concentrate is leached ferric sulfate solution under atmospheric pressure at 373K. The solid sulfur in leached residue is separated as float products from other solids by sink-float separation and flotation. The sulfur in float products is purified by evaporation at 413K and recovered."

Jan 1, 2000

By Khoo Khyou Pin, Yoshiyuki Funaki, Hirotsugu Takeuchi, Ryoichi Urao, Naotatsu Asahi

"Steel is used to be ion carburized with mixing gas of methane and hydrogen. In carburizing, carbon in the methane decomposes and deposits on the steel by plasma, so methane gas flow may influence on ion carburizing of the steel. An apparatus in which works can transfer preheating, ion-carburizing and diffusion treating zones continuously was made for effective carburizing of steel. The gases were flown into above three zones with three different gas inlets. The hardness and microstructure of the works were investigated after ion carburizing and quenching. The steel is carburized deeper near the carburizing gas flow nozzle of the inlet than far from the nozzle. Hard surface layer fom1ed by quenching of ion-carburized steel.IntroductionGas carburizing is used for a surface hardening treatment which decreases fatigue and wear of the industrial parts used in automobile, machines etc. Ion and vacuum carburizing have been developed recently and applied to some industrial parts of restrictive purposes. The ion carburizing treatment which uses hollow cathode discharge (HCD ion-carburizing) is superior in energy saving, resource saving, environmental cleanness to the other carburizing treatment. Specially, carburizing energy can be saved in HCD ion-carburizing, because highly heated zone can be restricted in the range between work and subsidiary cathode where hollow cathode discharge arises, and the work is carburized in shorter tin1e in HCD ion carburizing method than other carburizing methods. Three treatments of preheating, carburizing methods and carbon potential controlling by hollow cathode discharge tried to be carried out in one continuous transferring series to carburize works more effectively, so the HCD ion-carburizing apparatus with continuous transferring system was made and gears of works were HCD ion-carburized in continuous transferring. The works were rotated themselves to get homogeneous carburizing by continuous transferring in glow of hollow cathode discharge."

Jan 1, 2000

By J. V. Happ

The investigation reported in this paper was prompted by the belief that vacuum processing of copper mattes could provide significant advancement to present-day copper smelting and converting technology. Specifically, vacuum distillation of copper mattes in a unit such as the R.H. vessel used in vacuum degassing of steel, can lead to improvements in: converter flue-gas-cleaning system, purity of acid (or liquid SO2), aisle hygiene, purity of electrorefined copper and smelter flexibility. In the study conducted, removal of Volatile impurities (arsenic, antimony, bismuth, lead and zinc) from liquid mattes, by vacuum distillation in a laboratory-scale equipment was performed. The conditions investigated covered a temperature range of 1123-1223K, absolute pressure of 6.5-0.5kPa (50 - 3 mm Hg) and with bleed gas consisting either of pure oxygen or argon. Six matte samples (four U.S. and two foreign) were tested. Under the "best" conditions arsenic and antimony were reduced to << 0.01% in the product matte. The removal of bismuth, lead and zinc was variable and appeared to be influenced by the matte composition of the sample. As might be expected, the rates of distillation of the various species were increased at higher temperatures and lower absolute pressures. The influence of a small flow rate of gas (02 or Ar) over the melt did not have a signifi¬cant influence on the extent of impurity removal. The magnetite content of the matte was reduced by up to 30% during vacuum treatment and was favored by a low partial pressure of oxygen over the melt. Substantial amounts of sulfur were also evaporated and an, overall increase in copper grade of the matte was realized. The paper concludes with an evaluation of industrial aspects of the process as applied to conventional smelters.

Jan 1, 1983

By Robert Kozicki, Eric Graham, George Wrightson

"IntroductionThe manufacture of Ferro Chromium involves the smelting of various ores and fluxes to produce the metallic product.Slag is inherent in the process. It has a much lower density than the metallic FeCr. Some chrome may be trapped in the slag as either FeCr or Cr203.Previous methods to estimate the slag in the FeCr have revolved around separating the slag and metallic portions by exploiting the differences in density. The downside with that procedure is that material will often contain pieces that are adhered FeCr and slag. The Metallic FeCr may also be completely encapsulated in the slag.An alternative and more precise method involves calculating the slag content based on chemical analysis of Mg and Al. The Mg and Al will be at relatively low levels (less than 0.1 % ) in the Metallic FeCr pieces and considerably higher in the slag (3% or greater). The overall sample will have a proportional amount and is calculated using simultaneous equations with the assumption there is only one kind of slag and one kind ofFeCr present. ""Pure"" slag and ""pure"" FeCr are needed in order to determine the Mg and Al in each. The detemlination of the Mg and Al in the overall sample would then be used to calculate the amount of slag.When the particle size is small, it is difficult to sample and get ""pure"" pieces of the slag and FeCr of sufficient quantity to perform a proper analysis. Often, historic data is used but that is dependent on the source of the FeCr and the materials used in its production. Mg and Al levels in slag can vary between 3% and 20% in different FeCr slags depending on their origin."

Jan 1, 2013

By Donghai Li, Cheng Pan, Xuyang Liu, Xuewei Lv, Chenguang Bai

"Fine chromite ore is the common raw material to produce ferrochrome alloy through the submerged electric furnace process. The electric resistivity of fine chromite ore plays an important role in the operation efficiency because it determines the current distribution. The effect of particle size and the contact area of the particles on electric resistivity for several of chromite were investigated at room temperature, and the relationship between the electric resistivity of mixed particles and the volume fraction of lump ore to fine ore was also studied. The results shown that the electric resistivity increases with the increase of particle size, and the electric resistivity of mixture decreases with the increase of volume ratio of fine ore.IntroductionChromium is one of the most important alloying elements in manufacturing of stainless steel that used at high temperature and corrosive environment applications [I, 2]. As the raw materials to be charged into the steel, ferrochromium alloys and charge chromium are produced directly by smelting of chromite ore with the reducing agent in submerged electric arc furnace (SAF). During the process, the oxides of chromium and iron were reduced by carbon and meanwhile the electrical energy were consumed [3,4]. The ideal industrial process is to achieve high recovery level of Cr and Fe with minimal power consumption. In SAF process, the electric resistivity of charge stock has significant effect on the current distribution, which determines the heat distribution, molten bath structure and chemical reactions in the furnace. High resistance of the charge is desired to reduce the current distribution through the charge stock, thus the electrodes may insert into the charge stock with proper depth to form a high temperature arc heat source, and proper smelting can be realized[5]."

Jan 1, 2012

By Krishna Kumar

"Growth of electronics waste (e-waste) and lack of appropriate disposal mechanism are the great concern for developing countries like India. The domestic generation of e-waste in India is rapidly growing with the development. The imported substance is also substantially contributing to the e-waste inventory. Recycling of e-waste is mainly carried out in unorganized units in India. The primitive recycling technique used by the unorganized sector is a great threat to the environment and the health of the operators involved in these profession. Therefore, improvement of technology used by these units towards a cost effective, environmental friendly alternative could be the solution to the present crisis. Few initiatives of recycling have, however, come up in recent years in organized units. The precious metals are still recycled in the developed countries. This report discusses the inventory, technology status, legal legislative and existing practices of e-waste management in India.1. INTRODUCTIONInnovation, research and development in the field of electronics and information and communication technology (ICT) lead to convenient, independent human life. Consumption of electronics and hardware products has enhanced by manifold. Electronics and hardware sectors have, thus, become the fastest growing sector in the world. Faster obsolescence of these products is forcing users to replace products with an advanced technology. Life cycles of these products are few years. Discarded electronics products are, therefore, accumulating alarmingly in our society. Electronics waste (e-waste) is a crisis not only due to its volume but also for presence of its toxic ingredients, like heavy metals (e.g. lead, mercury, cadmium, hexavalent chromium) and flame retardants such as poly brominated biphenyles and poly brominated diphenyles ether. These substances create potential occupational and environmental health hazardous."

Jan 1, 2011

By D. Kennis

"Union Miniere Precious Metal's (UMPM's) Hoboken Business Unit has a long tradition in complex Pb-Cu metallurgy, focussing on the recovery of precious metals from various types of secondary and recyclable materials. Although the old flow sheet, based on a traditional sinter plant, blast furnace, and lead refinery process was a very complete flow-sheet with the capability of dealing with almost every impurity, the weaknesses became clear:1. old and costly technology,2. too many unit operations,3. too much internal recycling, and4. dependency on concentrates for the sintering process.To maintain the competitiveness of the Hoboken Business Unit, the project ""Smelter 2000"" was born. This project represents a breakthrough in metallurgical processes and technology. A modem smelting technology was chosen together with the development of a new process. A lead-copper process combining lead slag and blister copper production, carried out in an ISASMEL T vessel, was the key to simplifying the Hoboken flowsheet. ISASMEL T smelting technology was chosen for its flexibility towards feed characteristics and process parameters.The new smelter was commissioned at the end of 1997. Although there were a lot of problems due to the high degree of technical innovations in the process, the new smelter came to design capacity within 1 year after start-up. During this period, however, UMPM had, a very difficult time because of the extreme clear-cut nature of going from the old to the new flowsheet.After two and a half years of operation, the new flowsheet has proven to fit with the strategy of UMPM, focussing on treating secondary Pb-Cu materials and a broad range of recyclable feeds such as electronic scrap (E-scrap) and catalysts. Together with the new Precious Metals Plant, efficient logistics, recognised world class sampling practices and a customer-focussed commercial organisation, UMPM Hoboken can definitely be considered reborn."

Jan 1, 2000

By Bora Derin, Onuralp Yucel, M. Seref Sonmez, Murat Alkan

"Latest stage in the production of boron carbide by metallothermic methods using magnesium was the leaching process. Boron carbide particles obtained by self-propagating high temperature synthesis contained several impurities such as magnesium oxide and magnesium borates after the metallothermic reactions. Removal of such contaminates by hydrometallurgical methods required to produce high purity boron carbide. Leaching by concentrated hydrochloric acid solutions resulted in the production of pure boron carbide together with high magnesium and boron containing solutions. Removal of such ions from the spent liquor was the necessity to have dischargeable solution. In this study, precipitation of magnesium and boron compounds from relevant chloride containing spent liquors and the production of saleable products was aimed. The effects of chemical reagents, pH of the solution on the precipitation efficiency of magnesium and boron compounds were investigated in the study. Chemical analysis and the characterisationof solid phases by using x-ray diffraction analysis were the latest stage.Introduction A variety of advanced ceramics, inter-metallic, organic and inorganic compounds, oxygen free single crystals, and polymers can be synthesized by using different SHS techniques [1, 2, 3]. In the SHS process, after initiation, reaction becomes self-sustaining and propagates in the reactant mixture. A high amount of heat which is generated during the process accelerates the reaction rate and thus it makes the process highly productive and economically feasible for different production scales. After the SHS process obtained powder mixture needs to reacted with acidic solutions to purify the product. In this case B2O3 was reacted together with C and Mg to synthesis fine B4C powder resulted in the production of MgO as well according to the Eq. 1 and then MgO was removed from the mixture by leaching with the concentrated HCl solution as shown in Eq. 2, respectively [4, 5]."

Jan 1, 2008

By Takahiko Okura

"It is said that the energy and resources crisis will come before long because the lifetime of known deposits of crude oil and common metals such as Pb, Zn, Cu is estimated to be less than 50 years. Establishing the sustainable society by means of resources-recycling has become an absolute necessity.The non-ferrous metals industry in Japan has been involved in the resource- recycling business for many years, along with the introduction and enforcement of various legislations to preserve the environment and natural resources. Including process-linkage during various manufacturing activities, the non-ferrous metals industry, the iron-making and cement industries are treating considerable amounts of recycled materials and wastes, in an environmentally-sound and economic manner.The Mining and Materials Processing Institute of Japan has submitted “The present and issues in Japanese non-ferrous metals and recycling industries.”The topic of the paper is to highlight the actual conditions within the resources-recycling structures and the present issues.IntroductionGlobalization has been changing the world, introducing the spike of energy and metals price. In addition, the preservation of the environment has also been strongly facing the crisis and many people have been aggrieved by both shortage and the increment in the price of the meals.In the world of metals, even though their reserves are coming depleted, the production rates are increasing, and then the industry has to enhance their productivity under stricter environmental regulations. The Japanese industry experimented the same scenario some 40 years ago, facing big pollution problems, but concurred them and enhanced the technology to overcome the more severe regulations. It will be fruitful to present the current situation in the Japanese industry for the world. The present issues are also presented."

Jan 1, 2008

By Biserka Lucheva, Tzonio Tzonev

"A unique DC electric arc rotary furnace with capacity 150 kg has been designed and constructed for the recycling of low-quality scrap and aluminum dross. The main constructive feature of this furnace is that the axially positioned graphite electrodes (cathode and anode) are placed 100 mm away from the rotation axis of the furnace. A specific characteristic of the construction is the possibility one of the electrodes (the anode) apart from moving axially (parallel to the furnace axis) to move at 90° outside the working space. High recovery rate of metal aluminum from aluminum dross (92%) was realized in this furnace. This is the reason for construction of industrial DC electric arc furnace.IntroductionThe consumption of aluminum waste has been rising continuously on a world scale, which is a great stimulus for the development of the technology for aluminum recycling.To recover the aluminum in dross, the conventional recycling process uses salt rotary furnaces heated with a fuel or a gas burner. This treatment process produces a secondary dross containing alumina, salts, impurities and a small amount of aluminum. Molten aluminum is tapped from the furnace and the residue is then dumped from the furnace. It has been the practice to dispose the residue in a landfill. Improvement of this technology, known as the oxy-fuel process, uses a gas burner enriched with oxygen to increase the thermal efficiency [1]. Recent studies show that the most efficient aggregate for recycling of aluminum scrap has turned out to be the rotary tilting furnaces, heated by plasma or electric arc, for which the use of flux is not necessary [2,3].Accordingly, there is a substantial need in the industry for an improved process for recovering free aluminium. It is particularly desirable that such process be cost effective and ecologically safe."

Jan 1, 2008

By Vittorio Basilico, Marco Quattrone, Mario Bassan

"In Italian building market one of the reasons that often stop building contractors from not taking into consideration the possibility to recycle rubble from building is represented by the increase of costs for rubble separation. However the recycling of C&DW can also allow a decrease in disposal costs and a reduction in raw materials requirement.In this paper the results of a testing conducted on a case study through economic and technical analyses are presented.Results highlight that a wise management of demolition and disposal processes can generate a remarkable saving and that it is possible, on the other side, to achieve environmental benefits such as reduction of raw material consumption and dump life lengthening.IntroductionTwo major factors have been found to have considerably influenced the market of recycled aggregates in Europe and Italy: the EU and national regulations and environmental awareness. The market of recycled aggregate has grown in countries with limited natural resources.Waste disposal has also been one of the top EU political and environmental priorities. In the complex interaction between human activities and the environment, waste is proved to be one of the most environment-degrading products.In 1972 the European Commission introduced measures on waste reduction, reuse and recycling. In 2006, directive 2006/12/EC (European Commission) on waste was issued. It covers the scope of minimizing the waste, prevent hazardous waste, maximize reclamation, reuse, recycling and energy-recovery.No specific directive refers to management and recycling of construction and demolition wastes. However, in 1992 the European Commission listed debris among waste management priorities because of its growing amount.Only recently, effective environmental policies have been implemented in Italy, even though relevant environmental issues started rising as early as the beginning of the 1970s. In the 1980s the Government undertook the first significant measures to handle the waste management."

Jan 1, 2008

By František Molnar, Zsolt Szentirmai, Juraj Schmiedl, Felix Sekula

"Hydrometallurgical nickel production in Sered Nickel Plant (Slovakia) that treated roasted Albanian ore left behind a considerable amount of the solid leaching residue. About 6 million tons of this fine-powder residue containing approximately 52 wt.% of iron in the form of oxides is to the present day stored in a stockpile. However, its iron content makes it a potentially interesting secondary raw material for iron production. This secondary raw material is not, unfortunately, suitable for direct treatment in iron and steelmaking processes.This paper presents results of the laboratory tests of pyrometallurgical method of processing of the leaching residue by its roasting and subsequent refining melting. The objective of the selective reducing agglomeration roasting was to reduce iron oxides and to simultaneously avoid reduction of chromium oxides and silica. Refining melting is carried out in an inert atmosphere. The products of melting are technically pure iron and slag.IntroductionThe leaching residue stockpiled on waste dump near already non-existing Nickel Plant Sered, Slovakia, is considered to be one of the most important environmental burdens in this country. The 40-years of an on-going effort focused on finding the methods for extracting metals and thus remove the waste dump have not been successful [1,4,5,6]. From the literature survey it is evident that past investigations have been following three main routes:1.Removal of chromium by mineral processing methods prior to its metallurgical treatment to achieve final chromium concentrations below 0.3 wt.%.2.Pelletization of solid leaching residue and its subsequent reduction in blast furnace and steelmaking plant and simultaneous removal of chromium.3.Pelletization of solid leaching residue followed by metallurgical processing of preliminary reduced semi-product in electric arc furnace (EAF) accompanied by partial reduction of chromium."

Jan 1, 2008