By Xiyun Yang, Hui Xu, Xichang Shi, Xiang Xiao

"Rod-like magnetite particles were prepared by precipitation of iron salts with urea under the induction of magnetic field. Temperature and initial Fe3+/Fe2+ ratio have a significant effect on the composition of the product. Magnetite particles change from spherical into rod shape in the presence of a 0.35 T magnetic field, The addition of a small amount of spherical seeds increases the rod-like magnetite particles yield. The seeds are prepared by aging ferrous and ferric solution with sodium hydroxide as precipitator. The aspect ratio of the rod is controlled by varying the volume ratio of seed to iron salt.IntroductionMagnetite, an important member of magnetic materials, has attracted a lot of attentions for its super magnetic properties. The rod-like magnetite particles have high anisotropy and coercive force as well as super magnetic properties compared to other shapes, and are widely used as high magnetic density media, magnetic devices and microwave materials [1-4]. Recent studies have found that magnetic field can direct magnetite growing along easy magnetization axis to get one-dimension particles [5-6]. Chen et al. [7] synthesized single crystalline nanorod magnetite under magnetic field. Wang et al. [8] discovered that magnetite grew along easy-magnetization directions under 0.35T magnetic field. Vereda et al. [9-1 O] found that magnetic field had a dramatic effect on the morphology, inducing the aggregates to line along one direction to form rodlike particles.At present, most of the synthesis methods reported in the literature result in a low yield of rod particles and the aspect ratio are difficult to control. Recently, we developed a seed-mediated growth approach to making rod-like particles in an aqueous solution. The spherical magnetite generated by oxidation serves as a seed. These seeds are then added to a solution containing iron salt and urea, and provide nucleation sites for magnetite rod growth."

Jan 1, 2011

By Yufeng Guo, Tao Jiang, Jianjun Fan, Haizheng Hao

"Function of High Pressure Roll Grinding (HPRG) in production of oxidized pellets from magnetite concentrate as raw material was systematically studied. It was found that bentonite dosage decreased from 1.3% to 0.8% if specific surface area of magnetite concentrate pretreated by HPRG was up to 2553.41cm2.g-1. The green ball quality improved obviously due to the increase of specific surface area and fine particles content, and the improvements of size distribution and the ballability of pretreated materials. However, the decrease of pellet porosity accelerated the primary solid phase reaction and oxidation reaction, which made the pellets surface form compacted layer that handicapped the diffusion and migration of oxygen, promoting the formation of double layer structure of finished pellet. Consequently, the compression strength of preheated and roasted pellets was not markedly improved by HPRG.IntroductionWith the increase of proportion of pellets in the BF recently, the technical-economic index of BF has obviously been improved. Consequently, the production and the quality of BF pellet are given more attention [1]. However, with the decrease of the quality of iron ore concentrate, the problems such as poor ballability, high bentonite dosage, high preheating and roasting temperature are becoming the great challenges to not only the quality of finished pellets, but also the energy consumption [2, 3]. In order to overcome these problems, mechanical pretreating technologies such as the High Pressure Roll Grinding (HPRG) and Damp-grinding are widely applied. HPRG has a number of advantages such as low energy consumption, high productivity and easy-maintaining. It is more economic and environmentally friendly than the Damp-grinding technology [4, 5]. A great number of experiments have revealed that HPRG can improve the quality of hematite pellets. Although there are some studies of function of HPRG in the magnetite oxidized pellet production, they are not comprehensive and systematic, especially to the preheating and roasting system [1, 2, 6, 7]. Accordingly, the influence of HPRG on the pelletizing system and the preheating and roasting system are systematically studied in production of magnetite oxidized pellets in this article."

Jan 1, 2011

By C. D. Mishra

The recycling potential for any gainful utilisation of the waste products is dictated by their quality, especially the chemical characterisation. The methods commonly used for the analysis of fly ash e.g. wet chemical, AAS, ICP-AES etc are time consuming. The paper describes a rapid XRF-based method for routine analysis of fly ash which involves preparation of local standards, optimisation of sample preparation technique and use of a simple PC-based software to account for interelement effects. The matrix corrected values are found to agree well with the wet chemical data.

Jan 1, 1992

By Ricardo Melamed

Metallic mercury has been extensively used for gold recovery. Although the solubility and mobility of metallic mercury is low, this metal can undergo many transformations, leading to mercury contamination in humans. The complexity of Hg chemistry in the environment reflects its different possible oxidation states and species, with different physical-chemical properties. The interaction of Hg in the terrestrial system, as well as in the aquatic environment, is important to understand the mercury cycle. This paper reports data on the adsorption of Hg onto an Oxisol soil. Results show that the interaction of Hg(II) at the soil-solution interface depends strongly on ligand concentration in solution, which can affect Hg mobility. The presence of the chloride anion in solution increases the mobility of Hg(II) through the soil, due to a relative lower affmity of mercury chloride at the oxide surface. In the absence of chloride, Hg(II) form strong complexes with the surface, and its adsorption behaviour is similar to the adsorption of other hydrolizable cations.

Jan 1, 1996

By I. B. Scorzelli

The aim of this paper is to make a detailed mineralogical characterization of a typical brazilian xenotime and zircon from the Pitinga Mine using SEMIEDS techniques, On the other hand, superficial pretreatments with HCI, HN03 and HF were done to evaluate the modifications on surface compositions and the morphology of the particles for flotation purposes, The studies showed that both xenotime and zircon present very small inclusions of thorite; zircon is strongly metamictizated given rise to malacon. The HF pretreatment deeply affected the morphology of the particles as well as the surface properties in relation to flotation.

Jan 1, 1996

By Katsunori Yamaguchi

A new technique for the removal of tramp-elements from steel scrap has been required from the viewpoint of saving energy and protection of environment. In order to obtain fundamental information on the removal of copper, tin and zinc from molten iron, the extraction method by using of phase separation in the liquid Fe-Pb-C system was investigated at 1453K. A mixture of iron, lead and carbon melted in a carbon crucible separates into two phases of lead and iron containing carbon. The compositions on the miscibility gap in the Fe-Pb-C system are 95.4%Fe-4.5%C-0.1 %Pb and 99.9%Pb-0.I%Fe. The distribution ratios of copper, tin and zinc between the lead and the iron phases, Lx [mass%X in molten Pb]/(mass%X in molten Fe), are 2.2, 2.2 and 1.4, respectively. Seventy percent of copper and tin from iron scrap can be eliminated with comparable lead addition. Gold, silver and palladium are enriched in the lead rich phase, on the contrary platinum and rhodium are more distributed to the iron rich phase than to the lead phase.

Jan 1, 2003

By A. V. Tarasov, V. M. Paretsky

"The knowledge of the true phase composition of the liquid slag is a very important problem, mastering of which grants the possibilities for the scientifically founded choosing of the decoppering method of the autogenous smelting slags. The investigation using different methods of the phase composition of the flash quenched autogenous copper melt's slags has shown, that the most effective method of the slags' decoppering during smelting with the white matte production is the flotation of the recrystallized slags. In this work the authors posed the problem to realize the slags quenching with the rates similar to those, which are used in the modem investigations devoted to the flash quenching of the ironcontaining alloys, with the subsequent study of the quenched samples using the Mossbauer spectroscopy methods in order to establish the connection between the liquid slag's structure and the metals losses with the slag."

Jan 1, 2000

By P. T. Velu, R. G. Reddy

"The use of emf measurements to derive classical thermochemical data has been in use for many years. The reaction associated with electrochemical process is harnessed in a galvanic cell and energy involved measured in terms of electromotive force. The property requirements of sensor electrodes used differ for various aqueous, molten salt and solid electrolyte systems. The electrodes for molten salt electrolytes need special care for construction. This paper describes the studies carried out using an Ag/ AgCI reference electrode. This electrode was used to measure the solubility of compounds in molten salt electrolytes. The results obtained using this electrode are in excellent agreement with the values from chemical analysis method.I. IntroductionThe technique of obtaining a metal from its oxides by electrolysis is more than a century old process now. In these processes, it has been well established that for halide electrolytes, only the dissolved oxides are available for the dissociation at the electrode to release the metal during electrolysis. Therefore, the solubility of metallic oxides in the molten salt electrolytes is an important parameter which determines the economical and technical viability of these processes. The widely used molten salts systems in halides are fluorides and chlorides. The fluoride electrolyte system is used in our present study.The viability of obtaining aluminum alloys by in-situ electrochemical processing has been outlined in our earlier publications[1-8]. Studies on the solubility of various alloying element compounds is a part of our ongoing research efforts for the direct production of Al-Li alloys. As mentioned above, the solubility of lithium oxide and lithium carbonate compounds in molten fluoride electrolyte system have studied using EMF technique. The change in potential of the molten electrolyte was measured by a working electrode against the reference electrode with the addition of lithium compound."

Jan 1, 1997

By Dai Yongnian

The methods of treating zinc crust and its development in the last hundred years are compared and reviewed. There are better effects from normal pressure metallurgy turned into vacuum metallurgy. The traditional methods dezinc only. But we must consider that delead on further step. From lab tests to industrial scale experiment are researched. The first step-dezinc, second-delead, crude ,metal of, zinc, lead and silver are produced, The flowsheet of treating zinc crust are simplified, material consumption reduced, work condition improved, environment protect mended. This method is pointed out that its application can be expanded.

Jan 1, 1992

By Linfeng Zhou, Rong Sun, Guanghui Li, Zhiwei Peng, Tao Jiang

The effects of microwave roasting on separation of rhenium (Re) and molybdenum (Mo) from a molybdenite concentrate have been investigated based on evaluation of the heating characteristics of the concentrate in the microwave field. The results show that a variety of operating variables, namely microwave power, sample weight, sample geometry, roasting temperature, roasting time and atmosphere significantly impact on the volatilization rates of Re and Mo. The optimum conditions for Re-Mo separation are microwave power 1300 W, sample weight 20 g, sample geometry pellets, temperature 600 oC, time 1.5 h, and atmosphere 20%O2. Under these experimental conditions, the volatilization rate of Re reaches 88.12%, while that of Mo is just 5.15%. Microwave-assisted roasting provides an alternative route to separating Re and Mo from molybdenite concentrate.

Jan 1, 2016

By Kazuyoshi Shimakage, Shinji Hirai, Kenji Wada

"An amorphous zirconium oxide coating was prepared by the sol-gel process using zirconium tetra-n-butoxide on the surface of aluminum to improve the corrosion resistance to salt, acid and alkaline attacks. The coating films formed on the smooth aluminum substrates under UV-irradiation indicated an excellent corrosion resistance for salt, acid and alkaline attack tests. For example, the corroded area of coating film in salt attack test for 3600ks in the order of sol-gel coating· film< chromate film <boehmite film, and the sol-gel coating film had the best corrosion resistance. The coating film prepared on the coarse aluminum substrate by a boiling treatment after heat treatment at 573K also had greater corrosion resistance, and a water-avid surface appeared a contact angle of approximately 3°.IntroductionAs given in a previous paper1; a composite film consisting of a porous layer of anodically grown aluminum oxide filled with amorphous zirconium oxide and an amorphous zirconium oxide coating layer deposited thereon via the sol-gel process utilizing the dip-coating technique, was prepared to improve the alkaline corrosion resistance of aluminum. The alkaline corrosion resistance of these composite films was increased in the range of 24 to 50 times those of conventional anodic oxide films anodized in sulfuric acid. As a result, it was proved that heat treatment at 573K after dip-coating was an important process to .remove organic component from gel film and to accelerate the densification of coating layer. Furthermore, the effect of ultraviolet (UV) irradiation at ambient temperature on the densification of coating layer was also examined to lower the heat-treatment temperature2.Then, a sol-gel film prepared by UV irradiation at ambient temperature indicated that alkaline corrosion resistance of aluminum was superior in the range of 2.4 times to 2. 6 times that of the conventional composite film heated at 573K."

Jan 1, 2000

By Petrus Christiaan Pistorius, Farzin Fatollahi-Fard

The production of titanium oxycarbide – a consumable anode material used in molten-salt processes for electrowinning titanium – from heavy mineral concentrate, such as a high-titania leucoxene and natural rutile is described. The oxycarbide is prepared by carbothermic reduction of the oxide at elevated temperature. Particle size distribution (of the titanium oxide raw material) and temperature have large effects on the kinetics of the reaction, which seem to follow a “shrinking-core” model. It is anticipated that low porosity (in the anode pellets) would be advantageous during electrolysis. Particle size distribution, extent of reaction during carbothermic reduction, and sintering temperature are expected to affect pellet porosity after sintering, and are being tested experimentally.

Jan 1, 2015

By Elliot Schwartz, Julian Szekely

"In this paper we describe an experiment that was recently performed on the IML-2 Space Shuttle mission in which the thermophysical properties of molten metals were measured using electromagnetic levitation. In the planning of these experiments calculations had to be performed to predict the levitation and stirring forces, heating rates, sample deformation, and internal flows within the sample. These predictive calculations were essential for both the planning of the experiments and for the re-planning of experimental runs during the actual Space Shuttle mission.Introduction""Materials Processing in the Computer Age"" involves the use of mathematical modeling to obtain a quantitative understanding of the phenomena that govern materials processing operations. Microgravity, or space shuttle experimentation represents a specific case in point here; the very high cost of the space shuttle flights, the very limited flight opportunities that are available, and the tight resources aboard a shuttle clearly mandate that these experiments be very precisely planned and that all possible opportunities for mathematical modeling be fully exploited.The purpose of this paper is to present the results of calculations performed for the planning of a space shuttle experiment involving electromagnetic levitation and wherever possible present a comparison of the computational predictions with both experimental measurements and asymptotic analyses. Finally we shall seek to discuss the practical implications of both the computational methodologies and the potential experimental findings."

Jan 1, 1994

By H. V. R. von Rhaden

Systematic quantitative X-ray diffraction analyses performed on diamond-drill cores originating from the Aandenk formation at the Loraine Gold Mine, located in the Welkom goldfield, Orange Free State, South Africa, have revealed the presence of a number of phyllosilicate mineral assemblages which have not hitherto been reported from this region. Rectorite, a regularly interstratified 1:1 mica-montmorillonite "swelling clay", is found to occur together with paragonite, muscovite, pyrophyllite, kaolinite, and chlorite in highly-altered friable rocks. The presence of rectorite in mill feeds may have potentially serious implications with respect to gold recovery. Quantitative X-ray diffraction analysis for phyllosilicates can be used as an aid to correlation, and also to guide the widths of stopes in underground mining. Rectorite has a unique mode of origin, which is discussed.

Jan 1, 1991

By Chonghun Han, Tae-Hwa Choi, Young-Hwan Chu

"A statistical optimization method is proposed to maintain stable operation in a blast furnace with stave coolers. The objective of this study is to find the operating condition which maximizes productivity as well as minimizes the heat load on the stave coolers. In this method, we first analyzed historical data and calculated the heat flux of stave coolers and the burden distribution by mathematical models. In this approach, we determined the variables to optimize and manipulated variables to adjust these response variables. Next, we collected the necessary data for the data variables after preprocessing such as removal of noise and outlier. Finally, we constructed empirical models describing the patterns of response variables in terms of manipulated variables by partial least squares regression method, and then these models were used as objective functions for entire optimization problem. By using appropriate optimization algorithm, we determined the compromised optimum operating condition considering all response variables from the past operating conditions.IntroductionBlast furnace operation which is accompanied by complex physical and chemical phenomena is an essential process for steel industry. In this process, iron ore which is charged into the blast furnace from the top goes downward. It is reduced to iron by CO gas and is melted by the heat of combustion of coke and pulverized coal. The pig iron is tapped at the bottom in liquid phase after removing the slag, which floats on the pig iron.The cooling equipment of the blast furnace wall is changed from the plate type to the stave cooler recently. In order to cool the shell uniformly and eliminate shell spray cooling, Pohang No.2 blast furnace of POSCO (Pohang Iron & Steel Company) was equipped with 11 rows of stave coolers. These staves are only 350mm-thick including the 170 mm-deep refractory on the hot face."

Jan 1, 2001

By A. Rawat

The removal of oxyanions of arsenic present in mine process water and drinking water to a regulatory level is a challenging problem. Recently a patented adsorbent lanthanum oxide has been developed which has shown strong specificity for the anions of arsenic. In this paper the kinetic and thermodynamic aspects of arsenic adsorption on to lanthanum oxide are discussed. Adsorption tests were performed at different temperatures using synthetic solutions of arsenic of varying concentrations. From the kinetic data and adsorption isotherms thermodynamic properties such as Gibb&apos;s free energy, standard enthalpy of adsorption, standard entropy, isosteric heat of adsorption and activation energy were determined. The results showed that temperature had a positive effect on the rate and degree of adsorption:The activation energy decreased with increase in the initial concentration thus indicating solute-solute interactions in the system. Also, the isosteric heat was found to decrease with increase in the adsorption density implying a heterogeneous adsorbent surface.

Jan 1, 1998

By P. R. Taylor

Titanium carbide and titanium diboride powders have been successfully synthesized by direct treatment of ilmenite concentrates in a non-transferred arc thermal plasma reactor. Methane gas was used as the reducing agent and boron oxide was used as the boron source in these processes. Free energy minimization plots were used to predict the behavior of each system under different molar ratios and operating conditions. Products were characterized by XRD, SEM and chemical analytical techniques. The average size of the ceramic product is in the submicron range. Metallic iron apparently is finely deposited on the surface of the titanium carbide or titanium diboride particles. Minor impurities such as silica, manganese and zircon were converted to the carbide form.

Jan 1, 1995

By Jafar Safarian, Merete Tangstad, Leiv Kolbeinsen

"Silicon and its binary alloys have several applications in metallurgical, chemical, photovoltaic and semiconductor industries. Silicon goes to its liquid state within its production, refining and when it is alloyed with other elements. Therefore, the characterization of silicon melts thermodynamics is important and useful. The liquidus and activities in several silicon binary systems have been recently calculated by the application of two liquidus constants, which were established using the experimentally determined liquidus data. In the present study, the thermodynamic properties of six silicon binary melts, which are simple eutectics, are calculated by analytical approaches. In this case, the changes in the partial and integral Gibbs free energies and enthalpies of mixing are calculated and compared with the experimental data in literature. The enthalpies are calculated by two methods and the calculation results are compared to the data from the literature. It is shown that thermodynamic properties of silicon binary melts can be accurately predicted without the use of complicated thermodynamic software.IntroductionSilicon and its alloys have several industrial applications. Silicon is used for making aluminium-silicon alloys to produce cast parts, mainly for automotive industry. Silicon in the form of ferro-silicon is used to deoxidize and alloy steel and cast iron. The photovoltaic (PV) industry has had a rapid growth in the recent years and silicon is the dominant material used for the fabrication of solar cells. Silicon is primarily produced through carbothermic reduction of quartz in electric arc furnaces and the produced metallurgical grade silicon (MG-Si) contains around 1 wt% impurities. It is further refined to produce solar grade silicon (SoG-Si) with above 99.9999 wt% Si to fulfil the chemical requirement for PV application. Since molten silicon is processed all along the metallurgical route, obtaining fundamental thermodynamics knowledge about silicon melts is valuable for the related industries."

Jan 1, 2012

By Hong Ro Lee, Seang Suk Cho, Byung Sun Chun, Chang Whan Won

"The preparation of Al203-SiC-TiC composite powders was studied by SHS process using silica (source of Si02) powder instead of Si which is expensive. And, aluminum powder was used as reducing agent of silica and charcoal activated was used as carbon source. Effects of the molar ratio in raw material mixtures and compaction pressure and initial temperature of reactant on the products and combustion process were studied. The most important variable affecting the synthesis of Al203-SiC-TiC was the molar ratio of carbon. The combustion reaction generated in powder state without preheating. But the unreactants exist in the product on all molar ratio. When the preheating temperature is over 400 °C, the combustion reaction was able to be generated in pellet state. Without preheating, the combustion reaction was possible by Ti02 addition. The optimum condition in this system was the molar ratio of Si02:Ti02:Al:C=2.5:0.5:4:3.1. INTRODUCTIONCeramics have demonstrated a capability as a cutting tool, especially in competition with WC-Co cermets (ceramic-metal composites) as inserts for metal turning and milling operation. The advantage of ceramics compared with carbides is retention of high hardness, strength, and chemical inertness to temperatures in excess of 1000 ·c . This allows use of the ceramics at much higher machining speeds than can be tolerated by carbides. However, the ceramics have lower toughness than the carbide materials, and have only been used successfully in the limited operations of turning and milling. There are several classes of cutting tools. The addition of TiC or PSZ, or both, and reinforcement with SiC overcame the poor fracture toughness and thermal-shock resistance that limited Al203 use in the past [1]."

Jan 1, 1998

By Bradford C. Wesstrom

The extraction of metals from Copper Refinery Slimes may involve many different processes. This paper describes the use of pressure leaching for decopperizing of copper refinery slimes at the El Paso Refinery. Process equipment will be described, along with the process chemistry, unit operations and unit processes associated with the decopperizing process. Copper contained in the raw slimes ranges from 15-35%. After autoclaving less than 1 % copper remains.

Jan 1, 2000